solid state ionics: a japan perspective · from the beginning of electrochemistry, as an indivis-...

Science and Technology of advanced MaTerialS, 2017vol. 18, no. 1, 504–527https://doi.org/10.1080/14686996.2017.1328955

KEYWORDSSolid state ionics; solid electrolyte; ionic conductor; mixed conductor; diffusion; average structure; solid state battery; sensor; fuel cell

ARTICLE HISTORYreceived 17 March 2016 revised 15 March 2017 accepted 8 May 2017

© 2017 The author(s). Published by national institute for Materials Science in partnership with Taylor & francis.This is an open access article distributed under the terms of the creative commons attribution license (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

CONTACT osamu yamamoto [email protected]

CLASSIFICATION50 energy materials; 207 fuel cells / Batteries / Super capacitors; 206 energy conversion / transport / storage / recovery

Solid state ionics: a Japan perspective

Osamu Yamamoto

graduate School of engineering, Mie University, Tsu, Japan

ABSTRACTThe 70-year history of scientific endeavor of solid state ionics research in Japan is reviewed to show the contribution of Japanese scientists to the basic science of solid state ionics and its applications. The term ‘solid state ionics’ was defined by Takehiko Takahashi of Nagoya University, Japan: it refers to ions in solids, especially solids that exhibit high ionic conductivity at a fairly low temperature below their melting points. During the last few decades of exploration, many ion conducting solids have been discovered in Japan such as the copper-ion conductor Rb4Cu16I7Cl13, proton conductor SrCe1–xYxO3, oxide-ion conductor La0.9Sr0.9Ga0.9Mg0.1O3, and lithium-ion conductor Li10GeP2S12. Rb4Cu16I7Cl13 has a conductivity of 0.33 S cm–1 at 25 °C, which is the highest of all room temperature ion conductive solid electrolytes reported to date, and Li10GeP2S12 has a conductivity of 0.012 S cm–1 at 25 °C, which is the highest among lithium-ion conductors reported to date. Research on high-temperature proton conducting ceramics began in Japan. The history, the discovery of novel ionic conductors and the story behind them are summarized along with basic science and technology.

OPEN ACCESS

1. Introduction

The scientific term ‘ionics’ has been commonly used, from the beginning of electrochemistry, as an indivis-ible pair of components of the electrochemistry disci-pline together with ‘electrodics’, and majority of ionics research has been limited to aqueous or liquid electro-lytes. Looking back at the history after the pioneering works of Faraday, who found ion transport not only in liquid electrolytes but also in solids of Ag2S and PbF2, one may find that only little attention has been payed to ‘solid ionics’ materials, in contrast to the rich and variety applications of ‘liquid’ electrochemistry. The dis-advantage of low conductivity in electrochemical appli-cations at low temperatures, which has been considered as a detrimental problem, overrides advantages, such as applications at elevated temperatures, possible integra-tion with other solid devices, and so on. From the Nernst

grower, the first practical application of solid state ionics materials, to oxygen sensors to monitor oxygen activ-ity in molten metals and exhaust gas from combustion engines, only zirconia-based ceramics materials have been used in limited applications of potentiometric use at high temperatures.

About 130 years after Faraday’s discovery, the term ‘solid state ionics’ was introduced and defined by Takehiko Takahashi of Nagoya University, Japan. He first used the term ‘solid ionics’ in a paper submitted to Denki Kagaku in 1967 [1], the title of which was ‘Study on solid ionics-electrical conductivity of solid electro-lyte: electrical conductivity in a Ag2S-HgI2 system’. The coincidence of the materials used by Faraday’s discovery suggests the presence of limited materials systems that show fast ion conductivity. Later, Professor Takahashi submitted another paper, in 1971, to the Journal of the

http://creativecommons.org/licenses/by/4.0/

mailto: [email protected]

http://www.tandfonline.com

http://crossmark.crossref.org/dialog/?doi=10.1080/23080477.2017.1348061&domain=pdf

Sci. Technol. Adv. Mater. 18 (2017) 505 O. YAMAMOTO

Electrochemical Society. The term, ‘solid ionics’, was slightly modified and this was the very first article that used ‘solid state ionics’ in its title: ‘Solid-state ionics—coulometric titrations and measurements of the ionic conductivity of beta Ag2Se and beta Ag2Te and use of these compounds in an electrochemical analog memory element’ [2]. Still, the materials are closely related to the one discovered by Faraday. One of the hopes behind the modification of the name to ‘solid state ionics’ includes a wish for ‘solid state ionics’ to become as popular as ‘solid state electronics’, which had been quite rapidly grow-ing, and became a core of the science and engineering field. The term was also used in ‘The Third International Conference on Solid Electrolyte-Solid State Ionics and Galvanic Cells’, held in 1980 in Tokyo, Japan, where the definition of solid state ionics was introduced as the phenomena related to mobile ions in solids; more pre-cisely, ‘solid state ionics’ as a science about solids that can exhibit extraordinarily high ionic conductivity at a fairly low temperature, far below their melting points, and applications as electrochemical devices [3]. After the fourth conference in 1983 in Grenoble, France, the conference name was consolidated as ‘International Conference on Solid State Ionics’, and this series of con-ference has been held to date. Elsevier launched a new international journal, Solid State Ionics in 1980, and the term was thus widely accepted as a branch of solid state science and its applications in international scientific communities.

Professor T. Takahashi (1916–1995)

In Japan, the main research activity in the field of solid state ionics (SSI) started in the early 1950s. The early studies focused on the crystal structure analysis and phase transition in highly ion conductive solid elec-trolytes, such as silver and copper halides and chalco-genides, which exhibit high ionic conductivity at high temperatures. One of the first reports in this field was published in 1952 in the Journal of the Physical Society of Japan by Miyake, Hoshino, and Takenaka [4]. In 1966, Yokota proposed a caterpillar mechanism for the correlated diffusion of Ag+ ions in silver-ion solid con-ductors [5]. During the past few decades, many highly ion conductive solid electrolytes were found in Japan; a copper-ion conducting solid Rb4Cu16I7Cl13 by Yamamoto and co-workers in 1979 [6], proton conducting oxides

of composition SrCe1-xYxO3 by Iwahara and co-work-ers in 1981 [7], oxide-ion conducting solid Sr-doped LaGaO3 by Ishihara and co-workers in 1994 [8], and lith-ium-ion conducting sulfide Li10GeP2S12 by Kanno and co-workers in 2011 [9]. The first domestic solid state ionics symposium was held in 1972 in Nagoya, Japan. Twenty-four papers were presented at this symposium, at which the main research topics were ion conduction mechanisms, the conducting behaviors of Ag+, Cu+, Na+, and O2- ion conductors, and the application of these materials in sensors and batteries. A total of 118 papers were presented at the 38th symposium in 2012, at which the main research topics were electrode materials and electrolytes for lithium batteries and oxide-ion and pro-ton conductors for fuel cells.

One of the dreams for scientists in solid state ionics is still to discover fast, novel, and even exotic ion conduc-tors in the solid state, since most of the solid state ion conductors suffer from low conductivity in comparison with liquid systems owing to slow diffusion kinetics in the solid state. Japanese scientists have been contrib-uting by their achievement in discovering new materi-als systems as described above and their application as energy and information devices, such as solid oxide fuel cells, NaS battery, Couliode, Memoriode, and so on. This review is aimed to introduce the historical background and recent scientific achievements in the field of solid state ionics in Japan.

2. Crystal structure of highly silver-ion conducting solid electrolyte α-AgI

Silver iodide has three solid phases at ambient pres-sure: body-centered cubic α-AgI, hexagonal β-AgI, and face-centered cubic γ-AgI. The α-phase is stable from 147 °C to its melting point at 555 °C [10], exhibiting an extremely high silver-ion conductivity of about 1.3 to about 2.6 S cm–1 that then drops by about 10% upon melting [11]. The conductivity of β-AgI at room tem-perature is around 10–6 S cm–1. This low conductivity can be explained by Frenkel defects [12] and silver ion vacancies produced by aliovalent impurities. γ-AgI is metastable at ambient pressure and stable at high pres-sure; its conductivity at 500 MPa and room temperature has been reported to be 10–4 S cm–1 [13].

The extraordinarily high silver-ion conductivity of α-AgI in the solid phase was explained by its abnor-mal crystal structure. The crystal structure of the α-AgI phase was first determined in 1934 and then further modified in 1936 by Strock [14]. The structure is famous as a typical example of the ‘average structure’. According to the X-ray diffraction (XRD) analysis by Strock, α-AgI has a cubic unit cell in which two silver atoms are distrib-uted statistically over 42 sites around a body- centered arrangement of iodine atoms. Strock considered that the silver atoms may behave almost liquid-like, in accord-ance with the remarkably high ionic conductivity of


this phase. However, the results were still qualitative. Subsequently, Hoshino [15] measured the XRD intensity of the diffuse background from α-AgI and compared it with that calculated assuming short-range order, and appropriate probability functions for the presence of atoms in different sites. It was confirmed that the inten-sity of the diffused background (IB) measured at 250 °C and 400 °C was in fair agreement with the theoretical intensity in the lower diffraction angle range, as shown Figure 1. The thin dashed curve indicates IB+Io, where IB is the diffuse background and Io is total intensity flux of the incident beam. The difference between the dashed curve and the dotted curve corresponds to the theoret-ical value of ID. The deviation seemed to result from the rough approximation used in the calculation of IB where the correlation among the displacements of atoms was neglected. Hoshino considered that the liquid-like state of silver atoms suggested by Strock may be a valid picture for the structure of α-AgI in view of its high randomness of silver atoms owing to their statistical distribution over many sites, and the large statistical displacements from the mean positions of atoms. Hoshino et al. [16] also measured only the elastic scattering caused by a disor-dered distribution of cations in α-AgI type AgI, Ag3SI and Ag2S using a neutron disuse scattering technique. In 1977, Hoshino et al. [17] reported a powder XRD and neutron diffraction analysis of α-AgI, which showed that two silver ions in the unit cell are distributed over 12(d) sites as a mean with large asymmetric anharmonic thermal vibrations, as shown in Figure 2. This structural model has been supported by the single crystal neutron diffraction study by Cava et al. [18].

3. Caterpillar mechanism for diffusion of ions in highly ion conductive solids

In 1966, Yokota [5] proposed a new diffusion mech-anism to interpret the remarkable deviation from the Nernst–Einstein relation observed for the diffusion

of silver-ions in the high-temperature phases of Ag2S, Ag2Se, and alloy Ag2S1-xSex reported by Yokota [5] and Okazaki [19]. The diffusion coefficient D of silver-ions in a solid electrolyte is expected to be related to the mobility μ by the Nernst–Einstein relation:

The deviation from the Nernst–Einstein relation was estimated by measuring the drift of silver-ions using an electrochemical ion probe method, and the diffu-sion coefficient was measured using a tracer diffusion method with the 110Ag radioisotope. Okazaki observed a large deviation from equation (1). It is generally con-sidered that a correlation factor f should be introduced into the Nernst–Einstein relation:

f is known as the Haven ratio and is dependent on the crystal structure and the conduction mechanism. The meaning of the Haven ratio is best understood in terms of linear response theory as introduced by Kubo in 1957 [20]. For example, the vacancy diffusion is estimated to

(1)�∕D = e/kT

(2)�∕D = e/fkT

Figure 1. observed and calculated intensities of the diffuse background in X-ray signals from α-agi. reprinted with permission from [15].

Figure 2. ag+ ion asymmetric anharmonic thermal vibration model of α-agi. reprinted from [17] with permission from elsevier.


is occupied by ion A1. Ion A1 will be induced to jump to site 2. If site 2 is occupied by ion A2, then A2 will be induced to jump to site 3. If all the sites from 0 to n−1 are occupied by ions, then An–1 will be induced to jump to site n. Such successive jumps contribute in steps to the electrical conduction, which contributes only one step to the self-diffusion of a specified A0 ion. According to this single direction model, the Haven ratio f is calculated from a simple equation using an occupancy fraction P as

in which it is assumed that there is no difference between the probability per unit time that an ion will make a spontaneous jump to a vacant neighboring site and that to an occupied site. In the case of α-AgI, two Ag+ ions are distributed over the 12 (d) sites, but Ag+ cannot occupy the nearest neighboring sites, therefore, P is 1/3 and f is calculated to be 0.5. In the case of α-Ag2S, four Ag+ ions are distributed over the 12 (d) sites, so P is 2/3 and f is 0.2. Thus, the Haven ratio was semi-quanti-tatively explained by this simple theoretical calculation.

4. Highly silver-ion and copper-ion conducting solid electrolytes

In the early twentieth century, the electrical conduc-tivities and ionic transport numbers of many types of ionic compounds were measured, and these results were summarized by Tubandt [11]. Almost all of the compounds exhibited low ionic conductivity below their melting temperature, except for AgI, CuBr and CuI. AgI, CuBr and CuI exhibited high silver and cop-per-ion conductivity at fairly low temperatures below their melting temperatures [11]. The high ionic con-ductivity of these compounds was explained by their abnormal crystal structure, referred to as the average structure [24]. The possibility of finding other solid electrolytes that possessed high ionic conductivity at ambient temperature was of significant interest. However, no solid electrolyte with the average structure at room temperature was reported until 1961. Reuter and Hardel [25] found that Ag3SI had an extremely high silver-ion conductivity of ca. 1 × 10–2 S cm–1 and no electronic conductivity at room temperature; this value is several orders higher than that of β-AgI. The high ionic conductivity was explained by it having the average structure, which is the existence of considerable ionic probability density along the passageways used by the mobile ions.

(3)= (1 − P)/(1 + P)

be 0.78 in the face-centered cubic structure and 0.72 in the body-centered cubic structure [19]. The temperature dependences of the Haven ratio for the highly silver-ion conducting solids α-AgI, α-Ag2S, and α-Ag2Se are shown in Figure 3. The Haven ratios of α-Ag2S and α-Ag2Se are remarkably low. Yokota explained the low Haven ratio of these compounds using the caterpillar mechanism.

The process of diffusion in solids has been interpreted in terms of vacancy or interstitialcy mechanisms, and the deviation from the Nernst–Einstein relation has been attributed to the correlation effect [19–23], i.e. the existence of a correlation between successive jumps of an ion. The correlation effect theory presupposes the solid to be an almost perfect crystal; however, the crystal structures of these highly silver-ion conducting solids are far from perfect. The mobile silver-ions are known to be randomly distributed over the available sites in the crystal lattice [14]. In a highly silver-ion conducting solid such as α-AgI, a low f-value must imply that one jump of a tracer ion is accompanied by jumps of adjacent several ions and that the directions of the later jumps are the same as or at least positively correlated with the direction of the initial jump. Yokota proposed a diffu-sion mechanism that allows such cooperative jumps of several ions. It was supposed that an ion in a site is able to jump not only into a vacant neighboring site but also into an occupied site, which would induce the ion in the latter site to make a jump. The direction of this induced jump will be the same (if crystallographically possible) as or at least positively correlated with the direction of the preceding jump. For simplicity, it was assumed that there are straight lines in the crystal lattices along which sites available to the diffusing ions lie with equal spacing and that the cooperative jumps can take place only along these lines. One of these lines is shown in Figure 4. Suppose that ion A0 on site 0 makes a spon-taneous jump to site 1, which is neighboring site 0 and

Figure 3. Temperature dependence of the haven ratio for α-agi, α-ag2S, and α-ag2Se. replotted from [19].

Figure 4. cooperative jump of ions associated with the spontaneous jump 0→1 of tracer ion ao [5].


the temperature range of −40 to 65 °C. A theoretical capacity of 80% was obtained at current density of up to 40 mA cm–2, above which many systems have been shown to develop a highly silver-ion conducting solid electrolyte. However, no highly silver-ion conducting solid electrolyte with conductivity higher than that of RbAg4I5 has been reported yet.

Takahashi et al. [30] reported a new highly silver-ion conducting solid electrolyte stable in ambient atmos-phere, because RbAg4I5 is thermodynamically unstable below 27 °C. They studied the phase diagram of AgI and Ag2WO4 and found two intermediate compounds, Ag6I4WO4 and Ag5I(WO4)2, as shown in Figure 6. The temperature dependences of the electrical conductivity (σ) of the AgI-AgWO4 system are shown in Figure 7 as a function of Ag2WO4 content. The conductivity curves of the samples containing 0 and 10 mol% Ag2WO4 show an abrupt change at 147 °C, which corresponds to the transition of silver iodide from the β to α-phase. In contrast, that for the 20 mol% Ag2WO4 sample shows no abrupt change at the same temperature. The ionic conductivity of Ag6I4WO4 was reported to be as high as 0.047 S cm–1 at 25 °C, and the compound was stable below room temperature. The discharge curve of the Ag/Ag6I4WO4/I2 cell at a constant load of 7.5 kΩ (ca. 0.1 mA cm–2) at 0 °C is shown in Figure 8 along with that of the Ag/RbAg4I5/I2 cell. The Ag/Ag6I4WO4/I2 cell had an open-circuit voltage of 681 mV and a terminal voltage of 668 mV at the initial stage of discharge, and showed a terminal voltage of 575 mV at 21% anode efficiency. The Ag/RbAg4I5/I2 cell showed a low terminal voltage of

This high silver-ion conductor was applied as an electrolyte in an all-solid electrolyte cell fabricated by Takahashi and Yamamoto in 1966 [26]. They constructed a cell with a silver amalgam anode, a Ag3SI electrolyte, and an acetylene black with I2 cathode. The open- circuit voltage of the cell at room temperature was 0.675 V, which was comparable with the theoretical value. The cell showed a low cell voltage drop of 0.1 V after 3 h at 1 mA cm–2, as shown in Figure 5. Previously reported all-solid-state cells using AgI could only pass a current of microamperes per cm2 because of their high internal cell resistance. The cell with the high silver-ion conducting Ag3SI solid electrolyte, the thick-ness and diameter of which were ca. 0.15 cm and 1.2 cm, respectively, exhibited a low cell resistance of ca. 9 Ω. The internal resistance was constant during discharge, which raised the question as to where the high resistivity products were forming. Takahashi and Yamamoto sug-gested that the AgI product dissolved in the electrolyte and could not form a resistive phase for the AgI-Ag2S system in the solid solution region between the AgI and Ag2S. The dashed line in Figure 5 shows the change in cell voltage during the discharge period with the IR drop for the resistance of the reaction product AgI. The cell was able to operate at −17 °C and a current density of several hundred microamperes per square centimeter.

In 1967, Bradley and Greene [27] and Owens and Argue [28] independently reported the isostructural group of compounds MAg4I5, where M was selected from K, Rb, NH4, and to a limited extent Cs. The conductivity of RbAg4I5, which is 0.26 S cm–1 at 20 °C, is comparable to those of aqueous KOH and H2SO4. Liquid electro-lyte solutions are more conductive at room temperature, whereas solid electrolytes have higher conductivity than the liquid electrolyte at and below −40 °C. Therefore, bat-teries with a solid electrolyte could be especially useful in applications where low-temperature performance is required. Argue and Owens [29] have reported some discharge performance for a Ag/RbAg4I5/RbI3,C cell in

Figure 5. Steady current (1 ma cm–2) discharge curve and the change in internal resistance of the ag-hg/ag3Si/i2-acetylene black cell at 25 °c. reprinted from [26] with permission from elsevier.

Figure 6. Phase diagram of the agi-ag2Wo4 system. reprinted with permission from J. Electrochem. Soc., 120, 647 (1973). copyright 1973, The electrochemical Society [30].


0.875CuBr-0.125C6H12N4CH3Br. Takahashi et al. [33,34] and Matsui and Wagner studied the phase diagrams of copper (I) halide-alkali halide systems and found many intermediate compounds, but no highly copper-ion conducting solid electrolyte has been observed at room temperature except for 0.75CuCl-0.25RbCl, the conduc-tivity of which is 2.25 × 10–3 S cm–1 at 25 °C [35]. Phillips proposed that the high ionic conductivity of α-AgI may be related to the crystal bound ionicity (fi) theory [36], which predicts a 4-fold or a 6-fold coordination for the cations in MnX8-n salts according to whether the ionicity of the crystal bond lies below or above a critical value of 0.785. The ionicity of AgI is 0.770, which is just below the critical value that results in comparable stability of the Ag ions in 4-and 6- coordination and provides large validity for low symmetry scaffold structures. The formation of the highly ion conductive double salt MAg4I5 (M = K or Rb) can be explained theoretically: the addition of a high ionic salt such as KI or RbI to AgI increases the ionicity of AgI slightly, to near the critical value. Further, at high temperature, CuI transforms into a phase that has a high copper-ion conductivity at 408 °C. The ionicity of CuI is 0.692, and the double salt KCu4I5 has a high copper-ion conductivity at 257 °C [37]; the ionicity of CuI increases upon the addition of KI and the highly ion conductive compound appears at a temperature below 408 °C. The mean ionicity of the compounds that exist in the copper halide-alkaline halide and silver halide-alkaline halide systems are summarized in Table 1. The mean ionicity of the double salts is taken as the algebraic means of the ionicity of the copper (I) or silver halides and alka-line halide as a zero approximation. The ionicities of these compounds are taken from the values reported by Phillips [38]. The high and low conductivity labels in this table indicate that the conductivity of the compound is higher or lower than 10–2 S cm–1 at temperatures below its melting point, respectively. The relationship between ionicity and conductivity suggests that the ionicities of all the high conductivity double salts should be less than

220 mV at the initial stage, because the cell resistance at 0 °C was increased by the decomposition of RbAg4I below 27 °C. Takahashi et al. have also reported the dis-covery of other new highly silver-ion conducting solid electrolytes, Ag7I4PO4 and Ag10I5P2O7 [31].

A solid electrolyte, RbAg4I5, with a high conduc-tivity comparable to that of liquid electrolytes was found in 1967. After that, many systems based on cop-per (I) halide were examined to find a room temper-ature highly copper-ion conducting solid electrolyte. The first highly copper-ion conducting solid electro-lyte CuBr-C6H12N4CH3Br was reported by Takahashi et al. in 1973 [32]. The highest copper-ion conduc-tivity was found to be 1.7 × 10–2 S cm–1 at 20 °C for

Figure 7. Temperature dependence of electrical conductivity for the agi-ag2Wo4 system, where m/o stands for mol%. reprinted with permission from J. Electrochem. Soc., 120, 647 (1973). copyright 1973, The electrochemical Society [30].

Figure 8. Time dependence of voltage for ag/ag6i4Wo4/i2 and ag/rbag4i5/i2 cells at constant load discharge of 7.5 kΩ at 0°c. reprinted with permission from J. Electrochem. Soc., 120, 647 (1973). copyright 1973, The electrochemical Society [30].


cubic symmetry with a lattice parameter of 1.002 nm. The X-ray and observed densities suggested the chemical formula to be Rb4Cu16I7Cl13 per unit cell. The number of constituent atoms in the unit cell coincides with that of RbAg4I5, which has four entities in a unit cell with a = 1.124 nm. These results suggested that the struc-tures of RbAg4I5 and Rb4Cu16I7Cl13 are probably closely related. Figure 10 shows the temperature dependence of the electrical conductivity of Rb4Cu16I7Cl13 from −140 to 130 °C. The conductivities in the cooling and heating cycles are in good agreement with each other. This con-ductivity versus temperature plot shows a transition at approximately −25 °C. A similar conductivity knee was observed for RbAg4I5 at −64 °C, which undergoes a high order phase transition [28]. The activation energy for conduction was found to be 7.0 kJ mol–1 in the high-tem-perature range and 19 kJ mol–1 in the low-temperature range. The powder XRD patterns of Rb4Cu16I7Cl13 at

0.809. However, not all of the double salts with ionicity lower than 0.809 exhibit high conductivity: CsCu2Br3 (fi = 0.809) and RbCu3I4 (fi = 0.779) have low conductiv-ity. Thus, a critical ionicity value is a necessary require-ment to obtain a high conductivity double salt of copper and silver halide systems. Furthermore, Table 1 shows that the high conductivity double salts with ionicity near 0.80 exist at around room temperature while those with lower ionicity such as 0.75 or 0.72 exist only at higher temperatures. Figure 9 shows the relationship between the ionicity and the temperature of the phase transition to the high conductivity phase. The phase transition tem-perature decreases linearly with increasing ionicity, and the critical ionicity at room temperature is 0.808. These results may provide some information to assist in the search for highly ion conductive double salts.

Kanno et al. [41] reported that Rb3Cu7Cl10 has a rela-tively high copper-ion conductivity of 3.32 × 10–3 S cm–1 at room temperature and an iconicity of 0.809, which is similar to that of RbAg4I5; however, its conductivity is two orders of magnitude lower than that of RbAg4I5. No new high-conductivity compounds have been found in the other copper (I) halide and alkaline halide binary systems. Meanwhile, Takahashi et al. searched ternary systems of copper (I) halide and alkaline halide according to the above ionicity considerations. In 1979, Takahashi et al. [6] reported a highly copper-ion conducting solid electrolyte at room temperature in the CuCl-CuI-RbCl system. The highest electrical conductivity in this system was found for 0.45CuCl-0.35CuI-0.20RbCl, 3.4 × 10–1 S cm–1 at 25 °C. XRD results indicated that a sample of Rb4Cu16I7Cl13 in composition was a single phase and all the diffraction lines were indexed to a

Table 1. Mean ionicity (fi) and conductivity of compounds in the silver halide-alkali halide and copper (i) halide-alkali halide systems [40].

Compound Stability

range ( °C) Conductivity fi Referencesrb2agBr3 <310 low 0.921 28csagBr2 <265 low 0.904 28cs2agBr3 <275 low 0.921 28Kag4i5 38–253 high 0.806 40K2agi3 <130 low 0.890 40rbag4i5 27–228 high 0.807 28, 29rb2agi3 <298 low 0.892 28csag2i3 <210 low 0.831 28cs2agi3 <253 low 0.892 28K2cucl3 <148 low 0.884 41rb3cu7cl10 <165 high 0.809 42rb2cu3cl5 <187 low 0.830 42rb2cucl3 <205 low 0.902 42cscu2cl3 <277 low 0.816 42cs3cu2cl5 <310 low 0.871 42K2cuBr3 <228 low 0.880 43rb2cuBr3 <251 low 0.883 42cscu9Br10 290–306 high 0.757 42cscu2Br3 <355 low 0.809 42Kcu4i5 257–332 high 0.745 38, 41rbcu2i3 <285 low 0.779 28rb2cui3 <298 low 0.866 31cscu9i10 333–348 high 0.718 42cscu2i3 <348 low 0.779 42cs3cu2i5 <352 low 0.849 39

Figure 9. relationship between ionicity (fi) and temperature of the phase transition (Tt) to the high ionic conductivity phase. replotted from [40].

Figure 10. Temperature dependence of the conductivity (σ) of rb4cu16i7cl13. ○: cooling; Δ: heating. reprinted with permission from J. Electrochem. Soc., 126, 1654 (1979). copyright 1979, The electrochemical Society [6].


Figure 11(b) shows the schematic energy diagram of the galvanic cell Pt/sample/Cu or Ag, where H is the chemical potential, Ξ is the electrochemical potential, φ is the electrostatic potential, and suffixes i and h refer to Cu+ (or Ag+) ion and hole, respectively. Ishikawa and Miyatani measured the electronic and ionic conductiv-ity, Hall coefficient, and thermoelectric power of the electron and ion mixed conductors as a function of the electromotive force (E) for Ag/AgI/silver chalcogenide/Pt and Cu/copper ion conductor/copper chalcogenide/Pt cells, where E may be considered as the relative poten-tial of the Fermi level in the chalcogenides. Figure 12 shows σe, Δ(en)/Δε, Δe/Δ(en), Rσe, and θ versus E curves for α-Cu2-xS at 100 °C, where σe is the electronic con-ductivity, n is the number of electrons, ε is the dielectric constant, and θ is the thermoelectric power. Ishikawa and Miyatani [53] also proposed a model where E does not represent the relative value of the Fermi energy and instead they assumed that E represents the height of the Fermi level, although the measurement of the sur-face potential fails to give convincing evidence for this assumption. Therefore, we consider the position of the bottom of the conduction band to be dependent on the

room temperature and −100 °C were compared and found to be in good agreement; except for a change in the relative intensity of each peak, no extra peaks or peak splitting were observed. This result suggests that the transition at −25 °C is a high order phase transition, i.e., Rb4Cu16I7Cl13 has a high disorder structure above −25 °C and a low disorder structure below −25 °C. Atake et al. [43] measured the heat capacity of Rb4Cu16I7Cl13 between 10 and 300 K using a high precision adiabatic calorimeter. An abnormal increase was observed in the heat capacity curve above 90 K, and above 130 K the heat capacity exceeded the classical limit value of 120 R = 998 J K–1 mol–1. The excess heat capacity showed a broad anomaly with a maximum at about 150 K, which indicates a non-cooperative mechanism for the redistri-bution of Cu ions among the crystal sites. The abnormal excess heat capacity corresponds to the remarkable vari-ation in the occupancy of the 8-fold site, as shown by the neutron diffraction results reported by Kanno et al. [44]. The physical properties of Rb4Cu16I7Cl13 are compared with those of RbAg4I5 [45–48] in Table 2. The copper ion conductivity of 3.4 × 10–1 S cm–1 at 25 °C is as high as that of an aqueous electrolyte solution, and is still the highest of all room temperature ionic conducting solid electrolytes.

5. Ion and electron mixed conductors

The ionic conductivity of the α-Ag2S group (the high-temperature phase of Ag2S, Ag2Se, and Ag2Te), which exhibits mixed conduction of electrons and sil-ver-ions, has been extensively studied by Miyatani and Yokota using an ionic probe [49–51]. The basic con-cept was proposed by J.B. Wagner and C. Wagner [52]. Figure 11(a) shows a typical setup used to measure the electronic and ionic conductivity separately, where P is platinum, S is the sample, I is the ionic conductor and C is copper (for copper conductors, or silver for silver conductors). By sending a current across C and P, the Cu content in the sample can be varied and the change determined according to Faraday’s law. The electronic conductivity of the sample can be determined by meas-uring the potential drop between two metal probes, P1 and P2, by sending a current through the metallic elec-trodes, while the ionic conductivity can be determined by measuring the potential drop between two ionic probes of I1 and I2.

Table 2. Physical properties of rb4cu16i7cl13 and rbag4i5.

Rb4Cu16I7Cl13 RbAg4I5 Referencescrystal structure cubic a = 1.002 nm cubic a = 1.124 nm 6, 46X-ray density (g cm–3) 4.47 5.38 6, 46electrical conductivity at 25 °c (S cm–1) 0.34 0.28 6, 29activation energy for conduction (kJ mol–1) 7.0 7.1 6, 47electronic conductivity (S cm–1) 10–12 at 60 ℃ 10–11 at 25 ℃ 6, 48copper ion or silver ion transport number 1.0 1.00 6, 49decomposition potential (v) 0.69 0.67 6, 49Melting point (℃) 234 (incongruent) 228 (incongruent) 6, 28

Figure 11. (a) Schematic of the arrangement used for mixed conductivity measurements; i: ionic conductor, S: sample, P: platinum, c: copper or silver; and (b) schematic energy diagram of the Pt/sample/cu or ag galvanic cell. reproduced with permission from [53].


Mixed conductors with high ionic conductiv-ity were found among the high-temperature phases of silver and copper chalcogenides. Takahashi and Yamamoto reported Ag2Se–Ag3PO4 solid solution to be a mixed conductor with high silver-ion conduc-tivity at room temperature [60]. Solid solutions in the Ag2Se-Ag3PO4 system containing 5–10 mol% Ag3PO4 have the high-temperature cubic α-Ag2S structure and high silver-ion conductivity at room temperature. The silver-ion conductivity was measured using the electron blocking cell shown in Figure 14. The ionic conductivity of the solid solution was high so a cylindrical sample 2–3 mm in diameter and 12–13 mm long was used, and Ag/RbAg4I5 probes were used for potential difference measurements. The effects of the electrode polarization were negligible using this arrangement.

The silver-ion conductivity measured at 30 °C is shown as a function of Ag3PO4 content in Figure 14. The ionic conductivity increased with the content of Ag3PO4 in the Ag2Se up to 10 mol% and then decreased. Measurement of the lattice constants of the solid solu-tion suggested that the upper limit of Ag3PO4 content in Ag2Se-Ag3PO3 was approximately 10 mol%. Samples containing greater than 10 mol% Ag3PO4 were a mixture of the solid solution and Ag3PO4. The silver-ion conduc-tivity of 0.9Ag2Se-0.1Ag3PO4 was as high as 0.1 S cm–1 at 30 °C, which is comparable to that of RbAg4I5. The activation energy for silver-ion conduction in this solid solution was estimated to be 4.0 kJ mol–1 from

increasing excess Ag content in α-Ag2S [50] as well as the excess Cu content in Cu2-xSe, Cu2-xS, and C2-x(S, Se) [53]. The extent of the Ag or Cu excess can be interpreted as arising from the screening effect of carriers (holes) on copper or silver ion vacancies.

A theoretical description of mixed electron and ion conductors was made by Wagner [54]. However, his the-ory is limited to the equilibrium and steady states. The theory of the transition phenomena characteristics of mixed conductors was presented by Yokota and Miyatani [55–57]. The one-dimensional transport of charge car-riers in mixed conductors can be described using the following transport equations [58]:

where je and ji are the electronic and ionic current, respectively, and σei and σie are the respective cross- conductivities. According to the Onsager reciprocal relation [59],

Yokota and Miyatani [56] measured σei and σie inde-pendently using the ionic and electronic electrode showed in Figure 11. The experimental results for Cu2-

xS at 340 °C are shown in Figure 13, where the abscissa is the electromotive force (emf) E for the Cu/Cu2-x S/CuBr/Cu cell.

(4)je =(

�e∕ze)(

�e∕dx)

−(

�ei∕ze)(

�i∕dx)

(5)je =(

�i∕ze)(

�i∕dx)

−(

�ie∕ze)(

�e∕dx)

(6)�ei = �ie

Figure 12. σe, Δ(en)/Δε, Δe/Δ(en), rσe, and θ versus E curves for α-cu2-xS at 100 °c. reproduced with permission from [53]. Figure 13. observed values of cross-conductivity σei and σie of

cu2-xS plotted against e for the cu2-xS/cuBr/cu cell. reprinted from [56] with permission from elsevier.


non-stoichiometry and thermo-chemical stability of these oxides as a function of temperature and oxygen partial pressure using thermos-gravimetry and cou-lometric titration. These perovskite-type oxides have been investigated for applications such as solid oxide fuel cells (SOFCs), gas separators, and oxygen sensors [65–67]. Ishigaki et al. [63] reported that the oxygen non-stoichiometry of La1-xSrxCrO3-δ can be described not by an ideal solution model, but by a regular solu-tion model that takes the effect of defect interaction into account. Yasuda and Hikita [68] and Boroomand et al. [69] reported that defect formation in La1-xCaxCrO3-δ can be explained with the ideal solution model. Onuma et al. [70] precisely determined δ for La1-xCaxCrO3-δ as a function of composition, temperature, and P(O2) using a thermogravimetric technique to elucidate a

the temperature dependence of the silver ion conduc-tivity. A non-stoichiometry of Ag in this solid solution was observed in the range of 0 to 0.002 in Ag2.075-

xSe0.925(PO4)0.075 and the activity of silver was changed with the non-stoichiometry. The electrode potential of (Ag2Se)0.925(Ag3PO4)0.075 was changed from 0 to 150 mV by removing Ag from the solid solution. Electrochemical potential memory devices were developed by Ikeda and Tada [61] using this mixed conductor and the stable sil-ver-ion conductor Ag6I4WO4.

Doped perovskite-type oxides of composition La1-xAExMO3-δ (AE = Ca, Sr, M = Cr, Mn, Fe, Co) have large oxygen deficiency (oxygen non-stoichiometry), high oxide-ion diffusion and high electronic conduc-tivity [62–64]. Mizusaki and his co-workers at Tohoku University [63,64] extensively studied the oxygen

Figure 14. ionic conductivity measurement setup and ionic conductivity at 30 °c as a function of ag3Po4 content for ag2Se-ag3Po4. reprinted with permission from J. Electrochem. Soc., 119, 1735 (1972). copyright 1972, The electrochemical Society [60].

Figure 15. Schematic of the thermogravimetric measurement system. reprinted from [70] with permission from elsevier.


where σh and σi are the hole conductivity and ion con-ductivity, respectively, and σi can be expressed as

where NA is the Avogadro number, Vm is the molar vol-ume, and μV is the mobility of an oxygen vacancy. σi is expected to be proportional to x and dependent on P(O2). The best fitting curves are shown in Figure 17.

Fueki et al. measured the oxygen vacancy diffusion coefficient of some perovskite-type oxides, using the chemical relaxation method for La1-xSrxCoO3-δ [74] and the isotopic exchange reaction for La1-xSrxCoO3-δ [63,75,76] and La1-xSrxFeO3-δ [76]. Figure 18 shows the temperature dependence of the oxygen vacancy diffusion coefficient (DV) of these oxides measured by Mizusaki et al. [71]. The oxygen vacancy diffusion coefficient of the perovskite-type oxides is close, both in absolute val-ues and in activation energy. Thus, it is suggested that the diffusivity of oxygen vacancies is determined essentially by crystal structure.

(11)�i = x(

NA/Vm

)

e�V

suitable defect chemical model for this solid solution. Figure 15 shows a schematic of their thermogravimet-ric measurement system. In the system, a sample rod was suspended from the electrical microbalance with alumina sticks, quartz sticks, and Pt-Rh wire. The tem-perature around the sample was controlled within 1 K. The weight change caused by oxygen non-stoichiom-etry of the La1-xCaxCrO3-δ was measured under con-trolled oxygen partial pressure using O2-Ar, CO-CO2, and H2-H2O-Ar mixtures. Three yttria-stabilized zir-conia (YSZ) oxygen sensors were installed to monitor P(O2). Figure 16 shows the oxygen non-stoichiometry of La1-xCaxCrO3-δ and La1-xSrxCrO3-δ as a function of log P(O2) at 1373 K [70]. There is almost no difference between La1-xCaxCrO3-δ and La1-xSrxCrO3-δ, which means that δ is not dependent on the A-site dopant species, but on the dopant concentration. The exchange of oxygen between La1-xCaxCrO3-δ and gas phase can be presented using the Kröger–Vink notation:

The equilibrium constant for reaction (7), K, is

where γ1, γ2, γ3 and γ4 are the activity coefficients of CrCr

x, CrCr•, OO

x, and VO••, respectively. The solid curves

in Figure 16 represent the fitting results, which agree well with the experimental data. The K values of a non-ideal solution tend to be smaller than those reported in the lit-erature because Yasuda and Hikita [68] and Boroomand et al. [69] assumed the defect formation occurred as in an ideal solution.

Mizusaki et al. also determined the ionic and elec-tronic conductivity of oxide-ion and electron mixed conductors of oxygen partial pressure using high-tem-perature gravimetry and DC conductivity measure-ments as a function [71]. Figure 17 shows a typical example of the oxygen partial pressure dependence of the conductivity of a single crystal of composi-tion La1-xCaxAlO3-δ, which was reported as a typical perovskite-type oxide-ion conductor by Takahashi and Iwahara [72,73]. The conductivity is essentially constant, irrespective of P(O2) at lower P(O2). With increasing P(O2), the conductivity gradually increases asymptotically approaching the P(O2)

1/4 relationship, which suggests that p-type conduction becomes pre-dominant with increasing P(O2). The equilibrium between the gas phase and La0.995Ca0.005AlO3-δ can be expressed as

The total conductivity σ can be expressed as

(7)1∕2O2(g) + VO∙∙ + 2CrxCr = OxO + 2CrCr

∙

(8)K = P(

O2

)1/2[

CrCr∙]2[

OxO

]

�22�3/

[

CrxCr]2[

V∙∙O

]

�21�4

(9)(1/2)O2

(

g)

+ V∙∙o = Ox

o + 2h

(10)� = �hP(

O2

)1/4+�i

Figure 16. oxygen non-stoichiometry of la1-xcaxcro3-δ and la1-xSrxcro3-δ. at 1377 K as a function of log P(o2). The fitting results for la1-xcaxcro3-δ are shown as solid lines. reprinted from [70] with permission from elsevier.

Figure 17. P(o2) dependence of conductivity at 868 °c for single crystals of la1-xcaxalo3-δ with different values of x. reprinted with permission from J. Electrochem. Soc., 140, 467 (1993). copyright 1993, The electrochemical Society [71].


They are written in the Kröger–Vink notation, where Vo••

is oxygen vacancy, Oox is oxygen in an oxygen site, and

h• is a hole. The concentration of holes increases with oxygen partial pressure, while that of protons increases with water and hydrogen partial pressure. The proton transport number of SrCe0.95Y0.05O3-δ was reported to be 0.99 at 700 °C with an H2O partial pressure of 0.002 MPa. The proton transport number decreased slightly with increasing temperature; that at 1000 °C was 0.84. High proton conductivity was observed in a series of doped alkali earth cerates ACe1-xMxO3-δ (A = Sr, Ba, Ca; M = Y, Nd, Yb) [77–82]. Some doped zir-conias based on CaZrO3, SrZrO3, and BaZrO3 [83,84] have also been confirmed to exhibit proton conduction. Figure 20 shows the temperature dependence of typ-ical proton-conducing perovskite-type oxide ceramics under a hydrogen atmosphere. BaCeO3-based ceramics showed the highest conductivity among these oxides. However, the contribution of oxide ions to the conduc-tion increases significantly as the temperature is raised.

Figure 21 shows the hydrogen evolution rate of a H2,Pt/BaCe1-xNdxO3-δ/Pt,Ar cell as a function of current density at 800 °C. The evolution rate coincided with the theoretical rate calculated from Faraday’s law. This is evi-dence of proton conduction in these ceramics, because the proton formed at the anode (H2(g) → 2H+ + 2e–) must migrate across the oxide ceramic to discharge at the cathode (2H+ + 2e– → H2(g)). Although the conductiv-ity of SrCeO3-based ceramics is rather low, their proton transport number is higher than that of BaCeO3-based ceramics. The zirconia-based ceramics exhibit lower con-ductivity than the cerates, but are superior with respect to their chemical stability and mechanical strength.

Various applications can be devised using proton con-ducting ceramics [85,86]. Proton conducting ceramics can be used as hydrogen sensors for high-temperature

(13)H2O + 2h∙ = 2H+ + 1/2O2

(14)H2O + V∙∙O = 2H+ + Ox

O

(15)H2 + 2h∙= 2H+

6. High-temperature proton-conducting ceramics

Research on the high-temperature proton-conducting ceramics began in Japan. In 1981, Iwahara of Tottori University, who was a student of Professor Takahashi at Nagoya University, and his co-workers reported that strontium cerate based ceramics showed a relatively high proton conductivity at elevated temperatures [7]. A typical example of a proton conducting oxide of this class is SrCe0.95Y0.05O3-δ. This material is a substituted solid solution based on a perovskite-type oxide, in which 5 mol% of Ce are replaced with Y, and it exhibits pro-tonic conduction in a hydrogen containing atmosphere at elevated temperature. The proton conductivity of this solid solution is approximately 10–2 S cm–1 at 900 °C in hydrogen atmosphere. Proton conduction in this oxide was verified by electrochemical hydrogen transport experiments under hydrogen or water vapor-containing atmosphere at elevated temperatures. A schematic of a steam concentration cell using a solid proton conductor is shown in Figure 19.

The proton conduction of this oxide is explained by the following mechanism. At higher oxygen partial pressure, this oxide exhibits a p-type (hole) conduction. When water vapor or hydrogen is introduced to the atmosphere, the concentration of holes decreases and that of protons increases according to the following equi-librium reactions:

(12)V∙∙

o + 1/2O2 = Oxo + 2h∙

Figure 18. log dv versus temperature curves for the perovskite-type oxides. reprinted with permission from J. Electrochem. Soc., 140, 467 (1993). copyright 1993, The electrochemical Society [71].

Figure 19. Schematic of steam concentration cell using a solid proton conductor as the electrolyte. reprinted from [7] with permission from elsevier.


hydrogen fuel cell using SrCe0.95Yb0.05O3-δ that exhibited stable operation at 800–1000 °C [80]. When the cell was discharged, water vapor was generated at the cathode at the same rate as the theoretical rate calculated from Faraday’s law, which indicates that the conduction in the electrolyte was protonic. When a hydrogen fuel cell is operated inversely, water vapor at the anode is decom-posed to form protons that migrate to the cathode, where they discharge to produce hydrogen. This is a type of steam electrolyzer for hydrogen production. A bench-scale steam electrolyzer was fabricated using a ceramic tube of SrCe0.95Yb0.05O3-δ electrolyte closed at one end. The electrolyzer was operated at 750 °C, and produced pure and very dry hydrogen (dew point < −30 °C) that could be extracted at a rate of 3 L h–1 [85].

7. Highly oxide-ion and hydride-ion conducting solid conductors

Since Nernst reported the oxide-ion conduction of doped zirconia in 1897 [88], the zirconia family of oxide-ion conductors has been extensively studied by many research groups. The candidate electrolytes can be divided into two major structures; fluorite and per-ovskite. Both ceria and high temperature-stabilized zir-conia take a fluorite structure, and lanthanum gallates have the perovskite structure. The fluorite structure is a face-centered cubic arrangement of cations with anions occupying all the tetrahedral sites, which leads to a large number of octahedral voids. This arrangement is rather open and, thus, rapid ion diffusion may be expected. At high temperature, zirconia has the fluorite structure, and the high-temperature phase can be stabilized at lower temperatures by the addition of divalent or trivalent cat-ions such as Ca2+ or Y3+ [88]. The dissolution of yttria into the fluorite phase of ZrO2 can be expressed by the following defect equation in the Kröger–Vink notation:

Each additional yttria molecule creates one oxygen vacancy. The conductivity of doped zirconia varies as a function of dopant concentration and has a maximum at or near the minimum quantity of dopant required to fully stabilize the cubic fluorite phase [89]. Arachi et al. [90] analyzed the effect of the dopant on the conduc-tivity of ZrO2–Ln2O3 (Ln = Sc, Yb, Er, Y, Dy, or Eu). The dependence of the conductivity on the dopant con-centration at 1000 °C is shown in Figure 22. Doping with Sc3+, which has the closest ionic radius to the host ion Zr4+, results in the highest conductivity of approxi-mately 0.3 S cm–1 at 1000 °C. However, this system has been reported to exhibit an aging effect upon annealing at high temperature [91]. The change in the electrical conductivity of the ZrO2–Sc2O3 system (ScSZ) after an annealing period at 1000 °C was examined by Yamamoto et al. [92]. The change in conductivity with the annealing

(16)Y2O3

(

ZrO2

)

= 2Y�

Zr + 3OxO + V∙∙

O

industrial processes. Galvanic-cell-type hydrogen sen-sors, steam sensors, and hydrocarbon sensors that are usable at high temperature have been fabricated [87]. These sensors are essentially based on the principle of the hydrogen concentration cell using a proton conducting solid electrolyte.

Hydrogen sensors based on CaZr0.9In0.1O3-δ ceramic have been commercialized by TYK, Japan [87] to meas-ure the hydrogen partial activity in fused aluminum during the casting process. These sensors could also be applied to other fused metals such as zinc and cop-per. Iwahara has proposed other applications, such as a

Figure 20. conductivity of typical proton conducting perovskite-type oxide ceramics under a hydrogen gas atmosphere. reprinted from [85] with permission from elsevier.

Figure 21. Plot of hydrogen evolution rate versus current density for h2,Pt/Bace1-xndxo3-δ/Pt, ar; ○: x = 0.10, ●: x = 0.05. dashed line indicates the theoretical line. replotted from [80].


number increases with temperature and was less than 0.95 for Ce0.7Ln0.3O1.85 (Ln = Sm or Dy), whereas that of the compounds containing Nd, Gd and Er was unity at high temperatures.

In addition to the fluorite structure oxide-ion con-ductors, some perovskite-type oxides exhibit high ion conductivity. In 1971, Takahashi and Iwahara reported the electrical conductivities of some per-ovskite-type oxides [73]. Figure 25 shows the temper-ature dependence of many perovskite-type oxides. The highest conductivity was found for Al- or Mg-doped CaTiO3. However, the CaTiO3-based oxides had low ionic transport numbers at high temperature and in reduced atmosphere.

period was found to be dependent on the dopant con-tent. ScSZ with 8 mol% Sc2O3 exhibited a significant aging effect upon annealing at 1000 °C. The conduc-tivity of 0.3 S cm–1 for the as-sintered ScSZ at 1000 °C decreased to 0.12 S cm–1 after aging for 1000 h. In con-trast, ScSZ with 11 mol% Sc2O3 (11ScSZ) showed no aging effect, even after annealing at 1000 °C for 6000 h. However, 11ScSZ shows a phase transition at 600 °C with a small volume change. Mizutani et al. reported that the cubic phase of 11ScSZ is stabilized at room temperature by the addition of small amounts of Al2O3 [93]. The elec-trical conductivity of 11ScSz-1 wt%Al2O3 was found to be 0.2 S cm–1 at 1000 °C, which is slightly lower than that of 11ScSZ, but this composition shows no phase transition. This type of scandia-doped zirconia oxide is now widely used as an electrolyte for SOFCs.

The other reported fluorite-type oxide-ion conductors are based on CeO2 [88]. However, systematic research on this system was lacking before the study by Kudo and Obayashi [94] in 1975. They systematically studied the oxide-ion conductivity and the transport number of fluorite-type Ce1-xLnxO2-x/2 (Ln = lanthanide element) as a function of the dopant content and oxygen par-tial pressure. The maximum conductivity was found at around x = 0.3 with a lattice constant of 0.53 to 0.54 nm. Figure 23 shows temperature dependence of the resis-tivity in the Ce0.7Ln0.3O1.85 system. The conductivity of Ce0.7Gd0.3O1.85 at 750 °C is 7 × 10–2 S cm–1, which is several times higher than that of zirconia-based oxide-ion conductors. However, at 1000 °C, its conductivity is comparable to that of zirconia-based oxide-ion conduc-tors. The ceria-based oxide-ion conductors exhibit high conductivity at lower temperatures and have applied as the electrolyte for intermediate temperature SOFCs. Ceria-based oxide-ion conductors were found to show electron hole conduction under reduced atmosphere [88]. Kudo and Obayashi measured the ionic transport number of the ceria-based oxide-ion conductors using an oxygen concentration cell. Figure 24 shows the oxide-ion transport numbers for Ce0.7Ln0.3O1.85. The transport

Figure 22. compositional dependence of the electrical conductivity of the Zro2-xln2o3 system at 1000 °c. reprinted from [90] with permission from elsevier.

Figure 23. arrhenius plot of resistivity for ce0.7ln0.3o1.85. lines 1–5 are for ln = gd, dy, ho, er, and yb, respectively. reprinted with permission from J. Electrochem. Soc., 122, 142 (1975). copyright 1975, The electrochemical Society [94].

Figure 24. oxide-ion transport number for ce1.7ln0.3o1.85. curves 1−5 are for ln = nd, Sm, gd, dy and er, respectively. reprinted with permission from J. Electrochem. Soc., 122, 142 (1975). copyright 1975, The electrochemical Society [94].


conductivity increased with the Mg content and a max-imum was observed for La0.9Sr0.1Ga1-xMgxO3 at x = 0.2. The concentration cell had an almost theoretical emf at PO2 = 10–5 atm. The electrical conductivity did not change within an oxygen partial pressure range of 1 to 10–21 atm. at 1123 K, which suggests that the Mg-doped La0.9Sr0.1Ga1-xMgxO3 perovskite-type oxide is almost a pure oxide-ion conductor over a wide range of oxygen partial pressures. The advantage of the LaGaO3-based oxide ion conductors is a high conductivity in the lower temperature range. Ishihara et al. have extensively stud-ied intermediate temperature SOFCs using this type of oxide-ion conductor. SOFCs are typically operated at around 1000 °C because of the conductivity limitation of the conventional Y2O3 stabilized ZrO2 (YSZ) oxide-ion conductor. SOFCs containing LaGaO3-based oxides exhibit a high power density of 0.5 W cm–2 at 700 °C, which is comparable to that of SOFCs with YSZ electro-lyte at 1000 °C [97].

In 1995, a new class of highly oxide-ion conducting solid electrolytes was reported by Nakayama et al. [98]. They investigated the electrical conductivity of lan-thanide silicate oxyapatites of Ln10(SiO4)6O3 (Ln = La, Nd, Sm, Gd, and Dy) in composition and found the highest conductivity of 2.3 × 10–4 S cm–1 at 500 °C for Nd10(SiO4)6O3. The temperature dependence of the elec-trical conductivity of Nd10(SiO4)6O3 and La10(SiO4)6O3 is shown in Figure 29. The oxide-ion transport number of Nd10(SiO4)6O3 was estimated to be around unity using an oxygen gas concentration cell, O2–Ar/ Nd10(SiO4)6O3/air. Many studies related to their crystal structure and conductivity have been published since the discovery of the lanthanum silicate oxyapatites by Nakayama et al. Yoshioka and Tanase [99] reported a high conductivity of 4.5 × 10–3 S cm–1 at 500 °C for La9.6Si5.7Mg0.3O26,1,

The electrical conductivities reported by Takahashi and Iwahara for the perovskite-type oxides were lower than those of the fluorite-type oxides. After the pioneer-ing work by Takahashi and Iwahara, some perovskite-type oxides were found to have high oxide-ion conductivity. Cook et al. [95] reported a high electrical conductivity for BaTh0.9Gd0.1O3, 8.7 × 10–2 at 550 °C. In 1994, Ishihara et al. [8] and Feng and Goodenough [96] reported high oxide-ion conductivities for doped perovskite-type oxides of LaGaO3. In particular, Ishihara et al. reported a high conductivity for La0.9Sr0.1Ga0.9Mg0.1O3. Figure 26 shows the effect of the addition of alkaline earth cations to the La site in LaGaO3 on its electrical conductivity. The electrical conductivity of LaGaO3 was dependent on the added alkaline earth cation and increased in the order Ca < Ba < Sr. The electrical conductivity increased with the amount of Sr additive and attained a maximum at x = 0.1. Impurity phases of SrGaO3 and LaSrO3 were detected above x = 0.1.

The effect of additives at the Ga site of La0.9Sr0.1GaO3 on the electrical conductivity was also studied. The results are shown in Figure 27. The highest electrical conductivity was found for La0.9Sr0.1Ga0.9Mg0.1O3, as high as 0.1 S cm–1 at 800 °C. The ionic transport num-ber of La0.9Sr0.1Ga1-xMgxO3 was examined using a H2-O2 concentration cell. Figure 28 shows the effect of the amount of Mg substitution on the electrical conductivity of La0.9Sr0.1Ga1-xMgxO3 at 1223 K and E for a H2-O2 con-centration cell with La0.9Sr0.1Ga1-xMgxO3. The electrical

Figure 25. arrhenius plots of the oxide-ion conductivity of the perovskite-type oxides measured in air; 1: laalo3, 2: caTio3, 3: SrTio3, 4: la0.7ca0.3alo3, 5: la0.9Ba0.1alo3, 6: SrTi0.9al0.1o3, 7: caTi0.95Mg0.05o3, 8: caTi0.5al0.5o3, 9: caTi0.9al0.1o3. reprinted from [73] with permission from elsevier.

Figure 26. effect of alkaline earth cation doping at the la sites in lagao3 on the electrical conductivity of la1-xMxgao3 for M = ca, Sr, Ba (Po2 = 10–5 atm). reprinted from [8] with permission. copyright 1994 american chemical Society.


La8Sr2Si6O26 has no oxide-ion vacancies and its electrical conductivity is low [100]. To obtain a high oxide-ion conductivity, oxyapatites with high oxide-ion vacancy should be prepared

Recently, Irvine and co-workers reported a high H– ion conduction in BaH2, the electrical conductiv-ity of which was 0.2 S cm–1 at 630 °C [103]. Although some conductivity studies have been reported for related materials, the nature of the charge carriers has not yet been determined. More recently, Kanno and co-workers found that a series of K2NiF4-type oxyhydrides, La2-x-ySrx+yLiH1-x+yO3-y, show hydride-ion conductivity [104]. Hydride-ion solid conductors are attractive as an electrolyte for high energy density batteries, because of their strong reducing properties and standard potential of H2/H

– (−2.3 V), which is close to that of Mg2+/Mg (−2.4 V). Utilization of alkaline earth hydrides as a battery electrolyte is difficult because of their struc-tural inflexibility. Figure 30 shows the temperature dependence of the electrical conductivity of La1-xSr1+x LiH2-xO2. An electrical conductivity of 2.1 × 10–4 S cm–1 was observed at 317 °C for La0.6Sr1.4LiH1.6O2. To iden-tify the nature of the charge carriers, the electron (and hole) conductivity was measured by the Hebb-Wagner polarization method [105] using an asymmetric (-)Pd/La0.6Sr1.4LiH1.6O2/Mo(+) cell at 207 and 317 °C. The total conductivity (electron + hole) at 207 and 317 °C was 2.9 × 10–8 and 4.1 × 10–7 S cm–1, respectively.

It is evident that La0.6Sr1.4LiH1.6O2 is a pure ionic con-ductor. An all-solid-state Ti/o-La2LiHO3/TiH2 cell was constructed to confirm the ion carrier in orthorhombic La2LiHO3. Figure 30(B) shows the discharge curve at a constant current of 0.5 μA and 300 °C. The cell showed an initial open circuit voltage of 0.28 V, which is con-sistent with the theoretical value calculated from the standard Gibbs energy of formation of TiH2. The cell reaction products were analyzed by synchrotron XRD. Phase changes detected for the cathode and anode

five times higher than that for Y2O3 stabilized ZrO2 [88] and comparable to that for the perovskite oxide La0.9Sr0.1Ga0.9Mg0.1O3 [8]. The crystal structure of the oxyapatites has been extensively studied; the diffusion path was proposed for La9.33Si6O26 and La8Sr2Si6O26 by Sansom et al. [100] and for La9.69Si5.7Mg0.3O26,24 by Ali et al. [101] using neutron diffraction analysis. These results suggested that La9.33Si6O26 and La9.69Si5.7Mg0.3O26,24 have oxide-ion lattice vacancies and oxide ions migrate via a vacancy mechanism. As shown by the electrical conductivity data for lanthanum silicate oxyapatites by Kobayashi and Sakka [102], the conductivity was dependent on the preparation method because of high grain boundary resistances and impurity phases.

Figure 27. effect of doping of various cations into the ga sites in lagao3 on the electrical conductivity of la0.9Sr0.1ga0.9M0.1o3 for M = al, in, Mg, (Po2 = 10–5 atm.). reprinted from [8] with permission. copyright 1994 american chemical Society.

Figure 28. effect of amount of Mg substitution on the electrical conductivity of la0.9Sr0.1ga1-xMgxo3 at 1223 K (Po2 = 10–5 atm.) and emf of an h2-o2 concentration cell based on la0.9Sr0.1 ga1-xMgxo3 at 1273 K. reprinted from [8] with permission. copyright 1994 american chemical Society.

Figure 29. Temperature dependence of electrical conductivity for (a) y2o3 stabilized Zro2, (b) la10(Sio4)6o3 and (c) nd10(Sio4)6o3. reproduced with permission from [98].


The crystallization of glassy materials is gener-ally known to lower conductivity [113]. However, the enhancement of conductivity by careful heat-treatment was reported for Li2S-P2S5 glasses by Tatsumisago and co-workers in 2001 [114]. Figure 32 shows the tem-perature dependence of the electrical conductivity of 70Li2S-30P2S5 samples prepared by mechanical mill-ing and solid-state reaction. The crystallized sample was obtained by solid-state reaction of Li2S-P2S5 and glass-ceramic by crystallization of the glass at 360 °C. The room temperature conductivity of the glass was 5.4 × 10–5 S cm–1, while that of the glass-ceramic was

materials were consistent with those expected from the Ti–H phase diagram. From these results, Kanno et al. concluded that La1-xSr1+xLiH2-xO2 is a pure hydride-ion conductor. Yamaguchi predicted that this result by Kanno and co-workers is just the beginning of a new field of material science of H– conductivity in oxyhy-dride systems that will require further elaboration of the underlying mechanism, as well as potential applica-tion of the extremely good reducing ability of H– ions in chemical synthesis [106].

8. Highly lithium-ion conducting solid electrolytes

Many new types of highly lithium-ion conducting solid electrolytes have been reported by Japanese researchers. In 1989, Aono et al. [107] reported a highly lithium-ion conducting solid electrolyte of composition Li1+xMx Ti2-x(PO4)3 (M = Al, Sc, Y, and La). This system has the NASICON-type structure. Figure 31 shows the con-ductivity of Li1+xMxTi2-x(PO4)3 at 25 °C as a function of x, in which the highest conductivity was observed at x = 0.3 for all systems examined. The conductivity of Li1.3Al0.3Ti1.7(PO4)3 at 25 °C almost attains the values previously reported for the highly lithium-ion conduct-ing LISICON-type solid electrolytes with composition Li2+2xZn1-xGeO4 [108] and for the layered-structure material Li3 N [109]. LISICON-type conductors and Li3 N are unstable in ambient atmosphere, but the NASICON-type lithium conducting solid electrolytes are stable both in ambient atmosphere and in aqueous solution with a high content of LiCl and LiNO3 [110]. This type of lithium-ion solid conductors has been used as a protective layer for the water-stable lithium elec-trode of aqueous lithium-air batteries by Visco et al. [111] and Imanishi et al. [112].

Figure 30. (a) Temperature dependence of the ionic conductivity of la1-xSr1+xlih2-xo2; and (B) discharge curve for the Ti/orthorhombic la2liho3/Tih2 cell at 300 °c. from [104]. reprinted with permission from aaaS.

Figure 31. conductivity measured at 25 °c as a function of x in li1+xMxTi2-x(Po4)3 ○: liTi2(Po4)3, ●: li1+xalxTi2-x(Po4)3, ▲: li1+xScxTi2-x(Po4)3, : li1+xyxTi2-x(Po4)3, ◇: li1+xlaxTi2-x(Po4)3. reprinted with permission from J. Electrochem. Soc., 136, 590 (1989). copyright 1989, The electrochemical Society [107].


A new thio-LISICON crystalline material family was found in the Li2S-GeS2-P2S5 system by Kanno and Murayama in 2001 [121]. The solid solution member x = 0.75 in Li4-xGe1-xPxS4 showed the highest conductiv-ity of 2.2 × 10–3 S cm–1 at 25 °C, together with negligible electronic conductivity, high electrochemical stability, no reaction of lithium metal, and no phase transition up to 500 °C. The thio-LISICON has a similar structure to that of the Li14Zn(GeO4)4 LISICON [122]. Kanno and co-workers [9] reported on the discovery of a fast lithium-ion conductor of composition Li10GeP2S12, the conductivity of which is as high as 0.012 S cm–1 at room temperature. The lithium ion conductivity of this solid electrolyte is higher than those of the conventional non-aqueous electrolytes, and its room temperature lithium ion conductivity is the highest reported to date. Li10GeP2S12 was synthesized by reacting stoichiometric quantities of Li2S, GeS2, and P2S5 at 550 °C in an evacu-ated quartz tube. The XRD pattern of the reaction prod-uct indicated a new phase with a structure that differed from those of previously reported lithium-ion conduc-tors such as thio-LISICON Li7PS5. The composition and the structure of Li10GeP2S12 were determined by syn-chrotron XRD and neutron diffraction measurements. Figure 34 shows the conductivity measurement results for Li10GeP2S12.. The activation energy for conduction was found to be 24 kJ mol–1.

The electrochemical stability of Li10GeP2S12 was examined by cyclic voltammetry of a Li/Li10GeP2S12/Au cell with a lithium reference electrode. No significant current due to electrolyte decomposition was detected up to 5 V. The electronic conductivity at 25 °C was meas-ured by the Hebb-Wagner polarization method using a Li/Li10GeP2S12/Au cell. The total electronic conductivity (electron and hole) was found to be 5.7 × 10–9 S cm–1. The new highly lithium-ion conducting solid electro-lyte was identified as well suited for all-solid-state lith-ium batteries. Figure 35 shows the charge–discharge curves of a battery that consisted of a LiCoO2 cathode,

3.2 × 10–3 S cm–1. The activation energy for conduction of the glass-ceramic was as low as 13 kJ mol–1, which is approximately one-third of that of the glass. This con-ductivity enhancement by crystallization of the glass is explained by the precipitation of a highly lithium-ion conducting crystal phase of Li2S-P2S5 [115]. A new crys-talline phase was observed in the glass-ceramic heated at 240 and 360 °C that was not obtained in solid-state reactions. The crystalline structure of the new phase Li7P3S11 was determined from synchrotron XRD data [116]. The high conductivity of the glass-ceramic heat-treated at 360 °C was caused by both the precipitation of the Li7P3S11 phase and the increase in the crystal-linity of the phase. The lower conductivity Li4P2S6 and Li3.55P0.89S4 crystals were mainly present in the sample obtained by solid-state reaction. Thus, the highly con-ducting L7P3S11 crystals precipitate as a metastable phase when the glass is crystalized. The metastable phase is responsible for the high conductivity and low activation energy for conduction of 70Li2S-30P2S5. Tatsumisago and Hayashi have extensively examined all-solid-state batteries containing this highly lithium-ion conducting glass ceramic compound [117]. Figure 31 shows some results for all-solid-state batteries with a Li-In anode, a highly lithium-ion conducting glass ceramic electrolyte, and a sulfur cathode. Excellent charge–discharge perfor-mance was obtained at room temperature and a current density of 0.046 mA cm–2. The all-solid-state batteries with sulfur exhibited a much larger capacity than that of the conventional lithium-ion battery with LiCoO2, greater than 1000 mAh g–1. In the case of Li-In/S batter-ies with S-C composite, this large capacity was retained after many charge–discharge cycles [118].

Takada and coworkers [119,120] reported that the low capacity of a cell with a LiCoO2 cathode could be explained by a space charge layer formed between the electrolyte and LiCoO2, which resulted in the formation of a large interface resistance. They improved the inter-face resistance by adding an interlayer of Li4Ti5O12 or LiNbO3 between the electrolyte and LiCoO2

Figure 32. Temperature dependence of electrical conductivity of 70li2S-30P2S5. reprinted from [113] with permission from elsevier.

Figure 33. charge-discharge curves for all-solid-state li-in/80li2S-20P2S5 glass ceramic/S-c (or S-cu, licoo2) cell. reprinted from [117] with permission from elsevier.


their engines. These oxygen sensors typically contain the stabilized zirconia oxide-ion conducting solid electrolyte that was used as a heat element in 1897 by Nernst. At present, 67% of the zirconia-type oxygen sensors in all cars are supplied by Japanese companies.

In the battery industry, many types of solid ionic materials have been used. The largest commercial appli-cation for solid ionic materials is lithium-ion batteries, which were first commercialized by Sony, Japan, in 1990. Lithium-ion and electron mixed conductors such as LiCoO2 and LiC6 have been widely used as cathode and anode materials, for which high lithium-ion diffusion is desirable to achieve a high power density. Small-sized lithium-ion batteries have a large market in portable electronic equipment such as mobile phones. More recently, lithium-ion batteries have been used in elec-tric and hybrid vehicles by Japanese motor companies, and are also planned for use in the storage of electricity from solar cells and wind power generators. Thus, the lithium-ion battery market is expected to grow rapidly in the next ten years, both in Japan and globally.

SOFCs also consist of solid state ionic materials; an oxide-ion conductor as the electrolyte and a per-ovskite-type oxide for the air electrode. Many Japanese companies have been developing SOFCs for many years, and a 0.7 kW-type SOFC system had been commercial-ized. The flat tubular-type SOFC stack was designed by Kyocera, Japan. Its energy efficiency for electricity is 46.5% lower heating value (LHV), and its total efficiency, including hot water generation, is 80% (LHV). The price of the unit is approximately US$26,000. At present, the cost of such units remains expensive and a government support through subsidies would increase the uptake by private households.

The most successful application of solid state ionic materials in Japan is sodium-sulfur batteries (NAS batteries). NAS batteries consist of a sodium anode, a β-alumina sodium-ion conducting solid electro-lyte, and a sulfur cathode. This battery system was proposed by Ford Motors in the 1960s [126]. The key material is the β-alumina sodium-ion conducting solid electrolyte. Yao and Kummer [127] reported that β- alumina exhibits rapid sodium-ion diffusion, and its high ionic conductivity has led to intense effort to develop high energy batteries. The two most highly conductive members of the Na2O-Al2O3 sys-tem are Na2O·1Al2O3 (β-alumina) and Na2O·5Al2O3 (β'-alumina). The electrical conductivity of poly-crystalline β'-alumina is approximately 0.2 S cm–1 at 300 °C [128]. NAS batteries are expected to have high energy density, high charge/discharge efficiency, and long cycle life. Therefore, early studies on this battery were focused on exploiting these properties for appli-cation in electric vehicles in Europe and the United States. However, batteries with the high energy den-sity required for electric vehicles have not yet been

a Li10GeP2S12 electrolyte, and an In metal anode at a current density of 14 mA g–1. The battery exhibited a dis-charge capacity of 120 mAh g–1 and an excellent charge and discharge efficiency of approximately 100% after the second cycle, which demonstrated Li10GeP2S12 to be applicable as a practical electrolyte for all-solid-state batteries. More recently, Kanno and co-workers [123] found a new lithium-ion conducting solid electrolyte, Li9.54Si1.74P1.44S11.7Cl0.3, the lithium-ion conductivity of which is 2.5 × 10–2 S. This conductivity value is about double those of Li10GeP2S12 and conventional non- aqueous lithium conducting liquid electrolytes. The crystal structure of the new compound was analyzed by high power neutron diffraction analysis

9. Applications of solid ionic materials in Japan

Solid ionic materials have been mainly used in two industrial fields, sensors [124] and batteries [125]. Most cars have oxygen sensors to control the exhaust gas from

Figure 34. lithium ion conductivity of li10geP2S12. reprinted by permission from Macmillan Publishers ltd [9], copyright 2011.

Figure 35. charge-discharge curves of an all-solid-state battery consisting of a licoo2 cathode, a li10geP2S12 electrolyte, and an in metal anode. reprinted by permission from Macmillan Publishers ltd [9], copyright 2011.


in 1972. The main research topics in the symposium were the properties of the typical highly ion conducting solid electrolytes and ionic and electron mixed conductors, most of which were already known, with an addition of newly discovered fast ion conductors, then, such as β-alumina and RbAg4I5. In contrast, the 38th Solid State Ionics Symposium in Japan in 2012 mostly concentrated on materials for lithium batteries and fuel cells, where research into new electrode materials and electrolytes is a key for the development of high energy and high power density secondary batteries for electric vehicle applica-tions. In particular, electrode materials with high ion diffusivity should be developed to obtain high specific power density. SOFCs are one of the high-efficiency ener-gy-conversion systems consisting of electrolytes and elec-trode materials developed in the field of solid state ionics. Thus, fundamental studies on the structure and proper-ties of solid state ionic materials are essential to discover new materials for such batteries and energy-conversion devices. In addition, although ion migration in nano-electronic devices, such as CMOS devices, has beven considered a detrimental issue best avoided, utilization of local ion migration and resultant local redox reaction is growing and expanding very rapidly, receiving much attention as one of most advanced topics to realize nano-electronic devices controlled by ionic motion.

Research activity in solid state ionics has been dependent on the discovery of new solid ionic mate-rials; novel materials open the door of a new material science. For half a century, many new solid state ionics materials have come from Japan, as reviewed here, and the author hopes for more to come in future. Finally, solid state ionics originated in Europe, and an excellent review of the development of solid state ionics there, from foundation up to the present day, was presented by Funke [131].

Disclosure statementNo potential conflict of interest was reported by the author.

References [1] Takahashi T, Yamamoto O. 固体電解質の導電

率-6-AgS-HgI2系の導電率 [Conductivity of solid state electrolyte - 6-AgS-HgI2]. Denkikagaku (Electro-chemistry, in Japanese). 1967;35:32. http://dl.ndl.go.jp/info:ndljp/pid/3381401

[2] Takahashi T, Yamamoto O. The relevance of accelerated electrochemical pitting tests to the long-term pitting and crevice corrosion behavior of stainless steels in marine environments. J Electrochem Soc. 1971;118:1057. doi:https://doi.org/10.1149/1.2408246.

[3] Takahashi T. Opening remarks. Solid State Ionics. 1981;3-4:ix-x. doi:https://doi.org/10.1016/0167-2738 (81)90043-6

[4] Miyake S, Hoshino S, Takenaka T. On the phase transition in cuprous iodide. J Phys Soc Japan. 1952;7(1):19–24. doi:https://doi.org/10.1143/JPSJ.7.19.

developed with this system. NAS batteries have also been considered as promising candidates for station-ary storage applications. Significant achievements have been made in such applications, especially in Japan [129,130]. Figure 36 shows a cross-sectional view of a NAS battery in which molten sodium metal serves as the negative electrode and is contained inside a β'-alu-mina tube with a porous metal wick. The β' alumina tube is sealed with glass solder to an α-alumina header that electrically insulates it from the negative electrode. A pre-cast matrix of graphite felt impregnated with molten sulfur, which serves as the positive electrode, is placed in the gap between the β’-alumina tube and the cell container. NGK Insulators, Ltd. had commer-cialized NAS batteries in Japan in 2002. Their standard 2 MW and 12 MWh (forty 50 kW units) system has a guaranteed service life of 15 years (2500 cycles at 100% discharge depth, 4500 cycles at 90% discharge depth). The NAS based batteries installed worldwide reached 530 MW in 2012, according to NGK Insulators.

10. Conclusions and future developments

In this article, the author reviewed the development of solid state ionics from its basic science to possible appli-cations, from the viewpoint of discovery of new mate-rials. If we look back through the last 70-year history of solid state ionics research, Japan was a major contribut-ing country that played an active role in the discovery, theoretical modeling, and applications of new materials. The development of solid state ionics can be illustrated by comparing the popular topics today with those in the early days: 24 papers were presented at the first Solid State Ionics Symposium in Japan, organized in Nagoya

Figure 36. cross-sectional view of a naS battery. reprinted from [130] with permission from elsevier.

http://dl.ndl.go.jp/info:ndljp/pid/3381401

http://dl.ndl.go.jp/info:ndljp/pid/3381401

https://doi.org/10.1149/1.2408246

https://doi.org/10.1016/0167-2738(81)90043-6

https://doi.org/10.1016/0167-2738(81)90043-6

https://doi.org/10.1143/JPSJ.7.19



[22] Leclaire AD, Lidiard AB. LIII. Correlation effects in diffusion in crystals. Phil Mag. 1956;1(6):518. doi:https://doi.org/10.1080/14786435608238133.

[23] Manning JB. Correlation effects in impurity diffusion. Phys Rev. 1959;116(4):819–827. doi:https://doi.org/10.1103/PhysRev.116.819; Manning JB. Correlation factors for impurity diffusion—fcc Lattice. Phys. Rev. 1962;128:2169. doi:https://doi.org/10.1103/PhysRev.128.2169.

[24] Hoshino S. Crystal structure and phase transition of some metallic halides (II) on the phase transition and the crystal structures of cuprous bromide. J Phys Soc Japan. 1952;7(6):560–564. doi:https://doi.org/10.1143/JPSJ.7.560

[25] Reuter B, Hardel K. Ueber die Hochtemperatur modifikation von Silbersulfidjodid. Naturwissen schaften. 1961;48(6):161–161. doi:https://doi.org/ 10.1007/BF00639542.

[26] Takahashi T, Yamamoto O. The Ag/Ag3SI/I2 solid electrolyte cell. Electrochimica Acta. 1966;11(7):779–789. doi:https://doi.org/10.1016/0013-4686(66) 87055-X.

[27] Bradley JN, Greene PD. Solids with high ionic conductivity in group 1 halide systems. Trans Faraday Soc. 1967;63:424. doi:https://doi.org/10.1039/TF967 6300424.

[28] Owens BB, Argue GR. High-Conductivity solid electrolytes: MAg4I5. Science. 1967;157(3786):308–310. doi:https://doi.org/10.1126/science.157.3786.308.

[29] Argue GR, Owens BB. 133rd National Meeting of the Electrochemical Society. Boston, MA. MS Abstract #281; 1968.

[30] Takahashi T, Ikeda S, Yamamoto O. Solid-state ionics: a new high ionic conductivity solid electrolyte Ag6I4WO4 and use of this compound in a solid-electrolyte cell. J Electrochem Soc. 1973;120(5):647. doi:https://doi.org/10.1149/1.2403524.

[31] Takahashi T, Ikeda S, Yamamoto O. Solid-state ionics—Solids with high ionic conductivity in the systems silver iodide-silver oxyacid salts. J Electrochem Soc. 1972;119(4):477–482. doi:https://doi.org/10.1149/1.2404235.

[32] Takahashi T, Yamamoto O, Ikeda S. Solid‐state ionics: high‐conductivity solid copper ion conductors: N‐Alkyl (or Hydro)‐hexa methyl enetetra mi ne Halide‐Copper(l) Halide double salts. J Electrochem Soc. 1973;120;1431. doi: https://doi.org/10.1149/1.2403276

[33] Takahashi T, Kanno R, Takeda Y, et al. Solid-state ionics-the CuCl-CuI-RbCl system. Solid State Ionics. 1981;3/4:283–287. doi:https://doi.org/10.1016/0167-2738(81)90099-0.

[34] Takahashi T, Yamamoto O. 5th Symp. Solid State Ionics Japan, Nagoya, Japan. Abstract P199; 1977.

[35] Matsui T, Wagner JB. Investigations on a high conductivity solid electrolyte system, RbCl + CuCl. J Electrochem Soc. 1977;124(6):941–944. doi:https://doi.org/10.1149/1.2133458.

[36] Phillips JC. Structural principles of α - AgI and related double salts. J Electrochem Soc. 1976;123(6):934–940. doi:https://doi.org/10.1149/1.2132971.

[37] Bonino F, Lazzari M. Electrical conductivity of KCu4I5. J Power Sources. 1976;1(1):103–106. doi: https://doi.org/10.1016/0378-7753(76)80012-2.

[38] Phillips JC. Ionicity of the chemical bond in crystals. Rev Modern Phys. 1970;42(3):317–356. doi: https://doi.org/10.1103/RevModPhys.42.317.

[5] Yokota I. On the deviation from the Einstein relation observed for diffusion of Ag+ Ions in α-Ag2S and others. J Phys Soc, Japan. 1966;21(3):420–423. doi:https:// doi.org/10.1143/JPSJ.21.420

[6] Takahashi T, Yamamoto O, Yamada S, Hayashi S. Solid-state ionics: high copper ion conductivity of the system CuCl - CuI - RbCl. J Electrochem Soc. 1979;126(10):1654. doi:https://doi.org/10.1149/1. 2128770.

[7] Iwahara H, Esaka T, Uchida H, et al. Proton conduction in sintered oxides and its application to steam electrolysis for hydrogen production. Solid State Ionics. 1981;3/4:359–363. doi:https://doi.org/10.1016/0167-2738(81)90113-2.

[8] Ishihara T, Matsuda H, Takita Y. Doped LaGaO3 Perovskite type oxide as a new oxide ionic conductor. J Am Chem Soc. 1994;116:3801. doi:https://doi.org/10.1021/ja00088a016.

[9] Kamaya N, Honma K, Yamakawa Y, et al. A lithium superionic conductor. Nature Mat. 2011;10(9):682–686. doi:https://doi.org/10.1038/nmat3066.

[10] Jost W. Specific heats of -silver iodide. J Chem Phy. 1971;55:4680. doi:https://doi.org/10.1063/1.1676826.

[11] Tubandt C. Leitfähigkeit and Überführungszahlen in festen Elektrolyten. In: Handbuch der Experimentalphysik. Wien W, Harms F, editors. Leipzig: Akademische Verlagsgesell schaft, 12, pt. 1; 1932. p. 383–469.

[12] Frenkel J, Physik Z. Über die Wärmebewegung in festen und flüssigen Körpern. Physik Z. 1926;35:652. doi:https://doi.org/10.1007/BF01379812.

[13] Takahashi T, Kuwabara K, Yamamoto O. The electrical conductivity and the crystal structure of silver iodide. J Electrochem Soc. 1969;116(3):357–360. doi:https://doi.org/10.1149/1.2411846.

[14] Strock LW. Z Phys Chem. 1934;B25:441–459; Strock LW. Z Phys Chem. 1936;B31:132–136.

[15] Hoshino S. Crystal structure and phase transition of some metallic halides (IV) on the anomalous structure of α-AgI. J Phys Soc Japan. 1957;12(4):315–326. doi:https://doi.org/10.1143/JPSJ.12.315.

[16] Hoshino S, Sakuma T, Fujishima H, et al. Neutron scattering study on distribution of cations in α-AgI-type superionic conductors. J Phys Soc Japan. 1983;52(4):1261–1269. doi:https://doi.org/10.1143/JPSJ.52.1261.

[17] Hoshino S, Sakuma T, Fujii Y. Distribution and anharmonic thermal vibration of cations in α-AgI. Solid State Commun. 1977;22(12):763–765. doi:https://doi.org/10.1016/0038-1098(77)90063-1.

[18] Cava RJ, Reidinger F, Wuensh BJ. Single-crystal neutron-diffraction study of AgI between 23° and 300 °C. Solid State Commun. 1977;24(6):411–416. doi:https://doi.org/10.1016/0038-1098(77)91306-0.

[19] Okazaki H. Deviation from the Einstein relation in average crystals self diffusion of Ag+ ions in α-Ag2S and α-Ag2Se. J Phys Soc Japan. 1967;23(2):355–360. doi:https://doi.org/10.1143/JPSJ.23.355.

[20] Kubo R. Statistical-mechanical theory of irreversible processes. I. General theory and simple applications to magnetic and conduction problems. J Phys Soc Japan. 1957;12(6):570–586. DOI: https://doi.org/10.1143/JPSJ.12.570

[21] Compaan K, Haven Y. Correlation factors for diffusion in solids. Trans Faraday Soc. 1956;52:786. DOI: https://doi.org/10.1039/TF9565200786; Compaan K, Haven Y. Correlation factors for diffusion in solids. Part 2. —Indirect interstitial mechanism. Trans Faraday Soc. 1958;54:1498. doi:https://doi.org/10.1039/TF9585401498.

https://doi.org/10.1080/14786435608238133

https://doi.org/10.1103/PhysRev.116.819






https://doi.org/10.1007/BF00639542

https://doi.org/10.1007/BF00639542

https://doi.org/10.1016/0013-4686(66)87055-X

https://doi.org/10.1016/0013-4686(66)87055-X

https://doi.org/10.1039/TF9676300424

https://doi.org/10.1039/TF9676300424

https://doi.org/10.1126/science.157.3786.308

https://doi.org/10.1149/1.2403524

https://doi.org/10.1149/1.2404235

https://doi.org/10.1149/1.2404235

https://doi.org/10.1149/1.2403276

https://doi.org/10.1149/1.2403276

https://doi.org/10.1016/0167-2738(81)90099-0

https://doi.org/10.1016/0167-2738(81)90099-0

https://doi.org/10.1149/1.2133458

https://doi.org/10.1149/1.2133458

https://doi.org/10.1149/1.2132971

https://doi.org/10.1016/0378-7753(76)80012-2

https://doi.org/10.1016/0378-7753(76)80012-2

https://doi.org/10.1103/RevModPhys.42.317

https://doi.org/10.1103/RevModPhys.42.317



https://doi.org/10.1149/1.2128770

https://doi.org/10.1149/1.2128770

https://doi.org/10.1016/0167-2738(81)90113-2

https://doi.org/10.1016/0167-2738(81)90113-2

https://doi.org/10.1021/ja00088a016

https://doi.org/10.1021/ja00088a016

https://doi.org/10.1038/nmat3066

https://doi.org/10.1063/1.1676826

https://doi.org/10.1007/BF01379812

https://doi.org/10.1149/1.2411846

https://doi.org/10.1149/1.2411846



https://doi.org/10.1016/0038-1098(77)90063-1

https://doi.org/10.1016/0038-1098(77)90063-1

https://doi.org/10.1016/0038-1098(77)91306-0




https://doi.org/10.1039/TF9565200786

https://doi.org/10.1039/TF9565200786

https://doi.org/10.1039/TF9585401498


[58] Wagner C. Equation for transport in solid oxide and sulfides of transition metals. Progs Solid State Chem. 1975;10:3–16. doi:https://doi.org/10.1016/0079-6786(75)90002-3.

[59] de Groot SR, Mazur P. Non-equilibrium thermo dynamics. North-Holland, Amsterdam; 1969. OCLC No.：301696976

[60] Takahashi T, Yamamoto O. Solid-state ionics-mixed ionic and electronic conduction in Ag2Se-Ag3PO4 solid solutions. J Electrochem Soc. 1972;119(12):1735. doi:https://doi.org/10.1149/1.2404089.

[61] Ikeda H, Tada K. Application of solid electrolyte. Takahashi T, Kozawa A, editors. Cleveland, USA: JES press Inc; 1980.

[62] Taguchi H, Shimada M, Koizumi M. The effect of oxygen vacancy on the magnetic properties in the system SrCoO3-δ (0 < δ < 0 5). J Solid State Chem. 1979;29 (2):221–225.

[63] Ishigaki T, Yamauchi S, Mizusaki J, et al. Tracer diffusion coefficient of oxide ions in LaCoO3 single crystal. J Solid State Chem. 1984;54(1):100–107. doi:https://doi.org/10.1016/0022-4596(84)90136-1.

[64] Mizusaki J, Yamauchi S, Fueki K, et al. Nonstoichiometry of the perovskite-type oxide La1−xSrxCrO3−δ. Solid State Ioncis. 1984;12:119–124. doi:https://doi.org/10.1016/0167-2738(84)90138-3.

[65] Minh NQ, Takahashi T. Science and technology of ceramic fuel cell. Amsterdam: Elsevier; 1995. ISBN 9780080540764.

[66] Zeng Y, Lin YS. A transient TGA study on oxygen permeation properties of perovskite-type ceramic membrane. Solid State Ionics. 1998;110(3-4):209–221. doi:https://doi.org/10.1016/S0167-2738(98)00136-2.

[67] Obayashi H, Kudo T. Application of solid electrolyte. T. Takahashi, A. Kozawa, editors. Clevland, OH: JEC press; 1980. P102.

[68] Yasuda I, Hikita T. Electrical conductivity and defect structure of calcium-doped lanthanum chromites. J Electrochem Soc. 1993;140(6):1699–1704. doi:https://doi.org/10.1149/1.2221626.

[69] Boroomand F, Wessel E, Bausinger H, et al. Correlation between defect chemistry and expansion during reduction of doped LaCrO3 interconnects for SOFCs. Solid State Ionics. 2000;129(1-4):251–258. doi:https://doi.org/10.1016/S0167-2738(99)00330-6.

[70] Onuma S, Yashiro K, Miyoshi S, et al. Oxygen nonstoichiometry of the perovskite-type oxide La1−xCaxCrO3−δ (x=0.1, 0.2, 0.3). Solid State Ionics. 2004;174(1-4):287–293. doi:https://doi.org/10.1016/ j.ssi.2004.07.037.

[71] Mizusaki J, Yasuda I, Shimoyama J, et al. Electrical conductivity, defect equilibrium and oxygen vacancy diffusion coefficient of La1−x Cax AlO3−δ single crystals. J Electrochem Soc. 1993;140(2):467–471. doi:https://doi.org/10.1149/1.2221070.

[72] Takahashi T, Iwahara H. Denkikagaku (Electro chemistry, in Japanese). 1967;35(6):433-437.

[73] Takahashi T, Iwahara H. Ionic conduction in perovskite type oxide solid solution its application to the solid electrolyte fuel cell. Energy Conv. 1971;11(3):105–111. doi:https://doi.org/10.1016/0013-7480(71)90100-8.

[74] Fueki K, Mizusaki J, Yamauchi S, et al. Reactivity of solids, Barret P, Dufour LC, editors. Elsevier, Amsterdam; 1986. p 339

[39] Bradley JM, Green D. Potassium iodide + silver iodide phase diagram. High ionic conductivity of KAg4I5. Trans Faraday Soc. 1966;62:2069. doi: https://doi.org/10.1039/TF9666202069.

[40] Yamamoto O. Report of works supported by grant-in-aid for co-operation research; 1983. p. 42.

[41] Kanno K, Takeda Y, Masuyama Y, et al. Phase diagram and high copper ion conductivity of the copper(I) chloride-rubidium chloride system. Solid State Ionics. 1983;11(3):221–226. doi:https://doi.org/ 10.1016/0167-2738(83)90027-9.

[42] Biefeld RM. The KBr-CuBr and NaBr-CuBr phase diagrams. Mat Res Bull. 1975;10(11):1151–1156. doi:https://doi.org/10.1016/0025-5408(75)90019-7.

[43] Atake T, Kawaji H, Kanno R, et al. Heat capacity anomaly in the high ionic conductor Rb4Cu16I7Cl13. Solid State Ionics. 1992;53-56:1260–1263. doi:https://doi.org/10.1016/0167-2738(92)90322-G.

[44] Kanno R, Ohno K, Kawamoto Y, et al. Neutron diffraction study of high ionic conductor Rb4Cu16I7+xCl13-x at 50-300 K: correlation with ionic conductivity. J Solid State Chem. 1993;102(1):79–92. doi:https://doi.org/10.1006/jssc.1993.1009.

[45] Geller S. Crystal structure of the solid electrolyte, RbAg4I5. Science. 1967;157(3786):310–312. doi:https://doi.org/10.1126/science.157.3786.310.

[46] Owens BB, Argue GR. High conductivity solid electrolyte system Rbl ‐ AgI. J Electrochem Soc. 1970;117(7): 898-900. doi:https://doi.org/10.1149/ 1.2407666

[47] Owens BB, Argue GR, Groce IJ. Power Sources. Collins DH, editor. Vol. 2. Oxford: Pergamon Press; 1970. p. 389. ISBN 0080134351

[48] Rossi M, Pistoia G, Scrosati B. A reversible solid-state battery with RbAg4I5 as Electrolyte. J Electrochem Soc. 1969;116(12):1642–1646. doi:https://doi.org/10.1149/ 1.2411648.

[49] Miyatani S. Point contact of Pt and γ-Cu2S. J Phys Soc Japan. 1956;11(10):1059–1063. doi:https://doi.org/10.1143/JPSJ.11.1059.

[50] Miyatani S. α-Ag2S as a mixed conductor. J Phys Soc Japan. 1968;24(2):328–336. doi:https://doi.org/10.1143/JPSJ.24.328.

[51] Miyatani S, Yokota I. Galvano- and thermomagnetic effects in α-Ag2Te. J Phys Soc Japan. 1959;14(6):750–754. DOI:https://doi.org/10.1143/JPSJ.14.750

[52] Wagner JB, Wagner C. Investigations on cuprous sulfide. J Chem Phys. 1957;26(6):1602–1606. doi:https://doi.org/10.1063/1.1743591.

[53] Ishikawa T, Miyatani S. Electronic and ionic conduction in Cu2-δSe, Cu2-δS and Cu2-δ(Se, S). J Phys Soc Japan. 1977;42(1):159–167. doi:https://doi.org/10.1143/JPSJ.42.159.

[54] Wagner C. Z Physik Chem. 1933;B21:25. [55] Yokota I. On the theory of mixed conduction with

special reference to conduction in silver sulfide group semiconductors. J Phys Soc Japan. 1961;16(11):2213–2223. doi:https://doi.org/10.1143/JPSJ.16.2213

[56] Yokota I, Miyatani S. Conduction and diffusion in ionic-electronic conductors. Solid State Ionics. 1981;3/4:17–21. doi:https://doi.org/10.1016/0167-2738(81)90047-3.

[57] Miyatani S. An extension of Yokota’s diffusion theory on mixed conduction to larger applied voltages. J Phys Soc Japan. 1981;50(5):1595–1602. doi:https://doi.org/10.1143/JPSJ.50.1595.

https://doi.org/10.1016/0079-6786(75)90002-3

https://doi.org/10.1016/0079-6786(75)90002-3

https://doi.org/10.1149/1.2404089

https://doi.org/10.1016/0022-4596(84)90136-1

https://doi.org/10.1016/0167-2738(84)90138-3

https://doi.org/10.1016/S0167-2738(98)00136-2

https://doi.org/10.1149/1.2221626

https://doi.org/10.1149/1.2221626

https://doi.org/10.1016/S0167-2738(99)00330-6

https://doi.org/10.1016/S0167-2738(99)00330-6

https://doi.org/10.1016/j.ssi.2004.07.037


https://doi.org/10.1149/1.2221070

https://doi.org/10.1149/1.2221070

https://doi.org/10.1016/0013-7480(71)90100-8

https://doi.org/10.1039/TF9666202069

https://doi.org/10.1039/TF9666202069

https://doi.org/10.1016/0167-2738(83)90027-9

https://doi.org/10.1016/0167-2738(83)90027-9

https://doi.org/10.1016/0025-5408(75)90019-7

https://doi.org/10.1016/0167-2738(92)90322-G

https://doi.org/10.1016/0167-2738(92)90322-G

https://doi.org/10.1006/jssc.1993.1009



https://doi.org/10.1149/1.2407666

https://doi.org/10.1149/1.2407666

https://doi.org/10.1149/1.2411648

https://doi.org/10.1149/1.2411648






https://doi.org/10.1063/1.1743591

https://doi.org/10.1063/1.1743591




https://doi.org/10.1016/0167-2738(81)90047-3




[91] Badwal SPS. Effect of dopant concentration on electrical conductivity in the Sc2O3-ZrO2 system. J Material Science. 1987;22(11):4125–4132. doi:https://doi.org/10.1007/BF01133368.

[92] Yamamoto O, Arachi Y, Takeda Y, et al. Electrical conductivity of stabilized zirconia with ytterbia and scandia. Solid State Ionics. 1995;79: 137–142. doi:https://doi.org/10.1016/0167-2738(95) 00044-7.

[93] Mizutani Y, Kawai M, Nomura K, et al. Proceeding of 5th International Symposium on Solid Oxide Fuel Cells. Stimming U, Singhal SC, Tagawa H, et al. Pennington, NJ: The Electrochem. Soc; 1997. p. 196. ISBN 1566771455 OCLC 421665039

[94] Kudo T, Obayashi H. Oxygen ion conduction of the fluorite-type Ce1−xLnxO2−x/2 (Ln = Lanthanoid Element). J Electrochem Soc. 1975;122(1):142–147. doi:https://doi.org/10.1149/1.2134143.

[95] Cook Rl, Osborne JJ, White JH, et al. Investigations on BaTh0.9Gd0.1 O 3 as an intermediate temperature fuel cell solid electrolyte. J Electrochem Soc. 1992;139(2):L19-L20. doi:https://doi.org/10.1149/1.2069273

[96] Feng M, Goodenough JB. A superior oxide-ion electrolyte. Eur J Inorg Chem. 1994;131:663-672. ISSN: 0992-4361

[97] Ishihara T, Ando M, Enoki M, et al. Proceedings of rare earths’04 in Nara, Japan oxide ion conductivity in La(Sr)Ga(Fe, Mg)O3 and its application for solid oxide fuel cells. J Alloys Compounds. 2006;408-412:507–511. doi:https://doi.org/10.1016/j.jallcom.2004. 12.086.

[98] Nakayama S, Aono H, Sadaoka Y. Ionic conductivity of Ln10(SiO4)6O3 (Ln = La, Nd, Sm, Gd and Dy). Chem Lett. 1995;24(6):431–432. doi:https://doi.org/10.1246/cl.1995.431.

[99] Yoshioka H, Tanase S. Magnesium doped lanthanum silicate with apatite-type structure as an electrolyte for intermediate temperature solid oxide fuel cells. Solid Stat Ionics. 2005;176(31-34):2395–2398. doi:https://doi.org/10.1016/j.ssi.2005.06.026.

[100] Samson JEH, Richings D, Slater PR. A powder neutron diffraction study of the oxide-ion-conducting apatite-type phases, La9.33Si6O26 and La8Sr2Si6O26. Solid State Ionics. 2001;139:205. doi:https://doi.org/10.1016/S0167-2738(00)00835-3.

[101] Ali R, Yashima M, Matsushima Y, et al. Diffusion path of oxide ions in an apatite-type ionic conductor La9.69(Si5.70Mg0.30)O26.24. Chem Mater. 2008;20(16):5203–5208. doi:https://doi.org/10.1021/cm7035234.

[102] Kobayashi K, Sakka Y. Research progress in nondoped lanthanoid silicate oxyapatites as new oxygen-ion conductors. J Ceram Soc Japan. 2014;122(1431):921–939. doi:https://doi.org/10.2109/jcersj2.122.921.

[103] Verbraeken MC, Cheung C, Sauard E, et al. High H− ionic conductivity in barium hydride. Nat Mater. 2015;14:95. doi:https://doi.org/10.1038/nmat4136.

[104] Kobayashi G, Hinuma Y, Matsuoka S, et al. Pure H– conduction in oxyhydrides. Science. 2016;351(6279):1314–1317. DOI:https://doi.org/10.1126/science.aac9185

[105] Wagner J, Wagner C. Electrical conductivity measurements on cuprous halides. J Chem Phys. 1957;26(6):1597–1601. doi:https://doi.org/10.1063/1.1743590.

[106] Yamaguchi S. Large, soft, and polarizable hydride ions sneak around in an oxyhydride. Science. 2016;351(6279):1262–1263. DOI:https://doi.org/10.1126/science.aaf3361

[75] Ishigaki T, Yamauchi J, Mizusaki J, et al. Tracer diffusion coefficient of oxide ions in LaCoO3 single crystal. J Solid State Chem. 1984;54(1):100–107. doi:https://doi.org/10.1016/0022-4596(84)90136-1.

[76] Ishigaki T, Yamauchi S, Kishio K, et al. Diffusion of oxide ion vacancies in perovskite type oxides. J Solid State Chem. 1988;73(1):179–187. doi:https://doi.org/10.1016/0022-4596(88)90067-9.

[77] Iwahara H, Esaka T, Uchida H, et al. Proton conduction in sintered oxides and its application to steam electrolysis for hydrogen production. Solid State Ionics. 1981;3/4:359–363. doi:https://doi.org/10.1016/0167-2738(81)90113-2.

[78] Iwahara H, Uchida H, Maeda N. High temperature fuel and steam electrolysis cells using proton conductive solid electrolytes. J Power Sources. 1982;7(3):293–301. doi:https://doi.org/10.1016/0378-7753(82)80018-9.

[79] Iwahara H, Uchida H, Yanaka S. High temperature type proton conductor based on SrCeO3and its application to solid electrolyte fuel cells. Solid State Ionics. 1983;9/10:1021–1025. doi:https://doi.org/10.1016/0167-2738(83)90125-X.

[80] Iwahara H, Uchida H, Ono K, et al. Proton conduction in sintered oxides based on BaCeO3. J Electrochem Soc. 1988;135(2):529. doi:https://doi.org/10.1149/1.2095649.

[81] Ma G, Shimura T, Iwahara H. Ionic conduction and nonstoichiometry in BaxCe0.90Y0.10O3−α. Solid State Ionics. 1998;110(1-2):103–110. doi:https://doi.org/10.1016/S0167-2738(98)00130-1.

[82] Yajima T, Kazeoka H, Yogo T, Iwahara H. Proton conduction in sintered oxides based on CaZrO3. Solid State Ionics. 1991;47(3-4):271–275. doi:https://doi.org/10.1016/0167-2738(91)90249-B.

[83] Iwahara H, Yajima T, Hibino T, et al. Protonic conduction in calcium, strontium and barium zirconates. Solid State Ionics. 1993;61(1-3):65–69. doi:https://doi.org/10.1016/0167-2738(93)90335-Z.

[84] Iwahara H. Technological challenges in the application of proton conducting ceramics. Solid State Ionics. 1995;77:289–298. doi:https://doi.org/10.1016/0167-2738(95)00051-7.

[85] Iwahara H. Proton conducting ceramics and their applications. Solid State Ionics. 1996;86/88:9–15. doi:https://doi.org/10.1016/0167-2738(96)00087-2.

[86] Iwahara H. 1994. Solid State Ionic Materials. Chowdari BVR, Yahaya M, Talib IA, Salleh MM, editors. (World Science, Singapore). Proceedings of the 4th Asian Conference on Solid State Ionics. Solid State Ionic Materials. Chemical Sensors using Proton Conducting Ceramics p 79. p. 1-472. doi:https://doi.org/10.1142/9789814533942.

[87] Yajima T, Koide K, Fukatsu N, et al. A new hydrogen sensor for molten aluminum. Sensor and Actuator. 1993;14(1-3):697–699. doi:https://doi.org/10.1016/0925-4005(93)85149-5.

[88] Etell TH, Flenas SN. Electrical properties of solid oxide electrolytes. Chem Rev. 1970;70(3):339–376. doi:https://doi.org/10.1021/cr60265a003.

[89] van de Graaf MACG, Burggraaf AJ. 1984. Science and Technology of Zirconia II, Claussen N, Ruhel M, Heuer AH, editors. Columbus, OH: American Ceramics Society. p. 744. ISBN 0916094642

[90] Arachi Y, Sakai H, Yamamoto O, et al. Electrical conductivity of the ZrO2–Ln2O3 (Ln=lanthanides) system. Solid State Ionics. 1999;121(1-4):133–139. doi:https://doi.org/10.1016/S0167-2738(98)00540-2.

https://doi.org/10.1007/BF01133368

https://doi.org/10.1007/BF01133368

https://doi.org/10.1016/0167-2738(95)00044-7

https://doi.org/10.1016/0167-2738(95)00044-7

https://doi.org/10.1149/1.2134143

https://doi.org/10.1149/1.2069273

https://doi.org/10.1016/j.jallcom.2004.12.086

https://doi.org/10.1016/j.jallcom.2004.12.086

https://doi.org/10.1246/cl.1995.431

https://doi.org/10.1246/cl.1995.431



https://doi.org/10.1016/S0167-2738(00)00835-3

https://doi.org/10.1016/S0167-2738(00)00835-3

https://doi.org/10.1021/cm7035234

https://doi.org/10.2109/jcersj2.122.921

https://doi.org/10.1038/nmat4136

https://doi.org/10.1126/science.aac9185

https://doi.org/10.1126/science.aac9185

https://doi.org/10.1063/1.1743590

https://doi.org/10.1126/science.aaf3361

https://doi.org/10.1126/science.aaf3361

https://doi.org/10.1016/0022-4596(84)90136-1

https://doi.org/10.1016/0022-4596(88)90067-9

https://doi.org/10.1016/0022-4596(88)90067-9

https://doi.org/10.1016/0167-2738(81)90113-2

https://doi.org/10.1016/0167-2738(81)90113-2

https://doi.org/10.1016/0378-7753(82)80018-9

https://doi.org/10.1016/0167-2738(83)90125-X

https://doi.org/10.1016/0167-2738(83)90125-X

https://doi.org/10.1149/1.2095649

https://doi.org/10.1149/1.2095649

https://doi.org/10.1016/S0167-2738(98)00130-1

https://doi.org/10.1016/S0167-2738(98)00130-1

https://doi.org/10.1016/0167-2738(91)90249-B

https://doi.org/10.1016/0167-2738(91)90249-B

https://doi.org/10.1016/0167-2738(93)90335-Z

https://doi.org/10.1016/0167-2738(95)00051-7

https://doi.org/10.1016/0167-2738(95)00051-7

https://doi.org/10.1016/0167-2738(96)00087-2

https://doi.org/10.1142/9789814533942

https://doi.org/10.1142/9789814533942

https://doi.org/10.1016/0925-4005(93)85149-5

https://doi.org/10.1016/0925-4005(93)85149-5

https://doi.org/10.1021/cr60265a003

https://doi.org/10.1016/S0167-2738(98)00540-2


[119] Ohta N, Takada K, Zhang L, et al. You have full text access to this contentEnhancement of the high-rate capability of solid-state lithium batteries by nanoscale interfacial modification. Adv Mater. 2006;18(17):2226–2229. doi:https://doi.org/10.1002/adma.200502604.

[120] Ohta N, Takada K, Sakaguchi I, et al. LiNbO3-coated LiCoO2 as cathode material for all solid-state lithium secondary batteries. Electrochem Commun. 2007;9(7):1486–1490. doi:https://doi.org/10.1016/j.elecom.2007.02.008.

[121] Kanno R, Murayama M. Lithium ionic conductor Thio-LISICON: the Li2 S GeS2 P 2 S 5 System. J Electrochem Soc. 2001;148(7):A742–A746. doi:https://doi.org/10.1149/1.1379028.

[122] Hong HYP. Crystal structure and ionic conductivity of Li14Zn(GeO4)4 and other new Li+ superionic conductors. Mater Res Bull. 1978;13(2):117–124. doi:https://doi.org/10.1016/0025-5408(78)90075-2.

[123] Kato Y, Hori S, Saito T, et al. High-power all-solid-state batteries using sulfide superionic conductors. Nat Energy. 2016;1(4):16030. doi:https://doi.org/10.1038/nenergy.2016.30.

[124] Fleming WJ. Physical principles governing nonideal behavior of the Zirconia Oxygen Sensor. J Electrochem Soc. 1977;124(1):21–28. doi:https://doi.org/10.1149/1.2133235

[125] Tarascon JM, Armand M. Issues and challenges facing rechargeable lithium batteries. Nature. 2001;414(6861):359–367. doi:https://doi.org/10.1038/35104644.

[126] Kummer JT, Weber N. Battery having a molten alkali metal anode and a molten sulfur cathode. U.S.Patent 3,413,150; 1968.

[127] Yao YF, Kummer JT. Ion exchange properties of and rates of ionic diffusion in beta-alumina. J Inorg Nucl Chem. 1967;29:2453. doi:https://doi.org/10.1016/0022-1902(67)80301-4.

[128] Kennedy JH. The β-aluminas. In: Solid Electrolyte Geller S, editor. Berlin: Springer. p. 105-141. ISBN 978-3-540-37308-7. 1977. DOI:https://doi.org/10.1007/3-540-08338-3

[129] Oshima T, Kajita M, Okuno A. Development of sodium-sulfur batteries. Int J Appl Ceram Technol. 2004;1:269. doi:https://doi.org/10.1111/j.1744-7402.2004.tb00179.x.

[130] Okuyama R, Nomura E. Relationship between the total energy efficiency of a sodium-sulfur battery system acid the heat dissipation of the battery case. J Power Sources. 1999;77(2):164–169. doi:https://doi.org/10.1016/S0378-7753(98)00190-6.

[131] Funke K. Solid state ionics: from Michael Faraday to green energy—the European dimension. Sci Technol Adv Mater. 2013;14(4):043502. doi:https://doi.org/10.1088/1468-6996/14/4/043502.

[107] Aono H, Sugimoto E, Sadaoka Y, et al. Ionic conductivity of the Lithium Titanium Phosphate (Li1+xMxTi2-x(PO4)3, M = Al, Sc, Y, and La) Systems. J Electrochem Soc. 1989;136(2):590–591. doi:https://doi.org/10.1149/1.2096693.

[108] Bruce PG, West AR. Ionic conductivity of LISICON solid solutions, Li2+2xZn1−xGeO4. J Solid State Chem. 1982;44(3):354–365. doi:https://doi.org/10.1016/0022-4596(82)90383-8.

[109] von Alpen U, Rabenau A, Talat GH. Ionic conductivity in Li3N single crystals. Appl Phys Lett. 1977;30:621. doi:https://doi.org/10.1063/1.89283

[110] Shimonishi Y, Zhang T, Imanishi N, et al. A study on lithium/air secondary batteries—Stability of the NASICON-type lithium ion conducting solid electrolyte in alkaline aqueous solutions. J Power Sources. 2011;196:5128. doi:https://doi.org/10.1016/j.jpowsour.2011.02.023

[111] Visco SJ, Nimon N, Katz B, et al. 210th Electrochemical Society Meeting, Cancun, Mexico; 2006. Abstract # 388.

[112] Zhang T, Imanishi N, Shimonishi Y, et al. Stability of a water-stable lithium metal anode for a Lithium-Air Battery with acetic acid-water solutions. J Electrochem Soc. 2010;157(2):A214–A218. doi:https://doi.org/10.1149/1.3271103.

[113] Minami T, Hayashi A, Tatsumisago M. Recent progress of glass and glass-ceramics as solid electrolytes for lithium secondary batteries. Solid State Ionics. 2006;177(26-32):2715–2720. doi:https://doi.org/10.1016/j.ssi.2006.07.017.

[114] Hayashi A, Hama S, Morimoto H, et al. High lithium ion conductivity of glass-ceramics derived from mechanically milled glassy powders. Chem Lett. 2001;30(9):872–873. doi:https://doi.org/10.1246/cl.2001.872.

[115] Mizuno F, Hayashi A, Tadanaga K, et al. New, highly ion-conductive crystals precipitated from Li2S–P2S5 Glasses. Adv Mater. 2005;17(7):918–921. doi:https://doi.org/10.1002/adma.200401286.

[116] Yamane H, Shibata M, Shimane Y, et al. Crystal structure of a superionic conductor, Li7P3S11. Solid State Ionics. 2007;178(15-18):1163–1167. doi:https://doi.org/10.1016/j.ssi.2007.05.020.

[117] Tatsumisago M, Hayashi A. Superionic glasses and glass–ceramics in the Li2S–P2S5system for all-solid-state lithium secondary batteries. Solid State Ionics. 2012;225:342–345. doi:https://doi.org/10.1016/j.ssi. 2012.03.013.

[118] Nagao M, Hayashi A, Tatsumisago M. Sulfur–carbon composite electrode for all-solid-state Li/S battery with Li2S–P2S5 solid electrolyte. Electrochimica Acta. 2011;56:6055–6059. doi:https://doi.org/10.1016/j.electacta.2011.04.084.

https://doi.org/10.1002/adma.200502604

https://doi.org/10.1016/j.elecom.2007.02.008

https://doi.org/10.1016/j.elecom.2007.02.008

https://doi.org/10.1149/1.1379028

https://doi.org/10.1149/1.1379028

https://doi.org/10.1016/0025-5408(78)90075-2

https://doi.org/10.1038/nenergy.2016.30

https://doi.org/10.1038/nenergy.2016.30

https://doi.org/10.1149/1.2133235

https://doi.org/10.1149/1.2133235

https://doi.org/10.1038/35104644

https://doi.org/10.1016/0022-1902(67)80301-4

https://doi.org/10.1016/0022-1902(67)80301-4

https://doi.org/10.1007/3-540-08338-3

https://doi.org/10.1007/3-540-08338-3

https://doi.org/10.1111/j.1744-7402.2004.tb00179.x

https://doi.org/10.1016/S0378-7753(98)00190-6

https://doi.org/10.1016/S0378-7753(98)00190-6

https://doi.org/10.1088/1468-6996/14/4/043502

https://doi.org/10.1088/1468-6996/14/4/043502

https://doi.org/10.1149/1.2096693

https://doi.org/10.1149/1.2096693

https://doi.org/10.1016/0022-4596(82)90383-8

https://doi.org/10.1016/0022-4596(82)90383-8

https://doi.org/10.1063/1.89283

https://doi.org/10.1016/j.jpowsour.2011.02.023

https://doi.org/10.1016/j.jpowsour.2011.02.023

https://doi.org/10.1149/1.3271103

https://doi.org/10.1149/1.3271103



https://doi.org/10.1246/cl.2001.872

https://doi.org/10.1002/adma.200401286





https://doi.org/10.1016/j.electacta.2011.04.084

https://doi.org/10.1016/j.electacta.2011.04.084