PENGELOMPOKKAN SIFAT MEKANIK MATERIALNama : Hengki Irawan/ 2714201002NOType of Mechanical BehaviorsDefinition Test Methode/ StandardKeywordUnitsFormula

1Kekerasan/ Hardness Suatu ukuran ketahanan material solid terhadap variasi jenis deformasi permanen ketika diberikan gaya tekan (scratch, indentation, rebound) Scratch test

ASTM Paper MNL 46, use sclerometer.

Indentation hardness

1. Rocwell (ASTM E18)

2. Vicker(ASTM E92/ISO 6507-1)

3. Brinell (ASTM E10/ISO6506-1)

4. Knoop (ASTM E384)

Rebound hardness/ Dinamic hardness

1. Leeb rebound hardness test (ASTM A956)

Hardness, HV, HRC,HB, etcHR Scale (table 5 ASTM E018), HV, BHN, HKHR (A,C,D) : 100- h/0,002

HR (B,E,F,G, et) : 130-h/0,002

h.: depth of penetration

HV : 1,8544 x P/d2

P : force in kg, d : diagonal length of impression (mm)

BHN : P/ x D/2 x (D-(D2-d2)

HK : 14,229 x F/ L2

NOType of Mechanical BehaviorsDefinition Test Methode/ StandardKeywordUnitsFormula

2Kekuatan/ Strength Kemampuan suatu material atau bahan untuk menerima beban tanpa failure (semakin besar material mampu menerima beban semakin tinggi kekuatan material tsb) Note :

1. Tipe Beban

a. Transversal

b. Axial

c. Torsional

2. Tipe stress

a. Compresive

b. Tensile

c. Shear

Uji Tarik (Yield Strength, Tensile Strength, Modulus Elasticity, stress vs strain curve)a. Logam : ASTM E8b. Plastic/ polymer : ASTM D683

c. Paper : ASTM D828-97

Stress strainN/m2 (Pa), lbf / in2 (psi): P/ Aoe : / Lo : L /Lo

luluh : P offste (o,2%)/ Ao

E : / e

EMBED PBrush

NOType of Mechanical BehaviorsDefinition Test Methode/ StandardKeywordUnitsFormula

3tangguh/ toughness Kemampuan bahan dalam menyerap energy tanpa mengakibatkan terjadinya kerusakan.Impacted test

ASTM E23-12C : Notched bar Impacted test for metallic material

Tangguh, Transisi temperatur, serapan energiJ (ft.lbf)E = m.g.(h-h ')

EMBED PBrush

NOType of Mechanical BehaviorsDefinition Test Methode/ StandardKeywordUnitsFormula

4Fatigue/ Lelah Kemampuan bahan dalam menerima beban berulang di bawah yield strength material tersebut tanpa failureFatigue test

ASTM E606-606M

Lelah, beban cyclic dibawah yield strength, S-N CurveN/m2 (Pa), lbf / in2 (psi) vs number of cylicCrack Growth behavior :ASTM E647, E1457

Structural calculating S-N Curve :

ASTM E739-10, E1089-85 (2011) e1

NOType of Mechanical BehaviorsDefinition Test Methode/ StandardKeywordUnitsFormula

5Creep/ Mulur Kemampuan material untuk menahan terjadinya deformasi plastis dan tidak failure pada elevated temperatur dan fungsi waktu.Creep test dan stress rupture test : ASTM E139-11 : Standard test method for conducting creep, creep rupture, and stress rupture test

Mulur, elevated temperatur, fungsi waktu.N/m2 (Pa), lbf / in2 (psi) vs temperatur vs timeHomologous temp > 0,5Ht : testing temp/ melting temp > 0,5

Creep data :

Temp Vs Time Vs Stress di dapat creep rate

Didapat kurva LMP : creep strength

EMBED PBrush

EMBED PBrush

EMBED PBrush

EMBED PBrush

NOType of Mechanical BehaviorsDefinition Test Methode/ StandardKeywordUnitsFormula

6Keuletan/ ductility Kemampuan material untuk terdeformasi dengan mudah saat dikenakan beban tarik atau kemampuan solid material untuk menahan deformasi plastis tanpa rupture Uji Tarik (Yield Strength, Tensile Strength, Modulus Elasticity, stress vs strain curve)a. Logam : ASTM E8

b. Plastic/ polymer : ASTM D683

c. Paper : ASTM D828-97

Bend testing ASTM E290-14

Ulet, Mudah terdeformasi, beban tarik, wiringN/m2 (Pa), lbf / in2 (psi) : P/ Ao

e : / Lo : L /Lo

luluh : P offste (o,2%)/ Ao

E : / eVisual check

NOType of Mechanical BehaviorsDefinition Test Methode/ StandardKeywordUnitsFormula

7Kekakuan/ stifnessKemampuan suatu material untuk menerima beban atau tegangan tanpa terjadi perubahan bentuk / defleksi Uji Tarik (Yield Strength, Tensile Strength, Modulus Elasticity, stress vs strain curve)d. Logam : ASTM E8

e. Plastic/ polymer : ASTM D683

f. Paper : ASTM D828-97

Stifness and reliance tester

ASTM D747

ASTM E855 Method A

FTMS 191- 5202

FTMS 311- 4211

Kaku, Momen inersia, defleksiN/m2 (Pa), lbf / in2 (psi)

EMBED PBrush

EMBED PBrush

NOType of Mechanical BehaviorsDefinition Test Methode/ StandardKeywordUnitsFormula

8Resilience/ kelentingan Kelentingan adalah kemampuan suatu bahan untuk menyerap energi pada waktu berdeformasi secara elastis dan kembali kebentuk awal apabila bebannya

dihilangkan.

Uji Tarik (Yield Strength, Tensile Strength, Modulus Elasticity, stress vs strain curve)a. Logam : ASTM E8

b. Plastic/ polymer : ASTM D683

c. Paper : ASTM D828-97

Stifness and reliance tester

ASTM D747

ASTM E855 Method A

FTMS 191- 5202

FTMS 311- 4211

elastis, balik ke posisi semulaN/m2 (Pa), lbf / in2 (psi)

Ur : Reliance Modulus.

EMBED PBrush