covered electrodes - kiswel · pdf filecovered electrodes classifications welding positions...

Covered ElectrodesFOR CARBON STEEL

FOR HIGH TENSILE STRENGTH STEEL

FOR ATMOSPHERIC CORROSION RESISTING STEEL

FOR LOW TEMPERATURE SERVICE STEEL

FOR HEAT-RESISTING STEEL

FOR HARDFACING

FOR STAINLESS STEEL

FOR CAST IRON

FOR SPECIAL PURPOSE

39

KCL-10For 420MPa mild steel

Covered Electrodes

Classifications

Description

Welding positions

Typical chemical composition of all-weld metal (%)

Typical mechanical properties of all-weld metal

Sizes available and recommended currents (DC +)

Approvals

Covering is high cellulose type for welding of pipe, shipbuildings, tanks or galvanized surfaces and steelcasting repairs. Good penetration combined with freedom from lack of fusion makes this electrode an excellent choice for pipe welding. Gives high ductility root weld and easy slag removal.Redry the electrode at 70~80℃ for 30~60 minutes prior to use.

Others : JIS, CE

AW : As-Welded

AWS A5.1EN ISO 2560-AExample

ABS

3,E6010

BV

3

GL

3

LR

3m

NK

KMW3

C0.11

Si0.36

Mn0.63

P0.015

S0.013

Ni0.02

Cr0.03

Mo0.01

V0.01

Y.S(MPa)

min. 330min. 380

420

T.S(MPa)

min. 430470~600

500

El.(%)

min. 22min. 20

29

IV (J)0℃ -30℃

≥ 27≥ 47

60 40

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

50~8040~70

3.2350

70~11060~100

4.0350

110~15090~130

5.0350

160~200140~170

EN ISO 2560-A:2006 : E 38 0 C 22EN ISO 2560-B:2006 : E 43 10 AAWS A5.1-04 : E6010

KS D 7004 : E4311JIS Z 3211 : E4310

KCL-11For 420MPa mild steel

Covered Electrodes

Classifications

Description

Welding positions



Sizes available and recommended currents (AC or DC +)

Approvals

Others : JIS, CE

Covering is high cellulose type for welding of steel sheets, pipes in building or shipbuilding. As the welding in poor groove fit up and vertical-down welding can be performed easily, it is used in all position welding of pipes.Good mechanical properties and the weld metal neets requirement X-ray.Gives high ductility root weld and easy slag removal.Redry the electrode at 70~80℃ for 30~60 minutes prior to use.


ABS

3,E6011

BV

3

GL

3

LR

3m

C0.08

Si0.31

Mn0.58

P0.017

S0.018

Ni0.02

Cr0.03

Mo0.01

V0.01

Y.S(MPa)

min. 330min. 380

410

T.S(MPa)

min. 430470~600

500

El.(%)

min. 22min. 20

24

IV (J)-20℃ -30℃

≥ 27≥ 47

60 40

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

50~8040~70

3.2350

70~11060~100

4.0350

110~15090~130

5.0350

160~200140~170

EN ISO 2560-A:2006 : E 38 2 C 12EN ISO 2560-B:2006 : E 43 10 AAWS A5.1-04 : E6011

KS D 7004 : E4311JIS Z 3211 : E4311

AW : As-Welded

40

41

AW : As-Welded

K-6012For 420MPa mild steel

Covered Electrodes

Classifications

Description

Welding positions



Sizes available and recommended currents (AC or DC -)

Approvals

Covering is high titania type for welding of shells of railway vehicles, cars and othersteel structuresand general light structural steels.Good weldability in vertical-down welding.Excellent X-ray quslity and good bead appearance.Redry the electrode at 70~100℃ for 30~60 minutes prior to use.

JIS, CE


C0.07

Si0.39

Mn0.52

P0.020

S0.011

Ni0.02

Cr0.03

Mo0.01

V0.01

Y.S(MPa)

min. 330min. 380

400

T.S(MPa)

min. 430470~600

490

El.(%)

min. 17min. 20

30

IV (J)RT 0℃

≥ 27≥ 47

60 40

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

50~9540~95

3.2350

80~12070~110

4.0400

130~170100~140

5.0400

180~230120~160

6.0450

240~300

EN ISO 2560-A:2006 : E 38 0 R 12EN ISO 2560-B:2006 : E 43 12 AAWS A5.1-04 : E6012

KS D 7004 : E4313JIS Z 3211 : E4312

KR-3000For 420MPa mild steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Others : KS, JIS, CE

Covering is high titania type for welding of all kinds of light constructional work in all positions, including pipe welding. Excellent striking and restriking properties. Excellent slag removal and bead appearance without undcut.Redry the electrode at 70~100℃ for 30~60 minutes prior to use.


ABS

2

BV

2

DNV

2

GL

2

KR

2

LR

2m

NK

KMW2

C0.06

Si0.35

Mn0.40

P0.020

S0.011

Ni0.02

Cr0.03

Mo0.01

V0.01

Y.S(MPa)

min. 330min. 380

430

T.S(MPa)

min. 430470~600

490

El.(%)

min. 17min. 20

28

IV (J)RT 0℃

≥ 27≥ 47

75 60

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~10060~90

3.2350

80~13080~110

4.0400

130~18090~140

5.0400

160~220120~190

6.0450

210~280

EN ISO 2560-A:2006 : E 38 0 R 11EN ISO 2560-B:2006 : E 43 13 AAWS A5.1-04 : E6013

KS D 7004 : E4313JIS Z 3211 : E4313

AW : As-Welded

42

43

AW : As-Welded

KR-3000VFor 420MPa mild steel

Covered Electrodes

Classifications

Welding positions




Approvals



ABS

2

BV

2

LR

2m

C0.09

Si0.38

Mn0.49

P0.020

S0.013

Ni0.02

Cr0.03

Mo0.01

V0.01

Y.S(MPa)

min. 330min. 380

420

T.S(MPa)

min. 430470~600

490

El.(%)

min. 17min. 20

29

IV (J)RT 0℃

≥ 27≥ 47

65 50

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

V-down

2.6350

80~120

3.2350

100~150

4.0400

150~200

5.0400

210~250

EN ISO 2560-A:2006 : E 38 0 R 15EN ISO 2560-B:2006 : E 43 13 A AWS A5.1-04 : E6013

KS D 7004 : E4313JIS Z 3211 : E4313

DescriptionWelding of shells of railway vehicles, cars and other steel sheet structures and general light structural steels.In vertical-down welding, excellent bead appearance can be obtained by taking a little bit higher welding amperage and holding the electrode at the illustrated angles.Welding under excessive amperage conditions can cause the deterioration of radiographic soundness.Redry the electrode at 70~100℃ for 30~60 minutes prior to use.

60~80°

45°

KI-101LFFor 420MPa mild steel

Covered Electrodes

Classifications

Description

Welding positions



Sizes available and recommended currents (AC or DC +, -)

Approvals


Covering is ilmenite type for welding of high pressure boilers, ship hulls, building, bridges and other structural fabrications.The most excellent mechanical properties and also suitable for welding of structural steels of heavy section about 25mm thickness. Redry the electrode at 70~100℃ for 30~60 minutes prior to use.


ABS

3

BV

3

DNV

3

GL

3

KR

3

LR

3m

NK

KMW3

C0.07

Si0.15

Mn0.47

P0.020

S0.012

Ni0.01

Cr0.02

Mo0.01

V0.01

Y.S(MPa)

min. 330min. 380

400

T.S(MPa)

min. 430470~600

490

El.(%)

min. 22min. 20

30

IV (J)0℃ -20℃

≥ 27≥ 47

100 80

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~9050~75

3.2350

80~13560~120

4.0400

135~190100~160

5.0400

180~240135~210

6.0450

250~310-

EN ISO 2560-A:2006 : E 38 2 RA 12 EN ISO 2560-B:2006 : E 43 19 A U AWS A5.1-04 : E6019

KS D 7004 : E4301JIS Z 3211 : E4319

AW : As-Welded

44

45

AW : As-Welded

K-6022For 420MPa mild steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is high iron oxide type for welding of flat and horizontal fillet welding of sheet metal.Highly efficient welding.Welding under excessive amperage conditions can cause the deterioration of radiographic soundness.Redry the electrode at 70~100℃ for 30~60 minutes prior to use.

JIS, CE


C0.14

Si0.28

Mn1.20

P0.025

S0.012

Ni0.02

Cr0.03

Mo0.01

V0.01

Y.S(MPa)

min. 330min. 380

450

T.S(MPa)

min. 430470~600

480

El.(%)

min. 17min. 20

26

IV (J)RT 0℃

≥ 27≥ 47

75 55

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~110

3.2350

80~140

4.0400

160~200

5.0400

180~240

6.0450

260~320

EN ISO 2560-A:2006 : E 38 0 A 23AWS A5.1-04 : E6022

46

KF-300LFFor 420MPa mild steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals


Covering is high iron oxide, iron powder type for welding of flat and horizontal fillet welding of ship hull constructions, bridges and general structures. Beautiful bead appearance with undercut.Extremely high efficient welding because of high deposition rate by much iron powder.Easy slag removal.Redry the electrode at 120~150℃ for 30~60 minutes prior to use.


ABS

3

BV

3

DNV

3

GL

3

KR

3

LR

3m

NK

KMW3

C0.07

Si0.47

Mn0.76

P0.020

S0.014

Ni0.02

Cr0.03

Mo0.01

V0.01

Y.S(MPa)

min. 330min. 380

490

T.S(MPa)

min. 430470~600

560

El.(%)

min. 22min. 20

28

IV (J)0℃ -30℃

≥ 27≥ 47

60 40

Remarks

AW

Dia.Length

Amp.(A)Leg

(mm)(mm)

FH-Fillet(mm)

4.0550

150~180

5.0~5.5

4.5550700

180~200

5.5~6.0

5.0550700

180~230

6.0~6.5

5.5550700

220~270

6.5~7.0

6.0550700

250~290

7.0~8.0

6.4550700

280~310

7.5~8.5

EN ISO 2560-A:2006 : E 38 0 A 53EN ISO 2560-B:2006 : E 43 27 A AWS A5.1-04 : E6027

KS D 7004 : E4327JIS Z 3211 : E4327

AW : As-Welded

KT-303For 420MPa mild steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is lime titania type for welding of cars, other vehicles, light structural steels and pedestrian bridges.High welding efficiency and restriking property.Suitable for tack welding and intermittent welding.Excellent slag removal. Redry the electrode at 70~100℃ for 30~60 minutes prior to use.


JIS Z 3211EN ISO 2560-AExample

ABS

3,D4303

DNV

3

GL

3

KR

3

LR

3m

NK

KMW3

C0.06

Si0.24

Mn0.40

P0.017

S0.016

Ni0.01

Cr0.02

Mo0.01

V0.01

Y.S(MPa)

min. 330min. 380

420

T.S(MPa)

min. 430470~600

530

El.(%)

min. 20min. 20

32

IV (J)0℃ -20℃

≥ 27≥ 47100 60

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

65~10050~90

3.2350

100~14080~130

4.0400

140~190110~170

5.0400

200~260140~210

6.0450

250~330-

EN ISO 2560-A:2006 : E 38 0 RB 12 EN ISO 2560-B:2006 : E 43 03 A U

KS D 7004 : E4303JIS Z 3211 : E4303

AW : As-Welded

47

KH-500LFFor 490MPa high tensile steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals


Covering is low hydrogen type for welding of strength members of ship hulls and general heavy structural steels, medium carbon steel, high sulphur steel. Underlaying of hardfacing.Excellent mechanical properties and radiographic soundness.Excellent crack resistance even in the welding of difficult to weld steels.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


ABS

3YH10

BV

3YHH

DNV

3YH10

GL

3YH10

KR

3YH15

LR

3YmH15

NK

KMW3H

C0.07

Si0.46

Mn*0.96

P0.015

S0.011

Ni*0.02

Cr*0.03

Mo*0.01

V*0.01

*Sum1.03

Y.S(MPa)

min. 330min. 380

460

T.S(MPa)

min. 430470~600

540

El.(%)

min. 20min. 20

28

IV (J)-20℃ -30℃

≥ 27≥ 47

120 100

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~9050~80

3.2350

90~13080~110

4.0400

140~190120~160

5.0400

180~240160~200

6.0450

250~300-

EN ISO 2560-A:2006 : E 38 3 B 12 H10EN ISO 2560-B:2006 : E 43 16 A U H10AWS A5.1-04 : E7016

KS D 7006 : E4316JIS Z 3211 : E4316

AW : As-Welded

48

49

AW : As-Welded

KH-500TFor 490MPa high tensile steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen type for tack welding of steels of ships, buildings and bridges.Good arc restriking properties.Designed for tack welding and intermittent welding.Easy slag removal.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

KS, JIS, CE


C0.07

Si0.59

Mn*0.86

P0.018

S0.009

Ni*0.02

Cr*0.03

Mo*0.01

V*0.01

*Sum0.93

Y.S(MPa)

min. 330min. 380

450

T.S(MPa)

min. 430470~600

550

El.(%)

min. 20min. 20

29

IV (J)0℃ -30℃

≥ 27≥ 47

65 50

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

All

2.6350

90~150

4.0400

140~200

5.0400

190~240

EN ISO 2560-A:2006 : E 38 0 B 12 H10EN ISO 2560-B:2006 : E 43 16 A H10AWS A5.1-04 : E7016

KS D 7006 : E4316JIS Z 3211 : E4316

50

AW : As-Welded

KH-500WFor 490MPa high tensile steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals

KS, JIS, CE

Specifically designed for one side welding of pipes and general structures.Covering is low hydrogen type for welding of all positions except vertical-down.Extremely good usability in flat positions.Easy slag removal and beautiful bead appearance.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


C0.09

Si0.58

Mn*0.98

P0.014

S0.011

Ni*0.02

Cr*0.03

Mo*0.01

V*0.01

*Sum1.05

Y.S(MPa)

min. 330min. 380

460

T.S(MPa)

min. 430470~600

560

El.(%)

min. 20min. 20

32

IV (J)0℃ -30℃

≥ 27≥ 47

70 50

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

F OSW

2.6350

30~70

3.2350

60~110

4.0400

90~140

4.5400

120~160

5.0400

130~180


KS D 7006 : E4316JIS Z 3211 : E4316

51

AW : As-Welded

KH-500VLFFor 490MPa high tensile steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen type for vertical-down welding of general structures and strength members of machinery, ship construction, bridges.In vertical-down welding, excellent bead appearance can be obtained by taking a little bit higher welding amperage and holding the electrode at the illustrated angles.Excellent mechanical properties and crack resistance.Redry the electrode at 300~400℃ for 1~2 hours prior to use.



ABS

3YH10

BV

3YHH

DNV

3YH10

KR

3YH15

LR

3YmH15

NK

KMW3H

C0.06

Si0.53

Mn*0.72

P0.012

S0.011

Ni*0.02

Cr*0.03

Mo*0.01

V*0.01

*Sum0.79

Y.S(MPa)

min. 330min. 380

460

T.S(MPa)

min. 430470~600

550

El.(%)

min. 20min. 20

33

IV (J)0℃ -30℃

≥ 27≥ 47

70 60

Remarks

AW


KS D 7006 : E4316JIS Z 3211 : E4948

Dia.Length

Amp.(A)

(mm)(mm)

V-down

3.2400

120~160

4.0450

150~210

4.5450

180~240

5.0450

220~280

5.5450

260~330

60~80°

45°

K-7014For 490MPa high tensile steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Others : JIS, CWB, CE

Covering is iron powder, titania type for fillet welding of ship structure, bridges, structural steels.Designed for high efficiency in single pass and multiple pass welding.Excellent slag removal and good bead appearance.Quiet and stable arc.Redry the electrode at 120~150℃ for 30~60 minutes prior to use.


ABS

2Y,E7014

KR

2Y

LR

2Ym

NK

KMW52

C0.08

Si0.41

Mn*0.73

P0.020

S0.014

Ni*0.02

Cr*0.03

Mo*0.01

V*0.01

*Sum0.80

Y.S(MPa)

min. 400min. 420

470

T.S(MPa)

min. 490500~640

550

El.(%)

min. 17min. 20

30

IV (J)RT 0℃

≥ 27≥ 47

65 50

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~10050~90

3.2350

90~14080~130

4.0400

140~200110~170

5.0400

190~240150~200

6.0450

250~310-

EN ISO 2560-A:2006 : E 42 A RR 32EN ISO 2560-B:2006 : E 49 14 A AWS A5.1-04 : E7014

JIS Z 3211 : E4914

AW : As-Welded

52

53


Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is iron powder, titania type for flat and horizontal fillet welding of ship structure, bridges, structural steels for buildings and general structures.Designed for high efficiency in single pass.Excellent slag removal and good bead appearance.Redry the electrode at 120~150℃ for 30~60 minutes prior to use.



ABS

2Y,E7024

BV

2Y

DNV

3

GL

2Y

KR

2Y

LR

2Ym

NK

KMW52

C0.08

Si0.35

Mn*0.78

P0.020

S0.014

Ni*0.02

Cr*0.03

Mo*0.01

V*0.01

*Sum0.85

Y.S(MPa)

min. 400min. 420

480

T.S(MPa)

min. 490500~640

570

El.(%)

min. 17min. 20

28

IV (J)RT 0℃

≥ 27≥ 47

65 50

Remarks

AW

Dia.

Length

Amp.(A)

(mm)

(mm)

FH-Fillet

3.2400

100~150

4.0450550

140~190

4.5450550700

180~230

5.0450550700

200~250

5.5450550700

230~270

6.0450550700

260~300

EN ISO 2560-A:2006 : E 42 A RR 53EN ISO 2560-B:2006 : E 49 24 A AWS A5.1-04 : E7024

KS D 7004 : E4324JIS Z 3211 : E4924

AW : As-Welded

54

AW : As-Welded

K-7024NFor 490MPa high tensile steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals

JIS, CE


C0.08

Si0.63

Mn*0.88

P0.024

S0.020

Ni*0.15

Cr*0.03

Mo*0.01

V*0.01

*Sum1.08

Y.S(MPa)

min. 400min. 420

500

T.S(MPa)

min. 490500~640

590

El.(%)

min. 17min. 20

27

IV (J)0 -20℃

≥ 27≥ 47

60 40

Remarks

AW

EN ISO 2560-A:2006 : E 42 0 RR 53EN ISO 2560-B:2006 : E 49 24 A AWS A5.1-04 : E7024-1

KS D 7004 : E4324JIS Z 3211 : E4924-1

Dia.

Length

Amp.(A)

(mm)

(mm)

FH-Fillet

3.2400

100~150

4.0450550

140~190

4.5450550700

180~230

5.0450550700

200~250

5.5450550700

230~270

6.0450550700

260~300

Covering is iron powder, titania type for flat and horizontal fillet welding of ship structure, bridges, structural steels for buildings and general structures.Designed for high efficiency in single pass.Good notch toughness of the deposited weld metal.Excellent slag removal and good bead appearance.Redry the electrode at 120~150℃ for 30~60 minutes prior to use.

55

AW : As-Welded

K-7010GFor 490MPa high tensile steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is high cellulose type for all positions welding of pipes, general light structural steels.This electrode is characterized by deeply penetrating, forceful, spray type arc.Readily removable, thin friable slag.Good mechanical properties and the weld metal neets requirement X-ray.Redry the electrode at 70~80℃ for 30~60 minutes prior to use.

JIS, CE


C

0.10

Si

0.56

Mn

0.87

P

0.014

S

0.013

Ni

0.34

Cr

0.03

Mo

0.28

V

0.01

Y.S(MPa)

min. 390min. 420

470

T.S(MPa)

min. 490500~640

570

El.(%)

min. 22min. 20

27

IV (J)0℃ -30℃

≥ 27≥ 47

60 40

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6300

50~8040~70

3.2350

70~11060~100

4.0400

110~15090~130

5.0400

160~200140~170

EN ISO 2560-A:2006 : E 42 0 C 22EN ISO 2560-B:2006 : E 49 10-G AAWS A5.5-06 : E7010-G

JIS Z 3211 : E4910-G

KK-50LFFor 490MPa high tensile steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals


Covering is low hydrogen type for welding of 490MPa class high tensile steel in ships, bridges.Excellent mechanical properties and radiographic soundness.Excellent crack resistance even in the welding of difficult to weld steels.Satisfactory bead appearance and slag removal.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


ABS

3YH10

BV

3YHH

DNV

3YH10

GL

3YH10

KR

3YH15

LR

3YmH15

NK

KMW53H

C0.07

Si0.53

Mn*0.93

P0.013

S0.012

Ni*0.02

Cr*0.03

Mo*0.01

V*0.01

*Sum1.00

Y.S(MPa)

min. 400min. 420

480

T.S(MPa)

min. 490500~640

560

El.(%)

min. 22min. 20

32

IV (J)-20℃ -30℃

≥ 27≥ 47

110 80

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~9050~80

3.2350

90~13080~110

4.0400

140~190120~160

5.0400

180~240160~200

6.0450

250~310-


KS D 7006 : E5016JIS Z 3211 : E4916

AW : As-Welded

56

K-7016HRFor 490MPa high tensile steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen type for welding of 490MPa class high tensile steel in ships, bridges.Excellent mechanical properties and radiographic soundness.Good impact properties and very low hydrogen contens. (HD ≤4ml/100g)Satisfactory bead appearance and slag removal.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

Others : JIS, CCS, CE


ABS

3YH5

BV

3YHHH

DNV

3YH5

GL

3YH5

KR

3YH5

LR

3YmH5

NK

KMW53H5

C0.07

Si0.57

Mn*0.87

P0.013

S0.011

Ni*0.02

Cr*0.03

Mo*0.01

V*0.01

*Sum0.94

Y.S(MPa)

min. 400min. 420

500

T.S(MPa)

min. 490500~640

610

El.(%)

min. 22min. 20

27

IV (J)-20℃ -30℃

≥ 27≥ 47

110 90

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~9050~80

3.2350

90~13080~110

4.0400

140~190120~160

5.0400

180~240160~200

6.0450

250~310

EN ISO 2560-A:2006 : E 42 3 B 12 H5EN ISO 2560-B:2006 : E 49 16 A U H5 AWS A5.1-04 : E7016 H4R

KS D 7006 : E5016JIS Z 3211 : E4916 H5

AW : As-Welded

57


Covered Electrodes

Classifications

Description

Welding positions




Approvals

Others : KS, JIS, CWB, CE

Covering is low hydrogen, iron powder type for welding of 490MPa class high tensile steel in ships, bridges, storage tank, building and industrial machinery.Excellent mechanical properties and radiographic soundness.Satisfactory bead appearance and slag removal. Redry the electrode at 300~400℃ for 1~2 hours prior to use.


BV

3YHH

DNV

3YH10

GL

3YH10

KR

3YH15

LR

3YmH15

NK

KMW53H

ABS

3YH10,E7018

C0.07

Si0.61

Mn*0.87

P0.015

S0.011

Ni*0.02

Cr*0.03

Mo*0.01

V*0.01

*Sum0.94

Y.S(MPa)

min. 400min. 420

480

T.S(MPa)

min. 490500~640

570

El.(%)

min. 22min. 20

30

IV (J)-20℃ -30℃

≥ 27≥ 47

100 70

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~10050~80

3.2350

90~13080~120

4.0400

130~180110~170

5.0400

200~250160~210

6.0450

250~310-


KS D 7006 : E5016JIS Z 3211 : E4918

AW : As-Welded

58

K-7018HRFor 490MPa high tensile steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen, iron powder type for welding of 490MPa class high tensile steel in ships,bridges, storage tank, building and industrial machinery.Good impact properties and very low hydrogen contens. (HD ≤4ml/100g)Excellent bead appearance and radiographic soundness.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

Others : JIS, CCS, CE


ABS

3YH5

BV

3YHHH

DNV

3YH5

GL

3YH5

KR

3YH5

LR

3YmH5

NK

KMW53H5

C0.07

Si0.60

Mn*0.98

P0.015

S0.012

Ni*0.02

Cr*0.03

Mo*0.01

V*0.01

*Sum1.05

Y.S(MPa)

min. 400min. 420

550

T.S(MPa)

min. 490500~640

620

El.(%)

min. 22min. 20

29

IV (J)-20℃ -30℃

≥ 27≥ 47

110 80

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~10050~80

3.2350

90~13080~120

4.0400

130~180110~170

5.0400

200~250160~210

6.0450

250~310-

EN ISO 2560-A:2006 : E 42 3 B 32 H5EN ISO 2560-B:2006 : E 49 18 A U H5AWS A5.1-04 : E7018 H4R

KS D 7006 : E5016JIS Z 3211 : E4918 H5

AW : As-Welded

59

K-7018NFor 490MPa high tensile steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals


Covering is low hydrogen, iron powder type for welding of nuclear reactor vessels, LPG tankers, LPG storage tanks and similar installations at low temperature.Good impact value at -45℃Excellent mechanical properties and radiographic soundness.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


DNV

5YH10

LR

5Y40mH15

C0.07

Si0.58

Mn*1.38

P0.013

S0.012

Ni*0.15

Cr*0.03

Mo*0.01

V*0.01

*Sum1.58

Y.S(MPa)

min. 400min. 420

510

T.S(MPa)

min. 490500~640

590

El.(%)

min. 22min. 20

32

IV (J)-30℃ -45℃

≥ 27≥ 47100 75

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

70~10060~90

3.2350

90~13085~120

4.0400

150~190110~160

5.0400

160~220130~180

6.0450

180~230-

EN ISO 2560-A:2006 : E 42 3 B 32 H10EN ISO 2560-B:2006 : E 49 18-1 A U H10AWS A5.1-04 : E7018-1

JIS Z 3214 : E4918-1

AW : As-Welded

60

61

AW : As-Welded

K-7028LFFor 490MPa high tensile steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen type for flat and horizontal fillet welding of 490MPa class high tensile steel.Extremely high deposition rate and good slag removal.For application of gravity welding and auto-contact welding.Quiet and stable arc.Redry the electrode at 200~250℃ for 30~60 minutes prior to use.

Others : JIS, CE


ABS

3YH10

BV

3YHH

DNV

3YH10

GL

3YH10

KR

3YH10

LR

3YmH15

NK

KMW53H

C0.06

Si0.37

Mn*0.98

P0.021

S0.013

Ni*0.02

Cr*0.03

Mo*0.01

V*0.01

*Sum1.05

Y.S(MPa)

min. 400min. 420

470

T.S(MPa)

min. 490500~640

550

El.(%)

min. 22min. 20

31

IV (J)0℃ -20℃

≥ 27≥ 47

65 50

Remarks

AW

EN ISO 2560-A:2006 : E 42 0 B 52EN ISO 2560-B:2006 : E 49 28 A AWS A5.1-04 : E7028

KS D 7006 : E5026JIS Z 3211 : E4928

Dia.

Length

Amp.(A)

(mm)

(mm)

FH-Fillet

5.0550700

200~250

5.5550700900

220~280

6.0550700900

270~320

6.4550700900

290~340

62

AW : As-Welded

K-8010GFor 560MPa high tensile steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals

JIS, CE

Covering is high cellulose type for all positions welding of pipes, general light structural steels.This electrode is characterized by deeply penetrating, forceful, spray type arc.Readily removable, thin friable slag.Good mechanical properties and the weld metal neets requirement X-ray.Redry the electrode at 70~80℃ for 30~60 minutes prior to use.


C0.09

Si0.43

Mn0.76

P0.011

S0.009

Ni0.32

Cr0.03

Mo0.25

V0.01

Y.S(MPa)

min. 460min. 460

520

T.S(MPa)

min. 550530~680

610

El.(%)

min. 19min. 20

24

IV (J)0℃ -30℃

≥ 27≥ 47

65 50

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6300

50~8040~70

3.2350

70~11060~100

4.0350

110~15090~130

5.0350

160~200140~170

EN ISO 2560-A:2006 : E 46 0 C 22EN ISO 2560-B:2006 : E 55 10-G AAWS A5.5-06 : E8010-G

JIS Z 3211 : E5510-G

63

AW : As-Welded

KK-55For 560MPa high tensile steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen type for welding of 560MPa class high tensile steel.Satisfactory bead appearance and slag removal.Excellent mechanical properties and radiographic soundness.Good weldability and usability.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

JIS, CE


C0.07

Si0.66

Mn1.45

P0.016

S0.011

Ni0.02

Cr0.03

Mo0.01

V0.01

Y.S(MPa)

min. 460min. 460

540

T.S(MPa)

min. 550530~680

600

El.(%)

min. 19min. 20

28

IV (J)-30℃ -40℃

≥ 27≥ 47

60 45

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~9050~80

3.2350

90~13080~120

4.0400

140~190110~170

5.0400

180~240160~200

6.0450

250~310-

EN ISO 2560-A:2006 : E 46 3 B 12 H10EN ISO 2560-B:2006 : E 55 16-G A H10AWS A5.5-06 : E8016-G

KS D 7006 : E5316JIS Z 3211 : E5516-G

64


Covered Electrodes

Classifications

Description

Welding positions




Approvals

Others : JIS, CE

Covering is low hydrogen, iron powder type for welding of 560MPa class high tensile steel in ships, bridges, penstocks and rails.Excellent mechanical properties and radiographic soundness.Satisfactory bead appearance and slag removal.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


ABS

3Y

C0.06

Si0.56

Mn1.32

P0.018

S0.011

Ni0.35

Cr0.03

Mo0.25

V0.01

Y.S(MPa)

min. 460min. 460

490

T.S(MPa)

min. 550530~680

590

El.(%)

min. 19min. 20

28

IV (J)-20℃ -30℃

≥ 27≥ 47

95 80

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~9050~80

3.2350

90~13080~110

4.0400

140~190120~170

5.0400

180~230160~200

6.0450

250~310-

EN ISO 2560-A:2006 : E 42 3 B 32 H10EN ISO 2560-B:2006 : E 49 18-G H10AWS A5.5-06 : E8018-G

KS D 7006 : E5316JIS Z 3211 : E5518-G

AW : As-Welded

65

AW : As-Welded


Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen type for welding of 620MPa class high tensile steelin bridges, vehicles.Mn-Ni-Mo type deposites weld metal.Satisfactory bead appearance and slag removal.Excellent mechanical properties and radiographic soundness.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

JIS, CE


C0.07

Si0.58

Mn1.04

P0.018

S0.011

Ni0.64

Cr0.03

Mo0.29

V0.01

Y.S(MPa)

min. 530min. 500

550

T.S(MPa)

min. 620560~720

650

El.(%)

min. 17min. 18

28

IV (J)0℃ -20℃

≥ 27≥ 47

80 50

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~9050~80

3.2350

90~13080~110

4.0400

140~190120~170

5.0400

180~230160~200

6.0450

250~300-

EN ISO 2560-A:2006 : E 50 0 1Ni B 12 H10EN ISO 2560-B:2006 : E 55 16-G A H10AWS A5.5-06 : E9016-G

KS D 7006 : E5816JIS Z 3211 : E6216-G

66

AW : As-Welded


Covered Electrodes

Classifications

Description

Welding positions




Approvals

JIS, CE

Covering is low hydrogen type for welding of 690MPa class high strength low alloy steel, yield point 620MPa of pressure vessels, penstocks and bridges.Satisfactory bead appearance and slag removal.Excellent crack resistance and radiographic soundness.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


C0.07

Si0.49

Mn1.05

P0.015

S0.011

Ni1.87

Cr0.05

Mo0.37

V0.01

Y.S(MPa)

min. 600min. 550

640

T.S(MPa)

min. 690610~780

730

El.(%)

min. 16min. 18

26

IV (J)-20℃ -30℃

≥ 27≥ 47

100 90

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~9050~80

3.2350

90~13080~110

4.0400

140~190120~170

5.0400

180~230160~200

6.0450

250~300-

EN 757:1997 : E 55 3 Z B 12 H10AWS A5.5-06 : E10016-G

KS D 7006 : E7016JIS Z 3211 : E6916-G

67

AW : As-Welded


Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen type for welding of 760MPa class high strength low alloy steel, yield point 690MPa of pressure vessels, penstocks and bridges.Satisfactory bead appearance and slag removal.Excellent crack resistance and radiographic soundness.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


C0.07

Si0.60

Mn1.10

P0.013

S0.012

Ni1.84

Cr0.23

Mo0.43

V0.01

Y.S(MPa)

min. 670min. 620

730

T.S(MPa)

min. 760690~890

830

El.(%)

min. 15min. 18

22

IV (J)0℃ -20℃

≥ 27≥ 47

60 40

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~9050~80

3.2350

90~13080~110

4.0400

140~190120~170

5.0400

180~230160~200

6.0450

250~300-

EN 757:1997 : E 62 0 Z B 12 H10AWS A5.5-06 : E11016-G

KS D 7006 : E8016JIS Z 3211 : E7616-G

JIS, CE

K-9018MFor 620MPa high tensile steel

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Others : JIS, CE

Covering is low hydrogen, iron powder type for welding of 620MPa class high tensile steel in bridge, pressure vessels, penstocks and machinery.Excellent mechanical properties especially in notch toughness.Satisfactory bead appearance and slag removal. Redry the electrode at 300~400℃ for 1~2 hours prior to use.


ABS

E9018M-H8

C0.05

Si0.51

Mn0.88

P0.013

S0.011

Ni1.58

Cr0.10

Mo0.20

V0.01

Y.S(MPa)

540~620min. 500

570

T.S(MPa)

min. 620560~720

670

El.(%)

min. 24min. 18

30

IV (J)-40℃ -50℃

≥ 27≥ 47

110 90

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

50~10040~80

3.2350

90~13080~115

4.0400

140~190110~160

5.0400

190~240140~170

6.0450

250~310-

EN ISO 2560-A:2006 : E 50 5 Z B 32 H10AWS A5.5-06 : E9018-M

KS D 7006 : E5816JIS Z 3211 : E6218-N3M1

AW : As-Welded

68

69

AW : As-Welded


Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen, iron powder type for welding of 690MPa class high tensile steel in bridge, pressure vessels, penstocks and machinery.Excellent mechanical properties especially in notch toughness.Satisfactory bead appearance and slag removal.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

JIS, CE

AWS A5.5EN 757Example

C0.07

Si0.46

Mn1.35

P0.015

S0.012

Ni1.63

Cr0.20

Mo0.28

V0.01

Y.S(MPa)

610~690min. 550

640

T.S(MPa)

min. 690610~780

750

El.(%)

min. 16min. 18

29

IV (J)-30℃ -50℃

≥ 27≥ 47

80 45

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

3.2350

90~13080~115

4.0400

130~180110~170

5.0400

180~240140~200

6.0450

250~320-

EN 757:1997 : E 55 3 Z B 32 H10AWS A5.5-06 : E10018-M

KS D 7006 : E7016JIS Z 3211 : E6918-N3M2


Covered Electrodes

Classifications

Description

Welding positions




Approvals

Others : JIS, CE

Covering is low hydrogen, iron powder type for welding of low alloy high strength steels having tesile properties of about 740~790MPa such as HY80, etc.Excellent mechanical properties especially in notch toughness.Satisfactory bead appearance and slag removal.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


ABS

E11018M-H8

C0.08

Si0.41

Mn1.49

P0.015

S0.012

Ni1.86

Cr0.25

Mo0.35

V0.01

Y.S(MPa)

680~760min. 620

730

T.S(MPa)

min. 760690~890

830

El.(%)

min. 20min. 18

22

IV (J)-30℃ -50℃

≥ 27≥ 47

80 45

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

50~10040~90

3.2350

90~13080~120

4.0400

130~180110~160

5.0400

180~240140~200

6.0450

240~320-

EN 757:1997 : E 62 3 Z B 32 H10AWS A5.5-06 : E11018-M

KS D 7006 : E8016JIS Z 3211 : E7618-N4M2

AW : As-Welded

70

71

AW : As-Welded


Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen, iron powder type for welding of 890MPa class high tensile steel in bridge, pressure vessels, penstocks and machinery.Excellent mechanical properties especially in notch toughness.Good radiographic soundness.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

JIS, CE


C0.08

Si0.30

Mn1.46

P0.014

S0.013

Ni1.86

Cr0.95

Mo0.41

V0.01

Y.S(MPa)

740~830min. 690

800

T.S(MPa)

min. 830760~960

940

El.(%)

min. 18min. 17

20

IV (J)-30℃ -50℃

≥ 27≥ 47

70 40

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

70~10060~90

3.2350

90~13070~100

4.0400

150~190120~160

5.0400

180~230140~180

6.0450

220~300-

EN 757:1997 : E 69 3 Z B 32 H10AWS A5.5-06 : E12018-M

JIS Z 3211 : E8618-N4C2M2

72

PWHT : 620℃x1Hr

K-8018D1For 560MPa high tensile steel (Mn-Mo steel)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

JIS, CE

Covering is low hydrogen, iron powder type for welding of 560MPa class high tensile steel or 1.5%Mn-0.35%Mo steel.Very low hydrogen contens. (HD ≤4ml/100g)Excellent mechanical properties and radiographic soundness.Good notch toughness at -50℃.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

AWS A5.5EN ISO 2560-BExample

C0.07

Si0.47

Mn1.33

P0.013

S0.013

Ni0.77

Cr0.02

Mo0.30

V0.01

Y.S(MPa)

min. 460min. 460

640

T.S(MPa)

min. 550min. 550

690

El.(%)

min. 19min. 17

25

IV (J)-40℃ -50℃

≥ 27≥ 27

60 40

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

3.2350

70~10060~90

4.0400

90~15080~130

5.0400

150~190120~170

6.0450

190~260140~200

EN ISO 2560-B:2006 : E 55 18-3M2 P H5AWS A5.5-06 : E8018-D1 H4

JIS Z 3211 : E5518-3M2 P H5

73

PWHT : 620℃x1Hr


Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen, iron powder type for welding of 560MPa class high tensile steel (ASTM A302 Gr.B) or 1.85%Mn-0.35%Mo steel.Very low hydrogen contens. (HD ≤4ml/100g)Excellent mechanical properties especially in notch toughness.Satisfactory bead appearance and slag removal.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

JIS, CE


C0.10

Si0.58

Mn1.71

P0.017

S0.015

Ni0.74

Cr0.02

Mo0.31

V0.01

Y.S(MPa)

min. 600min. 550

680

T.S(MPa)

min. 690610~780

760

El.(%)

min. 16min. 18

23

IV (J)-30℃ -50℃

≥ 27≥ 47

60 40

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

3.2350

70~10060~90

4.0400

90~15080~130

5.0400

150~190120~170

6.0450

190~260140~200

EN 757:1997 : E 55 3 Z B T 32 H5AWS A5.5-06 : E10018-D2 H4

JIS Z 3211 : E6918-4M2 P H5

74

PWHT : 620℃x1Hr

Covered Electrodes

Classifications

Description

Welding positions




Approvals


JIS

Covering is low hydrogen, iron powder type for welding of 560MPa class high tensile steel or 1.5%Mn-0.5%Mo steel.Very low hydrogen contens. (HD ≤4ml/100g)Excellent mechanical properties and radiographic soundness.Good notch toughness at -50℃.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


C0.05

Si0.37

Mn1.39

P0.014

S0.010

Ni0.77

Cr0.05

Mo0.55

V0.01

Y.S(MPa)

min. 460min. 460

660

T.S(MPa)

min. 550min. 550

730

El.(%)

min. 19min. 17

23

IV (J)-40℃ -50℃

≥ 27≥ 27

55 35

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

3.2350

70~10060~90

4.0400

90~15080~130

5.0400

150~190120~170

6.0450

190~260140~200

EN ISO 2560-B:2006 : E 55 18-3M3 P H5AWS A5.5-06 : E8018-D3 H4

JIS Z 3211 : E5518-3M3 P H5

75

AW : As-Welded

Covered Electrodes

Classifications

Description

Welding positions




Approvals

KW-50GFor atomospheric corrosion resisting steel

Covering is low hydrogen type for welding of 490MPa class high tensile strength weathering type structural steel for vehicles, building and bridges.Excellent weather-proof property and crack resistance.Satisfactory bead appearance and slag removal.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

CE


C0.06

Si0.46

Mn0.74

P0.018

S0.009

Ni0.63

Cr0.52

Mo0.01

V0.01

Cu0.40

Y.S(MPa)

min. 400min. 420

450

T.S(MPa)

min. 490500~640

610

El.(%)

min. 22min. 20

28

IV (J)-20℃ -30℃

≥ 27≥ 27

70 50

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

3.2350

90~13070~110

4.0400

150~190120~160

5.0400

180~230130~170

6.0450

240~280-

EN ISO 2560-A:2006 : E 42 3 Z B 12 H10EN ISO 2560-B:2006 : E 49 16-G A H10AWS A5.5-06 : E7016-G

KS D 7101 : DA5016WJIS Z 3214 : DA5016W

76

AW : As-Welded

Covered Electrodes

Classifications

Description

KW-50VFor atomospheric corrosion resisting steel

Welding positions




Covering is low hydrogen type for vertical-down welding of 490MPa class high tensile strength weathering type structural steel for vehicles, building and bridges.Excellent working efficieny in vertical-down welding.Excellent weather-proof property and crack resistance.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

AWS A5.5JIS Z 3214Example

C0.06

Si0.54

Mn0.86

P0.015

S0.011

Ni0.60

Cr0.51

Mo0.01

V0.01

Cu0.27

Y.S(MPa)

min. 400min. 390

440

T.S(MPa)

min. 490min. 490

540

El.(%)

min. 22min. 23

32

IV (J)0℃ -30℃

≥ 27≥ 47100 50

Remarks

AW

Dia.Length

Amp. (A)

(mm)(mm)

V-down

3.2350

120~160

4.0400

170~210

5.0400

220~280

AWS A5.5-06 : E7016-G KS D 7101 : DA5016G JIS Z 3214 : DA5016G

77

AW : As-Welded

Covered Electrodes

Classifications

Description

KW-50WHFor atomospheric corrosion resisting steel

Welding positions




Covering is low hydrogen, iron powder type for flat and horizontal fillet welding of 490MPa class high tensile strength weathering type structural steel for buildings, bridges and other steel structures.Extremely high deposition rate and easy slag removal.Quiet and stable arc.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

JIS Z 3214 Example

C0.07

Si0.30

Mn0.92

P0.015

S0.012

Ni0.53

Cr0.51

Mo0.01

Cu0.39

Y.S(MPa)

min. 390510

T.S(MPa)

min. 490560

El.(%)

min. 2327

IV (J)0℃ -30℃

≥ 4765 40

Remarks

AW

Dia.

Length

Amp.(A)

(mm)

(mm)

FH-fillet

4.0400

160~200

5.0450500550

200~250

5.5450500550

220~270

6.0450500550

250~300

KS D 7101 : DA5026W JIS Z 3214 : DA5026W

78

AW : As-Welded

Covered Electrodes

Classifications

Description

Welding positions




Approvals

KW-60GFor atomospheric corrosion resisting steel

CE

Covering is low hydrogen type for welding of 560MPa class high tensile strength weathering type structural steel for buildings, bridges and other steel structures.Excellent weather-proof property and crack resistance.Satisfactory bead appearance and slag removal. Redry the electrode at 300~400℃ for 1~2 hours prior to use.


C0.07

Si0.65

Mn0.75

P0.016

S0.011

Ni0.62

Cr0.53

Mo0.01

Cu0.50

Y.S(MPa)

min. 460min. 500

530

T.S(MPa)

min. 550560~720

590

El.(%)

min. 19min. 18

24

IV (J)0℃ -20℃

≥ 27≥ 47100 70

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

3.2350

90~13070~110

4.0400

150~190120~160

5.0400

180~230130~170

6.0450

240~280-

EN ISO 2560-A:2006 : E 50 0 Z B 12EN ISO 2560-B:2006 : E 55 16-G AAWS A5.5-06 : E8016-G

KS D 7101 : DA5816WJIS Z 3214 : DA5816W

79

AW : As-Welded

Covered Electrodes

Classifications

Description

Welding positions




Approvals

K-8018WFor atomospheric corrosion resisting steel

Covering is low hydrogen, iron powder type for welding of 560MPa class high tensile strength weathering type structural steel for buildings, bridges and other steel structures.(ASTM A67 Gr.1 ; A242 Gr.all ; A588 Gr.all ; A606 Gr.all ; A709 Gr.70W)Excellent weather-proof properties and crack resistance of the deposited weld metal.Good weldability and usability.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

CE


C0.05

Si0.47

Mn0.70

P0.015

S0.015

Ni0.69

Cr0.54

Mo0.01

Cu0.45

Y.S(MPa)

min. 460min. 460

530

T.S(MPa)

min. 550530~680

590

El.(%)

min. 20min. 20

24

IV (J)-20℃ -30℃

≥ 27≥ 47

80 60

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

70~11060~90

3.2350

90~13070~110

4.0400

150~190120~160

5.0400

180~230130~170

EN ISO 2560-A:2006 : E 46 2 Z B 32 H10 EN ISO 2560-B:2006 : E 55 18-NCC1 A U H10 AWS A5.5-06 : E8018-W2

80

AW : As-Welded

Covered Electrodes

Classifications

Description

Welding positions




Approvals

KK-50NFor low temperature service steel (490MPa)

Others : CE

Covering is low hydrogen type for welding of aluminium-killed steel to be used for LPG tankers, LPG storage tanks, machineries and structures.Excellent notch toughness of deposited weld metal at low temperature.Satisfactory bead appearance and slag removal.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


DNV

5YH10

LR

5Y40mH15

C0.08

Si0.42

Mn1.35

P0.014

S0.011

Ni0.47

Cr0.02

Mo0.01

V0.01

Y.S(MPa)

min. 400min. 420

490

T.S(MPa)

min. 490500~640

570

El.(%)

min. 22min. 20

30

IV (J)-30℃ -45℃

≥ 27≥ 47130 90

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

50~10030~80

3.2350

70~13070~100

4.0400

150~190120~160

5.0400

220~250150~200

6.0450

250~310-


KS D 7101 : DL5016-4A0JIS Z 3211 : E4916-G

81

AW : As-Welded

Covered Electrodes

Classifications

Description

Welding positions




Approvals

KK-50NNFor low temperature service steel (490MPa)

Covering is low hydrogen type for welding of aluminium-killed steel to be used for LPG tankers, and LPG storage tanks, etc.Excellent notch toughness of deposited weld metal at low temperature.Satisfactory bead appearance and slag removal.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

CE


C0.07

Si0.37

Mn1.45

P0.013

S0.010

Ni1.37

Cr0.03

Mo0.01

V0.01

Y.S(MPa)

min. 400min. 420

520

T.S(MPa)

min. 490500~640

590

El.(%)

min. 22min. 20

28

IV (J)-50℃ -60℃

≥ 27≥ 27120 100

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

50~10030~80

3.2350

70~13070~100

4.0400

150~190120~160

5.0400

220~250130~200

6.0450

250~300-


KS D 7101 : DL5016-6A1JIS Z 3211 : E4916-G

82

PWHT : 605℃x1Hr

Covered Electrodes

Classifications

Description

Welding positions




Approvals

K-8016C1For low temperature service steel (560MPa)

CE

Covering is low hydrogen type for welding of 2.5%Ni steel and aluminium-killed steel used at low temperature, LPG tanks, etc.Excellent impact value at -60℃Good weldability and usability.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


C0.07

Si0.45

Mn0.98

P0.016

S0.013

Ni2.25

Cr0.03

Mo0.02

V0.01

Y.S(MPa)

min. 460min. 460

520

T.S(MPa)

min. 550500~550

600

El.(%)

min. 19min. 17

30

IV (J)-50℃ -60℃

≥ 27≥ 47

140 120

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~9050~80

3.2350

110~150100~140

4.0400

150~190120~170

5.0400

200~240150~200

6.0450

250~310-

EN ISO 2560-A:2006 : E 46 6 2Ni B 12 H10EN ISO 2560-B:2006 : E 55 16-N5 P U H10AWS A5.5-06 : E8016-C1

KS D 7023 : DL5016-6P2JIS Z 3211 : E5516-N5 P U

83

PWHT : 605℃x1Hr

Covered Electrodes

Classifications

Description

Welding positions




Approvals


Covering is low hydrogen, iron powder type for welding of 2.5%Ni steel and aluminium-killed steel used at low temperature, LPG tanks, etc.Stable arc in flat and horizontal fillet welding.Weld metal of fine ripple mark without undercut can be obtained.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

Others : CE


ABS

3YH10,E8018-C1

DNV

3YH15

LR

3YmH15

C0.06

Si0.60

Mn0.96

P0.015

S0.012

Ni2.41

Cr0.03

Mo0.01

V0.01

Y.S(MPa)

min. 460min. 460

500

T.S(MPa)

min. 550500~550

600

El.(%)

min. 19min. 17

32

IV (J)-50℃ -60℃

≥ 27≥ 47

120 100

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~10060~90

3.2350

90~13085~120

4.0400

130~190110~160

5.0400

190~250-

6.0450

250~300-

EN ISO 2560-A:2006 : E 46 6 2Ni B 32 H10EN ISO 2560-B:2006 : E 55 18-N5 P U H10AWS A5.5-06 : E8018-C1

JIS Z 3211 : E5518-N5 P U

84


Covered Electrodes

Classifications

Description

Welding positions




Approvals

CE

Covering is low hydrogen type for welding of 3.5%Ni steel and aluminium-killed steel used at low temperature, LPG tanks, etc.Excellent impact value at -75℃Good weldability and usability.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


C

0.07

Si

0.45

Mn

1.10

P

0.014

S

0.011

Ni

3.46

Cr

0.04

Mo

0.01

V

0.01

Y.S(MPa)

min. 460min. 460

500

T.S(MPa)

min. 550500~550

610

El.(%)

min. 19min. 17

30

IV (J)-60℃ -75℃

≥ 27≥ 27

70 55

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

50~9050~80

3.2350

90~13080~120

4.0400

130~180110~160

5.0400

180~240150~200

6.0450

220~260-

EN ISO 2560-A:2006 : E 46 6 3Ni B 12 H10EN ISO 2560-B:2006 : E 55 16-N7 P H10AWS A5.5-06 : E8016-C2

KS D 7023 : DL5016-6P3JIS Z 3211 : E5516-N7 P

PWHT : 605℃x1Hr

85

PWHT : 605℃x1Hr


Covered Electrodes

Classifications

Description

Welding positions




Covering is low hydrogen, iron powder type for welding of 3.5%Ni steel and aluminium-killed steel used at low temperature, LPG tanks, etc.Fast, efficient metal transfer in all positions.Excellent notch toughness of the deposited weld metal at low temperature.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


C0.07

Si0.32

Mn1.12

P0.013

S0.012

Ni3.45

Cr0.03

Mo0.01

V0.01

Y.S(MPa)

min. 460min. 460

530

T.S(MPa)

min. 550500~550

620

El.(%)

min. 19min. 17

28

IV (J)-60℃ -75℃

≥ 27≥ 27

55 40

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~9050~80

3.2350

90~13080~120

4.0400

135~180110~170

5.0400

190~240-

6.0450

250~310-

EN ISO 2560-A:2006 : E 46 6 3Ni B 32 H10EN ISO 2560-B:2006 : E 55 18-N7 P H10AWS A5.5-06 : E8018-C2

JIS Z 3211 : E5518-N7 P

86

AW : As-Welded


Covered Electrodes

Classifications

Description

Welding positions




Approvals


C0.07

Si0.45

Mn0.91

P0.013

S0.012

Ni1.03

Cr0.02

Mo0.01

V0.01

Y.S(MPa)

470~550min. 460

530

T.S(MPa)

min. 550530~680

600

El.(%)

min. 24min. 20

28

IV (J)-30℃ -40℃

≥ 27≥ 47

100 60

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~9560~90

3.2350

90~13080~120

4.0400

135~180110~170

5.0400

190~240-

EN ISO 2560-A:2006 : E 46 6 3Ni B 32 H10EN ISO 2560-B:2006 : E 55 18-N2 A U H10AWS A5.5-06 : E8018-C3

JIS Z 3211 : E5518-N2 U

Covering is low hydrogen, iron powder type for welding of 1%Ni steel and high tensile strength steel for military and commercial applications where good impact property.Fast, efficient metal transfer in all positions.Excellent deposited weld metal with both AC and DC power source. Redry the electrode at 300~400℃ for 1~2 hours prior to use.

Others : CE

ABS

3YH10,E8018-C3

LR

3YmH15

87

AW : As-Welded

K-7018C3LFor low temperature service steel (490MPa)

Covered Electrodes

Classifications

Description

Welding positions




Covering is low hydrogen, iron powder type for welding of 1%Ni steel and aluminium-killed steel used at low temperature, LPG tanks, etc.Fast, efficient metal transfer in all positions and very low hydrogen contens. (HD ≤4ml/100g)Excellent notch toughness of the deposited weld metal at low temperature.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


C0.05

Si0.31

Mn0.86

P0.016

S0.016

Ni1.01

Cr0.05

Mo0.02

V0.01

Y.S(MPa)

min. 390min. 420

530

T.S(MPa)

min. 490500~640

620

El.(%)

min. 22min. 20

34

IV (J)-30℃ -50℃

≥ 27≥ 47

90 50

Remarks

AW

EN ISO 2560-A:2006 : E 42 3 1Ni B 32 H5EN ISO 2560-B:2006 : E 49 18-N2 A H5 AWS A5.5-06 : E7018-C3L H4R

JIS Z 3211 : E4918-N2 H5

Approvals

CE

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~9050~80

3.2350

90~14080~120

4.0400

150~190120~160

5.0400

180~230-

88

AW : As-Welded


Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen, iron powder type for welding of 1.5%Ni steel and aluminium-killed steel used at low temperature, LPG tanks, etc.Excellent notch toughness of the deposited weld metal at low temperature.Good weldability and usability and very low hydrogen contens. (HD ≤4ml/100g)Redry the electrode at 300~400℃ for 1~2 hours prior to use.

C0.06

Si0.56

Mn0.85

P0.013

S0.011

Ni1.26

Cr0.03

Mo0.01

V0.01

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~9050~80

3.2350

90~14080~120

4.0400

150~190120~160

5.0400

180~230-

EN ISO 2560-A:2006 : E 46 5 Z B 12 H5EN ISO 2560-B:2006 : E 55 16-N3 A U H5AWS A5.5-06 : E8016-C4 H4

JIS Z 3211 : E5516-N3 U H5

CE


Y.S(MPa)

min. 460min. 460

530

T.S(MPa)

min. 550530~680

600

El.(%)

min. 19min. 20

28

IV (J)-30℃ -50℃

≥ 27≥ 47

110 70

Remarks

AW

89

PWHT : 620℃x1Hr

K-7010A1For heat-resisting steel (0.5%Mo)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is high cellulose type for all positions welding of 0.5%Mo steel pipes used for high pressure, high temperature steam service, structural steel and plates or castings.Extremely good radiographic soundness and mechanical properties.Not to use the currents exceeding the recommended currents. Redry the electrode at 70~80℃ for 30~60 minutes prior to use.

C0.09

Si0.14

Mn0.43

P0.015

S0.009

Ni0.05

Cr0.06

Mo0.58

V0.01

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

50~7530~70

3.2350

70~11060~100

4.0350

110~15090~130

5.0350

160~200130~170

EN ISO 3580-B:2008 : E 49 10-1M3 AWS A5.5-06 : E7010-A1

Others : CE


ABS

3Y,E7010-A1

Y.S(MPa)

min. 390min. 390

440

T.S(MPa)

min. 490min. 490

550

El.(%)

min. 22min. 20

29

IV (J)20℃ 0℃

≥ 27≥ 47

60 50

Remarks

PWHT

90

PWHT : 620℃x1Hr


Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen type for welding of alloys used for hign temperature service such as C-Mo steel pipes(STPA 12, A335-P1), boiler and heat exchanger steel tubes, rolled steel and cast steel.Preheat at 100~200℃ and postheat treat at 620~680℃Satisfactory bead appearance and slag removal.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


C0.07

Si0.54

Mn0.83

P0.015

S0.009

Ni0.02

Cr0.03

Mo0.52

V0.01

Y.S(MPa)

min. 390min. 355

560

T.S(MPa)

min. 490min. 510

650

El.(%)

min. 22min. 22

31

IV (J)20℃ 0℃

≥ 27≥ 47

60 50

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

55~8550~80

3.2350

90~13080~120

4.0400

140~190110~170

5.0400

180~250130~200

6.0450

240~300-

EN ISO 3580-A:2008 : E Mo B 12 H10EN ISO 3580-B:2008 : E 49 16-1M3 H10AWS A5.5-06 : E7016-A1

KS D 7022 : DT1216JIS Z 3223 : DT1216

CE

91

PWHT : 620℃x1Hr


Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen, iron powder type for welding of alloys steel of 490MPa minimum yield point 0.5%Mo steel of pressure pipe, casting and general fabrication of pressure vessel.Preheat at 100~200℃ and postheat treat at 620~680℃High deposition rate in all positions.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


C0.06

Si0.49

Mn0.72

P0.015

S0.011

Ni0.02

Cr0.03

Mo0.53

V0.01

Y.S(MPa)

min. 390min. 355

590

T.S(MPa)

min. 490min. 510

680

El.(%)

min. 22min. 22

28

IV (J)20℃ 0℃

≥ 27≥ 47130 110

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~9050~80

3.2350

80~12070~110

4.0400

130~180100~160

5.0400

190~240-

6.0450

240~300-

EN ISO 3580-A:2008 : E Mo B 32 H10EN ISO 3580-B:2008 : E 49 18-1M3 H10AWS A5.5-06 : E7018-A1

CE

92

PWHT : 690℃x1Hr

K-8016B1For heat-resisting steel (0.5%Cr-0.5%Mo)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen type for welding of 0.5%Cr-0.5%Mo steel used high temperature high pressure boilers, chemical equipment and oil refining plants.(A335-P2, A213-T2)Preheat at 150~250℃ and postheat treat at 620~680℃Excellent crack resistance because of low hydrogen contents.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


C0.07

Si0.51

Mn0.81

P0.014

S0.010

Ni0.02

Cr0.51

Mo0.49

V0.01

Y.S(MPa)

min. 460min. 355

590

T.S(MPa)

min. 550min. 510

670

El.(%)

min. 19min. 22

26

IV (J)20℃ 0℃

≥ 27≥ 47

70 50

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

50~8540~80

3.2350

90~13080~120

4.0400

130~180100~160

5.0400

190~240130~200

6.0450

250~320-

EN ISO 3580-A:2008 : E CrMo0.5 B 12 H10 EN ISO 3580-B:2008 : E 55 16-CM H10 AWS A5.5-06 : E8016-B1

CE

93

PWHT : 690℃x1Hr


Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen type for welding of 1.25%Cr-0.5%Mo steel used for super-heater tubes, steampipes, heaters of boilers for thermoelectric power plant and equipments oil refining industries.Preheat at 150~300℃ and postheat treat at 680~730℃Excellent crack resistance because of low hydrogen contents.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

CE


C0.06

Si0.47

Mn0.65

P0.014

S0.012

Ni0.03

Cr1.31

Mo0.52

V0.01

Y.S(MPa)

min. 460min. 355

570

T.S(MPa)

min. 550min. 510

650

El.(%)

min. 19min. 22

26

IV (J)20℃ 0℃

≥ 27≥ 47

80 60

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~9050~80

3.2350

80~12075~110

4.0400

130~180100~160

5.0400

180~230-

6.0450

240~300-

EN ISO 3580-A:2008 : E CrMo1 B 12 H10EN ISO 3580-B:2008 : E 55 16-1CM H10AWS A5.5-06 : E8016-B2

KS D 7022 : DT2316JIS Z 3223 : DT2316


Covered Electrodes

Classifications

Description

Welding positions




Approvals

Others : CE

Covering is low hydrogen, iron powder type for welding of 1.25%Cr-0.5%Mo steel used for steam pipesof boilers, oil refining industries, pressure vessels for high temperature service.Preheat at 150~300℃ and postheat treat at 680~730℃High deposition rate in all positions.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


ABS

3YH10, E8018-B2

DNV

3YH10

LR

3YmH15

C0.06

Si0.61

Mn0.70

P0.014

S0.011

Ni0.02

Cr1.32

Mo0.55

V0.01

Y.S(MPa)

min. 460min. 355

590

T.S(MPa)

min. 550min. 510

670

El.(%)

min. 19min. 22

25

IV (J)20℃ 0℃

≥ 27≥ 47

80 65

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

65~9560~90

3.2350

90~13080~120

4.0400

130~190110~170

5.0400

190~250-

6.0450

250~300-


KS D 7022 : DT2318JIS Z 3223 : DT2318

PWHT : 690℃x1Hr

94

95

PWHT : 690℃x1Hr

K-9016B3For heat-resisting steel (2.25%Cr-1%Mo)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen type for welding of 2.25%Cr-1%Mo steel used for super-heater tubes, steam pipes, heaters of boilers for thermoelectric power plant and equipments oil refining industries.Preheat at 150~300℃ and postheat treat at 680~730℃Excellent crack resistance because of low hydrogen contents.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

CE


C0.08

Si0.45

Mn0.78

P0.016

S0.011

Ni0.03

Cr2.37

Mo1.03

V0.01

Y.S(MPa)

min. 530min. 400

620

T.S(MPa)

min. 620min. 500

710

El.(%)

min. 17min. 18

24

IV (J)20℃ 0℃

≥ 27≥ 47

55 40

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~10060~90

3.2350

90~13075~115

4.0400

130~190110~170

5.0400

190~240-


KS D 7022 : DT2416JIS Z 3223 : DT2416

96

PWHT : 690℃x1Hr

K-9018B3For heat-resisting steel (2.25%Cr-1%Mo)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

CE

Covering is low hydrogen, iron powder type for all positions welding of 2.25%Cr-1%Mo steel used for steam pipe of boilers, oil refining industries, pressure vessels for high temperature service.Preheat at 150~300℃ and postheat treat at 680~730℃High deposition rate in all positions.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


C0.08

Si0.50

Mn0.77

P0.018

S0.011

Ni0.03

Cr2.25

Mo1.02

V0.01

Y.S(MPa)

min. 530min. 400

680

T.S(MPa)

min. 620min. 500

750

El.(%)

min. 17min. 18

21

IV (J)20℃ 0℃

≥ 27≥ 47

50 35

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~10060~90

3.2350

90~13080~120

4.0400

140~190110~170

5.0400

190~250-


KS D 7022 : DT2418JIS Z 3223 : DT2418

97

PWHT : 740℃x1Hr

K-8015B6For heat-resisting steel (5%Cr-0.5%Mo)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen type for welding of 5%Cr-0.5%Mo steel used in oil refining and chemical industries, heat treated high tensile strength steel for aircraft part such as SAE 4130.Preheat at 250~350℃ and postheat treat at 750~850℃Excellent crack resistance because of low hydrogen contents.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

CE


C0.08

Si0.35

Mn0.84

P0.017

S0.012

Ni0.04

Cr5.25

Mo0.55

V0.01

Y.S(MPa)

min. 460min. 400

670

T.S(MPa)

min. 550min. 500

720

El.(%)

min. 19min. 17

23

IV (J)20℃ 0℃

≥ 27≥ 47

60 50

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

50~9050~80

3.2350

75~11570~110

4.0400

120~16090~130

5.0400

160~210

6.0450

210~260


KS D 7022 : DT2516JIS Z 3223 : DT2516

98

PWHT : 740℃x1Hr

K-8016B6For heat-resisting steel (5%Cr-0.5%Mo)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

CE

Covering is low hydrogen type for welding of 5%Cr-0.5%Mo steel used in oil refining and chemical industries, heat treated high tensile strength steel for aircraft part such as SAE 4130.Preheat at 250~350℃ and postheat treat at 750~850℃Excellent crack resistance because of low hydrogen contents.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


C0.06

Si0.43

Mn0.57

P0.018

S0.012

Ni0.04

Cr4.98

Mo0.51

V0.01

Y.S(MPa)

min. 460min. 400

680

T.S(MPa)

min. 550min. 500

740

El.(%)

min. 19min. 17

22

IV (J)20℃ 0℃

≥ 27≥ 47

55 45

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

50~9050~80

3.2350

80~12070~110

4.0400

120~16090~130

5.0400

160~210-

5.0400

210~260-


KS D 7022 : DT2416JIS Z 3223 : DT2416

99

PWHT : 740℃x1Hr

K-8015B8For heat-resisting steel (9%Cr-1%Mo)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is low hydrogen type for welding of super-heater tubes of high temperature and high pressure boilers, heater tubes of oil refining equipments.Preheat at 250~350℃ and postheat treat at 750~850℃ because of high self-hardening property of the deposited weld metal.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

CE


C0.08

Si0.45

Mn0.88

P0.018

S0.011

Ni0.03

Cr8.86

Mo0.95

V0.01

Y.S(MPa)

min. 460min. 530

670

T.S(MPa)

min. 550min. 620

760

El.(%)

min. 19min. 15

22

IV (J)20℃ 0℃

≥ 27≥ 47

45 40

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

60~9050~60

3.2350

80~12070~110

4.0400

120~16090~150

5.0400

160~220

6.0450

210~260

EN ISO 3580-B:2008 : E 62 15-9C1M H10AWS A5.5-06 : E8015-B8

KS D 7022 : DT2616JIS Z 3223 : DT2616

100

PWHT : 740℃x1Hr

K-8016B8For heat-resisting steel (9%Cr-1%Mo)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

CE

Covering is low hydrogen type for welding of super-heater tubes of high temperature and high pressure boilers, heater tubes of oil refining equipments.Preheat at 250~350℃ and postheat treat at 750~850℃ because of high self-hardening property of the deposited weld metal.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


C0.08

Si0.74

Mn0.98

P0.020

S0.013

Ni0.03

Cr8.48

Mo0.90

V0.01

Y.S(MPa)

min. 460min. 530

690

T.S(MPa)

min. 550min. 620

780

El.(%)

min. 19min. 15

21

IV (J)20℃ 0℃

≥ 27≥ 47

50 45

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

55~9050~80

3.2350

80~12070~110

4.0400

120~16090~150

5.0400

160~220-

6.0450

210~260-

EN ISO 3580-B:2008 : E 62 16-9C1MH10AWS A5.5-06 : E8016-B8

KS D 7022 : DT2616JIS Z 3223 : DT2616

101

KM-100For hardfacing (Hv 250)

Covered Electrodes

Classifications

Description

Welding positions




Covering is high titania type for hardfacing of shafts, tires, gears, crane wheels, etc.Easy slag removal.Beautiful, smooth bead appearaqnce.Extremely machinable the deposited weld metal.Preheat at 150~200℃ only for low alloy steel and high carbon steel. Redry the electrode at 70~100℃ for 30~60 minutes prior to use.

Conditions

HVHRCHS

C0.11

Si0.42

Mn0.98

P0.016

S0.013

Ni0.02

Cr0.03

Mo0.01

W0.01

225~24016~2033~34

245~26521~2535~38

Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

80~120

4.0400

140~170

5.0400

170~210

6.0450

200~250

EN 14700:2005 : E Fe 1KS D 7035 : DF2A-250-RJIS Z 3251 : DF2A-250-R

As weldedContinuous surfacing nterpass temperature max.100℃

102


Covered Electrodes

Classifications

Description

Welding positions




Covering is low hydrogen type for hardfacing and repairing of worn parts such as shafts, gears, wheels, etc.Stable arc, smooth bead appearance and easy slag removal.High abrasion resistance and impact resistance.Good machinable the deposited weld metal.Preheat at 150~200℃ only for multilayer welding of low alloy steell and high carbon steel.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

C0.18

Si0.69

Mn2.28

P0.013

S0.009

Ni0.02

Cr0.03

Mo0.01

W0.01

Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

90~130

4.0400

140~180

5.0400

180~240

6.0450

220~300

EN 14700:2005 : E Fe 1KS D 7035 : DF2A-250-BJIS Z 3251 : DF2A-250-B

Conditions

HVHRCHS

27826.839

25022.236

39540.354

As weldedInterpass temp. 150℃

Heat treated900℃ oil quenching 650℃ stress relief

103

KM-300RFor hardfacing (Hv 300)

Covered Electrodes

Classifications

Description

Welding positions




Covering is high titania type for hardfacing of shaft, roller, spindle, crane wheel, etc.Excellent slag removal and smooth bead appearance.Good machinable the deposited weld metal.Preheat at 150℃ only for multilayer welding of low alloy steell and high carbon steel.Redry the electrode at 70~100℃ for 30~60 minutes prior to use.

C0.20

Si0.28

Mn0.30

P0.025

S0.022

Ni0.03

Cr2.40

Mo0.01

W0.01

KS D 7035 : DF2A-300-R JIS Z 3251 : DF2A-300-R

Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

80~130

4.0400

140~180

5.0400

170~240

6.0450

240~300

Conditions

HVHRCHS

30830.843

28527.841

42042.757



104


Covered Electrodes

Classifications

Description

Welding positions




Covering is low hydrogen type for hardfacing of shafts, roller, spindle, crane wheel, etc.Good usability.High abrasion resistance and impact resistance.Good machinable the deposited weld metal.Preheat at 150℃ only for multilayer welding of low alloy steell and high carbon steel.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

C0.20

Si0.60

Mn1.48

P0.018

S0.011

Ni0.02

Cr0.70

Mo0.01

W0.01

EN 14700:2005 : E Fe 1 KS D 7035 : DF2A-300-BJIS Z 3251 : DF2A-300-B

Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

80~130

4.0400

140~180

5.0400

170~240

6.0450

240~300

Conditions

HVHRCHS

30830.843

28027.140

40841.656



105

KM-100CFor hardfacing (Hv 350)

Covered Electrodes

Classifications

Description

Welding positions


Covering is high titania type for hardfacing of shaft and clutch lugs, etc.Easy slag removal and smooth bead appearance.Extremely machinable the deposited weld metal.Preheat at 150℃ and over only for cast steel, low alloy steell and high carbon steel.Redry the electrode at 70~100℃ for 30~60 minutes prior to use.

C0.19

Si0.44

Mn0.74

P0.015

S0.011

Ni0.02

Cr2.60

Mo0.01

W0.01

EN 14700:2005 : E Fe 1 KS D 7035 : DF2A-350-R JIS Z 3251 : DF2A-350-R

Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

90~120

4.0400

140~170

5.0400

190~230

6.0450

220~280



Conditions

HVHRCHS

35035.548

30029.842

43544.159



106


Covered Electrodes

Classifications

Description

Welding positions




Covering is low hydrogen type for hardfacing of fans, upper rollers, shafts and sprockets.Machining is possible in general.Hardness increases by quenching after machining.Suitable for intermetallic abrasion and moderate impact abrasion.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

C0.36

Si0.65

Mn0.74

P0.014

S0.011

Ni0.02

Cr2.00

Mo0.01

W0.01

KS D 7035 : DF2B-350-BJIS Z 3251 : DF2B-350-B

Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

90~130

4.0400

140~180

5.0400

190~240

6.0450

220~300

Conditions

HVHRCHS

35836.149

30029.842

44044.559



107

C0.38

Si0.84

Mn1.56

P0.014

S0.011

Ni0.02

Cr2.52

Mo0.03

W0.01


Covered Electrodes

Classifications

Description

Welding positions


Covering is low hydrogen type for hardfacing of idlers, rollers, bulldozer blades, sprockets, caterpillar links, crushers, dipper teeth and conveyors, etc.The deposited weld metal has typical martensite structure and high grade of hardness and ductility as welded.Machining is impossible as welded.Preheat at 150℃ and over in general.Redry the electrode at 300~400℃ for 1~2 hours prior to use.




Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

80~120

4.0400

130~170

5.0400

170~230

6.0450

220~280

Conditions

HVHRCHS

45245.560

40841.656

34835.848

44344.859

As weldedInterpass temp. 150℃ Interpass temp. 300℃

Heat treated (furnace coding)550℃x6Hr. 625℃x6Hr.


Covered Electrodes

Classifications

Description

Welding positions




Covering is low hydrogen type for hardfacing of cutter knives, dredger and mixer.The deposited weld metal has martensite structure.In the case of multilayer build-up welding base plates of hardening properties, under-laying with low hydrogen type carbon steel electrode.Preheat at 150℃ and over in general.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

C0.48

Si1.42

Mn1.36

P0.015

S0.012

Ni0.03

Cr3.65

Mo0.02

W0.01


Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

90~130

4.0400

140~170

5.0400

190~240

6.0450

220~300

108

Conditions

HVHRCHS

68859.681

58554.473

69059.781


Heat treated600℃ stress relief

KSB-2For hardfacing (High Cr, Hv 600)

Covered Electrodes

Classifications

Description

Welding positions


Covering is lime titania type for hardfacing of dies, clutch cams and metal mould.Excellent working efficiency.Excellent slag removal and restriking properties.Excellent heat-resisting, crack-resisting, wear-resisting and impact-resisting properties.In the case of multilayer build-up welding base plates of hardening properties, under-laying with low hydrogen type carbon steel electrode.Redry the electrode at 70~120℃ for 30~60 minutes prior to use.

KS D 7035 : DF3B-600-BR JIS Z 3251 : DF3B-600-BR

C0.50

Si0.09

Mn0.52

P0.021

S0.012

Ni0.04

Cr6.1

V0.4

W1.8

Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

80~100

4.0400

120~150

5.0400

160~200



109

Conditions

HVHRCHS

57053.671

58054.172

65057.878

Continuous surfacing

As weldedInterpass temp.

max.100℃Preheating 200℃,



Covered Electrodes

Classifications

Description

Welding positions




Covering is low hydrogen type for hardfacing of impellers, pump casings.The deposited weld metal has an extremely hard martensite structure.Machining is impossible as welded.Preheat at 200℃ and over.Postheat treat at about 600℃ immediately after welding.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

C0.47

Si1.45

Mn1.51

P0.017

S0.012

Ni0.03

Cr4.10

Mo0.02

W0.01

KS D 7035 : DF3C-700-BJIS Z 3251 : DF3C-700-B

Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

90~130

4.0400

140~170

5.0400

190~240

6.0450

220~300

110

Conditions

HVHRCHS

72361.183

53551.469

81064.489


Heat treated600℃ stress relief

KM-11CrFor hardfacing (Hign Cr, Hv 500)

Covered Electrodes

Classifications

Description

Welding positions


Covering is low hydrogen type for hardfacing of cold or hot shearer blade, liner pump casing generator water turbine, liner dredger.The deposited weld metal has the microstructure of martensite.Abrasion resisting properties is good at elevated temperature, so it is used for repairing of hot tool.Preheating is not necessary in general, but preheat at 150 and over only for high carbon steels and low alloy steels.Redry the electrode at 300~400℃ for 1~2 hours prior to use.


C0.40

Si1.28

Mn0.46

P0.025

S0.010

Ni0.35

Cr11.2

Mo1.40

W0.01

Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

90~110

4.0400

110~150

5.0400

150~200



111

Conditions

HVHRCHS

54051.769



Covered Electrodes

Classifications

Description

Welding positions




Covering is high titania type for hardfacing of crushers, high manganese rails, buckets, bulldozer parts and build-upof parts subject to serene impact and abrasion.The deposited weld metal has austenite structure.Extremely ductile deposited weld metal.When the base metal of 13% Mn steel is hardened, cut off the hardened zone before welding. Redry the electrode at 300~400℃ for 1~2 hours prior to use.

C0.52

Si0.30

Mn12.10

P0.018

S0.012

Ni0.02

Cr2.52

Mo0.03

W0.01

KS D 7035 : DFMA-250-B JIS Z 3251 : DFMA-250-B

Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

90~130

4.0400

140~180

5.0400

190~240

6.0450

220~300

112

Conditions

HVHRCHS

22516.933

51049.866.5

As weldedInterpass temp. 150℃ Work hardenability


Covered Electrodes

Classifications

Description

Welding positions


Hardfacing of cutter knives, shovel teeth, cutter for coal, concrete cutters and earth drills.The deposited weld metal is harder than other kinds of deposited weld metal.Extremely excellent heavy soil abrasion resistance.The deposited weld metal has tungsten carbide alloy.Machining is impossible.Preheat at 300℃ and high over.Postheat treat at about 600℃ immediately after welding.Redry the electrode at 70~120℃ for 30~60 minutes prior to use.

KS D 7035 : DFWA-700-S JIS Z 3251 : DFWA-700-S

C2.98

Si0.60

Mn1.88

P0.022

S0.014

Ni0.04

Cr0.02

Mo0.01

W48.0

Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

90~130

4.0400

120~180

5.0400

170~230



113

Conditions

HVHRCHS

82064.790

As weldedInterpass temp. max. 350℃

Conditions

HVHRCHS

580~62054~5670~75

590~61055~5673~75

As weldedContinuous surfacing Interpass temp, max. 100℃

114

KQD-600For hardfacing (High Cr&W, Hv 600)

Covered Electrodes

Description

Welding positions




Covering is low hydrogen type for hardfacing of press mould, forged metal mould, tool steel and hardened part by quenching.The microstructure of deposited weld metal has martensite.Excellent impact-resisting and wear-resisting properties at high temperature as well as room temperature.Redry the electrode at 300~400℃ for 1~2 hours prior to use.

C0.30

Si0.36

Mn0.3

P0.035

S0.009

Ni0.45

Cr9.4

Mo1.3

W12.1

Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

70~90

4.0400

100~120

5.0400

130~170

Conditions

HVHRCHS

3103143

As welded

115

Dia.Length

Amp. (A)

(mm)(mm)

F

4.0400

140~170

5.0400

190~230

C0.30

Si0.48

Mn12.4

P0.016

S0.014

Ni0.02

Cr11.8

Mo1.5

W1.8

KM-13CrMFor hardfacing (High Cr, Hv 300)

Covered Electrodes

Description

Welding positions


Covering is lime titania type for hardfacing of hot roller dies, tong punch and hot cutting knife, etc.The deposited weld metal has the microstructure of a fine carbide precipitation in austenite matrix.The high temperature hardness over 600℃ is high, so it has execllent abrasion-resistance.Machining is possible in general.Good bead appearance and restriking properties, preheating is not necessary in general, but preheat at 150℃ and over only for high carbon steels and low alloy steels.Redry the electrode at 70~120℃ for 30~60 minutes prior to use.



Conditions

HVHRCHS

25022.236

32032.245

As weldedContinuous surfacing Interpass temp. max. 150℃

116

KBH-2For hardfacing (High Cr, Hv 300)

Covered Electrodes

Description

Welding positions




Hardfacing of roller and shear used at elevated temperature, ingot tongs and forged metal mould.The deposited weld metal has the microstructure of carbide precipitation in the austenite matrix.Preheat at about 150℃ and maintain the interpass tepmerature above 150℃ for multilayer welding of low alloy steels and high carbon steel.Redry the electrode at 70~120℃ for 30~60 minutes prior to use.

C0.29

Si0.15

Mn1.25

P0.015

S0.012

Ni8.2

Cr16.4

Mo45.0

W5.4

Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

100~120

4.0400

120~150

5.0400

150~180

Conditions

HVHRCHS

520~57051~5467~71

570~62054~5671~75

640~69057~6077~81

530~58051~5467~72

280~32027~3240~45

560~60053~5571~74

As weldedContinuoussurfacing

Preheat andinterpass temp. 150℃

Heat treated(Air cooling)

117

Dia.Length

Amp. (A)

(mm)(mm)

F

2.6350

90~130

3.2400

100~150

4.0400

120~170

5.0400

150~200

C0.25

Si0.59

Mn0.95

P0.018

S0.013

Ni0.02

Cr2.5

V1.0

W4.2

KOSPEL-600HFor hardfacing (Hv 600)

Covered Electrodes

Description

Welding positions


Covering is low hydrogen type for hardfacing of metal mould, thermal cutting off machine, forging moule, dotting punch, compression tap, impact tap and axis of rotation.The microstructure of deposited weld metal has mertensite.Preheat at 200~300℃ and postheat treat at 500~600℃, if possible.Keep up interpass temperature same as preheating temperature, if possible.Redry the electrode at 300~400℃ for 1~2 hours prior to use.



350℃ X 2Hr 550℃ X 2Hr 650℃ X 2Hr 780℃ X 2Hr

Conditions

HVHRCHS

760~82063~6586~90

700~75060~6281~85

As weldedPreheat and interpass

tem. max 300℃

118

KOSPEL-800RFor hardfacing (Hv 800)

Covered Electrodes

Description

Welding positions




Covering is lime titania type for hardfacing of conveyor screw, caterpillar, crusher and dredger teeth.Excellent friction and impact abrasion resisting properties.Preheat at 200℃ and postheat treat at 500~600℃.Redry the electrode at 70~120℃ for 30~60 minutes prior to use.

C0.38

Si0.42

Mn0.32

P0.025

S0.015

Ni0.04

Cr5.5

V0.8

W2.5

Dia.Length

Amp. (A)

(mm)(mm)

F

2.6350

80~140

3.2350

90~160

4.0400

120~180

5.0400

140~200


119

C0.06

Si0.76

Mn4.68

P0.028

S0.012

Ni9.3

Cr18.5

Mo0.6

Cu0.3

KST-307-15For stainless steel (19%Cr-9%Ni-5%Mn)

Covered Electrodes

Classifications

Description

Welding positions


Welding of dissimilar steel such as austenitic manganese steel to carbon steel forgings. Joining work-hardenable steels, armour plate, austenitic manganese steels, and heat-resisting steels for temperatures up to 350℃ and dissimilar metals. Hardfacing of hot working tools, stainless valve steels and carbon steel items that must possess abrasion resistance in cold working.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

AWS A5.4-06 : E307-15 KS D 7014 : E307-15 JIS Z 3221 : ES307-15


Sizes available and recommended currents (DC +) Dia.

Length

Amp.(A)

(mm)(mm)

FV·OH

2.6300

55~8045~60

3.2350

80~12070~90

4.0350

100~15090~130

5.0350

140~180-

AW : As-Welded

AWS A5.4JIS Z3221Example

Y.S (0.2%OS)(MPa)

min. 330min. 380

470

T.S(MPa)

min. 590min. 590

650

El.(%)

min. 30min. 25

48

Remarks

AW

120

AW : As-Welded

Approvals

CE

KST-308-15For stainless steel (18%Cr-8%Ni)

Covered Electrodes

Classifications

Description

Welding positions




Covering is lime titania type for welding of 18%Cr-8%Ni stainless steel. (AISI 301, 302, 304, 308)Easy welding performance without hardening brittleness because of austenitic structure of thedeposited weld metal.Good heat resistance and corrosion resistance.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.06

Si0.38

Mn1.54

P0.025

S0.016

Ni9.6

Cr20.5

Mo0.2

Cu0.3

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

40~5035~45

2.6350

50~8040~60

3.2350

80~11070~100

4.0350

110~15090~130

5.0350

140~180-

EN 1600:1997 : E 19 9 B 22AWS A5.4-06 : E308-15

KS D 7014 : E308-15JIS Z 3221 : ES308-15


Y.S (0.2%OS)(MPa)

min. 400min. 350

480

T.S(MPa)

min. 550min. 550

600

El.(%)

min. 35min. 30

38

Remarks

AW

121

AW : As-Welded

KST-308For stainless steel (18%Cr-8%Ni)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is lime titania type for welding of 18%Cr-8%Ni stainless steel. (AISI 301, 302, 304, 308)Easy welding performance without hardening brittleness because of austenitic structure of the deposited weld metal.Good heat resistance and corrosion resistance.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.05

Si0.78

Mn1.22

P0.024

S0.018

Ni9.3

Cr19.3

Mo0.2

Cu0.3

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

40~5035~45

2.6350

50~8040~60

3.2350

80~11070~100

4.0350

110~15090~130

5.0350

140~180-

EN 1600:1997 : E 19 9 R 12 AWS A5.4-06 : E308-16

KS D 7014 : E308-16JIS Z 3221 : ES308-16

Others : CWB, CE

ABS

E308-16

BV

UP

DNV

308

GL

4306

KR

RD308


Y.S (0.2%OS)(MPa)

min. 400min. 350

470

T.S(MPa)

min. 550min. 550

620

El.(%)

min. 35min. 30

45

Remarks

AW

122

CE

KST-308L-15For stainless steel (Low C, 18%Cr-8%Ni)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is lime titania type for welding of 18%Cr-8%Ni stainless steel. (AISI 301, 302, 304, 308)Excellent welding dfficicncy because of high deposition rate.Remove water, rust, oil and all foreign matters from the groove prior to welding.Preheating is not necessary in general.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.03

Si0.41

Mn1.67

P0.022

S0.015

Ni9.5

Cr20.6

Mo0.2

Cu0.3

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

40~5035~45

2.6350

50~8040~60

3.2350

90~13070~90

4.0350

110~15090~130

5.0350

140~180-

EN 1600:1997 : E 19 9 L B 22AWS A5.4-06 : E308L-15

KS D 7014 : E308L-15JIS Z 3221 : ES308L-15

AW : As-Welded


Y.S (0.2%OS)(MPa)

min. 400min. 320

430

T.S(MPa)

min. 520min. 510

590

El.(%)

min. 35min. 30

44

Remarks

AW

123

AW : As-Welded

KST-308LFor stainless steel (Low C, 18%Cr-8%Ni)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is lime titania type for welding of 18%Cr-8%Ni stainless steel. (AISI 301, 302, 304, 308)Excellent welding dfficicncy because of high deposition rate.Remove water, rust, oil and all foreign matters from the groove prior to welding.Preheating is not necessary in general.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.03

Si0.80

Mn0.84

P0.023

S0.016

Ni9.6

Cr19.3

Mo0.2

Cu0.3

EN 1600:1997 : E 19 9 L R 12 AWS A5.4-06 : E308L-16

KS D 7014 : E308L-16JIS Z 3221 : ES308L-16

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

40~5035~45

2.6350

55~8040~60

3.2350

90~13070~90

4.0350

110~15090~130

5.0350

140~180


Y.S (0.2%OS)(MPa)

min. 400min. 320

430

T.S(MPa)

min. 520min. 510

600

El.(%)

min. 35min. 30

44

Remarks

AW

Others : CWB, TUV, CE

ABS

E308L-16

BV

UP

GL

4306

LR

304Lm. .

124

CE

KST-308HFor stainless steel (High C, 18%Cr-8%Ni)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is lime titania type for welding of 18%Cr-8%Ni stainless steel and it is recommended to be usefor high temperature(about 600℃) service. (STS 304H, 307H)Excellent creep resistance at elevated temperature.Good heat resistance and corrosion resistance.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.06

Si0.75

Mn0.85

P0.025

S0.016

Ni9.3

Cr19.6

Mo0.2

Cu0.3

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6350

50~8040~70

3.2350

70~11060~90

4.0400

110~15090~130

5.0400

140~180-

EN 1600:1997 : E 19 9 H R 12AWS A5.4-06 : E308H-16

JIS Z 3221 : ES308H-16

AW : As-Welded


Y.S (0.2%OS)(MPa)

min. 400min. 350

480

T.S(MPa)

min. 550min. 550

600

El.(%)

min. 35min. 30

38

Remarks

AW

125

AW : As-Welded

KST-308MoFor stainless steel (18%Cr-8%Ni-2.5%Mo)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is lime titania type for butt and fillet welding of ASTM CF8M stainless steel castings. Used for welding wrought materials such as Type 316L stainless when increased ferrite is desired.Good heat resistance and corrosion resistance.Welds are carefully cleaned using a stainless steel wire brush.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

CE

C0.05

Si0.36

Mn1.42

P0.024

S0.016

Ni9.4

Cr19.8

Mo2.1

Cu0.3

EN 1600:1997 : E 20 10 3 R 12AWS A5.4-06 : E308Mo-16

KS D 7014 : E308Mo-16JIS Z 3221 : ES308Mo-16

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6300

50~8040~70

3.2350

70~11060~90

4.0350

110~15090~130

5.0350

140~180-


Y.S (0.2%OS)(MPa)

min. 400min. 400

580

T.S(MPa)

min. 550min. 620

700

El.(%)

min. 35min. 20

20

Remarks

AW

126

AW : As-Welded

KST-309-15For stainless steel (Dissimilar joint welding)

Covered Electrodes

Classifications

Description

Welding positions




Covering is lime titania type for welding of 22%Cr-12%Ni stainless steel and heat-resisting castings, clad side of type 304 clad steels.As the deposited weld metal contains ferrite in austenitic structure, its crack resistance is good.Good heat resistance and corrosion resistance.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.05

Si0.36

Mn1.83

P0.029

S0.011

Ni13.3

Cr24.5

Mo0.2

Cu0.3

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

40~5035~45

2.6350

50~8045~60

3.2350

80~11070~90

4.0350

110~15090~130

5.0350

140~180-



Y.S (0.2%OS)(MPa)

min. 400min. 350

450

T.S(MPa)

min. 550min. 550

590

El.(%)

min. 30min. 25

40

Remarks

AW

127

KST-309For stainless steel (Dissimilar joint welding)

Covered Electrodes

Classifications

Description

Welding positions




Covering is lime titania type for welding of 22%Cr-12%Ni stainless steel and heat-resisting castings, clad side of type 304 clad steels. Welding of dissimilar steels such as Cr-Mo steel or carbon steel to stainless steel.As the deposited weld metal contains ferrite in austenitic structure, its crack resistance is good.Good heat resistance and corrosion resistance.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.06

Si0.72

Mn1.36

P0.028

S0.012

Ni12.6

Cr23.6

Mo0.2

Cu0.3

AWS A5.4-06 : E309-16KS D 7014 : E309-16JIS Z 3221 : ES309-16

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

40~5035~45

2.6350

50~8045~60

3.2350

80~11070~90

4.0350

110~15090~130

5.0350

140~180-

AW : As-Welded


Y.S (0.2%OS)(MPa)

min. 400min. 350

490

T.S(MPa)

min. 550min. 550

610

El.(%)

min. 30min. 25

38

Remarks

AW

Approvals

Others : CWB

ABS

E309-16

BV

UP

DNV

309

GL

4332

KR

RD309

LR

SS/CMn m

128

KST-309L-15For stainless steel (Dissimilar joint welding)

Covered Electrodes

Classifications

Description

Welding positions




Covering is lime titania type for welding of 22%Cr-12%Ni stainless steel and heat-resisting castings, clad side of type 304 clad steels. Welding of dissimilar steels such as Cr-Mo steel or carbon steel to stainless steel.As its deposited weld metal has austenitic structure, with suitable ferrite, crack resistance is good and intergranular corrosion resistance is superior to that of E309 type.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.03

Si0.40

Mn1.92

P0.026

S0.014

Ni13.2

Cr24.3

Mo0.2

Cu0.3

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

30~5025~45

2.6350

50~8045~60

3.2350

80~11070~90

4.0350

110~15090~130

5.0350

140~180-

EN 1600:1997 : E 23 12 L B 22AWS A5.4-06 : E309L-16

KS D 7014 : E309L-16JIS Z 3221 : ES309L-16

AW : As-Welded


Y.S (0.2%OS)(MPa)

min. 400min. 320

470

T.S(MPa)

min. 550min. 510

590

El.(%)

min. 30min. 25

39

Remarks

AW

Approvals

CE

129

AW : As-Welded

KST-309LFor stainless steel (Dissimilar joint welding)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is lime titania type for welding of 22%Cr-12%Ni stainless steel and heat-resisting castings, clad side of type 304 clad steels. Welding of dissimilar steels such as Cr-Mo steel or carbon steel to stainless steel.As its deposited weld metal has austenitic structure, with suitable ferrite, crack resistance is good and intergranular corrosion resistance is superior to that of E309 type.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.03

Si0.71

Mn1.34

P0.027

S0.013

Ni12.6

Cr23.7

Mo0.2

Cu0.3

EN 1600:1997 : E 23 12 L R 12 AWS A5.4-06 : E309L-16

KS D 7014 : E309L-16JIS Z 3221 : ES309L-16

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

30~5025~45

2.6350

50~8045~60

3.2350

80~11070~90

4.0350

110~15090~130

5.0350

140~180


Y.S (0.2%OS)(MPa)

min. 400min. 320

480

T.S(MPa)

min. 520min. 510

600

El.(%)

min. 30min. 25

40

Remarks

AW

Others : CWB, CE

ABS

E309L-16

130

KST-309Mo-15For stainless steel (Dissimilar joint welding)

Covered Electrodes

Classifications

Description

Welding positions




Build-up welding of Cr-Mo steel or carbon steel. Welding of AISI(SUS)316 clad steel or dissimilar steels.Excellent crack resistance especially in the welding of dissimilar steels such as stainless steel to carbon steel.It is only used in the direct current condition.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.06

Si0.35

Mn1.84

P0.027

S0.012

Ni12.4

Cr22.2

Mo2.4

Cu0.3

AWS A5.4-06 : E309Mo-15 KS D 7014 : E309Mo-15 JIS Z 3221 : ES309Mo-15

AW : As-Welded


Y.S (0.2%OS)(MPa)

min. 400min. 320

490

T.S(MPa)

min. 550min. 550

630

El.(%)

min. 30min. 25

36

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

30~5025~45

2.6350

50~8050~60

3.2350

80~11070~90

4.0350

110~14090~130

5.0350

140~180-

131

AW : As-Welded

KST-309MoFor stainless steel (Dissimilar joint welding)

Covered Electrodes

Classifications

Description

Welding positions




Build-up welding of Cr-Mo steel or carbon steel. Welding of AISI(SUS)316 clad steel or dissimilar steels.Excellent crack resistance especially in the welding of dissimilar steels such as stainless steel to carbon steel.It is only used in the direct current condition.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.06

Si0.35

Mn1.84

P0.027

S0.012

Ni12.4

Cr22.2

Mo2.4

Cu0.3

AWS A5.4-06 : E309Mo-16 KS D 7014 : E309Mo-16 JIS Z 3221 : ES309Mo-16

Approvals

DNV

309Mo


Y.S (0.2%OS)(MPa)

min. 400min. 320

500

T.S(MPa)

min. 550min. 550

630

El.(%)

min. 30min. 25

34

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6300

50~7040~60

3.2350

80~11070~90

4.0350

110~14090~130

5.0350

140~170-

132

AW : As-Welded

Others : CE

KST-309LMoFor stainless steel (Dissimilar joint welding)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Build-up welding of AISI(SUS)316 clad steel or dissimilar steels.Excellent crack resistance especially in the welding of dissimilar steels such as stainless steel to carbon steel.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

KR

RD309MoL

C0.03

Si0.76

Mn1.78

P0.026

S0.013

Ni13.1

Cr23.2

Mo2.4

Cu0.3

EN 1600:1997 : E 23 12 2 L R 12 AWS A5.4-06 : E309LMo-16

KS D 7014 : E309MoL-16JIS Z 3221 : ES309LMo-16


Y.S (0.2%OS)(MPa)

min. 400min. 350

490

T.S(MPa)

min. 520min. 550

650

El.(%)

min. 30min. 25

35

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

30~5525~45

2.6350

55~8045~60

3.2350

90~12070~90

4.0350

110~14090~130

5.0350

140~180-

133

KST-310For stainless steel (25%Cr-20%Ni)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is lime titania type for welding of AISI(SUS) 310S, SCS 18 and clad side of 18%Cr-8%Ni stainless clad steel.The deposited weld metal has perfect austenitic structure.Good mechanical property and heat resistance of the depodited weld metal.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

CWB, CE

C0.11

Si0.40

Mn1.86

P0.025

S0.013

Ni20.8

Cr25.6

Mo0.2

Cu0.3

EN 1600:1997 : E 25 20 R 12 AWS A5.4-06 : E310-16

KS D 7014 : E310-16JIS Z 3221 : ES310-16

AW : As-Welded


Y.S (0.2%OS)(MPa)

min. 400min. 350

490

T.S(MPa)

min. 550min. 550

620

El.(%)

min. 30min. 20

40

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

30~5025~45

2.6350

50~8045~60

3.2350

80~11070~90

4.0350

110~14090~130

5.0350

140~180-

134

AW : As-Welded

ClassificationsEN 1600:1997 : E 29 9 R 12 AWS A5.4-06 : E312-16

KS D 7014 : E312-16 JIS Z 3221 : ES312-16

KST-312For stainless steel (Cladding or Dissimilar joint)

Covered Electrodes

Description

Welding positions




Approvals

CE

Covering is lime titania type for welding of 29%Cr-9%Ni type cast steels and difficult to weld steels. Joint welding and hardfacing of stainless steel and heat resisting steels.Good crack resistance because of extremely much quantity of ferrite of the deposited weld metal.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.08

Si0.45

Mn1.30

P0.028

S0.012

Ni8.5

Cr29.1

Mo0.2

Cu0.3


Y.S (0.2%OS)(MPa)

min. 400min. 450

510

T.S(MPa)

min. 660min. 650

760

El.(%)

min. 22min. 15

25

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6300

40~8035~75

3.2350

70~11070~90

4.0350

110~14080~120

5.0350

140~180-

135

AW : As-Welded

TENSILE WELDFor stainless steel (Cladding or Dissimilar joint)

Covered Electrodes

Description

Welding positions




Covering is lime titania type for welding of 29%Cr-9%Ni type cast steels and difficult to weld steels. Joint welding and hardfacing of stainless steel and heat resisting steels.Good crack resistance because of extremely much quantity of ferrite of the deposited weld metal.Good usability and weldability.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.08

Si0.95

Mn1.48

P0.032

S0.015

Ni8.6

Cr29.8

Mo0.2

Cu0.3

Example

Y.S (0.2%OS)(MPa)

520

T.S(MPa)

770

El.(%)

24

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6300

40~8035~75

3.2350

70~10070~100

4.0350

110~14090~130

5.0350

140~180-

136

AW : As-Welded

Approvals

CE

ClassificationsEN 1600:1997 : E 19 12 2 B 22 AWS A5.4-06 : E316-15

KS D 7014 : E316-15JIS Z 3221 : ES316-15

KST-316-15For stainless steel (18%Cr-12%Ni-Mo)

Covered Electrodes

Description

Welding positions




Covering is lime titania type for welding of 18%Cr-12%Ni-Mo stainless steel. (AISI 316) or dissimilar steels.Especially suitable for flat and horizontal fillet welding. Excellent corrosion resistance against sulphurous acid, phosphoric acid and acetic acid.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.06

Si0.39

Mn1.18

P0.029

S0.013

Ni11.5

Cr18.9

Mo2.3

Cu0.3


Y.S (0.2%OS)(MPa)

min. 400min. 350

470

T.S(MPa)

min. 520min. 550

580

El.(%)

min. 30min. 25

41

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

40~5035~45

2.6350

50~7045~60

3.2350

80~12070~90

4.0350

110~14090~130

5.0350

140~170-

137

AW : As-Welded

KST-316For stainless steel (18%Cr-12%Ni-Mo)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is lime titania type for welding of 18%Cr-12%Ni-Mo stainless steel. (AISI 316) or dissimilar steels.Especially suitable for flat and horizontal fillet welding.Excellent corrosion resistance against sulphurous acid, phosphoric acid and acetic acid.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

Others : CWB, CE

C0.06

Si0.73

Mn1.18

P0.028

S0.012

Ni12.5

Cr18.3

Mo2.3

Cu0.3

EN 1600:1997 : E 19 12 2 R 12 AWS A5.4-06 : E316-16

KS D 7014 : E316-16JIS Z 3221 : ES316-16


Y.S (0.2%OS)(MPa)

min. 400min. 350

460

T.S(MPa)

min. 520min. 550

590

El.(%)

min. 30min. 25

42

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

30~5025~45

2.6350

50~8045~60

3.2350

80~11070~90

4.0350

110~14090~130

5.0350

140~180-

ABS

E316-16

BV

UP

GL

4435

138

CE

KST-316L-15For stainless steel (Low C, 18%Cr-12%Ni-Mo)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is lime titania type for welding of 18%Cr-12%Ni-Mo stainless stees, austenitic stainless steels which are required and the place where heat treatment after welding is impossible.Good Crack resistance and usability.As low carbon welded metal can be obtained, intergranular corrosion resistance is superior to that of E316 type.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.03

Si0.40

Mn1.21

P0.025

S0.022

Ni11.4

Cr19.2

Mo2.5

Cu0.3

EN 1600:1997 : E 19 12 3 L B 22 AWS A5.4-06 : E316L-15

KS D 7014 : E316L-15JIS Z 3221 : ES316L-15

AW : As-Welded


Y.S (0.2%OS)(MPa)

min. 400min. 320

470

T.S(MPa)

min. 490min. 510

580

El.(%)

min. 30min. 25

39

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

40~5035~45

2.6350

55~7045~60

3.2350

80~11070~90

4.0350

110~15090~130

5.0350

140~170-

139

AW : As-Welded

KST-316LFor stainless steel (Low C, 18%Cr-12%Ni-Mo)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is lime titania type for welding of 18%Cr-12%Ni-Mo stainless steel. (AISI 316) or dissimilar steels.Especially suitable for flat and horizontal fillet welding.Excellent corrosion resistance against sulphurous acid, phosphoric acid and acetic acid.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.03

Si0.72

Mn1.08

P0.028

S0.013

Ni12.5

Cr18.4

Mo2.5

Cu0.3

EN 1600:1997 : E 19 12 3 L R 12 AWS A5.4-06 : E316L-16

KS D 7014 : E316L-16JIS Z 3221 : ES316L-16


Y.S (0.2%OS)(MPa)

min. 400min. 320

440

T.S(MPa)

min. 490min. 510

570

El.(%)

min. 30min. 25

43

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

40~5035~45

2.6350

55~7045~60

3.2350

80~11070~90

4.0350

120~15090~130

5.0350

140~180-

Others : CWB, TUV, CE

ABS

E316L-16

BV

UP

DNV

316L

GL

4435

KR

RD316L

LR

316Lm. .

140

KST-317For stainless steel (18%Cr-12%Ni-Mo)

Covered Electrodes

Classifications

Description

Welding positions




Covering is lime titania type for welding of AISI 317 or dissimilar steels such as carbon steel to stainlesssteels.Good weldability and performance.Reduce the susceptibility of pitting.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.06

Si0.74

Mn1.20

P0.026

S0.017

Ni12.3

Cr18.5

Mo3.2

Cu0.3

AWS A5.4-06 : E317-16 KS D 7014 : E317-16JIS Z 3221 : ES317-16

AW : As-Welded


Y.S (0.2%OS)(MPa)

min. 400min. 350

490

T.S(MPa)

min. 550min. 550

580

El.(%)

min. 30min. 20

43

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

40~6035~45

2.6350

55~9045~60

3.2350

80~11070~90

4.0350

110~15090~130

5.0350

140~180-

141

AW : As-Welded

KST-317LFor stainless steel (Low C, 18%Cr-12%Ni-Mo)

Covered Electrodes

Classifications

Description

Welding positions




Covering is lime titania type for welding of 18%Cr-12%Ni-3%Mo which requires excellent corrosion resistance to sulfuric acid, solutions containing these salts and much hot organic acids such as formic acid.Good weldability and performance.Reduce the susceptibility of pitting.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.03

Si0.75

Mn1.24

P0.025

S0.016

Ni12.4

Cr18.6

Mo3.3

Cu0.3

EN 1600:1997 : E 19 13 4 N L R12AWS A5.4-06 : E317L-16

KS D 7014 : E317L-16JIS Z 3221 : ES317L-16


Y.S (0.2%OS)(MPa)

min. 400min. 350

450

T.S(MPa)

min. 520min. 550

570

El.(%)

min. 30min. 25

44

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

40~6035~45

2.6350

55~9045~60

3.2350

80~11070~90

4.0350

110~15090~130

5.0350

140~180-

Approvals

CE

142

AW : As-Welded

KST-318For stainless steel (18%Cr-12%Ni-2%Mo-Nb)

Covered Electrodes

Classifications

Description

Welding positions




Covering is lime titania type for welding of AISI 318, 316, 316L stainless steel.The deposited weld metal is highly resistant to pitting and general type of corrosion.Insensitive to intergranular corrosion because of Nb.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.05

Si0.76

Mn1.32

P0.022

S0.015

Ni11.9

Cr18.5

Mo2.3

Cu0.7



Y.S (0.2%OS)(MPa)

min. 400min. 350

500

T.S(MPa)

min. 520min. 550

630

El.(%)

min. 30min. 20

38

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

40~6035~45

2.6350

50~8045~60

3.2350

80~11060~90

4.0350

120~15090~130

5.0350

140~180-

143

AW : As-Welded

KST-347For stainless steel (18%Cr-8%Ni-Nb)

Covered Electrodes

Classifications

Description

Welding positions




Covering is lime titania type for welding of AISI 304L, 321, 347 stainless steel and the place where heat treatment after welding is impossible.Excellent intergranular corrosion resistance.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.06

Si0.42

Mn1.98

P0.029

S0.012

Ni9.5

Cr19.9

Mo0.2

Nb0.6

EN 1600:1997 : E 19 9 Nb R 12 AWS A5.4-06 : E347-16

KS D 7014 : E347-16JIS Z 3221 : ES347-16

Approvals

CE


Y.S (0.2%OS)(MPa)

min. 400min. 350

460

T.S(MPa)

min. 520min. 550

620

El.(%)

min. 30min. 25

42

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

40~6035~45

2.6350

50~7045~60

3.2350

70~11065~90

4.0350

100~15090~130

5.0350

140~180-

144

AW : As-Welded

KST-347LFor stainless steel (Low C, 18%Cr-8%Ni-Nb)

Covered Electrodes

Classifications

Description

Welding positions




Covering is lime titania type for welding of AISI 304L, 321, 347 stainless steel and the place where heat treatment after welding is impossible.Excellent intergranular corrosion resistance.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.03

Si0.46

Mn1.68

P0.028

S0.011

Ni9.8

Cr19.4

Mo0.2

Nb0.7

KS D 7014 : E347L-16 JIS Z 3221 : ES347L-16

JIS Z 3221Example

Y.S (0.2%OS)(MPa)

min. 350440

T.S(MPa)

min. 510600

El.(%)

min. 3039

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.0250

40~6035~45

2.6350

55~8045~60

3.2350

80~11070~90

4.0350

110~14090~130

5.0350

140~170-

145

PWHT : 750℃x1Hr.

KST-410For stainless steel (13%Cr, Hardfacing)

Covered Electrodes

Classifications

Description

Welding positions




Covering is lime titania type for welding of 13%Cr steel and surfacing of the part where require cavitation or corrosion resistance is required.Excellent oxidation corrosion and abrasion resistance of the deposited weld metal.Preheat at 100~250℃ and postheat treat at 700~800℃ because of high self-hardening property of the deposited weld metal.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.08

Si0.70

Mn0.76

P0.030

S0.012

Ni0.2

Cr12.1

Mo0.2

Cu0.3

EN 1600:1997 : E 13 R 12 AWS A5.4-06 : E410-16

KS D 7014 : E410-16JIS Z 3221 : ES410-16

Approvals

CE

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6300

60~9045~60

3.2350

80~11070~90

4.0350

110~15090~130

5.0350

150~170-


Y.S (0.2%OS)(MPa)

min. 400min. 250

400

T.S(MPa)

min. 450min. 450

560

El.(%)

min. 20min. 15

24

Remarks

PWHT

146

PWHT : 780℃x2Hr.

KST-430For stainless steel (17%Cr, Hardfacing)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

CE

Covering is lime titania type for welding of 17%Cr stainless steel or AISI 403, 405Preheat at 200~300℃ and postheat treat at 700~800℃.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

C0.07

Si0.42

Mn0.75

P0.028

S0.009

Ni0.2

Cr17.4

Mo0.2

Cu0.3

EN 1600:1997 : E 17 R 12 AWS A5.4-06 : E430-16

KS D 7014 : E430-16JIS Z 3221 : ES430-16


Y.S (0.2%OS)(MPa)

min. 400min. 300

380

T.S(MPa)

min. 450min. 450

530

El.(%)

min. 20min. 15

27

Remarks

PWHT

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6300

55~7545~60

3.2350

80~10070~90

4.0350

110~14090~130

5.0350

140~170-

147

AW : As-Welded

KST-2209For duplex stainless steel (22%Cr-9%Ni-Mo)

Covered Electrodes

Classifications

Description

Welding positions




Approvals

Covering is lime titania type for welding of 22%Cr-9%Ni-3%Mo duplex stainless steels, the principalapplicationsare chemical plant and shipbuilding as well as nuclear plant industries. (UNS S31803)Excellent pitting corrosion resistance and stress corrosion cracking resistance.Please perform welding with selecting proper heat input according to the required mechanical properties.Redry the electrode at 250~350℃ for 30~60 minutes prior to use.

CE

EN 1600:1997 : E 22 9 3 N L R 12 AWS A5.4-06 : E2209-16

JIS Z 3221 : ES2209-16

C0.02

Si0.62

Mn0.80

P0.025

S0.011

Ni9.3

Cr21.9

Mo3.2

N0.18


Y.S (0.2%OS)(MPa)

min. 400min. 450

550

T.S(MPa)

min. 690min. 550

780

El.(%)

min. 20min. 20

24

Remarks

AW

Dia.Length

Amp.(A)

(mm)(mm)

FV·OH

2.6300

50~8040~60

3.2350

80~11070~100

4.0350

110~15090~130

5.0350

140~180-

148

Hv HRC

280 27.1

Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

110~140

4.0400

150~190

5.0400

190~220

KL-100For cast iron

Covered Electrodes

Classifications

Description

Welding positions




Covering is graphite type for repairing of all kind of cast iron product cavity filling.Preheat at minimum 200℃. The temperature to be applied varies in accordance with kind, shape and size of base metal.Gradual cooling is recommended after welding.Redry the electrode at 70~120℃ for 30~60 minutes prior to use.

C3.16

Si6.27

Mn0.42

P0.015

S0.006

FeRem.

KS D 7008 : DFCCI JIS Z 3252 : DFCCI

149

Dia.Length

Amp. (A)

(mm)(mm)

F

2.6350

60~90

3.2350

90~130

4.0400

130~180

5.0400

150~200

KCF-50For cast iron

Covered Electrodes

Classifications

Description

Welding positions


Covering is graphite type for repairing of all kind of cast iron product.Stable arc, easy slag removal aqnd beautiful bead appearance.Preheat at minimum 200℃. The temperature to be applied varies in accordance with kind, shape and size of base metal.Gradual cooling is recommended after welding.Redry the electrode at 70~120℃ for 30~60 minutes prior to use.

AWS A 5.15-90 : Est


T.S El. Hardness(MPa) (%) (Hv)

490 33 200


C1.68

Si0.50

Mn0.35

P0.021

S0.006

FeRem.

150

HV

180~210

HardnessHB

171~200

HS

26~30

KFN-50For cast iron

Covered Electrodes

Classifications

Description

Welding positions




Covering is graphite type for joining of spheroidal graphit cast iron or repairing of cast iron products such as cylinder covers, motor beds, casings and gears.Good crack resistance and mechanical properties.Preheat at 150~300℃. The temperature to be applied varies in accordance with kind, shape and size of base metal.Redry the electrode at 70~120℃ for 30~60 minutes prior to use.

C0.80

Si0.36

Mn0.45

P0.008

S0.002

Ni55.5

Cu0.05

FeRem.

Al0.05

EN ISO 1071:2003 : E C NiFe-Cl 1AWS A 5.15-90 : ENiFe-CI

KS D 7008 : DFCNiFeJIS Z 3252 : DFCNiFe

T.S(MPa)

550

Dia.Length

Amp. (A)

(mm)(mm)

F

2.6300

60~90

3.2350

80~120

4.0350

120~150

5.0550

140~190

Approvals

CE

151

Dia.Length

Amp. (A)

(mm)(mm)

F

2.6300

60~90

3.2350

70~110

4.0350

110~130

5.0550

130~150

C0.55

Si0.40

Mn0.35

P0.009

S0.001

NiRem.

Cu0.05

Fe0.85

Al0.05

KSN-100For cast iron

Covered Electrodes

Classifications

Description

Welding positions


Covering is graphite type for repairing and joining of various kinds of cast iron products such as cylinder covers, motor beds, casings and gears or repairing co cast iron, alloy cast iron and malleable cast iron.Easily machinable deposited weld metal. Chip off base metal completely at the repairing part.Preheat at 150~300℃. The temperature to be applied varies in accordance with kind, shape and size of base metal.Redry the electrode at 70~120℃ for 30~60 minutes prior to use.

EN ISO 1071:2003 : E C Ni-Cl 1AWS A 5.15-90 : ENi-CI

KS D 7008 : DFCNiJIS Z 3252 : DFCNi



HV

160~190

HardnessHB

152~181

HS

24~28

T.S(MPa)

420

Approvals

CE

152

Removal of protrusion

Removal of down gate, cross gate, etc.

CUTTING RODFor special purpose (Cutting operation)

Covered Electrodes

Description

Illustration


Cutting of carbon steels, cast irons, stainless steels and nonferrous alloys, etc.Designed for high efficiency in cutting of all kinds of steel.Quiet and stable arc.Excellent usability.When the electrodes have absorbed moisture, redry the electrode at 70~80℃ for 30 minutes prior to use.

Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

150~130

4.0400

230~180

5.0400

300~400

153

Dia.Length

Amp. (A)

(mm)(mm)

F

3.2350

150~180

4.0400

230~260

5.0400

270~320

GOUGING RODFor special purpose (Gouging operation)

Covered Electrodes

Description

Gouging hints

Gouging of carbon steels, cast irons, stainless steels and nonferrous alloy, etc.Designed for high efficiency in gouging of all kinds of steel.Operated surface is very clean.Suitable for rapid removal of unnecessary parts.When the electrodes have absorbed moisture, redry the electrode at 70~80℃ for 30 minutes prior to use.


In gouging operation worker must maintain 10~30°between the electrode and base plate.

10~30。

Gouging direction

3 2 1