THE AUSTRALIAN
WELDING GUIDE
welding.com.au
The Ultimate Welding Reference Guide 2012
2 welding.com.au 1300 300 884
FOR OVER 50 YEARSWith a proven history of over 50 years in the Australian market, WIA has built a reputation for delivering high quality filler metal products for the industrial user. Known for their quality, consistency and performance, WIA filler metal products are preferred by operators across a wide range of industry sectors.
WIA offers an extensive range of consumables for various welding processes and applications. Choose from mild steel and low hydrogen electrodes to specialised flux cored wires and hardfacing products.
Backed by a team of technical professionals who understand our customers’ needs, we are committed to delivering welding products that offer peak performance in operability, mechanical properties and productivity, and backed by the delivery of technical expertise and support.
WIA is ISO 9001 certified. It’s your guarantee of the highest levels of quality, satisfaction and efficiency when you choose WIA products.
1
WELDING INDUSTRIES OF AUSTRALIA AN ITW COMPANY
USING THIS GUIDEPRODUCT SECTIONThe front section of this guide contains comprehensive product information on the range of WIA consumables. Access the latest information on WIA filler metal products, including technical data sheets at welding.com.au.
TECHNICAL REFERENCE SECTIONDesigned as a portable reference tool for welding engineers, design and costing personnel, workshop supervisors, welding specialists and students, the Technical Reference Section incorporates the information welding professionals need to have on hand.
VIEWING THIS GUIDE AS AN INTERACTIVE PDFDepending on the device or computer you are viewing this PDF in, all CONTENTS pages contain ‘clickable’ links to help you navigate easily through the document.
DISCLAIMER - Welding Industries of Australia (WIA) is a supplier of welding products, and does not operate as a provider of consultancy or other technical services or advice related to welding. The information provided in this document is offered as a guide only. Every effort has been made to ensure the information contained in this booklet was correct at the time of printing. WIA does not accept responsibility for errors or information which is found to be misleading. Prior to using WIA products, it is the purchasers’ responsibility to ensure the products selected are suitable for the application.
2
3
INTRODUCTION ELECTRODES General Purpose Electrodes - Mild Steel Hydrogen Controlled Electrodes Iron Powder Electrodes Cellulose Electrodes Stainless Steel Electrodes Cast Iron Electrodes Gouging and Cutting Electrodes WIRES Solid MIG Wires – Mild Steel Solid MIG Wires – Low Alloy Steel Solid MIG Wires – Aluminium Metal Cored Gas Shielded Wires Flux Cored Gas Shielded Wires Flux Cored Self Shielded Wires
HARDFACING PRODUCTS Hardfacing Electrodes Hardfacing Solid MIG Wires Hardfacing Self Shielded Flux Cored Wires Hardfacing Gas Shielded Flux Cored Wires
TECHNICAL INFORMATION
5
1
CONTENTS
33
65
86
5
GENERAL PURPOSE ELECTRODES - MILD STEEL Austarc 12P ................................................................ 6-7Austarc 13S ................................................................ 8-9
HyDROGEN CONTROLLED ELECTRODESAustarc 16TC ...........................................................10-11Austarc 18TC .......................................................... 12-13Austarc 77 ............................................................... 14-15
IRON POWDER ELECTRODESAustarc 24 ............................................................... 16-17
CELLULOSE ELECTRODESAustarc 11 ............................................................... 18-19
STAINLESS STEEL ELECTRODESStaincord 309Mo-16 ................................................ 20-21Staincord 316L-16 ................................................... 22-23Unicord 312 ............................................................ 24-25
CAST IRON ELECTRODESSupercast Ni ........................................................... 26-27 Suercast Ni/Fe ........................................................ 28-29
GOUGING AND CUTTING ELECTRODESAustarc C&G ........................................................... 30-31
ELECTRODESCONTENTS
CONTENTS
6CONTENTS
AUSTARC 12P SUMMARy
• General Purpose Rutile Type Electrode• Versatile/All Positional Capabilities Including Vertical Down• Smooth Performance on Low OCV AC Welding Machines
IDENTIFICATIONCoating - Brown Tip - Red Imprint - WIA 4313A
CLASSIFICATION
• AS/NZS 4855-B - E43 13 A • AWS A5.1: E6013
DESCRIPTION AND APPLICATIONAustarc 12P is a smooth running, rutile type electrode for all positional welding of mild steel. It is characterised by a moderately forceful and extremely stable arc. Superb arc starting and restriking on low voltage AC welding machines.
A stiff fast freezing slag for all positional (especially vertical down) fillet welding capabilities. Typical applications include, the all positional welding of galvanised gates/fences, steel furniture, trailers and wrought iron.
OPERATIONAL DATA
ELECTRODE SIZE (mm)
ELECTRODE LENGTH (mm)
WELDING CURRENT RANGE *(A)
ARC VOLTAGE RANGE **(V)
2.0 300 40-60 192.5 300 60-85 203.2 380 90-130 214.0 380 130-180 225.0 450 180-230 23
*Recommended for DC +/- or AC (minimum 45 OCV) operation. **Voltage is determined by arc current and electrode arc length. Arc voltage shown is typical and is only to be used as a guide.
7CONTENTS
SHIPPING APPROVALSLR 2Ym ABS 2 DNV 2
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si Fe0.07 0.5 0.3 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Yield Stress 450 MPaTensile Strength 500 MPaElongation 26%CVN Impact Values 70J @ 0°C
In as welded condition.
PACKAGING DATA
ELECTRODE SIZE (mm)
PACKAGING (KG)
APPROX NO. OF
RODS PER KG
PART NUMBER
Packet Carton2.0 2.5 12.5 103 12P202.5 2.5 12.5 67 12P253.2 5.0 15 31 12P324.0 5.0 15 20 12P405.0 5.0 15 11 12P50
ELECTRODES - GENERAL PURPOSE ELECTRODES - MILD STEEL1G
2G 3G4G 1F
2F4F
3G
8CONTENTS
AUSTARC 13S SUMMARy
• General Purpose/Rutile Type Electrode• Versatile/All Positional (especially vertical up) Capabilities• Ideal for Down Hand Fillet Welding of Mild Steel• Smooth Performance on Low OCV AC Welding Machines
IDENTIFICATIONCoating - Blue/White Stripe Tip - Plain Imprint - WIA 4313A
CLASSIFICATION
• AS/NZS 4855-B - E43 13 A• AWS A5.1: E6013
DESCRIPTION AND APPLICATION
Austarc 13S is the popular “blue and white striped” general purpose electrode for smooth mitre fillet welding applications. 13S has a soft and stable arc and produces flat, uniform fillet welds with ease and a self peeling slag action.
Austarc 13S is formulated primarily for fillet welding in all down hand positions. It is ideal for the general purpose and structural welding of sheet and plate steels (galvanised or otherwise) and tubular components, including trailers, duct work, hoppers and storage tanks, etc.
OPERATIONAL DATA
ELECTRODE SIZE (mm)
ELECTRODE LENGTH (mm)
WELDING CURRENT RANGE *(A)
ARC VOLTAGE RANGE **(V)
2.0 300 40-60 192.5 300 60-85 203.2 380 100-130 214.0 380 140-180 225.0 450 180-230 236.0 450 230-290 24
*Recommended for DC +/- or AC (minimum 45 OCV) operation. **Voltage is determined by arc current and electrode arc length. Arc voltage shown is typical and is only to be used as a guide.
9CONTENTS
SHIPPING APPROVALSLR 2m ABS 2 DNV 2
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si Fe0.07 0.55 0.45 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Yield Stress 450 MPaTensile Strength 520 MPaElongation 26%CVN Impact Values 60J @ 0°C
In as welded condition.
PACKAGING DATA
ELECTRODE SIZE (mm)
PACKAGING (KG)
APPROX NO. OF
RODS PER KG
PART NUMBER
Packet Carton2.0 2.5 12.5 99 13S202.5 2.5 12.5 63 13S253.2 5.0 15 29 13S324.0 5.0 15 10 13S405.0 5.0 15 6 13S506.0 5.0 15 6 13S60
ELECTRODES - GENERAL PURPOSE ELECTRODES - MILD STEEL1G
2G 3G4G 1F
2F4F
10CONTENTS
AUSTARC 16TC SUMMARy• Basic/Twin Coated (TC) Manual Arc Electrode• Low Hydrogen, “H10” Status• Versatile/All Positional (Especially Vertical Up) Capabilities• Reliable, Low Temperature Impact Toughness• Easy to Strike and Re-Strike• Smooth Performance on Low OCV AC Welding Machines IDENTIFICATIONCoating - Light Grey Tip - Bronze Imprint - WIA 4916A CLASSIFICATION
• AS/NZS 4855-B - E49 16-A U H10• AWS A5.1: E7116-1 H8 DESCRIPTION AND APPLICATION
Austarc 16TC is a smooth running, basic low hydrogen electrode, developed for all positional (except vertical down) welding, using AC or DC power sources. The electrode gives exceptional arc stability and weldability for its class and produces high quality weld deposits with reliable notch toughness to -40°C. Austarc 16TC is manufactured using a unique twin coating extrusion process, which produces electrodes with two concentric flux coatings. Arc stabilising elements are concentrated in the inner coating of the electrode for significantly improved arc stability on AC welding machines.Other features of 16TC include, a smooth rippled weld profile with excellent edge wetting and a fluid, easily removed glassy slag. Austarc 16TC deposits X-ray quality weld metal with typical diffusible hydrogen levels of 5-8 mls of hydrogen per 100 gms of deposited weld metal, for “as manufactured” product, thus satisfying the “H10” low hydrogen category of AS/NZS 4855 and “H8” of AWS A5.1. OPERATIONAL DATA
ELECTRODE SIZE (mm)
ELECTRODE LENGTH (mm)
WELDING CURRENT RANGE *(A)
2.5 300 60-903.2 380 90-1354.0 380 140-1905.0 450 190-2406.0 450 250-310
*Please note, 2.5 and 3.2 Austarc 16TC are recommended for DC+ or AC (minimum 45 OCV) operation, whereas 4.0, 5.0 and 6.0mm sizes require a minimum of 55 OCV for stable AC operation.
11CONTENTS
SHIPPING APPROVALSLRS 4Ym H10 ABS 3 H10 DNV 3Y H10 TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si P S Fe0.06 1.2 0.4 0.015 0.010 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Yield Stress 460 MPaTensile Strength 560 MPaElongation 28%CVN Impact Values 130J @ -20°C 110J @ -40°C
PACKAGING DATA
ELECTRODE SIZE (mm)
PACKAGING (KG)
APPROX NO. OF RODS
PER KG
PART NUMBER
Packet Carton2.5 2.5 12.5 61 16TC253.2 5.0 15 29 16TC324.0 5.0 15 19 16TC405.0 5.0 15 10 16TC506.0 5.0 15 7 16TC60
MATERIALS TO BE WELDED
CODE TyPE
Structural Steel
AS 1163 C250, C350, C450AS 1397 G250, G300, G350, G450AS 1450 C/H200, C/H250, C/H350, C/H450,
AS/NZS 3679.1 250, 300, 350, 400AS/NZS 3678.1 AS/NZS 3679.2
200, 250, 300, 350, 400, 450, A1006, XK1016, WR350
Pressure Equipment
SteelAS 1548 7-430, 7-460, 5-590, 7-490
Fine Grain Steel AS/NZS 1594
HAI, HA3, HA4N, HA200, HA250, HA300, HA1006, HA1010, HA1016,
HA350, HA400Cast Steel AS2074 C2, C3, C7A-1, C1, C4-1, C4-2, C7A-2
Pipe Material API 5LX X42, X46, X52, X60
ELECTRODES - HYDROGEN CONTROLLED ELECTRODES1G
2G 3G4G 1F
2F4F
12CONTENTS
AUSTARC 18TC SUMMARy• Basic Twin-Coated (TC) Iron Powder Electrode• Very Low Hydrogen H5 Status• Suitable for all Positional Welding Except Vertical Down• Excellent Low Temperature Fracture Toughness• Easy to Strike and Re-Strike• Smooth Performance on Low OCV AC Welding Machines
IDENTIFICATIONCoating - Light Grey Tip - Blue Imprint - WIA 4918-1A
CLASSIFICATION
• AS/NZS 4855-B - E49 18-A U H5• AWS A5. 1: E7018-1
DESCRIPTION AND APPLICATION
Austarc 18TC is a basic iron powder electrode used primarily on C-Mn and low alloy structural steels. The unique twin-coat design for 18 type low hydrogen electrode offers excellent AC arc stability and superb DC+ arc transfer, excellent re-strike, reduced spatter level and extraordinary ease of use for out-of-position welding.
Typical applications include oil and gas, pipe welding, structural steel construction, off-shore where Ni-alloying is prohibited, mining equipment, heavy girders and earth moving plant repair and maintenance.
OPERATIONAL DATA
ELECTRODE SIZE (mm)
ELECTRODE LENGTH (mm)
WELDING CURRENT RANGE *(A)
2.5 300 60-903.2 380 90-1354.0 380 140-190
*Please note, the recommended welding polarity for Austarc 18TC is DC + or AC (Min. 50 OCV).
SHIPPING APPROVALSLRS/Pending DNV/Pending
13CONTENTS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si P S Fe0.06 1.55 0.54 0.010 0.02 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Yield Stress 530 MPaTensile Strength 602 MPaElongation 24%CVN Impact Values 87J @ -50°C
PACKAGING DATA
ELECTRODE SIZE (mm)
PACKAGING (KG)
APPROX NO. OF RODS
PER KG
PART NUMBER
Packet Carton2.5 2.5 12.5 45 18TC253.2 5.0 15 26 18TC324.0 5.0 15 17 18TC40
MATERIALS TO BE WELDED
CODE TyPE
Structural Steel
AS 1163 C250, C350, C450AS 1397 G250, G300, G350, G450AS 1450 C/H200, C/H250, C/H350, C450AS 1450 250, 300, 350, 400
C/H200, C/H250,
200, 250, 300, 350, 400, 450, A1006, XK1016, WR350
AS/NZS 3679.1 250, 300, 350, 400
AS/NZS 3678.1 AS/NZS 3679.2
200, 250, 300, 350, 400, 450, A1006, XK1016, WR350
Pressure Equipment
SteelAS 1548 7-430, 7-460, 5-590, 7-490
Fine Grain Steel AS/NZS 1594
HA1, HA3, HA4N, HA200, HA250, HA300, HA1006, HA1010, HA1016,
HA350, HA400
Cast Steel AS2074 C2, C3, C7A-1, C1, C4-1, C4-2, C7A-2
Pipe Material API 5LX X42, X46, X52, X60
ELECTRODES - HYDROGEN CONTROLLED ELECTRODES1G
2G 3G4G 1F
2F4F
14CONTENTS
SUMMARy
• Basic Coated Iron Powder Electrode• Low Hydrogen Status• Suitable for All Positional Welding Except Vertical Down• Excellent Low Temperature Fracture Toughness
IDENTIFICATIONCoating - Light Grey Tip - Black Imprint - WIA 4918-1A
CLASSIFICATION
• AS/NZS 4855-B - E49 18-1 U H5• AWS A5.1: E7018-1
DESCRIPTION AND APPLICATION
The Austarc is a smooth running basic type of low hydrogen iron powder electrode used for all positional welding except vertical down. The arc is very quiet with little spatter and the welds are exceptionally smooth with excellent wash in at the toes of the weld, thus giving minimum undercut. This electrode is used where the highest restrained work pieces are fabricated for mining equipment, pressure vessels, heavy girders, earth moving plant, repair and maintenance etc.
For the highest weld quality with low hydrogen levels, Austarc 77 electrodes should be baked at 400˚C for one hour to obtain <5mL/100g weld metal. After baking, the electrodes should be used from a hot box set at 100 -150 ̊C.
OPERATIONAL DATA
ELECTRODE SIZE (mm)
ELECTRODE LENGTH (mm)
WELDING CURRENT RANGE *(A)
ARC VOLTAGE RANGE **(V)
2.5 305 60-105 203.2 380 90-145 224.0 380 140-200 245.0 455 180-300 26
*Recommended for DC +/- or AC (minimum 70 OCV) operation. **Voltage is determined by arc current and electrode arc length. Arc voltage shown is typical and is only to be used as a guide.
AUSTARC 77
15CONTENTS
SHIPPING APPROVALSLR 4Ym H5 ABS 3Y H5
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C S Mn P Si Fe0.05 0.011 1.28 0.022 0.30 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Yield Stress 455 MPaTensile Strength 534 MPaElongation 30%CVN Impact Values 123J @ -50°C
In as welded condition.
PACKAGING DATA
ELECTRODE SIZE (mm)
PACKAGING (KG)
APPROX NO. OF
RODS PER KG
PART NUMBER
Packet Carton2.5 2.2 11 45 77253.2 5.0 15 26 77324.0 5.0 15 17 77405.0 5.0 15 9 7750
ELECTRODES - HYDROGEN CONTROLLED ELECTRODES1G
2G 3G4G 1F
2F4F
16CONTENTS
SUMMARy
• High Iron Powder, Rutile Type Electrode• High Deposition Rates and Efficiencies• Suitable for Fast Downhand Fillet and Butt Welding
IDENTIFICATIONCoating - Brown Tip - Yellow Imprint - WIA 4924A
CLASSIFICATION
• AS/NZS 4855-B - E49 24 A• AWS A5.1: E7024
DESCRIPTION AND APPLICATION
Austarc 24 is a high iron powder, rutile type electrode designed for the fast down hand welding of mild steel using AC or DC power sources. Features include high deposition rates/efficiencies and flat to slightly concave fillet welds with excellent “edge wash” and slag detachability. With its smooth running, positive re strike and high current carrying capacity, Austarc 24 is the ideal fillet welding electrode for down hand positions aimed at higher productivity.
Austarc 24 is suited to long, heavy fillet and butt welding applications using a touch welding or `short arc’ technique. Such applications include the production welding of tanks, structural members/frames and truck and tractor bodies etc.
OPERATIONAL DATA
ELECTRODE SIZE (mm)
ELECTRODE LENGTH (mm)
WELDING CURRENT RANGE *(A)
ARC VOLTAGE RANGE **(V)
3.2 380 120-170 244.0 450 200-240 255.0 450 270-320 26
*Recommended for DC +/- or AC (minimum 55 OCV) operation. **Voltage is determined by arc current and electrode arc length. Arc voltage shown is typical and is only to be used as a guide.
AUSTARC 24
17CONTENTS
SHIPPING APPROVALSLR 2Ym ABS 2 DNV 2
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si Fe0.06 0.7 0.4 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Yield Stress 455 MPaTensile Strength 510 MPaElongation 27%CVN Impact Values 60J @ 0°C
In as welded condition
PACKAGING DATA
ELECTRODE SIZE (mm)
PACKAGING (KG)
APPROX NO. OF
RODS PER KG
PART NUMBER
Packet Carton3.2 5.0 15 18 24324.0 5.0 15 12 24405.0 5.0 15 6 2450
ELECTRODES - IRON POWDER ELECTRODES1G
1F2F
18CONTENTS
SUMMARy
• High Cellulose Coating• All Positional/High Penetration• Ideal for Site Welding
IDENTIFICATIONCoating - White Tip - Brown Imprint - WIA 4311A
CLASSIFICATION
• AS/NZS 4855-B - E4311A• AWS A5.1: E6011
DESCRIPTION AND APPLICATION Austarc 11 is a high cellulose electrode developed for all positional welding on both AC and DC power supplies.
Features include: Forceful, deep penetrating arc with fast freezing slag. Particularly suited for vertical and incline pipe welding where complete root penetration is required. The thin brittle slag is easily removed.
Austarc 11 is recommended for specific applications including pipeline welding and storage tank construction where either the “Stove Pipe” or “Flick” techniques can be used to obtain full root penetration in critical structural joints.
OPERATIONAL DATA
ELECTRODE SIZE (mm)
ELECTRODE LENGTH (mm)
WELDING CURRENT RANGE *(A)
ARC VOLTAGE RANGE **(V)
2.5 300 60-95 203.2 380 90-125 214.0 380 115-175 225.0 450 160-220 23
*Recommended for DC +/- or AC (minimum 70 OCV) operation. **Voltage is determined by arc current and electrode arc length. Arc voltage shown is typical and is only to be used as a guide.
AUSTARC 11
19CONTENTS
SHIPPING APPROVALSLR 3M ABS 3
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si Fe0.13 0.5 0.1 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Yield Stress 416 MPaTensile Strength 510 MPaElongation 32%CVN Impact Values 70J @ -30°C
In as welded condition
PACKAGING DATA
ELECTRODE SIZE (mm)
PACKAGING (KG)
APPROX NO. OF
RODS PER KG
PART NUMBER
Packet Carton2.5 2.5 12.5 66 11253.2 5.0 15 33 11324.0 5.0 15 21 11405.0 5.0 15 14 1150
ELECTRODES - CELLULOSE ELECTRODES1G
2G 3G4G 1F
2F4F
3G
20CONTENTS
SUMMARy
• All Positional, Rutile Type Stainless Steel Electrode• Moisture Resistant Flux Coating/”Extra” Low Carbon Deposit• Suitable for the Dissimilar Welding of Stainless Steel to Mild/Low Alloy Steels.
IDENTIFICATIONCoating - Grey Tip - Black Imprint - WIA 309MO-16
CLASSIFICATION
• AS/NZS 4854-B - E309LMo-16• AWS A5.4: E309MoL-16
DESCRIPTION AND APPLICATION Staincord 309Mo-16 is an extra low carbon, rutile type electrode exhibiting superior all positional (except vertical down performance with an improved moisture resistant coating for weld metal of high radiographic integrity. The smooth arc action of Staincord 309Mo-16, together with low spatter and excellent slag control/ detachability, promotes exceptional weld appearance and profile.
Staincord 309Mo-16 is a Molybdenum bearing, highly alloyed 23Cr/12Ni/2.5Mo stainless steel electrode for welding matching 309 and 309Mo base metals. Major applications of Staincord 309 Mo-16 also involve the welding of a wide range of 300 and 400 series stainless steels to mild/low alloy steels. 309M is also suitable for general welding applications with alloyed and non-alloyed dissimilar ferrous metal combinations.
OPERATIONAL DATA
ELECTRODE SIZE (mm)
ELECTRODE LENGTH (mm)
WELDING CURRENT RANGE *(A)
ARC VOLTAGE RANGE **(V)
2.5 300 50-75 223.2 350 75-110 264.0 350 110-150 28
*Recommended for DC +/- or AC (minimum 70 OCV) operation. **Voltage is determined by arc current and electrode arc length. Arc voltage shown is typical and is only to be used as a guide.
STAINCORD 309Mo-16
21CONTENTS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si Cr Ni Mo Fe0.025 0.8 0.7 23.5 13.0 2.4 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Yield Stress 400 MPaTensile Strength 670 MPaElongation 38%
In as welded condition.
PACKAGING DATA
ELECTRODE SIZE (mm)
PACKAGING (KG)
APPROX NO. OF RODS
PER KG
PART NUMBER
Packet Carton2.5 2.5 12.5 86 SC309MO253.2 2.5 12.5 55 SC309MO32
ELECTRODES - STAINLESS STEEL ELECTRODES1G
2G 3G4G 1F
2F4F
3G
22CONTENTS
SUMMARy
• All Positional, Rutile Type Stainless Steel Electrode• Moisture Resistant “Colour Coated” Flux Coating• Extra Low Carbon Weld Deposit• For the Critical Welding of Matching Type 316 and 316L Steels
IDENTIFICATIONCoating - Pink Tip - Green Imprint - WIA 316L-16
CLASSIFICATION
• AS/NZS 4854-B - ES316L-16• AWS A5.4: E316L-16
DESCRIPTION AND APPLICATION
New generation Staincord 316L-16 is an extra low carbon, rutile type electrode exhibiting superior all positional (except vertical down) performance with an improved moisture resistant “Pink” flux coating for weld metal of high radiographic integrity. The smooth arc action of Staincord 316L-16, together with low spatter and excellent slag control/detachability, promotes exceptional weld appearance and profile. Other features include high arc stability and easy restriking on low voltage AC welding machines.Staincord 316L-16 deposits Molybdenum bearing, 19Cr/12Ni/2.5Mo filler metal to meet the requirements for welding type 316 and 316L stainless steels in critical applications. Staincord 316L-16 is also recommended for the general purpose welding of common 300 series stainless steels, such as 301, 302, 304 and 304L. It is also suitable for the general welding of ferritic stainless steel alloys, such as 409, 444 and 3Cr12.
STAINCORD 316L-16STAINCORD 316L-16
23CONTENTS
OPERATIONAL DATA
ELECTRODE SIZE (mm)
ELECTRODE LENGTH (mm)
WELDING CURRENT RANGE *(A)
ARC VOLTAGE RANGE **(V)
2.0 300 30-50 202.5 300 50-75 213.2 350 75-110 26
*Recommended for DC +/- or AC (minimum 45 OCV) operation. **Voltage is determined by arc current and electrode arc length. Arc voltage shown is typical and is only to be used as a guide.
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si Cr Ni Mo Fe0.025 0.7 0.7 18.5 12.0 2.4 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Yield Stress 380 MPaTensile Strength 600 MPaElongation 40%
In as welded condition.
PACKAGING DATA
ELECTRODE SIZE (mm)
PACKAGING (KG)
APPROX NO. OF
RODS PER KG
PART NUMBER
Packet Carton2.0 2.5 12.5 86 SC316202.5 2.5 12.5 55 SC316253.2 2.5 12.5 27 SC31632
ELECTRODES - STAINLESS STEEL ELECTRODES1G
2G 3G4G 1F
2F4F
24CONTENTS
SUMMARy
• Universal AC/DC Maintenance Electrode for Welding Ferrous Metals• Ideal for Joining Dissimilar Steel Components• Suitable as a Buffer Layer Prior to Hard Surfacing• Stable Performance on Low OCV Welders
IDENTIFICATIONCoating - Grey Tip - Red Imprint - Unicord 312
CLASSIFICATION
• AS/NZS 4854-B - ES312-16• AWS A5.4: E312-16
DESCRIPTION AND APPLICATION Unicord 312 is a basic, rutile type electrode depositing a 29%Cr/9%Ni stainless steel weld metal for the high strength welding of a wide range of alloy steels and dissimilar ferrous metals. The high ferrite, austenitic stainless steel deposit has excellent resistance to hot cracking, even under dilution by high carbon, alloy and tool steels. Unicord 312 is a universal maintenance electrode combining high strength, toughness, wear and corrosion resistance with compatibility to most ferrous metals.
Unicord 312 is suitable for many repair and maintenance applications on steels of unknown composition. It is an ideal electrode for welding medium to high carbon steels, low alloy steels and dissimilar ferrous metal combinations. Unicord 312 is also suitable as a buffer or intermediate layer prior to the application of hard surfacing.
OPERATIONAL DATA
ELECTRODE SIZE (mm)
ELECTRODE LENGTH (mm)
WELDING CURRENT RANGE *(A)
ARC VOLTAGE RANGE **(V)
2.5 300 50-75 223.2 350 75-110 26
*Recommended for DC +/- or AV (minimum 45 OCV) operation. **Voltage is determined by arc current and electrode arc length. Arc voltage shown is typical and is only to be used as a guide.
UNICORD 312
25CONTENTS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si Cr Ni Fe0.04 0.9 0.85 30.0 9.0 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Yield Stress 500 MPaTensile Strength 770 MPaElongation 45%Deposit Hardness 28-35 HRc
In as welded condition.
PACKAGING DATA
ELECTRODE SIZE (mm)
PACKAGING (KG)
APPROX NO. OF RODS
PER KG
PART NUMBER
Packet Carton2.5 2.5 12.5 52 UC312253.2 2.5 12.5 27 UC31232
ELECTRODES - STAINLESS STEEL ELECTRODES1G
2G 3G4G 1F
2F4F
26CONTENTS
SUMMARy
• Pure Nickel Core Wire/Basic, Graphite Coating• Soft Machineable Nickel Deposit for the Lower Strength Welding of Cast Irons
IDENTIFICATIONCoating - Black Tip - Plain Imprint - WIA SC Ni
CLASSIFICATION
• AWS A5.15: ENi-Cl
DESCRIPTION AND APPLICATION Supercast Ni is a basic, graphite coated AC/DC electrode for the lower strength welding of cast irons. It is characterised by a soft, smooth arc with low penetration and spatter levels on both AC and DC power sources. Ease of striking is a feature of Supercast Ni and it also has a particularly good wetting action resulting in well bonded welds of regular contour and attractive appearance.
This electrode is made from a pure nickel core wire and produces a ductile, fully machineable weld deposit. Supercast Ni may be used for the repair and reclamation of all standard grades of grey cast iron, malleable iron, austenitic cast iron and some grades of mechanite cast iron.
OPERATIONAL DATA
ELECTRODE SIZE (mm)
ELECTRODE LENGTH (mm)
WELDING CURRENT RANGE *(A)
ARC VOLTAGE RANGE **(V)
3.2 350 50-100 23
*Recommended for DC +/- or AC (minimum 45 OCV) operation. **Voltage is determined by arc current and electrode arc length. Arc voltage shown is typical and is only to be used as a guide.
SUPERCAST Ni
27CONTENTS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
Mn Ni S Fe0.3 97.0 0.006 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Yield Stress 220 MPaTensile Strength 400 MPaDeposit Hardness 150-170 HV (30)
PACKAGING DATA
ELECTRODE SIZE (mm)
PACKAGING (KG)
APPROX NO. OF RODS
PER KG
PART NUMBER
Packet Carton3.2 2.5 12.5 37 SNI32
ELECTRODES - CAST IRON ELECTRODES1G
2G 3G4G1F
28CONTENTS
SUMMARy
• Nickel -Iron Core Wire/Basic, Graphite Coating• Machineable Nickel-Iron Deposit for the Higher Strength Welding of Cast Irons, Particularly SG Irons
IDENTIFICATIONCoating - Black Tip - Green Imprint - WIA SC NiFe
CLASSIFICATION
• AWS A5.15: ENiFe-Cl
DESCRIPTION AND APPLICATION Supercast Ni/Fe is a basic, graphite coated AC/DC electrode for the higher strength welding of cast irons. It is characterised by a soft, smooth arc with low penetration and spatter levels on both AC and DC power sources. Ease of striking is a feature of Supercast Ni/Fe.
This electrode is made from a Nickel-Iron core wire and produces a ductile, machineable weld deposit with the extra strength required for welding SG (Spheroidal Graphite) irons.
Supercast Ni/Fe may also be used for the repair and reclamation of all standard grades of grey cast iron, malleable iron, austenitic cast iron and some grades of mechanite cast iron. It is ideally suited to the dissimilar welding of these irons to steels.
OPERATIONAL DATA
ELECTRODE SIZE (mm)
ELECTRODE LENGTH (mm)
WELDING CURRENT RANGE *(A)
ARC VOLTAGE RANGE **(V)
3.2 350 50-100 23
*Recommended for DC +/- or AC (minimum 45 OCV) operation. **Voltage is determined by arc current and electrode arc length. Arc voltage shown is typical and is only to be used as a guide.
SUPERCAST Ni/Fe
29CONTENTS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
Mn Ni S Fe0.85 57.8 0.007 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Yield Stress 300 MPaTensile Strength 500 MPaDeposit Hardness 200-220 HV (30)
PACKAGING DATA
ELECTRODE SIZE (mm)
PACKAGING (KG)
APPROX NO. OF RODS
PER KG
PART NUMBER
Packet Carton3.2 2.5 12.5 39 SNIFE32
ELECTRODES - CAST IRON ELECTRODES1G
2G 3G4G1F
30CONTENTS
SUMMARy
• Heavy Coated Manual Electrode for Cutting, Gouging or Piercing Steels
IDENTIFICATIONCoating - Black End Tip - Plain
DESCRIPTION AND APPLICATION
Austarc C&G is a heavy coated electrode providing a highly mobile means of cutting, gouging and piercing most steels, using standard AC or DC arc welding equipment. Austarc C&G produces a very high arc force and can be used for general cutting and grooving in joint preparation, removing defective welds and reclaiming scrap metal, etc.
Oxy-acetylene and carbon arc-air cutting and gouging are two processes available to industry capable of giving high quality, smooth preparations. Austarc C&G will not replace these processes but rather provide a convenient, easy to use and mobile tool for the arc gouging and cutting of most metals. It is particularly useful to the maintenance welder operating in awkward locations to remove welds, open up joints and trim off bolt or rivet heads, etc. Similarly, the rural welder will find C&G handy in repairing or preparing joints when operating away from (or without) oxy-acetylene equipment.
Cutting - Direct the electrode into the work in the desired cutting direction, working from the outside edge. Use an up and down sawing motion, the “up” arc length being increased to increase heating, the “down” arc length being decreased to contact point to force the molten metal out of the groove. Angle of electrode should be approx 70° to the horizontal.
AUSTARC C&G
31CONTENTS
Gouging - Point the electrode in the direction of gouging at approx 10-20° to the plate surface. Strike the arc and move forward rapidly. If slag and molten metal start to clog the groove bring the electrode up to clear and, without breaking the arc, circle backwards and move forward again. This latter technique may prove more necessary than straight forward motion on lower amps or as the electrode becomes hotter. If amps are excessive, C&G will tend to “cut out” on AC and overheat, causing premature charring of the coating and reduced arc force.
Piercing - For holes, plunge the electrode into the plate at slightly off right angles. With a small circular motion to the holder, force the electrode into the plate until full penetration is achieved. Once the hole has been made it may be trimmed with an up and down sawing motion.
OPERATIONAL DATA
ELECTRODE SIZE (mm)
ELECTRODE LENGTH (mm)
PACKAGING (KG) WELDING CURRENT RANGE *(A)Packet Carton
3.2 380 4 12 170-2504.0 380 4 12 220-350
ELECTRODES - GOUGING AND CUTTING ELECTRODES
32
33
SOLID MIG WIRES Austmig ES6 ...................................................................... 34-35
SOLID MIG WIRES - LOW ALLOy STEELAustmig ESD2 ........................................................ 36-37Austmig NiCrMo ..................................................... 38-39
SOLID MIG WIRES - ALUMINIUMAustmig 5183 .......................................................... 40-41Austmig 5356 ......................................................... 42-43
METAL CORED GAS SHIELDED WIRESAustfil 70C-6M ........................................................ 44-45
FLUX CORED GAS SHIELDED WIRESAustfil 71T ............................................................... 46-47Austfil 71T-1M ......................................................... 48-49Hobart XL-525 ........................................................ 50-51TM-71HYD .............................................................. 52-53TM-811N2 ............................................................... 54-55
FLUX CORED SELF SHIELDED WIRESFabshield 4 ............................................................. 56-57 Fabshield 23 ........................................................... 58-59Fabshield 21B ......................................................... 60-61Fabshield XLR-8 ..................................................... 62-63
WIRESCONTENTS
CONTENTS
34CONTENTS
SUMMARy
• Electrostatically Copper Coated Gas Metal Arc (MIG) Wire• All Positional Welding of Mild and Medium Strength Steels• Precision Layer Wound, Very Low Diffusable Hydrogen• Suitable for all Transfer Modes• Designed for use with Argon/CO₂ and CO₂ Shielding Gases
CLASSIFICATION
• AS/NZS 2717.1: ES6-GC-W503AH• AS/NZS 2717.1: ES6-GM-W503AH• AWS A5.18: ER70S-6
DESCRIPTION AND APPLICATION Austmig ES6 is a copper coated, low carbon steel GMAW wire, formulated for optimum performance under Argon/CO₂ mixed gases and welding grade CO₂. Arc transfer characteristics are excellent with Argon based gas mixtures, particularly in spray and pulsed transfer modes. Austmig ES6 is an electrostatically copper coated wire providing excellent wire feeding and electrical conductivity and reducing contact tip wear. The higher manganese and silicon content of Austmig ES6 provides effective weld metal deoxidation for resistance to porosity.Austmig ES6 is suitable for a wide range of welding applications on mild and medium strength steels providing consistently very low “H5” weld metal diffusible hydrogen levels when used with suitable shielding gases.
OPERATIONAL DATA
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
0.6 40-100 12-160.8 60-180 14-220.9 70-230 15-261.0 100-290 16-291.2 120-350 18-321.6 160-390 18.34
Welding Current DC + *Voltage is determined by arc current and electrode arc length. Welding currents and voltage shown are operational guides only.
AUSTMIG ES6
35CONTENTS
SHIPPING APPROVALSLR 3S, 3YS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si S P Fe0.1 1.45 0.88 0.02 0.022 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Gas Type CO₂ Ar+18% CO₂Yield Stress 460 MPa 480 MPaTensile Stress 560 MPa 580 MPaElongation 28% 26%CVN Impact Values 80J @ -20ºC 70J @ -30ºC
PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE AND TyPE PART NUMBER
0.6 5kg spool 15kg spool
ES606M5KG ES606S
0.8 5kg spool 15kg spool
ES608M5KG ES608S
0.9 5kg spool 15kg spool
ES609M5KG ES609S
1.0 15kg spool ES610S1.2 15kg spool ES612S1.6 15kg spool ES616S
WIRES - SOLID MIG WIRES - MILD STEEL
1G2G 3G
4G 1F2F
4F
36CONTENTS
SUMMARy
• Copper Coated, High Manganese-Molybdenum Gas Metal Arc (MIG) Welding Wire• For the all Positional Welding of Medium to Higher Strength Steels
CLASSIFICATION
• AS/NZS 2717.1: ESD2-GC-W559AH• AS/NZS 2717.1: ESD2-GM-W559AH• AWS A5.18: ER80S-D2
DESCRIPTION AND APPLICATION
Austmig ESD2 is a copper coated, low alloy steel wire used for welding medium to higher strength steels, particularly where service temperatures up to 500°C are encountered. ESD2 gives excellent resistance to porosity using CO₂ or Argon based gas mixtures (i.e. Ar/CO₂, Ar/O₂, Ar/CO₂/O₂). When porosity is a potential problem due to dirty or rusty surfaces or higher than normal sulphur contents, Austmig ESD2 will provide a consistently sound weld deposit.Austmig ESD2 is also suitable for out-of-position welding due to its quick freezing weld pool. ESD2 produces high quality welds on plain carbon and C-Mn steels, low alloy steels and higher strength used in pressure vessels and boilers, such as petrochemical and power generation industries, operating at elevated temperatures. Austmig ESD2 may also be used for the fillet welding of higher tensile, quenched and tempered steels, such as Bisalloy 70 and 80 where the lower strength weld metal may be compensated by larger fillet sizes.When used with suitable shielding gases, Austmig ESD2 will consistently produce very low “H5”, weld metal diffusible hydrogen levels, for excellent resistance to HAZ or hydrogen induced cracking.
AUSTMIG ESD2
37CONTENTS
OPERATIONAL DATA
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
0.9 70-230 15-261.2 120-350 18-32
Welding Current DC + *Voltage is determined by arc current and electrode arc length. Welding currents and voltage shown are operational guides only.
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si Mo Fe0.1 1.95 0.75 0.5 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Gas Type CO₂ Ar+18% CO₂Yield Stress 560 MPa 570 MPaTensile Stress 645 MPa 660 MPaElongation 19% 20%CVN Impact Values 35J @ -20ºC 50J @ -30ºC
In as welded condition.NOTE: The use of less oxidizing Argon based gas mixtures will result in higher manganese and silicon weld metal recovery, leading to higher tensile properties, particularly in heavy multi pass butt welds.
PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE AND TyPE PART NUMBER
0.9 15kg spool ESD209S1.2 15kg spool ESD209S
WIRES - SOLID MIG WIRES - LOW ALLOY STEEL
1G2G 3G
4G 1F2F
4F
38CONTENTS
SUMMARy
• Copper Coated, Low Allloy Gas Metal Arc (MIG) Welding Wire• All Positional Welding of Medium and High Strength Steels• Welded Strength 760 MPa Tensile Class
CLASSIFICATION
• AS/NZS 2717.1: ESMG-GM-W769AH-G• AWS A5.28: ER110S-G
DESCRIPTION AND APPLICATION
Austmig NiCrMo is a copper coated, low alloy solid wire suitable for the all positional welding of high strength steels using Argon + CO₂ gas mixtures.
Austmig NiCrMo is ideal for the full strength welding of quenched and tempered structural steels, of the 760 MPa tensile class, such as USS-T1, CcMo Pipe, Welten 80, Weldox 700, X80, N-A-XTRA and Bisplate 80.
OPERATIONAL DATA
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
0.9 70-230 15-261.2 120-350 18-32
Welding Current DC + *Voltage is determined by arc current and electrode arc length. Welding currents and voltage shown are operational guides only.
NOTE: Austmig NiCrMo is NOT to be used in weldments which are to be stress relieved.
AUSTMIG NiCrMo
39CONTENTS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si Ni Cr Mo V Fe0.07 1.22 0.37 1.42 0.29 0.24 0.07 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Gas Type Ar+18% CO₂Yield Stress 732 MPaTensile Stress 799 MPaElongation 18%CVN Impact Values 78J @ -30ºC
In as welded condition
NOTE: The use of less oxidizing argon based gas mixtures (ie Ar/O₂, Ar/CO₂, Ar/CO₂/O₂), will result in higher alloy recovery in the weld metal, leading to higher tensile properties.
PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE AND TyPE PART NUMBER
0.9 15kg spool MNICRMO09S1.2 15kg spool MNICRMO12S
WIRES - SOLID MIG WIRES - LOW ALLOY STEEL
1G2G 3G
4G 1F2F
4F
40CONTENTS
SUMMARy
• Aluminium-Magnesium-Manganese, Metal Inert Gas (MIG) Welding Wire• Precision Layer Wound and Double Shaved for Superb Feedability• For Welding of Alloys of the same Composition
CLASSIFICATION
• AS/NZS ISO 18273 - S AI 5183• AWS A5.10: E5183
DESCRIPTION AND APPLICATION
Austmig 5183 is a precision layer wound aluminium wire alloyed with Mg, Mn and Cr.
It is recommended for welding Al/Mg material of the 5083 type in the annealed condition, particularly for low temperature applications where good ductility and toughness are required, ie cryogenic plant. It may also be used for welding medium strength Al/Zn/Mg alloys of the 7020 type and joining 5083 alloy to 5456 alloy.
Welding grade Argon or Argon/Helium shielding gas combinations are recommended with flow rates of 10-20 litres/minute.
OPERATIONAL DATA
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
1.2 150-250 20-271.6 200-350 23-30
Welding Current DC + *Voltage is determined by arc current and electrode arc length. Welding currents and voltage shown are operational guides only.
AUSTMIG 5183
41CONTENTS
SHIPPING APPROVALSLR WC/1-1S ABS AWS A5. 10-92/ER5183DNV 5183
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
Si Fe Cu Mn Mg Cr Zn Ti AI0.4 0.4 0.1 0.5-1.0 4.3-5.2 0.05-0.25 0.25 0.15 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Gas Type ArYield Stress 110 MPaTensile Stress 240 MPaElongation 17%
PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE AND TyPE PART NUMBER
1.2 6kg spool M518312S1.6 6kg spool M518316S
WIRES - SOLID MIG WIRES - ALUMINIUM
1G2G 3G
4G 1F2F
4F
42CONTENTS
SUMMARy
• Aluminium - 5% Magnesium Alloy, Metal Inert Gas (MIG) Welding Wire • Double Shaved and Precision Layer Wound for Superb Feedability• For Welding Cast and Wrought Aluminium Alloys Containing Magnesium
CLASSIFICATION
• AS/NZS ISO 18273 - S AI 5356• AWS A5.10: ER5356
DESCRIPTION AND APPLICATION
Austmig 5356 is a precision layer wound Aluminium - 5% Magnesium wire suitable for a wide range of gas metal arc welding applications on wrought or cast aluminium alloys containing magnesium as a major alloying element. Some grades of wrought aluminium - magnesium alloys which can be welded with Austmig 5356 are, 5083, 5086, 5454 and 5456.
OPERATIONAL DATA
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
0.9 80-190 16-221.0 100-230 18-221.2 150-250 20-271.6 200-330 23-30
Welding Current DC + *Voltage is determined by arc current and electrode arc length. Welding currents and voltage shown are operational guides only.
AUSTMIG 5356
43CONTENTS
SHIPPING APPROVALSLR WC/I-1,S; ABS AWS A5. 10-92/ER 5356; DNV 5356
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
Zn Mg Mn Cr Si Fe Ti AI0.1 5.2 0.15 0.1 0.25 0.4 0.15 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Gas Type ArYield Stress 125 MPaTensile Stress 275 MPaElongation 17%
PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE AND TyPE PART NUMBER
0.9 2kg spool 6kg spool
M5356092KG M535609S
1.0 2kg spool 6kg spool
M5356102KG M535610S
1.2 2kg spool 6kg spool
M5356122KG M535612S
1.6 6kg spool M535616S
WIRES - SOLID MIG WIRES - ALUMINIUM
1G2G 3G
4G 1F2F
4F
44CONTENTS
SUMMARy
• Gas Shielded, Metal-Cored Wire• Slag-Free Weld Bead• Higher Deposition Rates• Low Spatter/Smooth Appearance• Better Fusion Profile
CLASSIFICATION
• AS/NZS ISO 17632-B - T 492T15 0MA-UH5• AWS A5.18: E70C-6M
DESCRIPTION AND APPLICATION
Austfil 70C-6M is a metal-cored wire designed for high speed fillet and butt welding in the downhand position using Argon + 18-25% CO₂ shielding gas mixture. Weld beads are almost completely slag free with only minimal silicon islands, reducing the time and effort spent between runs and on cleanup prior to surface finishing.
Austfil 70C-6M is recommended for single and multi pass welding in both flat and horizontal positions for mild steel, carbon and maganese carbon steels with minimum clean up and where high deposition rates and efficiencies are required in high productivity, semi automatic and fully automatic welding installations. Suitable applications include mining buckets, structural fabrication and tank construction where high speed welding is required.
OPERATIONAL DATA
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
1.2 200-350 29-351.6 300-450 27-34
Welding Current DC + *Voltage is determined by arc current and wire arc length. Welding currents and voltage shown are operational guides only.
AUSTFIL 70C-6M
45CONTENTS
SHIPPING APPROVALSLR 3S, 3YS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si S P Cu Fe0.038 1.46 0.68 0.009 0.012 0.02 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Gas Type Ar+25%CO₂Yield Stress 628 MPaTensile Stress 587 MPaElongation 29%CVN Impact Values 51J @ -20ºC
PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE AND TyPE PART NUMBER
1.2 15kg spool 70C6M12S1.6 15kg spool 70C6M16S1.2 250kg drum 70C6M12D
WIRES - METAL CORED GAS SHIELDED WIRES
1G2G 1F
2F
46CONTENTS
SUMMARy
• All Purpose Rutile Flux Cored Wire• For Both Single or Multiple Pass Welds• All Positional Wire• Formulated Exclusively For CO₂ Gas
CLASSIFICATION
• AS/NZS ISO 17632-B - T492T1-1CA-UH10• AWS A5.20: E71T-1 H8
DESCRIPTION AND APPLICATION
Austfil 71T is a rutile flux cored wire designed for excellent performance in all positional fillet and butt-welding applications. Austfil 71T is formulated exclusively for use with cost effective CO₂ shielding gas.
Austfil 71T is recommended for general purpose all positional welding of mild, carbon and carbon-manganese steels where excellent weld profile and penetration is required. Suitable for applications such as storage tanks, structural fabrication, bridge construction, machinery and earthmoving equipment. Suitable for AS/NZS 1554.5 of the structural code; Part 5: Welding of the steel structures subject to high levels of fatigue loading.
OPERATIONAL DATA
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
1.2 130-230 25-321.6 200-350 25-32
Welding Current DC + Welding parameters shown above are for DC electrode positive using 100% CO₂ shielding gas at a flow rate of 15-20 litres/minute. *Voltage is determined by arc current and wire arc length. Welding currents and voltage shown are operational guides only.
AUSTFIL 71T
47CONTENTS
SHIPPING APPROVALSLR 3S, 3YS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si S P Fe0.03 1.28 0.44 0.01 0.013 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Gas Type CO₂Yield Stress 531 MPaTensile Stress 580 MPaElongation 26%CVN Impact Values 93J @ -20ºC
PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE AND TyPE PART NUMBER
1.2 15kg spool 71T112S1.6 15kg spool 71T116S
WIRES - FLUX CORED GAS SHIELDED WIRES
1G2G 3G
4G 1F2F
4F
48CONTENTS
SUMMARy
• Rutile Type Flux Cored Joining Wire, Micro Alloyed• Formulated Exclusively for use with Ar/CO₂ Shielding Gas Mixtures• Excellent Operator Appeal “Smooth Spray Arc Transfer”• Versatile all Positional Capabilities• Grade 3 Weld Metal Impact Properties
CLASSIFICATION
• AS/NZS ISO 17632-B - T492T1-1MA-UH10• AWS A5.20: E71T-1M
DESCRIPTION AND APPLICATION
An all positional rutile micro alloyed type flux cored welding wire specifically formulated for optimum performance using Ar/CO₂ shielding gas mixtures.
The exceptionally smooth arc performance produces a superb weld for single or multipass welding with low spatter losses in all positions and applications (except vertical down). Austfil 71T-1M is recommended for the welding of mild, carbon and carbon-manganese medium steels where good impact properties at -20°C are required.
This high deposition wire offers excellent operator appeal for general steel fabrications and constructions such as plate sections, beams, girders, truck chassis/bodies, shipbuilding, earth moving equipment, storage tanks, bridge construction etc.
Recommended shielding gases are: Argon + 18-25%CO₂
AUSTFIL 71T-1M
49CONTENTS
OPERATIONAL DATA
WIRE SIZE (mm)
WELD POSITION
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
1.2Flat Flat Fillet Vertical - up
250-300 230-280 170-220
29-35 28-30 24-28
1.6Flat Flat Fillet Vertical - up
300-350 200-350 200-250
28-34 24-34 26-28
Recommended electrical stick out is 15-20mm. Welding Current DC + *Voltage is determined by arc current and wire arc length. Welding currents and voltage shown are operational guides only.
SHIPPING APPROVALSLR 3S, 3YS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si S P B Fe0.04 1.20 0.42 0.012 0.013 0.001 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Gas Type Ar+25% CO₂Yield Stress 487 MPaTensile Stress 565 MPaElongation 25%CVN Impact Values 103J @ -20ºC
In as welded condition
PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE AND TyPE
PALLET SIZE (KG) PART NUMBER
1.2 15kg spool 1080 71T1M12S1.6 15kg spool 1080 71T1M16S
WIRES - FLUX CORED GAS SHIELDED WIRES
1G2G 3G
4G 1F2F
4F
50CONTENTS
SUMMARy
• Low Diffusible Hydrogen• Excellent Toughness at Low Temperatures• Outstanding Weldability• Exceeds 27J CVN @ -40℃
CLASSIFICATION
• AS/NZS ISO 17632-B - T494T1-1MA-UH5• AWS A5.20: E71T-1M, E71T-12MJ H8
DESCRIPTION AND APPLICATION
A rutile flux cored all position wire designed for welding mild and carbon steels, especially when good impact toughness is required at sub zero temperatures. Ideal for single and multi-pass applications, it delivers outstanding welding performance and produces high quality X-ray clear weld deposit with a bead contour that is flat to slightly convex. It can be used over rust, mill scale and some primers with no pre-cleaning of the steel necessary. Formula XL-525 has outstanding mechanical properties that resemble those of E7018 MMAW (SMAW) electrodes, plus high operator appeal with low fume levels, low spatter and easy slag removal.
Recommended for ship building, storage vessels, off-shore structures, earth moving equipment and pipe welding.
HOBART XL-525
51CONTENTS
OPERATIONAL DATA
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
1.2 150-300 24-311.6 200-350 24-34
Recommended electrical stick out is 15-20mm. Welding Current DC + *Voltage is determined by arc current and wire arc length. Welding currents and voltage shown are operational guides only.
SHIPPING APPROVALSLR 3S, 3YS; ABS 3SA, 3YSA Impact @ -40̊C 34 ft, lbs DNV Y40MS BV 3YM; CWB E491T-12MJ-H4;
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si Ni Fe0.04 1.24 0.29 0.37 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Gas Type Ar+20% CO₂Yield Stress 503 MPaTensile Stress 566 MPaElongation 29%CVN Impact Values 90J @ -40ºC
In as welded condition.
PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE AND TyPE PART NUMBER
1.2 15kg spool S283212-0291.6 15kg spool S283219-029
WIRES - FLUX CORED GAS SHIELDED WIRES
1G2G 3G
4G 1F2F
4F
52CONTENTS
SUMMARy
• Low Diffusible Hydrogen• Exceeds 27J CVN @ -40℃• Outstanding Weldability in all Positions• Actual Certification to AWS A5.01 Lot Class: T3
CLASSIFICATION
• AS/NZS ISO 17632-B - T494T1-1CA-UH5• 1.2mm, AWS E71T-1C, E71T-12CJ H4• 1.6mm, AWS E71T-1C, E71T-12CJ H8
DESCRIPTION AND APPLICATION
Formulated to provide extremely low hydrogen levels. This outstanding all positional wire produces a high quality X-ray clear weld deposit with high impact values at low temperature. Every batch of the TM-71HYD is actual tested to certify the quoted mechanical property, and the vacuum sealed packaging further ensures the product integrity upon delivery.
Applications include ship building and repair, earth moving equipment, structures, pressure vessel and storage vessels.
OPERATIONAL DATA
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
1.2 100-350 22-341.6 200-350 24-34
Recommended electrical stick out is 15-20mm. Welding Current DC + *Voltage is determined by arc current and wire arc length. Welding currents and voltage shown are operational guides only.
TM- 71HYD
53CONTENTS
SHIPPING APPROVALSMIL-71T-1-HYD
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si S P Ni Fe0.05 1.17 0.25 0.014 0.12 0.5 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Gas Type 100% CO₂Yield Stress 533 MPaTensile Stress 585 MPaElongation 26.6%CVN Impact Values 150J @ -18ºC
137J @ -40ºCAged 48 hours @ 104ºC
In as welded condition.
PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE AND TyPE PART NUMBER
1.2 15kg spool S245112-K531.6 15kg spool S245019-K53
WIRES - FLUX CORED GAS SHIELDED WIRES
1G2G 3G
4G 1F2F
4F
54CONTENTS
SUMMARy
• Fast-Freezing Slag• Low Spatter• Excellent Arc Characteristics• High Impact Strengths at Low Temperatures
CLASSIFICATION
• AS/NZS ISO 17632-B - T555T1-1C/MA-2Ni-UH5• AWS A5.29: E81T1-Ni2C/MJ H8
DESCRIPTION AND APPLICATION
Offers excellent arc stability and low spatter using either CO₂ or Ar/CO₂ mixtures with up to 80% Argon. These weldability features, combined with low diffusible hydrogen levels and good impact values makes the wire a good choice for single and multiple pass welding in all positions.
Applications include ship building, offshore drilling rigs, HSLA steels and weathering steels with no colour match requirement..
OPERATIONAL DATA
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
1.2 100-350 22.34
Recommended electrical stick out is 15-20mm. Welding Current DC + *Voltage is determined by arc current and wire arc length. Welding currents and voltage shown are operational guides only.
TM-811N2
55CONTENTS
SHIPPING APPROVALSABS 3YSA; DNV Y40MS; LR 3Ys
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
Shielding Gas C Mn Si P S Ni100% CO₂ 0.04 1.02 0.29 0.010 0.007 2.09
75% Ar/25% CO₂ 0.05 1.26 0.44 0.010 0.007 2.07
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Gas Type 100% CO₂ 75% Ar/25% CO₂
Yield Stress 535 MPa 579 MPaTensile Stress 600 MPa 662 MPaElongation 27.5% 26%CVN Impact Values 126J @ -40˚C
95J @ -51˚C104J @ -40˚C 71J @ -51˚C
In as welded condition.
PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE AND TyPE PART NUMBER
1.2 15kg spool S283712-K29
WIRES - FLUX CORED GAS SHIELDED WIRES
1G2G 3G
4G 1F2F
4F
56CONTENTS
SUMMARy
• Self Shielded or “Gasless” Flux Cored Joining Wires• For Fast Downhand Fillet and Butt Welding Applications• Excellent Bead Appearance/Low Spatter Levels• Crack Resistant Weld Deposits/Tolerant to Poor Joint Fit-up
CLASSIFICATION
• AS/NZS ISO 17632-B - T49ZT4-0NA-H15• AWS A5.20: E70T-4
DESCRIPTION AND APPLICATION
Fabshield 4 is an outstanding, high deposition rate, (up to 12.7kg/hr using 2.4mm size wire) self-shielded or “gasless” flux cored wire for downhand single or multi-pass welding applications.It is specifically designed to de-sulphurise the weld deposit and thereby resist cracking. Fabshield 4 is particularly suited to the fast fillet welding of mild and medium strength steels.
Typical applications include the welding of structural members and machinery. Due to its self shielding arc, Fabshield 4 is ideal for “on site” field construction and repair applications.
OPERATIONAL DATA
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
2.4 250-500 28-343.0 450-680 28-37
Welding Current DC - *Voltage is determined by arc current and wire arc length. Welding currents and voltage shown are operational guides only.
FABSHIELD 4
57CONTENTS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si P S AI Fe0.27 0.73 0.30 0.11 0.005 1.42 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Yield Stress 432 MPaTensile Stress 652 MPaElongation 25%CVN Impact Values Not Required
PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE AND TyPE PART NUMBER
2.4 22.7kg spool S224529-0143.0 22.7kg spool S224541-014
WIRES - FLUX CORED SELF SHIELDED WIRES
1G1F
2F
58CONTENTS
SUMMARy
• Self Shielded or “Gasless” Flux Cored Joining Wires• All Positional Welding Capabilities• Suitable for Single-Pass Applications only• Ideal for Mild and Galvanized Steels
CLASSIFICATION
• AS/NZS ISO 17632-B - T49ZTG-1SNA• AWS A5.20: E70T-GS
DESCRIPTION AND APPLICATION
Fabshield 23 is a general-purpose self-shielded tubular wire that is designed for welding thin gauge mild or galvanized steel. Suitable for single-pass applications, especially for fillet lap welds, you will get outstanding welding performance as Fabshield 23 produces a smooth spray arc type of transfer with goods wetting action.
Great for welding outdoors in draughty conditions, this all-positional wire also provides very low splatter levels, resulting in a weld bead that is excellent in appearance. Perfect for on site applications such as welding mild steel/galvanized gates, fences, frames, sheds, prefab building fabrications, ornamental ironwork, general fabrication, etc.
OPERATIONAL DATA
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
TyPICAL STICKOUT
(mm)0.8 25-125 14-16 120.9 55-120 17-20 12
Welding Current DC - *Voltage is determined by arc current and wire arc length. Welding currents and voltage shown are operational guides only.
FABSHIELD 23
59CONTENTS
WIRES - FLUX CORED GAS SHIELDED WIRES
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si S P AI Fe0.18 0.65 0.40 0.01 0.01 1.30 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Tensile Stress 572 MPa
NOTE: Yield Stress and impact values not applicable.
PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE AND TyPE PART NUMBER
0.8 4.5kg spool S222306-0220.9 4.5kg spool S222308-0220.9 15kg spool S222308-029
1G2G 3G
4G 1F2F
4F
60CONTENTS
SUMMARy
• Self Shielded or “Gasless” Flux Cored Joining Wires• All Positional Welding Capabilities• Suitable For Single Pass/Multi-pass Applications • Suitable for Mild/Galvanised Steels
CLASSIFICATION
• AS/NZS ISO 17632-B - T49ZT11-1NA-H15• AWS A5.20: E71T-11
DESCRIPTION AND APPLICATION
Fabshield 21B is a general purpose self-shielded tubular wire that is designed for single and multi-pass welding of thin gauge to 20mm thick mild or galvanized steels. Great for welding fillet or lap welds, you will find that this all-position wire has high operator appeal, producing a smooth spray-like transfer with low spatter levels, excellent weld appearance and easy to remove slag.
Perfect for on-site applications such as the welding of machine parts, galvanized steels tanks, gates, frames, sheds, prefab construction, light structures, general fabrication etc.
OPERATIONAL DATAWelding parameters shown below are for DC Electrode negative only.
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
TyPICAL STICKOUT
(mm)0.9 55-120 17-20 121.2 130-160 15-18 121.6 150-250 18-20 192.0 200-300 16-23 19
Welding Current DC - *Voltage is determined by arc current and wire arc length. Welding currents and voltage shown are operational guides only.
FABSHIELD 21B
61CONTENTS
WIRES - FLUX CORED GAS SHIELDED WIRES
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si S P AI Fe0.28 0.34 0.15 0.008 0.003 1.04 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Yield Stress 427 MPaTensile Stress 627 MPaElongation 22%CVN Impact Values Not Required
PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE AND TyPE PART NUMBER
0.9 4.5kg spool S222108-0221.2 4.5kg spool S222112-0221.2 15kg spool S222112-0291.6 15kg spool S222119-0292.0 15kg spool S222125-029
1G2G 3G
4G 1F2F
62CONTENTS
SUMMARy
• Welds Out of Position at High Currents• Low Hydrogen Weld Deposit • Excellent Slag Removal• No Shielding Gas Required• High Impact Strength at Low Temperatures• Excellent Mechanical Properties Under a Wide Range of Heat Input
CLASSIFICATION
• AS/NZS ISO 17632-B - T494T8-1NP-H10• AWS A5.20: E71T-8JD H8
DESCRIPTION AND APPLICATION
Low hydrogen T-8 self-shielded, all positional flux cored wire, producing a stable arc and flat bead profile, especially suited for vertical-up welds at high currents with excellent mechanical properties and a tensile strength of 490 MPa. Capable of depositing X-ray quality welds, making it highly suitable for critical welding applications requiring a high degree of crack resistance due to its low diffusible hydrogen levels, less than 6.7ml per 100g of weld metal deposited. XLR-8 has been designed for single and multi-pass welding applications with improved productivity in out-of-position welding, offering high impact strength of (42J) at sub zero temperatures to -40˚C.Specifically designed for increased productivity and high deposition rates on challenging structural steel erection, heavy equipment repair, mining equipment, bucket repairs, storage tanks, pipe spooling, ship construction and site work applications.
OPERATIONAL DATA
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
1.6 180-300 18-251.8 170-330 18-252.0 200-360 18-26
Recommended electrical stick out is 25-35mm. Welding Current DC - *Voltage is determined by arc current and wire arc length. Welding currents and voltage shown are operational guides only.
HOBART XLR-8
63CONTENTS
WIRES - FLUX CORED SELF SHIELDED WIRES
SHIPPING APPROVALSABS 3YSA; AWS D1.8 Conformance
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si P S AI Fe0.19 0.51 0.17 0.009 0.006 1.51 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Yield Stress 470 MPaTensile Stress 580 MPaElongation 25%CVN Impact Values 42J @ -40˚CDiffusible Hydrogen 6.7ml/100g of weld deposited
In as welded condition.
PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE AND TyPE PART NUMBER
1.6 15kg spool S225719-0531.8 15kg spool S225724-0532.0 15kg spool S225725-0532.0 22.7kg coil S225725-014
1G2G 3G
4G 1F2F
4F
64
65
HARDFACING ELECTRODES Abrasocord 43 ........................................................ 66-67Abrasocord 350....................................................... 68-69Abrasocord 700....................................................... 70-71Tubecord D - 2355 .................................................. 72-73Tubecord E - 2460 .................................................. 74-75
HARDFACING SOLID MIG WIRES Austmig TD-600 ..................................................... 76-77
HARDFACING SELF SHIELDED FLUX CORED WIRESMckay Tube-Alloy 240-0.......................................... 78-79Mckay Tube-Alloy 258-0.......................................... 80-81Mckay Tube-Alloy A43-0 ......................................... 82-83
HARDFACING GAS SHIELDED FLUX CORED WIRESMckay Vertiwear-600 .............................................. 84-85
HARDFACING PRODUCTSCONTENTS
CONTENTS
66CONTENTS
SUMMARy
• Tough, Wear Resistant Complex Carbide Type Deposit• For Hard Surfacing Components Subjected to Extreme Abrasion and Moderate to Heavy Impact• Similar Deposit Type to Tubecord E-2460
IDENTIFICATIONCoating - Black Tip - Plain Imprint - WIA AC 43
CLASSIFICATION
• AS/NZS 2576: 2465-A4
DESCRIPTION AND APPLICATION Abrasocord 43 is a heavy coated, hard surfacing electrode depositing extremely hard, abrasion resistant Chromium/ Niobium carbides in an austenitic matrix. It is ideal for hard surfacing applications where resistance to extreme abrasion (in particular sliding abrasion) and moderate to heavy impact are required. Due to the nodular shape of the complex carbides, Abrasocord 43 deposits are capable of withstanding heavier impact levels than standard chromium carbide grades. Typical applications include bucket teeth/lips, grizzlies, press screws, crusher hammers and ripper teeth to name but a few.
Abrasocord 43 deposits are non-machineable, grindable, prone to fine relief checking and should be restricted to 3 layers high. While two layers of Abrasocord 43 may be required for maximum wear resistance, this complex carbide alloy has lower dilution sensitivity than straight chromium carbide deposits.
OPERATIONAL DATA
ELECTRODE SIZE (mm)
ELECTRODE LENGTH (mm)
WELDING CURRENT RANGE *(A)
ARC VOLTAGE RANGE **(V)
3.2 380 115-140 194.0 380 140-185 225.0 450 190-255 24
*Recommended for DC +/- or AC (minimum 55 OCV) operation. **Voltage is determined by arc current and electrode arc length. Arc voltage shown is typical and is only to be used as a guide.
ABRASOCORD 43
67CONTENTS
HARDFACING PRODUCTS - HARDFACING ELECTRODES
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Cr Nb Fe5.0 0.7 22.0 7.0 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Single Layer onto Mild Steel Typical Hardness 60-65 HRcMulti-Layer Typical Hardness 64-69 HRc
Single layer deposit hardness may vary depending on base metal type and degree of dilution
PACKAGING DATA
ELECTRODE SIZE (mm)
PACKAGING (KG)
APPROX NO. OF RODS
PER KG
PART NUMBER
Packet Carton3.2 5 15 16 AC43324.0 5 15 11 AC43405.0 5 15 6 AC4350
1G2G
68CONTENTS
SUMMARy
• Tough, Machineable, Wear Resistant Martensitic Steel Deposit• For Hard Surfacing Steels Subjected to Metal-to-Metal Wear Under Compressive Loading
IDENTIFICATIONCoating - Brown Tip - Yellow Imprint - WIA AC 350
CLASSIFICATION
• AS/NZS 2576: 1435-A4
DESCRIPTION AND APPLICATION Abrasocord 350 is a smooth running, AC/DC electrode which deposits a tough wear resistant low carbon martensitic steel alloy. It is suitable for the heavy build-up and surfacing of steel components subjected to metal-to-metal wear and compressive loading such as, track components, gears and shafts, etc.
Abrasocord 350 deposits an air hardening C-Mn-Cr steel alloy which is machineable and can be readily hot forged. It offers high compressive strength and excellent resistance to impact for all types of metal-to-metal wear.
OPERATIONAL DATA
ELECTRODE SIZE (mm)
ELECTRODE LENGTH (mm)
WELDING CURRENT RANGE *(A)
ARC VOLTAGE RANGE **(V)
3.2 380 100-140 194.0 380 150-200 225.0 450 190-240 24
*Recommended for DC +/- or AC (minimum 45 OCV) operation. **Voltage is determined by arc current and electrode arc length. Arc voltage shown is typical and is only to be used as a guide.
ABRASOCORD 350
69CONTENTS
HARDFACING PRODUCTS - HARDFACING ELECTRODES
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si Cr Fe0.2 0.4 0.3 2.8 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Single Layer onto Mild Steel Typical Hardness 30-35 HRcMulti-Layer Typical Hardness 35-40 HRc
Single layer deposit hardness may vary depending on base metal type and degree of dilution
PACKAGING DATA
ELECTRODE SIZE (mm)
PACKAGING (KG)
APPROX NO. OF RODS
PER KG
PART NUMBER
Packet Carton3.2 5 15 24 HF350324.0 5 15 16 HF350405.0 5 15 9 HF35050
1G2G
70CONTENTS
SUMMARy
• Wear Resistant, High Carbon Martensitic Steel Deposit • For a Wide Range of General Hard Surfacing Applications, Such as Points, Tynes, Lips, Blades and Augers, ect.
IDENTIFICATIONCoating - Grey Tip - Orange Imprint - WIA AC 700
CLASSIFICATION
• AS/NZS 2576: 1855-A4
DESCRIPTION AND APPLICATION Abrasocord 700 is a smooth running, AC/DC electrode which deposits an air hardening martensitic Cr-Mo-V steel alloy. Abrasocord 700 deposits one of the hardest steel alloys available and is free from relief checks. Applications include the surfacing of post hole augers, agricultural points, shares and tynes, grader and cultivator blades and other components subject to fatigue or flexing during service.
Abrasocord 700 deposits an air hardening steel alloy which can be readily hot forged and offers good resistance to all types of abrasion under low to moderate impact conditions.
In the “as welded” condition Abrasocord 700 weld metal cannot be machined without prior heat treatment.
OPERATIONAL DATA
ELECTRODE SIZE (mm)
ELECTRODE LENGTH (mm)
WELDING CURRENT RANGE *(A)
ARC VOLTAGE RANGE **(V)
3.2 380 90-130 194.0 380 140-180 225.0 450 160-240 24
*Recommended for DC +/- or AC (minimum 45 OCV) operation. **Voltage is determined by arc current and electrode arc length. Arc voltage shown is typical and is only to be used as a guide.
ABRASOCORD 700
71CONTENTS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si Cr Mo V Fe0.7 0.3 0.5 8.5 0.3 0.5 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Single Layer onto Mild Steel Typical Hardness 53-56 HRcMulti-Layer Typical Hardness 55-60 HRc
Single layer deposit hardness may vary depending on base metal type and degree of dilution
PACKAGING DATA
ELECTRODE SIZE (mm)
PACKAGING (KG)
APPROX NO. OF RODS
PER KG
PART NUMBER
Packet Carton3.2 5 15 27 HF700324.0 5 15 18 HF700405.0 5 15 10 HF70050
HARDFACING PRODUCTS - HARDFACING ELECTRODES1G
2G
72CONTENTS
SUMMARy
• High Chrome Carbide• Improved Abrasion Resistance• Welds can be Shaped by Grinding
IDENTIFICATIONCoating - Black Tip - Light Green
CLASSIFICATION
• AS/NZS 2576: 2355-A1* * Nearest Classification
DESCRIPTION
Tubecord D - 2355 deposits are high in carbon and chromium resulting in improved abrasion resistance. Tubecord D - 2355 is ideal for hard surfacing components subjected to heavy abrasion and moderate impact loading.
No preheat is required for direct application onto grey cast iron, low carbon or manganese steels.
Applications include the hard surfacing of dredge bucket lips, shovel buckets, scraper and dozer sides, cone crushers and mill hammers, etc. Deposits are grindable, subject to relief checking and may be multi-layered up to 3 layers. Features include, controlled fume levels, minimal spatter, easy bead deposition and low penetration.
Tubecord D - 2355 is suitable for AC or DC applications.
OPERATIONAL DATA
ELECTRODE SIZE (mm)
ELECTRODE LENGTH (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
6.3 450 85-135 25
*Voltage is determined by arc current and electrode arc length. Arc voltage shown is typical and is only to be used as a guide.
TUBECORD D - 2355
73CONTENTS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Cr Fe5.5 1.5 40.0 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Single Layer Typical Hardness 55-60 HRc
PACKAGING DATA
ELECTRODE SIZE (mm)
PACKAGING (KG) PART
NUMBERPacket Carton
6.3 5 15 TUBD60
APPLICATIONS
• Dredge Bucket Lips• Shovel Buckets• Cone Crusher
HARDFACING PRODUCTS - HARDFACING ELECTRODES1G
2G 3G4G
74CONTENTS
SUMMARy
• All Tubecord Electrodes are 450mm Long.• 6.3mm Tubecord E - 2460 is also Suitable for Vertical Up and Overhead Welding Positions.• All Tubecore Electrodes are Coated with a Moisture Resistant, Non Alloying, Black Flux Coating, Resulting in Infinate Storage life!
IDENTIFICATIONCoating - Black Tip - Blue
CLASSIFICATION
• AS/NZS 2576: 2460-A1
DESCRIPTION
Tubecord E - 2460 deposits contain carbon, chromium, niobium and molybdenum alloys for good resistance to both impact and abrasion:
Tubecord E - 2460 produces a similar complex carbide iron deposit to the popular Abrasocord 43 electrode.No preheat is required for direct application onto grey cast iron, low carbon or manganese steels.Applications include the hard surfacing of grizzly bars, bucket teeth, crusher hammers, rail ballast tampers, dredger and ripper teeth, etc. Deposits are grindable, subject to relief checking and should be restricted to 3 layers high.Features include, controlled fume levels, minimal spatter, easy bead deposition and low penetration.Tubecord E - 2460 is suitable for AC or DC applications.
TUBECORD E - 2460
75CONTENTS
OPERATIONAL DATA
ELECTRODE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
6.3 90-130 258.0 135-185 29
*Voltage is determined by arc current and electrode arc length. Arc voltage shown is typical and is only to be used as a guide. **6.3mm only
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Cr Mo Nb V Mn Si Fe4.0 26.5 0.9 7.9 0.4 0.8 1.5 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
Single Layer Typical Hardness 58-61 HRc
PACKAGING DATA
ELECTRODE SIZE (mm)
PACKAGING (KG) PART
NUMBERPacket Carton
6.3 5 15 TUBE608.0 5 15 TUBE80
TyPICAL APPLICATIONS
Grily Bars Bucket Teeth Crusher Hammers
HARDFACING PRODUCTS - HARDFACING ELECTRODES2G3G
4G 1F** **
76CONTENTS
SUMMARy • Copper Coated, Chromium Alloy Gas Metal Arc (MIG) Welding Wire• For Hard Surfacing Components Subjected to Severe Abrasion and Heavy Impact CLASSIFICATION
• AS/NZS 2576: 1855-B6
DESCRIPTION
Austmig TD - 600 is a copper coated, chromium alloy welding wire depositing weld metal with a hardness of 55-60 HRc which has a high resistance against severe abrasion and impact.
The deposit is non-machineable but can be shaped by grinding
Typical applications include: excavator blades, bucket lips, bucket teeth, screw conveyors, crushing mills, shear blades.
OPERATIONAL DATA
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
1.2 120-340 18-32
Welding Current DC + *Voltage is determined by arc current and electrode arc length. Welding currents and voltage shown are operational guides only.
AUSTMIG TD - 600
77CONTENTS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Si Mn P S Cr Fe0.45 3.00 0.40 0.025 0.020 9.00 Bal
TyPICAL ALL WELD METAL MECHANICAL ANALySIS
As Welded - Two Layers 55-60 HRcRecommended Shielding Gases:Argon/18 - 25% CO₂, Ar/CO₂ or 100% CO₂
APPLICATIONS • Excavator Blades • Bucket Teeth• Screw Conveyors • Crushing Mills• Sheer Blades
PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE AND TyPE PART NUMBER
1.2 15kg MTD60012S
HARDFACING PRODUCTS - HARDFACING SOLID MIG WIRES1G
2G 3G4G
78CONTENTS
SUMMARy
• Self Shielded Hard Surfacing Flux Cored Wire• General Purpose Alloy with Good Abrasion and Impact Resistance• Chromium Carbide - Alloy Steel• Non Machinable, Difficult to Grind
CLASSIFICATION
• AS/NZS 2576: 2155-B7
DESCRIPTION
McKAY Tube-Alloy 240-O is a self shielded, flux cored hard surfacing wire that deposits a chromium carbide alloy steel. It is an “excellent general purpose alloy due to a combination of good abrasion and impact resistance.
McKAY Tube-Alloy 240-O is designed for overlaying carbon, low alloy or austenitic manganese base metals. The smooth globular type arc transfer gives minimal spatter and the minimum slag cover allows the wire to operate well without de-slagging between weld passes in automatic applications.
Some relief check cracking will occur however it is not detrimental to the wear properties of the deposit and provides some degree of stress relief for the weld metal.
OPERATIONAL DATA
The recommended operating parameters are for DC positive with an electrode stick out of 16-25mm for the 1.2mm size, 25-35mm for 1.6mm. Out-of-position welding is limited to a horizontal shelf technique.
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
1.2 120-275 19-271.6 275-400 24-29
Welding Current DC + *Voltage is determined by arc current and wire arc length. Welding currents and voltage shown are operational guides only.
McKAY TUBE-ALLOY 240-O
79CONTENTS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si Cr Fe3.20 1.80 1.90 15.50 Bal
TyPICAL MECHANICAL PROPERTIES (AS WELDED):
Number of Layers
As-deposited on
1020 Steel Mn Steel
Hardness1 40 Rc 35 Rc2 48 Rc 42 Rc
3-5 52 Rc 50 Rc
Abrasion Resistance: Very GoodImpact Resistance: FairNon-Machinable: Grinding is difficultCannot be Flame CutDeposit will Relief check CracksThickness should be Limited to Five Layers Maximum
APPLICATIONS
• Ammonia Knives • Hammer Mill Hammers• Augers • Impactor Crusher Bars• Bucket Teeth and Lips • Manganese Pump Shells• Bulldozer End Bits & Blades • Mill Guides• Conveyer Screws • Muller Tires• Crusher Jaws and Cones • Pipeline Ball Joints• Crusher Rolls • Pulverizer Hammers• Cultivator Chisels & Sweeps • Scraper Blades• Dragline Buckets • Screw Conveyors• Sheepsfoot Tampers • Sizing Screens• Dredge Pump Impellers and Side Plates
PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE (KG) PART NUMBER
1.2 11.3 S604012-0291.6 11.3 S604019-029
HARDFACING PRODUCTS - HARDFACING SELF SHIELDED FLUX CORED WIRES1G
80CONTENTS
SUMMARy
• Self Shielded or Open Arc Hard Surfacing Flux Cored Wire• Hard Wearing Martensitic Steel Alloy Deposit• Tough, Hard Tool Steel Weld Metal Composition• Good Impact and Abrasion Resistance• Excellent Resistance to Metal-to-Metal Wear• Weld Deposits Grindable Only
CLASSIFICATION
• AS/NZS 2576: 1550-B7* *Nearest Classification
DESCRIPTION
McKAY Tubealloy 258-O is a fabricated type, open arc tubular flux cored wire depositing a Cr-Mo-W Martensitic steel alloy. It is designed for surfacing mild and low alloy steel components subject to moderate abrasive wear and impact under high compressive stresses and/or at temperatures up to 530°C.
Crack free deposits can be obtained by controlled heat input or the use of preheat.
OPERATIONAL DATA
Welding parameters shown below are for DC electrode positive.An electrode stick out length of 12-25mm is recommended for 1.2mm size, 25-35mm for 1.6mm.
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
1.2 120-230 24-271.6 225-350 30-34*
Welding Current DC + *Voltage is determined by arc current and wire arc length. Welding currents and voltage shown are operational guides only.
McKAY TUBE-ALLOY 258-O
81CONTENTS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si Cr Mo W Fe0.45 1.40 0.80 6.00 1.50 1.50 Bal
TyPICAL MECHANICAL PROPERTIES (AS WELDED):
Number of Layers
As-deposited on
1020 Steel Mn Steel
Hardness1 49 Rc 51 Rc2 53 Rc 54 Rc3 57 Rc 57 Rc
Abrasion Resistance: GoodImpact Resistance: GoodNon-Machinable: Grinding onlyFlame Cutting: DifficultDeposit will Relief Check CracksThickness should be Limited to Five Layers Maximum
APPLICATIONS
• Coupling Boxes • Dragline Chains • Kiln Trunnions • Mill Guides• Spindles • Wobbler Ends PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE (KG) PART NUMBER
1.2 11.3 S605812-0291.6 11.3 S605819-029
HARDFACING PRODUCTS - HARDFACING SELF SHIELDED FLUX CORED WIRES1G
82CONTENTS
SUMMARy
• Self Shielded or Open Arc Hard Surfacing • Flux Cored Wire• Niobium-Chromium Carbide Iron Weld Deposit• Resistant to Severe High and Low Stress Abrasion• Low to Moderate Impact Loading• Weld deposits are to be Shaped by Grinding Only
CLASSIFICATION
• AS/NZS 2576: 2460-B7
DESCRIPTION
McKAY Tube-Alloy A43-O is a fabricated type, self shielding tubular flux cored wire depositing a high chromium-niobium surfacing alloy which resists severe high and low stress abrasion and low to moderate impact.
The weld deposit will check crack readily and out performs straight C-Cr hard surfacing alloys. It can also be used where high temperature (650°C) wear resistance is required. Spatter level is low, slag cover is minimal and is easily removed.
OPERATIONAL DATA
The recommended operating parameters are for DC positive with an electrode stick out length of 20-35mm.
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
1.6 300-350 30-34
Welding Current DC + Other wire sizes and spool weights are available on indent only. *Voltage is determined by arc current and wire arc length. Welding currents and voltage shown are operational guides only.
McKAY TUBE-ALLOY A43-O
83CONTENTS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si Cr Nb Fe5.50 0.20 1.0 22.00 6.50 Bal
TyPICAL MECHANICAL PROPERTIES (AS WELDED):
Number of Layers
As-deposited on
1020 Steel Mn Steel
Hardness 1 56-60 Rc 45-50 Rc2-3 60-64 Rc 54-58 Rc
Abrasion Resistance: ExcellentImpact Resistance: PoorNon-Machinable: Grinding onlyFlame Cutting: DifficultDeposit will Relief Check CracksThickness should be Limited to Five Layers Maximum
APPLICATIONS• Augers • Bucket Lips and Teeth• Coal Feeder Screws • Coal Pulverizer Rolls & Tables• Coke Chutes • Coke Pusher Shoes • Conveyer Screws • Fan Blades• Grizzly Bars and Fingers • Pipeline Ball Joints• Muller Tires • Paving Agitator Screws• Pipeline Ball Joints • Pub Mill Paddles• Scraper Blades • Sheepsfoot Tampers• Sizing Screws • Dredge Cutter Heads & Teeth• Dredge Pump Inlet Nozzle and Side Plates PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE (KG) PART NUMBER
1.6 11.3 S607719-029
HARDFACING PRODUCTS - HARDFACING SELF SHIELDED FLUX CORED WIRES1G
84CONTENTS
SUMMARy
• Suites Out-of Position Applications• Multi-Purpose Martensitic Steel• Moderate Abrasive Wear and Medium to High Impact• Weld Deposits - Machineable
CLASSIFICATION
• AS/NZS 2576: 1855-B5* *Nearest Classification
DESCRIPTION
McKAY Vertiwear 600 is a gas shielded, all position, hard surfacing fluxcored wire designed to operate in a smooth semi-spray arc transfer. The weld metal control is superior to competitive gas shielded hard surfacing wires allowing higher deposition and greater productivity in out-of-position applications. Excellent operator appeal in all positions.
McKAY Vertiwear 600 deposits a multi-purpose martensitic steel alloy and can be used to hard surface mild and low alloy steel components subject to moderate abrasion coupled with medium to high impact. It also exhibits excellent compressive strength and metal-to-metal wear resistance.
The recommended shielding gas for Vertiwear 600 is 75% Argon - 25% CO₂.
OPERATIONAL DATA
The recommended operating parameters are for DC positive with an electrode stick out length of 20-35mm.
WIRE SIZE (mm)
WELDING CURRENT RANGE (A)
ARC VOLTAGE RANGE *(V)
1.2 165-185 24-28
Welding Current DC + *Voltage is determined by arc current and wire arc length. Welding currents and voltage shown are operational guides only.
McKAY VERTIWEAR-600
85CONTENTS
TyPICAL ALL WELD METAL CHEMICAL ANALySIS
C Mn Si Cr Mo Fe0.40 0.75 0.60 6.50 1.00 Bal
TyPICAL MECHANICAL PROPERTIES (AS WELDED)
Number of Layers
As-deposited on
1020 Steel
Hardness1 52 Rc2 56 Rc
3-8 57 RcHardness as-
deposited Time at Temp Hardness after Tempering535C° 620C°
55 10 Hours 54 4620 Hours 49 4080 Hours 47 40
Abrasion Resistance: GoodImpact Resistance: GoodMachinability GoodFlame Cutting: DifficultMagnetic
APPLICATIONS
• Coupling Boxes • Dragline Chain• Dredge Ladder Rolls • Kiln Trunnions• Mill Guides • Sliding Metal Parts• Wobber Ends PACKAGING DATA
WIRE SIZE (mm)
PACK SIZE (KG) PART NUMBER
1.2 15 S607112-029
HARDFACING PRODUCTS - HARDFACING GAS SHIELDED FLUX CORED WIRES1G
2G 3G4G
The following pages cover a range of technical information and data tables pertaining to the field of welded fabrication and general engineering.
This section is designed to provide a ready reference guide for welding engineers, design costing personnel, workshop supervisors and welding operators, and to foster higher quality, higher productivity welding.
GLOSSARy .......................................................... 88-105
OXy-ACETyLENE FLAME ADJUSTMENT .........106-107
WELDING SyMBOLS .........................................108-115
ELECTRODE CLASSIFICATIONSManual Metal Arc Welding Electrodes ....................116-123Gas Metal Arc Welding Ferritic Steel Electrodes ...... 124-126Flux Cored Arc Welding Electrodes ....................... 127-129Manual Metal Arc and Gas Metal Arc Welding for Aluminium and Stainless Steel Electrodes .......... 130-131Repair and Hardfacing .......................................... 132-133Submerged Arc Welding Electrodes and Fluxes ... 134-135
WELD DEPOSITION AND COSTING DATAUsers Guide........................................................... 136-147Mass of Weld Metal in Joint ................................... 148-153Quantity of Consumables Required....................... 154-157Deposition Rates ................................................... 158-165Duty Cycles ........................................................... 166-167Electrode Consumption for Typical Butt Joints ...... 168-169
CONTENTS
TECHNICAL INFORMATION
CONTENTS
87
WELDABILITy GUIDE FOR STEELS .................170-193
COMMON WELD TROUBLES ...........................194-199
SI UNITS AND CONVERSION DATA ..................200-203Table 1. Conversion from Inches to Millimetres ..........................204Table 2. Travel and Wire Feed Speeds .......................................205Table 3 °C - °F Temperature Conversions.......................... 206-209Table 4. Comparison of Hardness Scales ...................................210Table 5. Stress and Energy Conversions ....................................211Table 6. Wire and Sheet Sizes ............................................ 212-213
SyMBOLS FOR ELEMENTS AND GEOMETRIC FORMULAE ........................................ 214
CONTENTS
TECHNICAL INFORMATION TECHNICAL INFORMATION
CONTENTS
88CONTENTS
The following is a selection of some of the more common welding terms and abbreviations in current Australian usage. Please refer to Australian Standard AS2812 (Welding, Brazing and Cutting of Metals - Glossary of Terms) for a more comprehensive list.AMPERAGE - The measurement of the amount of electricity flowing past a given point in a conductor per second. Current is another name for amperage.ANGLE OF BEVEL - The angle at which the edge of a joint is prepared for making a weld, refer to FIG 1. (A) - (F) for typical examplesARC BLOW - An uncontrolled deflection of a welding arc caused by an uneven distribution of magnetic field around the arc.ARC LENGTH - The distance from the end of the electrode to the parent material.ARC VOLTAGE - The voltage across the welding arc.ARC WELDING (AW) - Fusion welding in which heat for welding is obtained from an electric arc or arcs.ARC WELDING GUN - A device used in semi-automatic and automatic arc welding to transfer current, guide the consumable electrode and direct shielding gas when used.AS-WELDED - The condition of weld metal, welded joints or weldments after welding prior to any subsequent thermal or mechanical treatment.BACKING - A weld backing maybe incorporated in welded joint design to simplify the root pass. Backing of suitable material can be incorporated in the weldment, or alternativley removable temporary backing material can be used. e.g. ceramic tilesBACK-STEP WELDING - A welding technique wherein the increments of weld metal are deposited in a direction opposite to that of progression.BARE ELECTRODE - A filler metal electrode consisting of a single metal or alloy that has been produced into a wire, strip or bar form which has no flux coating or covering applied to it.
GLOSSARY
89CONTENTS
BASE (PARENT) METAL - The metal to be welded or joined other than the filler metal. BASIC ELECTRODE - A flux coated electrode in which the covering contains a high proportion of basic materials, such as limestone and flurospar etc.BRAZE WELDING (BW) - The joining of metals using similar joint designs as for fusion welding. However, the parent metal is not melted as in fusion welding. A non-ferrous alloy with a melting point above approx. 500°C and below that of the parent metal is normally used as the filler metal and is deposited without the aid of capillary action, as in brazing.BRAZING - A joining process in which, during heating, molten filler metal is made to flow by capillary action between a narrow joint preparation. In general, the melting point of the filler metal is above approx. 450°C, but is always below the melting temperature of the parent metal. A fluxing agent is usually used to promote the flow of filler metal along and around the joint.BRONZE WELDING - Term used to describe Braze Welding using a Copper rich filler metal.BUTTERING - A material preparation process in which one or two layers of weld metal are deposited on the surfaces to be joined. The buttering provides a suitable transition weld deposit for subsequent completion of the joint.BUTT WELD - A weld in which the weld lies substantially within the extension of the planes of the surfaces of one or more of the pads joined, see Fig 1 for typical examples.CDT - Controlled Droplet TransferCELLULOSE ELECTRODE - A flux coated electrode in which the covering contains at least 15 percent cellulose and up to 30 percent titania as rutile or titanium white.CO₂ WELDING - Gas Metal-Arc welding using CO₂ as the shielding gas, see preferred term - Gas Metal Arc Welding.CONSTANT VOLTAGE POWER SOURCE - An arc welding power source whose terminal voltage remains substantially constant between full load and no load conditions.
GLOSSARY
90CONTENTS
CONSUMABLES - Materials directly consumed in the making of a weld, including electrodes, flux heating and shielding gas and filler wire etc.CORED ELECTRODE - A consumable electrode having a core of flux and/or alloying ingredients. COVERED ELECTRODE - A filler metal electrode, used in arc welding, consisting of a metal core wire with a relatively thick covering of flux which provides protection for the molten metal from the atmosphere, improves the properties of the weld metal and stabilises the arc.CRATER - A depression left in the weld where the arc is broken.CONSUMABLE GUIDE WELDING - see Electroslag Welding.DEFECT - One or more discontinuities that cause non compliance of a weld.DEPTH OF FUSION - The distance from the fusion face to that point within the joint at which fusion ceases, see Fig 2.(a) and (b).DEPOSITION EFFICIENCy - (a) For manual metal arc welding electrodes, the ratio of the mass of deposited metal to the mass of the core wire consumed (excluding stubs); expressed as a percentage. (b) For continuous electrodes, the ratio of the mass of deposited metal to the mass of electrode consumed; expressed as a percentage. For 85% deposition efficiency means 85kg of weld metal was produced from 100kg of electrode metal.DEPOSITION RATE - The mass of metal deposited (excluding spatter) in a unit of time. DILUTION - The alteration of composition of the weld metal deposited from a filler metal or electrode due to mixing with the melted parent metal. It is expressed as a percentage of melted parent metal to the weld metal.DIP TRANSFER - see Short Circuiting Arc Transfer.DISCOUNTINUITy - a flaw in the weld which complies or may comply with the acceptance standard
GLOSSARY
91CONTENTS
DROOPING CHARACTERISTIC POWER SOURCE - An arc welding power source whose terminal voltage drops to a value appreciably below the open circuit voltage (O.C.V.) after the arc has been initiated.DUTy CyCLE - (a) Power Source Duty Cycle is the amount of time a welding machine can be used at a given amperage, generally expressed as a percentage of a 5 min. period, eg. 60% at 300amps means the machine can be used at 300 amps for 3 mins in every 5 mins(b) Operator Duty Cycle is the ratio of welding or cutting time to the total work time expressed as a percentage.ELECTRODE - A component of the welding circuit through which current is immediately conducted to the arc, molten slag, or base metal.(a) Non-consumable electrode - an electrode which does not provide metal eg. a Tungsten electrode.(b) Consumable electrode - an electrode which provides filler metal. ELECTRODE NEGATIVE - Arc welding using direct current in which the electrode is connected to the negative pole of the welding power source. Also referred to as, “straight polarity”. ELECTRODE POSITIVE - Arc welding using direct current in which the electrode is connected to the positive pole of the welding power source. Also referred to as, “reverse polarity”. ELECTRODE STICKOUT - In automatic and semi-automatic arc welding, the length of the electrode projecting beyond the region of current pick-up / contact tip during welding.ELECTROSLAG WELDING (ESW) - A continuous wire electrode, vertical fusion welding process in which the molten pool of metal and covering slag are confined to the joint by copper shoes. The wire feeding nozzle progresses automatically up the joint or in the case of the consumable guide variant, is melted as the weld level rises. The heat for fusion is generated by the electrical resistance of the slag bath.
GLOSSARY
92CONTENTS
FILLET WELD - A weld or series of welds of approximately triangular cross-section joining two surfaces approximately at right angles to each other in a lap joint, tee joint or corner joint. Note. The bulk of the weld metal is outside the planes made by the surfaces of the base metals, see Fig 2, (b) and (d) for typical examples.FLAT POSITION - The position in which welding is performed from the upper side of the joint and the weld face is approximately horizontal (Sometimes called downhand welding), see Fig 3, 1F and 1G positions.FLUID SLAG - A slag which flows freely during whilst molten during welding.FLUX - A substantially non-metallic material used during welding, brazing, braze welding or soldering to clean the surfaces of the joint chemically, to prevent atmospheric oxidation and to reduce impurities or float them to the surface in the form of a slag.FRIABLE SLAG - A slag that crumbles easily to aid removal.FUSION FACE - The portion of a surface, or an edge, which is to be fused (melted) in making a fusion weld, see Fig 2(a) and (b).FUSION ZONE - The area of parent metal melted as determined on the cross section of a weld, see Fig 2(a) and (b).FLUX CORED ARC WELDING (FCAW) - Arc welding using a continuous, consumable, flux cored wire (electrode) which provides the filler metal. Gas shielding, alloying addlions and slag coverage may be provided by the flux contained within the electrode. Gas shielding may or may not be required. FUSION WELDING - Welding in which similar parent metals are fused (melted) together with or without the use of a filler metal of similar composition.GAS METAL ARC WELDING (GMAW) - The preferred terminology for the process of arc welding using a continuous, consumable, solid wire (electrode) which provides the filler metal and in which shielding is obtained entirely from an externally supplied gas or gas mixture. The process is similar to and also known as MIG, MAG AND CO₂ welding.
GLOSSARY
93CONTENTS
GAS PORE - A weld cavity caused by entrapped gas.GAS TUNGSTEN ARC WELDING (GTAW) - The preferred terminology for the process of arc welding, with or without added filler metal, using a non-consumable electrode of pure or activated tungsten, shielded by an externally supplied gas or gas mixture. The process is similar to and also known as TIG, Heliarc or Argonarc welding.GAS WELDING - Welding in which the heat for welding is produced by the combustion of a gas mixture. Filler metal may or may not be used. The most popular gas combination is oxygen / acetylene however oxygen / LP gas, air / acetylene or air / LP gas are mixtures which may be used, depending on the joining process adopted.GLOBULAR TRANSFER - Metal transfer which takes place as globules of diameter substantially larger than that of the consumable electrode from which they are transferred.HARD SURFACING - Surfacing with a wear resistant material. The preferred term to hardfacing.HEAT AFFECTED ZONE (HAZ) - The portion of parent metal which has not been fused but has nevertheless been metallurgically affected by the heat of welding, brazing or cutting, Refer to Fig 2(a) and (b) for clarification.HERTZ - Hertz is often referred to as “cycles per second”. In Australia, the frequency or directional change of alternating current is usually 50 hertz.HIGH FREQUENCy - Covers the entire frequency spectrum above 50,000 Hz. Used in GTA welding for arc ignition and stabilization.HORIZONTAL POSITION - The position of welding wherein the line of the weld root is approximately horizontal, see Fig 3, 2F and 2G positions.
GLOSSARY
94CONTENTS
HyDROGEN CONTROLLED ELECTRODE - An electrode depositing weld metal containing not more than a specified quantify of diffusible hydrogen in the deposited weld metal when assessed in accordance with the appropriate standard. The category of such electrodes may be sub-divided into classifications of medium hydrogen, low hydrogen and “very low” hydrogen, each having successively lower allowable levels of diffusible hydrogen.INCLUDED ANGLE - The angle between the planes of the fusion faces of the parts to be welded, see Fig 1 for typical examples.INDUCTANCE - Inductance comes from an inductor (stabilizer). The inductor slows down the changes in current, changing the machine’s rate of response and number of short circuits per second. An inductor helps limit the amount of spatter, and generally improves the wetting out of the weld puddle.INTERMITTENT WELD - A series of welds at specified intervals along a joint, see Fig 7 (c).INTERRUN TEMPERATURE - In a multi run weld, the temperature of the weld and adjacent parent metal immediately prior to the deposition of the next weld run. Also called INTERPASS TEMPERATURE.INVERTER - Power source which increases the frequency of the incoming primary power, thus providing for a smaller size machine and improved electrical characteristics for welding, such as faster response time and more control for pulse welding.IRON POWDER ELECTRODE - A flux coated electrode in which the covering contains a high percentage of iron in the form of powder to improve deposition efficiency typically 110-130%.JOINT PENETRATION - The minimum depth of fusion into a joint, excluding reinforcement.JOINT PREPARATION - Details of the edge preparations and set up of workpieces for welding. Refer to Fig 1, (A)-(F) for examples. Ksi - (kips) kilo (1000) pounds per square inch.
GLOSSARY
95CONTENTS
LAND - The straight portion of a fusion face between the edge of the root face and: (a) the sloping face of a bevel preparation, or (b) the curved part of a J edge preparation, see Fig 1, (F).LANDING - See root faceLAP JOINT - A joint between two overlapping members approximately in the same plane, see Fig 9, (C).LEG LENGTH - The distance between the root and the toe of a fillet weld. Leg length is the dimension used to size a fillet weld to AS1101.3. Leg length is known as the ‘z’ dimension in ISO 2553, see Fig 2(d) and weld symbols section.LOW HyDROGEN ELECTRODE - see Hydrogen Controlled Electrode.MAG WELDING - “Metal Active Gas”, see Gas Metal Arc Welding.MANUAL METAL ARC WELDING (MMAW) - Arc welding with a flux covered electrode manually applied by the welder without automatic or semi-automatic replacement of the electrode. Shielding is provided only by decomposition of the electrode covering. In American terminology, known as, Shielded Metal Arc Welding (SMAW).MECHANISED WELDING - Welding with equipment which performs the welding operation under preset conditions under the constant control of a welding operator.MIG WELDING - “Metal Inert Gas”, see Gas Metal Arc Welding.MITRE FILLET WELD - A fillet weld of equal leg lengths in which the face of the weld is essentially flat.MULTIPLE ARC WELDING - Welding wherein a single process runs with more than one electrode from a single power source eg. twin arc, or a single process operates with more than one electrode from separate power sources and separate nozzles eg. tandem arc. Essentially a single weld pool is maintained throughout.
GLOSSARY
96CONTENTS
NARROW GAP WELDING - A modification of conventional automatic arc Welding of thick sections where square preparations or ‘V’ preparations with small included angles and narrow gaps are used.NON-TRANSFERRED ARC - A plasma arc struck between the tungsten electrode and the torch nozzle.OPEN-CIRCUIT VOLTAGE (OCV) - The voltage between the live output terminals of a welding power source when no current is flowing/no arc.OVERHEAD POSITION - The position in which welding is performed from the underside of the joint, see Fig 3, 4F and 4G positions.OVERLAP - Weld metal at the toe of a weld which covers the parent metal surface but is not fused to it.OXyGEN-ACETyLENE WELDING - Gas welding in which the heat for welding is produced by the combustion of an oxygen-acetylene gas mixture.PARTIAL PENETRATION - A butt weld where, by design, fusion does not extend the full depth of the joint.PASS - see Weld Run.PEENING - The mechanical working of weld metal by means of hammer blows or bombardment with shot or pellets to reduce residual stress or distortion.PENETRATION BEAD - Weld metal protruding through the root of a fusion weld made from one side only.PLASMA ARC WELDING (PAW) - A process in which the electric arc generates a hot ionised gas stream that both shields and transfers heat to the joint.POROSITy - Clustered/grouped gas pores or voids in weld metal.POROUS SLAG - A slag that has a honeycomb structure.POSITIONER - A mechanical device manually or power operated to hold, tilt or rotate the work to the desired position for welding.
GLOSSARY
97CONTENTS
POST WELD HEAT TREATMENT (PWHT) - Any thermal treatment carried out after welding.PREHEAT - The application of heat to the parent metal immediately prior to welding or cutting. PULSED ARC WELDING - Welding in which pulses of current are superimposed on a constant background current. In continuous electrode processes the pulses control metal transfer across the arc. Ideally, one pulse produces one droplet of molten metal across the arc.PULSING - Sequencing and controlling the amount of current, the polarity, and the duration of the welding arc.REINFORCEMENT - Weld metal lying outside the plane joining the weld toes.RESIDUAL WELDING STRESS - Stress remaining in a metal part of structure as a result of welding. RESISTANCE WELDING - A process in which two pieces of metal are joined by placing pressure on electrodes which are on opposite sides of the joint to be welded, maybe a spot or a continuous weld. There is no arc with this process, the resistance of the metal to the current flow is what causes fusion.RMS - Root Mean Square. The “effective” values of measured AC voltage or amperage. RMS equals 0.707 times the maximum, or peak value.ROOT FACE - The portion of a fusion face at the root which is not bevelled or grooved, Refer to Fig 1 for examples.ROOT GAP - The minimum distance at any cross-section between edges, ends or surfaces to be joined, Refer to Fig 1 for examples.ROOT OF WELD - The points as shown in cross-section, at which the back of the weld intersects the base metal surfaces, see Fig 2 (a) and (b) for examples.
GLOSSARY
98CONTENTS
SHORT CIRCUITING ARC TRANSFER - Metal transfer in which fused parts of a consumable electrode are detached in rapid succession during repeated short circuiting contacts with the molten weld pool. Also called short arc or dip transfer.SILVER BRAZING - Brazing in which a silver alloy is used as the filler metal. SILVER SOLDERING - See Silver Brazing.SIZE OF WELD - (a) Equal leg fillet weld - the length of the equal sides of the largest isoceles triangle which can be inscribed within the fillet cross-section, see leg length.(b) Unequal leg fillet weld - the lengths of the sides containing the angle of the largest triangle which can be inscribed within the fillet cross section.(c) Butt weld - the minimum depth which a butt weld extends into a joint, exclusive of reinforcement.SLAG INCLUSION - Slag entrapped in weld metal or between weld metal and base metal. Only present with welding processes that use a flux eg. MMA and SAW.SOFT SOLDERING - see Soldering.SOLDERING - A low strength joining process in which, during heating, a molten Lead-Tin filler alloy is made to flow onto and around the joint preparation. In general, the melting point of the filler metal is less than 450°C, but always below the melting temperature of the parent metal. A fluxing agent is often used to promote the flow of filler metal around the joint.SPATTER - Globules of weld metal which are expelled during welding and which do not form part of the weld.SUBMERGED ARC WELDING (SAW) - Arc welding in which a continuous, consumable, wire electrode (flux cored or solid) is used and the arc is submerged under a granular flux cover, some of which fuses to form a slag. Single or multiple electrodes in the form of solid or tubular wires or strip may be employed, attached to one or more power sources and feeding devices.
GLOSSARY
99CONTENTS
TIG WELDING - “Tungsten Inert Gas”, see Gas Tungsten Arc Welding.SPRAy TRANSFER - Metal transfer which takes pace as a rapid projected stream of droplets of diameter not larger than that of the consumable electrode from which they are transferred.STRESS RELIEF HEAT TREATMENT - Heating to, and if necessary holding at, some temperature generally below the transformation range, usually followed by slow cooling, for the purpose of reducing internal stresses.STRINGER BEAD RUN - A bead or run made without intentional weaving motion.TACK WELD - A weld (generally short) made to hold parts of a weldment in alignment until final welds are deposited.THROAT THICKNESS - (a) Actual throat thickness - the perpendicular distance between two lines (each parallel to a line joining the outer toes) one being a tangent at the weld face and the other being through the further most point of fusion penetration. Measured from the root to the weld face. Known as the ‘a’ dimension in ISO 2553.(b) Design throat thickness - the minimum dimension of throat thickness used for design purposes, refer to Fig 4, (a) and (b) for examples.TINNING - The term as applied to brazing and braze welding defines the deposition of a thin layer of fluxed filler metal onto joint surfaces in order to provide a sound and strong interface between parent metal and weld deposit.T-JOINT - A joint between the end or edge of one part and the face of the other part, The parts making an angle to one another of more Than 5 degrees up to and including 90 degrees in the region of the joint, see Fig 1, (E) and (F) for examples.TOE - The junction between a weld face and the base metal or between weld faces, refer to Fig 2, (C) and (d) for examples.
GLOSSARY
100CONTENTS
TOUCH OR SCRATCH START - An arc starting procedure for TIG (GTAW). The tungsten is touched or scratched on the workpiece; when the tungsten is lifted from the workpiece an arc is establishedTOUCH WELDING - Metal arc welding using a coated electrode, where, as a result of a characteristic of the coating, it can be kept in contact with the base metal during welding to facilitate control of arc length.TRANSFERRED ARC - A plasma arc which is struck between a tungsten electrode and the workpiece.UNDERCUT - A sharp groove at the toe of a weld flaw which is a run between the weld and the parent metal or in previously deposited weld metal caused by wastage of the underlying material, see Common Weld Defects section.VERTICAL POSITION - The position of welding wherein the line of the weld root is approximately vertical, see Fig 3, 3F and 3G positions.VISCOUS SLAG - A slag with characteristics which restrict the flow of molten slag into the weldpool during welding.VOLTAGE - The pressure or force that pushes the electrons through a conductor. Voltage does not flow, but causes amperage or current to flow. Voltage is sometimes termed electromotive force (EMP) or difference in potential.VOLTAGE REDUCTION DEVICE (VRD) - a device used to reduce the OCV of welding machines to lower and safer levelsWEAVING - Transverse movement of the end of an electrode during deposition of weld metal. WELDING PROCEDURE - The detailed methods and practices involved in the making of a weld eg. amps, volts, travel speed, material and consumable type etc.WELD FACE - The exposed surface of a weld on the side from which welding was performed, refer to Fig 2, (C) and (d) for examples.
GLOSSARY
101CONTENTS
WELD JUNCTION - The boundary between the fusion zone and the heat affected zone (HAZ) of a weld, see Fig 2, (a) and (b).WELD METAL - All metal melted during the making of a weld and retained in the weld, see Fig 2, (a) and (b).WELD RUN - The weld metal resulting from one passage of an electrode, torch or blowpipe, also called weld pass.WIRE FEED SPEED - Expressed in in/min or mm/s, and refers to the speed and amount of filler metal fed into a weld. Generally speaking the higher the wire feed speed, the higher the amperage.WORK - The material or object on which welding, brazing, soldering or cutting is carried out. Also called workpiece..
GLOSSARY
102CONTENTS
Included angle
(A) SINGLE-V BUTT JOINT
(C) DOUBLE-V BUTT JOINT
(E) SIBGLE BEVEL-T BUTT JOINT (F) SIBGLE-J T-BUTT JOINT
(B) SINGLE-U BUTT JOINT
Included angle
Angle of bevel
Root radius
Angle of bevel
Root face
Root gap
Root face
Angle of bevel
Included angle
Root face
Root gap
Root gap
(D) DOUBLE-U BUTT JOINT Root gap
Root face
Root radius
Angle of bevel
Included angle
Included angle & angle of bevel
Root face
Root gap
Included angle & angle of bevel
Root face
Root gap
Root radius
Land
GLOSSARY
103CONTENTS
Weld zone
Weld width
Weld width
Weld face
Weld face
Weld face
Toes
Leg (length)
Leg (length)
Toe
Toe
Toes
Toe
Weld zone
Fusion zone
Heat affected zone
Parent metal
Depth of fusionFusion
faceWeld
junction
Weld metal
Weld metal
Heat- affected
Zone
Fusion zone
Root of weld
(A) BUTT WELD
(C) BUTT WELD (D) FILLET WELD
(B) FILLET WELD
Root of weld
GLOSSARY
104CONTENTS
PIPE BUTT WELDS
FILLET WELDS
FLAT POSITION 1F
HORIZONTAL POSITION 2F
VERTICAL POSITION 3F
OVERHEAD POSITION 4F
Axis of Weld Horizontal
Axis of Weld Horizontal
Axis of Weld Vertical
Axis of Weld Horizontal
FLAT 1G
HORIZONTAL 2G
POSITION 5G
POSITION 6G
Pipe shall be turned or rolled while welding, Axis of Pipe Horizontal
Pipe shall NOT be turned or rolled while welding, Axis of Pipe HorizontalAxis of pipe
VerticalInclined Axis with Pipe Stationary
BUTT WELDS
FLAT POSITION 1G
HORIZONTAL POSITION 2G
VERTICAL POSITION 3G
OVERHEAD POSITION 4G
Plates Horizontal Plates HorizontalPlates Vertical Plates Vertical
45º± 5ºL
GLOSSARY
105CONTENTS
(A)
Design throat thickness
Actual throat
thickness
(B)
Actual throat
thickness
Design throat thickness
D₂
D₁ + 0.85 D₂
D₁
FIGURE 4 ACTUAL AND DESIGN THROAT THICKNESS OF TYPICAL WELDS
FIGURE 4A DEEP PENETRATION WELD AND DESIGN THROAT THICKNESS TO AS 1554.1
GLOSSARY
106CONTENTS
ADD
107CONTENTS
OXY-ACETYLENE FLAME ADJUSTM
ENT
FLAME ADJUSTMENTS FOR OXyGEN — ACETyLENE WELDINGFor oxy-acetylene welding there are essentially four main types of flame adjustments used for welding a wide variety of base metals. A neutral flame is the most common setting used for the majority of fusion welding and braze welding applications. The following diagrams are intended as a guide to the easy identification of these flame types and their use with specific base metals.
OXY-ACETYLENE FLAME ADJUSTMENT
(A) OXIDISING FLAME
Small inner cone
Bright inner cone
(B) NEUTRAL FLAME
Bright acetylene feather
(D) CARBURIZING FLAME
Small pale green feather
(C) REDUCING FLAME
For welding Copper and certain Copper based alloys
For welding Steel, Stainless Steel, Cast Iron, Aluminium and Copper etc.
For welding Aluminium and Low Alloy Steel etc.
Suitable for silver brazing, soldering and many hard surfacing applications.
108CONTENTS
Welding symbols are the shorthand of welding, they provide a concise means of relaying information on engineering drawings. Detailed information such as the type, size, orientation and finishing requirements of the weld joint can be communicated.Welding symbols do not always contain all the information required for welding. Reference is often given on the welding symbol, to a specification, process, procedure or other document which provides the necessary data to complete the welding operation.The use of welding symbols result in the following benefits:1.The complete translation of specific design requirements to the workshop; regarding such parameters as weld sizes, processes to be used, joint preparations etc thus allowing the welding task to be complete as per instruction.2.The elimination of unnecessary and incomprehensible details on drawings-when such details specify weld type, size, length, pitch etc.3.The establishment of a common understanding of design intent and welding prerequisites between designers, workshop welder/inspectors, welding engineers, Q.A./Q.C personnel and code authorities etc.4.Standardisation, within and across the welding, fabrication and construction industries.BASIC SyMBOLS There are different standards for welding symbols. The following pages are set out using the International Standard ISO2553 (Welded, brazed and soldered joints - Symbolic representation on drawings) and the Australian Standard AS1101.3 (Graphical Symbols for General Engineering - Welding and Non-Destructive Examination) which is based on the American Welding Society Standard. AWS A2.4 In AS1101.3, a clear distinction is made between the terms weld symbol and welding symbol. The term, weld symbol describes the type of weld to be deposited — see FIGURE 6A for the basic weld symbols in common use. The welding symbol is a method of representing the weld symbol on drawings and includes all the relevant information and references necessary to complete the welded joint.
WELDING SYMBOLS
109CONTENTS
WELDING SYM
BOLS
ELEMENTS OF A WELDING SyMBOL TO AS1101.3The major elements are:(a) Reference line (shown horizontally) (b) Arrow(c) Basic weld symbols(d) Dimensions and other data (e) Supplementary symbols(f) Finish symbol (g) Tail(h) Specification, process, or other references
Refer to Figure 5 for the standard location of these elements on a welding symbol.
110CONTENTS
WELDING SYMBOLS
FIG
UR
E 4:
LO
CAT
ION
OF
ELEM
ENTS
ON
A W
ELD
ING
SYM
BOL
Fini
sh s
ymbo
l
Prep
arat
ion
angl
e; in
clud
ed a
ngle
of
cou
nter
sink
for p
lug
wel
ds
Leng
th o
f wel
d
Pitc
h (c
entre
-to-c
entre
sp
acin
g) o
f wel
ds
Site
wel
d sy
mbo
l
Arro
w c
onne
ctin
g re
fere
nce
line
to a
rrow
sid
e m
embe
r of j
oint
Wel
d-al
l-aro
und
sym
bol
Ref
eren
ce li
ne
Con
tour
sym
bol
Roo
t gap
; dep
th o
f fillin
g fo
r plu
g an
d sl
ot w
elds
Des
ign
thro
at th
ickn
ess
Dep
th o
f pre
para
tion;
siz
e or
stre
ngth
for c
erta
in w
elds
Spec
ifica
tion,
pro
cess
, pr
oced
ure
or o
ther
refe
renc
e
Tail
(Tai
l om
itted
whe
n re
fere
nce
is n
ot u
sed)
Basi
c w
eld
sym
bol
or d
etai
l ref
eren
ce
Num
ber o
f spo
t, se
am, s
tud,
pl
ug o
r pro
tect
ion
wel
ds
Elem
ents
in th
is a
rea
rem
ain
as
sho
wn
whe
n ta
il an
d
arro
w a
re re
vers
ed
F
LP
A R
TS
(D)
BOTH SIDES
ARROW SIDE
OTHER SIDE
(N)
NO
TE: R
epro
duce
d w
ith p
erm
issi
on fr
om
SA
I Glo
bal u
nder
Lic
ence
111
0-c0
75
( ) ( )
( )
111CONTENTS
WELDING SYM
BOLS
Weld All Around Site Weld
Complete Penetration From One
Side
Backing Or Spacer Material
Surfacing Convex Concave
Fillet Weld
Plug Weld
Or Slot Weld
Spot Weld Or Projection
Weld
Seam Weld
Backing Run Or Backing
Weld
Surfacing Edge Weld
Stud Weld
BUTT WELD
Square Scarf V Bevel U J Flare V Flare Bevel
FIGURE 6B SUPPLEMENTARY SYMBOLS
FIGURE 6A BASIC WELD SYMBOLS
112CONTENTS
WELDING SYMBOLS
(D) COMBINED FILLET AND BUTT WELD IN T-JOINT WITH SPECIFIED ROOT GAP.
Symbol
(3)5
23
5
5Desired weld
2
(3)
(C) STAGGERED INTERMITTENT FILLET WELDS.
75-25075-250
75
250C Weld C Weld
Desired weldsC Weld C Weld
125 125
75 75 75
(B) UNEQUAL DOUBLE-FILLET WELDS.
612
SymbolDesired weld12
126
6
(A) SINGLE-FILLET WELD
8
SymbolDesired weld
8
8
113CONTENTS
WELDING SYM
BOLS(A) PARTIAL PENETRATION, SINGLE-V BUTT WELD
(B) FULL PENETRATION
690°6 (10)
Desired Weld (D=10) Symbol
90°
Desired WeldNote
overlapSymbol
Note: The total design throat thickness (D)=22mm
90°
5
5
22
(D=12)5 (12) 90°
90°5 (12)
See Note
(D=12)90°
Desired Weld
Symbol
Note: The total design throat thickness cannot be greater than plate thickness (10mm)
See Note
(4)(7)
2
60°
(4)
60°
10
(7)
2
Symbol
(D) COMBINED FILLET AND BUTT WELDS
970°
70°9
6 (14)6 (14)
Desired Weld9 9
6 6
25
70°70°
14 14
Note overlap
(C) SINGLE BEVEL BUTT WELD WITH ROOT OPENING
114CONTENTS
WELDING SYMBOLS
Symbol
See Note
NOTE: See drawing for dimensions and orientation
1245°
45°
12
Section of desired weld
Symbol
Desired weld 33
(A) SURFACE WELD
(B) PLUG WELD (D) SEAM WELD
115CONTENTS
WELDING SYM
BOLS
(D) SEAM WELD
(C) SPOT WELD
SymbolRSW - Resistance spot weldingDesired weld Section A-A
24 2412 12
6
12RSW6 24
(5)A
A
24 24
+ + + + +
Min acceptable shear strength 35 N/mm₂
Desired weld Section A-A SymbolEBW - Electron- beam welding
A
A
EBW35 N/mm₂
116CONTENTS
A GUIDE TO INTERPRETING THE AUSTRALIAN / NEW ZEALAND STANDARD CLASSIFICATION FOR LOW CARBON STEEL MMAW ELECTRODESThe Australian/New Zealand Standard 4855 for Manual Metal Arc Welding of non-alloy and fine grain steel is identical to ISO 2560 standard, and is to supersede AS/NZS 1553.1. Under the new AS/NZS 4855 standard, covered electrode can be classified based upon either yield strength and 47J minimum impact energy known as method -A, or tensile strength and 27J minimum impact energy known as method -B, which the second method is widely accepted in Australian market. For details of the complete range of classifications, please consult AS/NZS 4855.
AS/NZS 4855-B - E49 16 A U H10
Compulsory clalssification designatorsSpecification numberClassification by tensile strength and 27J CVN requirementCovered electrodeDeposit metal tensile strength. “49” indicates minimum tensile strength of 490 N/mm
₂,
other designator like “43, 55 or 57” is often usedType of flux coatingCondition of heat treatment. The symbols “A” and/or “P” are used to indicate the as-welded and/or heat treated condition/sOptional supplemental designatorsDiffusible hydrogen. “H5, H10,H15” is used to indicate a maximum diffusible hydrogen content of “5,10, and 15 ml/100g of deposited metal, respectively
Optional supplemental designators
47J impact energy at the normal
27J test temperature has also been met.
ELECTRODE CLASSIFICATIONS
117CONTENTS
ELECTRODE CLASSIFICATIONS - MANUAL METAL ARC WELDING ELECTRODES
A GUIDE TO INTERPRETING THE AMERICAN ANSI / AWS SPECIFICATION FOR CARBON STEEL ELECTRODES FOR SHIELDED METAL ARC WELDINGThe ANSI/AWS A5.1 Specification for Shielded Metal Arc Welding details classifications covering general purpose, iron powder and low hydrogen electrodes. The classification system consists of an alphanumeric group followed by a group of optional designators. Please consult ANSI/AWS A5.1 for further details on the range.
1ST GROUPMinimum Weld Metal Strength
Tensile Yield Elongation ksi ksi %
60 48 22
70 58 22
2ND GROUPWelding Position, Welding Current and Coating Type ie EXX12, EXX24 and EXX18For details refer to the Usability Digits of Major Classifications on next page.
3RD GROUPOptional Designator for Improved Impact ToughnessE7016-1=20 ft.lb @ -50°F av.min.E7018-1=20 ft.lb @ -50°F av.min.E7024-1=20 ft.lb @ -0°F av.min.
3RD GROUPOptional Diffusible Hydrogen Designator indicates that the low hydrogen electrode meets the requirements of the diffusible hydrogen test.
H4 <4mL/100g) of deposited weld metalH8 <8mL/100g) of deposited weld metal H16 <16mL/100g) of deposited weld metal
3RD GROUPOptional Coating Absorbed MoistureDesignator indicates that the coating of a low hydrogen electrode is moisture resistant after being exposed to an environment of 80°F and 80% relative humidity for a period of not less than 9 hours. Maximum specified moisturecontents are detailed in Table 10 of thespecifications.
E XX XX XHXRELECTRODE
3RD GROUP Optional designators
118CONTENTS
USABILITy DIGITS OF MAJOR CLASSIFICATIONS INDICATING TyPE OF POSITIONS AND CURRENT TyPE REQUIREMENTS
USABILITy CLASSIFICATION
WELDING POSITIONS
TyPE OF CURRENT AND POLARITy
TyPE OF COVERING AND
SLAG
10 F,V,OH,H D.C. electrode positive High cellulose
11 F,V,OH,H A.C. or D.C. electrode positive High cellulose
12 F,V,OH,HA.C. or D.C
electrode positive or negative
High titania viscous slag
13 F,V,OH,HA.C. or D.C
electrode positive or negative
High titania viscous slag
14 F,V,OH,HA.C. or D.C
electrode positive or negative
Low iron powder
15 F,V,OH,H D.C. electrode positive
*Hydrogen controlled
16 F,V,OH,H A.C. or D.C. electrode positive
*Hydrogen controlled
18 F,V,OH,H A.C. or D.C. electrode positive
*Hydrogen controlled basic, low iron powder
19 F,V,OH,HA.C. or D.C
electrode positive or negative
Limenite
20 F,H, Fillet A.C. or D.C. electrode positive High iron oxide
24 F,H, FilletA.C. or D.C electrode
positive or negativeHigh iron
oxide titania
27 F,H, FilletA.C. or D.C
electrode positive or negative
*Hydrogen controlled powder
iron oxide
28 F,H, Fillet A.C. or D.C. electrode positive
*Hydrogen controlled low iron
powder basic46 F,V-down
OH, HA.C. or D.C.
electrode positive*Hydrogen
controlled basic
48 F,V-down OH, H
A.C. or D.C. electrode positive
*Hydrogen controlled basic, low iron powder
99 As specified
As Specified by manufacturer As Specified by
NOTE: The abbreviations, F, V, V-Down, OH, H, and H-FiIIet indicate the following welding positions: F-Flat, V-Vertical, V-down - Vertical down, OH-Overhead, H-Horizontal, H-fillet-Horizontal fillet. *Unless otherwise indicated the classification digits have wide usage amongst the Australian AS, USA (AWS), Canadian (CSA), Japanese (JIS) and the new draft ISO Standards. European Economic Community Standards (CEN). As national standards are subject to regular revision these situations could alter.
ELECTRODE CLASSIFICATIONS
119CONTENTS
USABILITy DIGITS OF MAJOR CLASSIFICATIONS INDICATING TyPE OF POSITIONS AND CURRENT TyPE REQUIREMENTS
A GUIDE TO INTERPRETING THE AUSTRALIAN STANDARD CLASSIFICATION FOR HIGH STRENGTH STEEL MMAW The Australian/New Zealand Standard 4857 for Manual Metal Arc Welding of high-strength steesl is identical to ISO 18275 standard, and is to supersede AS/NZS 1553.2. Under the new AS/NZS 4857 standard, covered electrode can be classified based upon either yield strength and 47J minimum impact energy known as method -A, or tensile strength and 27J minimum impact energy known as method -B, which the second method is widely accepted in Australian market. For details of the complete range of classifications, please consult AS/NZS 4857.
AS/NZS 4857-B - E62 18-G A U H10
Compulsory clalssification designatorsSpecification numberClassification by tensile strength and 27J CVN requirementCovered electrodeDeposit metal tensile strength. “62” indicates minimum tensile strength of 620 N/mm
₂,
other designator like “59, 69, 76, 78 or 83” is often usedType of flux coatingAny other agreed chemical compositionCondition of heat treatment. The symbols “A” and/or “P” are used to indicate the as-welded and/or heat treated condition/sOptional supplemental designatorsDiffusible hydrogen. “H5, H10,H15” is used to indicate a maximum diffusible hydrogen content of “5,10, and 15 ml/100g of deposited metal, respectively
Optional supplemental designators
47J impact energy at the normal
27J test temperature has also been met.
ELECTRODE CLASSIFICATIONS - MANUAL METAL ARC WELDING ELECTRODES
120CONTENTS
A selection of designators for nominal alloy weld metal compositions widely used in ISO, Australian (AS) European and American (AWS) systems of classification for electrodes and weld metal. See the appropriate Standard for the fully specified composition requirements and the location(s) of the designator in the classification.
ALLOy GROUP DESIGNATOR NOMINAL COMPOSITION REQUIREMENTS
Carbon - Molybdenum A1 0.40 - 0.65Mo
Chromium - Molybdenum Steels
B1 B2 or B2L• B3 or B3L B6 (5Cr)#
B7, B7L (7Cr)# B8, B8L (9Cr)#
0.50Cr 0.5Mo 1.25Cr 0.5Mo 2.25Cr 0.5Mo
5Cr 1Mo 7Cr 5Mo 9Cr 1Mo
Nickel SteelsNi1, Ni3L or C3
Ni2, Ni2L or C1, C1L Ni3, Ni3L or C2, C2L
NM
1 Ni 2.5 Ni 3.5 Ni
1 Ni 0.5MoManganese
Molybdenum SteelsD1 D2
1.5 Mn 0.35 Mo 1.8 Mn 0.35 Mo
Mil. Spec. Type Low Alloy High Tensile Series, AS 1553.2 and AWS A5.23
Examples
M (eg. E7618-M) M1, M2, M3, M4
eg. F9A2-ECM1-M12)
A series of Mn-Ni-Cr-Mo specified compositions
for various strength levels Refer to standards
Other Low Alloy Steels of specified composition (SAW
and FCAW standards
EF1-EF6 series F1-F6 series K1-K7 series
SAW Electrodes• SAW Weld metals•
FCAW Weld metals• Refer to AWS Standards
Weathering Steels (Corten - Austen
etc.)W, W1, W2 Ni-Cr-Cu steels
typically 0.5Ni-0.5Cr 0.5Cu
Alloy unspecified G, GSComposition exceeds
minimum requirements in at least one specified element.
• L variants are a low carbon version (usually 0.05 % max) of the standard alloy carbon range # Alternative designators in some AWS standards.
ELECTRODE CLASSIFICATIONS
121CONTENTS
DESCRIPTION OF MMAW ELECTRODE TyPES AS CLASSIFIED By NATIONAL AND INTERNATIONAL STANDARDSEXX10 AND EXX11 TyPES (AUSTARC 11) Electrodes of these classifications have thin coatings which contain at least 15% cellulose and up to 30% titania as rutile or titanium white. The group is characterised by a forceful, deeply penetrating, spray type arc with fairly high spatter. A voluminous gas shield is produced, as a result of decomposition of the cellulose materials in the arc region, which protects the weld metal from atmospheric contamination. High weld metal quality (including radiographic soundness) is achieved in all welding positions and the electrodes operate satisfactorily from AC or DC (electrode positive) power sources for EXX11 types and from DC (electrode positive) only for EXX10 types.EXX12 TyPE (AUSTARC 12P) Electrodes of this classification have thin coatings which contain a high proportion of titania as rutile, ilmenite or titanium white. The group is characterised by a quiet, medium penetrating arc with low spatter. The slag is viscous, full covering and easily removed when cool. General ease of handling in all welding positions and an ability to bridge gaps in work having poor fit-up are features common to this electrode type. Due to the viscous slag, many of these electrodes are suitable for use in the vertical down position. In Europe, rutile-cellulose is a common designation, while in the AWS classification sodium binders are specified.EXX13 TyPE (AUSTARC 13S) Electrodes of this classification are similar in formulation to the EXX12 group. However, basic materials are added to increase the fluidity of the slag. Similar to EXX12 electrodes, they operate with a quiet medium-penetrating arc with low spatter. The slag is fluid, full covering and easily removed when cool. The fluid slag makes this electrode ideal for fillet welding in the flat or horizontal, vertical-up and overhead welding positions. Potassium binders give improved arc stability and are specified for the AWS classification. (cont. over)
ELECTRODE CLASSIFICATIONS - MANUAL METAL ARC WELDING ELECTRODES
122CONTENTS
EXX14 TyPE Electrodes of the EXX14 type have medium thick coatings, containing a high proportion of titania and sufficient iron powder to ensure a deposition efficiency of 105 - 130%. They operate with a smooth, medium penetrating arc with low spatter. The slag is fairly viscous, full covering and easily removed when cool. These electrodes are suitable for both single-run and multiple-run welds in all positions and can be used to bridge gaps in work having poor fit-up. Due to the viscous slag, many of these electrodes are suitable for use in the vertical down position.EXX15 TyPE The original basic low hydrogen type is suitable for use on DC electrode positive only. Similar characteristics and application to EXX16 and EXX18.EXX16 TyPE (AUSTARC 16TC) These electrodes have a chemically basic slag, generally of the limestone-fluoride type similar to the EXX15 group but with the ability to run on AC as well as DCEP Higher arc stability is provided by the use of potassium silicate binders and other potassium bearing materials in the coating. Coating materials are inorganic, selected for minimal combined moisture and coverings are baked at a high temperature to provide low hydrogen in the arc atmosphere. Basic coated electrodes are noted for their tough low oxygen weld metals and suitability for welding a wide range of carbon and low alloy steels. The fluid full covering slag gives slight convex beads and excellent all position welding capabilities.EXX18 TyPE (AUSTARC 18TC AND AUSTARC 77) Similar coating type and operational characteristics to the EXX16, but the somewhat heavier coating contains sufficient iron powder to give increased deposition efficiency to 105-130%. This still permits all position welding on AC or DCEP but the presence of the iron powder also improves metal transfer and operational characteristics. The EXX18 group are widely used in a range of steels and critical applications where weld quality is the main requirement, particularly in all position welding. The group also serves as the major basic group for a wide range of low alloy high tensile electrodes.
ELECTRODE CLASSIFICATIONS
123CONTENTS
EXX19 TyPE The slag type is based on the titanium oxide-iron oxide mineral, ilmenite, and therefore has similarities to the EXX12 & 13 types but with some distinct differences. Characterised by fluid slag and forceful arc it gives Grade 1 radiographic standards, good ductility and toughness down to -20°C.EXX20 TyPE A high iron oxide-manganese oxide/silicate type slag giving a spray type arc and smooth flat to concave welds. Easily removed honeycomb type brittle slag.EXX24 TyPE (AUSTARC 24) Similar slag type to EXXl2, 13 & 14 but with larger proportion of iron powder and heavier coating, approximating some 50% of electrode weight. High deposition rate, high speed runs and high efficiency in the 130 to 150% class. EXX27 TyPE Electrodes of this type have thick, heavy coatings which contain a high proportion of iron and manganese oxides and/or silicates, and sufficient iron powder to ensure a deposition efficiency greater than 130%. They operate with a vigorous, spray type arc with medium to deep penetration. The slag is fluid, voluminous, full covering and when cool well honeycombed on the underside, friable and easily removed. Electrodes of this type are suitable for high speed welding applications in the flat and horizontal-fillet positions where good penetration and easy deslagging are essential.EXX28 TyPE A heavy coated high iron powder version of the basic coated lime fluorspar EXX18 electrode. The coating usually contains approximately 50% of the weight of the electrode, restricting its use to the flat and horizontal fillet positions.EXX46 AND EXX48 TyPES Electrodes of the EXX46 and EXX48 classifications have respectively the same usability, composition and design characteristics as EXX18, except for excellent vertical-down performance.
ELECTRODE CLASSIFICATIONS - MANUAL METAL ARC WELDING ELECTRODES
124CONTENTS
A GUIDE TO INTERPRETING THE AUSTRALIAN STANDARD CLASSIFICATION FOR FERRITIC STEEL GMAW ELECTRODESThe standard AS/NZS 2717.1 for Gas Metal Arc Welding Ferritic Electrodes is the only AS/NZS standard for semi-automatic welding process that has not been superseded by ISO standards. Previous FCAW stand AS 2203.1 has been supersended by AN/NZS ISO 17632, 17634 and 18276. The system of classification consists of three alphanumeric groups separated by the hyphens, which may be summarised as follows. For full details of the complete range of classifications, testing, chemical, mechanical, radiographic and other requirements of the standard, please consult AS/NZS 2717.1.
AS 2717.1 ES6 - GC - W 50 3 A H
2ND GROUPType of external shielding gas First digit is G for gas.C = shielding with welding grade carbon dioxideM = shielding with mixed gases.I = shielding with inert gas.
3RD GROUPWeld metal properties.A indicates as-welded condition, or P after post weld heat treatmentH indicates hydrogen controlled weld metal.
AS WELDED TENSILE PROPERTIES*
Weld Metal Classification
Min. Tensile Strength
Min.Yield Strength
Min. Elongation on 5d
W50XH 500 MPa 360 MPa 22%W559H 550 MPa 470 MPa 19%For complete details refer to AS / NZS 2717.1
FIRST GROUP - ES = Electrodes, Solid, followed by a numerical or alphanumerical code which define the chemical composition of the wire. For example
Wire Class. C Mn Si Other
ES3 ES4 ES5 ES6 ES7
.06-.15
.07-.15
.06-.19
.06-.15
.07-.15
.90-1.40 1.00-1.50 .90-1.40 1.40-1.85 1.50-2.00
.45-.75
.60-.85
.30-.60
.80-1.15
.50-.80
- - .50-90AI- -
ESB2L ESNi2 ESD2 ESM3 ESMG ER70S-G
Low carbon Cr-Mo Alloy 2.5 Ni Alloy Mn-Mo-Alloy Mn-Ni-Cr-Mil Spec Alloy o specified composition
Refer AS / NZ 2717 for full range of classifications and compositions.
The third digit, for carbon steel electrodes, indicates the Impact energy grade number as specified below. For low alloy, ferritic steel electrodes, the third digit is 9 and the minimum average CVN impact values are as stated in AS / NZS 2717.1.Impact Energy Grade #
Min. Avrge Charpy ‘V’ notch impact value
Z Not requiredA 47J at +20°0 47J at 0°2 47J at -20°4 47J at -40°6 47J at -60°
ELECTRODE CLASSIFICATIONS
125CONTENTS
A GUIDE TO INTERPRETING THE ANSI /AWS GAS SHIELDED ARC WELDING FILLER METAL SPECIFICATIONThe ANSI / AWS A5.18 specification for Carbon Steel Electrodes and Rods for Gas Shielded Arc Welding includes Metal Cored electrodes formerly classified in ANSI / AWS A5.20 and an example is illustrated to acquaint the user with information provided by the specification.While the full range of classifications can be employed with GMAW only solid rods should by used for GTAW (TIG) and PAW processes. For full details of all test requirements, radiographic standards, manufacturing tolerances, packaging etc refer to the latest edition of the standard.
E R 7 0 S - 6 H 4E R 7 0 C - 6 M H 4
LETTER DESIGNATORSE = ElectrodeR = RodS = Solid WireC = Composite Metal Cored WireM = Mixed Shielding GasC = Cabon Dioxide Shielding Gas
OPTIONAL DESIGNATORS
Indicate diffusible weld metal hydrogen contentH4 = <4mL/100g)H8 = <8mL/100g)H16 = <16mL/100g)
AS WELDED TENSILE PROPERTIES*
Weld Metal Classification
Min. Tensile Strength
Min. Yield Strength
Min. Elongation %psi MPa psi MPa
ER 70-X 70,000 480 58,000 400 22
ER 70-XX 70,000 480 58,000 400 22
*Properties as detailed are appliccable for all classifications
DEPOSITION PROCESS
Class C Mn Si Other
ER70S-2 ER70S-3 ER70S-4 ER70S-5 ER70S-6 ER70S-7
0.07 0.06-0.15 0.07-0.15 0.07-0.19 0.06-0.15 0.07-0.15
0.90-1.40 0.90-1.40 1.00-1.50 0.90-1.40 1.40-1.85 1.50-2.00
0.40-0.70 0.45-0.75 0.60-0.85 0.30-0.60 0.80-1.15 0.50-0.80
Ti, Zr, AI 0.50 Cu 0.50 Cu Cu, Al 0.50 Cu 0.50 Cu
ER70S-G Agreed between the supplier & customer
WELD METAL ANALySISE70C-3X 0.12 1.75 0.90 0.50 CuE70C-6X 0.12 1.75 0.90 0.50 CuE70C-G Agreed between the suppler & customer E70C-GS(X) Agreed between the suppler & customerSingle figures are maximum G- general, GS = general, single pass only
DEPOSITION PROCESS
Class Ftlb JER70S-2 ER70S-3 ER70S-4 ER70S-5 ER70S-6 ER70S-7 ER70S-G ER70S-3X ER70S-6X ER70S- G(X) ER70S- GS(X)
20 @ -20°F 20 @ 0°F N/A N/A 20 @ -20°F 20 @ -20°F As Agreed 20 @ 0°F 20 @ -20°F As Agreed N/A
27 @ -29°F 27 @ -18°F N/A N/A 27 @ -29°F 27 @ -29°F As Agreed 27 @ -18°F 27 @ -29°F As Agreed N/A
ELECTRODE CLASSIFICATIONS - GAS METAL ARC WELDING FERRITIC STEEL ELECTRODES
126CONTENTS
EXAMPLES:1. AWS A5.18: ER70S-6 Indicates a solid wire electrode and filler rod. Mechanical testing of an all weld metal test plate, deposited under CO₂ shieldng will give min. 72 ksi (500 MPa) tensile strength, 60 ksi (420 MPa) yield strength, min. 22% elongation on 4D and a charpy impact strength of 27J at - 29°C. The weld will meet radiographic requirements. The wire meets a specffied chemical analysis, dimensional requirement and some additional testing where supplied as a filler rod only.2. AWS AS.28: ER80S-B2 Indicates a solid wire electrode and filler rod. Mechanical testing of an all weld metal deposit, welded under Argon+1-5% O₂ gas shielding is carried out after PWHT at 620°C. The requirements are a min. tensile strength of 80 ksi (550 MPa) yield strength at 0.2% offset of 68 ksi (470 MPa) and an elongation 19% min. on 4D. It has to meet radiographic soundness but no impact properties are specified for this alloy. The wire, a nominal 1.25% Cr/0.5% Mo alloy must meet a specific composition analysis, dimensional requirements and some addtional requirements for supply as a filler rod only.3. AWS A5.28: E80C-B2 A cored or composite electrode the dropping of the R indicates it meets the specification for an electrode only. It meets all the weld metal soundness and mechanical requirements specified in example 2 above but the B2 alloy specific composition is confirmed by anaysis of the deposited weld metal.
ELECTRODE CLASSIFICATIONS
127CONTENTS
A GUIDE TO INTERPRETING THE AS/NSZ ISO SPECIFICATIONS FOR FLUX CORED ARC WELDINGThe new AS/NZS ISO 17632 standard is a series of adopted ISO standards to cover Flux Cored Arc Welding (FCAW) electrodes for Non-alloy and fine grain steels. The following provides a brief introduction into the classification systems, and the standard series cover different electrode range. For full classification details, please consult the latest standards. AS/NZS ISO 18276: high strength Steels AS/NZS ISO 17634: creep resisting steels AS/NZS ISO 17633: Stainless steels.
ELECTRODE CLASSIFICATIONS - FLUX CORED ARC WELDING ELECTRODESAS/NZS ISO 17632-B - T 55 4 T5-1 M A-N2-U H5Optional supplemental designators47J impact energy at the normal 27J test temperature has also been met.
Diffusible hydrogen. “H5,H10,H15” is used to indicate a maximum
diffusible hydrogen content of “5, 10 and 15 ml/100g of deposited metal,
respectively.
Classification by tensile strength and 27J CVN requirementTubular cored electrode Minimum tensile strength meets 550MPa Tested temperature @ -40°C meets the minimum impact properties of 27JUsability designator. T5 indicates Lime-flouride flux, and generally referes to Basic flux systemWelding position. 1 indicates all positional; and 0 - downhand only.Shielding gas M indicates mixed gasesIndicates tested in the as welded conditionchemical composition designator, N2 indicate 2%Nil in deposited weld metal
Compulsory clalssification designators
128CONTENTS
A GUIDE TO INTERPRETING THE ANSI / AWS SPECIFICATIONS FOR FLUX CORED ARC WELDINGThe ANSI / AWS A5.20 (Plain Carbon) and A5.29 (Low AlIoy) Electrode specifications have similar classification systems. They are shown in a combined form to acquaint the user with the information provided by the classification. For full details of all test requirements, radiographic standards, manufacturing tolerances, packaging, weld metal compositions etc., please consult the latest edition of the appropriate specification
WELD METAL COMPOSITIONElectrodes to A5.20 have a weld metal composition requirement that ensures they are plain carbon steels and do not employ an alloy suffix. Electrodes to A5.29 have specific compositions and employ the designations as shown in Table 4 of this section (Page 126). These include the A1, B2, B3, Ni1, Ni2, D1, D2, D3, K1 to K7: W types. For full details of the chemical compositions, refer to Table 1 of A5.29
IMPACT STRENGTHThe A5.20 classification EXXT-1, T-5, T-6 & T-8 have min. impact requirements shown in the usability table. In A5.29 the requirement for impact testing on as-welded or PWHT specimens and the test temperature for min. 20ft-lb (27J) is specified in Table 4 against the complete classification eg. E81T1-Ni2 AW-40°F (40°C)E80T5-Ni2 PWHT - 75°F (-60°C)
USABILITy AND PERFORMANCENote: A5.20 Classifications shown here are T-X, A5.29 as TX. For details of usability and performance refer to Page 135.
POSITIONAL CAPABILITIES“0” = Flat and Horizontal “1” = All Positions
TUBULARFlux Cored Electrode
ELECTRODE
WELD METAL STRENGTH DIGITSThe strength digits ‘6’ and ‘7’ in A5.20 and ‘6’, ‘7’, ‘8’, ‘9’, ‘10’, ‘11’ and ‘12’ in A5.29 represent 0.1 of the min. tensile strength in ksi, eg. ‘8’=80ksi (550MPa) ‘11’=110ksi (760MPa)Each strength group has a min. yield strength, 12ksi (10ksi for ‘6’ in A5.29) below the min. tensile strength and a min. elongation requirement.
AWS A5.20 E X X T - XAWS A5.29 E X X T X - X
ELECTRODE CLASSIFICATIONS
129CONTENTS
USABILITy AND PERFORMANCE CAPABILITIES CLASSIFICATIONT-1, T1 - Almost invariably a Rutile (Titania) based flux imparting smooth running, spray transfer, low spatter using CO₂ shielding, electrode positive. Some designed for out of positioning welding when Argon/CO₂ mixtures may be preferred. Most popular group.E7XT-1 - Has impact requirement of 20ft-lb (27J) at 0°F. (-18°C).T-2 - Essentially similar to T-1 but higher Mn and Si for improved single pass welding over mill scale, rust or on rimmed steel in the flat and horizontal fillet positions.T-3 - Self shielded, high speed single pass welds on sheet metal up to 5mm thick using DCEP.T-4, T4 - Self shielded, very high deposition rate with globular transfer on DCEP. Low penetration, desulphurised welds, resistant to cracking, can be used on poor fit up. Suitable single or multiple run in flat and horizontal positions.T-5, 15 - Lime Fluoride basic flux for high toughness and crack resistance using DCEP and CO₂ shielding. Argon/CO₂ mixtures may be preferred for some applications.Globular transfer, convex beads (similar E7016-18 electrodes) for critical flat and horizontal fillet welds. Impact requirement for EXXXT-5 is 20ft-lb. (27J) at -20°F (-29°C).T-6 - Self shielded, DCEP, spray type transfer for single or multiple pass welding in flat or horizontal positions. Provides good low temperature impact properties 20ft-lb (27J) at -20°F (-29°C) and root penetration, easy slag removal in flat and horizontal positions. Single or multipass welds,T-7 - Self shielded, DCEN, single and multipass pass welds with desulphurising slag giving crack resistant welds. Larger sizes give high deposition rates, small sizes provide all position welding.T-8, T8 - Self shielded, DCEN, all position welding, single and multipass. The slag system produces good impact properties (T8 min. 20ft-lb (27J) at -20°F (-29°C). and a desulphurised weld metal resistant to weld cracking.T-10 - Self shielded, DCEN, single pass welding at high travel speeds in the flat, horizontal, down slopes (to 20°).T-11 - Self shielded, DCEN, with a smooth spray arc, General Purpose electrodes for single and multipass welding in all positions and high travel speed welding.T-G, TX-G - A classification for new multipass electrodes not covered by any of the above.T-GS - A classification for new single pass electrodes not covered by any of the presently defined classifications.
ELECTRODE CLASSIFICATIONS - FLUX CORED ARC WELDING ELECTRODES
130CONTENTS
STANDARDS AUSTRALIA AND THE ANSI/AWS SPECIFICATION STANDARDS FOR STAINLESS STEEL AND ALUMINIUM ALLOy ELECTRODESThe new AS/NZS standards offer two classification systems, which are according to nominal composition (-A) and alloy type (-B)respectively. In Australia market, the B system is widely accepted and substantially the same to AWS standards.The following provides a brief introduction into the classification systems employed and the information they provide to the user. These are:ANSI/AWS A5.4 - Stainless Steel MMAW ELECTRODES - AS/NZS 4854 ANSI/AWS A5.9 - Stainless Steel GMAW ELECT. - AS/NZS ISO 14343 ANSI/AWS A5.10 - Al./Al. Alloy GMAW - AS/NZS ISO 18273For full details of the manufacturing tolerances, testing requirements, packaging, chemical composition and other aspects of the standard specifications, please consult the latest edition of the appropriate above standard.1. CORROSION-RESISTING CHROMIUM AND CHROMIUM-NICKEL STEEL ELECTRODES (a) MMAW COVERED ELECTRODES - AS/NZS 4854-B and ANSI/AWS A5.4 The basis of these classifications is the chemical composition and mechanical properties of the deposited metal, the coating type and current.The system of designation is as follows:
COATING TIME-15 DC Electrode Positive Lime Type-16 AC or DCEP Lime or Rutile Type-17 AC or DCEP Acid Rutile Type•-25 DC EP Heavy Coated Lime Type•-26 AC or DCEP Heavy Coated Rutile Type •
An alphanumeric system of alloy designation almost universally employed. eg. 308, 316L, 309Mo, 310 etc.
X X X - XELECTRODE
EALLOy DESIGNATION
The -17, -25, and -26 suffixes are recent additions to the classifications. The -17 is a more siliceous version of the -16. The -25 and -26 coatings are designed for flat and horizontal welding and are generally “synthetic” versions using lower alloyed or plain carbon core wires. (b) GMAW ELECTRODES The Standards Australia AS/NZS ISO 14343 for gas metal arc electrodes bases its classification of the electrode range on the composition of the solid wire. This is followed by the commonly employed alphanumeric designation of the chromium nickel steel, the actual composition of which is specified in the standard.
ELECTRODE CLASSIFICATIONS
131CONTENTS
No mechanical properties are specified. The ANSI/AWS A5.9 Specification covers solid wires, and metal cored, stranded or composite wires and again bases its classification on the chemical composition of the solid wires or a fused sample of the cored or composite wires. This specification covers electrodes or filler metals for GMAW, GTAW or SAW processes. For this reason, no mechanical testing requirements are specified. The designations in the classifications differ slightly.2. ALUMINIUM AND ITS ALLOyS — GMAW ELECTRODESThe AS/NZS ISO 18273 and ANSI / AWS A5.10 standards specifications for Aluminium and Aluminium alloys GMAW electrodes (and in the case of A5.10, filler rods) both base their classification on the chemical composition of the solid wire. The alloy is designated by an internationally accepted system involving a four digit number, the first indicating the aluminium content or the main alloying element, Of these, the following are employed in welding as electrodes or filler rods, viz.1XXX = Aluminium content 99% min. 2XXX = Copper is main alloying element 4XXX = Silicon is main alloying element. 5XXX = Magnesium is main alloying element.The second digit indicates modifications to the basic alloy or impurity limits while the third and fourth digits identity the aluminium alloy or indicate the aluminium purity.A prefix of E indicates an electrode wire in the Australian Standard and ER indicates Electrode/Filler Rod in the ANSI / AWS System.Example:- E5356 and ER5356 are classifications for a popular 4.5-5.5% Mg aluminium alloy with minor additions of Mn, Cr and Ti and limits on Si,Fe,Cu,Zn and others.Modifying the alloy designation to 5556 indicates mainly a rise in Mn level from approximately 0.1 to 0.5-1.0% and marginally higher “aim” value for Mg and Zn (0.1 max to 0.25 max.), which results in a higher tensile strength deposit.Alloy E5183 and ER5183 has become a popular filler metal used in the fabrication of marine passenger, car ferry and pleasure craft. It is a modification of the 5356 alloy with increases in Si, Mn and Zn and is particularly suitable for welding 5083 alloy in marine applications because of the higher tensile strength weld metal.The composition of the wires in both standards are almost identical with slightly narrow tolerance on Beryllium content from AWS standard and an electrode fully meeting the requirements of AWS A5.10 will be deemed to be qualified to the AS/NZS ISO 18273.
ELECTRODE CLASSIFICATIONS - MANUAL METAL ARC & GAS METAL ARC WELDING
132CONTENTS
133CONTENTS
ELECTRODE CLASSIFICATIONSA GUIDE TO INTERPRETING THE AUSTRALIAN ANDNEW ZEALAND SPECIFICATION FOR REPAIR AND HARDFACING CONSUMABLEThe AS/NZS 2576 Welding Consumable for Build-Up and Wear Resistance is based on the Welding Technology Institute of Australia (WTIA) Technical Note 4. The standard classifies consumables by alloy type, deposit hardness, welding process and consumable type. For complete details of the consumable classifications please refer to the latest edition of AS/NZS 2576.
2ND DIGIT = ALLOy TyPEIn combination with the first digit it indicates the specific type of alloy whithin a group. 23XX = Austenitic chromium-carbide iron
2 3 6 0 - A 4
1ST = ALLOy GROUP1 = Steels2 = Chromium white irons3 = Tungsten carbide composites4 = Cobolt alloys5 = Nickel alloys6 = Copper alloys
3RD & 4TH DIGIT = DEPOSIT HARDNESSIndicates mean undiluted deposit hardness prior to any heat treatment or work in service. Hardness is expressed in Rockwell C (HRC) units. ie. XX60 = 60-65 HRC
DEPOSITION PROCESSThe letter indicates the welding process.A = Manual Metal Arc WeldingB = Submerged Arc Welding and Flux Cored Arc WeldingC = Gas Welding
5TH DIGIT = CONSUMABLE TyPEA1 = Tubular electrode no alloy contribution from the flux coating.A4 = Low carbon steel core wire alloy additive flux coating.B1 = Tubular wire no alloy. contribution from the flux coating.B5 = Gas shielded tubular flux core wire.B7 = Self shielded tubular flux core wire.C1 = Filler Rod.C3 = Powder.
ELECTRODE CLASSIFICATIONS - REPAIR AND HARDFACING
134CONTENTS
A GUIDE TO INTERPRETING THE AUSTRALIAN STANDARD CLASSIFICATION FOR SUBMERGED ARC WELDING ELECTRODES AND FLUXESThe Australian Standard for electrodes and fluxes for SAW, AS 1858.1 (C and C-Mn Steels) published by Standards Australia and its classification system has strong similarities with the ANSI / AWS SAW specifications, particularly in relation to electrode and alloy weld metal designations and compositions. The following provides a guide to the designations and layout of the classification systems (shown in combined form) to acquaint the user with the information provided by the classifications. For full details of the complete range of classification testing requirements, chemical, mechanical, radiographic and other requirements of the standard, consult AS 1858.1.EXAMPLE: AS1858.1 EL12-FMM-W404 is a complete designation. It refers to a flux and wire combination that will produce weld metal which in the as-welded condition, will have a tensile strength no lower than 430 MPa and Charpy V-notch impact strength of a minimum of 35J at -40°C when deposited with an EMK12 electrode under the conditions called for in this specification.
ELECTRODE CLASSIFICATIONS
135CONTENTS
A GUIDE TO INTERPRETING THE AUSTRALIAN STANDARD CLASSIFICATION FOR SUBMERGED ARC WELDING ELECTRODES AND FLUXES
E or EC XXX - F X X - W XX X X X HX
ELECTRODE AND WELD METAL DESIGNATIONS AND COMPOSITIONS
Electrode C Mn Si
EL8 EL12 EM12K
0.10max 0.05-0.15 0.05-0.15
0.25/0.60 0.25/0.60 0.80/1.25
.0.07max 0.07max 0.10/0.35
Note: A small selection only of carbon steel electrodes. For full list and details refer tothe appropriate part of the standard
FLUX APPLICATIONS = Single RunM = Multi RunB = Basic FluxG = General Purpose
FLUX CONTRIBUTION TO WELD ANALySIS
HyDROGEN
A suffix indicatinghydrogen controlled weld metal may be added when max. H2 level is established.(AS 3752 - 1996)H15 <15mL/100gH10 <10mL/100gH5 <5mL/100gof deposits of metal
ELECTRODE (SOLID)
ELECTRODE COMPOSITE (CORED)
WELD METAL HEAT TREATMENTA+ Tested “As Welded”P=Tested “Post Weld heat treated”
WELD METAL STRENGTH DIGITSThe strength digits ‘40’ and ‘50 in part 1 of AS 1858 represent one-tenth of the approximate min. tensile strength in MPa of the tensile range. Each strength level also has a min. Proof Stress (0.2% Offset) and Elongation requirements specified by this standard.
IMPACT ENERGy NUMBER‘0’ = No impact required‘1’-‘5’ = test temperature of +20°C to -60°C in 20° intervals.Energy Requirement W40X = 35JW50X = 40JWXXX = 27J
FLUX
A = Alloys other than Mn & Si and added to L, M or H eg.LA, MA or HA
L = Low Mn & SiM = Medium Mn & SiH = High Mn & Si
ELECTRODE CLASSIFICATIONS - SUBMERGED ARC WELDING ELECTRODES AND FLUXES
136CONTENTS
WELD DEPOSITION AND COSTING DATAWeld costing systems differ throughout the world and between companies in similar operations but with different methods of cost accounting. Some variations in systems are due to variations in methods of selling consumables. For example, MMAW consumables may be sold by the number, length or mass of the electrodes. However, all systems invariably rely on a basic philosophy of determining the quantity (in kg.lb, m etc) of consumable required to produce a given volume of joint. From this, the labour time for joint completion, based on the deposition rate and duty cycle estimates for the welding consumables/processes, welding positions and workshop/site situations, in question, can be determined.The costs of joint preparation and finishing must also be considered, and like the other factors mentioned can be substantially influenced at the design stage. The lowest welding costs are achieved when full use is made of the high productivity welding processes and when joints are designed specifically for these processes.Australia sells all major solid (and some gas) welding consumables by mass (kg), and all requirements can be related back to the mass of added weld metal required to produce a unit length of joint. Most well equipped welding shops have a range of processes, particularly MMAW, GMAW and SAW machines, and the following approach to weld costing is based on a system which can integrate the various methods and allow for substitution as desired.THE WIA APPROACH TO WELD COSTS DETERMINATIONS TO ASSIST yOU IN ESTIMATING WELDING COSTS WE HAVE PUT TOGETHER THE FOLLOWING GUIDE IN FOUR SECTIONS. A COMPREHENSIVE GUIDE TO USING SECTIONS 1-4 The mass of weld metal in a length of joint is a product of its volume (cross-sectional area x length) and its density. Most weld joint cross-sections can be broken up into basic shapes as detailed below and illustrated in Figure 10
137CONTENTS
WELD DEPOSITION AND COSTING DATA - USERS GUIDE
RECTANGULAR CROSS SECTIONS
Major area of the square, vee and U joints and roof gap components.
TABLE 1.0
TRIANGULAR CROSS-SECTIONS
Major areas of vee and bevel joints, fillet sections TABLE 1.1
REINFORCMENT CROSS-SECTIONS
1 Semi-elliptical shapes of predictable or measurable heights and widths reinforcing the weld face.
TABLE 1.2
RADIUS CROSS-SECTIONS
Part circle segments associated with U and J joints
TABLE 1.3
BACK GOUGED CROSS-SECTIONS
The carbon arc electrode selected Or gas nozzle) determines the width, while the rate of travel and angle determines the depth of gouge. Areas of predicable contours are covered.
TABLE 1.4
FILLET WELD SECTIONS
A range of fillet sizes and shapes including convexity and concavity allowances.
TABLE 1.5
138CONTENTS
Figure 10TABLES 1.0-1.5 of SECTION 1 are a convenient means of determining the mass of weld metal per unit length of joint for each of the simple joint cross-sections described. Simply look up the appropriate dimensions of the shape in question, and the weld metal mass, in kilograms per metre (kg/m), is calculated for you. By referring to GUIDE 1, shown in the following pages, a practical example is given illustrating the correct usage of TABLES 1.0-1.5Where ready made tables are not available or greater accuracy is required you can calculate the area. Given the length of the required weld, the volume of weld metal can be calculated and converted to the mass of weld metal, using an appropriate density figure. For example, 1 mm² cross-sectional area of steel weld metal by 1000 mm (1 metre) long has a mass of .00785 kg. Therefore, finding the cross-sectional area, in mm², and multiplying by .00785 will give the mass of weld metal per metre of joint, in kg/m.
Side A
Side b
f A h A
h B
f B
dr
d 2
T1/2 L
WELD DEPOSITION AND COSTING DATA
W= 2r
139CONTENTS
A COMPREHENSIVE GUIDE TO USING SECTIONS 1-4 CONT.“Quantity of consumables” data, tabled in section 2, allows the quantity of consumable(s) required to weld a given joint, to be calculated. Further to this, the “DEPOSITION RATE” and “Duty Cycle” data of sections 3 & 4 enable realistic estimates of actual welding speeds and times to be determined for specific consumables/welding processes, welding positions and workshop/site situations. Detailed practical examples, illustrating the use of information contained in Sections 2-4 are featured respectively in Guides 2-4.By FOLLOWING THE GUIDES THROUGH FROM 1-4 THE USER IS GIVEN A STEP-By-STEP METHOD FOR DETERMINING:1. the mass of weld metal required per metre of joint 2. the quantity of consumable(s) required per metre of joint 3. the continuous (100% duty cycle) welding speed/time for one metre of joint 4. a realistic estimate of the actual welding speed/time to complete one metre of joint.GUIDE 1 - DETERMINE MASS OF WELD PER METRE USING TABLES 1.0 - 1.5 OF SECTION 1 (a) Fillet Welds For fillet welds the user is directed to TABLE 1.5. Select the desired leg length (L) with the likely degree of convexity (h) given the electrode size/type used, the welding position and process etc., and read off the mass of weld metal per metre of joint (kg/m).For acute angle or obtuse angle fillets or fillets of unequal leg length treat as for a butt weld and refer to (b).(b) Butt WeldsFor butt welds, first sketch the joint cross-section under consideration, breaking it down into fundamental shapes such as rectangles, triangles and reinforcement and radius sections as shown in figure 10.Dimension the shapes, from available information, by calculation or by “intelligent guessing”. Using these dimensions, the mass of weld metal per metre of joint can be arrived at for each shape segment using the data from TABLES 1.0-1.4. From here, the total mass of weld metal required per metre of joint can be simply calculated by adding the figures obtained for each shape segment.
WELD DEPOSITION AND COSTING DATA - USERS GUIDE
140CONTENTS
PRACTICAL EXAMPLE 1 For the U-joint illustrated in FIGURE 10, assume the following dimensions:T (plate thickness) = 60 mm Ø = 10° (therefore, included angle is 20°) r (root radius) = 10 mm d₂ (root face) = 8 mmSide A Rectangular, Triangular and Radius Cross-SectionsWith a root face (d₂) of 8 mm and a root radius (r) of 10 mm, the depth of the rectangular and triangular sections (d) will be, d = T - (d₂ + r) = 60 - 18 = 42 mm. The width of the rectangle (w) is of course equal to 2r = 20 mm.From table 1.0, the mass of weld metal per metre of joint required for a rectangle of area, 20 x 42 mm = 840 mm2, is approximately 6.59 kg/m (A).From table 1.1, two triangles with an included angle of 20° and a depth of 42 mm will need a mass of weld metal per meter of joint of approximately ....................................................2.50 kg/m (B). From table 1.3, a semi-circular section of radius 10 mm will require a mass of weld metal per metre of joint of approximately . ................................................................................1.23 kg/m (D).GUIDE 1 CONT. SIDE A REINFORCEMENT CROSS-SECTION The reinforcement width of Side A (fA ) will be the addition of 2r (20mm) and L (15mm, taken from TABLE 1.1) plus whatever overlap onto the parent metal is considered desirable practice. For this example, assume an average overlap of 3mm on each side of the joint which gives fA = 6 + 20 + 15 = 41 mm. Also let us assume a reinforcement height on Side A (hA ) of 3 mm.From table 1.2, the mass of weld metal required per metre of joint for the reinforcement section of Side A of f = 41 mm and h = 3 mm is approximately ...................................................0.75 kg/m (C1).
WELD DEPOSITION AND COSTING DATA
141CONTENTS
SIDE B BACK GOUGED CROSS-SECTION Here the user will be guided by such factors as, the welding process used for the root pass, to determine resultant root penetration, the fracture toughness requirements of the root and established workshop practices, etc. to determine the extent of back gouging required. For this example, we will assume a carbon-arc gouge carried out with a 10 mm carbon electrode to produce a groove 14 mm wide and 10 mm deep. From TABLE 1.4, the mass of weld metal required per metre of joint to fill a groove of these dimensions is approximately .........................................................0.86kg/m (E).Side B Reinforcement Cross-Section With a gouge width of 14 mm (allow a little more for uneven gouging) and estimating a 3 mm overlap onto each side of the joint gives a reinforcement width for Side B (f8) of 21 mm.From TABLE 1.2, the mass of weld metal required per metre of joint for a reinforcement section of f = 21 mm and an assumed height of h = 1.5 mm is approximately .................. 0.19 kg/m (C2).Therefore, A + B + D + C1 + E + C2 gives the total mass of weld metal required per metre of joint: 6.59 + 2.50 + 1.23 + 0.75 + 0.86 + 0.19 = 12.12 Kg/mGUIDE 2 - DETERMINE QUANTITy OF CONSUMABLES REQUIRED PER METRE USING TABLES 2.0 - 2.3 OF SECTION 2 Given the mass of weld metal required to “Fill” a metre of joint, the next step is to determine the mass of consumable(s) initially required. The weld metal yield achieved from welding with a consumable electrode or filler wire largely depends on the efficiency of the welding process / consumable in question. This efficiency is influenced by such inherent wastage factors as, weld metal spatter, slag coverage and gas plume production. The “Quantity of consumables” figures listed in tables 2.0-2.3 are for a weld metal yield of 1 kg and take account of these inherent losses. An additional percentage (listed in the ‘EXTRA FOR WASTAGE” column) is usually added to allow for typical shop wastage such as stub ends & wire snips etc.
WELD DEPOSITION AND COSTING DATA - USERS GUIDE
142CONTENTS
PRACTICAL EXAMPLE 1 CONTINUED For the U-joint discussed in EXAMPLE 1 of GUIDE 1 let us assume that 1.6 mm Austfil 71T with CO₂ shielding gas is used for the single root pass weld on Side A and for welding the entire back gouged section on Side B; and a SAW process using 4.0mm wire is used for the remainder of the joint.AUSTFIL 71T REQUIREMENTS (NOT INCLUDING ALLOWANCE FOR SHOP WASTAGE) Side A. Allow .25 kg of weld metal/metre of joint for the root pass deposit (assuming that a single pass with a 1.6 mm Austfil 71T is comparable in size to an 8 mm fillet weld).Side B. From Guide 1, the mass of weld metal per metre of joint for the back gouged cross-section (including reinforcement) is 1.05 kg/m. (0.86 +0.19)Therefore, the total weld metal required from Austfil 71T is 1.05 + 0.25 = 1.30 kg/m.From table 2.2 type A, 1.20 kg of Austfil 71T will produce 1 kg of weld metal. Therefore, 1.20 x 1.30 = 1.56kg of Austfil 71T will produce 1.30 kg of weld metal per metre of joint.CO₂ Shielding Gas ConsumptionTo estimate CO₂ gas consumption let us assume, the 1.6mm Austfil 71T is deposited at 350 Amps and 29 Volts, which will produce a weld metal deposition rate of approx 5.4 kg/hr (see table 3.2 part B of section 3).GUIDE 2 CONT.For a CO₂ flow rate of 12 L/min approximately 0.13m₃ (or .24kg) of CO₂ gas will be consumed per kg of weld metal deposited (see table 2.2). Therefore, 1.30 x 0.13 = 0.17 m3 (or .32 kg) of CO₂ will be used to deposit 1.30 kg of weld metal per metre of joint.SAW FILLER METAL AND FLUX REQUIREMENTS (NOT INCLUDING ALLOWANCE FOR SHOP WASTAGE) The wire/flux submerged arc combination is required to produce 12.12 - 1.30 = 10.82 kg of weld metal per metre of joint. From table 2.3 approximately 1.02 kg of wire will produce 1 kg of weld metal. Therefore, 1.02 x 10.82 = 11.04 kg of wire will produce 10.82 kg of weld metal per metre of joint. Also from table 2.3 approximately 1.1 kg of flux is required to produce 1 kg of weld metal. Therefore, 1.1 x 10.82 11.90 kg of flux will be consumed to produce 10.82 kg of weld metal per metre of joint.In the summary, the quantity of consumables required to complete one metre of joint are:
WELD DEPOSITION AND COSTING DATA
143CONTENTS
• 1.6 kg of 1.6 mm Austfil 71T wire • 0.2 m₃ (0.3 kg) of CO₂ shielding gas • 11.0kg of wire • 11.9 kg flux not including allowances for shop wastage. GUIDE 3 - DETERMINE 100% DUTy CyCLE WELDING SPEED TIME USING TABLES 3.0 - 3.6 of SECTION 3 From the “Deposition Rate” data in tables 3.0 - 3.6 of section 3 for the selected consumables and arc processes, the continuous welding speed (in m/hr) and welding time (in hr/m) can be determined. Where deposition conditions are substantially varied for different sections of a joint - for example narrow root passes versus wide weave capping passes, the welding speed should be calculated separately rather than an average taken.PRACTICAL EXAMPLE 1 — CONTINUED For the U-joint discussed in example 1 of guides 1 and 2 let us assume the 1.6 mm Austfil 71T (used for the single root pass weld on Side A and for welding the entire back gouged section on Side B) is deposited at 350 amps and 29 volts under CO₂ shielding gas with an electrode stickout of 25 mm. From table 3.2, part B, the typical deposition rate is 5.4 kg/hr.As calculated in guide 2, the wire requirements is 1.30 kg of weld metal per metre of joint. Therefore the welding speed for Austfil 71T will be 5.4 ÷ 1.30 = 4.15 metres of joint/hour or the welding time will be 0.24 hours/metre of joint.For welding the remainder of the joint with SAW process, assume a welding current of 700 amps and voltage of 34 volts for the 4 mm wire nominated. From table 3.3 the typical deposition rate is approximately 8.3 kg/hr.As determined in guide 2, the wire/flux combination is required to produce 10.82 kg of weld metal per metre of joint. Therefore, the welding speed will be:8.3 ÷ 10.82 = 0.77 metres of joint/hour or the welding time will be 1.30 hours/metre of joint. 10.82From the calculated welding time for continuous welding of the Austfil 71T /CO₂ and SAW process combinations, the total welding time is .24 + 1.30 = 1.54 hours/metre of joint.In summary, given a duty cycle of 100%, (that is continuous, uninterrupted, welding of the consumables detailed in this example) one metre of joint will be completed in 1.54 hours.
WELD DEPOSITION AND COSTING DATA - USERS GUIDE
144CONTENTS
GUIDE 4— DETERMINE REALISTIC ESTIMATE OF WELDING SPEED/TIME USING THE DUTy CyCLE DATA OF SECTION 4The continuous welding speeds and welding times, (That is for a Duty Cycle of 100%) calculated in practical example 1 of guide 3 serve as a starting point for determining realistic welding speeds and welding times for joint completion.As stated in section 4, Duty Cycle is a measure of the “arc on” time as a percentage of the total time elapsed. The total elapsed time must take into account all additional “non-arc” operations, such as materials handling, weld deslagging, electrode changes overs etc and personal allowances, as well as the total “arc-on” time.In order to arrive at realistic welding speeds and times which will approach the actual figures achieved, it is important to use duty cycle estimates which are realistic for the consumable/arc process combinations and workshop/site in question.The choice of a satisfactory duty cycle may be determined by referring to past records for workshop or site projects undertaken using similar welding consumables and arc processes under similar working conditions. Since detailed information of this nature is often unavailable, a suitable duty cycle figure may be arrived at by using “published data” and/or by “educated guessing”.section 4 entitled “Duty Cycles” details a range of achievable duty cycles for the main arc welding processes used. The duty cycles given under each heading are generally accepted as ‘maintainable’ by most reasonably equipped workshops or welding sites.To continue practical example 1 from guide 3, let us assume from the information in parts (b) and (c) of SECTION 4;• a duty cycle of 30% for the FCAW process • a duty cycle of 40% for the SAW processTherefore, a realistic estimate of the welding speed for Austfil 71T/CO₂ is 4.15 x .30 = 1.25 metres of joint/hour, and the welding time is 0.80 hours/metre of joint; and a realistic estimate of the welding speed for SAW process is 0.77 x .40 = 0.31 metres of joint/hour, and the welding time is 3.25 hours/metre of joint.
WELD DEPOSITION AND COSTING DATA
145CONTENTS
FROM THE CALCULATED WELDING TIMES FOR THE FCAW AND SAW COMBINATIONS THE TOTAL WELDING TIME TO COMPLETE ONE METRE OF JOINT IS 0.80 + 3.25 = 4.05 HRS.This welding time will be a good approximation of the actual time to complete one metre of join given that the duty cycle estimates used are realistic for the welding task involved.PRACTICAL EXAMPLE 2 If, for the joint described in example 1, the initial two passes on Side A and all of Side B is welded with MMAW electrodes, Austarc 77 and Austarc 24 -instead of Austarc 71T; and the remainder of the joint is welded with SAW process, the following variations could take place. Side A. The initial two passes with 4 mm Austarc 18TC will deposit 2 x .14 = .28 kg of weld metal per metre of joint (assuming, a single pass with 4 mm Austarc 18TC is comparable to a 5 mm fillet, see section 1, Table1.5). The remainder of Side A is to be welded with SAW process.Side. The first pass welded with 4 mm Austarc 18TC will deposit .14 kg of weld metal per metre of joint. The remainder of Side B is to be complete with 5 mm Austarc 24.GUIDE 4 CONT. 4 MM AUSTARC 18TC REQUIREMENT The total mass of weld metal required from 4 mm Austarc 18TC is .28 + .14 = .42 kg per metre of joint. At a typical current setting of 170 amps, the deposition rate (at 100% duty cycle) is 170 x .01 = 1.70 kg/hr (see section 3 table 3.0) Therefore, the continuous welding time to deposit .45 kg of weld metal with 4 mm Austarc 18TC is..42 = 0.25 hours/metre of joint 170Assuming a duty cycle of 25% (see section 4), a realistic estimate of the actual welding time is.25 = 1,00 hours/metre of joint .25
WELD DEPOSITION AND COSTING DATA - USERS GUIDE
146CONTENTS
5 MM AUSTARC 24 REQUIREMENT The remainder of Side B requires 1.05 - 0.14 = 0.91 kg of weld metal per metre of joint, deposited with 5 mm Austarc 24.At a typical current setting of 300 amps, the deposition rate (at 100% duty cycle) is 300 x 0.135 =4.05 kg/hr (see section 3, table 3.0) Therefore, the continuous welding time to deposit 0.92 kg of weld metal with 5 mm Austarc 24 is 0.91 = 0.22 hours/metre of joint 4.05Assuming a duty cycle of 30% (see section 4), a realistic estimate of the actual welding time is .22 = 0.73 hours/metre of joint .30SAW CONSUMABLE The remainder of Side A requires 11.07 - .28 = 10.79 kg of weld metal per metre of joint.A typical current and voltage setting of 700 amps and 34 volts, for the 5 mm SAW wire nominated will produce a typical deposition rate (at 100% duty cycle) of 8.3 kg/hr (see section 3, table 3.3)Therefore, the continuous welding time to deposit 10.72 kg of weld metal with 5 mm wire is10.79 = 1.30 hours/metre of joint 8.3Assuming a duty cycle of 40% (see SECTION 4), a realistic estimate of the actual time is1.30 = 3.25 hours/metre of joint .40For Example 2, The Total Welding Time To Complete One Metre Of Joint May Be Summarised As Follows: 4mm Austarc 18TC (at 25% duty cycle) - 1.00 hrs/metre of joint 5mm Austarc 24 (at 30% duty cycle) - 0.73 hrs/metre of joint 5mm wire/flux combination (at 40% duty cycle) - 3.25 hrs/metre of joint Estimate of actual welding time to complete joint - 4.98 hrs/metre of joint
WELD DEPOSITION AND COSTING DATA
147CONTENTS
WELD DEPOSITION AND COSTING DATA - USERS GUIDE
RECTANGULAR WELD CROSS-SECTIONS TABLESI
MPL
y, M
ULT
IPLy
“D
X W
” FO
R C
RO
SS-S
ECTI
ON
AL
AR
EA (M
M₂ ) A
ND
REA
D D
IREC
TLy
FRO
M T
HE
TAB
LE. W
HER
E A
SEC
TIO
NA
L O
R T
OTA
L JO
INT
AR
EA IS
ALR
EAD
y K
NO
WN
IN
SQ
UA
RE
INC
HES
, MU
LTIP
Ly B
y 64
5.2
FOR
MM
₂ AN
D U
SE T
HIS
TA
BLE
.Th
is ta
ble
prov
ides
the
mas
s of
ste
el w
eld
met
al p
er m
etre
of j
oint
(kg/
in) f
or
know
n cr
oss-
sect
iona
l are
as.S
impl
y, m
ultip
ly “d
x w
” for
cro
ss-s
ectio
nal a
rea
(m
m₂ ) a
nd re
ad d
irect
ly fro
m th
e ta
ble.
Whe
re a
sec
tiona
l or t
otal
join
t are
a is
al
read
y kn
own
in s
quar
e in
ches
, mul
tiply
by 6
45.2
for m
m₂ a
nd u
se th
is ta
ble.
AR
EA
(mm
₂ )0
1020
3040
5060
7080
90
0-
0.08
0.16
0.24
0.31
0.39
0.47
0.55
0.63
0.71
100
0.79
0.86
0.94
1.02
1.10
1.18
1.26
1.33
1.41
1.49
200
1.57
1.65
1.73
1.81
1.88
1.96
2.04
2.12
2.20
2.28
300
2.36
4.43
2.51
2.59
2.67
2.75
2.83
2.90
2.98
3.06
400
3.14
3.22
3.30
3.38
3.45
3.53
3.61
3.69
3.77
3.85
500
3.93
4.00
4.08
4.16
4.24
4.32
4.40
4.47
4.55
4.63
600
4.71
4.79
4.87
4.95
5.02
5.10
5.18
5.26
5.34
5.42
700
5.50
5.57
5.65
5.73
5.81
5.89
5.97
6.04
6.12
6.20
800
6.28
6.36
6.44
6.52
6.59
6.67
6.75
6.83
6.91
6.99
900
7.07
7.14
7.22
7.30
7.38
7.46
7.54
7.61
7.69
7.77
1000
7.85
7.93
8.01
8.09
8.16
8.24
8.32
8.40
8.48
8.56
Whe
re in
crem
ents
of l
ess
than
10
mm
₂ are
con
side
red
nece
ssar
y, ad
d to
the
abov
e, o
n th
e ba
sis
of .0
08 k
g/in
for e
very
1 m
m₂ .
w
d
w
w
d ddw
148CONTENTS
MASS OF STEEL WELD METAL PER METRE OF JOINT (kg/m)
Depth d
(mm)
Width L
(mm)kg/m
Width L
(mm)kg/m
Width L
(mm)kg/m
Width L
(mm)kg/m
6 3.5 008 6.0 0.14 2.1 005 3.2 0.088 4.6 0.14 8.0 0.25 2.8 0.09 4.3 0.1410 5.8 0.23 10.0 0.39 3.5 0.14 5.4 0.2112 6.9 0.32 12.0 0.57 4.2 0.20 6.4 0.3014 8.1 0.45 14.0 0.77 4.9 0.27 7.5 0.4116 9.2 0.58 16.0 1.00 5.6 0.35 8.6 0.5420 11.5 0.90 20.0 1.57 7.1 0056 10.7 0.8422 12.7 1.10 22.0 1.90 7.8 0.67 11.8 1.0224 13.9 1.31 24.0 2.26 8.5 0.80 12.9 1.2226 15.0 1.53 26.0 2.65 9.5 0.94 13.9 1.4228 16.2 1.78 28.0 3.08 9.9 1.09 15.0 1.6530 17.3 2.04 30.0 3.53 10.6 1.25 16.1 1.9035 20.2 2.77 35.0 4.81 12.3 1.69 18.8 2.5840 23.1 3.63 40.0 6.28 14.1 2.21 21.4 3.3645 26.0 4.59 45.0 7.95 15.9 2.81 24.1 4.2650 28.9 5.67 50.0 9.81 17.6 3.45 26.8 5.2655 31.8 6.86 55.0 11.87 9.4 4.19 29.5 6.3760 34.6 8.15 60.0 14.13 21.2 5.99 32.2 7.5870 40.4 11.10 70.0 19.23 24.7 6.79 37.5 10.3075 43.3 12.75 75.0 22.08 26.4 7.77 40.2 11.8380 46.2 14.51 80.0 25.12 28.2 8.85 42.9 13.47
TABLE 1.1 TRIANGULAR WELD CROSS-SECTIONS
MASS OF WELD METAL IN JOINT
30˚ 45˚ 20˚
L L L
d
d d
30˚
L
d
SECTION SHAPES AND ANGLES
149CONTENTS
MASS OF STEEL WELD METAL PER METRE OF JOINT (kg/m)
Depth d
(mm)
Width L
(mm)kg/m
Width L
(mm)kg/m
Width L
(mm)kg/m
Width L
(mm)kg/m
6 3.5 008 6.0 0.14 2.1 005 3.2 0.088 4.6 0.14 8.0 0.25 2.8 0.09 4.3 0.1410 5.8 0.23 10.0 0.39 3.5 0.14 5.4 0.2112 6.9 0.32 12.0 0.57 4.2 0.20 6.4 0.3014 8.1 0.45 14.0 0.77 4.9 0.27 7.5 0.4116 9.2 0.58 16.0 1.00 5.6 0.35 8.6 0.5420 11.5 0.90 20.0 1.57 7.1 0056 10.7 0.8422 12.7 1.10 22.0 1.90 7.8 0.67 11.8 1.0224 13.9 1.31 24.0 2.26 8.5 0.80 12.9 1.2226 15.0 1.53 26.0 2.65 9.5 0.94 13.9 1.4228 16.2 1.78 28.0 3.08 9.9 1.09 15.0 1.6530 17.3 2.04 30.0 3.53 10.6 1.25 16.1 1.9035 20.2 2.77 35.0 4.81 12.3 1.69 18.8 2.5840 23.1 3.63 40.0 6.28 14.1 2.21 21.4 3.3645 26.0 4.59 45.0 7.95 15.9 2.81 24.1 4.2650 28.9 5.67 50.0 9.81 17.6 3.45 26.8 5.2655 31.8 6.86 55.0 11.87 9.4 4.19 29.5 6.3760 34.6 8.15 60.0 14.13 21.2 5.99 32.2 7.5870 40.4 11.10 70.0 19.23 24.7 6.79 37.5 10.3075 43.3 12.75 75.0 22.08 26.4 7.77 40.2 11.8380 46.2 14.51 80.0 25.12 28.2 8.85 42.9 13.47
MASS OF STEEL WELD METAL PER METRE OF JOINT (kg/m)
Depth d
(mm)
Width L
(mm)kg/m
Width L
(mm)kg/m
Width L
(mm)kg/m
Width L
(mm)kg/m
6 5.6 0.13 6.9 0.16 8.4 0.20 12.0 0.287.5 7.5 0.24 9.2 0.29 11.2 0.35 16.0 0.5010 9.3 0.37 11.5 0.45 14.0 0.55 20.0 0.7912 11.2 0.53 13.9 0.65 16.8 0.79 24.0 1.1314 13.1 0.72 16.2 0.89 19.6 1.08 28.0 1.5416 14.9 0.94 18.5 1.16 22.4 1.41 32.0 2.0120 18.7 1.47 23.1 1.81 28.0 2.20 40.0 3.1422 20.5 1.77 25.4 2.19 30.8 2.66 44.0 3.8024 22.4 2.11 27.7 2.61 33.6 3.17 48.0 5.4226 24.2 2.47 30.0 3.06 36.4 3.71 52.0 5.3128 26.1 2.87 32.3 3.55 39.2 4.31 56.0 6.1530 28.0 3.30 34.6 4.07 42.0 4.95 60.0 7.0735 32.6 4.48 40.4 5.55 49.0 6.73 70.0 9.6240 37.3 5.86 46.2 7.25 56.0 8.79 80.0 12.5645 42.0 7.42 52.0 9.18 63.0 11.13 90.0 15.9050 46.6 9.15 57.7 11.32 70.0 13.74 100.0 19.6355 51.3 11.07 63.5 13.71 77.0 16.62 110.0 23.7560 56.0 13.19 69.3 16.32 84.0 19.78 120.0 28.2670 65.3 17.94 80.8 22.20 98.0 26.93 140.0 38.4775 69.9 20.58 86.6 25.49 105.0 30.91 150.0 44.1680 74.6 23.42 92.4 29.01 112.0 35.7 160.0 50.24
TABLE 1.1 TRIANGULAR WELD CROSS-SECTIONS CONT.
SECTION SHAPES AND ANGLES70˚
L
d
90˚
L
d
60˚
L
50˚
L
d
WELD DEPOSITION & COSTING DATA - MASS OF WELD METAL IN JOINT
150CONTENTS
Depth, d
(mm)
MASS OF STEEL WELD METAL PER METRE OF JOINT (kg/m) REINFORCEMENT HEIGHT, h.
h=1.0mm h=1.5mm h=3.0mm h=4.5mm h=6.0mm
6 0.04 0.068 0.05 0.07
10 0.06 0.09 0.18 0.2812 0.07 0.11 0.22 0.3314 0.09 0.13 0.26 0.3916 0.10 0.15 0.30 0.4420 0.12 0.18 0.37 0.55 0.7422 0.14 0.20 0.41 0.61 0.8124 0.15 0.22 0.44 0.67 0.8926 0.16 0.24 0.48 0.72 0.9628 0.17 0.26 0.52 0.78 1.0430 0.18 0.28 0.55 0.83 1.1135 0.22 0.32 0.65 0.97 1.2940 0.25 0.37 0.74 1.11 1.4845 0.28 0.42 0.83 1.25 1.6650 0.31 0.46 0.92 1.39 1.85
Note. For face widths in excess of 50 mm, estimate average height of reinforcement and calculate as for a rectangle, referring to table 1.0
TABLE 1.2 WELD REINFORCEMENT CROSS-SECTIONS
MASS OF WELD METAL IN JOINT
Fh
151CONTENTS
Depth, d
(mm)
MASS OF STEEL WELD METAL PER METRE OF JOINT (kg/m) REINFORCEMENT HEIGHT, h.
h=1.0mm h=1.5mm h=3.0mm h=4.5mm h=6.0mm
6 0.04 0.068 0.05 0.07
10 0.06 0.09 0.18 0.2812 0.07 0.11 0.22 0.3314 0.09 0.13 0.26 0.3916 0.10 0.15 0.30 0.4420 0.12 0.18 0.37 0.55 0.7422 0.14 0.20 0.41 0.61 0.8124 0.15 0.22 0.44 0.67 0.8926 0.16 0.24 0.48 0.72 0.9628 0.17 0.26 0.52 0.78 1.0430 0.18 0.28 0.55 0.83 1.1135 0.22 0.32 0.65 0.97 1.2940 0.25 0.37 0.74 1.11 1.4845 0.28 0.42 0.83 1.25 1.6650 0.31 0.46 0.92 1.39 1.85
Radius r
(mm)
MASS OF WELD METAL PER METRE OF JOINT (kg/m)
“U” “J”3 0.11 0.064 0.20 0.105 0.31 0.156 0.44 0.227 0.60 0.308 0.79 0.399 1.00 0.50
10 1.23 0.6211 1.49 0.7512 1.18 0.8913 2.08 1.0414 2.42 1.2115 2.77 1.39
Depth r
(mm)Width (mm)
Area (mm²)
MASS OF WELD
METLEL PER METRE OF
JOINT (kg/m)1.5 6 7.07 0.062.5 8 15.71 0.123.5 7 19.24 0.154 12 37.70 0.305 10 37.27 0.317 12 65.97 0.528 19 119.38 0.94
10 14 109.96 0.9610 22 172.79 1.3612 20 188.50 1.4815 30 353.43 2.77
Note. Note: Appropriate reinforcement additions, selected from table 1.2, will generally be required to be added to the above figures.
TABLE 1.3 RADIUS WELD CROSS-SECTIONS
MASS OF WELD METAL IN JOINT
WELD DEPOSITION & COSTING DATA - MASS OF WELD METAL IN JOINT
1/2 width
dept
hL
J r
Ur
152CONTENTS
WELD SIZE
Cross- sectional Area (mm²)
MASS OF WELD METAL PER METRE (kg/m)
Leg Length, LThroat Thickness
T (mm)
Flat and Convex Welds Convex Welds
(mm) (inch) h=0 (There.) h=1.0mm h=1.5mm h=2.5mm
Throat Thickness
T (mm)
Typical Concave
Weld3.2 1/8 2.3 5.1 .04 .07 .08 - 2.3 0.053.5 2.5 6.1 .05 .08 .10 - 2.5 0.064.0 5/32 2.8 8.0 . 06 .09 .11 - 2.8 0.074.8 3/16 3.4 11.5 .09 .13 .15 - 3.4 0.105.0 3.5 12.5 .10 .14 .17 - 3.5 0.115.6 7/32 4.0 15.7 .12 .17 .19 - 4.0 0.136.0 4.2 18.0 .14 .19 .22 - 4.2 0.156.4 1/4 4.5 20.5 .16 .22 .24 - 4.5 0.177.0 4.9 24.5 .19 .25 .28 - 4.9 0.218.0 ~5/16 5.7 32.0 .25 .32 .35 - 5.7 0.279.5 3/8 6.7 45.1 .36 .44 .48 .57 7.7 0.39
10.0 7.1 65.0 .39 .48 .52 .61 7.1 0.4212.7 7.1 50.0 .63 .74 .80 .91 9.0 0.6815.9 5/8 11.2 126.4 .99 1.13 1.20 1.34 11.2 1.0619.0 ~3/4 13.4 180.5 1.42 1.59 1.67 1.84 13.4 1.5222.2 7/8 15.7 246.4 1.93 2.13 2.23 2.42 15.7 20.624.4 1.0 18.0 322.6 2.53 2.75 2.86 3.08 18.0 2.70
TABLE 1.5 FILLET WELDS The table shows the mass of steel weld metal per metre of joint (kg/m) for fillet welds of varying degrees of convexity and a typical concave profile. The figures are based on actual leg length being maintained. Note that the leg lengths shown are not applicable to the concave welds which are designated in this table by throat thickness.
153CONTENTS
WELD SIZE
Cross- sectional Area (mm²)
MASS OF WELD METAL PER METRE (kg/m)
Leg Length, LThroat Thickness
T (mm)
Flat and Convex Welds Convex Welds
(mm) (inch) h=0 (There.) h=1.0mm h=1.5mm h=2.5mm
Throat Thickness
T (mm)
Typical Concave
Weld3.2 1/8 2.3 5.1 .04 .07 .08 - 2.3 0.053.5 2.5 6.1 .05 .08 .10 - 2.5 0.064.0 5/32 2.8 8.0 . 06 .09 .11 - 2.8 0.074.8 3/16 3.4 11.5 .09 .13 .15 - 3.4 0.105.0 3.5 12.5 .10 .14 .17 - 3.5 0.115.6 7/32 4.0 15.7 .12 .17 .19 - 4.0 0.136.0 4.2 18.0 .14 .19 .22 - 4.2 0.156.4 1/4 4.5 20.5 .16 .22 .24 - 4.5 0.177.0 4.9 24.5 .19 .25 .28 - 4.9 0.218.0 ~5/16 5.7 32.0 .25 .32 .35 - 5.7 0.279.5 3/8 6.7 45.1 .36 .44 .48 .57 7.7 0.39
10.0 7.1 65.0 .39 .48 .52 .61 7.1 0.4212.7 7.1 50.0 .63 .74 .80 .91 9.0 0.6815.9 5/8 11.2 126.4 .99 1.13 1.20 1.34 11.2 1.0619.0 ~3/4 13.4 180.5 1.42 1.59 1.67 1.84 13.4 1.5222.2 7/8 15.7 246.4 1.93 2.13 2.23 2.42 15.7 20.624.4 1.0 18.0 322.6 2.53 2.75 2.86 3.08 18.0 2.70
h
L
LT
WELD DEPOSITION & COSTING DATA - MASS OF WELD METAL IN JOINT
154CONTENTS
CONSUMABLES TyPEELECTRODE
LENGTH (mm)
QUANTITy OF CONSUMABLES EXTRA
FOR WASTAGE50mm
Stub Length
75mm Stub
LengthHigh Efficiency (150%),
Iron Type Electrodes EXX24, 27 & 28 to
AS/NZS 4855
450 1.60 1.66 10%
380 1.63 1.75 10%
Conventional, Low Iron Powder or Hydrogen
Controlled Electrodes EXX12, 13, 14, 16 &18 Types to AS/NZS 4855
450 1.63 1.73 10%
380 1.66 1.73 10%
Cellulose Type Electrodes
(EXX10 & 11 Types to AS/NZS 4855)
380 1.73 1.87 10%
CONSUMABLES TyPE, CONDITIONS ECT.
QUANTITy OF
CONSUMABLE
EXTRA FOR
WASTAGEMild and Low Alloy Steel Welding Wire 1.02 2%Flux Consumption - For any given wire
size under the following conditionsLow Voltage, Normal Amperage 0.8 kg 15%Low Amperage, Normal Voltage 1.6 kg 15%
Normal Voltage, Normal Amperage 1.1 kg 15%High Voltage, Normal Amerpage 1.6 kg 15%Hight Amperage, Normal Voltage 0.8 kg 15%
Note. For Aluminium weld metal divide the steel weld metal mass per metre by 2.9
The “QUANTITy OF CONSUMABLE” figures listed in TABLES 2.0 - 2.3 are for a weld metal production of 1kg and to take into account inherent wastage losses such as weld metal spatter, slag coverage, and gas plume production. An additional percentage (listed in the “EXTRA FOR WASTAGE” column) is usually added to allow for typical shop wastage such as stub ends and wire snips etc.To obtain the quantity of consumable required to produce 1kg of weld metal read directly from tables 2.0 - 2.3 for the appropriate consumable, shielding gas, arc transfer mode etc.
QUANTITY OF CONSUMABLES REQUIRED
TABLE 2.0 MANUAL METAL-ARC WELDING (MMAW)
TABLE 2.3 SUBMERGED-ARC WELDING (SAW)
155CONTENTS
CONSUMABLES TyPE, SHIELDING GAS, ARC TRANSFER MODE ECT.
QUANTITy OF
CONSUMABLE
EXTRA FOR
WASTAGETyPE A MILD ALLOy STEEL WELDING WIRES (AUSTMIG ES6, ESD2 ECT)
USED WITH (i) CO₂ SHIELDING GAS
• Short Arc Transfer (95%)1.05 kg 2%
• Globular Transfer (90%) 1.11 kg 2 %• Globular ‘Free Flight’ Transfer (93%) 1.08 kg 2%
(ii) Ar + 15 - 25% CO₂ SHIELDING GAS • Short Arc Transfer (97%) 1.03 kg 2%
• Globular Transfer (94%) 1.06 kg 2%“Streaming Spray Transfer (96%) 1.04 kg 2%
(iii) Pulsed Arc Transfer (:Syncro-Pulse CDT”) and Programmed Shielding Gas
(98%)1.02 kg
TyPE B STAINLESS STEEL WELDING WIRES (eg. AUSTMIG 308LSI, 316SI ect):USED WITH Ar or Ar/He Based Shielding
Gases and all Arc Transfer Modes, including Pulsed Arc Transfer (98%)
1.02 kg
TyPICAL CONDITIONS
DEPOSITION RATE OF:
CONSUMPTION PER KG OF WELD METAL
EXTRA FOR
WASTAGE
Short Arc Transfer or Pulsed Arc Transfer with a Typical Gas
Flow rate of 15L/min
1.0 kg/hr; .90m₃ (1.68kg of CO₂+) 10%
2.8 kg/hr .32m₃ (.60kg of CO₂+) 10%
Globular, “FreeFlight” or “Streaming”
Spray Transfer with a typical Gas Flow
Rate of 20L/min
3.0 kg/hr .40m₃ (.75kg of CO₂+) 10%
7.0 kg/hr .17m₃ (32kg of CO₂+) 10%
TABLE 2.1 GAS METAL-ARC WELDING (GMAW) AND PULSED ARC WELDING
SHIELDING GAS CONSUMPTION FOR MILD, LOW ALLOy AND STAINLESS STEEL WIRES
WELD DEPOSITION & COSTING DATA - QUANTITY OF CONSUMABLES REQUIRED
(%) Typical Electrode Efficiency for wire type, shielding gas and transfer mode Indicated. + Where appropriate, the mass of CO₂ shielding gas required.NB. 1m₃ of CO₂ at 15.6°C and 1 atmosphere has a mass of 1.87 kg. 1m₃ = 1000 Litres.
156CONTENTS
CONSUMABLES TyPE, SHIELDING GAS, ARC TRANSFER MODE ECT.
QUANTITy OF CONSUMABLE
EXTRA FOR
WASTAGETyPE D ALUMINIUM WELDING WIRES (eg. AUSTMIG 5356, 4043, 5183 etc.)
Spray Arc Transfer (95%) 1.05 kg 1% Pulsed Arc Transfer (Syncro-Pulse CDT) (98%) 1.02 kg 1%
TyPICAL CONDITIONS DEPOSITION RATE OF:
QUANTITy OF CONSUMABLE
EXTRA FOR
WASTAGESpray Arc Transfer with a
Inert Gas Flow Rate 1.0kg/hr 1.68m3 10%
of 28L/min 2.0kg/hr 0.84m3 10%Pulsed Arc Transfer with a
Inert Gas Flow Rate 0.5kg/hr 2.16m3 10%
of 18L/min 2.0kg/hr 0.54m3 10%
(%) Typical Electrode Efficiency for arc transfer mode Indicated.
TABLE 2.1 GAS METAL-ARC WELDING (GMAW) AND PULSED ARC WELDING
SHIELDING GAS CONSUMPTION FOR FOR ALUMINIUM WIRES:
QUANTITY OF CONSUMABLES REQUIRED
157CONTENTS
CONSUMABLES TyPE, TyPICAL DEPOSITION EFFICIENCy ECT.
QUANTITy OF CONSUMABLE
EXTRA FOR
WASTAGETyPE A GAS SHIELDED, DOWNHAND
AND POSITIONAL, DCEP WIRES OF 83% EFFICIENCy:
(E70T-1, E71T-5 TYPES TO AWS A5.20)1.20 kg 2%
TyPE B SELF SHIELDED, DOWNHAND DCEP WIRES OF 83% EFFICIENCy:
(E70T-4, E70T-6 TYPES TO AWS A5.20)1.20 kg 2%
TyPE C GAS SHIELDED, DOWNHAND METAL CORED WIRES
OF 95% EFFICIENCy:1.05 kg 2%
TyPE D SELF SHIELDED, POSITIONAL DCEN WIRES OF 75% EFFICIENCy:
(E61T-8, E71T-8 TYPES TO AWS A5.20)1.20 kg 2%
Assuming a gas flow rate of 12 L/minfor a weld deposition rate of:
CONSUMPTION PER KG OF WELD METAL
EXTRA FOR
WASTAGE2 kg/hr; .36m₃ (.67kg of CO₂*) 10%4 kg/hr; .32m₃ (.18kg of CO₂*) 10%6 kg/hr; .40m₃ (.12kg of CO₂*) 10%8 kg/hr; .17m₃ (.09kg of CO₂*) 10%
* Where appropriate, the mass of CO₂ shielding gas required. NB. 1 m3 of CO₂ at 15.6°C and 1 atmosphere has a mass of 1.87 kg. 1 m3 = 1000 Litres.
TABLE 2.2 FLUX CORED ARC WELDING (FCAW)
TABLE 2.2 FLUX CORED ARC WELDING (FCAW)
WELD DEPOSITION & COSTING DATA - QUANTITY OF CONSUMABLES REQUIRED
158CONTENTS
DEPOSITION RATES
ELECTRODE TyPE,
CLALSSIFICATION TO AS/NZS 4855
WIA ELECT-RODES
TyPICAL (F)₁
FACTOR kg/amp/
hr
DEPOSITION F X A = kg/hr TyPICAL CURRENT, A( )
5mm 4mm 3.2mmE4110/11 11 .009 1.7(190) 1.4(150) 1.0(110)
E4112/13 12P, 13S .008 1.8(220) 1.4(170) 1.0(130)
E4814 - .01 2.4(240) 1.9(190) 1.4(135)E4824 24 .0135 4.1(300) 2.7(200) 2.0(150)E4127 .0135 4.1(300) 2.8(210) 2.0(150)E4816 16TC .009 2.0(220) 1.5(170) 1.2(130)
E4818 / E4846 18TC, 77 .01 2.0(200) 1.6(160) 1.2(115)
The factors (F) are typical for those low carbon steel electrodes, as classified to AS/NZS 4855 in popular use throughout Australia. Multiplying the FACTOR (F) by the CURRENT (A) selected for the electrode size (within its normal current range) will provide typical deposition rates (kg/hr) at 100% duty cycle.
TABLES 3.0-3.5 provide a comprehensive range of typical deposition rates for the continuous operation of various arc welding consumables and arc processes. The tables are designed as an easy-to-read guide to show typical deposition rates achievable tor the electrode/wire types, sizes, welding parameters and shielding gases shown. The tables also give useful information on suitable welding parameters such as welding current, voltage and modes of operation. It should be emphasised that the deposition rates tabulated are for continuous operation (100% duty cycle) of the consumable/arc process in question. Refer to SECTION 4 for further information on typical duty cycle estimates for the welding task involved. The typical deposition rates given for each current setting may vary with changes in arc voltage, electrode stickout and shielding gas composition - refer to the information given below each Table.For accurate deposition rate calculations for continuous wires, measure wire feed speed (in m/min) during welding and use the appropriate “Mass/Length” figures from table 3.6 and “Quantity of Consumables” data from tables 2.1-2.3.TABLE 3.0 TyPICAL DEPOSITION RATES USING MMAW
159CONTENTS
TABLE 3.1A TyPICAL DEPOSITION RATES USING GMAW WITH LOW CARBON AND LOW ALLOy STEEL WIRES (EG AUSTMIG ES6, ESD2 OR SIMILAR WIRES)
WELD DEPOSITION & COSTING DATA - DEPOSITION RATES
WIRE SIZE (mm)
WELDING CURRENT
(AMPS)
ARC VOLTAGE (VOLTS)
WIRE FEED SPEED (M/
MIN)DEPOSITION RATE (kg/hr)
0.8 60+ 16+ 3.3 0.70.8 80+ 17+ 4.4 1.00.8 100+ 18.5+ 5.9 1.30.8 120+ 20+ 7.0 1.60.8 140+ 20+ 9.9 2.20.8 160+ 22+ 12.4 2.80.8 180 30 14.3 3.20.9 70+ 15+ 3.7 1.10.9 100+ 19+ 6.0 1.70.9 120+ 19+ 6.9 2.00.9 150+ 20+ 8.7 2.50.9 180+ 21+ 11.5 3.30.9 180 29 12.0 3.40.9 200 31 14.0 4.01.0 90+ 19+ 3.3 1.21.0 100+ 19+ 3.6 1.31.0 150+ 20+ 5.6 2.01.0 100+ 20+ 7.0 2.51.0 220 28 14.6 5.21.0 250 32 15.7 5.61.0 280 34 16.8 6.01.2 120+ 18+ 2.7 1.41.2 150+ 18+ 3.5 1.81.2 170+ 19+ 3.9 2.01.2 220 30 6.2 3.21.2 250 32 9.1 4.71.2 310 34 11.3 5.81.2 340 36 12.9 6.61.6 140+ 19+ 1.7 1.61.6 200+ 19+ 1.7 1.61.6 250+ 21+ 3.1 2.81.6 300 30 4.9 4.51.6 350 34 6.2 6.71.6 400 34 7.5 6.8
+ Short arc transfer conditions. Note: Deposition rate data determined using: • DC+ (reverse polarity) with a conventional constant power source. • Ar - 16/18% CO2 shielding gas • An electrode stickout length at 8-10 mm for short arc transfer conditions and 15 mm for spray arc transfer conditions.• Deposition efficiency at 96% for both short arc transfer & spray arc transtor conditions
160CONTENTS
TABLES 3.1B TyPICAL DEPOSITION RATES USING PULSED ARC WELDING WITH LOW CARBON AND LOW ALLOy STEEL WIRES (EG AUSTMIG ES6)
DEPOSITION RATES
WIRE SIZE (mm)
WELDING CURRENT
(AMPS)
ARC VOLTAGE (VOLTS)
WIRE FEED SPEED (M/MIN)
DEPOSITION RATE (kg/hr)
0.8 35 17.0 2.0 0.50.8 70 20.0 5.3 1.20.8 105 23.0 8.6 2.90.8 140 25.0 11.9 2.70.8 175 28.0 15.2 3.50.9 40 18.0 2.5 0.70.9 45 17.0 1.9 0.70.9 90 21.0 6.1 1.80.9 135 24.0 9.3 2.70.9 180 27.0 12.5 3.70.9 230 30.0 16.0 4.71.0 110 21.0 5.3 1.91.0 170 24.0 8.4 3.11.0 230 28.0 11.5 4.21.0 290 31.0 14.6 5.31.2 40 19.0 1.5 0.81.2 100 21.5 3.5 1.81.2 160 24.0 5.5 2.91.2 220 26.5 7.4 3.91.2 280 29.0 94 4.91.2 350 32.0 11.7 6.11.6 70 20.0 1.3 1.21.6 165 24.0 2.8 2.61.6 260 28.0 4.4 4.11.6 355 31.0 5.9 5.51.6 450 35.0 7.5 7.0
WIRE SIZE (mm)
DEPOSITION RATE •(kg/hr) - WELDING CURRENT (AMPS)300 400 500 600 700 800 900
2.0 3.1 4.8 - - - - -2.4 2.9 4.1 5.5 7.5 - - -3.2 2.6 3.9 5.3 6.8 8.7 10.1 -4.0 - 3.6 5.1 6.7 8.3 10.0 11.94.8 - - - 5.0 7.4 8.9 10.4
• Deposition rate data achieved using DC+ (reverse polarity) with, normal voltage settings for the wire sizes listed. An electrode stickout of 25mm is used with all wire sizes & current settings. Note: Deposition rates may be increased by 30-50% using DC- (Straight Polarity) & approximately 15-25% using AC. The use of an electrode stickout longer than 25mm with the same welding current increases deposition rate significantly.
Note: Deposition rate data obtained using: • Ar + 16-18% CO2 shielding gas • A deposition efficiency of 98% for pulsed arc transferTABLE 3.3 TyPICAL DEPOSITION RATES USING SUBMERGED-ARC WELDING (SAW) WITH LOW CARBON AND LOW ALLOy STEEL WIRES
161CONTENTS
TABLE 3.2A TyPICAL DEPOSITION RATES USING FCAW
WELD DEPOSITION & COSTING DATA - DEPOSITION RATES
WIRE SIZE (mm)
WELDING CURRENT
(AMPS)
ARC VOLTAGE •••(VOLTS)
WIRE FEED SPEED (M/MIN)
DEPOSITION RATE (kg/hr)
PART A. T1 TyPE OF CORED WIRE1.2 130 23 3.4 1.41.2 150 24 5.3 2.21.2 200 26 7.4 3.31.2 250 28 9.8 4.51.6 200 26 3.7 2.41.6 250 28 5.1 3.41.6 300 30 6.7 4.41.6 350 32 8.2 5.41.6 400 34 10.8 7.11.6 425 36 11.5 7.62.4 300 27 2.4 3.42.4 350 28 3.0 4.32.4 400 32 3.7 5.22.4 450 32 4.3 6.12.4 500 34 5.0 7.12.4 525 35 5.5 7.8
PART B. T5 TyPE OF CORED WIRE1.2 130 22 3.4 1.41.2 150 23 5.3 2.21.2 200 24 7.4 3.31.2 250 26 9.8 4.51.6 200 25 3.7 2.41.6 250 27 5.1 3.41.6 300 28 6.7 4.41.6 350 29 8.2 5.41.6 375 30 9.4 6.12.4 300 25 2.4 3.42.4 350 26 3.0 4.32.4 400 28 3.7 5.22.4 450 29 4.3 6.12.4 475 30 4.7 6.6
Note. Deposition rate data determined using:• DC+ (reverse polarity) with a conventional Constant Potential power source• Welding grade CO₂ shielding gas• An electrode stickout length of, 15mm for 1.2mm, 25mm for 1.6mm & 2.4mm wire sizes• A deposition efficiency of 84% for globular transfer•••Voltage figures are typical machine meter readings-actual arc voltage will be 1-3 volts lower than meter reading due to voltage drop across welding leads. Reduce arc voltage by 2-3 volts when using mixed gas.
• Deposition rate data achieved using DC+ (reverse polarity) with, normal voltage settings for the wire sizes listed. An electrode stickout of 25mm is used with all wire sizes & current settings. Note: Deposition rates may be increased by 30-50% using DC- (Straight Polarity) & approximately 15-25% using AC. The use of an electrode stickout longer than 25mm with the same welding current increases deposition rate significantly.
162CONTENTS
TABLES 3.4A TyPICAL DEPOSITION RATES USING GMAW WITH “300” SERIES STAINLESS STEEL SOLID WIRES
TABLE 3.4B TyPICAL DEPOSITION RATES USING PULSED ARC WELDING WITH “300” SERIES STAINLESS STEEL SOLID WIRES
DEPOSITION RATES
WIRE SIZE (mm)
WELDING CURRENT
(AMPS)
ARC VOLTAGE (VOLTS)
WIRE FEED SPEED (m/min)
DEPOSITION RATE (kg/hr)
0.9 80+ 17+ 4.2 .30.9 100+ 18+ 5.1 1.50.9 150 20 8.4 2.50.9 200 23 12.5 3.71.2 125+ 18+ 3.1 1.61.2 200 20 5.9 3.11.2 250 27 8.1 4.31.2 300 29 10.9 5.8
WIRE SIZE (mm)
WELDING CURRENT
(AMPS)
ARC VOLTAGE • (VOLTS)
WIRE FEED SPEED (m/min)
DEPOSITION RATE (kg/hr)
0.8 30 17.0 2.4 0.60.8 60 19.0 5.8 1.40.8 90 21.0 9.2 220.8 120 230 12.6 3.00.8 150 25.0 16.0 3.90.9 35 17.0 2.5 0.80.9 75 20.0 5.6 1.70.9 120 235 9.1 2.70.9 165 26.5 12.5 3.80.9 210 30.0 16.0 4.81.0 35 16.0 1.5 0.61.0 80 18.0 4.2 1.61.0 130 21.0 7.1 2.61.0 180 24.0 10.1 3.71.0 225 26.0 12.7 4.71.2 50 17.0 1.5 0.81.2 100 19.5 2.8 1.51.2 150 22.0 4.1 2.21.2 200 24.5 5.3 2.81.2 250 27.0 6.6 3.51.2 300 295 7.9 4.21.2 350 32.0 9.1 4.8
Note: Deposition rate data obtained using: • A deposition efficiency of 98% for pulsed arc transfer • Ar + He + 1.5% CO₂
+ Short arc transfer conditions Note: Deposition rate data determined using: • DC+ (reverse polarity) with a conventional constant potential power source • Ar+ 1-2% O2 shielding gas • An electrode stickout length of, 8-10mm for short arc transfer conditions and 15mm for spray arc transfer conditions• A deposition efficiency of 98% for both short arc transfer and spray arc transfer conditions
163CONTENTS
TABLES 3.5A TyPICAL DEPOSITION RATES USING GMAW WITH AUSTMIG ALUMINIUM ALLOy WIRES (EG. AUSTMIG 5183)
TABLE 3.5B TyPICAL DEPOSITION RATES USING PULSED ARC WELDING WITH AUSTMIG ALUMINIUM ALLOy WIRES (EG. AUSTMIG 5183)
WELD DEPOSITION & COSTING DATA - DEPOSITION RATES
WIRE SIZE (mm)
WELDING CURRENT
(AMPS)
ARC VOLTAGE (VOLTS)
WIRE FEED SPEED (m/min)
DEPOSITION RATE (kg/hr)
0.9 100 17 9.2 0.90.9 125 18 10.9 1.10.9 175 21 15.0 1.50.9 200 22 18.0 1.71.2 150 22 7.8 1.41.2 175 23 9.0 1.61.2 225 05 13.8 2.41.2 250 25 13.8 2.4
WIRE SIZE (mm)
WELDING CURRENT
(AMPS)
ARC VOLTAGE • (VOLTS)
WIRE FEED SPEED (m/min)
DEPOSITION RATE (kg/hr)
0.9 25 14.0 2.8 0.30.9 50 16.0 5.6 0.60.9 70 17.0 7.9 0.80.9 90 18.0 10.1 1.00.9 115 20.0 13.0 1.31.0 35 15.0 3.6 0.51.0 70 17.0 6.5 0.81.0 110 19.0 10.0 1.31.0 140 21.0 12.6 1.61.0 180 23.0 16.0 2.11.2 35 15.0 2.8 0.51.2 85 18.0 6.1 1.11.2 135 21.0 9.4 1.71.2 185 24.0 12.7 2.31.2 235 27.0 16.0 2.91.6 80 15.0 2.5 0.81.6 140 17.5 4.6 1.51.6 200 20.0 6.7 2.11.6 265 22.5 8.8 2.81.6 325 25.0 10.9 3.5
Note: Deposition rate data determined using: • Welding grade Ar shielding gas • A deposition efficiency of 98% for pulsed arc transfer
Note: Deposition rate data determined using:• DC+ (reverse polarity) with a conventional constant potential power source. • Welding grade Ar shielding gas • An electrode stickout length of 20mm • A deposition efficiency of 95%
164CONTENTS
165CONTENTS
WELD DEPOSITION & COSTING DATA - DEPOSITION RATES
TABLES 3.6 MASS / LENGTH TABLES
PART A. LOW CARBON AND LOW ALLOy STEEL GMAW WIRES
PART B. FCAW WIRES
PART C. LOW CARBON AND LOW ALLOy STEEL SAW WIRES
PART D. STAINLESS STEEL WELDING WIRES
PART E. ALUMINIUM WELDING WIRES
DEPOSITION RATES
WIRE SIZE (mm) 0.6 0.8 0.9 1.0 1.2 1.6
GRAM OF WIRE PER METRE 2.2 3.9 5.0 6.2 8.9 15.8
METRES OF WIRE PER KG 450.5 253.7 200.4 161.3 112.7 63.4
WIRE SIZE (mm) 1.2 1.6 2.0 2.4 3.2
GRAM OF WIRE PER METRE 7.6 13.0 20.0 28.0 50.1
METRES OF WIRE PER KG 131.6 76.9 50.0 34.7 20.0
WIRE SIZE (mm) 2.0 2.4 3.2 4.0 4.8
GRAM OF WIRE PER METRE 24.6 35.5 63.1 98.6 141.0
METRES OF WIRE PER KG 40.6 28.2 15.9 10.1 7.0
WIRE SIZE (mm) 0.8 0.9 1.0 1.2 1.6
GRAM OF WIRE PER METRE 4.1 5.1 6.3 9.0 16.0
METRES OF WIRE PER KG 245 197.7 158 111.2 62.6
WIRE SIZE (mm) 0.8 0.9 1.0 1.2 1.6
GRAM OF WIRE PER METRE 1.4 1.7 2.2 3.1 5.4
METRES OF WIRE PER KG 712 528.2 455 327.5 184.2
166CONTENTS
The deposition rates tabled in SECTION 3, are for a duty cycle of 100% - that is continuous (uninterrupted) welding of the consumable/arc process in question.DUTy CyCLE IS, By DEFINITION, A MEASURE OF THE “ARC ON” TIME EXPRESSED AS A PERCENTAGE OF THE TOTAL ELAPSED TIME, IE
DUTY CYCLES
Duty Cycle = (%)arc time x 100total elapsed time
Dut
y C
ycle
%
100
80
60
40
20
0
Surfacing Operations
Automatic Welding
SAW
GM
AW
FCAWRW
MM
AW
GW Manual Welding
Machine or Mechanised Welding
Figure 4.0
This parameter indicates the proportion of the operating time during which weld metal is actually being deposited. The duty cycle can vary considerably according to a number of factors including:• the welding process • the type of consumable • operating conditions • the application involved • the degree of mechanisation • general workshop efficiency • a variety of human factors or personal allowances such as putting gloves and helmet on, putting aside and picking up electrode holder etc.Figure 4.0 summarizes the potential range of duty cycles for various arc welding processes and modes of operation.
167CONTENTS
(a) Manual Metal-Arc Welding (MMAW) The maximum obtainable duty cycle for MMAW is of the order of 65% but most applications will not permit a duty cycle greater than 50% to be achieved over a day’s production. The duty cycle for MMAW operations varies widely with the type of application and operating conditions. Electrode changes, slag removal, intermittent welding and changing positions etc all play a part in reducing the actual “arc on” time. With added delays, such as personal allowances and materials handling, most welding workshops are capable of maintaining duty cycles of 15-30%(b) Gas Metal-Arc Welding (GMAW) and Flux Cored Arc Welding (FCAW) —Semi-automatic Arc Processes For semi-automatic surfacing operations a duty cycle approaching 80% is possible. However, most GMAW and FCAW operates between 30-60%; with mechanised semi-automatic welding yielding duty cycles of 45-60% and conventional (or manual) semi-automatic processes producing duty cycles of typically 30-40%.(c) Submerged-Arc Welding (SAW) For fully automatic hard surfacing operations, a 95% duty cycle is possible with the submerged-arc process; however most submerged-arc welding operates between 40-60% duty cycle due to essential setting up, deslagging, loading / positioning and other handling operations.
WELD DEPOSITION & COSTING DATA - DUTY CYCLES
168CONTENTS
OPEN SQUARE GROOVE BUTT JOINT - WELDED BOTH SIDES Reinforcement height, r = 2 mm.
JOINT DIMENSIONS (MM)
Mass of steel weld metal per metre.
(D) (kg/m)
Mass of MMAW** electrodes required per metre (M) (kg/m)T R W
3 0 7 0.17 0.283 1 7 0.20 0.336 1.5 10 0.32 0.536 3 10 0.39 0.64
ELECTRODE CONSUMPTION FOR TYPICAL BUTT JOINTS
W
R
rT
ELECTRODE CONSUMPTION FOR SOME COMMON BUTT JOINTS The following Tables provide useful data on the mass of weld metal and MMAW electrodes required to complete some common butt joints. Electrode consumption is calculated using the following simple equation:
where M = Mass of electrodes required per metre of joint. D = Mass of weld metal deposited per metre of joint. P** = Proportion of electrode lost, due to spatter, slag loss, stub end etc.
M = D1-P
169CONTENTS
WELD DEPOSITION & COSTING DATA - ELECTRODE CONSUMPTION FOR BUTT JOINTS
JOINT DIMENSIONS (MM)
Mass of steel weld metal per metre.
(D) (kg/m)
Mass of MMAW** electrodes required per metre (M) (kg/m)T R L W
6 3.5 1.5 10.0 0.26 0.438 3.5 1.5 13.0 0.57 0.95
10 3.5 1.5 15.0 0.79 1.3112 3.0 3.0 15.0 0.83 1.3916 3.0 3.0 19.0 1.38 2.2920 3.0 3.0 23.0 2.06 3.43
SINGLE V BUT JOINT Reinforcement height, r = 2mm
W
60°
RL
T
r
W60°
R
L T
r
JOINT DIMENSIONS (MM)
Mass of steel weld metal per metre.
(D) (kg/m)
Mass of MMAW** electrodes required per metre (M) (kg/m)T R L W
12 3.0 3.0 10.0 0.71 1.1816 3.0 3.0 12.0 1.06 1.7520 3.0 3.0 15.0 1.50 2.4825 3.0 3.0 18.0 2.13 3.5350 3.0 3.0 32.0 6.97 11.58
Single V But Joint Reinforcement height, r = 2mm
• For 380mm long EXX12, 13, 14, 16 & 18 type MMAW electrodes to AS/NZS 4855, P is typically 0.4. This figure assumes a stub end length of 50mm. (See table 2.0 for further details.)
170CONTENTS
WELDABILITY GUIDE FOR STEELSThe majority of steels in general use are considered “Weldable” using most arc welding processes. The degree to which they are rated as weldable is indicated by an imprecise term, “Weldability” which is (as yet) not fully assessable by a laboratory test or series of tests. We have included two different weldability guides to assist you in determining preheat of materials. The first guide is the same as that used in Australian Standards and WTIA technical notes the second guide is a method adopted by WIA and known as the “WIA Welability Guide”Furthermore, what is considered to be a satisfactory joint for one set of service conditions, possibly, steel sections embedded in concrete under static loading, may not be acceptable for another set of service conditions, such as in the tension member of a flexing structure or under corrosive conditions. For this reason, no economically acceptable hard and fast rules can be provided in a Guide such as this and the recommendations should always be tempered in their translation into practice with a knowledge of the intended application and other factors relevant to the situation.Arc welding is a process of intense localised heating and rapid cooling, providing a sudden heating-quenching heat treatment effect on both the weld metal and the adjacent parent metal (HAZ). As a general rule the tendency of a steel to strengthen and harden, following this heat treatment, increases as the carbon and alloy content increases. Its composition is therefore an important factor in assessing weldability.CARBON EQUIVALENT Carbon is the most effective of the commonly used alloying elements in achieving increased strength and hardness (increased hardenability) and is present in all steels. Over many years, researchers have established numerous rating systems to compare the hardening potential of other common elements such as manganese and chromium against that of carbon. This has led to the concept of calculating “Carbon Equivalent” (CE) from the chemical composition of the steel as a means of assessing its weldability. The following is the IIW formula used for determining Carbon Equivalent from the percentage of elements present:
CE = C + + +Mn Cr + Mo + V Ni + Cu6 5 15
171CONTENTS
WELDABILITY GUIDE FOR STEELS
The Weldability Reference Numbers used in this guide, relate to the following carbon equivalents:
NOTE: Reference numbers above 12 are not related to CE. In instances where the ladle analysis is given for a steel, the maximum specification limits have been used to calculate CE. For steels containing multiple alloy additions, the use of maximum specification limits to calculate CE give conservative results; because the possibility of all alloying elements simultaneously achieving their maximum limit is remote. In these circumstances, it is recommended that the CE be calculated using 80-85% of the ladle analysis maximum specification limits.
OTHER FACTORS INFLUENCING WELDABILITy Composition, although important, is not the only criterion used to assess the weldability, of a given steel, in a given joint situation. Other influences can be broadly related either to their effect on the “heat treatment” or the “stress level” of the joint.
CE REFERENCE NUMBER CE REFERENCE
NUMBERbelow 0.30 1 0.55 to below 0.60 7
0.30 to below 0.35 2 0.60 to below 0.65 80.35 to below 0.40 3 0.65 to below 0.70 90.40 to below 0.45 4 0.70 to below 0.75 100.45 to below 0.50 5 0.75 to below 0.80 110.50 to below 0.55 6 0.80 and above 12
172CONTENTS
WELDABILITY GUIDE FOR STEELSOTHER FACTORS INFLUENCING WELDABILITy Factors which can have an effect on the “heat treatment and hence (with composition) the microstructure include; the mass of the section, its initial temperature, the heat input per unit length and the interpass temperature in multipass welds. Factors which relate generally to the “stress level” include; the degree of restraint imposed on the joint by its own mass and from external sources, base metal strength (rigidity, hardness) and geometry, uneven heating and cooling conditions and geometrical considerations such as joint preparation and alignment, notches due to weld contour, weld nugget shape and the presence of non-metallic inclusions, etc. The tendency towards weld and base metal cracking is further influenced by the inherent toughness and strength of the weld metal, the effect of base metal dilution on these properties and the presence of hydroge in the arc atmosphere.NOTES ON USING THE GUIDE The following pages list recommendations for welding some of the more commonly available steels in Australia. Based primarily on the steel composition, they assume moderate conditions of restraint and joint complexity. Where low hydrogen or hydrogen controlled conditions are nominated, electrodes should be dried accordingly to meet the required level. For MMAW, the use of 4mm electrodes (minimum size) has been assumed, although the user is expected to use the largest size practicable. The use of higher and lower heat inputs by other electrode sizes or processes can respectively lower and raise the recommended preheat temperature.Silicon levels are not listed for steels unless their content, within a particular group, exceeds the normal maximum limit of .35%, for other steels, typical Silicon figures have been quoted for interest sake. For further details regarding the Sulphur, Phosphorus and Silicon levels in a particular steel, refer to the manufacturers specification.
173CONTENTS
WELDABILITY GUIDE FOR STEELS
The term “Combined Joint Thickness” (CJT) is used in many instances in conjunction with recommended preheat temperatures as a measure of the quenching severity of the joint. For simple butt and corner joints the CJT is the sum of each plate thickness, whilst for more complex joints, such as T joints, the CJT can be calculated as shown in figure 11.
FIGURE 11 Combined Joint Thickness (CJT) calculations for welds shown in black.
If t₃ is already welded to t₂ as shown then: CJT = t₃ + t₂ + t₁
t₁
t₂
CJT = t₁ + 2t₂
t₂
If t₃ is already welded to t₂ then: CJT = t₁ + 2t₂ + t₃
t₃
t₁
t₂ t₂
t₃
t₃
t₁t₂
t₁t₃
t₁ = average thickness over 75mm CJT = t₁ + t₃75mm
174CONTENTS
WELDABILITY GUIDE FOR STEELSHyDROGEN CONTROLThe term “low hydrogen” or “hydrogen controlled” is not indicative of no hydrogen, but of products and processes which have controlled limits on moisture or hydrogen producing materials. The fact that a product can meet the specified requirements of a code is not necessarily indicative of its ability to meet requirements in more critical situations. Some codes have maximum permissible moisture levels for lower strength electrodes and more stringent requirements for higher strength. As a general rule, as the retainability of the base material and weld metal increase, the allowable maximum limit for hydrogen is reduced. This situation is further complicated when restrictions are placed on preheat temperature and heat input - which normally help to increase the diffusion rate of hydrogen; such as for the welding of quenched and tempered steels. Flux coated “hydrogen controlled” electrodes when used in critical applications should be thoroughly dry prior to use. If any doubt exists, electrodes should be rebaked and used from a hot box.WIA WELDABILITy REFERENCE NUMBERS AND RECOMMENDATIONS1&2 Readily weldable with any low carbon steel electrodes (for example, Austarc 11, 12P, 13S, 24) or arc welding process without special precautions.1A Rimmed steels welded with the GTAW Process (TIG) without added filler metal will give porous welds, due to gas evolution, caused by resumption of the rimming process. Use double deoxidised filler wire for sound joints.2A The sulphur or lead content of these steels can lead to “hot shortness” during welding and sulphur can also cause porosity. Welding is therefore not generally recommended except for non-critical applications. Basic coated, MMAW electrodes such as Austarc 16TC, 18TC, 77 should be used or specially formulated electrodes for welding sulphurised steels. The use of an intermediate buffer pad is recommended in extreme cases and through thickness joints are preferred to fillet welds. No preheat required.
175CONTENTS
3&4 Readily weldable with any low carbon steel electrode, such as Austarc, 11, 12P, 13S, 24. For CJT’s of 50mm or greater a preheat temperature of 50-75°C is recommended, depending on the degree of restraint. Alternatively hydrogen controlled electrode such as Austarc 16TC, 18TC or 77 may be used with a preheat temperature of only 25°C.3A As for 2A, but use 50°C preheat on heavy sections.3B Check if Shipping Society approval and specific CVN impact gradings are required for electrode,then as for 3 4B Check if Shipping Society approval and specific CVN gradings are required for electrode, then as for 4.5 Conventional low carbon electrodes, such as Austarc 13S & 24 are still acceptable however,special notch toughness requirements etc. may dictate a preference for basic electrodes, particularly for butt welding applications. The use of “hydrogen controlled” basic electrodes, such as Austarc 16TC, 18TC & 77, reduce the preheat temperature necessaryto prevent HAZ weld metal cracking in highly restrained, heavy sections. No preheat is generally required for CJTs up to 40mm, welded with “hydrogen controlled” electrodes or CJTs up to 30mm, welded with conventional low carbon electrodes. When using conventional low carbon electrodes, preheat joint to 50°C for CJT’s of 40mm, and 125°C for CJT’s of 80mm. Using “hydrogen controlled” electrodes, preheat joint to 50°C for CJT’s of 55mm and 100°C for CJT’s of 80mm and above. For welding with semi automatic solid or flux cored wire like the Formula XL-525, Austmig ES6 or Austmig 70C-6M etc. at a heat input of 2.2kJ/mm, use a preheat temperature of 50°C for CJTs of 80mm and above.
WELDABILITY GUIDE FOR STEELS
176CONTENTS
WELDABILITY GUIDE FOR STEELSWIA WELDABILITy REFERENCE NUMBERS AND RECOMMENDATIONS 6A As for 5, except when matching colour and corrosion resistance are required, an electrode depositing a Ni-Cu weld metal is recommended.6B “Hydrogen controlled” electrodes of matching weld metal analysis and strength are normally recommended. For minimum preheat temperatures, refer to 5.6 “Hydrogen controlled” electrodes are generally considered essential for the deposition of sound welds — use a preheat temperature of 70°C for CJT’s of 40mm. 100°C preheat for CJT’s of 60mm and 150°C preheat for CJT’s of 110 mm and above. When using semi automatic solid or flux cored wire like the Formula XL-525, Austmig ES6 or Austmig 70C-6M etc., at approximately 2.2kJ/mm, a preheat temperature of 50°C is recommended for CJT’s of 60mm and 125°C for CJT’s of 110mm and above.7 “Hydrogen controlled” electrodes must be used with a preheat temperature of 70°C for CJT’s of 28mm, 100°C for CJT’s of 40mm and 170°C for CJT’s of 110mm and above. For welding with appropriate solid or flux cored wires, at approximately 2.2kJ/mm, a minimum preheat of 70°C is required for CJT’s of 45mm and 125°C for CJT’s of 80mm. Slow cooling from interpass temperature is required and critical weldments should be stress relieved.7A Follow the general advice of 2A The welding of sulphur bearing steels is not generally recommended, except for non-critical applications. For general preheat requirements refer to 7.7B “Hydrogen controlled” electrodes of matching chemical analysis and strength are recommended. The service requirements of weldments employing this type of alloy demand high integrity welding. A minimum preheat temperature of 150°C is generally recommended, for CJT’s of 30-60mm, followed by slow cooling. A stress relieving heat treatment to 650°C is common practice, following welding.
177CONTENTS
8 Use “hydrogen controlled” electrodes with a preheat temperature of 75°C for CJT’s of 20mm. 120°C for CJT’s of 40mm and 170°C for CJT’s of 80mm. For semi- automatic welding with appropriate solid or flux cored wires, at approximately 2.2kJ/mm, use a preheat of 100°C for CJTs of 40mm, and 200°C for CJT’s of 100mm. Slow cooling is essential, followed by a stress relieving heat treatment for critical joints.9 Use “hydrogen controlled” electrodes such as Austarc 16TC, 18TC or 77 with a minimum preheat of 90°C for CJT’s of 20mm, 150°C for CJT’s of 40mm and 200°C for CJT’s of 80mm. For semi-automatic welding with appropriate solid or flux cored wires, at approximately 2.2kJ/mm, a minimum preheat of 50°C is recommended or CJT’s of 20mm, 120°C for CJTs of 40mm and 180°C for CJT’s of 80mm.9A Follow the general advice of 2A. The welding of sulphur bearing steels is not generally recommended, except for non-critical applications. For general preheat requirements, refer to 9.10&11 Use “hydrogen controlled” electrodes such as Austarc 16TC, 18TC or 77 which have been thoroughly dried, with the following minimum preheat temperatures.
Alternatively use austenitic, stainless steel electrodes such as Unicord 312 with preheat temperatures approximately 50°C less than those recommended above for “hydrogen controlled” electrodes. The use of dry electrodes is essential, as is slow cooling after welding. A post weld heat treatment is considered good welding practice.
CJT WIA WELDABILITy
20 mm 40 mm 80mm REF: NUMBER
120°C 170°C 220°C 10140°C 190°C 230°C 11
WELDABILITY GUIDE FOR STEELS
178CONTENTS
WELDABILITY GUIDE FOR STEELSWIA WELDABILITy REFERENCE NUMBERS AND RECOMMENDATIONS 11A Following the general advice of 2A. The welding of higher carbon, sulphur bearing steels is not generally recommended, except for non-critical applications For general preheating requirements, refer to 11.9C, 11C For high strength butt and filet welding of these steels, use “Hydrogen controlled” electrode & 12C of matching chemical analysis or strength. Refer to the minimum preheat temperatures and welding details described in 9,11 and 12 respectively. When welding these steels in the heat treated (hardened and tempered) condition check that the post weld heat treatment temperature chosen does not exceed the tempering temperature of the base material.10B, 11B The welding of alloy spring steels in the heat treated (hardened and tempered) condition & 12B can be carried out using preheat and interpass temperatures of 200-300°C, with extra slow cooling in insulating powder, a lime bath or a thermal blanket etc. Austarc 16TC, 18TC and 77 is recommended for root pass welding whilst subsequent higher strength passes may be made with high strength electrode eg. AWS A5.5: E110XX. Thoroughly dried electrodes are essential and post weld heat treatment is generally not recommended.12 Use hydrogen controlled electrodes’-in thoroughly dry condition, with the following minimum preheat temperatures:
CJT WIA WELDABILITy
20 mm 40 mm 80mm REF: NUMBER
170°C 220°C 260°C 12
179CONTENTS
Welding on these steels is preferred in the annealed condition and low dilution techniques should be employed. Under higher degrees of restraint a further 50°C of preheat is recommended to avoid cracking. In some applications, the use of Unicord 312 is acceptable, especially where high preheats are difficult to achieve. Dry electrodes and clean joints are essential. Slow cooling followed by a PWHT immediately after welding is a compulsory practice.13 Arc welding of these steels should be avoided if possible. Welding is best carried out on tool steels in the annealed condition, however, repair work on heat treated (hardened and tempered) material or minor attachments can be welded with Unicord 312. A preheat temperature of 150-500°C is required as is a Post Weld Heat Treatment (PWHT) of 150-650°C — for exact heat treatment details refer to manufacturers data on the tool steel being welded. It is important that the “PWHT” temperature chosen does not exceed the tempering temperature of the tool or mould steel being welded. “Hydrogen controlled” ferritic electrodes, such as Austarc 16TC, 18TC and 77, should only be used on annealed tool steels, with accordingly higher preheat temperatures.14 Should be welded with “hydrogen controlled” electrodes or wires of matching chemical analysis and strength. Low hydrogen conditions are essential. Preheat and interpass temperatures of the order of 250°C-300°C are recommended followed by retarded cooling and a stress relieving heat treatment of 650-700°C.14A As for 14, except that a matching 5% Cr - 1/2 Mo “hydrogen controlled” electrode is essential for matching strength and corrosion. An alternative approach of using Unicord 312 is acceptable for joints not subject to thermal fatigue conditions and allows the use of lower preheat temperatures and higher interpass temperatures.
WELDABILITY GUIDE FOR STEELS
180CONTENTS
WELDABILITY GUIDE FOR STEELSWIA WELDABILITy REFERENCE NUMBERS AND RECOMMENDATIONS 15 Should be welded with a type 420 filler metal for matching chemical analysis and mechanical properties. However, Staincord 309Mo-16, Unicord 312 are suitable austenitic, stainless steel electrodes for repair welds. A preheat and interpass temperature of 200°C is recommended, immediately followed by a post weld heat treatment of 370°C. Allow component to cool to 40°C and post heat a second time, to ensure optimum properties.16 This class of alloy is best treated by water quenching during welding and remains a tough austenitic structure, unless reheated above 400°C. Use 1220-A4 type electrode, for build-up or reclamation and Unicord 312 for butt and fillet welds. The base metal should be kept cool during welding by intermittent quenching, skip welding etc.17 The use of “hydrogen controlled” consumables is compulsory for welding Quenched and Tempered (Q & T) steels. Electrodes and wires providing matching strength to the structural grades are recommended for butt welding, however, consumables of under-matching strength such as Austarc 18TC, 77 may be suitable for fillet welding applications on both structural and abrasion resistant grades.Because of the risk of stress relief cracking, post weld heat treatment of Q & T steels should not be undertaken, unless absolutely necessary. If so stress relieving temperatures should not exceed the tempering temperature of the Q & T steel being welded. Refer to WTIA Technical Note 15 for complete details on the welding of Q & T steels. The following minimum pre-heat temperatures, maximum interpass temperatures and maximum arc heat input energies should be used as a guide for welding both structural and abrasion resistant grades of Q & T steels.
181CONTENTS
GRADE OF Q & T STEEL <13 13 ~15 25 ~50 <50
MINIMUM PREHEAT TEMPERATURES (°C) (HIGH RESISTANT)
HIGH STRENGTH GRADES450 MPa min. Yield Stress 10 25 75 10620 MPa min. Yield Stress 50 100 125 150680 MPa min. Yield Stress 50 100 125 150
ABRASION RESISTANT GRADES320 HB (3000/10) 50 100 125 150360 HB (3000/10) 50 100 125 15500 HB (3000/10) 100 100 150 -
ALL GRADESMAXIMUM INTERPASS TEMPERATURES (°C)
150 175 200 220
ALL GRADESMAXIMUN ARC HEAT INPUT (kj/mm)2.5 3.5 4.5 5.0
WELDABILITY GUIDE FOR STEELS
182CONTENTS
WELDABILITY GUIDE FOR STEELSSTEEL TyPES
FREE MACHINING STEELS
STEEL DESIGNATION
CHEMICAL ANALySIS (%) WIA WELDABILITy REF: NUMBERC Mn
LOW CARBON AND MILD STEELS1008 .10 max .20-.50 1,1A1020 .18-23 .30.60 31022 .18-23 .70-1.00 41025 .22-28 .30-60 4
MEDIUM CARBON STEELS1030 .28-.34 .60-.90 51035 .32-.38 .60-.90 6
X 1038 .35-.42 .70-1.00 81040 .37-.44 .60-.90 71045 .43-.50 .60-.90 7
HIGH CARBON STEELS1050 .48-55 .60-.90 101055 .50-.60 .60-.90 111060 .55-.60 .60-.90 111070 .65-.75 .60-.90 12
STEEL DESIGNATION
CHEMICAL ANALySIS (%) WIA WELDABILITy
REF: NUMBERC Mn S Pd
RESULPHURISED AND RESULPHERISED-REPHOSPHORISED GRADES1110 .06-.11 .30-.60 .05-1.0 - 2A
X1112 .08-.15 1.10-1.40 .20-.30 - 3A1214 .15 max .80-1.20 .25-.35 - 3A1137 .32-.39 1.35-1.65 .08-.13 - 9A1144 .40-.48 1.35-1.65 .08-.13 - 11A1146 .42-.49 .701-.00 0.089-.13 - 9A
X1147 .40-.47 1.60-1.90 .10-.35 - 11ARESULPHURISED AND RESULPHERISED-REPHOSPHORISED GRADES
12L14 .15 max .80-1.20 .25-.35 .15 -.35 2A
183CONTENTS
STEEL TyPES
STEEL DESIGNATION
CHEMICAL ANALySIS (%) WIA WELDABILITy REF: NUMBERC Mn
CARBON-MANGANESE STEELSX1320 .18-.23 1.40-1.70 5X1325 .23-.28 1.40-1.70 6X1330 .28-.33 1.40-1.70 8X1340 .38-.43 1.40-1.70 10
STEEL DESIGNATION
CHEMICAL ANALySIS (%) WIA WELDABILITy
REF: NUMBERC Mn Si Cr
SPRING STEELSXK 55S .50-.60 .70-1.00 .10-.35 .70-.90 11B
XK 5160S .50-.65 .70-1.00 .10-.35 .70-.90 12BXK 9258S .50-.65 .70-1.05 1.60-2.20 - 12BXK 9261S .50-.65 .70-1.00 1.80-2.20 1 12B
ALLOy STEELS (FOR OTHER THAN SPRING APPLICATIONS)5155 .50-.60 .70-1.00 .10-.35 .70-.90 115160 .55-.65 .70-1.00 .10-.35 .70-.90 129255 .50-.60 .70-1.05 1.60-2.20 - 129261 .50-.65 .70-1.00 1.80-2.20 .10-.25 12
STEEL DESIGNATION
CHEMICAL ANALySIS (%) WIA WELDABILITy
REF: NUMBERC Mn Si Ni Cr Mo Other
ALLOy CONSTRUCTION STEELS4140 .40 .60 .25 - .90 .20 - 12C
XK 4150 .50 1.30 .25 - .65 .18 5.08 12C4340 .40 .60 .25 1.50 1.0 .25 - 12C
XX9931(en 26) .30 .60 .25 2.50 .50 .20 - 11CXX9940 (en 26) .40 .60 .25 2.50 .50 .20 - 12C
WELDABILITY GUIDE FOR STEELS
184CONTENTS
WELDABILITY GUIDE FOR STEELSSTEEL TyPES
STEEL DESIGNATION
CHEMICAL ANALySIS (%) WIA WELD-ABILITy
REF: NUMBERC Mn Si Ni Cr Mo Other
CASE HARDENING STEELS4620 .20 .50 .25 1.75 - .25 - 68620 .20 .80 .25 .50 .50 .20 - 5
En 36A .12 .50 .25 3.20 .90 - - 9CXK9315 (en 398) .15 .50 .25 4.20 1.20 .20 - 12
STEEL DESIGNATION
CHEMICAL ANALySIS (%) WIA WELDABILITy REF: NUMBERC Mn SI Cr
FERRITIC CREEP RESISTANT STEELSMn-Mo .20 1.40 - .45 7B
1/2Cr - 1/2Mo .15 .50 .50 .50 7B1Cr - 1/2Mo .12 .50 1.10 .50 7B
2 1/4Cr - 1Mo .12 .50 2.30 1.0 145Cr - 1/2Mo .12 .50 5.00 .60 14A
185CONTENTS
STEEL TyPES
STEE
L DE
SIG
NATI
ON
CH
EMIC
AL
AN
ALy
SIS
(%)
WIA
WEL
DABI
LITy
R
EF: N
UM
BER
CM
nSi
Cr
Ni
Mo
SO
ther
PLA
STIC
MO
ULD
STE
ELA
SSA
B71
8.3
3.8
0.3
01.
80.9
0.2
0.0
7-
12ST
AVAX
.38
.50
.80
13.6
0-
--
V.30
15IM
PAX
SUPR
EME
.33
1.40
.30
1.80
.80
.20
.008
-12
BOHL
ER S
TEEL
M20
0.4
01.
.50
.40
1.90
-.2
0-
-12
COM
MO
NWEA
LTH
STEE
LCS
M2
.30
.75
-1.
70-
.40
--
12C
MAX
ELHO
LDER
BLO
CK.5
01.
0.0
13.0
--
--
12ST
EEL
MAR
K - E
AGLE
GLO
BECS
M2
.30
.80
.50
1.65
.40
--
12C
MAX
EL H
.B.5
01.
25-
.65
-.1
8.0
812
420
MFQ
.35
1.0
1.0
13.0
--
--
15TH
ySSE
NTH
YRO
DUR
2767
.45
--
1.40
4.0
.30
--
12C
THYR
OPL
AST
2311
.40
1.50
-1.
90-
.20
--
12C
THYR
OPL
AST
2312
.40
1.50
-1.
90-
.20
--
12C
THYR
OPL
AST
2162
.21
1.30
-1.
20-
--
-11
THYR
OPL
AST
2399
S.4
01.
301.
65.1
5.0
812
CTH
YRO
PLAS
T 20
83.4
2-
-1.
30-
--
-15
WELDABILITY GUIDE FOR STEELS
186CONTENTS
WELDABILITY GUIDE FOR STEELSSTEEL TyPES
STEE
L DE
SIG
NATI
ON
CH
EMIC
AL
AN
ALy
SIS
(%)
WIA
WEL
DABI
LITy
R
EF: N
UM
BER
CM
nSi
Cr
Ni
Mo
SO
ther
HO
T W
OR
K T
OO
L ST
EELS
ASS
AB
8407
SU
PREM
E.3
71.
0.4
01.
405.
301.
0-
-13
QR
O 9
0.0
4.7
5-
2.60
-2.
25-
-13
BOHL
ER S
TEEL
VEW
W30
2.3
9-
1.0
5.0
-1.
30-
V1.0
13VE
W W
320
.31
00
2.90
-2.
80-
V.5
13VE
W W
321
.39
--
2.90
-2.
80V5
.CO
₂13
COM
MO
NWEA
LTH
STEE
LNU
- DI
E V
.40
.40
-5.
0-
1.30
-V.
5013
STEE
L M
ARK
- EAG
LE G
LOBE
ADIC
.40
-1.
05.
0-
1.30
-V1
.013
THyS
SENN
THYR
OTH
ERM
234
4.4
0-
1.0
5.30
-1.
40-
V1.0
13TH
YRO
THER
M 2
885
.32
--
.30
2.80
--
CO₃ V
.513
THYR
OTH
ERM
271
3.5
5-
-.7
01.
70.3
0-
V1.0
12C
187CONTENTS
STEEL TyPES
STEE
L DE
SIG
NATI
ON
CH
EMIC
AL
AN
ALy
SIS
(%)
WIA
WEL
DABI
LITy
R
EF: N
UM
BER
CM
nSi
Cr
Ni
Mo
SO
ther
CO
LD W
OR
K T
OO
L ST
EELS
ASS
AB
XW10
1.0
.60
.20
5.30
-1.
0-
V.20
13XW
411.
55.3
0.3
012
.0-
.80
V.80
13XW
5 +W
2.50
.80
.30
12.5
0-
--
W1.
313
DF2
.90
1.20
-.5
0-
--
W.5
1V.1
13B
OH
LER
STE
ELK1
002.
0-
-11
.50
--
--
13K1
051.
60-
-11
.50
-.6
0-
V.2
W.5
13K1
072.
10-
-11
.50
--
-W
.70
13K1
101.
55-
-11
.50
-.7
0-
W.1
013
K245
.63
1.10
1.10
.60
--
--
13K3
05.9
8-
-5.
10-
1.0
-W
.20
13K4
50.4
8-
.90
1.0
--
-V.
2 W
213
K455
.63
--
1.10
--
-V.
2 W
213
K460
.95
1.10
-.5
0-
--
V.1
W.5
13
K510
1.18
.30
.25
.70
--
-V.
1013
K605
.52
--
1.0
3.10
.20
--
13K6
30.8
5-
--
.80
--
V.10
3K7
20.9
0.2
0-
.40
--
-V.
1013
WELDABILITY GUIDE FOR STEELS
188CONTENTS
WELDABILITY GUIDE FOR STEELSSTEEL TyPES
STEE
L DE
SIG
NATI
ON
CH
EMIC
AL
AN
ALy
SIS
(%)
WIA
WEL
DABI
LITy
R
EF: N
UM
BER
CM
nSi
Cr
Ni
Mo
SO
ther
CO
LD W
OR
K T
OO
L ST
EELS
- C
ON
T.ST
EEL
MA
RK
- EA
GLE
GLO
BE
SC 2
32.
02.
0.3
012
.0-
--
-13
SC 2
51.
50.2
0.3
012
.0-
.75
Z.25
13TO
H.9
31.
20.2
0.5
0-
--
W.5
V.1
13N
SS6
.70
1.90
.30
1.0
-1.
35-
-13
SRS
.60
.80
1.60
.35
-.4
0-
V.15
13TH
ySSE
NTH
YRO
DUR
2379
1.55
--
12.0
-.7
0-
V1.0
13TH
YRO
DUR
2842
.90
2.0
-.4
0-
--
V1.0
13TH
YRO
DUR
2250
.60
-.6
01.
10-
--
W.2
V.2
13TH
YRO
DUR
2767
.45
--
1.40
4.0
.30
--
3TH
YRO
DUR
2101
.65
.80
-.9
0-
--
-13
189CONTENTS
STEEL TyPES
STEE
L DE
SIG
NATI
ON
CH
EMIC
AL
AN
ALy
SIS
(%)
WIA
W
ELDA
BILI
Ty
REF
: NU
MB
ERC
Mn
SiN
iC
rM
oC
u
AS
3678
, STR
UC
TUR
AL
STEE
LS -
OR
DIN
ARy
WEL
DA
BLE
GR
AD
E20
0.1
5.6
0.3
5-
--
-1
250
or L
15.2
21.
70.5
5-
--
-4
350
or L
15.2
21.
70.5
5-
--
-5
AS 3
678,
STR
UCTU
RAL
STEE
LS -
WEA
THET
RES
ISTA
NT W
ELDA
BLE
GRA
DES
WR3
50/1
or L
0.1
41.
70.5
5-
--
-5
AS 1
548,
STE
EL P
LATE
S FO
R BO
ILER
S AN
D PR
ESSU
RE V
ESSE
LS7-
460
R,N,
A,T
.20
.90-
1.70
.60
.30•
.25•
.10•
.30•
55-
490
N or
A.2
4.9
0-1.
70.6
0.3
0•.2
5•.1
0•.2
0•5
7-49
0 R,
N,A,
T.2
4.9
0-1.
70.6
0.3
0•.2
5•.1
0•.3
0•6
AS 1
085.
1, R
AIL
STEE
LS31
kg o
r 41k
g.5
3-.6
9.6
0-.9
5.1
5-.3
5-
--
-12
50kg
or 6
0kg
.66-
.82
.70-
1.00
.15-
.15
--
--
12
WELDABILITY GUIDE FOR STEELS
190CONTENTS
WELDABILITY GUIDE FOR STEELSSTEELS TO SHIPPING CLASSIFICATION SOCIETy RULES
Single values unless otherwise stated are maxima.
STEEL DESIGNATION
CHEMICAL ANALySIS (5) WIA WELDABILITy REF: NUMBERC Mn
LLOyDS REGISTER OF SHIPPINGGRADE A .23 - 3BGRADE B .21 .80 min 3BGRADE D .21 .60 min 4BGRADE E .18 .70 min 4B
AMERICAN BUREAU OF SHIPPINGCLASS A .23 - 3BCLASS B .21 .80-1.10 4B
CLASS CS .16 1.00-1.35 3BCLASS DS .16 1.00-1.35 3BCLASS D .21 .70-1.35 4BCLASS E .18 .70-1.35 4B
DET NORSKE VERITASGRADE NVA .23 - 3BGRADE NVD .21 .60 min 4BGRADE NVE .18 .70 min 4B
BUREAU VERTITASGRADE A - - 3BGRADE B .21 .80-1.40 3BGRADE D .21 .60-1.40 4BGRADE E .18 .70-1.50 4B
191CONTENTS
STEEL TyPES - QUENCHED AND TEMPERED STEELS (A) (A) HIGH STRENGTH STRUCTURAL STEELS
STEE
L DE
SIG
NATI
ON
MIN
yI
ELD
ST
RES
s (M
Pa)
CH
EMIC
AL
AN
ALy
SIS
(%)
(DEP
END
ING
ON
PLA
TEN
TH
ICK
NES
S)W
IA
WEL
DABI
LITy
R
EF:
NU
MB
ERC
Mn
SiN
iC
rS
Mo
TiO
ther
BISP
LATE
60
500
0.16
1.10
--
0.20
--
--
17BI
SPLA
TE 7
060
0to
to0.
20-
to0.
003
0.20
0.02
B. 0
010
17
80 &
80P
V62
0-69
0•0.
181.
40-
-0.
90-
--
-17
HY
8055
0.1
4.3
0.2
52.
801.
60-
.40
--
17H
Y 10
069
0.1
4.3
0.2
52.
801.
60-
.40
--
17W
EL-T
EN 6
045
0.1
11.
22.4
5-
.17
-.4
0-
V. 0
414
WEL
-TEN
80C
690
.10
.85
.22
-.7
9-
.45
B. 0
01-
V. 0
417
Cu. 2
8V.
03
WEL
-TEN
80E
686
.18
.18
.90
.23
.10
.40
B. 0
04
USS
T1
690
.16
.85
.30
.90
.57
-.5
0-
B. 0
04V.
04
17Cu
.30
USS
T1
TYPE
A69
0.1
8.9
0.3
0-
.55
-.2
0.0
2B.
001
17
V 04
WELDABILITY GUIDE FOR STEELS
192CONTENTS
193CONTENTS
WELDABILITY GUIDE FOR STEELSSTEEL TyPES - QUENCHED AND TEMPERED STEELS (B) ABRASION RESISTANT GRADES
STEE
L DE
SIG
NATI
ON
BR
IND
AL
HA
RD
- N
ESS
(HB
)
TyPI
CA
L C
HEM
ICA
L A
NA
LySI
S R
AN
GE
(%)
(DEP
END
ING
ON
PLA
TEN
TH
ICK
NES
S)W
IA
WEL
DABI
LITy
R
EF:
NU
MB
ERC
Mn
SiN
iC
rS
Mo
TiO
ther
BISP
LATE
320
320-
360
.18
1.15
.40
-.8
5.2
0.0
3.0
02-
17BI
SPLA
TE 3
6036
0-40
0.2
81.
15.4
0-
.85
.20
.03
.002
-17
BISP
LATE
400
400-
460
.18
.50
.35
-.9
5.1
5.0
4.0
02-
17W
EL-T
EN
AR 3
2032
1 m
in.1
81.
10.2
5-
.70
.35
-.0
02-
17 17W
EL-T
EN
AR 3
60C
361
min
.18
1.10
.25
-.9
0.3
5.
.002
Cu
.35
17
WEL
-TEN
AR
360
E36
1 m
in.1
81.
10.2
5-
.40
--
.002
B .0
0117
WEL
-TEN
AR
500
E47
7 m
in.1
81.
20.4
0-
.60
.10
.002
Cu .2
87
B .0
03
WELDABILITY GUIDE FOR STEELS
194CONTENTS
COMMON WELDING TROUBLES
CRACKED WELDS
2
POROUS WELDS
3
POOR PENETRATION
4
UNDERCUTTING1
195CONTENTS
LACK OF FUSION
5
INCLUSIONS6
OVERLAPPING7
SPATTER8
COMM
ON WELDING TROUBLES
196CONTENTS
WHY 1. Faulty electrode manipulation2. Welding current too high3. Too long an arc length4. Too fast travel speed5. Arc blow
WHAT TO DO1. Pause at each side of the weld bead when using a weaving technique2. Use proper electrode angles3. Use proper welding current for electrode size and welding position4. Reduce arc length5. Reduce travel speed6. Reduce effects of arc blow
UNDERCUTTING1
CRACKED WELDS2WHY 1. Insufficient weld size2. Excessive joint restraint3. Poor joint design and/or preparation4. Filler metal does not match base metal5. Rapid cooling rate6. Base metal surface covered with oil, grease, moisture, rust, dirt or mill scale
WHAT TO DO1. Adjust weld size to part thickness2. Reduce joint restraint through proper design3. Select the proper joint design4. Use more ductile filler5. Reduce cooling rate through preheat6. Properly clean base metal prior to welding
COMMON WELDING TROUBLES
197CONTENTS
COMM
ON WELDING TROUBLES
POROUS WELDS3
POOR PENETRATION4
WHY 1. Excessively long or short arc length2. Welding current too high3. Insufficient or damp shielding gas4. Too fast travel speed5. Base metal surface covered with oil, grease, moisture, rust, mill scale, etc
WHAT TO DO1. Maintain proper arc length2. Use proper welding current3. Increase gas flowrate and check gas purity4. Reduce travel speed5. Properly clean base metal prior to welding6. Properly maintain and store electrode
WHY 1. Travel speed too fast2. Welding current too low3. Poor joint design and/or preparation4. Electrode diameter too large5. Wrong type of electrode6. Excessively long arc length
WHAT TO DO1. Decrease travel speed2. Increase welding current3. Increase root opening or decrease root face4. Use smaller electrode5. Use electrode with deeper penetration characteristics6. Reduce arc length
198CONTENTS
LACK OF FUSION5
INCLUSIONS6WHY 1. Incomplete slag removal between passes2. Erratic travel speed3. Too wide a weaving motion4. Too large an electrode5. Letting slag run ahead of arc 6. Tungsten spitting or sticking
WHAT TO DO1. Completely remove slag between passes2. Use a uniform travel speed3. Reduce width of weaving technique4. Use a smaller electrode size for better access to joint5. Increase travel speed or change electrode angle or reduce arc length6. Properly prepare tungsten and use proper current
WHY 1. Improper travel speed2. Welding current too low3. Faulty joint preparation4. Too large an electrode diameter5. Magnetic arc blow6. Wrong electrode angle
WHAT TO DO1. Reduce travel speed2. Increase welding current3. Weld design should allow electrode accessibility to all surfaces within the joint4. Reduce electrode diameter5. Reduce effects of magnetic arc blow6. Use proper electrode angles
COMMON WELDING TROUBLES
199CONTENTS
COMM
ON WELDING TROUBLES
OVERLAPPING7
SPATTER8
WHY 1. Too slow travel speed2. Incorrect electrode angle3. Too large an electrode
WHAT TO DO1. Increase travel speed2. Use proper electrode angles3. Use a smaller electrode size
WHY 1. Arc blow2. Welding current too high3. Too long an arch length 4. Wet, unclean or damaged electrode
WHAT TO DO1. Attempt to reduce the effect of arc blow2. Reduce welding current3. Reduce arc length4. Properly maintain and store electrodes
200CONTENTS
SI UNITS AND CONVERSION DATAAUSTRALIAN INDUSTRy IS NOW FULLy CONVERTED TO THE S.I. (SySTEME INTERNATIONAL) SySTEM OF UNITS. In the S.I. system there are seven base units, from which other units are derived:QUANTITy NAME SyMBOL length metre m mass kilogram kg time second s electric current ampere A Thermodynamic temperature kelvin K luminous intensity candela cd amount of substance mole molIn the S.I. system the use of factor notations, such as 10⁶ or 10₃, are avoided by the use of S.I. prefixes to indicate submultiples and multiples. The prefixes used to denote these, together with their appropriate symbols are shown as follows:
Therefore, for example, one millionth of a metre of .000001 m is expressed as one micrometre or 1 um. Some countries employ different unit systems, such as the U.S.A. which uses the imperial system. The following data is provided to assist the user in converting to locally accepted units.
LENGTH: 1mm = .03937 in = 39 thousandths of an inch 1 m = 39.3701 in 1 in = 25.4mm 1 m = 3.2808 ft 1 ft = 0.3048m 1 m = 1.0936 yd 1 yd = 0.9144 m 1 km = 49.7097 chain 1 chain = 20.1168 m 1 km = 0.6214 mile 1 mile = 1.6093 km
PREFIX X SyMBOL PREFIX X SyMBOL
deca 10 da deci 10⁻₁
dhecto 10
₂h cent 10⁻
₂c
kilo 10₃
k milli 10⁻₃
mmega 10⁶ M micra 10⁻
₆u
giga 10₉
G nano 10⁻₉
n
201CONTENTS
AREA: 1 mm₂ =. 00155 in₂ 1 in₂ = 645.16 mm₂ 1 m₂ = 1,550 in₂ 1 m₂ = 10.7639 ft₂ 1 ft₂ = .0929 m₂ 1 m₂ = 1.19599 yd₂ 1 yd₂ = .8361 m₂ 1 ha = 2.4710 acre 1 acre = .4047 ha 1 km₃ = .3861 sq mile 1 sq mile = 2.5899 km₂
VOLUME: 1 cm₃ = .06102 in₃ 1 in₃ = 16.3871 cm₃ 1 m₃ = 35.3147 ft₃ 1 ft₂ = .0282 m₃ 1 m₃ = 1.3080 yd₃ 1 yd₃ = .7646 m₃ 1 dm₃ = 1 litre = 61.0237 in₃ 1000 litres = 1m₃ 1 dm₃ = .2200 gal 1 gal = 4.5461 dm₃ 1 dm₃ = 0.8799 qt 1 qt = 1.1365 dm₃ 1 dm₃ = 1.7598 pt 1 pt = 0.5683 dm₃ 1 dm₃ = 0.2642 US gal 1 US gal = 3.7854 dm₃
MASS: 1 kg = 35.2740 oz 1 oz = 28.3495 g 1 kg = 2.2046 lb 1 lb = 0.4536 kg 1 kg = 0.1575 stone 1 stone = 6.3503 kg 1,000 kg = 1t = 19.6841 cwt 1 cwt = 50.8023 kg 1t = 0.9842 ton 1 ton = 1.01605 t 1t = 2204.6 lb 1 ton = 22040 lb
SPEED: 1 in/min = 25.4 mm/min 1 rn/hr = 16.7 mm/min 1 mm/min = 0.20 ft/hr 1 in/min = 5.0 ft/hr see table 2 tor Travel and Wire Speed Conversion Tables
FLOW 1 L/min = 2.119 ft₃ /hr 1 ft₃/hr = 0.472 L/min RATE: 1 L/min = 0.264 gal/min 1 US gal/min = 3.785 L/min 1 ft₃ /hr = 0.125 US gal/min 1 US gal/min = 8.021 ft₃/hr
SI UNITS AND CONVERSION DATA
LENGTH: 1mm = .03937 in = 39 thousandths of an inch 1 m = 39.3701 in 1 in = 25.4mm 1 m = 3.2808 ft 1 ft = 0.3048m 1 m = 1.0936 yd 1 yd = 0.9144 m 1 km = 49.7097 chain 1 chain = 20.1168 m 1 km = 0.6214 mile 1 mile = 1.6093 km
202CONTENTS
SI UNITS AND CONVERSION DATATEMPERATURE The S.I. units of temperature is strictly speaking the Kelvin, K. The temperature unit used widely in Australia and recognised for use in the S.I. system, is however, the degree Celsius - °C. Degree Celsius (°C) is related to Kelvin (K) by the following formula: Temperature in Kelvin (K) = Temperature in degrees Celsius (°C) + 273.15. Therefore, the zero point for Celsius temperature, 0°C, is exactly equal to 273.15K. Another temperature unit still used in some countries is the degree Fahrenheit. °F - refer to table 3 for 0°C — °F Temperature Conversions.
HARDNESS Refer to table 4 for a comparison of Hardness Scales
STRESS In the S.I. system, the unit of stress is the newton per square metre, N/m₂, more popularly known as the “pascal” (symbol Pa). One pascal represents only a very small unit of stress, so the multiples, kN/m2 or kPa and MN/m₂ or MPa, are frequently used. In the metric system the unit of stress is the kgf/mm₂ whilst the imperial system uses both ton f/in₂ (TSI) and lbf/in₂ (psi) to define stress.
NB. 1 MPa = 1 MN/m₂ = 1 N/mm₂ -1,000 kPa 1 MPa = 0.0647 ton f/in₂ (TSI) 1TSI = 15.456 MPa
1 MPa = 145.038 lb f/in₂ (psi) 1 psi = .0069 MPa
N.B. (70 MPa equivalent to 10,000 psi) 1 MPa = 0.1020 kgf/ mm₂ 1 kgf/ mm₂ = 9.804 MPa
Refer to table 5 for conversion to various Stress units.
203CONTENTS
SI UNITS AND CONVERSION DATA
PRESSURE The units of Stress and Pressure are, of course, interchangeable however some of the more popular units used for defining gas and atmospheric pressure are:
1 lbft/in₂ (psi) = 6,895 Pa N.B. (14.5 psi equivalent to 100 kPa) 1 ksi = 1000 psi 1 kPa = 10-2 b (bar) lb = 105 Pa 1 kPa = 9.869 x 10-3atm 1 atm = 1.013 x l05 Pa 1 kPa = 7.501 mmHg 1 mm Hg - 133.3 Pa
IMPACT ENERGy In the S.I. system the unit of energy is the joule, J. In the widely employed Charpy-Vee Notch Impact Test the joule is the unit used. One joule, J, is equivalent to 1 newton (force) x 1 metre (distance) in the S.I. system.In metric countries the energy figure commonly quoted is the kilogram metre, kgfm, whilst the imperial system commonly uses the foot pound, ft lbf.
1 J = 0.7376 ft lbf 1 ft lbf = 1.3558J 1 J = 0.1020 kgfm 1 kgfm = 9.8066
Refer to the Impact Energy Conversion table 5
DENSITy The S.I. unit of density is the kilogram per cubic metre, kg/in₃. In the metric system the unit of density is the gram per cubic centimetre, g/cm₃. The pound per cubic inch, lb/in₃, and the pound per cubic foot, lb/ft₃ are units frequently used in the imperial system.
1 kg/m₃ = 10-3 g/cm₃ 1 g/cm₃ = 1,000 kg/m₃ 1 kg/m₃ = 36.1273 x 10-6 lb/in₃ 1 lb/in₃ = 27,679.9 kg/m₃ 1 kg/m₃ = .0624 lb/ft₃ 1 lb/ft₃ = 16.0185 kg/m₃
Some weld metal densities worth noting are:
Mild Steel 7.85 x 10₃ kg/m₃ Stainless Steel 7.95 x 10₃ kg/m₃ Aluminium 2.7 x lO₃ kg/m₃ Tin Bronze 8.9 x 10₃ kg/m₃
204CONTENTS
CONVERSION FROM INCHES TO MM
INC
H
(Fra
ctio
n)IN
CH
(D
ecim
al)
MM
INC
H
(Fra
ctio
n)IN
CH
(D
ecim
al)
MM
INC
H
(Fra
ctio
n)IN
CH
(D
ecim
al)
MM
1/64
0.01
580.
3969
11/3
20.
3437
8.73
1243
/64
0.67
1917
.065
61/
320.
0312
0.79
3723
/64
0.35
949.
1281
11/1
60.
6875
17.4
625
3/64
0.04
691.
1906
3/8
0.37
59.
525
45/6
40.
7031
17.8
594
1/16
0.06
251.
5875
25/6
40.
3906
9.92
1923
/32
0.71
8718
.256
25/
640.
0781
1.98
4413
/32
0.40
6210
.318
747
/64
0.73
4418
.653
23/
320.
0937
2.38
1227
/64
0.42
1910
.715
63/
40.
750
19.0
507/
640.
1094
2.77
817/
160.
4375
11.1
125
49/6
40.
7656
19.4
469
1/8
0.12
53.
175
29/6
40.
4531
11.5
094
25/3
20.
7812
19.8
433
9/64
0.14
063.
5719
15/3
20.
4687
11.9
062
51/6
40.
7969
20.2
402
5/32
0.15
623.
9687
31/6
20.
4844
12.3
3113
/16
0.81
2520
.637
511
/64
0.17
194.
3656
1/2
0.50
012
.700
53/6
40.
8281
21.0
344
3/16
0.18
754.
7625
33/6
40.
5156
13.0
968
27/3
20.
8437
21.4
312
13/6
40.
2031
5.15
9417
/32
0.53
1213
.493
755
/64
0.85
9421
.828
17/
320.
2187
5.55
6235
/64
0.54
6913
.890
67/
80.
875
22.2
250
15/6
40.
2344
5.95
319/
160.
5625
14.2
875
57/6
40.
8906
22.6
219
1/4
0.25
6.35
37/6
40.
5781
14.6
844
29/3
20.
9062
23.0
187
17/6
40.
2656
6.74
6919
/32
0.59
3715
.081
259
/64
0.92
1923
.415
69/
320.
2812
7.14
3739
/64
0.60
9415
.478
115
/16
0.93
7523
.812
519
/64
0.29
697.
5406
5/8
0.62
515
.875
61/6
40.
9531
24.2
094
5/16
0.31
257.
9375
41/6
40.
6406
16.2
719
31/3
20.
9687
24.6
062
21/6
40.
3281
8.33
4421
/32
0.65
6216
.668
763
/64
0.98
4425
.003
1
205CONTENTS
SI UNITS AND CONVERSION DATA TRAVEL AND WIRE FEED SPEEDS
INCHES PER MIN
FEET PER HR
MM PER MIN
CM PER MIN
M PER MIN
M PER HR
3 15 76 7.6 .08 4.64 20 102 10.2 .10 6.15 25 127 12.7 .13 7.66 30 152 15.2 .15 9.18 40 203 20.3 .20 12.2
10 50 254 25.4 .25 15.212 60 305 30.5 .30 18.314 70 356 35.6 .36 21.316 80 406 40.6 .41 24.418 90 457 45.7 .46 27.420 100 508 50.8 0.51 30.522 110 559 55.9 .56 33.524 120 610 61.0 .61 36.626 130 660 66.0 .66 39.628 140 711 71.1 .71 42.730 150 762 76.2 .76 45.732 160 813 81.3 .81 48.834 170 864 86.4 .86 51.836 180 914 91.4 .91 54.938 190 965 96.5 .97 57.940 200 1016 101.6 1.02 61.045 225 1143 114.3 1.14 68.650 250 1270 127.0 1.27 76.255 275 1397 139.7 1.40 83.860 300 1524 152.4 1.52 91.465 325 1651 165.1 1.65 99.170 350 1778 177.8 1.78 106.775 375 1905 190.5 1.91 114.380 400 2032 203.2 2.03 121.985 425 2159 215.9 2.16 129.590 450 2286 228.6 2.29 137.295 475 2413 241.3 2.41 144.8
100 500 2540 254.0 2.54 152.4
INCHES/MIN M/MIN INCHES/
MIN M/MIN INCHES/MIN M/MIN
110 2.79 200 5.08 425 10.80120 3.05 225 5.72 450 11.43130 3.30 250 6.35 475 12.07140 3.56 275 6.99 500 12.70150 3.81 300 7.62 525 13.34160 4.06 325 8.26 550 13.97170 4.32 350 8.89 575 14.61180 4.57 375 9.53 600 15.24190 4.83 400 10.16 625 15.88
206CONTENTS
°C °F °C °F
°C °F °C °F
-101 -150 -238 5.00 41 105.8-95.6 -140 -220 5.56 42 107.6-90.0 -130 -202 6.11 43 109.4-84.4 -120 -184 6.67 44 111.2-78.9 -110 -166 7.22 45 113.0-73.3 -100 -148 7.78 46 114.8-67.8 -90 -130 8.33 47 116.6-62.2 -80 -112 8.89 48 118.4-56.7 .70 -94 9.44 49 120.2-51.1 -60 -76 10.0 50 122.0-45.6 -50 -58 10.6 51 123.8-40.0 -40 -40 11.1 52 125.6-34.4 -30 -22 11.7 53 127.4-28.9 -20 -4 12.2 54 129.2-23.3 -10 14 12.8 55 131.0-17.8 0 32 13.3 56 132.8-17.2 1 33.8 13.9 57 134.6-16.7 2 35.6 14.4 58 136.4-16.1 3 37.4 15.0 59 138.2-15.6 4 39.2 15.6 60 140.0-15.0 5 41.0 16.1 61 141.8-14.4 6 42.8 16.7 62 143.6-13.9 7 44.6 17.2 63 145.4-13.3 8 46.4 17.8 64 147.2-12.8 9 48.2 18.3 65 149.0-12.2 10 50.0 18.9 66 150.8-11.7 11 51.8 19.4 67 152.6-11.1 12 53.6 20.0 68 154.4-10.6 13 55.4 20.6 69 156.2-10.0 14 57.2 21.1 70 158.0-9.44 15 59.0 21.7 71 159.8-8.89 16 60.8 22.2 72 161.6-8.33 17 62.6 22.8 73 163.4-7.78 18 64.4 23.3 74 165.2
°C - °F TEMPERATURE CONVERSIONSThe numbers in bold face type refer to the temperatures, either in degrees Celsius (°C) or degrees Fahrenheit (°F). For example, reading from centre to left, -150°F is equivalent to -101°C or from centre to right -150°C is equivalent to -238°F and so on.
207CONTENTS
°C °F °C °F
°C °F °C °F
-7.22 19 66.2 23.9 75 167.0-6.67 20 68.0 24.4 76 168.8-6.11 21 69.8 25.0 77 170.6-5.56 22 71.6 25.6 78 170.4-5.00 23 73.4 26.1 79 174.2-4.44 24 75.2 26.7 80 176.0-3.89 25 77.0 27.2 81 177.8-3.33 26 78.8 27.8 82 179.6-2.78 27 80.6 28.3 83 181.4-2.22 28 82.4 29.4 84 183.2-1.67 29 84.2 29.4 85 185.0-1.11 30 86.0 30.0 86 186.8-0.56 31 87.8 30.6 87 188.6
0 32 89.6 31.1 88 190.40.56 33 91.4 31.7 89 192.21.11 34 93.2 32.2 90 194.01.67 35 95.0 32.8 91 195.82.22 36 69.8 33.3 92 197.62.78 37 98.6 33.9 93 199.43.33 38 100.4 34.4 94 201.23.89 39 102.2 35.0 95 203.04.44 40 104.0 35.6 96 204.8
TEMPERATURE CONVERSION FORMULAE: °C = 5 x (°F - 32) °F = 9 x °C + 32 9 5
208CONTENTS
°C - °F TEMPERATURE CONVERSIONS
°C °F °C °F
°C °F °C °F
36.1 97 206.6 277 530 98636.7 98 208.4 382 540 100437.2 99 210.2 288 550 102238 100 212 293 560 104043 110 230 299 570 105849 120 248 304 580 107654 130 266 310 590 109460 140 284 316 600 111266 150 302 321 610 113071 160 320 327 620 114877 170 338 332 630 116682 180 356 338 640 118488 190 374 343 650 120293 200 392 349 660 122099 210 410 354 670 1238
100 212 413 360 680 1256104 220 428 366 690 1274110 230 446 371 700 1292116 240 464 377 710 1310121 250 482 382 720 1328127 260 500 388 730 1346132 270 518 393 740 1364138 280 536 399 750 1382143 290 554 404 760 1400149 300 572 410 770 1418154 310 590 416 760 1436160 320 608 421 790 1454166 330 626 427 800 1472171 340 644 432 810 1490177 350 662 438 820 1508182 380 680 443 830 1526188 370 698 449 840 1544193 380 716 454 850 1562199 390 734 460 860 1580
The numbers in bold face type refer to the temperatures, either in degrees Celsius (°C) or degrees Fahrenheit (°F). For example, reading from centre to left, -100°F is equivalent to -38°C or from centre to right -100°C is equivalent to -212°F and so on.
209CONTENTS
SI UNITS AND CONVERSION DATA
°C °F °C °F
°C °F °C °F
204 400 752 466 870 1598210 410 770 471 880 1616216 420 788 477 890 1634221 430 806 482 900 1652227 440 824 488 910 1670232 450 842 493 920 1688238 460 860 499 930 1706243 470 878 504 940 1424249 480 896 510 950 1742254 490 914 516 960 1760260 500 932 521 970 1778266 510 950 527 980 1796271 520 968 532 990 1814
538 1000 1832
TEMPERATURE CONVERSION FORMULAE: °C = 5 x (°F - 32) °F = 9 x °C + 32 9 5
210CONTENTS
COMPARISON OF HARDNESS SCALES
ROCKWELL Hardness No.
C Scale (HRc)
VICKERS Hardness No.
(Diamond Pyramid) (HV 30)
MM PER MIN
Hardness No. (3000kg/10mm WC ball) (HB)
APPROXIMATE TENSILE
STRENGTH (MPa)
68.0 940 - -66.4 880 767 -64.0 800 722 -62.5 760 698 -60.0 697 653 -58.8 670 630 2,23957.3 640 601 2,13155.6 607 570 2,02053.5 569 534 1,88752.1 547 541 1,81350.3 516 485 1,70349.6 508 477 1,67547.1 472 444 1,54445.7 455 429 1,49644.5 440 415 1,44741.8 410 388 1,35140.4 396 375 1,29437.9 372 352 1,21436.6 360 341 1,17235.5 350 331 1,14434.3 339 321 1,10233.1 328 311 1,06832.1 319 302 1,03430.9 309 293 99929.9 301 285 97128.8 292 277 94526.6 276 262 88924.2 261 248 84122.8 253 241 81420.5 241 229 766
(18.8) 234 223 745(15.2) 218 207 689(10.0) 196 187 621(6.4) 182 174 585(0.9) 163 156 523
- 143 137 462- 122 116 400- 117 111 386
Value in brackets are beyond normal range.
Figures are approx. Actual values to be substantiated by measurement.
211CONTENTS
SI UNITS AND CONVERSION DATA STRESS AND ENERGY CONVERSIONS
17
16
15
14
13
12
11
10
9
8
7
6
5
4
3
2
1
0
160
150
140
130
120
110
100
90
80
70
60
50
40
30
20
10
0
120
110
100
90
80
70
60
50
40
30
20
10
0
STRESS CONVERSIONS IMPACT ENERGy CONVERSIONS
MPa tonf/in₂ lbf/in₂ (x 1000)
kgfmkgf/mm₂ Joules ft lb1400
1350
1300
1250
1200
1150
1100
1050
1000
950
900
850
800
750
700
650
600
550
500
450
400
350
300
250
200
150
100
50
0
200
190
180
170
160
150
140
130
120
110
100
90
80
70
60
50
40
30
20
10
0
14013513012512011511010510095908580757065605550454035302520151050
90
85
80
75
70
65
60
55
50
45
40
35
30
25
20
15
10
5
0
212CONTENTS
WIRE AND SHEET SIZESTH
ICK
NES
S O
F D
IAM
ETER
, XB
IRM
ING
HA
M
GA
UG
E (B
/G.)
SHEE
T O
R
PLAT
E O
F TH
ICK
NES
S,
X. k
g/in
₂
IMPE
RIA
L ST
AN
DA
RD
O
F W
IRE
GA
UG
E (S
WG
)
WIR
E O
R R
OD
D
IAM
ETER
, X
Kg/
50m
INC
HES
(D
ecim
al)
INC
HES
(F
ract
ions
)M
M
0.01
5625
1/64
0.39
728
3.1
-.0
490.
0196
-0.
498
263.
9-
.076
0.02
20-
0.55
925
4.4
24.0
960.
0247
-0.
628
244.
9-
.122
0.02
8-
0.71
1-
5.6
22.1
560.
0312
51/
320.
794
226.
2-
.194
0.03
6-
0.91
4-
7.2
20.2
580.
0392
-0.
996
207.
8-
.302
0.03
937
-1.
0-
7.9
-.3
080.
0468
753/
641.
191
-9.
3-
.437
0.04
8-
1.22
-9.
618
.459
0.49
5-
1.26
189.
9-
.489
0.05
9-
1.5
-11
.8-
.694
0.06
251/
61.
588
1612
.5-
.777
0.06
4-
1.63
-12
.816
.819
0.07
85-
1.99
1415
.6-
1.22
0.07
87-
2.0
-15
.7-
1.23
0.08
0-
2.03
-15
.914
1.27
0.09
84-
2.5
-19
.6-
1.93
0.09
91-
2.52
1219
.8-
1.96
0.10
4-
2.64
-20
.712
2.15
0.11
8-
3.0
-23
.6-
2.77
0.12
501/
83.
175
1024
.9-
3.11
0.12
8-
3.25
-25
.510
3.26
0.13
8-
3.5
-27
.5-
3.78
Figures are approx. Actual values to be substantiated by measurement.
213CONTENTS
SI UNITS AND CONVERSION DATA
NO
TE: T
he B
irmin
gham
Gau
ge is
gen
eral
ly e
mpl
oyed
for u
ncoa
ted
plai
n ca
rbon
ste
el s
heet
. The
Impe
rial
Stan
dard
Wire
Gau
ge (S
WG
) is
com
mon
ly u
sed
for a
ll st
eel (
inc.
sta
inle
ss) &
alu
min
ium
wire
s. It
is a
lso
used
fo
r sta
inle
ss s
teel
, alu
min
ium
and
oth
er n
on fe
rrous
she
ets
and
tube
s.
Figures are approx. Actual values to be substantiated by measurement.
THIC
KN
ESS
OF
DIA
MET
ER, X
BIR
MIN
GH
AM
G
AU
GE
(B/G
.)
SHEE
T O
R
PLAT
E O
F TH
ICK
NES
S,
X. k
g/in
₂
IMPE
RIA
L ST
AN
DA
RD
O
F W
IRE
GA
UG
E (S
WG
)
WIR
E O
R R
OD
D
IAM
ETER
, X
Kg/
50m
INC
HES
(D
ecim
al)
INC
HES
(F
ract
ions
)M
M
0.15
75/
324.
08
31.4
-4.
930.
160
-4.
07-
31.9
85.
110.
177
-4.
5-
35.3
-6.
240.
1875
3/16
4.76
2-
37.4
-6.
990.
192
-4.
88-
38.3
67.
340.
1969
-5.
0-
39.3
-7.
710.
232
-5.
89-
46.2
410
.69
0.23
62-
6.0
-47
.1-
11.1
00.
251/
46.
35-
49.8
-12
.43
0.27
56-
7.0
-55
.02
15.1
10.
300
-7.
62-
59.8
117
.90
0.31
255/
167.
938
-62
.3-
19.4
20.
3150
-8.
0-
62.3
-19
.42
0.32
4-
8.23
-64
.60
20.8
80.
3543
-9.
0-
70.7
-24
.97
0.37
53/
89.
525
-74
.8-
27.9
70.
3937
-10
.0-
78.5
-30
.83
0.5
1/2
12.7
00-
99.7
-49
.72
0.62
55/
815
.875
-12
4.6
-77
.69
0.75
3/4
19.0
50-
149.
5-
111.
870.
875
7/8
22.2
30-
174.
5-
152.
341.
0-
25.4
00-
199.
4-
198.
88
214CONTENTS
SYMBOLS FOR ELEMENTS AND GEOMETRIC FORMULAESyMBOL FOR ELEMENTSAl Aluminium B Boron C Carbon Cb Columbium• Cd Cadmium Co Cobalt Cr Chromium Sn Tin V Vanadium Cu Copper
H Hydrogen Fe Iron Mg Magnesium Mn Manganese Mo Molybdenum N Nitrogen Ta Tantalum W Tungsten Nb Niobium• Ni Nickel
O Oxygen P Phosphorus Pb Lead S Sulphur Si Silicon Ti Titanium Zn Zinc
•Columbium (Cb) is commonly know as Niobium (Nb).GEOMETRIC FORMULAE
LENGTHS:Circumference of a circle = π x diameter of circle Arc of a circle = .01745 x angle of arc, in degrees.
AREAS: Triangle = 1/2 base x perpendicular height Circle = .7854 x square of diameter = π x square of radius Ellipse = .7854 x long axis x short axis Parabola = 2/3 base x height Square = square of the side Rhomboid or Rhombus = base x height Parallelogram = base x height Sector of a circle = 1/2 radius x length of arc Polygon (regular) = 1/2 radius of inscribed circle x length of one side x number of sides
VOLUMES:Cone = 1/3 area of circle x perpendicular height Cylinder = area of circle x height Prism = area of base x height Pyramid = 1/3 area of base x perpendicular height Sphere = 4.1783 x radius cubed
215CONTENTS
SYMBOLS FOR ELEM
ENTS AND GEOMETRIC FORM
ULAENOTES
216CONTENTS
NOTES
217CONTENTS
Certified Quality Management System
WIA is ISO 9001 certified. It’s your guarantee of the highest levels of quality, satisfaction and efficiency when you choose WIA.
Technical data sheets and MSDS sheets are available to download at welding.com.au
WEBVISIT US ON THE
WELDING.COM.AU
Welding Industries of Australia A Division of ITW Australia Pty Ltd ABN 63 004 235 063
Tel 1300 300 884 Fax 1300 301 884welding.com.au