47 lampiran 1. hasil analisa saringan agregat 1

47

LAMPIRAN 1. HASIL ANALISA SARINGAN AGREGAT

1. SIEVE ANALYSIS OF COARSE AGGREGATE (F1)

ORDER : Mahasiswa UKP

STANDARD : ASTM T.27 - 74 ASTM C.136 -92

SAMPLE : Agregat Ukuran F1 ( 10-15 ) mm

PROJECT : Skripsi

DATE : 18 Mar 15

TESTED BY :

SIEVE Retained

Weight (gram)

Comulative Weight

of retained (gram)

% Retained % Passing

Inch mm

3/4" 19,1 0 0 0,00 100,00

1/2" 12,5 543,69 543,69 45,70 54,30

3/8" 9,5 570,46 1114,15 93,65 6,35

No. 4 4,75 74,36 1188,51 99,90 0,10

No. 8 2,36 1,19 1189,7 100,00 0,00

No. 16 1,18 0 0

No. 30 0,3 0 0

No. 50 0,6 0 0

No. 100 0,149 0 0

No. 200 0,075 0 0

Total 1189,7 0

http://www.petra.ac.id

http://dewey.petra.ac.id/dgt_directory.php?display=classification

http://digilib.petra.ac.id/help.html

http://www.petra.ac.id/

http://dewey.petra.ac.id/dgt_directory.php?display=classification

http://digilib.petra.ac.id/help.html

48

2. SIEVE ANALYSIS OF COARSE AGGREGATE (F2)

ORDER

: Mahasiswa UKP


SAMPLE : Agregat Ukuran F2 ( 05-10 ) mm

PROJECT : Skripsi

DATE

: 18 Mar 15

TESTED BY :

SIEVE Retained

Weight

(gram)

Comulative

Weight of

retained

(gram)

%

Retained

%

Passing

Inch mm

3/4" 19,1 0 0 0,00 100,00

1/2" 12,5 0 0 0,00 100,00

3/8" 9,5 76,26 76,26 7,04 92,96

No. 4 4,75 826,75 903,01 83,39 16,61

No. 8 2,36 178,79 1081,8 99,90 0,10

No. 16 1,18 1,1 1082,9 100,00 0,00

No. 30 0,3 0

No. 50 0,6 0

No. 100 0,149 0

No. 200 0,075 0

Total 1082,9


49

3. SIEVE ANALYSIS OF FINE AGGREGATE (F3)

ORDER

: Mahasiswa UKP


SAMPLE

: Agregat Ukuran F3 ( 00 -05 ) mm

PROJECT : Skripsi

DATE

: 18 Mar 15

TESTED BY :

SIEVE Retained

Weight

(gram)

Comulative

Weight of

retained

(gram)

%

Retained

%

Passing

Inch mm

3/4" 19,1 0 0 0 100,00

1/2" 12,5 0 0 0 100,00

3/8" 9,5 0 0 0 100,00

No. 4 4,75 3,42 3,42 0,34 99,66

No. 8 2,36 341,12 344,54 34,62 65,38

No. 16 1,18 231,88 576,42 57,91 42,09

No. 30 0,3 118,7 695,12 69,84 30,16

No. 50 0,6 83,55 778,67 78,23 21,77

No. 100 0,149 86,62 865,29 86,94 13,06

No. 200 0,075 47,95 913,24 91,76 8,24

Dasar 82,06 995,3 100 0,00

Total 995,3


50

LAMPIRAN 2. GRAFIK DISTRIBUSI ANALISA SARINGAN

Distibusi Grafik AC-WC


51

LAMPIRAN 3. PEMERIKSAAN KUALIFIKASI AGREGAT

1. Not Qualified Aggregate Composition AC-WC

2. New Aggregate Composition AC-WC (used)

Passing 20% Passing 34% Passing 46% Passing 0% COMB % Ideal Spec Spec

100,00 20,00 100,00 34,00 100,00 46,00 100 0 100,00 100 100

54,30 10,86 100,00 34,00 100,00 46,00 100 0 90,86 95 90-100

6,35 1,27 92,96 31,61 100,00 46,00 100 0 78,88 81 72-90

0,10 0,02 16,61 5,65 99,66 45,84 100 0 51,51 53 43-63

0,00 0,10 0,03 65,38 30,08 100 0 30,11 33,55 28-39,1

0,00 0,00 42,09 19,36 100 0 19,36 22,3 19-25,6

0,00 0,00 30,16 13,87 100 0 13,87 16,05 13-19,1

0,00 0,00 21,77 10,01 100 0 10,01 12,25 9-15,5

0,00 0,00 13,06 6,01 100 0 6,01 9,5 6-13

0,00 0,00 8,24 3,79 100 0 3,79 7 4-10

(F1) 10 - 15 mm (FII) 05 - 10 mm (FIII) 00 - 05 mm (FIV) Semen

Passing 20% Passing 28% Passing 50% Passing 2% COMB % Ideal Spec Spec

100,00 20,00 100,00 28,00 100,00 50,00 100 2 100,00 100 100

54,30 10,86 100,00 28,00 100,00 50,00 100 2 90,86 95 90-100

6,35 1,27 92,96 26,03 100,00 50,00 100 2 79,30 81 72-90

0,10 0,02 16,61 4,65 99,66 49,83 100 2 56,50 53 43-63

0,00 0,10 0,03 65,38 32,69 100 2 34,72 33,55 28-39,1

0,00 0,00 42,09 21,04 100 2 23,04 22,3 19-25,6

0,00 0,00 30,16 15,08 100 2 17,08 16,05 13-19,1

0,00 0,00 21,77 10,88 100 2 12,88 12,25 9-15,5

0,00 0,00 13,06 6,53 100 2 8,53 9,5 6-13

0,00 0,00 8,24 4,12 100 2 6,12 7 4-10

(F1) 10 - 15 mm (FII) 05 - 10 mm (FIII) 00 - 05 mm (FIV) Semen


52

LAMPIRAN 4. BERAT JENIS AGREGAT

1. BERAT JENIS AGREGAT KASAR DAN HALUS

F1 A B AVG.

Berat Benda Uji 1200 1200 1200

Berat Kering (Bk) 1174 1185,9 1179,95

Berat SSD (Bj) 1182,7 1194,5 1199,95

Berat dalam Air (Ba) 763 770,2 766,6

F2 A B AVG.

Berat Benda Uji 1100 1100 1100

Berat Kering (Bk) 1026,1 1035 1030,55

Berat SSD (Bj) 1042,4 1052,1 1047,25

Berat dalam Air (Ba) 650,5 667,6 659,05

F3 A B AVG.

Berat SSD (X) 500 500 500

Berat Kering (Bk) 495,35 493,35 494,35

Berat Pikno + Air + Agg (Bt) 987,8 988 987,9

Berat Pikno + Air (B) 667,7 667 667,35

Berat Agg 320,1 321 320,55

Perhitungan Berat Jenis bulk, apparent, absorb

Pengetesan Agregat

size agragat % J(BULK) J(APP) ABSORB

F1 20 2,72286 2,8546 1,69499

F2 28 2,65469 2,77402 1,62049

F3 50 2,75481 2,84436 1,14291

FILLER 2


53

LAMPIRAN 5. KEAUSAN AGREGAT

Lolos Tertahan Berat sebelum Berat sesudah Berat sebelum Berat sesudah

19,0 mm (3/4") 12,5 mm (1/2") 2499,5

12,5 mm (1/2") 9,5 mm (3/8") 2500

9,5 mm (3/8") 6,3 mm (1/4") 2500

6,3 mm (1/4") 4,75 mm (no. 4) 2500

5000 3210,2 4999,5 3913,1

Saringan I II

Rata-rata Keausan 28,763

Gradasi Pemeriksaan Agregat Pandaan

Keausan 35,796 21,730

Jumlah Berat


54

LAMPIRAN 6. INDEKS KEPIPIHAN AGREGAT (FLAKINESS TEST)

Berat Total Berat Lolos Alur Nilai Flakiness

(A) (C) (C/A)x100%

1 904,5 85,2 9,42

2 961,8 88,2 9,17

9,29

Agregat Pandaan

No.

Sampel

Nilai Flakiness Rata-rata (%)


55

min max hasil

Aspal + 0% Karet 48,00 54,00 52,15

Aspal + 1% Karet 54,00 54,06

Aspal + 2% Karet 54,00 57,96

Aspal + 3% Karet 54,00 58,10

Titik lembek

LAMPIRAN 7. HASIL PENGUJIAN ASPAL PEN. 60/70 DAN

ASPAL MOD.

Aspal Penetrasi 60/70 A B C Rata-rata

Penetrasi pada 25 ̊C (dmm) 62 64 67 64,33

Titik Lembek ( ̊ C) 52,15 52,15

Titik Nyala ( ̊C) 340 340

Duktilitas pada 25 ̊C, (cm) 105 105

Berat Jenis 1,0335 1,033

Aspal Modifikasi Karet 1 %

Penetrasi 42 41 41 41,33

Titik Lembek ( ̊ C) 53,75 54,37 54,06





Penetrasi 42 44 46 44,00

Titik Lembek ( ̊ C) 56,37 59,54 57,955





Penetrasi 43 47 45 45,00

Titik Lembek ( ̊ C) 58,45 57,75 58,1




Min.40

48 ̊ C - 58 ̊ C

≥232 ̊ C

≥100 ̊ C

≥1

Min.40

≥54 ̊ C

≥232 ̊ C

≥100 ̊ C

≥1

Min.40

48 ̊ C - 58 ̊ C

≥232 ̊ C

≥100 ̊ C

≥1

≥100 ̊ C

≥1

Keterangan

Aspal Pen. 60/70

48 ̊ C - 58 ̊ C

≥232 ̊ C

60-70

Aspal Mod.

PengujianHasil Benda Uji


56

min max hasil

Aspal + 0% Karet 232 ̊ C 340,00

Aspal + 1% Karet 232 ̊ C 334,00

Aspal + 2% Karet 232 ̊ C 345,00

Aspal + 3% Karet 232 ̊ C 330,00

Titik Nyala

Kadar Karet 0% 1% 2% 3%

A 62 42 42 43

B 64 41 44 47

C 67 41 46 45

Rata-rata 64,33 41,33 44,00 45,00

Penetrasi

karet berat piknoberat pikno

+ air

berat pikno

+ aspal

berat pikno +

air + aspalmin

berat

jenis

0% 33,001 59,171 39,1076 59,369 >1 1,03351

1% 33,194 60,136 40,362 60,366 >1 1,03315

2% 29,927 54,915 33,775 55,039 >1 1,0333

3% 37,649 61,409 41,2 61,523 >1 1,03317

Pengujian Berat Jenis


57

LAMPIRAN 8. KOMPOSISI BENDA UJI

5,00% 5,50% 6,00% 6,50%

Brt.total 1200 60 66 72 78

1140 1134 1128 1122

Filler 2% 22,80 22,68 22,56 22,44

1117,20 1111,32 1105,44 1099,56

Saringan Combain % Tertahan

1" 100 0

1" 100 0 0,00 0,00 0,00 0,00

3/4" 100,00 0 0,00 0,00 0,00 0,00

1/2' 90,86 9,14 102,11 101,57 101,04 100,50

3/8' 79,30 11,56 129,15 128,47 127,79 127,11

No. 4 56,50 22,80 254,72 253,38 252,04 250,70

No. 8 34,72 21,78 243,33 242,05 240,76 239,48

Dasar 34,72 387,89 385,85 383,81 381,77

100

0,00 0,00 0,00 0,00

3/4" 0,00 0,00 0,00 0,00

1/2' 102,11 101,57 101,04 100,50

3/8' 231,26 230,04 228,83 227,61

No. 4 485,98 483,42 480,87 478,31

No. 8 729,31 725,47 721,63 717,79

Dasar 1117,20 1111,32 1105,44 1099,56

Filler 1140,00 1134,00 1128,00 1122,00

Aspal 60,00 66,00 72,00 78,00

Brt.Agg - Filler - aspal

Jumlah

AC-WC

Aspal

Berat agregat - aspal

BERAT TERTAHAN MASING-MASING SARINGAN

BERAT KOMULATIF


58

stability

udara dlm air ssd reading

1 62,7 63,44 62,96 63,03 5,0% 1188 702,7 1205,1 85 11

2 62,57 62,5 62,85 62,64 5,0% 1179 696,6 1198,2 82 14

3 62,78 63,46 63,27 63,17 5,0% 1190 704,6 1209,1 96 14

4 62,15 62,36 62,1 62,20 5,5% 1178 698 1189,6 95 13

5 61,52 60,65 60,85 61,01 5,5% 1189 708,2 1200,7 86 12

6 61,69 62,47 61,82 61,99 5,5% 1172 693,4 1182,2 83 12

7 65,38 64,55 64,33 64,75 6,0% 1174 683,5 1191,8 49 25

8 61,83 59,91 61,9 61,21 6,0% 1180 704,6 1189 95 16

9 60,8 61,35 61,42 61,19 6,0% 1176 698,7 1185,1 80 17

10 60,86 60,87 60,51 60,75 6,5% 1169 696,5 1174,9 88 10

11 60,56 60,76 60,84 60,72 6,5% 1184 705,1 1190,1 88 14

12 60,01 59,64 60,7 60,12 6,5% 1174 699,9 1179,2 86 13

flowTINGGI CONTOHthickness

(mm)NO. % AC

weight - grams

LAMPIRAN 9. HASIL PENGUJIAN MARSHALL

1. DATA UMUM PERHITUNGAN

TRIAL MIX SERIES AC IV

COMPACTION BLOWS 2 X 75

PEN. GRADE AC 60-70

AVG. BULK SP.GR. TOTAL AGG

(Gsb) 2,7190

TEMPERATUR COMPACTINGS 140OC

AVG. EFF. SP.GR. TOTAL AGG (Gse) 2,77248

ABSORBED AC (Pba) 0,73285

SPECIFIC GRAFITY AC (Gb) 1,033

2. PEMERIKSAAN BENDA UJI DENGAN KADAR KARET 0%

a. Hasil Pemeriksaan Laboratorium


59

udara dlm air ssd

C D E F G H

1187,5 702,7 1197 494,3 2,40 2,56

1178,5 696,6 1188,1 491,5 2,40 2,56

1190 704,6 1199,5 494,9 2,40 2,56

1178 698 1187,7 489,7 2,41 2,54

1189 708,2 1198,8 490,6 2,42 2,54

1171,5 693,4 1181,4 488 2,40 2,54

1174 683,5 1184 500,5 2,35 2,52

1180 704,6 1190,1 485,5 2,43 2,52

1176 698,7 1186,2 487,5 2,41 2,52

1169 696,5 1179,3 482,8 2,42 2,50

1184 705,1 1194,4 489,3 2,42 2,50

1173,5 699,9 1184 484,1 2,42 2,50

bulk densitymax. Theo

density

bulk vol.

Cc.

weight - grams

b. Perhitungan Komponen Campuran

% AC % eff AC

A B B'

1 62,7 63,44 62,96 63,03 5,0 4,99

2 62,57 62,5 62,85 62,64 5,0 4,99

3 62,78 63,46 63,27 63,17 5,0 4,99

4 62,15 62,36 62,1 62,20 5,5 5,49

5 61,52 60,65 60,85 61,01 5,5 5,49

6 61,69 62,47 61,82 61,99 5,5 5,49

7 65,38 64,55 64,33 64,75 6,0 5,99

8 61,83 59,91 61,9 61,21 6,0 5,99

9 60,8 61,35 61,42 61,19 6,0 5,99

10 60,86 60,87 60,51 60,75 6,5 6,49

11 60,56 60,76 60,84 60,72 6,5 6,49

12 60,01 59,64 60,7 60,12 6,5 6,49

no. tinggi contoh

thickness

(mm)

% AC by wt. of mix


60

EFF - AC Aggregat air void (VIM) reading adjust

I J K L M N O

1 11,61 83,94 6,05 17,66 65,73 85 1099,79

2 11,59 83,78 6,23 17,82 65,02 82 1071,29

3 11,62 84,01 5,97 17,59 66,07 96 1237,92

4 12,79 83,61 5,20 17,99 71,10 95 1254,39

5 12,89 84,23 4,49 17,38 74,16 86 1174,57

6 12,76 83,43 5,39 18,16 70,30 83 1101,51

7 13,61 81,09 6,85 20,45 66,53 49 588,75

8 14,10 84,03 3,48 17,58 80,21 95 1289,71

9 13,99 83,40 4,20 18,19 76,92 80 1086,81

10 15,22 83,26 3,11 18,33 83,04 88 1211,07

11 15,21 83,21 3,17 18,38 82,76 88 1212,00

12 15,24 83,36 3,00 18,23 83,57 86 1205,14

stability - kgs

No.

Volume % of total% VMA

%

Voids

P Q R S T

2,79 3,86 28,13695 1,01166667 11

3,56 2,95 28,13695 1,0215 14

3,56 3,41 28,13695 1,00825 14

3,30 3,72 28,13695 1,03241667 13

3,05 3,78 28,13695 1,06789333 12

3,05 3,54 28,13695 1,03766667 12

6,35 0,91 28,13695 0,93946 25

4,06 3,11 28,13695 1,06148667 16

4,32 2,47 28,13695 1,06221 17

2,54 4,67 28,13695 1,07605333 10

3,56 3,34 28,13695 1,07688 14

3,30 3,58 28,13695 1,09568333 13

pembacaan

korelasi

flow

(inches)

flow

(mm)

MQ

kN/mmkalibrasi

c. Hasil Marshall Test


61

stability

A B C udara dlm air ssd reading

1 62 62,07 62,12 62,06 5,0% 1191,7 717,3 1201,1 80 12

2 61,47 61,58 60,68 61,24 5,0% 1181,7 714 1191,2 87 11

3 61,74 61,81 61,51 61,69 5,0% 1182,6 710,4 1192,1 89 15

4 60,21 60,58 60,37 60,39 5,5% 1182,9 709,6 1192,5 86 11

5 61,18 61,04 61,35 61,19 5,5% 1174,2 702 1183,9 78 16

6 60,17 60,03 60,08 60,09 5,5% 1178,5 707,4 1188,3 77 13

7 59,67 59,68 60,29 59,88 6,0% 1175,1 704,2 1185 84 16

8 62,17 61,95 62,27 62,13 6,0% 1175,3 699,7 1185,3 70 27

9 59,43 59,59 60,04 59,69 6,0% 1185,8 712,5 1195,3 80 14

10 59,08 59,26 59,12 59,15 6,5% 1161,5 696,1 1171,1 73 12

11 58,54 58,42 58,43 58,46 6,5% 1164,9 698,5 1174,6 67 14

12 58,4 59,94 58,39 58,91 6,5% 1161,3 694,4 1173,4 73 14

TINGGI CONTOHNO.

thickness

(mm)% AC

weight - gramsflow

3. HASIL PEMERIKSAAN BENDA UJI DENGAN KADAR KARET 1%



% AC % eff AC

A B B'

1 62 62,07 62,12 62,06 5 4,99

2 61,47 61,58 60,68 61,24 5 4,99

3 61,74 61,81 61,51 61,69 5 4,99

4 60,21 60,58 60,37 60,39 5,5 5,49

5 61,18 61,04 61,35 61,19 5,5 5,49

6 60,17 60,03 60,08 60,09 5,5 5,49

7 59,67 59,68 60,29 59,88 6 5,99

8 62,17 61,95 62,27 62,13 6 5,99

9 59,43 59,59 60,04 59,69 6 5,99

10 59,08 59,26 59,12 59,15 6,5 6,49

11 58,54 58,42 58,43 58,46 6,5 6,49

12 58,4 59,94 58,39 58,91 6,5 6,49

% AC by wt. of mix

no. tinggi contoh

thickness

(mm)


62

EFF - AC Aggregat air reading adjust

I J K L M N O

1 11,91 86,06 3,67 15,58 76,41 80 1059,91

2 11,97 86,52 3,16 15,13 79,10 87 1180,03

3 11,87 85,78 3,99 15,86 74,82 89 1191,39

4 13,02 85,14 3,46 16,49 78,99 86 1195,91

5 12,96 84,69 3,98 16,93 76,52 78 1059,62

6 13,03 85,17 3,42 16,45 79,20 77 1079,78

7 14,18 84,49 2,94 17,12 82,83 84 1185,11

8 14,04 83,67 3,88 17,92 78,34 70 925,929

9 14,25 84,91 2,46 16,71 85,27 80 1134,86

10 15,37 84,09 2,15 17,52 87,73 73 1051,12

11 15,38 84,14 2,09 17,47 88,04 67 983,624

12 15,24 83,37 2,98 18,22 83,63 73 1058,22

stability - kgsVolume % of totalNO

.

%

Voids

%

VMA


udara dlm air ssd

C D E F G H

1191,7 717,3 1201,1 483,8 2,46 2,56

1181,7 714 1191,2 477,2 2,48 2,56

1182,6 710,4 1192,1 481,7 2,46 2,56

1182,9 709,6 1192,5 482,9 2,45 2,54

1174,2 702 1183,9 481,9 2,44 2,54

1178,5 707,4 1188,3 480,9 2,45 2,54

1175,1 704,2 1185 480,8 2,44 2,52

1175,3 699,7 1185,3 485,6 2,42 2,52

1185,8 712,5 1195,3 482,8 2,46 2,52

1161,5 696,1 1171,1 475 2,45 2,50

1164,9 698,5 1174,6 476,1 2,45 2,50

1161,3 694,4 1173,4 479 2,42 2,50

bulk vol.

Cc.bulk density

max. Theo

density

weight - grams


63

P Q R S T

3,05 3,41 28,137 1,03591667 12

2,79 4,14 28,137 1,06052083 11

3,81 3,07 28,137 1,04666667 15

2,79 4,20 28,137 1,08729167 11

4,06 2,56 28,137 1,0621875 16

3,30 3,21 28,137 1,09645833 13

4,06 2,86 28,137 1,103125 16

6,86 1,32 28,137 1,03425 27

3,56 3,13 28,137 1,10916667 14

3,05 3,38 28,137 1,12583333 12

3,56 2,71 28,137 1,14788889 14

3,56 2,92 28,137 1,1334375 14

flow

(inches)

pembacaan

korelasi

kalibra

si

MQ

kN/mm

flow

(mm)

stability


1 59,73 60,43 59,7 59,95 5 1177,5 707,9 1189,8 94 11

2 60,24 60,19 60,2 60,21 5 1163,2 699,2 1175,3 95 12

3 62,45 62,28 61,87 62,20 5 1193,7 719,8 1204 92 13

4 59,64 59,18 60,03 59,62 5,5 1168 705,1 1176 95 16

5 60,78 60,91 61,27 60,99 5,5 1171,1 707,7 1187,3 80 11

6 61,11 61,11 61,27 61,16 5,5 1179 707 1189,6 87 12

7 59,38 59,44 59,86 59,56 6 1171,4 705,4 1178,4 85 19

8 55,98 56 56,61 56,20 6 1054,6 625,5 1065,8 55 15

9 60,36 61,29 60,46 60,70 6 1188,5 715,3 1194,5 92 17

10 61,44 61,4 62,22 61,69 6,5 1211 727 1215,5 91 15

11 58,91 58,81 59,47 59,06 6,5 1177,9 707,1 1183,1 78 20

12 59,36 59,57 59,36 59,43 6,5 1158,6 695,3 1165,3 85 13

NO. flowweight - gramsTINGGI CONTOH thickness

(mm)% AC




64


% AC % eff AC

A B B'

1 59,73 60,43 59,7 59,95 5 4,99

2 60,24 60,19 60,2 60,21 5 4,99

3 62,45 62,28 61,87 62,20 5 4,99

4 59,64 59,18 60,03 59,62 5,5 5,49

5 60,78 60,91 61,27 60,99 5,5 5,49

6 61,11 61,11 61,27 61,16 5,5 5,49

7 59,38 59,44 59,86 59,56 6 5,99

8 55,98 56 56,61 56,20 6 5,99

9 60,36 61,29 60,46 60,70 6 5,99

10 61,44 61,4 62,22 61,69 6,5 6,49

11 58,91 58,81 59,47 59,06 6,5 6,49

12 59,36 59,57 59,36 59,43 6,5 6,49

% AC by wt. of mix

no. tinggi contoh

thickness

(mm)

udara dlm air ssd

C D E F G H

1177,5 707,9 1189,8 481,9 2,44 2,56

1163,2 699,2 1175,3 476,1 2,44 2,56

1193,7 719,8 1204 484,2 2,47 2,56

1168 705,1 1176 470,9 2,48 2,54

1171,1 707,7 1187,3 479,6 2,44 2,54

1179 707 1189,6 482,6 2,44 2,54

1171,4 705,4 1178,4 473 2,48 2,52

1054,6 625,5 1065,8 440,3 2,40 2,52

1188,5 715,3 1194,5 479,2 2,48 2,52

1211 727 1215,5 488,5 2,48 2,50

1177,9 707,1 1183,1 476 2,47 2,50

1158,6 695,3 1165,3 470 2,47 2,50

weight - grams bulk vol.

Cc.bulk density

max. Theo

density


65

P Q R S T

2,79 4,644 28,13695 1,1008333 11

3,05 4,271 28,13695 1,0928125 12

3,30 3,607 28,13695 1,0325 13

4,06 3,257 28,13695 1,1113542 16

2,79 3,836 28,13695 1,0685417 11

3,05 3,805 28,13695 1,0630208 12

4,83 2,458 28,13695 1,113125 19

3,81 2,222 28,13695 1,227625 15

4,32 2,878 28,13695 1,0773958 17

3,81 3,135 28,13695 1,0466667 15

5,08 2,173 28,13695 1,1286458 20

3,30 3,606 28,13695 1,1171875 13

flow

(mm)kalibrasi

MQ

kN/mm

pembacaan

korelasi

flow

(inches)


EFF - AC Aggregat air void (VIM) reading adjust

I J K L M N O

1 11,81 85,37 4,45 16,26 72,64 94 1323,44

2 11,81 85,36 4,46 16,27 72,60 95 1327,77

3 11,92 86,14 3,59 15,51 76,83 92 1214,88

4 13,19 86,21 2,25 15,44 85,42 95 1350,30

5 12,98 84,87 3,77 16,75 77,50 80 1093,29

6 12,99 84,91 3,72 16,71 77,73 87 1182,81

7 14,37 85,62 1,65 16,02 89,70 85 1210,09

8 13,90 82,81 4,88 18,77 74,01 55 863,54

9 14,39 85,74 1,50 15,89 90,53 92 1267,70

10 15,58 85,25 0,80 16,38 95,13 91 1218,16

11 15,55 85,10 0,98 16,53 94,10 78 1125,92

12 15,49 84,77 1,35 16,85 91,96 85 1214,51

NO

.

Volume % of total

% VMA

%

Voids

filled

stability - kgs


66

stability


1 61,21 60,5 61,9 61,20 5 1183,8 713,8 1192,5 98 13

2 61,71 61,79 61,75 61,75 5 1196,5 718,1 1205,6 100 14

3 61,52 62,2 62,36 62,03 5 1192,8 715,1 1202,8 95 15

4 60,31 60,66 60,84 60,60 5,5 1185,2 715,4 1195 89 15

5 60,71 59,64 60,3 60,22 5,5 1186,7 716,8 1196,2 85 12

6 60,48 60,7 61,1 60,76 5,5 1177,7 712 1187 90 14

7 60,98 60,69 61,11 60,93 6 1187,4 716,6 1196,5 80 13

8 60,49 61,8 58,82 60,37 6 1182,8 713,9 1191,7 81 15

9 61,5 61,48 60,99 61,32 6 1189 715,3 1199 97 14

10 60,9 59,44 61,26 60,53 6,5 1191 718,2 1199,5 70 15

11 58,76 59,22 60,16 59,38 6,5 1194,2 722 1203,2 98 14

12 61,18 60,35 59,75 60,43 6,5 1192,1 720,6 1200,8 78 14

thickness

(mm)NO.

TINGGI CONTOH% AC

weight - gramsflow




% AC % eff AC

A B B'

1 61,21 60,5 61,9 61,20 5 4,99

2 61,71 61,79 61,75 61,75 5 4,99

3 61,52 62,2 62,36 62,03 5 4,99

4 60,31 60,66 60,84 60,60 5,5 5,49

5 60,71 59,64 60,3 60,22 5,5 5,49

6 60,48 60,7 61,1 60,76 5,5 5,49

7 60,98 60,69 61,11 60,93 6 5,99

8 60,49 61,8 58,82 60,37 6 5,99

9 61,5 61,48 60,99 61,32 6 5,99

10 60,9 59,44 61,26 60,53 6,5 6,49

11 58,76 59,22 60,16 59,38 6,5 6,49

12 61,18 60,35 59,75 60,43 6,5 6,49

% AC by wt. of mix

no. tinggi contoh

thickness

(mm)


67

EFF - AC Aggregatair

void reading adjust

I J K L M N O

1 11,95 86,40 3,29 15,25 78,40 98 1330,8

2 11,86 85,75 4,02 15,88 74,69 100 1336,11

3 11,82 85,45 4,36 16,18 73,07 95 1259,76

4 13,14 85,89 2,61 15,75 83,43 89 1229,92

5 13,16 86,03 2,45 15,61 84,32 85 1187,78

6 13,18 86,17 2,29 15,47 85,20 90 1238,11

7 14,35 85,54 1,74 16,09 89,19 80 1095,21

8 14,36 85,58 1,69 16,05 89,47 81 1126,92

9 14,26 84,98 2,38 16,64 85,70 97 1312,56

10 15,55 85,09 0,98 16,53 94,09 70 969,313

11 15,60 85,34 0,69 16,29 95,76 98 1402,21

12 15,60 85,37 0,66 16,26 95,95 78 1083,42

NO

.

Volume % of total

% VMA

%

Voids

filled

stability - kgs


udara dlm air ssd

C D E F G H

1183,8 713,8 1192,5 478,7 2,47 2,56

1196,5 718,1 1205,6 487,5 2,45 2,56

1192,8 715,1 1202,8 487,7 2,45 2,56

1185,2 715,4 1195 479,6 2,47 2,54

1186,7 716,8 1196,2 479,4 2,48 2,54

1177,7 712 1187 475 2,48 2,54

1187,4 716,6 1196,5 479,9 2,47 2,52

1182,8 713,9 1191,7 477,8 2,48 2,52

1189 715,3 1199 483,7 2,46 2,52

1191 718,2 1199,5 481,3 2,47 2,50

1194,2 722 1203,2 481,2 2,48 2,50

1192,1 720,6 1200,8 480,2 2,48 2,50

weight - grams bulk vol.

Cc.bulk density

max. Theo

density


68

Q R S T

3,95 28,13695 1,0617708 13

3,68 28,13695 1,0446875 14

3,24 28,13695 1,0368333 15

3,16 28,13695 1,0805208 15

3,82 28,13695 1,0926042 12

3,41 28,13695 1,075625 14

3,25 28,13695 1,0704167 13

2,90 28,13695 1,0878125 15

3,62 28,13695 1,0580208 14

2,49 28,13695 1,0827083 15

3,87 28,13695 1,11875 14

2,99 28,13695 1,0860417 14

MQ

kN/mmkalibrasi

pembacaan

korelasi

flow

(inches)