MILD & MEDIUM CARBON STEEL ELECTRODES 1-16
17-48
49-79
80-95
96-110
111-119
120-125
LOW ALLOY STEEL ELECTRODES
STAINLESS STEEL ELECTRODES
HARD FACING ELECTRODES
NON FERROUS ELECTRODES
CAST IRON & CUTTING ELECTRODES
FLUX CORED WIRE & CO2 WELDING WIRES
Abbreviations and Symbols
Types of Current Codes
Abbreviations
Notes:
Direct current electrode attached to positive pole
Direct current electrode attached to negative pole
Direct current electrode attached to either positive or negative pole
Alternating current
Preferably direct current attached to positive pole, but also alternating current may be used
Preferably direct current attached to negative pole, but also alternating current may be used
Preferably direct current attached to either positive or negative pole, but also alternating current maybe used
tensile strengthyield strengthelongation after rupture (1=5d)impact valueas- weldedstress relieved
(brackets) - Minimum open circuit voltage when welding using an alternating current
Rm [MPa]Rp 0.2 [MPa]A5 [%]Impact (ISO) [J]US
= -
~
= + ~
= +
_
= + ~
_
= - ~
= +
All values listed in this guide are indicative only.All information contained within this guide is based on careful evaluation.Regardless, the manufacturer does not assume any liability for their correctness.Further, the manufacturer reserves the right to change the specifications listed in this guide at any time andwithout prior notice.
Electrode Brand Name - International Standards
Z-610Z-611Z-6Z-9Z-11Z-14Z-15Z-15 (14)
A5. 1: E 6010A5. 1: E 6011A5. 1: E 6013A5. 1: E 6013A5. 1: E 6013A5. 1: E 6013A5. 1: E 6013A5. 1: E 6013
1913: E 43 43 C41913: E 43 43 C41913: E 43 22 RR61913: E 42 22 R(C) 31913: E 43 22 RR61913: E 51 22 RR61913: E 43 22 RR61913: E 51 22 RR61913: E 51 22 R(C)31913: E 51 22 RR(C) 61913: E 51 22 RR11 1401913: E 51 22 RR11 1601913: E 51 22 RR11 1801913: E 51 32 RR11 1601913: E 51 22 RR11 180
1913: E 51 44 B9 H101913: E 51 44 B10 H101913: E 51 44 B10 H101913: E 51 44 B10 H51913: E 51 44 B10 H58529: EY 46 66 Mn BH51913: E 51 43 B(R)12 160 H51913: E 51 44 B(R)9 H10-8575: E Mo B 26-8575: E CrMo1 B 268575: E CrMo1 B 268529: E SY 42 77 2Ni B H58529: E Y 46 76 1Ni B H51913: E 51 33 B10 H58529: E Y 50 76 Mn1Ni B H58529: E SY 50 66 Mn B H58529: E Y 50 32 1NiCu B H58575: E CrMo2 B 268575: E CrMo2 B 268529: E SY 55 65 MnMo B H58529: E SY 50 0 1NiMo B H58529: E Y 55 87 2NiMo B H58529: E Y 62 87 Mn2NiMo B H58529: E Y 69 76 Mn2NiCrMo B H58529: E Y 79 76 Mn2Ni1.5CrMo B H58575: E CrMo5 B 268575: E CrMo9 B 26
639: E 43 43 C 19639: E 43 43 C 16639: E 43 22 RR 22639: E 43 22 R 12639: E 43 22 RR 22639: E 51 22 RR 32639: E 43 22 RR 32639: E 51 22 RR 32639: E 51 22 R 12639: E 51 22 RR 12639: E 51 22 RR 140 35639: E 51 22 RR 160 32639: E 51 22 RR 190 35639: E 51 22 RR 160 32639: E 51 22 RR 190 35
639: E 51 44 B 16 HH639: E 51 44 B 26 HH639: E 51 44 B 26 HH639: E 51 44 B 26 H639: E 51 44 B 26 H639: E 51 55 B 120 16 H639: E 51 43 B 160 36 H639: E 51 44 B 110 54 HH2493: E Mo C2493: E Mo B639: E 51 32 C 102493: E 1CrMo B2493: E 1CrMo L B2493: E 2Ni B H2493: E 1Ni B H639: E 51 33 B 120 26 H639: E 51 54 B 120 26 H639: E 51 55 B 120 16 H-2493: E 2CrMo B2493: E 2CrMo L B2493: E MnMo B H-2493: E MnNi B H2493: E NiMo B H2493: E 2NiMo B H2493: E 2NiCrMo B H2493: E 5CrMo B2493: E 9CrMo B
499: E 42 2 C 41499: E 42 2 C 31499: E 42 0 RR 12499: E 42 0 R 12499: E 42 0 RR 12 499: E 42 0 RR 12499: E 38 0 RR 12499: E 42 0 RR 12
12345678910111213141516
1718192021222324252627282930313233343536373839404142434445464748
499: E 42 0 RC 12499: E 46 0 RR 32499: E 42 0 RR 53499: E 46 0 RR 73499: E 46 0 RR 73499: E 46 0 RR 73499: E 46 0 RR 732560-A: E-5000Z1
499: E 46 3 B 11 H10499: E 42 3 B 12 H10499: E 42 3 B 32 H10499: E 46 3 B 32 H5499: E 42 3 B 32 H15499: E 46 5 B 32 H5499: E 42 3 RB 53 H5499: E 42 3 B 35 H10499: E 42 0 Mo C 411599: E Mo B 32 mod499: E 46 2 1NiMo C 411599: E CrMo1 B 32mod1599: E CrMo1 L B 32 mod499: E 46 6 2Ni B 42 H5-499: E 50 2 B 32 H5503Mo: B 42 H5499: E 50 6 Mn1Ni B 32 H5499: E 50 5 B 32 H5499: E 50 2 B 32 H51599: E CrMo2 B 32mod1599: E CrMo2 L B 32mod499: E 50 5 MnMo B 32 H5499: E 50 A 32 H5499: E 50 A 32 H5499: E 50 5 Z B 32 H5499: E 50 5 Z B 32 H5499: E 50 5 Z B 32 H5499: E 50 5 Z B 32 H51599: E CrMo5 B 32mod1599: E CrMo9 B 32mod
A5. 1: E 6013A5. 1: E 7014A5. 1: E 7024A5. 1: E 7024A5. 1: E 7024A5. 1: E 7024-1A5. 1: E 70245.5 E-9010-G
A5. 1: E 7016A5. 1: E 7016A5. 1: E 7018A5. 1: E 7018A5. 1: E 7018A5. 1: E 7018-1A5. 1: E 7028A5. 1: E 7048A5. 5: E 7010-A1A5. 5: E 7018-1A5. 5: E 8010-GA5. 5: E 8010-B2A5. 5: E 8010-B2LA5. 5: E 8010-C1A5. 5: E 8010-C3A5. 5: E 8010-GA5.5 E-8018-GA5. 5: E 8018-GA5. 5: E 8018-GA5. 5: E 8018-WA5. 5: E 9018-B3A5. 5: E 9018-B3LA5. 5: E 9018-D1A5. 5: E 9018-GA5.5 E-9018-GA5. 5: E 9018-MA5. 5: E 10018-MA5. 5: E 11018-MA5. 5: E 12018-MA5. 4: E 502-15A5. 4: E 505-15A5.5 E-9015-B9
Z-26Z-16Z-17Z-18Z-19Z-20Z-21Z-910
Z-7DIALOGUEZ-2Z-4Z-4 ACZ-55Z-42Z-47Z-710Z-23Z- CELLUPIPEZ-31 SZ-31Z-32Z-34Z-3Z-3PZ-8Z-33Z-3 WZ-41 SZ-41Z-46Z-40 SZ-X70Z-48Z-50Z-52Z-53 MZ-502Z-505Z-91
MILD & MEDIUM CARBON STEEL ELECTRODES
LOW ALLOY STEEL ELECTRODES
ELECTRODE
ELECTRODE
AWS/ASME SFA
AWS/ASME SFA
DIN
DIN
BS
BS
EN
EN
Z-307 BZ-307 RZ-307 HRZ-308 BZ-308 LZ-308 LVDZ-308 LHRZ-308 HZ-309 BZ-309 SZ-309 CbZ-309 MoZ-310Z-312Z-312 SZ-316 BZ-316 LZ-316 LVDZ-316 LHRZ-316 HSZ-317Z-318 BZ-318Z-320Z-347 BZ-347Z-ARM BSZ-Ni ViZ-2209 BZ-2209 RZ-2594 R
A5. 4: E 307-15A5. 4: E 307-16A5. 4: E 307-16A5. 4: E 308L-15A5. 4: E 308L-16A5. 4: E 308L-17A5. 4: E 308L-16A5. 4: E 308-16A5. 4: E 309L-15A5. 4: E 309L-16A5. 4: E 309Cb-16A5. 4: E 309MoL-16A5. 4: E 310-16A5. 4: E 312-16A5. 4: E 312-16A5. 4: E 316L-15A5. 4: E 316L-16A5. 4: E 316L-17A5. 4: E 316L-16A5. 4: E 316-16A5. 4: E 317L-16A5. 4: E 318-15A5. 4: E 318-16A5. 4: E 385-16modA5. 4: E 347-15A5. 4: E 347-16A5. 4: E 308Mo-15 mod A5. 4: E 308Mo-16 modA5. 4: E 2209-15A5. 4: E 2209-16A5. 4: E 2594-16
----------A5. 13: EFe5-B mod A5. 13: EFeMn-AA5. 13: EFeMn-A modA5. 13: ECoCr-AA5. 13: ECoCr-B-
---8556: E 19 9 L B 20+8556: E 19 9 L R 238556: E 19 9 L R 138556: E 19 9 L R 36 1508556: E 19 9 R 238556: E 23 12 L B 20+8556: E 23 12 L R 238556: E 23 12 Nb R 238556: E 23 12 3 R 238556: E 25 20 R 268556: E 29 9 R 238556: E 29 9 R 238556: E 19 123 L B 20+8556: E 19 123 L R 238556: E 19 12 3 L R 138556: E 19 12 3 L R 26 1508556: E 19 12 3 MPR 23 170-8556: E 19 12 3 Nb B 20+8556: E 19 12 3 Nb R 238556: E 20 25 5 L Cu R 38556: E 19 9 Nb B 20+8556: E 19 9 Nb R 23--8556: E 22 9 3 L B 20+8556: E 22 9 3 L R 23
---2926: E 19 9 L B2926: E 19 9 L R2926: E 19 9 L R2926: E 19 9 L R2926: E 19 9 R2926: E 23 12 L B2926: E 23 12 L R2926: E 23 12 Nb R2926: E 23 12 2 R2926: E 25 20 R2926: E 29 9 R2926: E 29 9 R2926: E 19 12 3 L B2926: E 19 12 3 L R2926: E 19 12 3 L R2926: E 19 12 3 L R2926: E 19 12 3 RMP2926: E 19 13 4 L R2926: E 19 12 3 Nb B2926: E 19 12 3 Nb R-2926: E 19 9 Nb B2926: E 19 9 Nb R2926: E 19 9 3 B2926: E 19 9 3 R--
---1600: E 19 9 L B 221600: E 19 9 L R 121600: E 19 9 L R 111600: E 19 9 L R 53 mod1600: E 19 9 R 121600: E 23 12 L B 421600: E 23 12 L R 121600: E 23 12 Nb R 121600: E 23 12 2 L R 121600: E 25 20 R 12 mod1600: E 29 9 R 121600: E 29 9 R 121600: E 19 12 3 L B 221600: E 19 12 3 L R 121600: E 19 12 3 L R 111600: E 19 12 3 L R 53 mod1600: E 19 12 2 R 721600: E 19 13 4 L R 12 mod1600: E 19 12 3 Nb B 221600: E 19 12 3 Nb R 121600: E 20 25 5 Cu L R 121600: E 19 9 Nb B 221600: E 19 9 Nb R 12--1600: E 22 9 3 L B 221600: E 22 9 3 L R 121600: E 2594 NLR Z3
8555: E 1 UM 3008555: E 1 UM 4008555: E 6 UM 55 R8555: E 6 UM 558555: E 6 UM 608555: E 6 UM 608555: E 10 UM 60 Z8555: E 10 UM 60 GR8555: E 10 UM 65 GR8555: E 10 UM 65 GR8555: E 4 UM 60 S8555: E 7 UM 250 KP8555: E 7 UM 250 KP-8555: E 20 UM 45 CTZ8555: E 20 UM 50 CTZ
----------------
----------------
49505152535455565758596061626364656667686970717273747576777879
80818283848586878889909192939495
Z-104Z-105Z-110Z-111Z-113Z-114Z-120Z-120 BZ-123Z-125Z-130Z-151Z-151 NCZ-152Z-STEL 6Z-STEL 12
STAINLESS STEEL ELECTRODESELECTRODE AWS/ASME SFA
HARD FACING ELECTRODESELECTRODE AWS/ASME SFA
DIN BS EN Pg.
DIN BS EN Pg.
Z-Ni 1Z-Ni BZ-Ni A2Z-Ni 182Z-Ni 182R1Z-Ni 112Z-Ni 112RZ-NiCroMo3Z-NiCroMo4Z-Ni CZ-Ni 190Z-Ni 187Z-BRONZE AZ-BRONZEZ-BRONZE M
Z-SuperNiZ-Ni 99Z-Ni 99 NCZ-Ni 55Z-GSMZ-GMZ-71Z-72Z-OXYCUT
Z-71T1Z-71T5
Z-R2Z-R3Z-R6Z-RMo
A5. 11: ENi-1A5. 11: ENiMo-1A5. 11: ENiCrFe-2A5. 11: ENiCrFe-3A5. 11: ENiCrFe-3A5. 11: ENiCrMo-3A5. 11: ENiCrMo-3A5. 11: ENiCrMo-3A5. 11: ENiCrMo-4A5. 11: ENiCrMo-5A5. 11: ENiCu-7A5. 6: ECuNiA5. 6: ECuSn-AA5. 6: ECuSn-CA5. 6: ECuSn-C
A5. 15: ENi-CIA5. 15: ENi-CIA5. 15: ENi-CIA5. 15: ENiFe-CI-A5. 15: ENiCu-B---
A5. 20: E71T-1A5. 20: E71T-5
A5. 18: ER-70S-2A5. 18: ER-70S-3A5. 18: ER-70S-6A5. 28: ER-80S-D2
8573: E Ni-BG-218573: E Ni-BG-238573: E Ni-BG-238573: E NiFe-1-BG-238573: E FeC-G-BG-268573: E NiCu-BG-23---
-8559: SG 18559: SG 28559: SG Mo
--2901: A 182901: A 30/A 31
440: G2 Ti-440: G3 Si 1 mod440: G4 Mo
1736: EL-NiTi 31736: EL-NiMo 291736: EL-NiCr 15 FeNb1736: EL-NiCr 15 FeMn1736: EL-NiCr 15 FeMn1736: EL-NiCr 20 Mo 9 Nb1736: EL-NiCr 20 Mo 9 Nb1736: EL-NiCr 20 Mo 9 Nb1736: EL-NiMo15 Cr 15 W1736: EL-NiMo15 Cr 15 W mod1736: EL-NiCu 30 Mn1733: EL-CuNi 30-1733: EL-CuSn 71733: EL-CuSn 7
---------------
---------
--
--
--
---------------
96979899100101102103104105106107108109110
111112113114115116117118119
120121
122123124125
NON FERROUS ELECTRODESELECTRODE AWS/ASME SFA DIN BS EN Pg.
CAST IRON & CUTTING ELECTRODESELECTRODE AWS/ASME SFA DIN BS EN Pg.
FLUX CORED WIRE
ELECTRODE AWS/ASME SFA DIN BS EN Pg.
SEMI AUTOMATIC SOLD WIREELECTRODE AWS/ASME SFA DIN BS EN Pg.
---------
1
Mild & Medium Carbon Steel Electrodes
Z-610
Cellulose electrode for pipe and general weldingDeep penetration and good X-ray qualitySuitable for welding pipes, pressure vessels, storagetanks, ships
Description and Applications:
Welding position
ASME: 1G 2F 2G 3G 3G 4G 5G
ISO 6947 PA PB PC PF PG PE PF/PG
C Mn Si0.10 0.50 0.20
Unalloyed construction steelsBoiler and pressure vessel steelsPipe steels
DIN 17 100DIN 17 155DIN 17 172DIN 17 175DIN 1629API 5LXDIN 17 102
St 33 to St 52.3HI, HIIStE 210.7 to StE 415.7St 35.8 to ST 45.8St 35 to St 52.4X42 to X63StE 255 to StE 355A,B,D
Fine grained steelsShipbuilding steels
Re-drying not necessary.
3/321/85/323/161/4
2.53.254.05.06.0
1414141414
350350350350350
60-9080-125
120-180160-230220-280
1.82.94.36.69.5
5.05.05.05.05.0
15.015.015.015.015.0
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V] Heat Treatment430 550 25 80 J @- 20
o-C U
45 J @- 30o-C
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.1 : E 6010DIN 1913 : E 43 43 C4BS 639 : E 43 43 C 19EN 499 : E 42 2 X 41
Specifications:
= +
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Mild & Medium Carbon Steel Electrodes
Z-611
Description and Application:
Welding position
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Current
Cellulose electrode for pipe and general weldingDeep penetration and good X-ray qualitySuitable for welding pipes, pressure vessels, storagetanks, ships on both AC and DC
ASME:ISO 6947
1GPA
C0.12
Mn0.50
Si0.20
2GPB
2GPC
3GPF
3GPG
4GPE
5GPF/PG
AWS/ASME SFA A5.1 : E 6011DIN 1913 : E 43 43 C4BS 639 : E 43 43 C 16EN 499 : E 42 2 C 31
Rp 0.2[MPa]430
Unalloyed construction steelsBoiler and pressure vessel steelsPipe steels
Fine grained steelsShipbuilding steels
Rm [MPa]550
Heat TreatmentU
2
A5 [%]25
Impact [ISO-V]80 J @-20oC45 J @-30oC
Specifications:
= + ~ (Uo : 70 v)
DIN 17 100DIN 17 155DIN 17 172DIN 17 175DIN 1629API 5LXDIN 17 102
St 33 to St 52.3HI, HIIStE 210.7 to StE 415.7St 35.8 to ST 45.8St 35 to St 52.4X42 to X63StE 255 to StE 355A,B,D
Re-drying not necessary.
3/321/85/323/161/4
2.53.254.05.06.0
1414141414
350350350350350
60-9080-125
120-180160-230220-280
1.82.94.36.69.5
5.05.05.05.05.0
15.015.015.015.015.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
3
Mild & Medium Carbon Steel Electrodes
Z-6
Rutile coated electrode for welding on uncleanedsurfaces like paint, oil or galvanized steelUsable for pipes, storage tanks and machine parts
Description and Applications:
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
C0.07
Mn0.50
Si0.25
DIN 17 100DIN 17 172DIN 1629API 5LXDIN 1681
St 33 to St 37.2 to St 44.3StE 210.7 to StE 360.7St 35 to St 52.4X42, X46GS 38A,B,C,D
Cast steelsShipbuilding steels
Re-drying not necessary.
3/321/85/323/16
2.53.254.05.0
14141414
350350350350
70-95100-150140-200180-270
1.93.04.57.0
5.55.55.55.5
16.516.516.516.5
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]450
Rm [MPa]550
A5 [%]23
Impact [ISO-V]70 J @ 0oC
Heat TreatmentU
Typical all weld metal mechanical properties
Unalloyed construction steelsPipe steels
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.1 : E 6013DIN 1913 : E 43 22 RR6BS 639 : E 43 22 RR 22EN 499 : E 42 0 RR 12
Specifications:
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 50 V)
4
Mild & Medium Carbon Steel Electrodes
Z-9
Rutile coated universal electrode for welding generalstructural steelsSuitable for badly prepared plates of differentthicknesses and bad surface conditionsEasy slag release and arc striking
Description and Applications:
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
C0.08
Mn0.50
Si0.30
DIN 17 100DIN 17 172DIN 1629API 5LXDIN 1681
St 33 to St 37.2 to St 44.3StE 210.7 to StE 360.7St 35 to St 52.4X42, X46GS 38A,B,C,D
Cast steelsShipbuilding steels
Re-drying not necessary.
5/643/321/85/323/16
2.02.53.254.05.0
12141414
14/18
300350350350
350/450
55-8570-100
100-150140-200180-230
1.11.93.04.5
7.0/9.0
4.05.55.55.5
5.5/7.0
12.016.516.516.5
16.5/21
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]400
Rm [MPa]520
A5 [%]24
Impact [ISO-V]70 J @ 0oC
Heat TreatmentU
Typical all weld metal mechanical properties
Unalloyed construction steelsPipe steels
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.1 : E 6013DIN 1913 : E 43 22 R(C)3BS 639 : E 43 22 R 12EN 499 : E 42 0 R 12
Specifications:
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 50 V)
5
Mild & Medium Carbon Steel Electrodes
Z-11
Thickly coated all purpose rutile electrodeSuitable for badly prepared surfaces such asrust and paint and different plate thicknessVery easy slag release and arc striking
Description and Applications:
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
C0.08
Mn0.50
Si0.25
DIN 17 100DIN 17 172DIN 17 175DIN 1629DIN 1681
St 33, St 37.2 to St 52.3StE 210.7 to StE 360.7St 35.8, St 45.8St 35 to St 52.4GS 38Cast steels
Re-drying not necessary.
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1214
14/1814/1814/18
300350
350/450350/450350/450
50-7060-100
100-150140-200180-260
1.12.0
3.3/4.24.9/6.27.7/9.9
4.05.0
5.0/6.05.0/6.05.0/6.0
12.015.0
15.0/18.015.0/18.015.0/18.0
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]440
Rm [MPa]520
A5 [%]26
Impact [ISO-V]70 J @ 0oC
Heat TreatmentU
Typical all weld metal mechanical properties
Unalloyed construction steelsPipe steels
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.1 : E 6013DIN 1913 : E 43 22 RR6BS 639 : E 43 22 RR 22EN 499 : E 42 0 RR 12
Specifications:
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 50 V)
6
Mild & Medium Carbon Steel Electrodes
Z-14
Thickly coated electrode for general purposesExceptionally smooth welding seams, low spatterloss and self detaching slag
Description and Applications:
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
C0.09
Mn0.55
Si0.30
DIN 17 100DIN 1681DIN 17 172DIN 17 175DIN 1629
St 33, St 37.2 to St 52.3GS 38, GS 45StE 210.7 to StE 360.7St 35.8 to St 45.8St 35 to St 52.4A,B,C,D,EShipbuilding steels
Re-drying not necessary.
3/321/8
5/323/16
2.53.254.05.0
14181818
350350/450350/450
450
70-110100-160160-200200-270
2.14.87.2
10.3
5.05.0/6.05.0/6.0
6.0
15.015.0/18.015.0/18.0
18.0
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]420
Rm [MPa]520
A5 [%]24
Impact [ISO-V]70 J @ 0oC
Heat TreatmentU
Typical all weld metal mechanical properties
Unalloyed construction steelsCast steelsPipe steels
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.1 : E 6013DIN 1913 : E 51 22 RR6BS 639 : E 51 22 RR 32EN 499 : E 42 0 RR 12
Specifications:
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 50 V)
7
Mild & Medium Carbon Steel Electrodes
Z-15
Heavy coated rutile electrode for general purposesVery even weld in flat and fillet positions
Description and Applications:
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
C0.09
Mn0.60
Si0.50
DIN 17 100DIN 1681DIN 17 172DIN 17 175DIN 1629
St 33, St 37.2 to St 52.3GS 38, GS 45StE 210.7 to StE 360.7St 35.8 to St 45.8St 35 to St 52.4A,B,C,D,EShipbuilding steels
Re-drying not necessary.
3/321/8
5/323/16
2.53.254.05.0
14181818
350450450450
70-110100-160160-200200-270
2.14.87.2
10.3
5.06.06.06.0
15.018.018.018.0
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]400
Rm [MPa]480
A5 [%]24
Impact [ISO-V]60 J @ 20oC
Heat TreatmentU
Typical all weld metal mechanical properties
Unalloyed construction steelsCast steelsPipe steels
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.1 : E 6013DIN 1913 : E 43 22 RR6BS 639 : E 43 22 RR 32EN 499 : E 38 0 RR 12
Specifications:
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 50 V)
8
Mild & Medium Carbon Steel Electrodes
Z-15 (14)
Rutile coated electrode for general purposesExceptionally smooth welding seamsSuitable for welding thin metal plates
Description and Applications:
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
C0.07
Mn0.55
Si0.50
DIN 17 100DIN 1681DIN 17 172DIN 17 175DIN 1629
St 33, St 37.2 to St 52.3GS 38, GS 45StE 210.7 to StE 360.7St 35.8 to St 45.8St 35 to St 52.4A,B,C,D,EShipbuilding steels
Re-drying not necessary.
3/321/8
5/323/16
2.53.254.05.0
14181818
350350/450350/450
450
70-110100-160160-200200-270
2.14.87.2
10.30
5.05.0/6.05.0/6.0
6.0
15.015.0/18.015.0/18.0
18.0
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]420
Rm [MPa]520
A5 [%]24
Impact [ISO-V]50 J @ 0oC
Heat TreatmentU
Typical all weld metal mechanical properties
Unalloyed construction steelsCast steelsPipe steels
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.1 : E 6013DIN 1913 : E 51 22 RR6BS 639 : E 51 22 RR 32EN 499 : E 42 0 RR 12
Specifications:
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 50 V)
9
Mild & Medium Carbon Steel Electrodes
Z-26
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
C0.07
Mn0.55
Si0.25
DIN 17 100DIN 17 155DIN 17 172DIN 17 175DIN 1629DIN 1681
St 33, St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7 to StE 360.7St 35.8, St 45.8St 35 to St 52.4GS 38, GS 45Cast steels
Re-drying not necessary.
5/643/321/8
5/323/161/4
2.02.5
3.254.05.06.0
121414
14/181414
300350350
350/450350/450
450
55-7070-100
100-150140-200160-230240-340
1.11.93.0
4.5/5.89.0
13.0
4.0/2.05.55.5
5.5/7.05.5/7.0
7.0
12.016.516.5
16.5/21.016.5/21.0
21.0
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]470
Rm [MPa]550
A5 [%]25
Impact [ISO-V]60 J @ 0oC
Heat TreatmentU
Typical all weld metal mechanical properties
Unalloyed construction steelsBoiler and pressure vessel steelsPipe steels
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.1 : E 6013DIN 1913 : E 51 22 R(c)3BS 639 : E 51 22 R 12EN 499 : E 42 0 RC 12
Specifications:
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 50 V)
Rutile Coated all position electrode with a widerange of applications in shipbuilding and structuralworkSuitable for badly prepared plates of differentthicknesses
Description and Applications:
10
Mild & Medium Carbon Steel Electrodes
Z-16
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
C0.08
Mn0.60
Si0.25
DIN 17 100DIN 17 155DIN 17 172DIN 17 175DIN 1629DIN 1681
St 33, St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7 to StE 360.7St 35.8, St 45.8St 35 to St 52.4GS 38, GS 45Cast steels
Re-drying not necessary.
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1214141414
300350350350350
50-7060-100
110-150130-170190-230
1.12.03.64.97.5
4.05.05.05.05.0
12.015.015.015.015.0
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]460
Rm [MPa]540
A5 [%]25
Impact [ISO-V]70 J @ 0oC
Heat TreatmentU
Typical all weld metal mechanical properties
Unalloyed construction steelsBoiler and pressure vessel steelsPipe steels
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.1 : E 7014DIN 1913 : E 51 22 RR(C)6BS 639 : E 51 22 RR 12EN 499 : E 46 0 RR 32
Specifications:
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Thick rutile electrode for fast deposition rateFocused, stable and penetrating arcSelf detaching slagSuitable for badly prepared plates of differentthicknesses
Description and Applications:
Current
= + ~ (Uo : 50 V)
11
Mild & Medium Carbon Steel Electrodes
Z-17
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
C0.08
Mn0.50
Si0.30
Re-drying: not necessary.
3/321/8
5/323/16
2.53.254.05.0
14181818
350450450450
60-110120-150150-190200-250
2.45.57.8
11.5
5.06.06.06.0
15.018.018.018.0
Typical all weld metal composition [wt%]
Welding parameters and packaging data
AWS/ASME SFA A5.1 : E 7024DIN 1913 : E 51 22 RR11 140BS 639 : E 51 22 RR 140 35EN 499 : E 42 0 RR 53
Specifications:
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 50 V)
Rutile coated electrode for welding engineeringstructures140% metal recoverySmooth weld appearance and self detaching slag
Description and Applications:
Rp 0.2 [MPa]430
Rm [MPa]510
A5 [%]25
Impact [ISO-V]60 J @ 0oC
Heat TreatmentU
Typical all weld metal mechanical properties
DIN 17 100DIN 17 155DIN 17 172DIN 1629DIN 1681
St 33, St 37.2 to St 52.3HI, HII, 17Mn4StE 210.7 to StE 360.7St 35 to St 52.4GS 38A,B,C,D
Cast steelsShipbuilding steels
Unalloyed construction steelsBoilerPlatePipe steels
Materials to be welded
12
Mild & Medium Carbon Steel Electrodes
Z-18
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
C0.07
Mn0.70
Si0.25
DIN 17 100DIN 17 155DIN 1681
St 33, St 37.2 to St 52.3HI, HII, 17Mn4GS 38A,B,C,D
Re-drying: not necessary
3/321/8
5/323/161/4
2.53.254.05.06.0
1418181818
350450450450450
85-125130-175150-240210-290290-420
3.06.5
10.015.019.5
4.56.06.06.06.0
13.518.018.018.018.0
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]480
Rm [MPa]550
A5 [%]26
Impact [ISO-V]60 J @ 0oC
Heat TreatmentU
Typical all weld metal mechanical properties
Unalloyed construction steelsBoiler and pressure vessel steelsCast steelShipbuilding steel
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.1 : E 7024DIN 1913 : E 51 22 RR11 160BS 639 : E 51 22 RR 160 32EN 499 : E 46 0 RR 73
Specifications:
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 50 V)
Rutile electrode for fillet welds and horizontalV-welds165% metal recovery with high speed weldingSmooth weld appearance and self detaching slag
Description and Applications:
13
Mild & Medium Carbon Steel Electrodes
Z-19
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
C0.07
Mn0.70
Si0.25
Re-drying not necessary.
1/85/323/161/4
3.254.05.06.0
18181818
450450450450
130-170150-230200-350280-480
6.911.215.722.1
6.06.06.06.0
18.018.018.018.0
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]460
Rm [MPa]550
A5 [%]27
Impact [ISO-V]60 J @ 0oC
Heat TreatmentU
Typical all weld metal mechanical properties
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 50 V)
AWS/ASME SFA A5.1 : E 7024DIN 1913 : E 51 22 RR11 180BS 639 : E 51 22 RR 190 35EN 499 : E 46 0 RR 73
Specifications:Rutile electrode for fillet welds and horizontalV-welds185% metal recovery with high speed weldingSmooth weld appearance and self detaching slag
Description and Applications:
DIN 17 100DIN 17 155DIN 1681
St 33, St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn5GS 38A,B,C,D
Cast steels
Unalloyed construction steelsBoiler and pressure vessel steelsCast steelsShipbuilding steels
Materials to be welded
14
Mild & Medium Carbon Steel Electrodes
Z-20
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
Re-drying not necessary.
1/85/323/161/4
3.254.05.06.0
18181818
450450450450
130-170150-230200-350280-480
7.210.616.023.8
6.06.06.06.0
18.018.018.018.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 50 V)
AWS/ASME SFA A5.1 : E 7024-1DIN 1913 : E 51 32 RR11 160BS 639 : E 51 32 RR 160 32EN 499 : E 46 0 RR 73
High speed, high deposit (160% metal recovery),rutile electrodeIdeal for very fast fillet welding and for fillinghorizontal groovesFully controlled molten pool, spatter free and selfdetaching slagSuitable for welding on moderate and thick platesfor buildings, bridges, shipbuilding, etc
Description and Applications: Specifications:
C0.09
Mn0.85
Si0.45
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]460
Rm [MPa]550
A5 [%]25
Impact [ISO-V]65 J @ 0oC
50 J @ -20oC
Heat TreatmentU
Typical all weld metal mechanical properties
DIN 17 100DIN 17 155DIN 1681
St 33, St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn5GS 38A,B,C,D
Unalloyed construction steelsBoiler and pressure vessel steelsCast steelsShipbuilding steels
Materials to be welded
15
Mild & Medium Carbon Steel Electrodes
Z-21
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
Re-drying not necessary.
1/85/323/161/4
3.254.05.06.0
18181818
450450450450
130-170150-230200-350280-400
7.210.616.024.3
6.06.06.06.0
18.018.018.018.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 50 V)
AWS/ASME SFA A5.1 : E 7024DIN 1913 : E 51 22 RR11 180BS 639 : E 51 22 RR 190 35EN 499 : E 46 0 RR 73
Rutile electrode for fillet and horizontal V-welds190% metal recovery with high speed weldingSmooth weld appearance and self detaching slag
Description and Applications: Specifications:
C0.07
Mn0.70
Si0.25
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]460
Rm [MPa]550
A5 [%]27
Impact [ISO-V]70 J @ 0oC
Heat TreatmentU
Typical all weld metal mechanical properties
DIN 17 100DIN 17 155DIN 1681
St 33, St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn4GS 38A,B,C,D
Unalloyed construction steelsBoiler and pressure vessel steelsCast steelsShipbuilding steels
Materials to be welded
16
Mild & Medium Carbon Steel Electrodes
Z-910
C0.11
Mn1.1
Si0.55
Ni0.62
Mo0.23
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]690
Rm [MPa]616
A5 [%]21
Impact [ISO-V]79 J @ 0oC
Typical all weld metal mechanical properties
API SPEC5L: X65, X70
Materials to be welded
AWS/ASME SFA 5.5 : E 9010-GEN ISO 2560-A E50021
Specifications:Cellulose electrode designed for welding in all positionincluding vertical down for high diameter pipelines.
Especially recommended for hot passes, filler and coverlayers.
Description and Applications:
Re-drying not necessary.
3/321/8
5/32
2.53.254.0
141414
350350350
80-125110-180140-230
555
151515
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weight packet[kg]
Weight carton[kg]
Welding position
17
Low Alloy Steel Electrodes
Z-7
Welding position
AWS/ASME SFA A5.1 : E 7016DIN 1913 : E 51 44 B9 H10BS 639 : E 51 44 B 16 HEN 499 : E 46 3 B 11 H10
Specifications:Basic coated electrode for high quality joiningof general construction steelsVery good X-ray propertiesSuitable for rool pass welding in narrow jointsGood impact toughness at low temperatures
Description and Applications:
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
3G
PG
4G
PE
C0.07
Mn1.00
Si0.60
Re-drying: 2h/300oC
3/321/8
5/323/16
2.53.254.05.0
14141418
350350350450
70-80100-120140-160190-210
1.93.14.79.2
5.05.05.06.0
15.015.015.018.0
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]490
Rm [MPa]570
A5 [%]26
Impact [ISO-V]120 J @ 0oC
100 J @ -20oC80 J @ -30oC
Heat TreatmentU
Typical all weld metal mechanical properties
DIN 17 100DIN 17 155DIN 17 172API 5LXDIN 1626-1630DIN 1681
St 33, St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE 360.7X42, X46, X52, X60St 37.0/4, St 44.0/4, St 52.0/4GS 38, GS 45, GS 52A,B,C,D,E AH, DH, EH
Cast steelsShipbuilding steels
General structure steelsBoiler and pressure vessel steelsPipe steels
Materials to be welded
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
18
Low Alloy Steel Electrodes
DIALOGUE
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
C0.06
Mn1.10
Si0.65
Re-drying: 300oC/2h
3/321/8
5/323/16
2.53.254.05.0
1414/18
1818
350350/450350/450
450
60-9095-150
140-190190-250
2.03.4/4.3
6.710
4.54.55/6
6
13.513.5
15/1818
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]420
Rm [MPa]530
A5 [%]30
Impact [ISO-V]110 J @ -20oC100 J @ -30oC
Heat TreatmentU
Typical all weld metal mechanical properties
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
AWS/ASME SFA A5.1 : E 7016DIN 1913 : E 51 44 B10 H10BS 639 : E 51 44 B 26 HHEN 499 : E 42 3 B 12 H10
Specifications:Double coated basic electrodeSuitable for repair and maintenance workExcellent for root pass and all positional weldingHigh impact toughness at low temperatures
Description and Applications:
DIN 17 100DIN 17 155DIN 17 172API 5LXDIN 1626-1630DIN 1681DIN 17 175DIN 17 102
St 33, St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE 360.7X42, X46, X52, X60St 37.0/4, St 44.0/4, St 52.0/4GS 38, GS 45, GS 52St 35.8, St 45.8StE 255 to StE 420A,B,C,D,E AH, DH, EH
Cast steelsElevated temperature steelsFine grained steelShipbuilding steels
General structure steelsBoiler and pressure vessel steelsPipe steels
Materials to be welded
19
Low Alloy Steel Electrodes
Z-2
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
C0.06
Mn1.00
Si0.35
Re-drying: 300oC/2h
3/321/8
5/323/161/4
2.53.254.05.06.0
1414/1814/18
1818
350350/450350/450
450450
60-9090-140
140-190190-240250-320
2.33.6/4.65.3/6.810.1014.20
4.54.5/6.04.5/6.0
6.06.0
13.513.5/18.013.5/18.0
18.018.0
Typical all weld metal composition [wt%]
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
AWS/ASME SFA A5.1 : E 7018DIN 1913 : E 51 44 B10 H10BS 639 : E 51 44 B 26 HHEN 499 : E 42 3 B 32 H10
Basic coated all position welding electrodeGood toughness at low temperaturesSuitable for welding general structural steels
Description and Applications: Specifications:
Rp 0.2 [MPa]430
Rm [MPa]510
A5 [%]28
Impact [ISO-V]130 J @ -20oC90 J @ -30oC
Heat TreatmentU
Typical all weld metal mechanical properties
DIN 17 100DIN 17 155DIN 17 172DIN 1626-1630DIN 1681DIN 17 175DIN 17 102
St 33, St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE 360.7St 37.0/4, St 44.0/4, St 52.0/4GS 38, GS 45, GS 52St 35.8, St 45.8StE 255 to StE 420A,B,C,D,E
Cast steelsElevated temperature steelsFine grained steelShipbuilding steels
General structure steelsBoiler and pressure vessel steelsPipe steels
Materials to be welded
20
Low Alloy Steel Electrodes
Z-4
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Re-drying: 300oC/2h
3/321/8
5/323/161/4
2.53.254.05.06.0
1414/1814/18
1818
350350/450350/450
450450
75-100110-140140-190190-240230-330
2.63.8/4.95.6/7.2
10.514.3
4.54.5/6.05.0/6.0
6.06.0
13.513.5/18.015.0/18.0
18.018.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
AWS/ASME SFA A5.1 : E 7018DIN 1913 : E 51 44 B10 H5BS 639 : E 51 44 B 26 HEN 499 : E 46 3 B 32 H5
Basic coated low hydrogen electrode with highductilitySuitable for welding general construction steelsVery good bead appearranceGood impact toughness at -30oC
Description and Applications: Specifications:
C0.08
Mn1.00
Si0.60
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]480
Rm [MPa]570
A5 [%]26
Impact [ISO-V]130 J @ -20oC100 J @ -30oC
Heat TreatmentU
Typical all weld metal mechanical properties
DIN 17 100DIN 17 155DIN 17 172DIN 1626-1630DIN 1681DIN 17 175DIN 17 102
St 33, St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE 360.7St 37.0/4, St 44.0/4, St 52.0/4GS 38, GS 45, GS 52St 35.8, St 45.8StE 255 to StE 420A,B,C,D,E
Cast steelsElevated temperature steelsFine grained steelShipbuilding steels
General structure steelsBoiler and pressure vessel steelsPipe steels
Materials to be welded
21
Low Alloy Steel Electrodes
Z-4 AC
Re-drying: 300oC/2h
3/321/8
5/323/16
2.53.254.05.0
1414/1814/1814/18
350350/450350/450350/450
75-100110-140130-170180-240
2.53.7/4.95.5/7.1
8.1/10.4
4.54.5/6.05.0/6.05.0/6.0
13.513.5/18.015.0/18.015.0/18.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
C0.09
Mn1.00
Si0.65
DIN 17 100DIN 17 155DIN 17 172DIN 1626-1630DIN 1681DIN 17 175DIN 17 102
St 33, St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE 360.7St 37.0/4, St 44.0/4, St 52.0/4GS 38, GS 45, GS 52St 35.8, St 45.8StE 255 to StE 420A,B,C,D,E
Cast steelsElevated temperature steelsFine grained steelShipbuilding steels
General structure steelsBoiler and pressure vessel steelsPipe steels
Materials to be welded
AWS/ASME SFA A5.1 : E 7018DIN 1913 : E 51 44 B10 H5BS 639 : E 51 44 B 26 HEN 499 : E 42 3 B 32 H5
Basic coated low hydrogen electrode with highductilitySuitable for welding general construction steelsVery good bead appearranceGood impact toughness at -30oCPreferably welded on AC
Description and Applications: Specifications:
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Current
= + ~ (Uo : 70 V)
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]450
Rm [MPa]550
A5 [%]28
Impact [ISO-V]130 J @ -20oC100 J @ -30oC
Heat TreatmentU
Typical all weld metal mechanical properties
22
Low Alloy Steel Electrodes
Z-55
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Current
= + ~ (Uo : 70 V)
C0.06
Mn1.45
Si0.45
API SPEC5L: X65, X70, X70
Materials to be welded
AWS/ASME SFA A5.1 : E 7018-1DIN 8529 : EY 46 66 MN BH5EN 499 : E 46 5B 32 H5
Low hydrogen basic electrode designed for weldingin all positions.Excellent strength and high toughness down to -46oC. suitable for welding medium and highstrength steels.It can be used in as welded conditions or after heattreatment.
Description and Applications: Specifications:
Typical all weld metal composition [wt%]
Rp 0.2 [MPa]520
580
Rm [MPa]600
500
A5 [%]25
27
Impact [ISO-V]140 J @ -29oC140 J @ -30oC155 J @ -30oC115J @ -46oC
Heat Treatment
PWHT620oC@8hr
Typical all weld metal mechanical properties
3/321/8
5/323/16
2.53.254.05.0
141418
17.7
350350450450
60-90110-140140-190190-260
5566
15151818
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weight packet[kg]
Weight carton[kg]
23
Low Alloy Steel Electrodes
Z-42
Re-drying: 300oC/2h
1/85/323/161/4
3.254.05.06.0
18181818
450450450450
120-190190-230230-300300-350
6.710.216.023.0
5.55.55.55.5
16.516.516.516.5
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Welding position
ASME:
ISO 6947
1G
PA
2F
PB
Current
= + ~ (Uo : 70 V)
Rp 0.2 [MPa]540
Rm [MPa]550
A5 [%]24
Impact [ISO-V]120 J @ -20oC100 J @ -30oC
Heat TreatmentU
Typical all weld metal mechanical properties
AWS/ASME SFA A5.1 : E 7028DIN 1913 : E 51 43 B(R)12 160 H5BS 639 : E 51 43 B 160 36 HEN 499 : E 42 3 RB 53 H5
High efficiency basic electrode (160% metalrecovery)Fast deposition rates and high productivityIdeal for steel construction, bridges, ship building,containers and storage tank weldingHigh porosity resistance
Description and Applications: Specifications:
C0.05
Mn1.10
Si0.30
Typical all weld metal composition [wt%]
DIN 17 100DIN 17 155DIN 17 172DIN 1681DIN 17 102DIN 17 175
St 33 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE 360.7GS 38, GS 45, GS 52StE 255 to StE 420St 35.8, St 45.8A,B,C,D,E,AH,DH,EH
Unalloyed construction steelsBoiler and pressure vessel steelsPipe steelsCast steelsElevated temperature steelsFine grained steelsShipbuilding steels
Materials to be welded
24
Low Alloy Steel Electrodes
Z-47
Welding position
Re-drying: 300oC/2h
3/321/8
5/323/16
2.53.254.05.0
14141418
350350/450
350450
70-9090-140
135-180175-255
1.72.94.48.9
5.05.0/6.05.0/6.0
6.0
15.015.0/18.015.0/18.0
18.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
Rp 0.2 [MPa]430
Rm [MPa]530
A5 [%]26
Impact [ISO-V]100 J @ -29oC
Heat TreatmentU
C0.08
Mn1.00
Si0.60
Typical all weld metal composition [wt%]
AWS/ASME SFA A5.1 : E 7048DIN 1913 : E 51 44 B(R)9 H10BS 639 : E 51 44 B 110 54 HHEN 499 : E 42 3 B 35 H10
Vertical down welding basic electrodeRecommended for welding in shipbuildingconstructionVery little slag and spatter lossHigh welding speed
Description and Applications: Specifications:
ASME:
ISO 6947
1G
PA
2F
PB
3G
PG
5G
PG
Typical all weld metal mechanical properties
DIN 17 100DIN 17 155DIN 17 172DIN 1626-1630DIN 1681DIN 17 175DIN 17 102
St 33 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE 360.7St37.0/4, St44.0/4, St52.0/4GS 38, GS 45, GS 52St 35.8, St 45.8StE 255 to StE 420A,B,C,D,E,AH,DH,EH
General structural steelsBoiler and pressure vessel steelsPipe steelsCast steelsElevated temperature steelsFine grained steelsShipbuilding steels
Materials to be welded
25
Low Alloy Steel Electrodes
Z-710
Welding position
Re-drying: not necessary
3/321/8
5/323/16
2.53.254.05.0
14141414
350350350350
60-9090-120
120-160160-200
1.62.84.36.6
5.05.05.05.0
15.015.015.015.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= +
Rp 0.2 [MPa]500
Rm [MPa]580
A5 [%]23
Av [ISO-V]70 J @ 0oC
Heat TreatmentS
C0.10
Mn0.50
Si0.20
Mo0.50
Typical all weld metal composition [wt%]
AWS A5.5 : E 7010-A1BS 2493 : E MoCEN 499 : E 42 0 Mo C 41
Cellulose coated electrodeVertical down welding of high strength pipesHigh mechanical properties
Description and Applications: Specifications:
Typical all weld metal mechanical properties
DIN 17 100DIN 17 155DIN 17 172DIN 17 175DIN 1629API 5LXDIN 17 102
St 37 to St 52.3HIIStE 210.7 to StE 415.7St 35.8, St 45.8St 35 to St 52.4X42 to X63StE 255 to StE 355
Unalloyed construction steelsBoiler and pressure vessel steelsPipe steels
Fine grained steels
Materials to be welded
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
3G
PG
4G
PE
5G
PF/PG
26
Low Alloy Steel Electrodes
Z-23
Welding position
Re-drying: 300oC/2h
3/321/8
5/323/16
2.53.254.05.0
1414
14/1814
350350
350/450450
60-9090-130
130-190180-220
2.33.5
5.0/6.06.0
4.55.0
5.0/6.06.0
13.515.0
15.0/18.018.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]410
Rm [MPa]540
A5 [%]28
Impact [ISO-V]140 J @ 20oC
Heat TreatmentS
C0.05
Mn0.70
Si0.40
Mo0.50
Typical all weld metal composition [wt%]
AWS/ASME SFA A5.5 : E 7018-A1DIN 8575 : E Mo B 26BS 2493 : E Mo BEN 1599 : E Mo B 32 mod
Basic coated electrodeFor welding creep resistant Mo containing low-alloy steelsWithstands service temperatures up to 525oC
Description and Applications: Specifications:
Typical all weld metal mechanical properties
DIN 17 155
DIN 17 245DIN 17 175DIN 17 102
14Mn4, 19Mn5, 15Mo3St 45.8, 15Mo3GS C25, GS 22 Mo415Mo3, 16Mo5StE 285 to StE 420
Boiler and pressure vessel steelsPipe steel for elevated temperaturesCast steelsElevated temperature steelsFine grained steels
Materials to be welded
27
Low Alloy Steel Electrodes
Z-CELLUPIPE
Welding position
Re-drying: not necessary
3/321/8
5/323/16
2.53.254.05.0
14141818
350350450450
60-9080-125
120-180160-230
1.82.95.68.6
5.05.05.05.0
15.015.015.015.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= +
Rp 0.2 [MPa]550
Rm [MPa]600
A5 [%]23
Impact [ISO-V]60 J @ 0oC
50 J @ -20oC
Heat TreatmentU
C0.10
Mn0.80
Si0.25
Ni0.45
Mo0.45
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 17 172API 5LXDIN 17 102
StE 290.7 to StE 415.7, StE 290.7 TM to StE 445.7 TMX42 to X70StE 255 to StE 355
Pipe steels
Fine grained steels
Materials to be welded
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
3G
PG
4G
PE
5G
PF/PG
AWS/ASME SFA A5.5 : E 8010-GBS 639 : E 51 32 C 10EN 499 : E 46 2 1NiMo C 41
Cellulosic electrode for vertical down pipe weldingEasy peentration due to forceful arcSuitable for hot passes in the root, filler andcapping passesLow suscptability to wagon tracks, windowsand pinholesGood X-ray quality
Description and Applications: Specifications:
28
Low Alloy Steel Electrodes
Z-31 S
Welding position
Re-drying: 300o C/2h
3/321/8
5/323/16
2.53.254.05.0
1414
14/1818
350350
350/450450
60-10090-130
130-180180-250
2.23.4
5.0/6.410.0
4.55.0
5.0/6.06.0
13.515.0
15.0/18.018.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
AWS/ASME SFA A5.5 : E 8018-B2DIN 8575 : E CrMo1 B 26BS 2493 : E 1 CrMo BEN 1599 : E CrMo 1 B 32 mod
Basic coated electrode for welding creep resistingsteels containing 1% Cr and 0.5% MoService temperatures of maximum 550oC
Description and Applications: Specifications:
Rp 0.2 [MPa]540
Rm [MPa]690
A5 [%]20
Import [ISO-V]120 J @ 20oC
Heat TreatmentS
C0.08
Mn0.80
Si0.35
Cr1.10
Mo0.50
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 17 155
DIN 17 200DIN 17 210DIN 17 245
13CrMo44, 16CrMo44, 15CrMo5, 24CrMo5,22CrMo4425CrMo415Cr3, 16MnCr5, 20MnCr5GS 17CrMo55, GS 22CrMo54, GS 17CrMo55
Elevated temperature steels
Quenched and tempered steelsCase hardening steelsCast steels
Materials to be welded
29
Low Alloy Steel Electrodes
Z-31
Welding position
Re-drying: 300o C/2h
3/321/8
5/323/16
2.53.254.05.0
1414
14/1818
350350
350/450450
60-10090-130
130-180180-250
2.23.4
5.0/6.410.0
4.55.0
5.0/6.06.0
13.515.0
15.0/18.018.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
AWS/ASME SFA A5.5 : E 8018-B2 LDIN 8575 : E CrMo1 B 26BS 2493 : E 1 CrMo L BEN 1599 : E CrMo 1 L B 32 mod
Basic coated electrode for welding creep resistingsteels containing 1% Cr and 0.5% MoService temperatures of maximum 550oC
Specifications:Description and Applications:
Rp 0.2 [MPa]540
Rm [MPa]690
A5 [%]20
Import [ISO-V]120 J @ 20oC
Heat TreatmentS
C0.05
Mn0.90
Si0.50
Cr1.15
Mo0.55
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 17 155DIN 17 200DIN 17 210DIN 17 245
13CrMo44, 16CrMo44, 15CrMo5, 24CrMo5, 22CrMo4425CrMo415Cr3, 16MnCr5, 20MnCr5GS 17CrMo55, GS 22CrMo54, GS 17CrMo55
Elevated temperature steelsQuenched and tempered steelsCase hardening steelsCast steels
Materials to be welded
30
Low Alloy Steel Electrodes
Z-32
Welding position
Re-drying: 300o C/2h
3/321/8
5/323/161/4
2.53.254.05.06.0
1414/1814/18
1818
350350/450350/450
450450
80-100100-140130-185190-250240-320
2.23.6/4.
5.4/6.910.815.0
4.55.0/6.05.0/6.0
6.06.0
13.515.0/18.015.0/18.0
18.018.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]520
Rm [MPa]590
A5 [%]27
Import [ISO-V]110 J @ -59oC
Heat TreatmentS
AWS/ASME SFA A5.5 : E 8018-C1DIN 8529 : E SY 42 77 2Ni B H5BS 2493 : E 2Ni B HEN 499 : 46 6 2Ni B 42 H5
Basic coated electrode for welding low alloystructures subjected to service down to -60oCGood corrosion resistance to chloric and sulphuricacid
Specifications:Description and Applications:
C0.05
Mn0.90
Si0.40
Ni2.15
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 17 102DIN 17 280
StE315 to StE46011MnNi53, 13MnNi63, 14NiMn6, 10Ni14
Fine grained steelsLow temperature steels
Materials to be welded
31
Low Alloy Steel Electrodes
Z-34
Welding position
Re-drying: 300o C/2h
3/321/8
5/323/16
2.53.254.05.0
1414/1814/18
18
350350/450350/450
450
75-110100-140130-200200-275
2.33.8/4.95.5/7.0
11.0
4.55.0/6.05.0/6.0
6.0
13.515.0/18.015.0/18.0
18.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]490
Rm [MPa]580
A5 [%]28
Import [ISO-V]70 J @ -40oC40 J @ -60oC
Heat TreatmentU
AWS/ASME SFA A5.5 : E 8018-C3DIN 8529 : E Y 46 76 1Ni B H5BS 2493 : E 1Ni B H
Low hydrogen basic coated electrodeSuitable for welding of low alloyed, fined grained,high tensile strength steels
Specifications:Description and Applications:
C0.05
Mn0.90
Si0.35
Ni0.90
Mo0.25
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 17 102DIN 17 280
StE255 to StE50011MnNi53, 13MnNi63, 14NiMn6, 10Ni14
Fine grained steelsLow temperature steels
Materials to be welded
32
Low Alloy Steel Electrodes
Z-3
Welding position
Re-drying: 300o C/2h
3/321/8
5/323/161/4
2.53.254.05.06.0
1414/1814/1814/18
18
350350/450350/450
450450
75-110110-140140-180190-260240-330
2.53.6/4.65.1/6.6
8.0/10.315.0
4.55.0/6.05.0/6.0
6.06.0
13.515.0/18.015.0/18.0
18.018.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]500
Rm [MPa]580
A5 [%]26
Impact [ISO-V]150 J @ -20oC
Heat TreatmentU
AWS/ASME SFA A5.5 : E 8018-GDIN 1913 : E 51 33 B10 H5BS 639 : E 51 33 B 120 26 HEN 499 : E 50 2 B 32 H5
Basic coated low hydrogen electrodeSuitable for maintenance repairing of agriculturalequipmentElectrode produces crack free and tough weldedjoints
Specifications:Description and Applications:
C0.06
Mn1.30
Si0.25
Mo0.20
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 17 100DIN 1681DIN 17 175DIN 17 102
St 52.3GS 52St45.8StE 315 to StE 500
General structural steelsCast steelsElevated temperature steelsFine grained steels
Materials to be welded
33
Low Alloy Steel Electrodes
Z-3P
Welding position
Re-drying: 300o C/2h
3/321/8
5/32
2.53.254.0
1414/18
18
350350/450
450
60-9090-140
110-190
4.55.0/6.0
6.0
13.513.5/18.0
18.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]620
Rm [MPa]540
A5 [%]26
Impact [ISO-V]85 J @ -30oC
AWS/ASME SFA A5.5 : E 8018-GEN ISO 2500-A2005 E503MoB42H5
Low hydrogen welding electrode with basic coating.Designed for all position welding except vertical down.Especially recommended for filler and cover layers ofpipeline.
Specifications:Description and Applications:
C0.050
Mn1.03
Si0.38
Mo0.36
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
API SPEC 5L: X46, X52, X56, X60
Materials to be welded
34
Low Alloy Steel Electrodes
Z-8
Welding position
Re-drying: 300o C/2h
3/321/8
5/323/161/4
2.53.254.05.06.0
1414/1814/18
1818
350350/450350/450
450450
60-9090-135
140-180180-240260-310
2.13.5/4.56.8/8.7
10.615.1
4.55.0/6.05.0/6.0
6.06.0
13.515.0/18.015.0/18.0
18.018.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]500
Rm [MPa]590
A5 [%]30
Impact [ISO-V]100 J @ -20oC90 J @ -40oC60 J @ -60oC
Heat TreatmentU
AWS/ASME SFA A5.5 : E 8018-GDIN 8529 : E Y 50 76 Mn 1Ni B H5BS 639 : E 51 54 B 120 26 HEN 499 : E 50 6 Mn 1Ni B 32 H5
Basic coated electrode with maximum 1% NiExcellent impact toughness at very lowtemperatures
Specifications:Description and Applications:
C0.06
Mn1.60
Si0.30
Mo0.60
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 17 100DIN 1681DIN 17 175DIN 17 102DIN 17 280
St 52.3GS 52St45.8StE 315 to StE 50011MnNi53, 13MnNi63, 14MnNi6
General structural steelsCast steelsElevated temperature steelsFine grained steelsLow temperature steels
Materials to be welded
35
Low Alloy Steel Electrodes
Z-33
Welding position
Re-drying: 300o C/2h
5/643/321/8
5/323/161/4
2.02.5
3.254.05.06.0
1214
14/1814/18
1818
300350
350/450350/450
450450
50-7575-95
90-140135-185175-255250-330
1.22.3
3.7/4.85.8/7.5
11.416.5
4.04.5
4.5/6.05.0/6.0
6.06.0
1213.5
13.5/18.015.0/18.0
18.018.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]530
Rm [MPa]600
A5 [%]25
Impact [ISO-V]135 J @ -29oC105 J @ -46oC
Heat TreatmentS
AWS/ASME SFA A5.5 : E 8018-GDIN 8529 : E SY 50 66 Mn B H5BS 639 : E 51 55 B 120 16 HEN 499 : E 50 5 B 32 H5
Basic coated low hydrogen electrodeDesigned for all position weldingSuited for welding high strength fine grainedstructural steelsHigh impact toughness at -46oC
Specifications:Description and Applications:
C0.08
Mn1.50
Si0.35
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 17 100DIN 1681DIN 17 175DIN 17 102DIN 17 280
St 52.3GS 52St45.8StE 315 to StE 50011MnNi53, 13MnNi63, 14MnNi6
General structural steelsCast steelsElevated temperature steelsFine grained steelsLow temperature steels
Materials to be welded
36
Low Alloy Steel Electrodes
Z-3 W
Welding position
Re-drying: 300o C/2h
3/321/8
5/323/16
2.53.254.05.0
1414/1814/1814/18
350350/450350/450
450
75-110110-140150-200190-260
2.53.7/4.85.5/7.1
8.2/10.5
4.54.5/6.05.0/6.0
6.0
13.513.5/18.015.0/18.0
18.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]500
Rm [MPa]600
A5 [%]25
Impact [ISO-V]70 J @ -20oC
Heat TreatmentU
AWS/ASME SFA A5.5 : E 8018-WDIN 8529 : E Y 50 32 1NiCu B H5EN 499 : E 50 2 B 32 H5
Basic coated electrode for welding thick structural“weathering” steels of similar compositionresistant to atmospheric corrosionHigh mechanical properties
Specifications:Description and Applications:
C0.05
Mn1.20
Si0.35
Cr0.50
Ni0.60
Cu0.50
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 17 100DIN 17 175API 5LXDIN 17 102
St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn5X42, X52, X60StE 255 to StE 420A,B,C,D,E, AH, DH, EHWTSt 37, WTSt 52.3
Unalloyed construction steelsBoiler and pressure vessel steelsPipe steels Fine grained steelsShipbuilding steelsWeather resistant structural steels
Materials to be welded
37
Low Alloy Steel Electrodes
Z-41 S
Welding position
Re-drying: 300o C/2h
3/321/8
5/323/16
2.53.254.05.0
1414
14/1818
350350
350/450450
70-11090-130
130-180180-250
2.23.5
5.1/6.610.0
4.55.0
5.0/6.06.0
13.515.0
15.0/18.018.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]580
Rm [MPa]720
A5 [%]18
Impact [ISO-V]110 J @ 20oC
Heat TreatmentS
AWS/ASME SFA A5.5 : E 9018-B3DIN 8575: E CrMo2 B 26BS 2493 : E 2CrMo BEN 1599 : E CrMo2 B 32 mod
Basic coated electrode for welding creep resistingsteels containing 2% Cr and 1% MoService temperatures of maximum 600oC
Specifications:Description and Applications:
C0.09
Mn0.75
Si0.40
Cr2.25
Mo1.05
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 17 175
DIN 17 245
10CrMo9 10, 12CrMo9 10, 10CrSiMo V7, 24CrMo10GS 12CrMo9 10, GS 18CrMo9 10GS 19CrMo9 10
Creep and hydrogenresisting steelsCast steels
Materials to be welded
38
Low Alloy Steel Electrodes
Z-41
Welding position
Re-drying: 300o C/2h
3/321/8
5/323/16
2.53.254.05.0
1414
14/1818
350350
350/450450
70-11090-130
130-180180-250
2.23.5
5.1/6.610.0
4.55.0
5.0/6.06.0
13.515.0
15.0/18.018.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]580
Rm [MPa]720
A5 [%]18
Impact [ISO-V]110 J @ 20oC
Heat TreatmentS
AWS/ASME SFA A5.5 : E 9018-B3 LDIN 8575: E CrMo2 B 26BS 2493 : E 2CrMo L BEN 1599 : E CrMo2 L B 32 mod
Basic coated electrode for welding creep resistingsteels containing 2% Cr and 1% MoService temperatures of maximum 600oC
Specifications:Description and Applications:
C0.05
Mn0.80
Si0.40
Cr2.00
Mo1.00
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 17 175
DIN 17 245
10CrMo9 10, 12CrMo9 10, 10CrSiMo V7, 24CrMo10GS 12CrMo9 10, GS 18CrMo9 10GS 19CrMo9 10
Creep and hydrogenresisting steelsCast steels
Materials to be welded
39
Low Alloy Steel Electrodes
Z-46
Welding position
Re-drying: 300o C/2h
3/321/8
5/323/16
2.53.254.05.0
14141418
350350/450350/450
450
75-100110-140150-190190-260
2.13.66.0
11.2
5.05.0/6.05.0/6.0
6.0
15.015.0/18.015.0/18.0
18.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]600
Rm [MPa]650
A5 [%]23
Impact [ISO-V]130 J @ -29oC80 J @ -51oC
Heat TreatmentS
AWS/ASME SFA A5.5 : E 9018-D1DIN 8529: E SY 55 65 MnMo B H5BS 2493 : E MnMo B HEN 499 : E 50 5 MnMo B 32 H5
Basic coated electrode suited for welding hightensile structural steels, working at very lowtemperaturesExtremely low diffusible hydrogen content
Specifications:Description and Applications:
C0.07
Mn1.45
Si0.40
Mo0.35
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 17 100
DIN 17 155
St 33, St 37.2 to St 52.3DOMEX 400TE, 450, 480HI, HII, 17Mn4, 19Mn5USS-T
General structural steels
Boiler and pressure vessel steelsFine grained steels
Materials to be welded
40
Low Alloy Steel Electrodes
Z-40 S
Welding position
Re-drying: 300o C/2h
3/321/8
5/323/16
2.53.254.05.0
14141418
350350350450
75-100110-140150-190190-260
2.13.65.2
10.3
4.55.05.06.0
13.515.015.018.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= +
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]500
Rm [MPa]600
A5 [%]25
Impact [ISO-V]-
Heat TreatmentS
AWS/ASME SFA A5.5 : E 9018-GDIN 8529: E SY 50 0 1NiMo B H5EN 499 : E 50 A 32 H5
Basic coated electrode for welding steels suchas 4130 and 8630 subjected to heat treatingWelded joints are crack free and tough
Specifications:Description and Applications:
C0.05
Mn1.25
Si0.40
Cr0.60
Mo0.35
Ni1.20
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
API 5LXDIN 17 102DIN 17 102
X70, X 75, X80StE420, StE460, StE50022NiMoCr37, 17MnMoV64, 15NiCuMoNb5,20MnMoNi45, 20MnMoNi55
Pipe steelsFine grained steelsHigh temperature fine grained steels
Materials to be welded
41
Low Alloy Steel Electrodes
Z-X70
Welding position
Re-drying: 300o C/2h
3/321/8
5/32
2.53.254.0
1414
14/18
350350
350/450
60-9090-140
110-190
2.252.52.5
13.51515
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70 V)
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]690
Rm [MPa]605
A5 [%]25
Impact [ISO-V]60 J @ -60oC
AWS/ASME SFA A5.5 : E 9018-GEN 757 E552MnMoB
Low hydrogen basic electrode designed for weldingin al positions except vertical down.Especially recommended for filler and cover layers of high diameter pipelines.
Specifications:Description and Applications:
C0.05
Mn1.5
Si0.32
Mo0.50
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
API SPEC5L: X65, X70,X70
Materials to be welded
42
Low Alloy Steel Electrodes
Z-48
Welding position
Re-drying: 300o C/2h
3/321/8
5/323/161/4
2.53.254.05.06.0
1414141818
350350
350/450450450
70-10090-140
140-190180-250240-320
2.13.65.2
10.414.9
4.55.0
5.0/6.06.06.0
13.515.0
15.0/18.018.018.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= ~ (Uo : 70 V)+
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]580
Rm [MPa]640
A5 [%]24
Impact [ISO-V]135 J @ -29oC105 J @ -51oC50 J @ -73oC
Heat TreatmentU
AWS/ASME SFA A5.5 : E 9018-MDIN 8529 : E Y 55 87 2NiMo B H5BS 2493 : E MnNi B HEN 499 : E 50 5 Z B 32 H5
Basic coated electrode for welding of lowtemperature, high strength, fine grained structuralsteelsGood impact toughness at low temperatures
Specifications:Description and Applications:
C0.05
Mn0.90
Si0.25
Ni1.75
Mo0.30
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 17 100DIN 17 155DIN 17 172 DIN 1681DIN 17 175DIN 17 102DIN 17 102
St 50.2, St 60.215Mo3StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE 360.7GS 6010Mo3, 16Mo5TStE420 to TStE50022NiMoCr37, 17MnMoV64, 15 NiCuMoNb5,20MnMoNi45, 20MnMoNi55
General structural steelsBoiler and pressure vessel steelsPipe steelsCast steelsElevated temperature steelsFine grained steelsHigh temperature fine grained steels
Materials to be welded
43
Low Alloy Steel Electrodes
Z-50
Welding position
Re-drying: 300o C/2h
3/321/8
5/323/161/4
2.53.254.05.06.0
1414141818
350350/450350/450
450450
70-9590-140
135-185175-255250-330
2.33.75.6
11.216.2
4.55.0/6.05.0/6.0
6.06.0
13.515.0/18.015.0/18.0
18.018.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= ~ (Uo : 70 V)+
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]630
Rm [MPa]790
A5 [%]22
Impact [ISO-V]95 J @ -29oC65 J @ -51oC45 J @ -73oC
Heat TreatmentU
AWS/ASME SFA A5.5 : E 10018-MDIN 8529 : E Y 62 87 2Mn2NiMo B H5BS 2493 : E NiMo B HEN 499 : E 50 5 Z B 32 H5
Basic coated electrode for welding of lowtemperature, high strength, fine grained structuralsteels such as navel crafts and submarines.Particularly low diffusible hydrogen content.
Specifications:Description and Applications:
C0.05
Mn1.65
Si0.40
Ni2.00
Cr0.20
Mo0.40
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 17 100DIN 17 155DIN 17 172 DIN 1681DIN 17 175DIN 17 102DIN 17 102
St 50.2, St 60.215Mo3StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE 360.7GS 6010Mo3, 16Mo5TStE420 to TStE50022NiMoCr37, 17MnMoV64, 15 NiCuMoNb5,20MnMoNi45, 20MnMoNi55
General structural steelsBoiler and pressure vessel steelsPipe steelsCast steelsElevated temperature steelsFine grained steelsHigh temperature fine grained steels
Materials to be welded
44
Low Alloy Steel Electrodes
Z-52
Welding position
Re-drying: 300o C/2h
3/321/8
5/323/161/4
2.53.254.05.06.0
1414141818
350350/450350/450
450450
70-9590-140
135-185175-255250-330
2.33.75.6
11.216.2
4.55.0/6.05.0/6.0
6.06.0
13.515.0/18.015.0/18.0
18.018.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= ~ (Uo : 70 V)+
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]700
Rm [MPa]780
A5 [%]22
Impact [ISO-V]90 J @ -29oC65 J @ -51oC
Heat TreatmentU
AWS/ASME SFA A5.5 : E 11018-MDIN 8529 : E Y 69 76 Mn2NiCrMo B H5BS 2493 : E 2NiMo B HEN 499 : E 50 5 Z B 32 H5
Basic coated electrode for welding high strengthsteels for military applicationsExcellent X-ray quality
Specifications:Description and Applications:
C0.05
Mn1.60
Si0.30
Cr0.25
Ni2.25
Mo0.40
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 17 100DIN 17 155DIN 17 172 DIN 1681DIN 17 175DIN 17 102DIN 17 102
St 50.2, St 60.215Mo3StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE 360.7GS 6010Mo3, 16Mo5TStE420 to TStE50022NiMoCr37, 17MnMoV64, 15 NiCuMoNb5,20MnMoNi45, 20MnMoNi55
General structural steelsBoiler and pressure vessel steelsPipe steelsCast steelsElevated temperature steelsFine grained steelsHigh temperature fine grained steels
Materials to be welded
45
Low Alloy Steel Electrodes
Z-53 M
Welding position
Re-drying: 300o C/2h
3/321/8
5/323/161/4
2.53.254.05.06.0
1414/1814/18
1818
350350/450350/450
450450
65-9590-135
140-185180-240240-320
2.13.6
5.2/6.810.414.9
4.55.0
5.0/6.06.06.0
13.515.0
15.0/18.018.018.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= ~ (Uo : 70 V)+
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]800
Rm [MPa]940
A5 [%]20
Impact [ISO-V]60 J @ -29oC50 J @ -51oC
Heat TreatmentU
AWS/ASME SFA A5.5 : E 12018-MDIN 8529 : E Y 79 76 Mn2Ni1.5CrMo B H5BS 2493 : E 2NiCrMo B HEN 499 : E 50 5 Z B 32 H5
Basic coated electrode for welding very highstrength steels for military applications
Specifications:Description and Applications:
C0.06
Mn1.90
Si0.30
Cr2.20
Ni1.20
Mo0.50
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 17 100DIN 17 155DIN 17 172 DIN 1681DIN 17 175DIN 17 102DIN 17 102
St 50.2, St 60.215Mo3StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE 360.7GS 6010Mo3, 16Mo5TStE420 to TStE50022NiMoCr37, 17MnMoV64, 15 NiCuMoNb5,20MnMoNi45, 20MnMoNi55
General structural steelsBoiler and pressure vessel steelsPipe steelsCast steelsElevated temperature steelsFine grained steelsHigh temperature fine grained steels
Materials to be welded
46
Low Alloy Steel Electrodes
Z-502
Welding position
Re-drying: 300o C/2h
3/321/8
5/323/16
2.53.254.05.0
12141414
300350350350
65-9590-130
125-180180-240
2.03.65.48.5
4.05.05.05.0
12.015.015.015.0
Welding parameters and packaging dataDia
in mmLength
in mmCurrent[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= ~ (Uo : 70 V)+
ASME:
ISO 6947
1G
PA
2F
PB
2G
PC
3G
PF
4G
PE
Rp 0.2 [MPa]490
Rm [MPa]620
A5 [%]20
Impact [ISO-V]80 J @ -20oC
Heat TreatmentS
AWS/ASME SFA A5.4 : E 502-15DIN 8575 : E CrMo5 B 26BS 2493 : E 5CrMo BEN 1599 : E CrMo5 B 32 mod
Basic coated 5% Cr - 0.5% Mo electrodeService temperature of maximum 600oCWelding of Cr-Mo alloys of similar compositionSuitable for critical thick joints
Specifications:Description and Applications:
C0.06
Mn0.60
Si0.35
Cr5.20
Mo0.60
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 17 155DIN 17 245
12CrMo19 5 GS 12CrMo19 5
Boiler and pressure vessel steelsCast steels
Materials to be welded
47
Low Alloy Steel Electrodes
Z-505
Basic coated 9% Cr- 1% Mo electrodeService temperatures of maximum 6500C
Description and Applications:
Current
Specifications:
= + ~ (Uo : 70V)
AWS/ASME SFA A5.4 : E 505-15DIN 8575: E CrMo9 B 26BS 2493 : E 9CrMO BEN 1599 : E CrMo9 B 32 mod
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
DIN 17 176DIN 17 245
Boiler and pressure vessel steelsCast steels
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
X12 CrMO91GX 12CrMo 10 1
C Mn Si Cr Mo0.08 0.75 0.65 9.50 1.00
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V] Heat Treatment550 700 22 80 J @ 20oC S
Re-drying : 3000C/2h
3/321/8
5/323/16
2.53.254.05.0
12141414
300350350350
65-105110-140150-190180-230
1.93.65.48.4
4.05.05.05.0
12.015.015.015.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
48
Low Alloy Steel Electrodes
Z-91
Low hydrogen electrode suitable for welding9%Cr-1%Mo steels, also known as GRADE 91designed to provide excellent endurance in creep,fatigue, oxidation and corrosion resistance on hightemperatures.
ASTMA213 T91A335 P91A369 FP91EN1.4903 (X10CrMoVNb 91)
A387 G91A217 C12A
A182/A336 F91A234 P91
Description and Applications:
Rp 0.2 [MPa] Rm[MPa] A5 [%] Impact [ISO-V]570 700 18 121J@20oC
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA 5.5: E9015-B9
Specifications:
C Mn* Si Cr Ni* Mo v0.1 1 0.25 9 0.3 1 0.2*Mn+Ni<1.5
= + ~ (Uo : 70V)
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
3/321/85/32
2.53.254.0
141414
350350350
75-10090-140
110-190
4.566
13.51818
Diain mm
Lengthin mm
Current[amps]
Weight packet[kg]
Weight carton[kg]
49
Stainless Steel Electrodes
Z-307 B
Basic coated stainless steel electrodeFor welding 14% Mn steels, armour plate, steelswith unknown composition and hardening steelsUsed for buffer layers in hardfacing applications
Description and Applications:
Various steel grades such as: Non-magnetic austenitic steelsWork hardening austenitic manganese steelsDissimilar steel grades (CMn-steels to stainless steel)
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]520 620 35 70 J @ 20oC
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 307-15Specifications:
C Mn Si Cr Ni Mo0.06 4.30 0.40 20.50 9.50 0.80
= +
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Re-drying : 3000C2h
3/321/8
5/323/16
2.53.254.05.0
12141414
300300300300
65-8095-120
110-160150-190
1.73.14.76.5
1.5/2.02.0/2.52.0/2.52.0/2.5
9.0/12.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
50
Stainless Steel Electrodes
Z-307 R
Rutile coated stainless steel electrodeFor welding 14% Mn steels, armour plate, steelswith unknown composition and hardening steelsUsed for buffer layers in hardfacing applications
Description and Applications:
Various steel grades such as: Non-magnetic austenitic steelsWork hardening austenitic manganese steelsDissimilar steel grades (CMn-steels to stainless steel)
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]520 620 35 70 J @ 20oC
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 307-16
Specifications:
C Mn Si Cr Ni Mo0.09 4.00 0.80 19.00 10.00 0.90
Re-drying : 3000C2h
Current
= + ~ (Uo : 70V)
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
3/321/8
5/323/16
2.53.254.05.0
12141414
300350350350
65-8095-120
110-160150-190
1.73.14.76.5
1.5/2.02.0/2.52.0/2.52.0/2.5
9.0/12.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
51
Stainless Steel Electrodes
Z-307 HR
Rutile coated high recovery stainless steelelectrodeFor welding 14% Mn steels, mixed joints betweenhigh alloyed steel, stainless steels and unalloyedbase materialsUsed for hard to weld steel joints and bufferlayers in hardfacing applications
Description and Applications:
Various steel grades such as: Non-magnetic austenitic steelsWork hardening austenitic manganese steelsDissimilar steel grades (CMn-steels to stainless steel)
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V] - 620 35 100 J @ 20oC
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 307-16Specifications:
C Mn Si Cr Ni Mo0.08 4.00 0.80 19.50 9.50 1.10
Re-drying : 3000C/2h
Current
= + ~ (Uo : 70V)
Welding position
ASME: 1G 2F 3G
ISO 6947 PA PB PF
3/321/8
5/323/16
2.53.254.05.0
14181818
350450450450
65-8095-120
110-160150-190
3.26.6
10.215.0
5.06.06.06.0
5.018.018.018.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
52
Stainless Steel Electrodes
Z-308 B
Description and Applications:Basic coated electrode for welding austeniticstainless Cr-Ni steelsSuited for positional welding of thick plates andhighly restrained jointsExcellent resistance to cold crackingGood mechanical properties
DIN 17 440/17 445
DIN 17 440/17 445
DIN 17 440/17 445
Extra loiw carbon C<0.035%
Medium carbon C>0.03%
Ti-, Nb Stabilized
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 308L-15DIN 8556 : E 19 9 L B 20 +BS 2926 : E 19 9 L BEN 1600 : 19 9 L B 22
Specifications:
X2 CrNi 19 11X2 CrNiN 18 10X5 CrNi 18 10G-X6 CrNi 18 9X6 CrNiTi 18 10X6 CrNiNb 18 10G-X5 CrNiNb 18 9
1.43061.43111.43011.43081.45411.45501.4552
C Mn Si Cr Ni0.03 1.00 0.50 19.00 10.00
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]440 580 40 80 J @ 20oC
Re-drying : 3000C/2h
= +Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1212141418
300300350350450
40-5555-80
75-110110-150140-180
1.21.83.65.6
10.4
1.5/2.01.5/2.02.0/2.52.0/2.5
6.0
9.0/12.09.0/12.0
12.0/15.012.0/15.0
18.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
53
Stainless Steel Electrodes
Z-308 L
Description and Applications:Rutile-basic coated electrode for welding nonstabilized and stabilized corrosion resistantaustenitic Cr-Ni steels up to 3500 CSmooth metal transfer with both AC and DCWeld metal beads exhibit fine ripple formationFocused and stable arc with low spatter lossSelf detachin slagMoisture resistant formulation producing weldsfree from porosity
DIN 17 440/17 445
DIN 17 440/17 445
DIN 17 440/17 445
Extra loiw carbon C<0.03%
Medium carbon C>0.03%
Ti-, Nb Stabilized
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 308L-16DIN 8556 : E 19 9 L R 23BS 2926 : E 19 9 L REN 1600 : E 19 9 L R 12
Specifications:
X2 CrNi 19 11X2 CrNiN 18 10X5 CrNi 18 10G-X6 CrNi 18 9X6 CrNiTi 18 10X6 CrNiNb 18 10G-X5 CrNiNb 18 9
1.43061.43111.43011.43081.45411.45501.4552
C Mn Si Cr Ni0.020 0.75 0.80 19.00 10.00
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]450 560 45 70 J @ 20oC
Re-drying : 3000C/2h
Current
= + ~ (Uo : 50V)
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1212141414
300300350350450
30-5050-75
75-110110-150140-190
1.11.73.34.97.1
1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5
9.0/12.09.0/12.0
12.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
54
Stainless Steel Electrodes
Z-308 LVD
Description and Applications:Ruitle-acid austenitic stainless Cr-Ni steel electrodefor welding 304L or equivalent steels in thevertical down positionDesigned for welding root passes in grooveswith root openingHigh corrosion resistance in oxidizing envionments
DIN 17 440/17 445
DIN 17 440/17 445
DIN 17 440/17 445
Extra loiw carbon C<0.03%
Medium carbon C>0.03%
Ti-, Nb Stabilized
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 308L-17DIN 8556 : E 19 9 L R 13BS 2926 : E 19 9 L REN 1600 : E 19 9 L R 11
Specifications:
X2 CrNi 19 11X2 CrNiN 18 10X5 CrNi 18 10G-X6 CrNi 18 9X6 CrNiTi 18 10X6 CrNiNb 18 10G-X5 CrNiNb 18 9
1.43061.43111.43011.43081.45411.45501.4552
C Mn Si Cr Ni0.025 0.70 0.70 19.50 10.00
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]440 600 40 70 J @ 20oC
Re-drying : 3000C/2h
Current
= + ~ (Uo : 50V)
Welding position
ASME: 1G 2F 2G 3G 3G 4G
ISO 6947 PA PB PC PF PG PE
3/321/8
2.53.25
1212
300300
60-7080-100
1.42.4
2.02.0
12.012.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
55
Stainless Steel Electrodes
Z-308 LHR
Description and Applications:
Rutile coated high recovery (145%) electrodees.Used whenever a high deposition rate is required.Easy slag realease, smooth and finely rippled deposit.Excellent for fillet and downhand welding.
for welding austenitic Cr- Ni steels.
Welding position
Welding parameters and packaging data
Specifications:
AWS/ASME SFA A5.4 : E-308L -16EN 1600: E 19 9 LR 53 mod
Current
= + ~ (Uo : 70V)
Typical all weld metal mechanical properties
Materials to be welded
ASME: 1G 2F
ISO 6947 PA PB
C Mn Si Cr Ni0.025 0.80 0.80 19.50 10.3
Typical all weld metal composition [wt%]
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]450 580 40 35J@- 105c
Extra low carbon C<0.03%Medium carbon C>0.03%Ti-, Nb Stabilezed
DIN 17 440/17 445DIN 17 440/17 445DIN 17 440/ 17 445
X2 CrNi 19 11X2 CrNiN 18 10X5 CrNi 18 10G-X6 CrNi 18 9X6 CrNiTi 18 10X6 CrNiNb 18 10G-X5 CrNiNb 18 9
1.43061.43111.43011.43081.45411.45501.4552
Re-drying: 3000 C/2h
3/321/8
5/323/16
2.53.254.05.0
1214/18
1818
300350/450
450450
75-95110-130135-155180-210
2.55.0/6.40
9.314.3
4.05.0/6.0
6.06.0
12.015.0/18.0
18.018.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
56
Stainless Steel Electrodes
Z-308 H
Rutile-basic all position stainless steel electrodeUsed for welding low-carbon stainless steels ofthe type AISI 304 in cases where maximumresistance to intergranular corrosion is requiredFor welding Titanium and Niobium stabilizedstainless steelsWeldable on both AC and DC
Description and Applications:
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
DIN 17 440/17 445
DIN 17 440/17 445
Medium carbon steels
Ti-: Nb stabilized steels
Re-drying : 3000C/2h
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]440 580 40 70 J @ 20oC
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 308-16DIN 8556 : E 19 9 R 23BS 2926 : E 19 9 REN 1600 : E 19 9 R 12
Specifications:
C Mn Si Cr Ni0.05 1.00 0.80 20.00 10.00
X5 CrNi 18 10G-X6 CrNi 18 9X6 CrNiTi 18 10X6 CrNiNb 18 10
1.43011.43081.45411.4550
= + ~ (Uo : 50V)
1/165/643/321/85/323/16
1.62.02.53.254.05.0
121212141414
300300300350350350
25-4030-5050-75
75-110110-150140-190
0.51.11.73.34.97.1
1.5/2.01.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5
9.0/12.09.0/12.09.0/12.0
12.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
57
Stainless Steel Electrodes
Z-309 B
Description and Applications:Basic coated stainless electrode for welding rootruns in acid resisting parts of clad steelUsed when overlaying on mild steel or low alloysteelsJoining dissimilar steels (austenitic steels to mildand low alloy steels)Suitable for welding similar metal joints andaustenitic-martensitic steels of the 13% Cr-6% Ni typeUsed for buffer layers in hardfacing applicaions
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
DIN 17 440/17 465Corrosion resistingClad steel
Dissimilar metals (mild and low alloyed steel to stainless steel)Build-up welding on mild and low alloyed steel
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 309L-15DIN 8556 : E 23 12 L B 20+BS 2926 : E 23 12 L BEN 1600 : E 23 12 L B 42
Specifications:
X2 CrNiN 18 10X2 CrNi 19 11X5 CrNi 18 10
1.43111.43061.4301
= +
C Mn Si Cr Ni0.02 0.90 0.40 24.00 12.00
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]470 560 35 70 J @ 20oC
3/321/8
5/323/16
2.53.254.05.0
12141414
300350350350
50-8080-110
100-150160-220
1.93.45.47.8
1.5/2.02.0/2.52.0/2.52.0/2.5
9.0/12.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Re-drying : 3000C/2h
58
Stainless Steel Electrodes
Z-309 S
Rutile coated low carbon electrode for joiningof dissimilar steels (austenitic steels to mild andlow alloy steels)Suitable for welding similar metal joints (23% Cr-12% Ni) and austenitic - martenistic steels of 13% Cr - 6% Ni typeUsed for buffer layers in hardfacing applicationsFocued and stable arcEasy slag release
Description and Applications:
Welding position
DIN 17 440/17 465
Re-drying : 3000C/2h
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 309L-16DIN 8556 : E 23 12 L R 23BS 2926 : E 23 12 L REN 1600 : E 23 12 L R 12
Specifications:
= + ~ (Uo : 50V)
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
C Mn Si Cr Ni0.025 0.80 0.80 22.00 12.00
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]420 560 40 60 J @ 20oC
Corrosion resistingClad steel
X2 CrNiN 18 10X2 CrNi 19 11X5 CrNi 18 10
1.43111.43061.4301
Dissimilar metals (mild and low alloyed steel to stainless steel)Build-up welding on mild and low alloyed steel
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1212141414
300300350350350
30-6040-70
70-110110-140140-180
1.21.83.45.17.3
1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5
9.0/12.09.0/12.0
12.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
59
Stainless Steel Electrodes
Z-309 Cb
High CrNiNb alloyed rutile-basic all positionbuffer electrodeDesigned for buffering mild and low alloyedsteels for nuclear applicationsUsed as a buffer electrode in AISI 312 and AISI347 claddingsUsed for the first run when welding 321 or 347clad steels, prior to completion with 347 typeweld metalFocused and stable arcEasy slag release
Description and Applications:
Welding position
DIN 17 440
DIN 17 440
DIN 17 440
Re-drying: 150o- 2000C/1-2h
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 309Cb-16DIN 8556 : E 23 12 Nb R 23BS 2926 : E 23 12 Nb REN 1600 : E 23 12 Nb R 12
Specifications:
= + ~ (Uo : 50V)
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
C Mn Si Cr Ni Nb0.04 0.90 0.80 23.50 13.50 0.80
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]560 680 32 60 J @ 20oC
Extra low carbon steels C<0.03%
Medium carbon steels C>0.03%
Ti-, Nb stabilized steels
1.43061.43111.43011.43081.45411.4550
X2 CrNi 19 11X2 CrNiN 18 10X5 CrNi 18 10G-X6 CrNi 19 9X6 CrNiTi 18 10X6 CrNiNb 18 10
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1212141414
300300350350350
30-6040-70
70-110110-140140-180
1.21.83.45.17.3
4.04.05.05.05.0
12.012.015.015.015.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
60
Stainless Steel Electrodes
Z-309 Mo
Description and Applications:
Welding position
DIN 17 440
Re-drying: 3000C/2h
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 309MoL-16DIN 8556 : E 23 13 2 R 23BS 2926 : E 23 12 2 REN 1600 : E 23 12 2 L R 12
Specifications:
= + ~ (Uo : 50V)
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
C Mn Si Cr Ni Mo0.025 0.90 0.80 22.50 12.50 2.80
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]560 550 32 60 J @ 20oC
CrNiMo - claddings
Welsing dissimilar metals: mild steel or low alloyed steel to stainless CrNiMo steel up to max thickness of 12mmBuild up welding on mild or low alloyed steel
1.44041.44351.44061.44291.44011.44361.45711.45731.45801.4583
X2 CrNiMo 17 13 2X2 CrNiMo 18 14 3X2 CrNiMoN 17 12 2X2 CrNiMoN 17 13 3X5 CrNiMo 17 12 2X5 CrNiMo 17 13 3X6 CrNiMoTi17 12 2X10 CrNiMoTi18 12X6 CrNiMoNb 17 12 2X10 CrNiMoNb 18 12
Rutile-basic coated low carbon all positionstainless steel electrodeSuitable for welding high alloyed corrosionresistant Cr-Ni-Mo steels, dissimilar steels(austenitic to ferritic steels)Depositon of austenitic cladding root runsFocused and stable arcEasy slag release
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1212141414
300300350350350
30-6040-70
70-110110-140140-180
1.21.83.55.27.5
1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5
9.0/12.09.0/12.0
12.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
61
Stainless Steel Electrodes
Z-310
Description and Applications:Basic-rutile coated, fully austenitic all positionelectrodeSuitable for welding heat resistant Cr and Cr-Ni steelsOxidation and scalig resistance up to 12000C
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
DIN 17 465/43 720Heat resisting stels
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 310-16DIN 8556 : E 25 20 R 26BS 2926 : E 25 20 REN 1600 : E 25 20 R 12 mod
Specifications:
X10 CrAI 24G-X25 CrNiSi 18 9G-X40 CrNiSi 22 9X15 CrNiSi 20 12G-X25 CrNiSi 20 12G-X40 CrNiSi 25 12X15 CrNiSi 25 20G-X15 CrNi 25 20X12 CrNi 25 21G-X40 CrNiSi 25 20
1.47621.48251.48261.48281.48321.48371.48411.48401.48451.4848
C Mn Si Cr Ni0.13 2.10 0.40 26.00 20.00
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]400 580 32 80 J @ 20oC
Re-drying : 3000C/2h
= + ~ (Uo : 70V)
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1212141414
300300350350350
30-6060-90
90-120130-160150-180
1.21.83.75.98.5
1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5
9.0/12.09.0/12.0
12.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
62
Stainless Steel Electrodes
Z-312
Description and Applications:
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Various steel grades such as: Hardenable steels including difficult to weld steelsNon-magnetic austenitic steelsWork hardening austenitic manganese steels
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 312-16DIN 8556 : E 29 9 R 23BS 2926 : E 29 9 REN 1600 : E 29 9 R 12
Specifications:
C Mn Si Cr Ni0.02 0.90 0.80 29.00 9.00
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]500 760 24 -
Re-drying :3000C/2h
= + ~ (Uo : 50V)
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1212141414
300300350350350
30-6060-80
70-11090-150
150-220
1.21.93.75.68.3
4.04.05.05.05.0
12.012.015.015.015.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Rutile-basic coated all position electrode forjoining dissimilar steels and surfacing applicationsSuitable for welding difficult to weld steels suchas: Mn-steel, armour platesExcellent weldability on both AC and DC
63
Stainless Steel Electrodes
Z-312 S
Description and Applications:
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Various steel grades such as: Hardenable steels including difficult to weld steelsNon-magnetic austenitic steelsWork hardening austenitic manganese steels
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 312-16DIN 8556 : E 29 9 R 23BS 2926 : E 29 9 REN 1600 : E 29 9 R 12
Specifications:
C Mn Si Cr Ni0.11 0.90 0.85 29.00 9.00
Re-drying :3000C/2h
= + ~ (Uo : 50V)
Rutile-basic coated all position electrode forjoining dissimilar steels and surfacing applicationsSuitable for welding difficult to weld steels suchas: Mn-steel, armour platesExcellent weldability on both AC and DC
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]500 800 24 50 J @ 20oC
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1212141414
300300350350350
30-6060-80
70-11090-150
150-220
1.11.73.34.97.0
1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5
9.0/12.09.0/12.0
12.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
64
Stainless Steel Electrodes
Z-316 B
Description and Applications:
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 316L-15DIN 8556 : E 19 12 3 L B 20+BS 2926 : E 19 12 3 L BEN 1600 : E 19 12 3 L B 22
Specifications:
C Mn Si Cr Ni Mo0.035 1.00 0.40 18.50 12.00 2.60
Re-drying :3000C/2h
= +
Basic coated low carbon electrode for weldingaustenitic stainless Cr-Ni-Mo steelsGood mechnical propertiesEXcellent position welding properties andpenetration
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]400 590 35 75 J @ 20oC
X2 CrNiMo 17 13 2X2 CrNiMo 18 14 3X2 CrNiMoN 17 12 2X2 CrNiMoN 17 13 3X5 CrNiMo 17 12 2X5 CrNiMo 17 13 3G-X6 CrNiMo 18 12G-X10 CrNiMo 18 9G-X6 CrNiMo 18 10X6 CrNiMoTi 17 12 2X6 CrNiNb 18 10G-X5 CrNiNb 18 9G-X5 CrNiMoNb 18 10X10 CrNiMoNb 18 12
1.44041.44351.44061.44291.44011.44361.44371.44101.44081.45711.45501.45521.45811.4583
DIN 17 440/17 445
DIN 17 440/17 445
DIN 17 440/17 445
Extra low carbonC<0.03%
Medium carbonC>0.03%
Ti-, Nb Stabilized
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1212141414
300300350350350
40-5555-80
75-110110-150140-180
1.21.83.65.6
10.4
1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5
9.0/12.09.0/12.0
12.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
65
Stainless Steel Electrodes
Z-316 L
Description and Applications:
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 316L-16DIN 8556 : E 19 12 3 L R 23BS 2926 : E 19 12 3 L REN 1600 : E 19 12 3 L R 12
Specifications:
C Mn Si Cr Ni Mo0.025 0.80 0.80 18.00 11.50 2.80
Re-drying :3000C/2h
Rutile coated electrode for welding on stabilizedcorrosion resistant Cr-Ni-Mo steelsSmooth metal transter with both AC and DCWeld metal beads exhibit fine ripple formatinFocused and stable arc with low spatter lossEasy slag releaseMoisture resistant formula producing welds freefrom porosity
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]450 580 40 70 J @ 20oC
X2 CrNiMo 17 13 2X2 CrNiMo 18 14 3X2 CrNiMoN 17 12 2X2 CrNiMoN 17 13 3X5 CrNiMo 17 12 2X5 CrNiMo 17 13 3G-X6 CrNiMo 18 12G-X10 CrNiMo 18 9G-X6 CrNiMo 18 10X6 CrNiMoTi 17 12 2X6 CrNiNb 18 10G-X5 CrNiNb 18 9G-X5 CrNiMoNb 18 10X10 CrNiMoNb 18 12
1.44041.44351.44061.44291.44011.44361.44371.44101.44081.45711.45501.45521.45811.4583
DIN 17 440/17 445
DIN 17 440/17 445
DIN 17 440/17 445
Extra low carbonC<0.03%
Medium carbonC>0.03%
Ti-, Nb Stabilized
= + ~ (Uo : 50V)
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1212141414
300300350350350
30-5050-75
75-110110-150140-190
1.11.83.45.17.3
1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5
9.0/12.09.0/12.0
12.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
66
Stainless Steel Electrodes
Z-316 LVD
Description and Applications:
Welding position
ASME: 1G 2F 2G 3G 3G 4G
ISO 6947 PA PB PC PF PG PE
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 316L-17DIN 8556 : E 19 12 3 L R 13BS 2926 : E 19 12 3 L REN 1600 : E 19 12 3 L R 11
Specifications:
C Mn Si Cr Ni Mo0.025 0.80 0.70 18.00 11.50 2.70
Re-drying :3000C/2h
Rutile-acid austenitic stainless Cr-Ni-Mo steelelectrode for welding 316L or equivalent steelsin the vertical down positionDesigned for welding root passes in grooveswith root openingHigh corrosion resistance in oxidizing environments
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]440 600 35 70 J @ 20oC
X2 CrNiMo 17 13 2X2 CrNiMo 18 14 3X2 CrNiMoN 17 12 2X2 CrNiMoN 17 13 3X5 CrNiMo 17 12 2X5 CrNiMo 17 13 3G-X6 CrNiMo 18 12G-X10 CrNiMo 18 9G-X6 CrNiMo 18 10X6 CrNiMoTi 17 12 2X6 CrNiNb 18 10G-X5 CrNiNb 18 9G-X5 CrNiMoNb 18 10X10 CrNiMoNb 18 12
1.44041.44351.44061.44291.44011.44361.44371.44101.44081.45711.45501.45521.45811.4583
DIN 17 440/17 445
DIN 17 440/17 445
DIN 17 440/17 445
Extra low carbonC<0.03%
Medium carbonC>0.03%
Ti-, Nb Stabilized
= + ~ (Uo : 50V)
3/321/8
2.53.25
1212
300300
60-7080-100
1.42.4
1.51.5
9.09.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
67
Stainless Steel Electrodes
Z-316 LHR
Description and Applications:
Welding position
ASME: 1G 2F
ISO 6947 PA PB
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 316L-16DIN 8556 : E 19 12 3 L R 26 150BS 2926 : E 19 12 3 L REN 1600 : E 19 12 3 L R 53 mod
Specifications:
C Mn Si Cr Ni Mo0.025 0.80 0.80 18.00 11.50 2.70
Re-drying :3000C/2h
Rutile coated high recovery (145%) electrodefor welding austenitic stainless Cr-Ni-Mo steelsUsed whenever a high deposition rate is requiredEasy slag rlease, smooth and finely rippleddepositExcellent for fillet and downhand welding
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]470 580 40 70 J @ 20oC
X2 CrNiMo 17 13 2X2 CrNiMo 18 14 3X2 CrNiMoN 17 12 2X2 CrNiMoN 17 13 3X5 CrNiMo 17 12 2X5 CrNiMo 17 13 3G-X6 CrNiMo 18 12G-X10 CrNiMo 18 9G-X6 CrNiMo 18 10X6 CrNiMoTi 17 12 2X6 CrNiNb 18 10G-X5 CrNiNb 18 9G-X5 CrNiMoNb 18 10X10 CrNiMoNb 18 12
1.44041.44351.44061.44291.44011.44361.44371.44101.44081.45711.45501.45521.45811.4583
DIN 17 440/17 445
DIN 17 440/17 445
DIN 17 440/17 445
Extra low carbonC<0.03%
Medium carbonC>0.03%
Ti-, Nb Stabilized
= + ~ (Uo : 70V)
3/321/8
5/323/16
2.53.254.05.0
1214/18
1818
300350/450
450450
75-95110-130135-155180-210
2.54.8/6.2
9.615.1
4.05.0/6.0
6.06.0
12.015.0/18.0
18.018.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
68
Stainless Steel Electrodes
Z-316 HS
Description and Applications:
Welding position Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 316-16DIN 8556 : E 19 12 3 MPR 23 170BS 2926 : E 19 12 3 RMPEN 1600 : E 19 12 2 R 72
Specifications:
C Mn Si Cr Ni Mo0.025 0.90 0.70 19.60 11.70 2.80
Re-drying :3000C/2h
High recovery (170%) rutile coated electrodefor welding austenitic stainless Cr-Ni-Mo steelsUsed whenever easy welding, smooth weldingsurfaces and a high deposition rate are required
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]470 580 35 60 J @ 20oC
X2 CrNiMo 17 13 2X2 CrNiMo 18 14 3X2 CrNiMoN 17 12 2X2 CrNiMoN 17 13 3X5 CrNiMo 17 12 2X5 CrNiMo 17 13 3G-X6 CrNiMo 18 12G-X10 CrNiMo 18 9G-X6 CrNiMo 18 10X6 CrNiMoTi 17 12 2X6 CrNiNb 18 10G-X5 CrNiNb 18 9G-X5 CrNiMoNb 18 10X10 CrNiMoNb 18 12
1.44041.44351.44061.44291.44011.44361.44371.44101.44081.45711.45501.45521.45811.4583
DIN 17 440/17 445
DIN 17 440/17 445
DIN 17 440/17 445
Extra low carbonC<0.03%
Medium carbonC>0.03%
Ti-, Nb Stabilized
= + ~ (Uo : 50V)
ASME: 1G 2F 3G
ISO 6947 PA PB PF
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1214
14/181818
300350
350/450450450
30-6065-10590-145
145-215180-270
1.83.3
5.6/7.210.917.2
4.05.0
5.0/6.06.06.0
12.015.0
15.0/18.018.018.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
69
Stainless Steel Electrodes
Z-317
Description and Applications:
Welding position Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 317L-16BS 2926 : E 19 13 4 L REN 1600 : E 19 13 4 L R 12 mod
Specifications:
C Mn Si Cr Ni Mo0.025 0.90 0.75 19.00 13.00 3.50
Re-drying : 3000C/2h
Rutile coated electrode for dissimilar weldingSuitable for difficult to weld steelsEnhanced corrosion resistance applications
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]500 650 37 100 J @ 20oC
X2 CrNiMoN 18 18 3X2 CrNiMoN 17 13 3X2 CrNiMo 18 14 3X2 CrNiMo 18 16 4
1.44281.44291.44351.4438
DIN 17 440/17 445Extra low carbonC<0.03%
= + ~ (Uo : 50V)
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1212141414
300300350350350
35-5540-80
80-110110-150150-220
1.21.83.45.27.4
1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5
9.0/12.09.0/12.0
12.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
70
Stainless Steel Electrodes
Z-318 B
Description and Applications:
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 318-15DIN 8556 : E 19 12 3 Nb B 20+BS 2926 : E 19 12 3 Nb BEN 1600 : E 19 12 3 Nb B 22
Specifications:
C Mn Si Cr Ni Mo Cb0.035 1.05 0.35 18.50 11.50 2.75 0.35
Re-drying :3000C/2h
Basic coated all position electrode for weldingTi, Nb stabilized austenitic stainless Cr-Ni-MosteelsHigh reistance to intergranular corrosion upto 4000CExcellent weldability and easy slag release
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]480 620 35 -
X2 CrNiMo 17 13 2X2 CrNiMo 18 14 3X2 CrNiMoN 17 12 2X2 CrNiMoN 17 13 3X5 CrNiMo 17 12 2X5 CrNiMo 17 13 3G-X6 CrNiMo 18 12G-X10 CrNiMo 18 9G-X6 CrNiMo 18 10X6 CrNiMoTi 17 12 2X6 CrNiNb 18 10G-X5 CrNiNb 18 9G-X5 CrNiMoNb 18 10X10 CrNiMoNb 18 12
1.44041.44351.44061.44291.44011.44361.44371.44101.44081.45711.45501.45521.45811.4583
DIN 17 440/17 445
DIN 17 440/17 445
DIN 17 440/17 445
Extra low carbonC<0.03%
Medium carbonC>0.03%
Ti-, Nb Stabilized
= +
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1212141414
300300350350350
30-5050-70
80-100110-140140-180
1.21.83.65.6
10.4
1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5
9.0/12.09.0/12.0
12.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
71
Stainless Steel Electrodes
Z-318
Description and Applications:
Welding position Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 318-16DIN 8556 : E 19 12 3 Nb R 23BS 2926 : E 19 12 3 Nb REN 1600 : E 19 12 3 Nb R 12
Specifications:
C Mn Si Cr Ni Mo Nb0.025 0.90 0.80 18.00 11.50 1.60 0.40
Re-drying :3000C/2h
Rutile-basic coated all position electrode forwelding Ti, Nb stabilized austenitic stainlessCr-Ni-Mo steelsHigh resistance to intergranular corrosion upto 4000CExcellent weldability and easy slag release an both AC and DC
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]490 600 35 60 J @ 20oC
X2 CrNiMo 17 13 2X2 CrNiMo 18 14 3X2 CrNiMoN 17 12 2X2 CrNiMoN 17 13 3X5 CrNiMo 17 12 2X5 CrNiMo 17 13 3G-X6 CrNiMo 18 12G-X10 CrNiMo 18 9G-X6 CrNiMo 18 10X6 CrNiMoTi 17 12 2X6 CrNiNb 18 10G-X5 CrNiNb 18 9G-X5 CrNiMoNb 18 10X10 CrNiMoNb 18 12
1.44041.44351.44061.44291.44011.44361.44371.44101.44081.45711.45501.45521.45811.4583
DIN 17 440/17 445
DIN 17 440/17 445
DIN 17 440/17 445
Extra low carbonC<0.03%
Medium carbonC>0.03%
Ti-, Nb Stabilized
= + ~ (Uo : 50V)
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1212141414
300300350350350
40-5550-80
80-110110-150150-180
1.11.73.34.97.2
1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5
9.0/12.09.0/12.0
12.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
72
Stainless Steel Electrodes
Z-320
Description and Applications:
Welding position Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 385-16 modDIN 8556 : E 20 25 5 L Cu R 26EN 1600 : E 20 25 5 Cu L R 12
Specifications:
C Mn Si Cr Ni Mo Cu0.025 1.30 0.85 20.00 25.50 4.70 1.70
Re-drying :3000C/2h
Rutie-basic fully austenitic stainless steel electrodeHigh resistance in phosphoric and sulphuricacid applicatonsSmooht metal trasfer on both AC and DC
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]410 600 40 80 J @ 20oC
G-X7 NiCrMoCuNb 25 20X5 NiCrMoCu Ti 20 18G-X2 NiCrMoCuN 20 18G-X2 NiCrMoCuN 25 20X1 NiCrMoCuN 25 20 5G-X7 CrNiMoCuNb18 18X5 NiCrMoCuNb 22 18
1.45001.45061.45311.45361.45391.45851.4586
DIN/SEW 400/410Fully austenitic NiCrMoCu andCrNiMoCu steel
= + ~ (Uo : 50V)
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
3/321/8
5/32
2.53.254.0
121414
300350350
40-7560-10580-140
1.83.14.6
1.5/2.02.0/2.52.0/2.5
9.0/12.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
73
Stainless Steel Electrodes
Z-347 B
Description and Applications:
Welding position Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 347-15DIN 8556 : E 19 9 Nb B 20+BS 2926 : E 19 9 Nb BEN 1600 : E 19 9 Nb B 22
Specifications:
C Mn Si Cr Ni Nb0.03 1.00 0.50 19.00 10.00 0.35
Re-drying :3000C/2h
Basic coated all position electrode for weldingTi, or Nb stabilized austenitic Cr-Ni steelsHigh reistance to intergranular corrosion upto 4000CExcellent weldability and easy slag release
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]480 620 35 -
X6 CrNiTi 18 10X6 CrNiNb 18 10G-X5 CrNiNb 18 9X5 CrNi 18 10X2 CrNi 19 11G-X6 CrNi 18 9G-10 CrNi 18 8
1.45411.45501.45521.43011.43061.43081.4312
DIN 17 440/17 445
DIN 17 440/17 445
Ti-, Nb Stabilized
Non Stabilized
= +
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1212141414
300300350350350
30-5050-70
80-100110-140140-180
1.21.83.65.6
10.4
1.5/2.01.5/2.02.0/2.52.0/2.5
6.0
9.0/12.09.0/12.0
12.0/15.012.0/15.0
18.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
74
Stainless Steel Electrodes
Z-347
Description and Applications:
Welding position Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 347-16DIN 8556 : E 19 9 Nb R 23BS 2926 : E 19 9 Nb REN 1600 : E 19 9 Nb R 12
Specifications:
C Mn Si Cr Ni No0.03 0.80 0.80 19.00 10.00 0.40
Re-drying :3000C/2h
Rutile-basic coated all position electrode forwelding Ti or Nb stabilized austenitic Cr-NisteelsHigh resistance to intergranular corrosion upto 4000CExcellent weldability and slag release an bothAC and DC
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]400 590 35 -
DIN 17 440/17 445
DIN 17 440/17 445
= + ~ (Uo : 50V)
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1212141414
300300350350350
35-5550-80
80-110120-150150-180
1.11.73.34.97.1
1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5
9.0/12.09.0/12.0
12.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Ti-, Nb Stabilized
Non Stabilized
X6 CrNiTi 18 10X6 CrNiNb 18 10G-X5 CrNiNb 18 9X5 CrNi 18 10X2 CrNi 19 11G-X6 CrNi 18 9G-10 CrNi 18 8
1.45411.45501.45521.43011.43061.43081.4312
75
Stainless Steel Electrodes
Z-ARM BS
Description and Applications:Basic coated austenitic stainless steel electrodeespecially designed for welding armour plateand other difficult to weld steelsAll position welding on DC currentNeat weld appearanceExcelent slag release
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Forged and cast armour steels, alloyed steels, high carbon steels, Mn steel, high strength steels, spring steels andstainless steelsJoining dissimilar steels and steels having different chemical composition
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Welding parameters and packaging data
AWS/ASME SFA A5.4 : E 308Mo-15 modBS 2926 : E 19 9 3 B
Specifications:
= +
C Mn Si Cr Ni Mo0.05 1.90 0.30 20.50 9.80 2.90
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]540 730 25 -
Re-drying : 3000C/2h
1/85/323/16
3.254.05.0
141414
350350350
90-120135-185175-255
3.24.76.9
2.0/2.52.0/2.55.0/6.0
12.0/15.012.0/15.012.0/18.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
76
Stainless Steel Electrodes
Z-Ni Vi
Description and Applications:
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
C Mn Si Cr Ni Mo0.03 0.85 0.75 19.50 9.80 2.60
Rutile coated austenitic stainless steel electrodeespecially designed for welding armour platesand other difficult to weld steelsAll position welding on both AC and DCNeat weld appearanceExcellent slag release
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]
= + ~ (Uo : 70V)
Forged and cast armour steels, alloyed steels, high carbon steels, Mn steel, high strength steels, spring steels andstainless steelsJoining dissimilar steels and steels having different chemical composition
AWS/ASME SFA A5.4 : E 308Mo-16 modBS 2926 : E 19 9 3 R
Specifications:
500 680 35 90 J @ 20oC
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Welding parameters and packaging data
Re-drying :3000C/2h
5/643/321/8
5/323/16
2.02.5
3.254.05.0
1212141414
300300350350350
35-6050-80
90-120130-170160-220
1.21.83.35.07.5
1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5
9.0/12.09.0/12.0
12.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
77
Stainless Steel Electrodes
Z-2209 B
Description and Applications:
Welding position Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
AWS/ASME SFA A5.4 : E 2209-15DIN 8556 : E 22 9 3 L B 20+EN 1600 : E 22 9 3 L B 22
Specifications:
C Mn Si Cr Ni Mo N<0.04 1.00 0.40 25.50 9.00 3.00 0.14
Basic coated electrode for welding stainlessferritic-austenitic Cr-Ni-Mo Steels (Duplex steels)Highly resistant to pitting and stess corrosioncrakingRecommended for sub-zero toughness, positionalwelding applicationsMaximum temperature of use +2500C
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]620 770 25 100 J @ 20oC
X2 CrNiMoN 22 5 3 1.4462DIN/SEW 400Duplex Stainless-Steels
= +
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Welding parameters and packaging data
Re-drying :3000C/2h
3/321/8
5/32
2.53.254.0
141818
350450450
50-7070-100
100-150
1.63.55.3
1.52.02.0
9.012.012.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
78
Stainless Steel Electrodes
Z-2209 R
Description and Applications:
Welding position
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
AWS/ASME SFA A5.4 : E 2209-16DIN 8556 : E 22 9 3 L R 23EN 1600 : E 22 9 3 L R 12
Specifications:
C Mn Si Cr Ni Mo N0.03 0.90 0.80 25.50 9.00 3.00 0.14
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]620 750 25 60 J @ 20oC
X2 CrNiMoN 22 5 3 1.4462DIN/SEW 400Duplex Stainless-Steels
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Welding parameters and packaging data
Re-drying :3000C/2h
3/321/8
5/32
2.53.254.0
141818
350450450
60-7070-10090-140
1.63.55.3
1.52.02.0
9.012.012.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Rutile-basic coated electrode for welding stainlessferritic-austenitic Cr-Ni-Mo Steels (Duplex steels)Highly resistant to pitting and stress corrosioncrakingSuited for all-position welding applications onboth AC and DCMaximum temperature of use +2500C
Current
= + ~ (Uo : 50V)
79
Stainless Steel Electrodes
Z-2594 R
Description and Applications:
Welding position
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
AWS/ASME SFA 5.4 : E 2594-16
EN 1600 2594 NLR 2 3
Specifications:
C Mn Si Cr Ni Mo Cu N FN0.03 0.9 0.9 25.25 9.8 4.0 0.75 0.25 30-50
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]
700 850 26 60 J@20oC
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Rutile electrode designed for welding ferritic- austenitic steels of
Super Duplex types.
Its chemical composition allows high resistance to pitting and
intergranular corrosion combined to excellent mechanical
properties.
Well suited for condition in the off-shore field.
Current
= + ~ (Uo : 50V)
40J@-40oC
Materials to be welded
1.4462
Super Duplex Stainless-Steel
SAFZERON100
ASTM EN1.44102507 S32750
S32760
Welding parameters and packaging data
3/321/8
5/32
2.53.254.0
141414
350450450
50-7570-12090-160
222
121212
Diain mm
Lengthin mm
Current[amps]
Weight packet[kg]
Weight carton[kg]
80
Hard Facing Electrodes
Z-104
Description and Applications:
Welding position Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 8555: E 1 UM 300Specifications:
C Mn Si Cr Fe0.10 0.50 0.80 3.40 Bal.
Basic coated abrasion resistant electrodeMachinable weld depositModerate impact toughnessApplicable for gear teeth, brake drums, sprockets,bushings and rail crossings
Hardness28-33 Rc 275-325 HB
= + ~ (Uo : 70V)
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Welding parameters and packaging data
Re-drying :3000C/2h
3/321/8
5/323/16
2.53.254.05.0
14181818
350350/450
450450
60-80110-130140-180190-240
2.14.56.7
11.2
5.05.0/6.0
6.06.0
15.015.0/18.0
18.018.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
81
Hard Facing Electrodes
Z-105
Description and Applications:
Welding position Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 8555: E 1 UM 400Specifications:
C Mn Si Cr Fe0.30 0.30 0.70 3.20 Bal.
Basic coated electrode for surfacing parts subjectedto medium abrasion and high compressionApplicable for runners, caterpillar track links,gear wheels and dredging machinery
Hardness37-42Rc 350-400 HB
= + ~ (Uo : 70V)
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Welding parameters and packaging data
Re-drying :3000C/2h
3/321/8
5/323/161/4
2.53.254.05.06.0
1414/18
181818
350350/450
450450450
70-100105-115120-160180-240250-290
2.23.5/4.5
6.610.315.0
5.05.0/6.0
6.06.06.0
15.015.0/18.0
18.018.018.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
82
Hard Facing Electrodes
Z-110
Description and Applications:
Welding position Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 8555: E 6 UM 55 RSpecifications:
C Mn Si Cr Mo Fe0.30 0.40 0.70 11.90 0.90 Bal.
Rutile coated electrode for corrosion resistanthard surfacing up to 5000CApplicable for shafts, rails, mixer arms, valveseats of cast steel leading buckets
Hardness53-56 Rc 525-580 HB
= + ~ (Uo : 70V)
ASME: 1G 2F 2G 3G
ISO 6947 PA PB PC PF
Welding parameters and packaging data
Re-drying :1200C/1h
1/85/323/16
3.254.05.0
1414/18
18
350350450
85-120120-150160-210
3.04.5/5.8
9.1
5.05.06.0
15.015.018.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
83
Hard Facing Electrodes
Z-111
Description and Applications:
Welding position Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 8555: E 6 UM 55Specifications:
C Mn Si Cr Mo Fe0.50 1.10 0.40 7.20 0.90 Bal.
Rutile coated electrode for hard surfacing of earth moving machinesLow open current voltageHeat resistant up to 6000CApplicable for buldozer blades, crusher jaws,excavator teeth and mixersNon machinable weld deposit
Hardness55-58Rc 560-615 HB
= + ~ (Uo : 50V)
ASME: 1G 2F 2G 3G
ISO 6947 PA PB PC PF
Welding parameters and packaging data
Re-drying : 1200C/1h
3/321/8
5/323/161/4
2.53.254.05.06.0
1414/1814/18
1818
350350/450350/450
450450
70-10090-110
140-180180-250220-280
2.13.5/4.65.3/6.8
10.615.0
5.05.0/6.05.0/6.0
6.06.0
15.015.0/18.015.0/18.0
18.018.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
84
Hard Facing Electrodes
Z-113
Description and Applications:
Welding position Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 8555: E 6 UM 60Specifications:
C Mn Si Cr Mo V Fe0.50 0.40 0.80 7.50 0.50 0.60 Bal.
Basic coated electrode for surfacing parts subjectedto impact, high compression stresses and severeabrasionApplicable for tracctor and crane parts, shovelteeth, crusher hammers and scraper blades
Hardness57-62 Rc
= + ~ (Uo : 70V)
ASME: 1G 2F 2G 3G
ISO 6947 PA PB PC PF
Welding parameters and packaging data
Re-drying : 3000C/2h
3/321/8
5/323/161/4
2.53.254.05.06.0
1414/1814/18
1818
350350/450350/450
450450
60-80100-130120-160180-210220-280
2.13.5/4.45.3/6.7
10.615.0
5.05.0/6.05.0/6.0
6.06.0
15.015.0/18.015.0/18.0
18.018.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
85
Hard Facing Electrodes
Z-114
Description and Applications:
Welding position Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 8555: E 6 UM 60Specifications:
C Mn Si Cr Mo0.60 0.90 0.70 4.70 1.80
Rutile coated electrode for surfacing partssubjected to abrasion and impactApplicable for rails truck wheels, worms, couplingshafts and spindlesNon machinable weld deposit
Hardness58-60 Rc 620-650 HB
= + ~ (Uo : 70V)
ASME: 1G 2F 2G 3G
ISO 6947 PA PB PC PF
Welding parameters and packaging data
Re-drying : 1200C/1h
3/321/8
5/323/16
2.53.254.05.0
1414
14/1818
350350
350/450450
75-110110-140150-190190-260
2.43.9
6.1/7.812.3
5.05.0
5.0/6.06.0
15.015.0
15.0/18.018.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
86
Hard Facing Electrodes
Z-120
Description and Applications:
Welding position Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 8555: E 10 UM 60 ZSpecifications:
C Mn Si Cr Fe3.00 0.20 0.90 29.00 Bal.
Rutile coated electrode for high abrasion withoutimpact applications160% weld metal recoveryCan be used both for buildups and rebuildingSuitable for crushing mills, rock drills, mixersand plough shares
Hardness60 Rc 60-650 HB
= + ~ (Uo : 70V)
ASME: 1G 2F
ISO 6947 PA PB
Welding parameters and packaging data
Re-drying : 3000C/1-2h
1/85/323/16
3.254.05.0
141414
350350350
100-130120-160150-240
5.68.3
13.3
4.04.04.0
12.012.012.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
87
Hard Facing Electrodes
Z-120 B
Description and Applications:
Welding position Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 8555: E 10 UM 60 GRSpecifications:
C Mn Si Cr Fe3.90 0.30 1.00 24.90 Bal.
Basic coated electrode for surfacing parts subjectedto severe abrasionApplicable for crusher parts, conveyer screwsand bucket teeth
Hardness60 Rc 650 HB
= +
ASME: 1G 2F
ISO 6947 PA PB
Welding parameters and packaging data
Re-drying : 3000C/1-2h
1/85/323/16
3.254.05.0
141818
350450450
110-140140-180185-230
5.310.616.3
4.56.06.0
13.518.018.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
88
Hard Facing Electrodes
Z-123
Description and Applications:
Welding position
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 8555: E 10 UM 65 GRSpecifications:
C Mn Si Cr Nb Fe6.50 0.80 0.60 22.70 7.00 Bal.
Basic coated electrode for hardsurfacing partssubjected to severe abrasion without impactUse up to 4500CApplicable for screws of refractory materialpresses, brick presses and cement presses
Hardness64 Rc 720 HB
ASME: 1G 2F
ISO 6947 PA PB
Welding parameters and packaging data
Re-drying : 3000C/1-2h
1/85/323/16
3.254.05.0
141818
350450450
115-150135-200195-255
5.711.517.6
4.56.06.0
13.518.018.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70V)
89
Hard Facing Electrodes
Z-125
Description and Applications:
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
DIN 8555: E 10 UM 65 GRSpecifications:
C Mn Si Cr Mo Nb V W Fe4.30 0.70 0.80 17.70 4.90 2.00 0.60 3.00 Bal.
Hardness66 Rc 760 HB
= +
Welding parameters and packaging data
Re-drying : 3000C/1-2h
Welding position
ASME: 1G 2F
ISO 6947 PA PB
Basic coated electrode for hardsurfacing partssubjected to severe abrasion without impactUse up to 6500CApplicable for sinter crushers, scraper wires inzinc industries, scrap collectors and mechanicalstokers
1/85/323/16
3.254.05.0
141818
350450450
125-160150-200220-300
6.312.519.7
4.56.06.0
13.518.018.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
90
Hard Facing Electrodes
Z-130
Description and Applications:
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Specifications:
C Mn Si Cr Mo W V Fe0.70 0.70 0.80 3.70 8.00 2.70 0.60 Bal.
Hardness60-65 Rc 650-740 HB
= +
Welding parameters and packaging data
Re-drying : 3000C/1-2h
Welding position
Basic coated electrode for high speed tool surfacingModerate resistance to impactHeat resistant up to 6000CApplicable for cutting tools, drills, knives, shears,punches and dies
AWS/ASME SFA A5. 13 : EFe5-B modDIN 8555 : E 4 UM 60 S
ASME: 1G 2F 2G
ISO 6947 PA PB PC
3/321/8
5/32
2.53.254.0
141414
350350350
80-100110-130130-160
2.74.36.7
4.54.5/5.04.5/5.0
13.513.5/15.013.5/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
91
Hard Facing Electrodes
Z-151
Description and Applications:
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Specifications:
C Mn Si Cr Ni Fe0.60 12.20 0.60 0.10 4.60 Bal.
Hardness
230 HBAs welded
500 HBAfter work hardening
= +
Welding parameters and packaging data
Re-drying : 3000C/1-2h
Welding position
Basic coated cold work hardening Mn austeniticelectrodeHigh resistance to impact and shockUsed for rebuilding and joining between Mnsteel and Carbon steelApplicable for crusher plates, dredger teeth andhammers
AWS/ASME SFA A5. 13 : EFeMn-ADIN 8555 : E 7 UM 250 KP
ASME: 1G 2F 2G 3G
ISO 6947 PA PB PC PF
1/85/323/161/4
3.254.05.06.0
14/1814/18
1818
350/450350/450
450450
100-130150-180200-250240-290
3.76.0
11.116.2
5.0/6.05.0/6.0
6.06.0
15.0/18.015.0/18.0
18.018.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
92
Hard Facing Electrodes
Z-151 NC
Description and Applications:
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Specifications:
C Mn Si Cr Ni Fe1.00 13.20 0.25 4.60 5.00 Bal.
Hardness
200 HBAs welded
520 HBAfter work hardening
= +
Welding parameters and packaging data
Re-drying : 3000C/1-2h
Welding position
Basic coated cold work hardening Mnaustenitic electrodeHigh resistance to impact and shockUsed for rebuilding and joining betweenMn steel and Carbon steelApplicable for crusher plates, dredger teethand hammersNon conductive coating
AWS/ASME SFA A5. 13 : EFeMn-A modDIN 8555 : E 7 UM 250 KP
ASME: 1G 2F 2G 3G
ISO 6947 PA PB PC PF
1/85/323/161/4
3.254.05.06.0
14141818
350350450450
95-130130-180190-250240-280
3.96.3
11.217.0
5.05.06.06.0
15.015.018.018.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
93
Hard Facing Electrodes
Z-152
Description and Applications:
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
C Mn Si Cr Fe0.60 12.90 0.30 14.70 Bal.
Hardness
200 HBAs welded
500 HBAfter work hardening
Welding parameters and packaging data
Re-drying : 3000C/1-2h
Welding position
Rutile coated electrode for surfacing partssubjected to high impact and cavitationJoining and surfacing Mn steels and hard toweld steelsApplicable for dredge pumps, hydraulic presspistons, crushing equipment and rails
1/85/323/161/4
3.254.05.06.0
18181818
450450450450
110-140165-175190-220260-290
6.49.6
13.519.5
6.06.06.06.0
18.018.018.018.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70V)
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
94
Hard Facing Electrodes
Z-STEL 6
Description and Applications:
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Specifications:
C Cr W Co1.10 28.00 4.50 Bal.
Hardness44 Rc
= +
Welding parameters and packaging data
Re-drying : 3000C/1-2h
Welding position
Cobalt base hard facing electrodeUsed for high temperature high impact applications(up to 9000C)Corrosion resistant in organic and anorganicmedia
AWS/ASME SFA A5. 13 : ECo Cr-ADIN 8555 : E 20 UM 45 CTZ
ASME: 1G 2F
ISO 6947 PA PB
1/85/323/16
3.254.05.0
141818
350350350
90-120120-155150-190
3.75.98.5
2.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
95
Hard Facing Electrodes
Z-STEL 12
Description and Applications:
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Specifications:
C Cr W Co1.40 29.00 8.00 Bal.
Hardness47 Rc
= +
Welding parameters and packaging data
Re-drying : 3000C/1-2h
Welding position
Cobalt base hard facing electrodeUsed for high temperature moderate impact applications (up to 9000C)Corrosion resistant in organic and anorganicmedia
AWS/ASME SFA A5. 13 : ECo Cr-BDIN 8555 : E 20 UM 50 CTZ
ASME: 1G 2F
ISO 6947 PA PB
1/85/323/16
3.254.05.0
141818
350350350
90-120120-155150-190
3.95.97.3
2.0/2.52.0/2.52.0/2.5
12.012.012.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
96
Non Ferrous Electrodes
Z-Ni 1
Description and Applications:
Welding position Current
Typical all weld metal composition [wt%]
Specifications:
C Mn Si Ti Fe Ni0.025 0.40 0.50 2.30 0.30 Bal.
Basic coated pure nickel electrodeEspecially for welding nickel and nickel alloysand joining to unalloyed and low alloyed steelsSuitable for welding NiCu and NiCu alloys tocarbon, stainless and nickel base alloys
= +
ASME: 1G 2F 2G 3G
ISO 6947 PA PB PC PF
AWS/ASME SFA A5. 11 : ENi-1DIN 1736 : EL-NiTi 3
Typical all weld metal mechanical properties
Materials to be welded
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]310 470 30 -
ASTMAlloy 200Alloy 201Alloy 205--------
UNSN02200N02201N02205--------
DINNi99.2LC Ni99LC Ni99.6Ni99.6Ni99.8Ni99.4FeNiMn1NiMn2NiMn3AlNiMn5NiA14Ti
W.Nr2.40662.40682.40612.40602.40502.40622.41061.42102.41222.41162.4128
Welding parameters and packaging data
Re-drying :2500C/1-2h
3/321/8
5/32
2.53.254.0
141414
350350350
50-8075-120
100-140
2.03.35.1
2.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.0
12.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
97
Non Ferrous Electrodes
Z-Ni B
Description and Applications:
Welding position
Typical all weld metal composition [wt%]
Specifications:
C Mn Si Fe Mo V Ni0.05 0.60 0.60 5.00 27.00 0.25 Bal.
Basic coated thick electrode for depositingNiMo-1 alloy and welding NiMo alloysCan be used at very high temperatures inreducing gases environmentExcellent resistance to acetic, phosphoric,sulphuric and hydrochloric acids
ASME: 1G 2F 2G 3G
ISO 6947 PA PB PC PF
AWS/ASME SFA A5. 11 : ENiMo-1DIN 1736 : EL-NiMo 29
Typical all weld metal mechanical properties
Materials to be welded
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]500 700 26 -
ASTMAlloy B2
UNSN10665
DINNiMo29
W.Nr2.4616
Welding parameters and packaging data
Re-drying :2500C/2h
3/321/8
5/32
2.53.254.0
141414
350350350
90-110130-150180-200
3.66.39.3
2.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70V)
98
Non Ferrous Electrodes
Z-Ni A2
Description and Applications: Specifications:Basic coated electrode designed for joining Nickel base alloys andfor joining dissimilar steels. The welding designed to endure widerange of temp from cryogenic up to 9800C
ASME: 1G 2F 2G 3G
ISO 6947 PA PB PC PF
AWS/ASME SFA A5. 11 : ENiCrFe-2DIN 1736 : EL-NiCr 15 FeNb
Typical all weld metal mechanical properties
Materials to be welded
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]410 650 32 50 J @ -196
0C
ASTMAlloy 800Alloy 600Alloy BAlloy C-Alloy 75Alloy 80AAlloy 9%Ni
UNSN08800N06600N06004N06003-N06075N07080K81340
DINX10 NiCrAlTi32 20NiCr 15FeNiCr60 15NiCr80 20NiCr10NiCr20TiNiCr20TiAlX8 Ni9
W.Nr1.48762.46402.48672.48692.48702.49512.49521.5662
Welding parameters and packaging data
Typical all weld metal composition [wt%]C Mn Si Cr Mo Nb Fe Ni
0.07 3.40 0.40 16.10 1.80 2.10 6.60 Bal.
Re-drying : 3000C/1-2h
3/321/8
5/323/16
2.53.254.05.0
14141414
350350350350
70-90100-135130-180190-220
2.64.36.5
10.2
2.0/2.52.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Current
= + ~ (Uo : 70V)
99
Non Ferrous Electrodes
Z-NI 182
Description and Applications: Specifications:AWS/ASME SFA A5. 11 : ENiCrFe-3DIN 1736 : EL-NiCr 15 FeMn
Typical all weld metal mechanical properties
Materials to be welded
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]380 620 32 80 J @ -196
0C
ASTMAlloy 600Alloy 601Alloy 800Alloy 800HAlloy 75Alloy 80AAlloy 90Alloy 9%Ni
UNSN06600N06601N08800N08810N06075N07080N07090K81340
DINNiCr15FeNiCr23FeX10 NiCrAlTi32 20X10 NiCrAlTi32 20NiCr20TiNiCr20TiAlNiCr20Co18TiX8 Ni9
W.Nr2.46402.48511.48761.48582.49512.49522.49691.5662
Welding parameters and packaging data
Typical all weld metal composition [wt%]C Mn Si Cr Nb Fe Ni
0.02 7.50 0.40 13.80 1.80 4.40 Bal.
Re-drying : 2500C/1-2h
3/321/8
5/323/16
2.53.254.05.0
14141414
350350350350
75-100100-140140-180170-210
2.64.67.0
10.0
2.0/2.52.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Synthetic basic coated NiCr electrodeFor welding Ni-base alloys, claddings anddissimilar metalsHigh creep resistant and high resistance toembrittlement
Current
= +
Welding position
ASME: 1G 2F 2G 3G
ISO 6947 PA PB PC PF
100
Description and Applications: Specifications:AWS/ASME SFA A5. 11 : ENiCrFe-3DIN 1736 : EL-NiCr 15 FeMn
Typical all weld metal mechanical properties
Materials to be welded
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]400 580 32 110 J @ -196
0C
ASTMAlloy 600Alloy 601Alloy 800Alloy 800HAlloy 75Alloy 80AAlloy 90Alloy 9%Ni
UNSN06600N06601N08800N08810N06075N07080N07090K81340
DIN NiCr15FeNiCr23Fe X10 NiCrAlTi32 20X10 NiCrAlTi32 20NiCr20TiNiCr20TiAlNiCr20Co18Ti X8 Ni9
W.Nr2.46402.48511.48761.48582.49512.49522.49691.5662
Welding parameters and packaging data
Typical all weld metal composition [wt%]C Mn Si Cr Nb Fe Ni
0.02 6.70 0.70 13.50 1.60 5.00 Bal.
Re-drying : 2500C/1-2h
3/321/8
5/323/16
2.53.254.05.0
14141414
350350350350
105-145140-180175-215225-265
2.84.87.3
11.2
2.0/2.52.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Rutile basic coated NiCr electrode For welding Ni-base alloys, claddings anddissimilar metals High creep resistant and high resistance toembrittlement
Welding position
ASME: 1G 2F 2G 3G
ISO 6947 PA PB PC PF
Current
= + ~ (Uo : 70V)
Non Ferrous Electrodes
Z-NI 182
101
Non Ferrous Electrodes
Z-Ni 112
Description and Applications: Specifications:AWS/ASME SFA A5. 11 : ENiCrMo-3DIN 1736 : EL-NiCr 20 Mo 9 Nb
Typical all weld metal mechanical properties
Materials to be welded
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]530 780 38 70 J @ -196
0C
ASTMAlloy 625Alloy 825Alloy 600Alloy 800Alloy 75Alloy 80AAlloy 9%NiAlloy 6%Mo
UNSN06625N08825N06600N08800N06075N07080K81340S31254
DINNiCr22Mo9NbNiCr21MoNiCr15FeX10 NiCrAlTi32 20NiCr20TiNiCr20TiAlX8 Ni9
W.Nr2.48562.48582.46401.48762.49512.49521.5662
Welding parameters and packaging data
Typical all weld metal composition [wt%]C Mn Si Cr Nb Mo Fe Ni
0.05 0.90 0.60 21.0 3.4 9.5 3.4 Bal.
Re-drying : 2500C/1h
Current
= + ~ (Uo : 70V)
Synthetic basic coated NiCrMo electrodeSuitable for welding alloy 625, alloy 825 orsimilar gradesJoining 9%Ni for high toughness at cryogenictemperaturesExtreme high rsistance to general andintergranular corrosion, pitting, crevice andstess corrosion crackingResistant to high temperature oxidaton andcarburization
Welding position
ASME: 1G 2F 2G 3G
ISO 6947 PA PB PC PF
3/321/8
5/323/16
2.53.254.05.0
14141414
350350350350
90-130120-160150-190190-230
2.74.67.0
10.7
2.0/2.52.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
102
Non Ferrous Electrodes
Z-Ni 112R
Description and Applications: Specifications:AWS/ASME SFA A5. 11 : ENiCrMo-3DIN 1736 : EL-NiCr 20 Mo 9 Nb
Typical all weld metal mechanical properties
Materials to be welded
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]420 760 32 70 J @ -196
0C
ASTMAlloy 625Alloy 825Alloy 600Alloy 800Alloy 75Alloy 80AAlloy 9%NiAlloy 6%Mo
UNSN06625N08825N06600N08800N06075N07080K81340S31254
DINNiCr22Mo9NbNiCr21MoNiCr15FeX10 NiCrAlTi32 20NiCr20TiNiCr20TiAlX8 Ni9
W.Nr2.48562.48582.46401.48762.49512.49521.5662
Welding parameters and packaging data
Typical all weld metal composition [wt%]C Mn Si Cr Nb Mo Fe Ni
0.04 0.70 0.70 20.00 3.30 9.50 3.50 Bal.
Re-drying : 2500C/1h
Current
= + ~ (Uo : 70V)
Synthetic rutile coated NiCrMo electrodeSuitable for welding alloy 625, alloy 825 orsimilar gradesJoining 9%Ni for high toughness at cryogenictemperaturesExtreme high rsistance to general andintergranular corrosion, pitting, crevice andstess corrosion crackingResistant to high temperature oxidaton andcarburization
Welding position
ASME: 1G 2F 2G 3G
ISO 6947 PA PB PC PF
3/321/8
5/323/16
2.53.254.05.0
14141414
350350350350
90-130120-160150-190190-230
4.45.97.38.8
2.0/2.52.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
103
Non Ferrous Electrodes
Z-NiCroMo3
Description and Applications: Specifications:AWS/ASME SFA A5. 11 : ENiCrMo-3DIN 1736 : EL-NiCr 20 Mo 9 Nb
Typical all weld metal mechanical properties
Materials to be welded
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]470 780 37 40 J @ -196
0C
ASTMAlloy 625Alloy 825Alloy 600Alloy 800Alloy 75Alloy 80AAlloy 9%NiAlloy 6%Mo
UNSN06625N08825N06600N08800N06075N07080K81340S31254
DINNiCr22Mo9NbNiCr21MoNiCr15FeX10 NiCrAlTi32 20NiCr20TiNiCr20TiAlX8 Ni9
W.Nr2.48562.48582.46401.48762.49512.49521.5662
Welding parameters and packaging data
Typical all weld metal composition [wt%]C Mn Si Cr Mo Nb Fe Ni
0.03 0.40 0.50 21.50 9.50 3.50 3.00 Bal.
Re-drying : 2500C/1-2h
Current
= +
All position electrode depositing austenitic Ni-base high CrMoNb weldMatching core wireEspecially designed to match th compositionans properties of alloy 625Extremely high resistance to general andintergranular corrosion, pitting and crevicecorrosion and strees corrosion crackingResistant to stress corrosion cracking in sulphuricacid solutions and chloride containingenvironmentsResistant to hot cracking and high temperatureoxidation and carburiztionHigh toughness at cryogenic temperatures
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
3/321/8
5/32
2.53.254.0
101212
250300300
40-7070-10090-140
1.92.93.7
2.02.02.0
12.012.012.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
104
Non Ferrous Electrodes
Z-NiCroMo4
Description and Applications: Specifications:AWS/ASME SFA A5. 11 : ENiCrMo-4DIN 1736 : EL-NiMo 15 Cr 15 W
Typical all weld metal mechanical properties
Materials to be welded
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]560 770 30 50 J @ -196
0C
ASTMAlloy C276Alloy C4Alloy 625Alloy GAlloy G3
UNSN10276N06455N06625N06007N06985
DINNiMo16Cr15WNiMo16Cr15TiNiCr22Mo9NbNiCr22Mo6CuNiCr22Mo7Cu
W.Nr2.48192.46102.48562.46182.4619
Welding parameters and packaging data
Typical all weld metal composition [wt%]C Mn Si Cr Mo W Fe Ni
0.015 0.30 0.10 16.00 16.50 3.50 6.00 Bal.
Re-drying : 2500C/1-2h
Current
= +
All position electrode depositing austenitic Ni-base high CrMoNb weldMatching core wireEspecially designed to match th compositionans properties of alloy C276Extremely high resistance to general andintergranular corrosion, pitting and crevicecorrosion and strees corrosion crackingResistant to stress corrosion cracking in sulphuricacid solutions and chloride containingenvironmentsResistant to hot cracking and high temperatureoxidation and carburiztionHigh toughness at cryogenic temperatures
3/321/8
5/32
2.53.254.0
101212
250300300
40-7070-10090-140
1.92.93.7
2.02.02.0
12.012.012.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
105
Non Ferrous Electrodes
Z-Ni C
Description and Applications: Specifications:AWS/ASME SFA A5. 11 : ENiCrMo-5DIN 1736 : EL-NiMo 15 Cr 15 W mod
Typical all weld metal mechanical properties
Materials to be welded
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]- 720 28 -
ASTMAlloy C276Alloy C4Alloy C625
UNSN10276N06455N06625
DINNi Mo 16Cr 15WNi Mo 16Cr 15TiNi Cr 22Mo 9NbNi Cr 22Mo 6CuNi Cr 22Mo 7Cu
W.Nr2.48192.46102.48562.46182.4619
Welding parameters and packaging data
Typical all weld metal composition [wt%]C Mn Si Cr Mo Fe W Ni
0.04 0.30 0.90 14.50 16.80 4.00 3.70 Bal.
Re-drying : 2500C/1-2h
Basic coated electrode giving a Ni-base weldmetal equivalent in composition of Hastelloy CIdeal for use as build ups in high temperaturesoxidation, corrosion and mechanical stressapplications
Current
= +
Welding position
ASME: 1G 2F 2G 3G
ISO 6947 PA PB PC PF
3/321/8
5/323/16
2.53.254.05.0
14141414
350350350350
70-90100-110130-160160-200
3.66.39.3
14.5
2.0/2.52.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
106
Non Ferrous Electrodes
Z-Ni 190
Description and Applications: Specifications:AWS/ASME SFA A5. 11 : ENiCu-7DIN 1736 : EL-NiCu 30 Mn
Materials to be weldedASTMMonel 400Monel K500
UNSN04400N65500
DIN 17 743NiCu 30 FeLC NiCu 30 FeG Ni Cu 30 NbNiCu30 AlNiCu 14 FeMo
W.Nr2.43602.43612.43652.43752.4400
Welding parameters and packaging data
Typical all weld metal composition [wt%]C Mn Si Cu Ti Fe Ni
0.03 2.60 0.60 33.00 0.30 1.30 Bal.
Re-drying : 3000C/2h
Basic coated Ni-Cu electrode for welding Ni-Cu alloy to mild and low alloy steelsHigh resistance to sea water corrosionExcellent resistance to stress corrosion cracking
Current
= +
Welding position
ASME: 1G 2F 2G 3G
ISO 6947 PA PB PC PF
Typical all weld metal mechanical propertiesRp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]
320 510 35 120 J @ -200C
3/321/8
5/323/16
2.53.254.05.0
14141414
350350350350
70-9090-125
110-160155-185
1.93.24.97.5
2.0/2.52.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
107
Non Ferrous Electrodes
Z-Ni 187
Description and Applications: Specifications:AWS/ASME SFA A5. 6 : ECuNiDIN 1733 : EL-CuNi 30 Mn
Materials to be weldedUNSC71500C71300C70600
DINCuNi 30Mn1FeCuNi 25CuNi 10Fe
W.Nr2.08822.08302.0872
Typical all weld metal composition [wt%]Mn Si Ni Fe Cu1.70 0.70 30.00 0.60 Bal.
Basic coated electrode for welding wrought ironor cast copper nickel alloys (max 30% Ni)Can be used for cladding steelsWeld metal Resistant to Corrosion, erosion andcavitation in sea-water
Typical all weld metal mechanical propertiesRp 0.2 [MPa] Rm [MPa] A5 [%] Hardness
220 370 30 105 HB
Current
= + ~
Welding position
ASME: 1G 2F 2G 4G
ISO 6947 PA PB PC PE
Welding parameters and packaging data
Re-drying : 3000C/1-2h
3/321/8
5/323/16
2.53.254.05.0
14141414
350350350350
50-7575-110
110-145145-185
2.23.45.07.9
2.0/2.52.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
108
Non Ferrous Electrodes
Z-BRONZE A
Description and Applications: Specifications:AWS/ASME SFA A5. 6 : ECuSn-A
Materials to be weldedUNSC50700C51100
DINCuSn2CuSn4
W.Nr2.10102.1016
Typical all weld metal composition [wt%]Sn P Cu5.00 0.30 Bal.
Basic coated electrode for joining phosphor-bronze platesApplicable for electrial conductorsUsed for surfacing bronze, cast steel and copperplates
Typical all weld metal mechanical propertiesRp 0.2 [MPa] Rm [MPa] Hardness
190 250 100 HB
Current= +
Welding parameters and packaging data
Re-drying : 2500C/1-2h
Welding position
ASME: 1G 2F
ISO 6947 PA PB
3/321/8
5/323/16
2.53.254.05.0
14141414
350350350350
40-6570-100
120-160160-200
1.93.14.86.8
2.0/2.52.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
109
Non Ferrous Electrodes
Z-BRONZE
Description and Applications:
Materials to be weldedUNSC50700C51100C51900C52100
DINCuSn2CuSn4CuSn6CuSn8
W.Nr2.10102.10162.10202.1030
Typical all weld metal composition [wt%]Sn P Cu7.80 0.20 Bal.
Basic coated electrode for assembly and surfacingwelds on copper alloysIdeal for surfacing on steel, cast steel and castiron
Typical all weld metal mechanical propertiesRp 0.2 [MPa] Rm [MPa] Hardness
140 300 105 HB
Current= +
Specifications:AWS/ASME SFA A5. 6 : ECuSn-CDIN 1733 : EL-CuSn 7
Welding position
ASME: 1G 2F
ISO 6947 PA PB
Welding parameters and packaging data
Re-drying : 2500C/1-2h
3/321/8
5/323/16
2.53.254.05.0
14141414
350350350350
40-6570-100
120-160160-200
1.93.14.86.8
2.0/2.52.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
110
Non Ferrous Electrodes
Z-BRONZE M
Description and Applications:
Materials to be weldedUNSC50700C51100C51900C52100
DINCuSn2CuSn4CuSn6CuSn8
W.Nr2.10102.10162.10202.1030
Typical all weld metal composition [wt%]Sn P Cu7.10 0.20 Bal.
Basic coated electrode for assembly and surfacingwelds on copper alloysIdeal for surfacing on steel, cast steel and castiron
Typical all weld metal mechanical propertiesRp 0.2 [MPa] Rm [MPa] Hardness
140 300 105 HB
Specifications:AWS/ASME SFA A5. 6 : ECuSn-CDIN 1733 : EL-CuSn 7
Welding position
ASME: 1G 2F
ISO 6947 PA PB
Current
= + ~ (Uo : 70V)
Welding parameters and packaging data
Re-drying : 2500C/1-2h
3/321/8
5/323/16
2.53.254.05.0
14141414
350350350350
40-6570-100
120-160160-200
1.93.35.07.0
2.0/2.52.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
111
Cast Iron & Cutting Electrodes
Z-SuperNi
Description and Applications: Specifications:AWSASME SFA A5. 15 : ENi-ClDIN 8573 : E Ni-BG-21
Typical all weld metal mechanical properties
Materials to be welded
Rp 0.2 [MPa] Rm [MPa] A5 [%] Hardness- 300 5 170HB
Castings, pump bodies, machine bases, engine blocks, gears, cylinders and valvesLamellar grey cast ironMalleable cast ironNodular cast iron
DIN 1691DIN 1692DIN 1693
GG 10 to GG 35GTS 35 10 to GTS 55 4, GTW 35 04 to GTW 45 07, GTW S 38 12GGG 40 to GGG 60
Typical all weld metal composition [wt%]C Si Fe Ni
1.50 3.00 4.00 Bal.
Current
= + ~ (Uo : 50V) _
Special nickel cored electrode for depositingsoft, machinable metal on grey cast ironSuitable for reclamation and repair of grey castiron and for joining these to mild and C-MnsteelsCan be used with low welding currentsWelding both positive direct current and negativeand alternating currents
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Welding parameters and packaging data
Re-drying : 100-1500C/1-2hr
3/321/8
5/323/16
2.53.254.05.0
14141414
350350350350
50-8080-110
110-150150-190
2.03.35.17.4
2.0/2.52.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
112
Cast Iron & Cutting Electrodes
Z-Ni 99
Description and Applications: Specifications:AWSASME SFA A5. 15 : ENi-ClDIN 8573 : E Ni-BG-23
Typical all weld metal mechanical properties
Materials to be welded
Rp 0.2 [MPa] Rm [MPa] A5 [%] Hardness- 300 5 170HB
Castings, pump bodies, machine bases, engine blocks, gears, cylinders and valvesLamellar grey cast ironMalleable cast ironNodular cast iron
DIN 1691DIN 1692DIN 1693
GG 10 to GG 35GTS 35 10 to GTS 55 4, GTW 35 04 to GTW 45 07, GTW S 38 12GGG 40 to GGG 60
Typical all weld metal composition [wt%]C Si Fe Ni
0.80 0.10 4.50 Bal.
Special electrode for depositing soft machinablemetal on grey cast ironExcellent for repairing casting defects in greycast ironCan join cast irons to steels, monels etc.
Welding parameters and packaging data
Re-drying : 1200C/1-2h
Current
= + ~ (Uo : 50V)
Welding position
ASME: 1G 2F 2G 4G
ISO 6947 PA PB PC PE
3/321/8
5/323/16
2.53.254.05.0
14141414
350350350350
50-8080-110
110-150150-190
2.03.45.27.4
2.0/2.52.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
113
Cast Iron & Cutting Electrodes
Z-Ni 99NC
Description and Applications: Specifications:AWS/ASME SFA A5. 15 : ENi-ClDIN 8573 : E Ni-BG-23
Typical all weld metal mechanical properties
Materials to be welded
Rp 0.2 [MPa] Rm [MPa] A5 [%] Hardness- 300 5 170HB
Castings, pump bodies, machine bases, engine blocks, gears, cylinders and valvesLamellar grey cast ironMalleable cast ironNodular cast iron
DIN 1691DIN 1692DIN 1693
GG 10 to GG 35GTS 35 10 to GTS 55 4, GTW 35 04 to GTW 45 07, GTW S 38 12GGG 40 to GGG 60
Typical all weld metal composition [wt%]C Si Fe Ni
0.75 0.20 5.30 Bal.
Electrode for welding cast iron or malleable castironNon conductive coatingMachinable weld deposit
Current
= + ~ (Uo : 50V)
Welding position
ASME: 1G 2F 2G 4G
ISO 6947 PA PB PC PE
Welding parameters and packaging data
Re-drying : 1200C/1hr
3/321/8
5/32
2.53.254.0
141414
350350350
60-9090-110
110-170
2.13.35.2
2.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
114
Cast Iron & Cutting Electrodes
Z-Ni 55
Description and Applications: Specifications:AWS A5. 15 : E NiFe-ClDIN 8573 : E NiFe-1-BG-23
Typical all weld metal mechanical properties
Materials to be welded
Rp 0.2 [MPa] Rm [MPa] A5 [%] Hardness- 450 10 200HB
Castings, pump bodies, machine bases, engine blocks, gears, cylinders and valvesLamellar grey cast ironMalleable cast ironNodular cast iron
DIN 1691DIN 1692DIN 1693
GG 10 to GG 35GTS 35 10 to GTS 55 4, GTW 35 04 to GTW 45 07, GTW S 38 12GGG 40 to GGG 60
Typical all weld metal composition [wt%]C Ni Fe
1.20 55.0 Bal.
Basic coated electrode which deposits a machinablenickel iron alloy weldDesigned for strength welding of high duty castiron such as mechanite, malleable and spheroidalgraphite and nodular ironsWelds high phosphorus castingsTypical components to be welded are machinebases, pump bodies, engine blocks, gears andtransmission housings
Current
= + ~ (Uo : 50V)
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Welding parameters and packaging data
Re-drying : 100-1500C/1-2hr
3/321/8
5/323/16
2.53.254.05.0
14141414
350350350350
50-8080-110
110-150150-190
2.03.35.17.4
2.0/2.52.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
115
Cast Iron & Cutting Electrodes
Z-GSM
Description and Applications: Specifications:DIN 8573 : E FeC-G-BG-26
Typical all weld metal mechanical properties
Materials to be welded
Rp 0.2 [MPa] Rm [MPa] A5 [%] Hardness- 520 10 200HB
Malleable cast ironNodular cast iron
DIN 1692DIN 1693
GTS 35, GTS 45GGG 40 to GGG 50
Basic coated electrode for hot welding of nodularcast ironSuitable for welding malleable black and greycast ironNon machinable weld deposit
Current
= + ~ (Uo : 70V)
Welding parameters and packaging data
Re-drying : 3000C/2h
Welding position
ASME: 1G 2F 2G 3G
ISO 6947 PA PB PC PF
Typical all weld metal composition [wt%]C Si Fe Mn Ni
1.00 0.80 3.60 1.30 Bal.
3/321/8
5/32
2.53.254.0
141414
350350350
60-9090-120
130-180
1.72.74.1
5.05.05.0
15.015.015.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
116
Cast Iron & Cutting Electrodes
Z-GM
Description and Applications: Specifications:AWS/ASME SFA A5. 15 : ENiCu-BDIN 8573 : E NiCu-BG-23
Typical all weld metal mechanical properties
Materials to be welded
Rp 0.2 [MPa] Rm [MPa] A5 [%] Hardness- 400 8 150HB
Lamellar grey cast ironMalleable cast ironNodular cast iron
DIN 1691DIN 1692DIN 1693
GG 10GTS 35GGG 40
Typical all weld metal composition [wt%]C Fe Cu Ni
0.40 2.60 33.00 Bal.
Monel type core wired electrode for weldinglamellar grey, nodular and malleable cast ironSuitable also for welding of cast iron to mildsteelMachinable weld deposit
Welding parameters and packaging data
Re-drying : 1200C/1-2h
Current
= + ~ (Uo : 50V)
Welding position
ASME: 1G 2F 2G 3G
ISO 6947 PA PB PC PF
3/321/8
5/323/16
2.53.254.05.0
14141414
350350350350
50-8080-110
110-150150-190
1.83.24.97.4
2.0/2.52.0/2.52.0/2.52.0/2.5
12.0/15.012.0/15.012.0/15.012.0/15.0
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
117
Cast Iron & Cutting Electrodes
Z-71
Description and Applications:
Working position Current
Electrode for scrapping and gougingUsable in all positions on mild and low alloysteels, stainless steels, cast iron, nickel basedalloys and aluminium alloys
Welding parameters and packaging data
All welding positions
3/321/8
5/323/161/4
2.53.254.05.06.0
1414141414
350350350350350
120 Min170 Min190 Mn275 Min350 Min
1.93.34.97.79.8
3.53.53.53.53.5
10.510.510.510.510.5
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
= + ~ (Uo : 50V)
118
Cast Iron & Cutting Electrodes
Z-72
Description and Applications:
Working position Current
Electrode for cutting and piercingUsable in all positions on mild and low alloysteels, stainless steels, cast iron, nickel basedalloys and aluminium alloys
Welding parameters and packaging data
All welding positions= + ~ (Uo : 50V)
3/321/8
5/323/16
2.53.254.05.0
14141414
350350350350
120 Min170 Min190 Min 275 Min
1.63.75.47.8
4.54.54.54.5
13.513.513.513.5
Diain mm
Lengthin mm
Current[amps]
Weightkg/100 pcs
Weight packet[kg]
Weight carton[kg]
119
Cast Iron & Cutting Electrodes
Z-OXYCUT
Description and Applications:
Working position Current
Flux coated tubular electrode for cutting anymaterial by means of oxygen pressure
Welding parameters and packaging data
All welding positions = +
3/169/32
5.07.0
1818/39.3
450450/1000
200-250250-300
Diain mm
Lengthin mm
Current[amps]
120
Flux Cored Wire
Z-71T1
Description and Applications:
Approvals
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
AWS/ASME SFA A5.20 : E71T-1Specifications:
C Mn Si0.06 1.45 0.45
Rutile Flux cored wire suitable for all-positionalweldingStable and penetrative arc with little spatterformationHigh impact toughness at sub-zero temperatures
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V] Heat Treatment540 580 26 110 J @ -20oC U
Non alloyed sturctural steelsBoiler platesPipe steels
DIN 17 100DIN 17 155DIN 1626/1629DIN 1628/1630DIN 17 175DIN 17 172DIN 17 172API 5LX
St 33, St 37.2, St 44.2, St 52.3Hl, Hll, 17 Mn 4St 37.0 to St 52.0St 37.4 to St 52.4St 35.8, St 45.8St E 210.7 to St E 415.7St E 290.7 TM to St E 480.7 TMX42 to X46St E 255 to St E 460A, B, D, E
Fine grained structural steelsShipbuilding steels
ABS3YSH5
Shielding gas: CO2
LR3YSH5
= +
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Packaging data
0.0450.063
1.21.6
15 .015.0
Diain mm
Weight/reel 300 DOutside Dia
121
Flux Cored Wire
Z-71T5
Description and Applications:
Approvals
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
AWS/ASME SFA A5.20 : E71T-5Specifications:
C Mn Si0.06 1.30 0.38
Low hydrogen basic flux cored wire suitable forall-positional weldingStable and penetrative arc with little spatterformationExtra high impact toughness at sub-zerotemperatures
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V] Heat Treatment480 550 27 100 J @ -30oC U
Non alloyed sturctural steelsBoiler platesPipe steels
DIN 17 100DIN 17 155DIN 1626/1629
DIN 17 102
St 33, St 37, St 44, St 52, St 50, St 60, St 70Hl, Hll, 17 Mn 4, 19 Mn 5St 37.0, St 37.4, St 44.0, St 44.4 St 52.0, St 52.4, St 35.8, St45.8, St E 210.7, ST E 240.7, St E 290.7, St E 320.7, St E 360.7including thermo-mechanical gradesSt E 255 to St E 355, W St E 255 to W St E 355,T St E 255 to T St E 255A, B, D, EGS 38, GS 52, GS 60
Fine grained structural steels
Shielding gas: CO2
LR3YSH5
= +
Packaging data
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
Shipbuilding steelsCast steels
0.0450.063
1.21.6
15 .015.0
Diain mm
Weight/reel 300 DOutside Dia
122
S MI AUTOMATIC SOLID WIRE
Z-R2
Description and Applications:
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
AWS/ASME SFA A5.18 : ER-70S-2 EN 440 : G2 Ti
Specifications:Double de-oxide mild steel mig solid wire for welding of unalloyed steels and fine grained C-Mn steels Capable of producing high quality welds where the steel is rusty
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V] Heat Treatment440 520 28 100 J @ -30oC U
Unalloyed construction steels Boiler plates Pipe steels Shipbuilding steels
DIN 17 100 DIN 17 155 DIN 1629
St 33 to St52.3 Hl, Hll , 17 Mn 4 St35 to St52.4 A, B, D, E
Shielding gas: Argon CO2 (M21)
= +
Packaging data
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
C Mn Si Ti Zr Al0.06 1.10 0.50 0.10 0.09 0.10
0.0240.0300.0350.0390.0450.063
0.60.80.91.01.21.6
15 Kgs15 Kgs15 Kgs15 Kgs15 Kgs15 Kgs
5Kgs 5Kgs 5Kgs 5Kgs 5Kgs5Kgs
Dia in mm
Weight/reel 300 D Outside Dia
Weight/reel 200 D Outside Dia
123
Z-R3
Description and Applications:
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
AWS/ASME SFA A5.18 : ER-70S-3DIN 8575 : SG 1 EN 440 : G2 Si
Specifications:Double de-oxide mild steel mig solid wire forwelding of unalloyed steels and fine grainedC-Mn steels
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V] Heat Treatment420 530 28 130 J @ -20oC U
Unalloyed construction steelsBoiler plates Pipe steels
Shipbuilding steels
DIN 17 100DIN 17 155DIN 17 172DIN 1629
St 33 to St52.3 Hl, Hll , 17 Mn 4 StE 210.7 to StE 310.7St35 to St52.4 A, B, D, E
Shielding gas: Argon CO2 (M21)
= +
Packaging data
C Mn Si0.07 1.20 0.60
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
0.0240.0300.0350.0390.0450.063
0.60.80.91.01.21.6
15 Kgs15 Kgs15 Kgs15 Kgs15 Kgs15 Kgs
5Kgs5Kgs5Kgs5Kgs5Kgs5Kgs
Diain mm
Weight/reel 300 DOutside Dia
Weight/reel 200 DOutside Dia
S MI AUTOMATIC SOLID WIRE
124
Z-R6
Description and Applications:
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
AWS/ASME SFA A5.18 : ER-70S-6DIN 8559 : SG 2 BS 2901 : A18 EN 440 : G3 Si 1 mod
Specifications:Double de-oxide mild steel mig solid wire forwelding of unalloyed steels and fine grained C-Mn steels Produces a quality weld with excellent radiographicand mechanical properties
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V] Heat Treatment480 580 27 60 J @ -30oC U
Unalloyed construction steelsBoiler plates Pipe steels
Shipbuilding steels
DIN 17 100DIN 17 155DIN 17 172DIN 1629
St 33 to St52.3 Hl, Hll , 17 Mn 4 StE 210.7 to StE 360.7St35 to St52.4 A, B, D, E
Shielding gas: Argon CO2 (M21)
Packaging data
C Mn Si0.08 1.50 0.90
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
ApprovalsLR
3YSH15
0.0240.0300.0350.0390.0450.063
0.60.80.91.01.21.6
15 Kgs15 Kgs15 Kgs15 Kgs15 Kgs15 Kgs
5Kgs5Kgs5Kgs5Kgs5Kgs5Kgs
Diain mm
Weight/reel 300 DOutside Dia
Weight/reel 200 DOutside Dia
S MI AUTOMATIC SOLID WIRE
125
Z-RMo
Description and Applications:
Current
Typical all weld metal composition [wt%]
Typical all weld metal mechanical properties
Materials to be welded
Specifications:Molybdenum mild steel wire Recommended for welding mild steels or 0.5% Moalloyed steels for high temperatures serviceIdeal for avoiding porosity and cracks
Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V] Heat Treatment500 620 25 80 J @ -30oC U
Cast ironBoiler plate
DIN 17 245DIN 17 155
GS 22 Mo 415 Mo 4
Shielding gas: Argon CO2 (M21)
= +
Packaging data
C Mn Si Mo0.08 1.90 0.70 0.50
AWS/ASME SFA A5.28 : ER-80S-D2DIN 8559 : SG Mo BS 2901 : A 30/A31 EN 440 : G4 Mo
Welding position
ASME: 1G 2F 2G 3G 4G
ISO 6947 PA PB PC PF PE
0.0300.0350.0390.0450.063
0.80.91.01.21.6
15 Kgs15 Kgs15 Kgs15 Kgs15 Kgs
10.510.510.510.510.5
Diain mm
Weight/reel 300 DOutside Dia
Weight/reel 200 DOutside Dia
S MI AUTOMATIC SOLID WIRE