preparation and characterization of needle-like zno on tio2 nanoparticles by solution-immersion...
TRANSCRIPT
Preparation and Characterization of Needle-like ZnO onTiO2 Nanoparticles by Solution-Immersion Method and RF Magnetron
Sputtering
N.A.M. Asib1 2, a, A. Aadila1 2, b, A.N. Afaah1 2, c, M. Rusop1 3, d, Z. Khusaimi1, e 1NANO-SciTech Centre, Institute of Sciences,
2Faculty of Applied Sciences,
3NANO-ElecTronic Centre, Faculty of Electrical Engineering,
Universiti Teknologi MARA, 40450 Shah Alam, Selangor, Malaysia
[email protected], [email protected], [email protected], [email protected], [email protected]
Keywords: Needle-like ZnO, TiO2 nanoparticles, Solution-immersion method, RF magnetron sputtering
Abstract. Needle-like zinc oxide (ZnO) nanostructures was deposited on titanium dioxide (TiO2)
nanoparticles by solution-immersion method and Radio Frequency (RF) magnetron sputtering with
diffferent RF powers, respectively on a glass substrate to synthesis nanocomposites of ZnO/TiO2.
Field Emission Scanning Electrons Microscope (FESEM) images demonstrate that needle-like ZnO
(112-1110 nm) are deposited on the surface of the TiO2 nanoparticles with the diameter of
approximately 36.3-62.9 nm. At 200 W, more needle-like ZnO with smallest average diameter (112
nm) appeared on the TiO2 nanoparticles, which also has the smallest average size of 36.3 nm. The
compositions of elements in the nanocomposites were showed by Energy Dispersive X-ray
Spectrometry (EDX). All elements of Ti, O, and Zn are observed as major components which
confirm the presence of TiO2 and ZnO in the composite. X-ray Diffraction (XRD) patterns of the
nanocomposites show ZnO formed on TiO2 nanoparticles are hexagonal with a wurtzite structure
and it revealed ZnO/TiO2 thin films were succesfully deposited as nanocomposites of ZnTiO3 at 100
W, Zn2TiO4 at 150 W and Zn2Ti3O8 at 200 W and above.
Introduction
Zinc oxide (ZnO) is an n-type semiconductor with a wide direct band-gap of 3.37 eV at room
temperature. ZnO have become one of the most widely studied metal oxide material due to the
attracting and unique properties of ZnO that able to exhibit high-transparency in the visible region,
near-UV emission, magnetic, high-conductivity [1], also have semiconducting and piezoelectric
dual properties [2]. However, its properties can be adjusted by controlling size and morphology [3].
The wide applications of ZnO can be found in numerous areas such as varistor, gas sensor [4], UV
photodetector material, high-efficient green phosphor, field emission displays and solar cell [3].
ZnO is also a very widely used photocatalyst due to its high activity and low cost [5].
In the last decade, titanium dioxide (TiO2) especially in thin film form have received wide
attention over the years, either as an optical coatings or as a protective layers for very large scale
integrated circuits because of their excellent properties. To demonstrate, TiO2-based nanomaterials
is good for the degradation of environmental contaminants due to high photocatalytic activity, low
cost, non-toxic, and excellent chemical stability [6]. Thus, it is worth mentioning that the
photocatalytic properties of TiO2 can be greatly influenced by modification of its surface and
coupling with other sulfides or oxides. For instance, the photocatalytic properties of TiO2 can be
greatly enhanced by coupling with ZnO [5].
Nowadays, it is reported that a wide variety of techniques such as sol–gel [7], hydrothermal
crystallization [1], pulsed laser deposition (PLD) also sputtering [1, 7] were used for the deposition
of porous TiO2 nanostructures. Here, attempts will be taken to produce nanostructures of TiO2 by
Advanced Materials Research Vol. 832 (2014) pp 596-601Online available since 2013/Nov/21 at www.scientific.net© (2014) Trans Tech Publications, Switzerlanddoi:10.4028/www.scientific.net/AMR.832.596
All rights reserved. No part of contents of this paper may be reproduced or transmitted in any form or by any means without the written permission of TTP,www.ttp.net. (ID: 129.110.33.9, Univ of Texas at Dallas, Richardson, United States of America-27/05/14,14:18:38)
using RF magnetron sputtering. Compared to other methods, RF magnetron sputtering is of
particular interest for its simplicity in producing optical coatings that having high density, adhesion,
hardness and good uniformity of thickness over a large area [8]. Sputtering methods also provide
more freedom in selection of the deposition parameters [9].
Besides that, porous ZnO films must be deposited in controlled scale of film surfaces, either
nano or micro-scale structures in order to improve the photocatalytic activity[10]. There are various
techniques used such as pulsed laser deposition [10, 11], physical vapor deposition, molecular beam
epitaxy (MBE) [11], and sol–gel [9, 10]. Comparatively, solution method process are more
attractive due to low cost, the precursors are homogenous, has high-purity with specific surface
area, and allows growth of nanostructures at low temperature [11, 12].
Experimental Procedure
Preparation of TiO2 nanoparticles. TiO2 nanoparticles were deposited on glass substrates by RF
magnetron sputtering using a pure TiO2 solid target. The target to substrate distance was kept fixed
at 22 cm. 50 sccm of argon and 2 sccm of oxygen were used for sputter deposition. Argon was used
as a carrier medium and oxygen as reactive gas. TiO2 nanoparticles were deposited at different RF
powers which vary from 100 W to 300 W with increment rate of 50 W. Meanwhile, the working
pressure was maintained at 5 mTorr. After one hour of deposition, all the samples were annealed at
450 ⁰C for 1 hour, using annealing chamber to crystallize the samples.
Preparation of needle-like ZnO. Solution-immersion method was used to fabricate needle-like
ZnO on TiO2 nanoparticles. TiO2 nanoparticles film was immersed in a centrifuged tube. The
precursor solution is aqueous solution of zinc nitrate hexahydrate (Zn (NO3)2.6H2O) and stabilizer
hexamethylenetetramine, HMTA (C6H12N4) were dissolved in deionized (DI) water. The precursor
solution was stirred thoroughly with a magnetic stirrer for 1 hour at 60 ⁰C and then aged for 24
hours. TiO2 films were placed inside centrifuged tubes and the solution will be poured until the
films were fully immersed. The centrifuged tubes were placed inside water bath at 70-90 °C for 4
hours. As a result, ZnO nanostructures will grow on the TiO2 nanoparticles and becomes ZnO/TiO2
nanocomposites. The sample were dried in oven and subsequently, annealed at 500 ⁰C for 1 hour.
Lastly, the samples were characterized by FESEM, EDX and XRD.
Results and Discussion
FESEM images. Fig. 1 (a) shows FESEM (at 10 000x magnification and 5.0 kV) image of surface
morphology for TiO2 nanoparticles formed at 200 W, on a glass substrate by RF magnetron
sputtering method with the average diameter of 36.3 nm. Later on, needle-like ZnO were fabricated
on the sputtered TiO2 films by solution-immersion method as shown in Fig. 1 (b-f).
It was observed that the surface morphologies and roughness of TiO2 films were different at
various sputtering powers. The highest roughness of TiO2 deposited at power of 300 W, can be
regarded as a factor of higher hydrophilicity [13] and higher energy sputtering [14] as compared to
the smoothest layers deposited at 200 W. Thus, the deposited TiO2 nanostructure is optimized at 200
W as it has the lowest roughness or the smoothest surface [15].
After fabrication of ZnO by solution-immersion process on the TiO2 nanoparticles as shown in
Fig. 1 (b-f), the needle-like ZnO in the range diameter of 112 to 1110 nm grow vertically and
horizontally on the TiO2 nanoparticles. Figure 1 (d) reveals that at 200 W, the needle-like ZnO with
smallest diameter (112 nm) were deposited on the smallest size of TiO2 nanoparticles and it
confirms that the needle-like were deposited with dense arrays and small diameter size. Meanwhile,
the largest diameter of needle-like ZnO with less dense arrays was deposited at 300 W on the
largest size of TiO2 nanoparticles (62.9 nm) as shown in Figure 1 (f). Thus, we can see that more
nanostructures of ZnO appeared in the film sputtered at 200 W compared to other samples. The
denser the film, more surface contact will exist between ZnO structures and the condition will
improve the mobility of electrons in the films and will contribute to better electrical properties [16].
Advanced Materials Research Vol. 832 597
Fig. 1, FESEM images of (a)TiO2 nanoparticles deposited at 200 W, and deposited of needle-like
ZnO on TiO2 nanoparticles sputtered at (b) 100 W, (c)150 W, (d) 200 W, (e) 250 W, and (f) 300 W.
Table 1, The diameter size of TiO2 nanoparticles and needle-like ZnO deposited at various RF
powers.
EDX analysis. Figure 2 (a) and (b) show EDX of the ZnO/TiO2 nanocomposites deposited at 100
W. There are two area were examined on the sample. First was the dark area (spectrum 1) which
represented as TiO2 nanoparticles and second was the bright area (spectrum 2) on top of the dark
area, represented as ZnO nanostructures.
Fig. 2, (a-b) EDX of the ZnO/TiO2 nanocomposites deposited at 100 W.
The EDX for Fig. 2 (a) confirm the elemental composition of Ti and O in the film as detected in
spotted area (spectrum 1). Meanwhile, at another spotted area (spectrum 2) in Fig. 2 (b), Zn and O
were observed as major components which confirmed the growth of ZnO on the TiO2 nanoparticles
for each samples. Other elements such as Si, Na and Ca were also detected in the samples due to the
existence of chemical composition ( SiO2, Na2O and CaO) in the glass substrate. In order to prevent
charging and distortion of the image during the scanning and captured process by FESEM, the
Power [W] Diameter size of TiO2 [nm] Diameter size of ZnO [nm]
100
150
200
250
300
50.2
44.9
36.3
41.6
62.9
400
560
112
880
1110
(a)
(e) (d)
(c) (b)
(f)
(a) (b)
598 Nanoscience, Nanotechnology and Nanoengineering
sample must be electrically connected to the sample holder [17]. Thus, carbon paint was used to
allow a path for the electrons to travel and connect with ground. This caused some low level
impurities to the sample, which have been detected by EDX as element C.
XRD analysis. Fig. 2 (a-e) show the XRD patterns of the samples with different RF powers.The
crystallinity of the film and the corresponding chemical formula for each peaks were determined by
XRD as shown in the figures below.
20 30 40 50 60 70
0
500
1000
1500
2000
2500
3000
3500
4000
(00
2)
(10
1)
Inte
nsi
ty (
counts
)
2 Theta (°)
ZnT
iO3
ZnT
iO3
Zn
TiO
3
(100)
20 30 40 50 60 70
200
400
600
800
1000
1200
1400
1600
(002)
(10
1)
(100
)Z
nT
iO3
ZnT
i O3
Zn
2T
iO4
Zn
2T
iO4
Zn
2T
iO4
Inte
nsi
ty (
counts
)
2 Theta(°)
20 30 40 50 60 70
0
1000
2000
3000
4000
5000
(10
1)
(002
)
(100
)T
iO2
Zn
2T
i 3O
8
Zn
2T
i 3O
8
Zn
2T
i 3O
8
Zn
2T
i 3O8
Zn
2T
i 3O
8
Inte
nsi
ty (
coun
ts)
2Theta (°)
20 30 40 50 60 70
0
500
1000
1500
2000
2500
3000
(10
1)
(002)
(10
0)
TiO
2
Zn
2T
i 3O
8
Zn
2T
i 3O
8
Zn
2T
i 3O
8
Inte
nsi
ty (
counts
)
2Theta(°)
Fig. 3, XRD patterns of ZnO/TiO2 nanocomposites deposited at (a) 100 W, (b) 150 W, (c) 200 W,
(d) 250 W, and (e) 300 W.
The obvious peaks were observed at angles (2θ) of 31.2⁰, 33.9⁰ and 35.7⁰ which correspond to
ZnO phase (100), (002) and (101) crystal planes, according to JCPDS 36-1451. Meanwhile, there
are additional peaks found at 47.1⁰, 56.1⁰ and 62.4⁰. This revealed that the needle-like ZnO formed
on TiO2 nanoparticles are hexagonal with a wurtzite structure as reported by Li Shi Wang et al.[18].
M. H. Habibi et al. reported that the intensities of the (100) peak was higher than the other peaks for
all the films, showing that there is highly oriented ZnTiO3 on the glass substrate [6]. The highest
intensity of (100) peak was observed in sample of 200 W and according to Wuff’s theorem, the
largest phase is suggested to be the phase which has the lowest surface energies [19].
For sample that deposited at 100W, all the observed peaks are corresponding to the peak of
ZnO/TiO2 nanocomposites which reported as ZnTiO3. Meanwhile, at 150 W the hexagonal ZnTiO3
were decomposed into cubic Zn2TiO4.When the RF power was further increased to 250 W, the peak
of TiO2 corresponding to crystal plane of (100) were observed at 250 W and above. The peak of
TiO2 then were decomposed into cubic Zn2Ti3O8
Conclusion
In summary, the needle-like ZnO nanostructures on TiO2 nanoparticles by the solution-
immersion method and RF magnetron sputtering, respectively were successfully prepared on the
glass substrates. The deposition of TiO2 nanoparticles on the substrate was controlled by RF powers
in the range of 100-300 W. The obtained ZnO/TiO2 nanocomposites are characterized by different
techniques: FESEM, EDX and XRD. At 200 W, more needle-like ZnO with smallest average
diameter (112 nm) appeared on the TiO2 nanoparticles, which also has the smallest average size of
36.3 nm . Zn, Ti and O were observed as major components in the thin films. The XRD results
showed the needle-like ZnO formed on TiO2 nanoparticles are hexagonal with a wurtzite structure.
20 30 40 50 60 70
200
400
600
800
1000
1200
1400
1600 (10
0)
(00
2) (1
01
)
Inte
nsi
ty (
counts
)
Zn
2T
i 3O
8
TiO
2
2Theta (°)
(a) (b) (c)
(d) (e)
Advanced Materials Research Vol. 832 599
It was found that ZnO/TiO2 thin films were succesfully deposited as nanocomposites with chemical
formula of ZnTiO3 at 100 W, Zn2TiO4 at 150 W and Zn2Ti3O8 at 200 W and above.
Acknowledgement We would like to express our gratitude to Research Management Institute, Universiti Teknologi
MARA (UiTM), Shah Alam, Selangor, Malaysia for financial support.
References
[1] Yi-Mu Lee and Hsi-WenYang, "Optimization of processing parameters on the controlled
growth of ZnO nanorod arrays for the performance improvement of solid-state dye-
sensitized solar cells," Journal of Solid State Chemistry, vol. 184, pp. 615-623, 2011.
[2] Z. L. Wang, "Nanostructures of zinc oxide," materialstoday, pp. 26-33, 2004.
[3] Bambang Veriansyah, Jae-Duck Kim, Byoung Koun Min, Young Ho Shin, Youn-Woo Lee,
and Jaehoon Kim, "Continuous synthesis of surface-modified zinc oxide nanoparticles in
supercritical methanol," J. of Supercritical Fluids vol. 52, pp. 76-83, 2010.
[4] Aarthy Sivapunniyam, Niti Wiromrat, Myo Tay Zar Myint, and Joydeep Dutta, "High-
performance liquefied petroleum gas sensing based on nanostructures of zinc oxide and zinc
stannate," Sensors and Actuators B vol. 157, pp. 232-239, 2011.
[5] Muzafar A. Kanjwal, Nasser A. M. Barakat, Faheem A. Sheikh, Soo Jin Park, and Hak
Yong Kim, "Photocatalytic Activity of ZnO-TiO2 Hierarchical Nanostructure Prepared by
Combined Electrospinning and Hydrothermal Techniques," Macromolecular Research, vol.
18, pp. 233-240, 2010.
[6] Mohammad Hossein Habibi and Maryam Mikhak, "Titania/zinc oxide nanocomposite
coatings on glass or quartz substrate for photocatalytic degradation of direct blue 71,"
Applied Surface Science vol. 258, pp. 6745– 6752, 2012.
[7] Y. Yang, Q.Zhang, B.Zhang, W.B.Mi, L.Chen, L.Li, C.Zhao, E.M.Diallo, and X.X.Zhanga,
"The influenceofmetalinterlayersonthestructuralandopticalpropertiesof nano-crystalline TiO2
films," Applied SurfaceScience, vol. 258, pp. 4532–4537, 2012.
[8] M. Abdul Khadar and N.A. Mohemmed Shanid, "Nanoscale fine-structure evaluation of RF
magnetron sputtered anatase films using HRTEM, AFM, micro-Raman spectroscopy and
fractal analysis," Surface & Coatings Technology, vol. 204, pp. 1366–1374, 2010
[9] S.K. Zheng, G. Xiang, T.M. Wang, F. Pan, C. Wang, and W.C. Hao, "Photocatalytic
activity studies of TiO2 thin films prepared by r.f. magnetron reactive sputtering," Vacuum
vol. 72, pp. 79–84, 2004.
[10] Red Sox Steve. The Foundation of Nanowires: Zinc Oxide [Online]. Available:
http://vagabondguru.com/BluePenguinReportDaily/2009/05/the_foundation_of_nanowires_
zinc_oxide.html
[11] Sheng Xu and Zhong Lin Wang, "One-Dimensional ZnO Nanostructures: Solution Growth
and Functional Properties," Nano Res, pp. 1-86, 2011.
[12] M. Z. M. M.H Abdullah, M.H Mamat, L.N Ismail, and M. Rusop, "Nanostructured Ti02
Photoanode prepared through sonication of P-25/Sol-Gel for Dye-sensitized Solar Cells,"
International Conference on Electronic Devices, Systems and Applications (ICEDSA), pp.
318-321, 2011.
[13] A. Sobczyk-Guzenda, M. Gazicki-Lipman, H. Szymanowski, J. Kowalski, P.
Wojciechowski, T. Halamus, and A. Tracz, "Characterization of thin TiO2 films prepared
by plasma enhanced chemical vapour deposition for optical and photocatalytic applications,"
Thin Solid Films, vol. 517, pp. 5409–5414, 2009.
[14] Cheol Ho Heo, Soon-Bo Lee, and Jin-Hyo Boo, "Deposition of TiO2 thin films using RF
magnetron sputtering method and study of their surface characteristics," Thin Solid Films,
vol. 475, pp. 183– 188, 2005
600 Nanoscience, Nanotechnology and Nanoengineering
[15] M. Z. M. N. A. M. Asib, S. Abdullah, and M.Rusop, "Effect of RF Power on Optimization
of Titanium Dioxide Nanostructures by RF Magnetron Sputtering," Advanced Materials
Research Vol. , vol. 667, pp. 104-109, 2013.
[16] S. A. Z. Khusaimi, H. A. Rafaie, F. W. M. Noor, M. H. Mamat, N. A. Ghani, N. Yusoff, N.
Abdullah, S. Abdullah, and M.Rusop, "A Surface Morphology Study On The Effect Of
Annealing Temperature To Nanostructured ZnO And Its Reaction Mechanism In Solution
Method," AIP Conf. Proc. , vol. 1136, p. 790, 2009.
[17] M. Hinman. (2012, 5 April 2013). Sample Preparation Guide. Available:
http://webs.wichita.edu/?u=semlab&p=/Sample_Preparation_Guide/
[18] Li ShiWang, MingWei Xiao, Xin Jian Huang, and Yan DanWu, "Synthesis,
characterization, and photocatalytic activities of titanate nanotubes surface-decorated by
zinc oxide nanoparticles," Journal of Hazardous Materials vol. 161, pp. 49-54, 2009.
[19] S. A. Z. Khusaimi, M. H. Mamat, M. Z. Sahdan, M. K. Ahmad, N. Abdullah, and M.
Rusop, "Controlled Growth of Zinc Oxide Nanorods by Aqueous-Solution Method,"
Synthesis and Reactivity in Inorganic, Metal-Organic, and Nano-Metal Chemistry, vol. 40,
pp. 190–194, 2010.
Advanced Materials Research Vol. 832 601
Nanoscience, Nanotechnology and Nanoengineering 10.4028/www.scientific.net/AMR.832 Preparation and Characterization of Needle-Like ZnO on TiO2 Nanoparticles by Solution-Immersion
Method and RF Magnetron Sputtering 10.4028/www.scientific.net/AMR.832.596