plasma coating on orthopaedic implant
TRANSCRIPT
On all types of substrates (metal, ceramic, PEEK)
Hydroxyapatite
Hydroxyapatite S101 Coating to help the primary anchoring and re-growth of bone. Thickness from 50 to 150µm according to demand
Porous titanium Porous coating to facilitate primary attachment. S301, S303 and S304, a roughness adapted to your needs.
Titanium / HAP Twin layer coating : the adhesion of titanium com-bined with the effectiveness of HA. S501 and S503 according to desired roughness
Alumina / HAP Twin layer coating S502 : The alumina ceramic protection against the metal ions and efficiency of HAP.
H I P
K N E E S H O U L D E R
S P I N E
HTI Technologies 49 av Franklin Roosevelt F-69150 Décines Cedex Tel :+33/4 72 02 56 96 Fax : +33/4 78 49 97 35 www.htitechnologies.com
Service
Metallic and ceramic coatings : Geometry and thickness adapted
to your specifications.
Monitoring of contamination with a test program shared
Booking planning according to your estimates, delivery to your of-
fice or directly to your sub-contractors.
Competence
30 years experience in the plasma coating technology.
Using high quality powder,
Upward and downward traceability from the powder to the deliv-
ered parts
Permanent monitoring of the parameters of spraying by computer
acquisition, automatic and permanent weighing powders, each or-
der is recorded.
Reactivity
Computer-assisted management of the entire process of production
for short and respected delivery times.
(In 2008, the average time to process an order less than 8 days).
All HTI team adapts to your needs and production requirements
and deadlines on a single phone call.
Advanced ceramics and coatings
PROCESS PLASMA
PLANNING
FIRST CONTROL
ORDER
SANDBLASTING
MASKING
BOOKING PLANNING
Installation
robot
Done in
certified clean
rooms
FINAL CONTROL
PACKAGING
FINITION
- Thickness control - Monitoring substrate heat + Test planning
- Roughness control
- Visual inspection + Test planning
- Visual inspection
STOCK
POWDER ORDER
CONTROL
CLEANING
SPRAYING
Validation process by methods QI QO QP
V2.2
009