Structural, morphological and optical studies of
nanocrystalline CuO thin films by solution processed
Spin Coating technique
1Mahipal Singh Deora and 2S. K. Sharma
1Research Scholar and 2Professor
Department of Physics, Jai Narain Vyas University, Jodhpur, India
Abstract: The nanocrystalline Copper oxide (CuO) thin films have been synthesized on glass substrate by a facile solution processed spin coating technique and as deposited CuO thin films were annealed at 150 °C and 500 °C temperature for 1 hour in air. X-ray
diffraction pattern shows that the films are nanocrystalline with the monoclinic structure and also present the random orientation of
crystallites. The crystallite size increases with increasing in the annealing temperature of CuO thin films. The crystallite size
corresponding to preferred diffraction peaks (111) were found to be 30 nm and 62 nm for thin films annealed at 150 °C and 500 °C
temperature. The SEM studies exhibited homogeneous surface morphological and uniform deposition of thin film on the glass
substrate. The EDAX spectra of thin film annealed at 150 °C confirmed the presence of copper, oxygen elements in the film. The
FTIR spectra displayed the formation of Cu-O bonding in thin films. The optical transmission of CuO thin films in the visible and
near infrared spectral region was found to be above 80%. The optical band gap energy decreases with increasing the annealing
temperature. The estimated energy band gap of CuO thin film annealed at temperature 150 °C and 500 °C were found to be 1.62eV
and 1.43 eV. The influence of annealing temperature on the physical properties of CuO thin films were examined.
Keywords: Nanocrystalline, Solution-processed Spin coating technique, Visible and near infrared spectral region.
1. Introduction
In recent years, the direct conversion of solar energy into electrical energy has become a highly attractive and economical
process for providing clean and renewable energy in worldwide. Inorganic semiconductor are promising nanomaterials with
different nanostructures such as nanoparticles, nanowires and nanotubes etc. which display novel electronic and optical properties
due to quantum confinement effects and unique structural properties at nanoscale level. Currently the industry standard transparent
semiconducting oxides (TSO) are ZnO, SnO2, ITO, FTO, Cu2O, CuO and NiO [1-4]. Among the various metal oxide materials the
cupric oxide (CuO) are promising p-type semiconductors material for solar cell and photodetector applications.
Copper oxide has many prospective applications in various fields such as catalysis [5], electrode material in batteries [6],
gas sensors [7], biosensors [8], magnetic storage devices [9], capacitors [10], optical switch [11] and active material for solar cell
[12]. It exists in two different crystalline phases, cupric oxide (CuO) and cuprous oxide (Cu2O). CuO has a monoclinic structure,
p-type semiconductor and nontoxic important low cost material with band gap between 1.4-1.9 eV [13]. It has high optical
absorption coefficient in visible and near infrared region due to its direct band gap [14]. The different morphology of CuO
nanostructure thin films have been prepared by various method thermal evaporation [15], RF-sputtering [16], pulsed laser deposition
(PLD) [17], spray pyrolysis, solvothermal [18], hydrothermal [19], sol gel spin coating [20] and chemical bath deposition (CBD)
methods [21,22].
Many authors have reported the deposition of CuO thin films by sol-gel spin coating method. Prabhu et al have reported
the deposition of CuO/ZnO thin films via sol-gel spin coating technique at 60 °C temperature [20]. Lim et al. have reported the
deposition of Cu2O and CuO thin films by sol-gel spin coating for photocatalytic water splitting and solar cell application [23].
Jundale et al. has demonstrated the preparation of CuO thin films by facile sol-gel method and its subsequent optoelectronic
properties [24].
The spin coating deposition technique is sol-gel solution processed method to deposit thin films in the form of
nanomaterials and nanostructures. It is simple, fast, convenient technique to produce uniform deposition over large areas at
relatively lower temperature and low cost. In present study, the nanocrystalline CuO thin films have been deposited on glass
substrates by using a new facile solution processed spin coating technique and their structural, morphological and optical properties
were studied.
2. Experimental details
Materials
The chemicals used for the thin film preparation were analytical grade cupric acetate monohydrate [Cu (CH3COO)2·H2O]
(99.99%) purchased from Alfa Asear. Solvent 2-methoxyethanol anhydrous [CH3OCH2CH2OH] (99.8%) purchased from Sigma-
Aldrich. Mono-ethanolamine (MEA) [C2H7NO] (98%) and Polyethylene Glycol 200 (PEG) (98%) purchased from Loba chemie.
Pvt Ltd. Commercially available micro glass slides with dimension of 25mm x 25mm x 2mm were used as glass substrates.
http://www.jetir.org/
-
© 2019 JETIR January 2019, Volume 6, Issue 1 www.jetir.org (ISSN-2349-5162)
JETIR1901993 Journal of Emerging Technologies and Innovative Research (JETIR) www.jetir.org 670
Preparation of cupric oxide (CuO) thin films
Copper oxide thin films were prepared by dissolving 0.2 M cupric acetate in 20 ml of 2-methoxyethanol solvent then 1.0
ml of mono-ethanolamine was added drop wise to achieve a homogeneous solution. The role of the mono-ethanolamine was to
stabilize the solution and prevent formation of aggregates. After 15 minutes of magnetic stirring a light blue solution was formed.
Finally 0.50 ml Polyethylene Glycol 200 (PEG) was added to enhance film forming properties. The above solution was magnetic
stirred at 60 °C for an hour after then this solution was aged for 24 hours. The colour of the solution became dark blue. The precursor
solution was uniformly deposited on cleaned glass substrates by spin coating technique at a spin speed of 3000 rpm for 30 sec and
then dried immediately on hot plate at 150 °C for 10 minutes after each layer deposition. This coating process was repeated 5-6
times to attain the desirable thickness. Finally samples were annealed in air at 150 °C and 500 °C temperature for 1hour.
The flow chat of procedure for preparing nanocrystalline CuO thin film is shown in fig. 1. The cupric oxide thin films
were characterized for structural, morphological and optical analysis. The crystalline structure of thin film has been studied by using
X- ray diffractometer ( Bruker AXS, D8 Advanced) with a Cu Kα (λ=1.5405Å) monochromatic incident radiation source, operating
at 40.0KV. XRD data of all thin film samples were recorded in detector scan mode with incident X-ray source fixed at the 3° glazing
incident angle and detector has moved to collect the 2θ diffraction ranging from 20° to 80° at a step size of 0.02° per second. The
surface morphology measurements along with elemental composition analysis were carried out using EVO 18, especial edition,
Carl Zeiss scanning electron microscopy coupled with energy dispersive X-Ray spectroscopy. The FTIR studies were done by a
BRUKER Vertex 70V Fourier transform infrared spectrometer in the range of wavelength (400-4000 cm-1). The optical
transmission spectra of the samples were obtained by carry 4000 UV-VIS-NIR Spectrophotometer in the range of 300-1500nm
wavelength at room temperature.
3. Results and discussion
3.1 Structural analysis
The structural determination of all the thin films were carried out by X- ray diffraction technique and diffraction patterns
were recorded by varying diffraction angle (2θ). Fig. 2 shows X- ray diffraction patterns of CuO thin films deposited on glass
substrate with annealed at 150 °C and 500 °C temperature. The major diffracted planes (002), (111) and (220) are located at 35.475°,
39.440° and 68.3° for the CuO thin films. The observed XRD patterns are matched with standard JCPDS (Joint Committee on
Powder Diffraction Standards) data card 45-0937 for the CuO and which shows the monoclinic phase of CuO thin film [25]. The
crystallite size increases with increasing in the annealing temperature of CuO thin films in air. The average crystallite size for CuO
http://www.jetir.org/
-
© 2019 JETIR January 2019, Volume 6, Issue 1 www.jetir.org (ISSN-2349-5162)
JETIR1901993 Journal of Emerging Technologies and Innovative Research (JETIR) www.jetir.org 671
thin films were calculated by using Debye Scherer’s formula D =0.94λ
BCosθ where B is full width half maxima (FWHM) of diffraction
peak, λ is wavelength of characteristic Cu Kα X-ray incident radiation. The calculated value of average crystallite size corresponding
to preferred diffraction peaks (111) were found to be 30nm and 62nm for CuO thin films annealed at 150 °C and 500 °C temperature
respectively.
3.2 Surface morphology and compositional analysis
The SEM images for the sample of CuO thin films annealed at 150 °C with different magnification are shown in fig. 3 (a-
b). The surface morphology of samples have homogeneous and uniform deposition of thin film on the glass substrate. It can be seen
that small particles were grown over the surface of glass substrate with spherical shaped. The overgrowth could be explained on the
basis of nucleation and coalescence. The average diameter of grain about 40 nm. It was also observed that the nanoparticles may
be converted into bigger clusters due to agglomeration of large number of nanoparticles. The fig. 3(c) shows EDAX spectra of
nanocrystalline CuO thin film annealed at 150 °C. It confirmed the presence of copper, oxygen and other elements from the glass
substrates. The atomic percentage of Cu and O elements were about 40% and 60% respectively.
Fig. 2 XRD patterns of CuO thin films deposited on glass substrate
for (a) annealed at 150 °C and (b) annealed at 500 °C
(b)
(c) (c)
Fig. 3(a-b) SEM images and Fig. 3(c) typical EDAX spectra of CuO thin film
annealed at 150°C
El AN Series C Atom. [at.%]
--------------------- O 8 K-series 60.24
Cu 29 K-series 39.76 --------------------- Total: 100.00
(a)
http://www.jetir.org/
-
© 2019 JETIR January 2019, Volume 6, Issue 1 www.jetir.org (ISSN-2349-5162)
JETIR1901993 Journal of Emerging Technologies and Innovative Research (JETIR) www.jetir.org 672
3.3 Optical analysis
3.3.1 FTIR Studies
Fourier transform infrared (FTIR) spectroscopy was performed by studying the adsorption of mono-ethanolamine (TEA)
and Polyethylene Glycol (PEG) as capping agent on the surface of CuO thin film. Fig. 4 shows the FTIR spectrum of nanocrystalline
CuO thin film annealed at 150 °C. All the data regarding to the spectrum is summarized in the Table 1, from which it was observed
that the most prominent peak at 3744 cm-1 is due to free O–H stretching of water molecule. The peaks at 3617 & 3676 cm-1 are due
to free O–H stretching of alcohol. The peaks at 1648 and 1695 cm-1 are due to C=O stretching vibration of carboxylic group. The
N-H vibration of secondary amine absorbs near 1519 cm-1. The peaks at 1441, 1423 cm-1 can be explained as –CH2 bending and –
CH2 wagging. There is a small band at 646 cm-1 is due to stretching of Cu-O bond.
Table 1
FTIR Spectra band position of nanocrystalline CuO thin film with their assignments
Assignments
Band position of CuO thin film
(in cm-1)
Free O–H stretching of water 3744
Free O–H stretching of alcohol 3676, 3617
C=O stretching vibration of Carboxylic group 1695, 1648
N-H vibration of secondary amine 1519
–CH2 bending 1441
–CH2 wagging 1423
Stretching of Cu–O bond 646
3.3.2 UV-VIS-NIR Spectrophotometer
The transmission measurements of all samples were carried out from the 300–1500 nm wavelength range at room
temperature. Fig 5 (a) shows the transmission spectra of CuO thin films annealed at temperature 150 °C and 500 °C. The
transmission of thin film shift towards the longer wavelength as the annealing temperature increases.
Fig. 4 FTIR spectra of CuO thin film annealed at 150 °C
http://www.jetir.org/
-
© 2019 JETIR January 2019, Volume 6, Issue 1 www.jetir.org (ISSN-2349-5162)
JETIR1901993 Journal of Emerging Technologies and Innovative Research (JETIR) www.jetir.org 673
The absorption coefficient (α) is calculated from transmission spectra by using the relation oatI I e . The calculated
values have been used to understand the optical energy bandgap of CuO thin films by using the Tauc relation1
( ) ( )n
Eh A h g , where α is absorption coefficient, hυ is the photon energy, A is proportionality constant and Eg is the band gap of the material. The
value of exponent ‘n’ can take 1/2, 3/2, 2 and 3 depending on the nature of optical transition corresponding to direct allowed, direct
forbidden, indirect allowed and indirect forbidden transitions respectively [26].
The absorbance band of the films were found around the wavelength 700–800 nm and there was also shifting in absorption
edge towards the shorter wavelength. Fig. 5 (b) shows the plot between (αhυ)2 versus photon energy (hυ) (Tauc plot) for CuO thin
films annealed at temperature 150 °C and 500 °C. The intercept of extrapolated linear region in these plots on energy axis gives the
values of direct band gap (Eg) of material. The estimated energy band gap of CuO thin film annealed at temperature 150 °C and 500
°C were found to be 1.62 eV and 1.43 eV. The direct band gap of CuO thin film was found from Tauc plot. It is observed that the
optical band gap energy decreases with increasing the annealing temperature of CuO thin film increase. The value of band gap
energy is attributed to the increase in crystallinity of the CuO phase in thin films.
4. Conclusions
In the present work, the nanocrystalline p-CuO thin films were prepared successfully by cupric acetate precursor solution
processed Spin Coating technique. The XRD measurement confirms the nanocrystalline nature and the monoclinic phase of CuO
thin film. SEM studies exhibited uniform surface morphological observations in all thin films. EDAX spectra confirmed the
presence of copper, oxygen elements in the CuO thin film. The FTIR studies displayed the formation of Cu-O bonding in thin films.
The optical studies revealed that films have direct energy band gap and the estimated energy band gap of CuO thin film annealed
at temperature 150 °C and 500 °C were found to be 1.62 eV and 1.43 eV. The CuO thin films have higher absorbance within the
visible and near infrared range of solar spectrum so it can be used as an absorber layer in heterojunction solar cell device.
Acknowledgements
The author Mahipal Singh Deora, acknowledges University Grants Commission (UGC), New Delhi for financial support
under Minor Research project for carrying out this experimental work. We are thankful to IIT, Jodhpur for providing us experimental
facilities in the campus. We also wish to thank to Defence Lab, Jodhpur and USIC, University of Rajasthan, Jaipur for providing
us XRD and SEM facilities respectively.
References
[1] E. Norton, L. Farrell, S.D. Callaghan, C. McGuinness, I.V. Shvets, K. Fleischer, X-ray spectroscopic studies of the electronic structure of chromium-based p-type transparent conducting oxides, Phys. Rev. B 93 (2016) 115302-115308.
[2] K.H.L. Zhang, K. Xi, M.G. Blamire, R.G. Egdell, P-type transparent conducting oxides, J. Phys.: Condens. Matter 28 (2016) - 383019.
[3] Z. Wang, P.K. Nayak, J.A. Caraveo-Frescas, H.N. Alshareef, Recent developments in p-type oxide semiconductor materials and devices, Adv. Mater. 28 (2016) 3831-3892.
[4] P. Wang, X. Zhao, B. Li, ZnO-coated CuO nanowire arrays: fabrications, optoelectronic properties, and photovoltaic applications, Opt. Express 19 (2011) 11271-11279.
[5] T. Ishihara, M. Higuchi, T. Takagi, M. Ito, H. Nishiguchi, T. Takita, Preparation of CuO thin films on porous BaTiO3 by self- assembled multibilayer film formation and application as a CO2 sensor, Journal of Materials Chemistry 8 (1998) 2037.
[6] X.P. Gao, J.L. Bao, G.L. Pan, H.Y. Zhu, P.X. Huang, F. Wu, D.Y. Song, Preparation and electrochemical performance of polycrystalline and single crystalline CuO nanorods as anode materials for Li ion battery, J. Phys. Chem. B 108 (2004) 5547-
5551.
Fig. 5 (a) Plot between transmission with wavelength of
CuO thin films with different annealing temperatures
Fig. 5 (b) Plot between (αhυ)2 vs. photon energy (hυ) of
CuO thin films with different annealing temperatures
http://www.jetir.org/http://refhub.elsevier.com/S0921-5107(17)30053-3/h0005http://refhub.elsevier.com/S0921-5107(17)30053-3/h0005http://refhub.elsevier.com/S0921-5107(17)30053-3/h0005http://refhub.elsevier.com/S0921-5107(17)30053-3/h0005http://refhub.elsevier.com/S0921-5107(17)30053-3/h0010http://refhub.elsevier.com/S0921-5107(17)30053-3/h0010http://refhub.elsevier.com/S0921-5107(17)30053-3/h0010http://refhub.elsevier.com/S0921-5107(17)30053-3/h0030http://refhub.elsevier.com/S0921-5107(17)30053-3/h0030http://refhub.elsevier.com/S0921-5107(17)30053-3/h0030http://refhub.elsevier.com/S0921-5107(17)30053-3/h0030http://refhub.elsevier.com/S0921-5107(17)30053-3/h0035http://refhub.elsevier.com/S0921-5107(17)30053-3/h0035http://refhub.elsevier.com/S0921-5107(17)30053-3/h0035http://refhub.elsevier.com/S0921-5107(17)30053-3/h0035http://refhub.elsevier.com/S0921-5107(17)30053-3/h0110http://refhub.elsevier.com/S0921-5107(17)30053-3/h0110http://refhub.elsevier.com/S0921-5107(17)30053-3/h0110http://refhub.elsevier.com/S0921-5107(17)30053-3/h0110http://refhub.elsevier.com/S0921-5107(17)30053-3/h0110http://refhub.elsevier.com/S0921-5107(17)30053-3/h0110
-
© 2019 JETIR January 2019, Volume 6, Issue 1 www.jetir.org (ISSN-2349-5162)
JETIR1901993 Journal of Emerging Technologies and Innovative Research (JETIR) www.jetir.org 674
[7] A. Ghosh, B.B. Show, S. Ghosh, N. Mukherjee, G. Bhattacharya, S.K. Datta, A. Mondal, Electrochemical synthesis of p-CuO thin Þlms and development of a p-CuO/n-ZnO heterojunction and its application as a selective gas sensor, RSC Adv. 4 (2014)
51569-51575.
[8] G.L. Luque, M.C. Rodriguez, G.A. Rivas, Glucose biosensors based on the immobilization of copper oxide and glucose oxidase within a carbon paste matrix, Talanta 66 (2005) 467.
[9] R.V. Kumar, Y. Diamant, A. Gedanken, Sonochemical synthesis and characterization of nanometer-size transition metal oxides from metal acetates, Chemistry of Materials 12 (2000) 2301.
[10] H. Zhang, M. Zhang, Synthesis of CuO nanocrystalline and their application as electrode materials for capacitors, Materials Chemistry and Physics 108 (2008) 184.
[11] J. Liu, X. Huang, Y. Li, K.M. Sulieman, X. He, F. Sun, Hierarchical nanostructures of cupric oxide on a copper substrate: controllable morphology and wettability, J. Mater. Chem. 16 (2006) 4427-4434.
[12] Y.F. Lim, J.J. Choi, T. Hanrath, Facile synthesis of colloidal CuO nanocrystals for light-harvesting applications, J. Nanomater. (2012), http://dx.doi.org/10.1155/ 2012/393160. Article ID 393160-6.
[13] W.L. Yu, Y.Z. Lin, X.W. Zhu, Z.G. Hu, M.J. Han, S.S. Cai, L.L. Chen, H.H. Shao, Diversity of electronic transitions and photoluminescence properties of p-type cuprous oxide films: a temperature-dependent spectral transmittance study, J. Appl.
Phys. 117 (2015) 045701-45709.
[14] A. Bhaumik, A.M. Shearin, R. Patel, K. Ghosh, SigniÞcant enhancement of optical absorption through nano-structuring of copper based oxide semiconductors: possible future materials for solar energy applications, Phys. Chem. Chem. Phys. 16 (2014)
11054-11066.
[15] P. Kasian, S. Pukird, Gas sensing properties of CuO nanostructures synthesized by thermal evaporation of copper metal plate, Adv. Mat. Res. 93–94 (2010) 316–319.
[16] K.C. Sanal, L.S. Vikas, M.K. Jayaraj, Room temperature deposited transparent pchannel CuO thin film transistors, Appl. Surf. Sci. 297 (2014) 153–157.
[17] H. Faiz, K. Siraj, M.F. Khan, M. Irshad, S. Majeed, M.S. Rafique, S. Naseem, Microstructural and optical properties of dysprosium doped copper oxide thin films fabricated by pulsed laser deposition technique, J. Mater. Sci. – Mater.Electron. 27
(2016) 8197–8205.
[18] F. Bayansal, S. Kahraman, G. C¸ ankaya, H.A. C¸ etinkara, H.S. Gu¨der, H.M. C¸ akmak, Growth of homogenous CuO nano-structured thin films by a simple solution method, Journal of Alloys and Compounds 509 (2011) 2094.
[19] F. Janene, H. Dhaouadi, L. Arfaoui, N. Etteyeb, F. Touati, Nanoplate-like CuO: hydrothermal synthesis, characterization, and electrochemical properties, Ionics 22 (2016) 1395–1403.
[20] R. Prabhu, A.C. Saritha, M.R. Shijeesh, M.K. Jayaraj, Fabrication of p-CuO/n-ZnO heterojunction diode via sol-gel spin coating technique, Material Science and Engineering B 220 (2017) 82-90.
[21] M. Izaki, Y. Yamane, J. Sasano, T. Shinagawa, M. Inoue, Direct preparation of 1.35-eV-bandgap CuO: S film by chemical bath deposition, Electrochem. Solid-State Lett. 14 (2011) D30–D32.
[22] H. Oh, H. Ryu, W. Lee, Effects of copper precursor concentration on the growth of cupric oxide nanorods for photoelectrode using a modified chemical bath deposition method, Journal of alloys and compounds, 620 (2015) 55-59.
[23] Y.F. Lim, C.S. Chua, C.J.J. Lee, D. Chi, Sol-gel deposited Cu2O and CuO thin films for photocatalytic water splitting, Phys. Chem. Chem. Phys. 16 (2014) 25928–25934.
[24] D.M. Jundale, P.B. Joshi,S. Sen, V.B.Patil, Nanocrystalline CuO thin films: synthesis, microstructural and optoelectronic properties, J. Mater Sci: Mater Electron (2012) 23: 1492-1499.
[25] .K. Mageshwari, R. Sathyamoorthy, Physical properties of nanocrystalline CuO thin films prepared by the SILAR method, Mater. Sci. Semicon. Proc. 16 (2013) 337–343.
[26] A. Bhaumik, A.M. Shearin, R. Patel, K. Ghosh, Significant enhancement of optical absorption through nano-structuring of copper based oxide semiconductors: possible future materials for solar energy applications, Phys. Chem. Chem. Phys. 16 (2014)
11054–11066.
http://www.jetir.org/http://refhub.elsevier.com/S0921-5107(17)30053-3/h0090http://refhub.elsevier.com/S0921-5107(17)30053-3/h0090http://refhub.elsevier.com/S0921-5107(17)30053-3/h0090http://refhub.elsevier.com/S0921-5107(17)30053-3/h0090http://refhub.elsevier.com/S0921-5107(17)30053-3/h0090http://refhub.elsevier.com/S0921-5107(17)30053-3/h0090http://refhub.elsevier.com/S0921-5107(17)30053-3/h0120http://refhub.elsevier.com/S0921-5107(17)30053-3/h0120http://refhub.elsevier.com/S0921-5107(17)30053-3/h0120http://refhub.elsevier.com/S0921-5107(17)30053-3/h0120http://dx.doi.org/10.1155/2012/393160http://dx.doi.org/10.1155/2012/393160http://refhub.elsevier.com/S0921-5107(17)30053-3/h0050http://refhub.elsevier.com/S0921-5107(17)30053-3/h0050http://refhub.elsevier.com/S0921-5107(17)30053-3/h0050http://refhub.elsevier.com/S0921-5107(17)30053-3/h0050http://refhub.elsevier.com/S0921-5107(17)30053-3/h0050http://refhub.elsevier.com/S0921-5107(17)30053-3/h0050http://refhub.elsevier.com/S0921-5107(17)30053-3/h0065http://refhub.elsevier.com/S0921-5107(17)30053-3/h0065http://refhub.elsevier.com/S0921-5107(17)30053-3/h0065http://refhub.elsevier.com/S0921-5107(17)30053-3/h0065http://refhub.elsevier.com/S0921-5107(17)30053-3/h0065http://refhub.elsevier.com/S0921-5107(17)30053-3/h0065