  • Lincoln Cellulosic Electrodes.

  • Liability: All information in this data sheet is based on the best available knowledge, is subject to change without notice and canonly be considered as suitable for general guidance Fumes: Consult information on Welding Safety Sheet, available upon request

    www.lincolnelectric.eu

    SM

    AW

    Fleetweld 5P+Cellulosic electrode

    ClassificationAWS A5.1 : E6010ISO 2560-A : E 42 3 C 25

    General descriptionCellulosic coated electrode for pipe and general weldingGives high ductility root weldsVery deep penetration ensures sound root passEasy striking, easy slag releaseHigh volume of generated gas eliminates porosityReduces problems from dirt and oil on surface

    Welding positions

    ISO/ASME PF/5Gup PG/5Gdown

    Current typeDC +

    ApprovalsLR TV3 +

    Chemical composition (w%), typical, all weld metal C Mn Si

    0.15 0.50 0.25

    Mechanical properties, all weld metalCondition Yield strength Tensile strength Elongation Impact ISO-V(J)

    (N/mm2) (N/mm2) (%) -20C -29C -30C

    Required: AWS A5.1 min. 331 min. 414 min. 22 27ISO 2560-A min. 420 500-640 min. 20 47

    Typical values AW 440 520 26 70 65

    Packaging and available sizesDiameter (mm) 2.5 3.2 4.0 5.0Length (mm) 350 350 350 350

    Unit: metal can Pieces / unit 325 205 130 83Net weight/unit (kg) 5.0 5.2 5.1 5.1

    Identification Imprint: 6010-FW5P+ Tip Color: none Fleetweld 5P+: rev. EN 22

    66

  • SM

    AW

    Fleetweld 5P+

    Materials to be weldedSteel grades/Code Type

    Pipe materialEN 10208-1 L 210, L 240EN 10208-2 L 240 , L 290, L 360EN 10216-1 / 10217-1 P 235, P 275, P 355API 5LX X42, X46, X52Gaz de France X42, X46, X52

    Calculation dataSizes Current Current Arc time Energy Dep.rate Weight/ Electrodes/ kg Electrodes/

    Diam. x length range type - per electrode at max. current - 1000 pcs. kg weldmetal kg weldmetal(mm) (A) (s)* E(kJ) H(kg/h) (kg) B 1/N

    2.5x350 40-70 DC+ 15.83.2x350 65-130 DC+ 26.24.0x350 90-175 DC+ 40.05.0x350 140-225 DC+ 61.5

    Welding parameters, optimum fill passesWelding positions PF/5G up PG/5G downDiameter (mm)

    2.5 55A 65A3.2 90A 110A4.0 130A 150A5.0 150A 165A

    Remarks/ Application advicePreheating pipe material L360 (X52) required (acc. EN 1011-1).Pipeclamps to be removed after finishing root pass, start welding hot pass (within 5 min) after root pass

    67

  • Liability: All information in this data sheet is based on the best available knowledge, is subject to change without notice and can

    only be considered as suitable for general guidance Fumes: Consult information on Welding Safety Sheet, available upon request

    www.lincolnelectric.eu

    SMAW

    Shield Arc 70+

    High strength cellulosic electrode

    Classification

    AWS A5.5 : E8010-GISO 2560-A : E 46 4 1Ni C 25

    General description

    Cellulosic coated electrode for vertical down pipe welding

    Suitable for pipe with strengths in the range of X56 - X70

    Can be used for root, fill and capping passes

    Low susceptibility to wagon tracks, windows and pinholes

    Good impact values

    Can be used for silicon-killed steels

    Welding positions

    ISO/ASME PG/5Gdown

    Current type

    DC +

    Approvals

    TV+

    Chemical composition (w%), typical, all weld metal

    C Mn Si Ni Cr V P S0.12 0.90 0.20 0.85 0.10 0.03 0.012 0.013

    Mechanical properties, all weld metal

    Condition 0.2% Proof strength Tensile strength Elongation Impact ISO-V(J)(N/mm2) (N/mm2) (%) -20C -40C

    Required: AWS A5.5 min. 460 min. 550 min. 19 not requiredISO 2560-A min. 460 530-680 min. 20 min. 47

    Typical values AW 510 570 24 75

    Packaging and available sizes

    Diameter (mm) 3.2 4.0 5.0Length (mm) 350 350 350

    Unit: Metal can Pieces / unit 320 195 125Net weight/unit (kg) 8.3 7.7 7.8

    Identification Imprint: 8010-G SA70+ Tip Color: none Shield Arc 70+: rev. EN 21

    126

  • SMAW

    Shield Arc 70+

    Materials to be welded

    Steel grades/Code Type

    Pipe material

    EN 10208-2 L 360, L 415, L 445, L 480

    EN 10216-1 / 10217-1 P 355

    API 5LX X 56, X60, X65, X70

    Gaz de France X52, X63

    Calculation data

    Sizes Current Current Arc time Energy Dep.rate Weight/ Electrodes/ kg Electrodes/Diam. x length range type - per electrode at max. current - 1000 pcs. kg weldmetal kg weldmetal

    (mm) A) (s)* E(kJ) H(kg/h) (kg) B 1/N

    3.2 x 350 75 - 130 DC+ 25.84.0 x 350 90 - 185 DC+ 39.55.0 x 350 140 - 225 DC+ 62.3

    Welding parameters, optimum fill passes

    Welding positions PG/5G downDiameter (mm)

    3.2 110A4.0 150A5.0 165A

    Remarks/ Application advice

    Preheating pipe material from L360 to L480 (X56 to X70) required (acc. EN 1011-1).Pipeclamps to be removed after finishing root pass, start welding hot pass (within 5 min) after root passUse electrodes directly from metal cansUse Fleetweld 5P+ for lower hardness in the root pass

    127

  • Liability: All information in this data sheet is based on the best available knowledge, is subject to change without notice and canonly be considered as suitable for general guidance Fumes: Consult information on Welding Safety Sheet, available upon request

    www.lincolnelectric.eu

    SMAW

    Shield Arc 6P+Cellulosic electrode

    ClassificationAWS A5.1 : E6010ISO 2560-A : E 42 3 C 25

    General descriptionCellulosic electrode for pipe weldingSmooth arcSoft and ductile root weldsSuitable for root, fill and cap passes up to X52 grades

    Welding positions

    ISO/ASME PF/5Gup PG/5Gdown

    Current typeDC + / -

    Chemical composition (w%), typical, all weld metal C Mn Si P S

    0.11 0.55 0.18 0.009 0.009

    Mechanical properties, all weld metalCondition Yield strength Tensile strength Elongation Impact ISO-V(J)

    (N/mm2) (N/mm2) (%) -29C -30C

    Required: AWS A5.1 min. 331 min. 414 min. 22 27ISO 2560-A min. 420 500-640 min. 20 47

    Typical values AW 420-524 503-594 24-33 51-85

    Packaging and available sizesDiameter (mm) 3.2 4.0Length (mm) 350 350

    Unit: metal can Pieces / unit 205 130Net weight/unit (kg) 5.2 5.1

    Identification Imprint: 6010 Shield Arc 6P+ Tip Color: none Shield Arc 6P+: rev. EN 02

    130

  • Liability: All information in this data sheet is based on the best available knowledge, is subject to change without notice and canonly be considered as suitable for general guidance Fumes: Consult information on Welding Safety Sheet, available upon request

    www.lincolnelectric.eu

    SMAW

    Shield Arc 6P+

    Materials to be weldedSteel grades/Code Type

    Pipe materialAPI 5LX X42, X46, X52

    Calculation dataSizes Current Current Arc time Energy Dep.rate Weight/ Electrodes/ kg Electrodes/

    Diam. x length range type - per electrode at max. current - 1000 pcs. kg weldmetal kg weldmetal(mm) (A) (s)* E(kJ) H(kg/h) (kg) B 1/N

    3.2x350 65-130 DC+/- 46 25.34.0x350 90-175 DC+/- 52 39.2

    Welding parameters, optimum fill passesWelding positions 5G up 5G downDiameter (mm)

    3.2 90A 110A4.0 130A 150A

    Remarks/ Application advicePreheating pipe material L360 (X52) required (acc. EN 1011-1).Pipeclamps to be removed after finishing root pass, start welding hot pass (within 5 min) after root passUse electrodes directly from metal cans

    131

  • Liability: All information in this data sheet is based on the best available knowledge, is subject to change without notice and canonly be considered as suitable for general guidance Fumes: Consult information on Welding Safety Sheet, available upon request

    www.lincolnelectric.eu

    SMAW

    Shield Arc 7P+High strength Cellulosic electrode

    ClassificationAWS A5.5 E7010-P1/E7010-GISO 2560-A : E 42 3 Z C 25

    General descriptionCellulosic electrode for pipe weldingSuitable for root, fill and cap passes up to X65 gradesHigh resistance to porosityEasy welding puddle controlHigh stacking efficiency: fill joints in fewer passesMicro-alloyed to ensure consistent mechanical properties

    Welding positions

    ISO/ASME PG/5Gdown

    Current typeDC + (Also DC- for dia.4mm)

    Chemical composition (w%), typical, all weld metal C Mn Si Ni Mo P S

    0.12-0.23 0.5-0.9 0.14-0.32 0.62-0.95 0.12-0.3 0.015 0.015

    Mechanical properties, all weld metalCondition Yield strength Tensile strength Elongation Impact ISO-V(J)

    (N/mm2) (N/mm2) (%) -20C -29C -40C

    Required: AWS A5.1 min.414 min480 min. 22 min.27ISO 2560-A min. 420 500-640 min. 20 47

    Typical values AW 427-520 496-635 23-30 34-102 27-85

    Packaging and available sizesDiameter (mm) 4.0 5.0Length (mm) 350 350

    Unit: metal can Pieces / unit 120 80Net weight/unit (kg) 4.7 5.0

    Identification Imprint: 7010-P1 Shield Arc 7P+ Tip Color: none Shield Arc 7P+: rev. EN 02

    132

  • Liability: All information in this data sheet is based on the best available knowledge, is subject to change without notice and canonly be considered as suitable for general guidance Fumes: Consult information on Welding Safety Sheet, available upon request

    www.lincolnelectric.eu

    SMAW

    Shield Arc 7P+

    Materials to be weldedSteel grades/Code Type

    Pipe materialAPI 5LX X42, X46, X52, X56, X60, X65

    Calculation dataSizes Current Current Arc time Energy Dep.rate Weight/ Electrodes/ kg Electrodes/

    Diam. x length range type - per electrode at max. current - 1000 pcs. kg weldmetal kg weldmetal(mm) (A) (s)* E(kJ) H(kg/h) (kg) B 1/N

    4.0x350 90-175 DC+/- 39.15.0x350 130-210 DC+ 62.5

    Welding parameters, optimum fill passesWelding positions 5G downDiameter (mm)

    4.0 150A5.0 165A

    Remarks/ Application advicePreheating pipe material from L360 to L450 (X52 to X65) required (acc. EN 1011-1).Pipeclamps to b

Recommended

View more >