Multinuclear solid state NMR studies of the Guest-Mediated
Zeolite Crystallization
Son-Jong Hwang1 and S.I. Zones2
1Division of Chemistry and Chemical Engineering, California Institute of Technology, Pasadena, CA 91125, USA.
2Chevron Research and Technology Company, P.O. Box 1627, Richmond, CA 94802, USA.
I. IntroductionThe present work focuses on the understanding of the mechanistic difference in the process of zeolitecrystallization for a system that the substituting trivalent metal ions determine the product selectivity. The synthetic route employs boron or aluminum metal ions and results in the formation of two different zeolitestructures, SSZ-42 (IFR) and beta (BEA) zeolite, respectively, when all the other components remain the same. IFR structure type has 1D pore system with 12 MR while BEA structure has intersecting 12 MR in 3D. Understanding of the mechanistic difference for boron vs aluminum should provide us with better prediction of product selection in the discovery of new zeolites. Multinuclear NMR methods were employed to follow the structural changes around the organo-cationguest molecule (N-Benzyl DABCO) as a function of crystallization time as well as the changes after calcination. The powder recovered at each point of reaction time frame was also analyzed with XRD, NMR, and elemental analysis.
1Zones, et al. Chem. Eur. J. 1998, 4, 1312
C2/m, 1D12 MR, 8T1-4
P4122, 3D12 MR, 9 sites
-100 -110 -120 -130ppm
IFR
*BEA
29Si NMR of pure slica zeolites
II. ExperimentalTable 1. Reagents and synthesis conditions used in thecomparative runs of SSZ-42 and beta ( 150° C, 43 rpm)
Ratio SSZ-42 RUN BETA RUNN-Benzyl-DABCO/SiO2 0.20 0.20NaOH/SiO2 0.10 0.10SiO2/Al2O3 ( SAR) 0.00 35*SiO2/B2O3 35* 0.00NET OH- /SiO2 0.30 0.30H2O / SiO2 44* 44
* Except when values have been varied in separate seriesTable 2. Elemental analyses for recovered run products (B series )
Sample # RUN TIME XRD B1 0 days Amorphous B2 1 day Amorphous B3 2 days 20% SSZ-42 B4 3 days SSZ-42 B5 6 days SSZ-42
Table 3. Elemental analyses for recovered run products (Al series )Sample # RUN TIME XRD A1 0 days Amorphous A2 1 days Amorphous A3 7 days Amorphous A4 9 days beta
Figure 1. Structure of the SDA(N-Benzyl-DABCO) used in this work.
NN +
Sample Preparations
NMR Solid state NMR spectra were obtained using Bruker DSX 200 (Bo=4.7 T) and DSX 500 (Bo=11.7 T) spectrometers and a 4mm CPMAS probe. Detail NMR operating parameters are given in the result section.
III. Results and discussionCrystallization : As were compiled in Table 1, for the two synthesis systems the borosilicate (BSSZ-42) reaction crystallizes much more rapidly to form SSZ-42 while aluminosilicate(Al-Beta) starts crystallizing Beta after 7 days.
0 1 2 3 4crystallization period (days)
0.0300
0.0400
0.0500
0.0600
0.0700
11B
con
cent
ratio
n [M
]
fully crystallized
mixture
amorphous
Figure 2. 11B concentration in supernatant
Fig. 2 shows the change of 11B concentrationof the supernatant during the crystallizationperiod.
Crystallization takes place with incorporationof boron in the framework. 11B MAS NMRspectra also measure the maturity of thecrystallization process. About half of theboron remains unreacted.
-60 -70 -80 -90 -100 -110 -120 -130 -140ppm
B2
B3
B4
B5
BSiO2 (a)
BSiO2(a)/BSSZ-42
BSSZ-42
BSSZ-42
B1 BSiO2 (a)
-60 -70 -80 -90 -100 -110 -120 -130 -140ppm
A1
A3
A4
5 0 -5 -10ppm
0.02
0.16
B wt %0.50
0.09
0.47
B3
B2
B1
B5
B4
SSZ-42 Al-beta
29Si
11B 27Al
80 70 60 50 40 30 20 10 0 -10ppm
A1
A2
A3
A4
NMR of as prepared powders: 29Si NMR and NMR on trivalent metals of powder materials recoveredat each time point eminently reveal the conversion to crystalline phases from amorphous phases. Note that 29Si NMR of powders before any thermal treatment (0 day) even shows difference when the metals
40 30 20 10 0 -10 -20 -30 -40 -50 -60ppm
B2
B3
B4
B5
40 30 20 10 0 -10 -20 -30 -40 -50 -60ppm
A1
A2
A4
A3
23Na
are different. The beta structure starts with much more of Q3 site (~-100 ppm) compared to SSZ-42 structure. Second, the kinetics of metal incorporation is different. Boron gets inserted into the framework progressively as was indicated in Figure 2. The content of aluminum, however, is rather constant regardless of the thermal treatment or the extent of crystallinity (crystallization time). Both 1H and 13C NMR indicate that the amount of SDA found in the recovered powders for both structures increases as a function of the reaction time. 23Na NMR measurements reveal in and out of Na ions as the nucleation proceeds. The role of Na+ ion is the counter ion for the negatively charged metal ions when the positively charged SDA is not available. The dramatic decrease of Na content for beta structure at the end indicates that the SDA moves progressively to Al locations and replace Na ions.
Boron DoubletUnlike broad feature of Al signal, 11B NMR spectra of SSZ-42 powders consist of at least three components, and decomposition using a peak fitting program reveals the distribution of boron atoms among the sites in the framework.
•Boron atoms are found to be all tetrahedrally coordinated (BO4-, -3 ~ -5 ppm) and in two different
environments with their chemical shift change is only 0.6 ppm. Note that four different T sites are present in the structure (see 29Si NMR).
•Borons in amorphous phase render a featureless broad line (FWHM~300 Hz at 11.7 T). Quantitationby spectral line fittings yields that the portions of amorphous phase for sample B3 and B5 are 46 % and 7 %, respectively.
2 1 0 -1 -2 -3 -4 -5 -6 -7 -8
decomposed peaks
Fitted
Exp.
ppm
Figure 3. Experimental and simulated 11B MAS NMR spectra of B3 compound obtained using Bruker DSX500 (νr =12 kHz).
BO4(I)
amorphous
BO4(II) •The relative intensity ratios BO4(I)/BO4(II) approaches to 1 as the crystallization completes.are 1.3 and 0.9 for sample B3 and B5, respectively.
•It is unrealistic to predict that only two of the four T sites are selectively replaced by boron atoms. In order to better characterize the boron doublets, several boron containing zeolites were synthesized and the similar boron NMR measurements were made (see Fig 4). SSZ-33 (CON) has seven T sites. It is clear that the boron doublet is unique to IFR structure.
•SSZ-42 was calcined, and also boron atoms were extracted with acetic acid treatment (Fig. 5). BO4(II) gets preferably removed upon calcination. The acetic acid treatment at 135 C removes most of BO4(I) sites, but both sites still exist. When the compound was heated at 185 C in acetic acid media, BO4(II) was completely removed.
0 -1 -2 -3 -4 -5 -6 -7 -8ppm
as made (B5)calcinedextracted (135 C)extracted (185 C)
2 1 0 -1 -2 -3 -4 -5 -6 -7 -8ppm2
B-beta
B-SSZ-42
B-SSZ-33
Figure 4. 11B NMR of different zeoliteStructures.
Figure 5. 11B NMR of B-SSZ-42 afterseveral treatments.
•The negatively charged boron sites can be compensated by either the SDA or Na+, and the counter ions can induce the chemical shift difference of boron atoms. In order to investigate this, another synthetic route employed NH4
+ as the counter cation, and SDA+ was more introduced to the system. The resulting 11B NMR spectra and the decomposition are seen in Fig. 6. The boron doublets are still present regardless of the changes in the counter ions although the relative intensity ratio and the line width are slightly varied. An extra resonance was needed in the fitting for the case of more SDA used.
0 -1 -2 -3 -4 -5 -6 -7ppm
with Na+
with NH4+
more SDA+
0 -1 -2 -3 -4 -5 -6 -7ppm
more SDA+
with NH4+
with Na+
Figure 6. 11B NMR of B-SSZ-42 prepared with different positive counter ions anddecomposition of lines.
11B CPMAS and 2D WISEFurther characterization was made for the boron doublet. Figure 7 shows 11B CPMAS NMR results as a function of contact time and a 2D WISE spectrum of as made B3 (BSSZ-42). Proximity from the SDA can be obtained qualitatively: Possible different BO4(I) and BO4(II) locations in the framework.• The CP dynamics distinguishes the proton source.
BO4(amorphous) TBH=140 us, T1ρ=1.87 ms (from sample B2); mostly water or OH groupsBO4(crystalline) TBH=530 us, T1ρ=22.1 ms (measured from sample B5) : SDA
Figure 7. 11B CPMAS NMR. a. sample B3. CP contact times (in ms) by each line. b. 2D WISE (CP contact time=0.2 ms) on sample B3(BSSZ-42). 1H MAS spectrum (red) as well as slices for aliphatic and aromatic protons are overlapped onto the 2D contour plot for comparison.
2 0 -2 -4 -6 -8ppm
0.1
10
6
0.350.5
1a b
0.0 0.5 1.0 1.5 2.0 2.5 3.0NcTr/ ms
0.0
0.2
0.4
0.6
0.8
1.0
∆S/
S o
BO4(I)BO4(II)
-200 -150 -100 -50 0 50 100 150 200frequency (kHz)
exp.
ωr=5 kHz
simulated
qcc=0.175 MHzη = 0.09 (0.026)
•As shown in Figure 7b, 2D WISE spectrum provide the proximity information between the BO4(I) and BO4(II). BO4(I) seems to be located closer to the aliphatic group of SDA while BO4(II) does so to the aromatic ring of SDA.•SDA with the perdeuterated benzyl ring was used to synthesize another BSSZ-42, and its 2H MAS NMR and 11B{1H} CPREDOR experiments were performed. 2H MAS indicates that benzyl ring has very limited motion even at room temperature. The REDOR effect support the conclusion from the WISE experiment that the BO4(I) site is closer to the aliphatic part of the SDA. Any quantitative analysis of the 11B{1H} REDOR experiment is not made.
a b
Figure 8. a. 2H MAS NMR spectrum and simulation (5 kHz spinning at 11.7 T).b. 11B{1H} CP-REDOR experiment (CP contact time=0.5 ms, υr=10 kHz, 11.7 T).
b. after calcination 11B MAS NMR spectra of two calcined (4 h at 540o C) zeolites are shown in Figure 9a. No additional dehydration was performed. Formation of trigonally coordinated boron (BO3) (quadrupolar power pattern at 8-0 ppm, BO3(II)) is seen for both samples after calcinationwhile the conversion in sample B3 is negligible. Another type of trigonal site(20-10 ppm, BO3(I)) is also visible in B5. A few interesting observations are• The conversion of BO4 to BO3 sites upon calcination is markedly higher for the crystalline BSSZ-42 (sample B5) than that found for sample B3 (amorphous mixture).
25 20 15 10 5 0 -5 -10 -15ppm
sample
B5
B3
11B MAS NMR of BSSZ-42 (Calcined)
fitted
30
Calcined
saturated w
rinse
a b
BO3(II)
BO4(I)
BO3(I)
σiso=9.7 ppmQcc=2.6 MHzη=0.15
σiso=19.8 ppmQcc=2.5 MHzη=0.15
25 20 15 10 5 0 -5 -10ppm
ith H2O
d and dried
11B MAS NMR of BSSZ-42 (B5)
Figure 9 11B MAS NMR spectra (DSX 500, νr=12 kHz) a. after calcination. b. effect of hydration
•Integration of the signal estimates the [BO3]/[BO4] = ~1.5 for sample B5 (crystalline BSSZ-42). BO4(II) sites shows a nearly complete conversion to BO3 unit while BO4(I) show about 50 % conversion. Correlation can be made based on the quantitation: BO4(I)=> BO3(I) and BO4(II)=> BO3(II)
•In sample B3, all the lines get narrowed significantly by calcination. The severe change in overall spectral lineshape is simply associated with the different extent of line narrowing among the sites. The relative intensity ratios are found to remain unchanged. No selective destruction of BO4(II) was observed.
•In the previous report by Fild et. al.2, trigonal site BO3(II) was assigned to be a trigonal site in the frame work while the other one (BO3(I) was to be outside of the framework. Note that the quantity of BO3(I) is negligible. The presence of both BO4 and BO3 units are also consistent with the previous result1 because both Na+ and H+ might act as the counterions.
•Interestingly hydration of calcined sample (see Figure 9-b) resulted in the formation of a peak at 18.5 ppm (B2O3 in aqueous phase) as well as some recovery of the tetrahedral sites (~20 % of BO3(II) site) as indicated by peak growth both at -3.8 and -4.5 ppm. 80 % of the trigonal sites are converted to form 18.5 ppm peak, which is not consistent with the postulation1 (see above) if BO3(II) is bridged by -Si-O-B bond in the framework. Peak at 18.5 ppm was negligibly small for hydration of sample B3 (amorphous mixture) as can be expected from the small quantity of BO3 sites (spectra not shown).
•Rinsing and drying of hydrated B5 (see Figure 9-b) lead to observation of the top spectrum in Figure 9-b, clearly indicating that the 18.5 ppm peak can be washed out. This result implies that significant portion of the trigonal sites created by calcination are already outside the framework or weakly bridged to the framework and therefore can be removed by hydration.
2Chirstian Fild, et al. Phys. Chem. Chem. 2000, 2, 30913Christian Fild, et al. Angew. Chem. Int. Ed. 1998, 37, 2505.4Christian Fild, et al. J. Am. Chem. Soc. 122, 12590 (2000).
IV. Summary1. Understanding of mechanistic difference in synthetic of BSSZ-42 and Al-Beta was attempted by studying recovered powders using solid state NMR methods.
2. 11B NMR methods were very sensitive to identify the coordination geometry of boron atoms in/outside the framework of forming zeolite during the crystallization process. Lattice substitution of boron atoms resulted in the formation of two distinctive BO4 (tetraherdally coordinated borons: Boron Doublets) sites in the SSZ-42 framework.Such doublets were found to be so far unique to the IFR structure. One of the site shows a strong selectivity toward to forming BO3 units upon calcination, then can be easily removed by hydration and rinsing. Such a discrepancy was not observed for the amorphous mixture of the same structure. Identification of the doublets is under progress.
3. Similar dealumination reaction occurred and two tetrahedral Al sites were observed when Al-Beta was calcined (results not shown).
Future work includes getting information about spatial proximity from the incorporated metal ions to the SDA as well as other changes during the aging process which can help us to understand the pathway better.
V. AcknowledgementsThe authors thank Professor M. Davis who allowed us to use his laboratory for calcinationprocedures.