novel polymer shelves (see projects section on linkedin)
TRANSCRIPT
PolymerWorks Team: Mick Blackwell, Ben Condro, Mark Dufresne, Brenton Lester, and Matt Lewis
Advisor: Dr. Gipson and Dr. Prins
Topic: Materials and Mechanics Project (SUDoKU Portfolio)
Non‐Traditional Polymer‐based Shelving Units
Shelf Unit Conceptual Portfolio (SUCP)
March 30, 2014
Mechanics and Materials Semester Project
Team: PolymerWorks
Students: Mick Blackwell, Ben Condro, Mark Dufresne, Brenton Lester, and Matt Lewis
Advisors: Dr. Kyle Gipson and Dr. Robert Prins
Page 2 of 38
Table of Contents
I. INTRODUCTION……………………………………………………………………… 3
II. LITERATURE REVIEW………………………………………………………………3
III. PURPOSE AND OBJECTIVES……………………………………………………… 4
IV. MATERIAL SELECTION ANALYSIS…………………………………………… .. 5
V. DESCRIPTION OF SHELVING UNITS…………………………………………….12
VI. MECHANICAL ANALYSIS………………………….……………………………..15
VII. SYNTHESIS OF ANALYSIS INTO DESIGN……………………………………..28
VIII. CONCLUSIONS AND RECCOMENDATIONS………………………………….30
IX. REFERENCES……..……………………………………………………………….. 30
X. APPENDIXES……………………………………………………………………..….32
Page 3 of 38
Introduction In order to properly design a product, mathematical analysis and analytical modeling for each component are necessary to obtain parameters and confirm feasibility of proposed designs. The following sections document four designs correlated to obtained customer needs in order design of a novel shelving system. Each design was modeled analytically using SolidWorks and mathematically analyzed using known mechanical methods. The mechanical analysis, ecological audits, and tabulated material properties were compared in order to choose the most appropriate material and design for fabrication of the product. Literature Review Research was conducted on common polymer-based product manufacturing methods due to project constraints requiring a polymer shelving unit, as well as known polymer benefits and disbenefits at large. An overview of the applicable research conducted will be explained and further information can be found in the references used. Polymers can be found in any department store or building around the globe. For instance, electrical outlets have a plastic face constructed from an electrically resistant polymer [8]. There are many methods of producing polymer products: thermoforming, extrusion, injection molding, blow molding, compression molding, plastic machining, and transfer molding [10]. However, some polymers are not feasible alternatives for select manufacturing processes. For example, polycarbonate is not normally shaped using the thermoforming process [10]. Moreover, blow molding is commonly used to produce thin walled products such as plastic bottles. Compression molding can only be used for a small subset of polymers and makes familiar items such as the previously mentioned wall outlet. Transfer molding is commonly used for molding of thermal sets, thus can only be used for a few select polymers [10]. For a shelving unit, a select set of polymers were chosen based off of needs discussed further in the document. Mentioned needs were established from surveys conducted within the target market. The surveys and results, in entirety, can be found in Appendix A3. As such, potential materials which passed screening were polycarbonate, high density polyethylene, and polypropylene. Materials such as polycarbonate and polypropylene are commonly molded using the process of injection molding. According to the Polymer Molding Handbook, “After over a century of world-wide production of all kinds of injection-molded products…the products can be processed successfully, yielding high quality, consistency, and profitability” [9]. Furthermore, note that different subsets of polymers will behave differently when molded by injection. For instance, polycarbonate (PC), if injection molded, would require special ventilation during cooling, since PC is hydroscopic material [9]. Therefore, designers must tradeoff between the only two viable methods remaining for a shelving unit: plastic machining and injection molding. Aspec Plastics states, “Molding theory states that you can purchase an expensive mold
Page 4 of 38
and produce inexpensive parts, or you can purchase an inexpensive mold and produce expensive parts” [11]. The general rule of thumb is as follows; when producing large amounts of products (100,000+) and low tolerances are acceptable, injection molding is considered the most cost efficient method [12]. Project constraints stated that the shelving unit would be produced in quantities larger than 100,000. Conversely, injection molding is heavy reliant on electricity for producing components. Approximately 90% of electricity consumed is used to operate the powerful machinery [13]. To better disperse the energy consumption into the actual components, multi-cavity molds should be utilized to increase component output per cycle [14, 15 (In particular, reference 15 offers many cost saving training videos correlated to injection molding)]. In conclusion, based off of conducted research and known product constraints, injection molding was the most feasible alternative for shelf production. A more detailed analysis of the project requirements and analysis is stated in the following sections. Purpose and Objectives The purpose of this project was to use the best aspects of a type of material to create a feasible and innovated shelving unit. The shelving unit should adhere to the four pillars of sustainability: technological, environmental, economic, and social. By using mechanical analysis, ecological audits, and found material properties, a designer can sufficiently validate the design decisions made during the process. The home market, described in the design restrictions, included college-aged 20-somethings. Furthermore, the material used for the fabrication of the shelving unit must consist mostly or entirely of plastics from the polymer class of materials. Objectives for the design process include the goals listed below:
Satisfy all customer needs while balancing the four pillars of sustainability. Design a shelving unit most suited for the injection molding process (See the Literature
Review section for the reasoning behind choosing injection molding). Minimize cycle time/material to minimize cost. Test all materials for coherence with known material property values. Rapid prototype the derived design for the shelving unit. Propose methods to increase incentives for the cradle-to-cradle life cycle.
The previous objectives were shown to be satisfied at project completion and/or addressed in the recommendations section.
Page 5 of 38
Section I: Material Selection Analysis Section I.1 discusses the steps taken to choose feasible materials for the customer’s desires. Section I.2 shows all ecological audit findings and discusses the societal, economical, and technical sustainability factors for each material.
Section I.1 Acquirement of customer needs began by formulating generalized survey questions pertaining to qualitative aspects of the storage unit. The survey questions used can be found in Appendix A3 along with pie charts depicting the numerical results. The results obtained from the surveys are shown below.
1. The storage unit should be stackable. Stackable was defined as the storage unit resting on a support structure. However, the unit should not be free standing, so the next best alternative was a wall mounted unit.
2. The storage unit must hold a minimum of 20 pounds. 3. The storage unit should cost between 0 to 100 USD. 4. The storage unit will most likely be used in a private room/study.
Following the establishment of basic product requirements, CES was utilized to help screen out unqualified polymers [6]. The chart shown below represents the materials qualified after a selection line and limitations were established (See Table 1 below).
Figure 1. Graph of Compressive Strength vs. Price for the CES class of polymers. The selection
line maintained a slope of 1.
Figure 1 shows only four polymers suitable for product development based off selection criteria and the selection line established. For all selection criteria, refer to the Selection Criteria section. Note the four materials: polyethylene, polycarbonate, polypropylene, and polystyrene. In order to further screen feasible material choices, research was conducted through CES to gather an understanding of all noted materials. Specifically, polystyrene was found to be unsuitable for storage needs due to the brittleness of the material (prone to chipping). Polystyrene is mostly used in small, rigid structures; such as pens, thus was not a feasible material choice for a shelf [6].
Page 6 of 38
The selection criteria for the three polymer choices can be seen in Table 1 below separated by general properties, processability, durability, and eco-properties. Shown below are the screening parameters utilized to choose the materials mentioned above. Table 1. All polymer selection criteria used for material selection.
For general properties, price constraints for all polymers were limited to less than 5 U.S. dollars per kilogram. The limit ensures cost effective material choices can be purchased within the provided stipend of 100$. Processability was limited by two processes: moldability and machinability. The values were ranked on a numeric scale from one to five; a value of one indicated the material was not recommended for the given process whereas a value of five corresponded to a highly recommended process. Moldability was selected at maximum process values, because the prototype storage unit will be designed for mass production. Castability and weldability were neglected in the limit stage created for the selection criteria, because neither process was being considered for the product production. Machinability was ranged between values of 4 and 5, which related to the assembly process and means of fabricating such as lathing and milling. Slight machining such as drill holes could pertain to the product design, therefore, the limit was included. Durability was governed by three limits: Thermal tolerance, resistance to aqueous solutions, and resistance to acids. The thermal tolerance described was constrained to a minimum temperature of 0°C and a maximum temperature of 150°C. The polymers selected were deemed excellent in terms of withstanding aqueous solutions of water, water with salt, and wine. All solution criteria chosen were typical to household use, thus common household items have the potential to interact with the material. Also, the polymers selected were labeled excellent when in contact with acetic acid (10%), citric acid (10%), and phosphoric acid (10%). The listed acids were included in the limit parameters, because the acids were common in cleaning chemicals. Therefore, the product must be compliant and resilient to the acids listed. The final limit described was the labeled recyclable under eco-properties. Recyclability was an important factor relative to sustainability. A recyclable product helps to complete the cradle-to-cradle life cycle, thus, the final constraint limiting the polymer selection was if the material was able to be recycled.
Page 7 of 38
Applying the above selection criteria with the CES software produced the polymers: polyethylene, polycarbonate, polypropylene, and polystyrene. The four polymers listed met the specified constraints described in the selection limits. As previously discussed, polystyrene was not considered due to the known usage and properties of the material. Therefore, the selected materials for the storage unit were: polyethylene, polycarbonate, and polypropylene. Furthermore, after the materials were chosen, all known CES parameterized were tabulated and the results are shown in Appendix A2.
Section I.2 The eco-audit was performed using the three chosen materials: polyethylene, polycarbonate, and polypropylene. When performing the eco-audit, CES asked for several criteria to ground the calculations. The criteria included the quantity of products, material used, mass of the product, end life, transport of the product, and the product use. The following section includes the values inserted for each criterion, explanations as to why each value was chosen, and presentation and explanation of the eco-audit.
-Criteria
The criteria set for the audit constraints were the material, manufacturing process, and end life for the product. The constraints included how many units of the product will be made, the material used, the manufacturing process, mass of each unit, and the end life goals for the product. Four concepts were developed using SolidWorks. Each concept included a shelf base and three supports. The supports can be made out the same material as the shelf base or out of a different material, such as a metal. For the eco-audit, the polymer concept designs 1 and 2 weighed approximately 16lb and were used as a baseline for comparison.
A quantity of 500,000 units were chosen to be manufactured, as determined from the project guidelines. The three materials audited were the three materials chosen as mentioned above: polypropylene, polycarbonate, and polyethylene.
The primary manufacturing process chosen was polymer extrusion, because the process is used mainly to make polymer sheets and most large polymer objects [6]. Polymer extrusion was most similar to injection molding, thus was a viable alternative for the analysis. Injection molding requires the purchase of plastic pellets, which are heated and forced into a mold. A more in-depth discussion of injection molding can be found in the Literature Review.
The end of life chosen was for the product to be downcycled. Recycle fractions for polymers are very low compared to other materials, with PET being the highest at about 18%. Thus, recycling polymers is expensive and can cost more than what the material is actually worth. Appropriately, the method of downcycling the products was chosen, which is the most similar to recycling. The polymer will be used for other products such as car upholsteries, park benches, etc.
Page 8 of 38
The criterion of transport was completed using all values given within the project instructions. The transport type was given to be a 32 tonne truck and the distance traveled was 1,000 miles. The use of the product was filled out using a combination of given values and assumed values. First, the country electricity mix was chosen to be North American. The product life was agreed to be 4 years, because the average college student attends school for 4 years. The criteria of mobile mode and static mode were disregarded as specified in the directions.
An example of the criteria that was inserted into CES is shown in Figure 2. In this example, polycarbonate was used as the material; the other two screens were the exact same, except polyethylene and polypropylene were used as the material.
Figure 2. Polycarbonate criteria.
-Results
The results of each of the materials are summarized in Tables 2-4 where the energy in kcal, energy %, CO2 in lb, and CO2 % were displayed for each process. As discussed previously, the processes included material, manufacturing, transport, use, and disposal.
Table 2. Polypropylene results.
Page 9 of 38
Table 3. Polycarbonate results.
Table 4. Polyethylene results.
The above results showed that the best selection for energy is polypropylene, because PP used the least total energy to manufacture, transport, and dispose. All of the EoL potentials for the materials were negative, meaning that there was energy available within the product at the end of products life. The more negative the value, the better the material was to downcycling. So, with respect to downcycling, polycarbonate is the best option.
The carbon footprint in pounds of each material was also derived and the best option was polyethylene, because PE created the least amount of carbon when manufactured, transported, and used. With respect to EoL potential, the best material to choose would be polycarbonate, because PC does not create any carbon when it is downcycled.
A better visual of the results for energy and carbon footprint are shown in Figures 3 and 4.
Figure 3. Energy summary chart for all three materials.
Page 10 of 38
Figure 4. CO2 footprint summary chart for all three materials.
To better compare the three materials with respect to total values and EoL potential, the results shown above were inserted into Excel and a new graph was created. The new graph was created by taking the total (for first life) values for each material and adding the first life totals to the EoL potential for each material. If the EoL potentials were negative, the values would decrease the total energy used or carbon created by the materials. The values and graph created are shown below in Figure 5.
Figure 5. Table and chart created using overall energy and carbon footprint.
Page 11 of 38
From the chart in Figure 6, the best choice of material, with regards to an eco-audit, was polyethylene. This material used slightly more overall energy than polypropylene, but created significantly less carbon throughout the life of the material. Polycarbonate created very little carbon throughout the process, however the overall energy needed is significantly higher than the other two materials.
In conclusion, the eco-audit showed that the best material to choose was polyethylene. Compared to polypropylene, PE used slightly more energy during the entire process, but created significantly less carbon compared to polypropylene. PC did not create significantly more carbon relative to polyethylene. Overall, considering the ranking for the eco-audit, the top choice was polyethylene. The true best choice should depend on consumer needs and minimize environmental impact. One may want a product that created the minimum amount of carbon during its lifetime and remain tough; the next best choice would be polycarbonate. If the user wanted a product that used the least amount of energy during the product life, then polypropylene would be the next best choice according to the audit.
-Further Impacts
Not only will the material selection have an effect on the environment, but the chosen material will affect the other three pillars of sustainability. With regards to the technical aspect, if the material selection were based just on the eco-audit, the chosen material may not be that the strongest material out of the considered materials. For instance, polyethylene was the most environmentally friendly, but with regards to strength; PE could support the least amount of weight. When the mechanical analysis was performed for each material, the analysis showed that polyethylene was the weakest. Therefore, there must be trade-offs when selecting the material to use. Depending on the desired trait, the product may be strong, but not environmentally friendly or vice versa.
If polyethylene was chosen, the actual product would not last as long as intended. The targeted life time of the shelving unit was to be 4 years, because that was the average time a person stays at college. If polypropylene was chosen as the fabrication material, the product may not last 4 years. See the durability properties of all materials in Appendix A2. The user would, thus, either buy a new shelf or get frustrated with the lack of strength and not purchase another unit.
With regards to social sustainability, customer dissatisfaction was not acceptable. A dissatisfied customer was considered a loss in potential profits. Conclusively, some of the four pillars may be positively affected by a certain design, while others may be negatively affected. Polycarbonate was chosen, because PC optimizes the strength vs. sustainability objectives proposed.
Page 12 of 38
Section II: Description of Shelving Units The four designs for each shelving unit were based off of known construction parameters. For instance, the studs in common households are placed between 16” and 24” apart center to center according to building code 5602.10.3 [1]. Given the shelf must be 45” wide, each support must also be placed 16” apart center to center, as the most common stud spacing was found to be 16” [16]. Appropriately, the following designs were produced with respect to the survey results obtained; the shelf should be wall mounted in a private study/room (Appendix A3). Shown below are the isometric 3D analytical shelving prototypes. Prototype 1 (also referred to as design 1 or concept 1) is shown below. Design 1 was based off of common household shelving systems.
Figure 7. The full-polymer shelving unit. Notice the shelf was supported by 3 truss-like
cantilever beams. A more involved representation of the model can be found in Appendix A1. Note design one failed to meet the thickness requirements for injection molding (less than 0.150”) [4 and 5]. Prototype 2 shown below incorporated metal supports in order to support the shelf. Prototype two could not be fabricated by injection molding, however, plastic machining was a viable alternative for this concept.
Figure 8. The polymer-metal shelving unit. Note the shelf was supported by thin metal braces. Again, see A1 for a more detailed view.
Note concept two was relatively simpler to machine, but required a material outside the polymer class.
Page 13 of 38
Prototype 3 shown below performed the highest when compared to all other shelving prototypes. However, concept 3 required a molding process that was unattainable.
Figure 9. The full polymer shelving unit with a bored shelf and triangular supports. Note concept 3 could not be machined with any known fabrication methods except for plastic machining due to the internal bores. Prototype 4, the chosen alternative, appropriately follows all injection molding guidelines established in the upcoming shelving analysis sections.
Figure 10. The full polymer shelving unit utilizing a ribbed shelving structure and the same supports as Figure 9.
Note concept 4 was able to be injection molded accorded to the established injection molding guidelines found in literature. Therefore, concept 4 was optimized for manufacturing purposes. Furthermore, based off of the known max force values shown in Section II and design specifications shown in Appendix A1, the prototypes should be used to support objects less than 12” in length from the wall and objects with a total weight less than the specified values in Section 2. Note each prototype requires external components for mounting purposes. As such, screws for mounting the supports to wall studs will need to be included and parameterized appropriately. The most applicable fabrication process for the shelving unit was derived through research and using the CES software. For practical purposes, two potential fabrication methods for a
Page 14 of 38
polycarbonate (PC) shelving system will be determined. PC was chosen based off of mechanical analysis results conducted, those of which can be found in the mechanical analysis section. The constraints derived from supplied analytical models and known material properties are shown below. For reference, the figure of the shelving system being discussed will also be shown below. Notice the shelf and supports are separate components.
Figure 10. The discussed PC shelvng system.
Material – PC, Thermoplastic (Use Tree-Limit, Polycarbonate)
Shape – 3D solid
Weight – 0.42kg (Support) and 4.89kg(Shelf)
Maximum Thickness – 0.15inch [2]
Precision – "(0.4mm) (Based on available shelving limitations)
Surface Finish– 0.5-2μm (Assuming quality relative to ordinary machined parts)
Batch Size – 500,000 (Base off of known project guidelines)
Primary Shaping Method
Using CES Level 3 with the above limiting factors, the following primary shaping processes could be used [6].
Primary Shaping Short list:
1. Compression Molding. 2. Injection Molding (Thermoplastics). 3. Thermoplastic Composite Molding (Ignored, since the material used will not be a
composite).
Thus, for primary shaping, compression molding and injection molding are viable alternatives. Benefits and disbenefits of the end product for each method are discussed below.
Compression Molding (CM):
Advantages – Cheaper relative to IM.
Disadvantages – High tooling costs, limited to simpler shapes, thermoplastics require heating and cooling cycles which reduce production rate.
Page 15 of 38
Injection Molding (IM):
Advantages – High production rate, high quality, inserts and screw-threads are possible, small angles are possible.
Disadvantages – Capital and tooling costs are very high, thick sections are not recommended, malfunctions during processing can be extremely dangerous.
For consolidation purposes, CM should not be used for the production of the shelving unit. The CM production rate for thermoplastics was much slower relative to IM [6]. However, IM would require higher startup costs for machinery. Thus, larger batch sizes will be needed to cover the accumulation of costs. IM, appropriately, could cover large batch sizes due to IM having a high production rate and high quality.
The IM complexity limits were of use due to the current design requiring screw holes. Even though thick sections are not recommended for IM, CES confirmed that a component with a thickness of 0.15” could be fabricated using IM. Note 0.15” was the maximum thickness in at any given section of the design.
In conclusion, the largest impact to the end product of shelving unit would be the accompanying costs of using IM. The price of the shelving unit will need to be fixed to off-set the operating costs of using IM. Therefore, pricing of the shelving unit may be closer to the client based max price of 100 USD.
Section III: Mechanical Analysis
A summary of derived mechanical analysis results is shown below separated into two sections. For free body diagrams and the derivation of forces acting on each component, please see the figures below. Supporting documentation for support analysis can be found in the support analysis section. The full free body diagrams for all shelving systems can be found in Appendix A4. Intermediate values used in calculation can be found in Appendix A5. SHELVING ANALYSIS.1 (Designs 1 and 2 shown in Figures 7 and 8, respectively) The loading scenarios described in the attached free-body diagrams included the weight of the shelving unit, shown as a uniformly distributed load, as well as the maximum allowable point load(s) spanning the shelving unit supports. The free-body diagrams shown were split into two different orientations. The first orientation entailed modeling the ends of the shelving unit as supported cantilever panels; the area spanned between the supports was modeled as simply supported panels. Considering that the unit was symmetric, only one analysis was needed for each scenario. In order to determine the loading scenarios present at the shelving supports, the maximum allowable loading force at the supports needed to be calculated. The shelving unit was required to support various loading scenarios and therefore cannot yield under stated conditions. The
Page 16 of 38
maximum allowable loading conditions, with respect to yielding, were dependent on the maximum allowable deflection of the unit. Following standard practice, the maximum deflection was described to be less than 1/360 the total length of the section being examined. The max deflection value for the cantilever scenario was calculated as 0.0167 in. and the max deflection value for the simply supported beam scenario was calculated as 0.0417 in. Following the standard values, deflection calculations were used to solve for maximum allowable point loading conditions. The loading scenarios and their corresponding deflection scenarios were described below: The maximum deflection for the cantilever panel was described by a uniformly distributed load and an end point load (as shown in the free body diagrams attached). Utilizing the free-body diagram, deflection equations were incorporated to model the deflection scenario present in the modeled cantilever panel. The conditions described produce the deflection scenario of:
, (Eq. 1)
Where delta represented the total deflection at the end of the panel by the summation of an applied point load (at maximum deflection scenario located at the end of the panel) and a uniformly distributed load. P was the unknown point load, l was the length of the panel, w represented the weight of the panel, E was Young’s Modulus, and I was the second moment of inertia for the panel.
Figure 11. Free-body Diagram of End Conditions for the Shelving Unit.
Following the free-body diagram above, the deflection scenario to calculate the maximum force load to yield the panel was described by manipulating Equation 1, to solve for the unknown force load P:
(Eq. 2)
P
Page 17 of 38
Inputting the appropriate variables into Equation 2 resulted in the maximum force load the cantilever panel could withstand without yielding. The maximum deflection for shelving sections spanning between the supports were modeled as simply supported beams and can be described by a uniformly distributed load covering the entire section and a point load located in at the center of the panel as shown below. Utilizing the free-body diagram, deflection equations were incorporated to model the deflection scenario present in the modeled panel. The conditions described produce the deflection scenario of:
, (Eq. 3) Where delta represented the total deflection across the panel by the summation of an applied point load (at the maximum deflection of a simply supported beam located at the center of the panel) and a uniformly distributed load. P was the unknown point load, l was the length of the panel, w represented the weight of the panel, E was Young’s Modulus, and I was the second moment of inertia for the panel.
Figure 12. Free-body Diagram of Mid-panel Conditions for the Shelving Unit.
Following the free-body diagram above, the deflection scenario to calculate the maximum force load to yield the panel was described by manipulating Equation 3, to solve for the unknown force load P:
(Eq.4)
Inputting the appropriate variables into Equation 4 resulted in the maximum force load the simply supported panel could withstand without yielding. Table 5 below shows the resulting values corresponding to the selected materials by solving Equations 2 & 3 for the maximum point loads with the respected scenarios mentioned above:
P
Page 18 of 38
Table 5. Maximum Force Loads for Modeled Scenarios
Note the full Excel sheet calculations can be found located in the Appendix A5. From Table 5 above, the resulting force values for variable P can be seen; that is, the forces shown were the maximum allowable loads that the shelf can be subjected to before yielding. These calculations were, as described earlier, based off of maximum conditions located at the shelving units’ most vulnerable points. Therefore, the shelf can withstand the described forces at the locations. However, to determine the total amount of force the shelf can withstand, a mechanics analysis was performed to determine the allowable forces provided by the shelving supports, shown below. Also note, the calculations described absolute max loading conditions without yielding; the values were calculated based off of modeling the ends of the shelving unit as panels—not the designed irregular shape. Therefore, the loading conditions should be considered to be less than that of allowable loading conditions. Also, because deflection was described with respect to Young’s modulus, the selected material should resemble the largest value for Young’s modulus, thus providing the largest magnitude of loading support.
SUPPORT ANALYSIS.1 (Designs 1 and 2 shown in Figures 7 and 8, respectively) The supporting structures of the shelf forces must be parameterized appropriately in order to not fail. Shown below are the methods taken to determine the max allowed force for both types of supporting structures. -Metal Braces Following the same procedure to determine the maximum load applied for the modeled cantilever panel, the support forces can be found utilizing a similar method. Notice, that for concept two, the metal supports were designed as thin connected metal panels. Thus, the supports were modeled as two parallel plates and a cantilever beam under deflection. By solving for the maximum load at which the panel yields, the maximum load the supports can hold was calculated. The maximum deflection for the cantilever support beam was described by a uniformly distributed load and a point load, as shown in the free body diagrams below. Utilizing the free-body diagram, deflection equations were incorporated to model the deflection scenario present in the modeled cantilever support. The conditions described produce the relation shown below.
, 3 (Eq. 5)
Material Young's Modulus, E (psi) Moment of Inertia (I), Iyy (in^4) Max force, lbf (Cantilever) Max force, lbf (Panel)
Polypropylene 177500 0.125 4.204 9.265
Polyethylene 110050 0.125 2.252 4.269
Polycarbonate 322000 0.125 8.385 19.969
Page 19 of 38
Where delta represented the total deflection across the support by the summation of an applied point load and a uniformly distributed load, P was the unknown point load, l was the length of the panel, a & x were the distance to the point load, w represented the weight of the panel, E was Young’s Modulus, and I was the second moment of inertia.
Figure 13. Free-body Diagram of Metal Support.
Following the free-body diagram directly above, the deflection scenario to calculate the maximum force load to yield the supports were described by manipulating Equation 5 to solve for the unknown force load P.
(Eq. 6)
Inputting the appropriate variables into Equation 6 resulted in the maximum force load the supports could withstand without yielding. Table 6 below shows the resulting values for the maximum point load allowable for the metal supports: Table 6. Maximum Force Loads for Metal Supports.
Note the full Excel sheet calculations can be located in Appendix A6. As seen in Table 6, the maximum force the supports can maintain is roughly 300 lbf. Thus, the calculated loading scenario for the supports are greater than those loads provided at the middle and end sections of the shelving unit. Therefore, the metal supports can support the shelf with applied loads described in Tables 5 & 6 at their respected locations.
Material Young's Modulus, E (psi) Moment of Inertia (I), Iyy (in^4) Max force, lbf (Cantilever)
Cast Stainless Steel 27557170.16 0.0247 300.209
P
Page 20 of 38
-Polymer Truss-like Supports In order to calculate the maximum force that the polymer truss-like supports could support, the frame must first be analyzed. When analyzing the frame, the assumption was made that the joints of the support were rigid and, as such, the support would fail when one of the three highlighted areas, seen below, would fail. The support can be seen below in Figure 14.
Figure 14. The free body diagram for the truss-like support.
The three main areas of concern for the shelf to fail are the areas in red. It is assumed that these three boxes can be looked at as a cantilever beam, a simply supported beam, and as a vertical column respectively. The cantilever beam (box one in Figure 14) is displayed below in Figure 15 where P represented the load from the shelf and Po represented the density of the material the support is made from times the cross sectional area of the beam.
Figure 15. The free body diagram of a cantilever beam in the truss-like support.
The max allowable deflection of a beam, , was found using Equation 7.
(Eq.7)
Po
P
Page 21 of 38
Where L was the length of the beam. Using this maximum allowable deflection, the maximum point load that the beam could handle, P, was found using Equation 8.
∗ 3 / (Eq.8)
Where E was the modulus of elasticity for each material, I was the moment of inertia for the beam, and Po was the distributed load as described previously. The results of Equation 8 for each material, which described the maximum allowable point load as shown in Figure 15, can be seen below in Table 7. Table 7. Cantilever analysis on truss-like support.
As seen from Table 7 polypropylene, polyethylene, and polycarbonate can support approximately 1.5 lbf, 1 lbf, and 3 lbf respectively. The simply supported beam (box two in Figure 14) is displayed below in Figure 16 where P represented the load from the shelf and Po represented the density of the material the support is made from times the cross sectional area of the beam.
Figure 16. The free body diagram of the simply supported beam in the truss-like support
The max allowable deflection of a beam, , was found using Equation 9.
(Eq.9)
Where L was the length of the beam.
Po
P
Page 22 of 38
Using this maximum allowable deflection, the maximum point load that the beam could handle, P, was found using Equation 10.
∗ 48 / (Eq.10)
Where E was the modulus of elasticity for each material, I was the moment of inertia for the beam, and Po was the distributed load as described previously. The results of Equation 10 for each material, which described the maximum allowable point load as shown in Figure 15, can be seen below in Table 8. Table 8. Simply supported beam analysis on truss-like support.
As seen from Table 8 polypropylene, polyethylene, and polycarbonate can support approximately 1650 lbf, 1000 lbf, and 3000 lbf respectively. The diagonal support (box three in Figure 14) was modeled as a vertical column and the critical load was modeled with Euler’s formula, as derived below. In order to determine the correct formula, the slenderness ratio must be compared to the column constant. The radius of gyration, r, was found using Equation 11.
/ (Eq.11) Where I was the moment of inertia and A was the cross-sectional area of the column. The slenderness ratio, S.R., was found using Equation 12.
. . (Eq.12)
Where K was the end condition constant for the column and L was the length of the column. The column constant, Cc, was found using Equation 13.
(Eq.13)
Where E was Young’s modulus of the material and σy was the yield strength of the material. Since for all three materials the slenderness ratio was larger than the column constant; the column was considered relatively long and was analyzed using the Euler formula seen below in Equation 14.
Page 23 of 38
(Eq.14)
Where Pcr was the critical load on the column before it could fail. The maximum supported force of the shelf, Fs, by all three supports was written in terms of the critical load of an individual column according to the angle, θ, made between the connection of the support and horizontal beam as seen in Equation 15.
3 (Eq.15) The results of the above equations can be found below in Table 9. Table 9. Maximum Force Loads for Polymer Supports.
As seen in Table 9, the polypropylene, polyethylene, and polycarbonate supports could support a maximum force of approximately 1375 lbf, 850 lbf, and 2500 lbf respectively. Through this analysis the truss-like support structure was limited due to the front cantilever section. This part of the support limited the design of the shelf so that it became the limiting factor of the entire shelving unit. SHELVING ANALYSIS.2 (Designs 3 and 4 shown in Figures 9 and 10, respectively) The previously proposed designs were unable to be fabricated with standard injection molding procedures. For instance the standard recommended thickness range for polycarbonate was 0.04” to 0.15” [2]. Injection molding has high start-up costs due to the initial cast-molds needed to begin processing. However, over time, the startup cost for injection molding has potential to be offset by the savings relative standard machining (milling and lathing being the only other feasible method to produce the shelving units) [3]. Thus, injection molding was determined to be the most cost efficient option to produce mass amounts of product. In general, injection molding has a lower tolerance and a rougher finish when compared to standard machining. Since Designs 3 and 4 both have no need for precision greater than 0.005”, injection molding was still a viable alternative. Injection molding requires a large amount of guidelines to be met in order to confirm successful product fabrication. Design criteria discussed below can be found by referring to the reference section [4 and 5]. In summary, drafts, fillets, radii, gussets, ribs, intersecting thicknesses, and overall product dimensions must be considered when designing a product for injection molding.
Page 24 of 38
The following diagrams show the cross sectional area for designs 3 and 4. Equations 1-6 were still valid for the panel force analysis, however, the moment of inertia differs from the previous designs.
Figure 17. The bored shelving unit design.
Figure 18. The ribbed shelving unit design.
Note the height of the cross section in Figure 18 (concept 4) was optimized to minimize material while still meeting the needed 20lbf minimum support. The minimum moment of inertia for the ribbing structure must be 0.066 in order to support 20lbf according to the Excel equation solver. Thus, due to the design guidelines discussed below, only the height of the shelf could be optimized. The minimum height value to achieve the 20lbf was found to be approximately 0.625" by constructing iterations of the SolidWorks model. Concept 4 utilized a height 0.65" to ensure the minimum standard was achieved. The previous cross sections were used to determine the moment of inertia for each respective design. The following parameters were determined based off of known design guidelines for injection molding and were described sufficiently [4 and 5]. Design Guidelines
Inner radii: 0.5*t, where t was the general thickness of the design and t equaled 0.15” for both designs.
Outer radii: 1.5*t Rib Spacing (RS): RS>2*t, 0.5” or 0.68” depending on design characteristics. Rib Width (RW): 40-60% of t, bored shelving unit RW = 0.1”, ribbed shelving unit RW
= 0.075”. Rib Height (RH): RH 3*t. RH = 0.45”.
Page 25 of 38
Gussets in Supports: Spacing = 0.5”, Length = 0.5”, width = 0.45”, gusset thickness = 0.075”, fillet radius = t*0.25, and spacing = 0.15”*2 (See Appendix A8 for an argument for gusset implementation).
Draft: Between 1° and 2° for all components. For design 3, the following max force allowed is shown below with accompanying intermediate results. Note by this time in the design process, polycarbonate was chosen as the appropriate material, thus only the average polycarbonate Young’s modulus E was used [6]. Table 10. The intermediate values and max force for design 3.
Panel Deflection Max, in Length, in Ixx, in^4 Eavg, psi Pmax, lbf
0.04 13.70 0.33 322000.00 75.83
Ends Deflection Max, in Length, in Pmax, lbf
0.01 5.35 31.08
For design 4, the following max force allowed is shown below with accompanying intermediate results.
Table 11. The intermediate values and max force for design 4.
Panel Deflection Max, in Length, in Ixx, in^4 Eavg, psi Pmax, lbf
0.03 11.88 0.06 322000.00 24.1
Ends Deflection Max, in Length, in Pmax, lbf
0.01 5 8.48
Thus, design 3 seemingly was the most appropriate choice based off of derived force values. However, design 3 had a major flaw in relation to draft required for injection mold extraction. Design 3 would require the draft to be placed along the large faces of the shelf, thus causing the main faces of the shelf to be non-uniform. The main faces for a shelf are necessarily flat, thus design 3 was disregarded. Design 4 is capable of being extracted perpendicular to the main face, thus the drafts were appropriately placed on the sides and the ribbing. For an example, see Figure 19 below.
Figure 19. Displays the draft on the outside edge and inner ribbing.
Page 26 of 38
Following the shelf analysis, the support analysis was conducted for feasibility. Note the maximum load experienced by design 4 at any given time should not exceed 50lbf Thus, the
supports should support at least 17 each (since there were 3 supports in this design).
SUPPORT ANALYSIS.2 (Designs 3 and 4 shown in Figures 9 and 10, respectively) Again, the supporting structures shown in Figures 9 and 10 were designed with injection molding in mind. Each support has an inward draft with respect to extraction. The supports were modeled as a cantilever beam with a linearly varying depth with respect to cross sectional area. Common practice dictates the moment of inertia be taken at the distance to the centroid of the cantilever shape for a minimum bound of derived values [7]. For reference, a free body diagram of the support is shown below. For the lowest possible sustainable force, only one triangular cantilever section was modeled.
Figure 20. The free body diagram for the support structure. The assumed moment of inertia (shape shown with the dashed line in Figure 18), thus, was that of a rectangular support of thickness 0.15”, length 11.15”, and depth of 1.33”. Table 12. The minimum sustainable force by one support.
Max Deflection, in thickness, in depth, in I, in^4 length, in Pmin, lbf
0.031 0.15 1.33 0.023 11.15 20.64
Note, the design will succeed based on the estimations above, since each support could support, at a minimum, 20lbf (exceeding the 19lbf estimated above Table 5). Therefore, design 4, shown in Figure 10, will be the design pursued for final product fabrication.
Page 27 of 38
Mounting Analysis (Screw Selection) In order to properly mount the shelving unit to specified wall studs, the selection of screws was necessary. The screws were selected based on known standards discussed below and qualitative reasoning. The shelf will support, at maximum, a total of 60lbf. Each screw was specced to support the 60 lbf maximum load. Thus, the shear force in the screw member is also 60lbf. Using the Fastenal Handbook and NDS building codes, the following relations were derived. The actual shear stress in a screw member was as follows.
4 ∗ (Eq. 12)
Where was the actual shear stress in a screw member of circular cross sectional area, was the circular cross section area for each screw [17]. The Fastenal Handbook stated the acceptable limit for screw shear stress could be approximated as follows.
∗ 0.6 (Eq. 13) Where was the acceptable shear stress and was the ultimate strength of low-carbon steel (material of commonly used screws, 50ksi) [18, 6]. Thus, = 30ksi. Now, the following relations was derived in order for a screw to be considered as a feasible alternative.
(Eq. 14) The screws to be considered for selection were tabulated using the information available from Bolt Depot [19]. The results obtained were as follows. Table 13. The screw diameters (D), calculated shear stress, safety factor in relation to the acceptable shear stress, and the known diameters of available washers. Note Fender washers were chosen due to out diameter being larger relative to normal washers [19].
Screw Size D, in , ksi Safety Factor , in
#2(Cannot use Fender washer) 0.086 13.77 2.18 Void
#4(Cannot use Fender washer) 0.112 8.12 3.69 Void
#5(Cannot use Fender washer) 0.125 6.52 4.60 Void
#6 0.138 5.35 5.61 0.625
#8 0.164 3.79 7.92 0.75
#10 0.19 2.82 10.63 1
#12(Cannot use Fender washer) 0.216 2.18 13.74 Void
Page 28 of 38
Note the largest possible washer, in relation to screws sizes shown in Table 11 that was able to fit between the gussets of concept 4, was 1in in diameter. In order to maximize the amount of surface contact from the screw member, the largest diameter washer possible was chosen, which allowed screw alternatives to be screened. The maximum amount of surface contact at the washer to support interface was necessary in order to minimize the stress around the screw holes. However, the previous statement was made on a qualitative basis and optimization of the washer surface area should be conducted in further studies. Section IV: Synthesis of Analysis into Design In order to choose the best alternative for the shelving material, a reflection on obtained mechanical analysis results, ecological audit results, and known tabulated material properties was necessary. The following sections describe the screening of polycarbonate, polyethylene, and polypropylene in order to choose one material for further product development.
Mechanical Analysis Polycarbonate, from the mechanical analyses, supported the largest applied loads, primarily due to Polycarbonate’s’ inherently large Young’s Modulus value. When calculating the applied force loads, the limiting factor for such calculations were dependent on Young’s modulus values. In turn, Polycarbonate had the largest of the three materials chosen. Therefore, it follows Polycarbonate was the material which could support the greatest loads. Polypropylene fell within the middle margin of the materials on the basis of the mechanical analyses. The values calculated for Polypropylene rested between Polycarbonate and polyethylene respectively. Therefore, Polypropylene remained relatively neutral with respect to the other material choices. Choosing polyethylene resulted in supporting the lowest applied load values, which was correlated to polyethylene having a lower Young’s Modulus value. Thus, polyethylene suffered in terms of supporting applied loads when compared to other materials chosen for the shelving unit.
Ecological Audit
Polycarbonate created the least amount of carbon throughout its lifetime and did not require significantly more energy than the other two materials. Polycarbonate used a large amount of energy to produce and use, but created small amounts of overall carbon during the product life cycle. Polypropylene was the opposite; PP does not require as much energy as polycarbonate, but created large amounts of carbon throughout its entire lifecycle. Throughout the lifecycle process, polypropylene required the least amount of energy, but produced the most amount of carbon. The overall calculations of carbon and energy required showed that polypropylene was not a viable choice regarding environmental sustainability.
Page 29 of 38
In regards to environmental sustainability, polyethylene was the top material to choose. PE required slightly more energy during the product lifetime, but created very little carbon during the overall lifecycle. The previous mentioned factors led PE to be the top choice in regards to the ecological audit.
Material Properties (Refer to Appendix A2)
PC had the highest maximum Young’s Modulus (E= 2.44 Gpa). Thus, PC could support the highest load with respect to the derivations produced in Section II. However, PC also cost the most per unit kg. Remember, in order to stay within the clients budget, the shelving system should cost less than 100 USD. Appropriately, the shelving unit was less than 20kg, causing the cost to be less than 100 USD. All PC shelving units were found to support over 40 Lbf (See Table 5), satisfying the customer need requirement of 20 . The max E for polypropylene was 1.55 Gpa. Thus, if the shelving unit was made from polypropylene, the shelving unit could not hold an appropriate amount of weight with respect client satisfaction (could only support 18.4 lbf, referring to Table 5). PE was not a feasible alternative due to the amount of weight supported when compared to PC and PP. PE had the lowest max E (0.896 Gpa). Thus, PE was found to only be able to support a max of approximately 10Lbf. Again, see Table 5 for all found shelving forces. Note each material above maintained similar material properties throughout screening (Refer to Section 3). Thus, when considering fabrication benefits between materials, all materials were machined similarly. SolidWorks fabrication analysis was used to test the fabrication capabilities of each component. According to SolidWorks, the polymer components were able to be milled and lathed and the steel component was made using sheet metal processing. The polymer and steel components were parameterized based off of known sheet thicknesses sold by manufactures. Injection molding was viable alternative relative to the design practices used in concept 4 (Figure 10). Injection molding was most viable when cycling time was minimized and product changes are unnecessary. As such, a design which can be molded in one molding instance would be the most cost and energy efficient option.
Page 30 of 38
Conclusions and Recommendations In conclusion, based on the above summaries for the three materials and when considering all aspects mentioned throughout the above documentation, polycarbonate will be the material chosen for further product development. PC was the only feasible alternative when considering acquired customer needs. Future work involves analyzing injection molded material samples in order to further verify material properties. Recommendations include optimizing the thicknesses parameterized for the injection molding process to use the least amount of material and still support the anticipated load. A design which can be easily molded in one molding instance should be considered, as the savings and negative impacts would be maximized and minimized, respectively. Incentives to increase recycling awareness should be displayed on packaging and made easily accessible. For instance, if the product was returned to the company after the useful life duration, a discount on the next model would be made available. Lastly, a scale model of concept four should be created to demonstrate feasibility. References (Number System: In-Text Citations)
[1] N.p. Web. 30 Mar 2014. <http://www.mass.gov/eopss/docs/dps/780-cmr/780056b.pdf>.
[2] "Basics of Injection Molding Design." Quickparts. 3DSystems, n.d. Web. 30 Mar 2014. <http://www.quickparts.com/LearningCenter/BasicsofInjectionMoldingDesign.aspx#wall thickness>.
[3] Gerard, Katie. "Plastic Injection Molding vs. Plastic Machining: How to Decide." Craftech Industries INC. N.P., 06 Sep 2013. Web. 30 Mar 2014. <http://info.craftechind.com/blog/bid/333498/Plastic-Injection-Molding-vs-Plastic- Machining-How-to-Decide>.
[4] "Injection Molding Design Guidelines." GE Plastics. General Electric Co. Web. 30 Mar 2014. <http://www.polymerhouse.com/datasheets/GE_Thermo Plastic DesignGuide_[1].pdf>.
[5] "Injection Molding Design Guidelines."Solid Concepts Inc. Web. 30 Mar 2014.
[6] "Granta's CES EduPack." Granta Material Intelligence. Granta Design Limited 2013.
[7] Paglietti, A, and G Carta. "Remarks on the Current Theory of Shear Strength of Variable Depth Beams."Bentham Science. Department of Structural Engineering, University of Cagliari, Italy, 02 Jan 2009. Web. 30 Mar 2014. <http://www.benthamscience.com/open/tociej/articles/V003/28TOCIEJ.pdf>.
[8] "History of Polymers and Plastics for Teachers." American Chemistry. American Chemistry Council, Inc., n.d. Web. 1 Apr 2014. <http://plastics.americanchemistry.com/Education- Resources/Hands-on-Plastics/Introduction-to-Plastics-Science-Teaching-
Page 31 of 38
Resources/History-of-Polymers-Plastics-for-Teachers.html>. [9] Rosato, Dominick V., Donald V. Rosato, and Marlene G. Rosato, eds. Injection molding handbook. Springer, 2000.
[9] Rosato, Dominick V., Donald V. Rosato, and Marlene G. Rosato, eds. Injection molding handbook. Springer, 2000. [10] Kopeliovich, Dmitri. "Methods of Polymers Fabrication."Subs Tech. N.P., 27 Jul 2013. Web. 1 Apr 2014. <http://www.substech.com/dokuwiki/doku.php?id=methods_of_polymers_fabrication>. [11] "ASPEC Secondary Machining of Plastic Parts." ASPEC. N.p. Web. 1 Apr 2014. <http://www.aspecplastics.com/secondary-machining.html>. [12] Admin, . "EPP Corporation." Plastic Machining: Custom Plastic Components- Molding vs. Machining. EPP Corporation-Plastic Machining Experts, 29 Jun 2011. Web. 1 Apr 2014. <http://eppcorp.com/custom-plastic-components-molding-vs-machining-2/>. [13] "Energy Efficiency in Plastics Processing." Tangram. Tangram Technologies. Web. 1 Apr 2014. <http://www.tangram.co.uk/TI-Energy Worksheets (Plastics) - Tangram.PDF>. [14] "Injection Molding." 3D Systems. N.p. Web. 1 Apr 2014. <http://www.3dsystems.com/solutions/injection-molding>. [15] BPF Training. British Plastics Federation. Web. 1 Apr 2014. <http://www.bpftraining.com/library/energy_efficiency_in_injection_moulding>. [16] Stansley, Kit. "Three Ways to Find a Wall Stud." Bobvila. Bobvila, n.d. Web. 20 Apr. 2014. <http%3A%2F%2Fwww.bobvila.com%2Farticles%2Fhow-to-find-a-wall- stud%2F%23.U1QZTfldXCs>. [17] Wood Council, American. "National Design Specification." NDS for Wood Construction. AWC, 1 Jan. 2005. Web. 28 Apr. 2014. <http://www.awc.org/pdf/NDSCommentary2005.pdf>. [18] "Fastenal Industrial and Construction Supplies." Technical Reference Guide. Fastenal, 1 Jan. 2005. Web. 28 Apr. 2014. <http://www.fastenal.com/content/documents/FastenalTechnicalReferenceGuide.pdf>. [19] "Bolt Depot." Bolt Depot.com. Bolt Depot, 1 Jan. 2014. Web. 28 Apr. 2014. <http://www.boltdepot.com/Fender_washers_Stainless_steel_18-8.aspx>.
Page 32 of 38
Appendix A1 Please see labeled attachments for the CAD drawings of Figures 7, 8, 9, and 10.
Attachment 1: Shows the support structure for Figure 7. Attachment 2: Shows the shelving structure for Figure 7. Attachment 3: Shows the support structure for Figure 8. Attachment 4: Shows the shelving structure for Figure 8. Attachment 5: Shows the shelving structure for Figure 9. Attachment 6: Shows the support structure for Figure 9 and Figure 10. Attachment 7: Shows the shelving structure for Figure 10.
A2 All CES values for each material are shown below [6]. Polypropylene Values:
General Properties Min Max Avg. Units
Density 890 910 900 kg/M^3
Price 1.92 2.21 2.065 USD/kg
Mechanical Properties Min Max Avg. Units
Young's Modulus 0.896 1.55 1.223 Gpa
Shear Modulus 0.316 0.548 0.432 Gpa
Bulk Modulus 2.5 2.6 2.55 Gpa
Poisson's Ratio 0.405 0.427 0.416 Gpa
Yield Strength (elastic) 20.7 37.2 28.95 Mpa
Tensile Strength 27.6 41.4 34.5 Gpa
Compressive Strength 25.1 55.2 40.15 Gpa
Elongation 100 600 350 %
Hardness 6.2 11.2 8.7 HV
Thermal Properties Min Max Avg. Units
Max Service Temperature 100 115 107.5 °C
Min Service Temperature ‐123 ‐73.2 ‐98.1 °C
Thermal Conductivity 0.113 0.167 0.14 W/m.°C
Specific Heat 1.87E+03 1.96E+03 1915 J/kg.°C
Page 33 of 38
Electrical Properties Min Max Avg. Units
Conductor/Insulator Good Insulator
Electrical Resistivity 2.1 2.3 2.2 μohm.cm
Optical Min Max Avg. Units
Transparency Translucent
Refractive Index 1.48 1.5 1.49 ‐
Processability Min Max Avg. Units
1 = Low 5 = High
Castability (1‐5) 1 2 1.5 ‐
Moldability 4 5 4.5 ‐
Machinability 3 4 3.5 ‐
Weldability 5 ‐ ‐ ‐
Eco Properties Min Max Avg. Units
Embodies Energy 75.7 83.7 79.7 MJ/kg
CO2 Footprint 2.96 3.27 3.115 kg/kg
Recyclable (Yes/No) Yes ‐ ‐ ‐
Polyethylene Values:
General Properties Min Max Avg. Units
Density 939 960 949.5 kg/M^3
Price 1.176 1.94 1.558 USD/kg
Mechanical Properties Min Max Avg. Units
Young's Modulus 0.621 0.896 0.7585 Gpa
Shear Modulus 0.218 0.314 0.266 Gpa
Bulk Modulus 2.15 2.25 2.2 Gpa
Poisson's Ratio 0.418 0.434 0.426 Gpa
Yield Strength (elastic) 17.9 29 23.45 Mpa
Tensile Strength 20.7 44.8 32.75 Gpa
Compressive Strength 19.7 31.9 25.8 Gpa
Elongation 200 800 500 %
Hardness 5.4 8.7 7.05 HV
Thermal Properties Min Max Avg. Units
Max Service Temperature 90 110 100 °C
Min Service Temperature ‐123 ‐73.2 ‐98.1 °C
Thermal Conductivity 0.403 0.435 0.419 W/m.°C
Specific Heat 1.81E+03 1.88E+03 1845 J/kg.°C
Page 34 of 38
Electrical Properties Min Max Avg. Units
Conductor/Insulator Good Insulator
Electrical Resistivity 3.30E+22 3.00E+24 1.52E+24 μohm.cm
Optical Min Max Avg. Units
Transparency Translucent
Refractive Index 1.5 1.52 1.51 ‐
Processability Min Max Avg. Units
1 = Low 5 = High
Castability 1 2 1.5 ‐
Moldability 4 5 4.5 ‐
Machinability 3 4 3.5 ‐
Weldability 5 ‐ ‐ ‐
Eco Properties Min Max Avg. Units
Embodies Energy 77 85.1 81.05 MJ/kg
CO2 Footprint 2.64 2.92 2.78 kg/kg
Recyclable (Yes/No) yes ‐ ‐
Polycarbonate Values:
General Properties Min Max Avg. Units
Density 1.14E+03 1.21E+03 1175 kg/M^3
Price 4.1 4.51 4.305 USD/kg
Mechanical Properties Min Max Avg. Units
Young's Modulus 2 2.44 2.22 Gpa
Shear Modulus 0.789 0.872 0.8305 Gpa
Bulk Modulus 3.7 3.9 3.8 Gpa
Poisson's Ratio 0.391 0.408 0.3995 Gpa
Yield Strength (elastic) 59 70 64.5 Mpa
Tensile Strength 60 72.4 66.2 Gpa
Compressive Strength 69 86.9 77.95 Gpa
Elongation 70 150 110 %
Hardness 17.7 21.7 19.7 HV
Thermal Properties Min Max Avg. Units
Max Service Temperature 101 144 122.5 °C
Min Service Temperature ‐123 ‐73.2 ‐98.1 °C
Thermal Conductivity 0.189 0.218 0.2035 W/m.°C
Specific Heat 1.53E+03 1.63E+03 1580 J/kg.°C
Page 35 of 38
Electrical Properties Min Max Avg. Units
Conductor/Insulator Good Insulator
Electrical Resistivity 1.00E+20 1.00E+21 5.5E+20 μohm.cm
Optical Min Max Avg. Units
Transparency Optical Qualtiy
Refractive Index 1.54 1.59 1.565 ‐
Processability Min Max Avg. Units
1 = Low 5 = High
Castability 1 2 1.5 ‐
Moldability 4 5 4.5 ‐
Machinability 3 4 3.5 ‐
Weldability 5 ‐ ‐ ‐
Eco Properties Min Max Avg. Units
Embodies Energy 103 114 108.5 MJ/kg
CO2 Footprint 5.74 6.35 6.045 kg/kg
Recyclable (Yes/No) yes ‐ ‐
A3 The list of survey questions in entirety are shown below. Note survey questions were approved by engineering faculty available for consultation. 1. When storing items, what type of unit would you prefer? “unit(explanation/visual)” A. Free Standing (supported by itself) B. Wall Mounted C. Stackable (rests on support structure) D. Free Hanging (chandelier) 2. How much weight would you store on/in your preferred unit? “weight(approximation of object weight)” A. 0-10lb (a few tools) B. 10-15lb (bowling ball) C. 15-20lb (a few textbooks) D. 20-30lb (3 gallons of water) 3. How much would you be willing to pay for your desired unit? A. 0-50$ B. 50-100$ C. 100-150$ D. 150-200$ E. $ > 200$ 4. Where would you want your desired unit? A. Public Room B. Private Room C. Utility Room D. Outside E. Other:_______________________ 5. Please flip the survey over and write any other queries or/and expand your answer choice(s).
Page 36 of 38
The following figure depicts the results obtained from the surveys.
Figure 21. Displays percent responses for the survey questions directly above. Figure 21 breaks down each survey question into percent pie charts for pictorial representation of the results. Notice in Question 1’s responses, A and C were split evenly with a majority of 40%. However, according to the given design guidelines, the storage unit should not be self-supported. Thus, a wall hanging unit was the chosen appropriate alternative. A4 The full free body diagram for both shelving systems.
Figure 22. The full free body diagram for both shelving units.
Page 37 of 38
A5 The intermediate values used in determine allowable forces acting on the shelf.
Figure 23. Intermediate calculations used as stated above. A6 The intermediate values for use in determining the max allowable load for the metal brace.
Figure 24. Intermediate calculations used as stated above.
A7 The attachments labeled 1-7 are shown directly after as referenced by A1. Attachments 1-7 corresponded to pages 39-45, respectively.
Page 38 of 38
A8 The qualitative benefits for implementing gussets into the chosen shelving supports are depicted below.
Figure 25. Stress locations when a 50lbf horizontal load is applied horizontally.
Figure 25 displaces the stress locations for when the supports undergo an unintended supporting scenario. The scenario depicted was most similar to a horizontal force being applied to the shelving supports, most likely by the swaying of the shelf. Note the model including the gussets was able to minimize the amount of stress near the wall-support interface.
QED
10.
500
2.4
52
0.500
12.500
3.10 6.90
9.0
0
R0.25 R0.25
R1.00
0.89 5.46 5.32
1.50
4.3
8 R2.00
R2.00
7.0
0 7
.54 8
.00
0.250 0.500 0
.500
1
0.00
0 1
0.50
0
2 X
0.250
0.500 0.5
00
10.
000
10.
000
10.
500
2 X 0.250
0.250
2.4
5
4.1
0 7
.64
8.0
0 0.50 0.500
12.
000
12.
500
5.5
0 9
.50
Top
Front
Back
+-0.005in
Attachment 1
DO NOT SCALE DRAWING
Support1SHEET 1 OF 1
UNLESS OTHERWISE SPECIFIED:
SCALE: 1:5 WEIGHT:
REVDWG. NO.
ASIZE
TITLE:
NAME DATE
COMMENTS:
Q.A.
MFG APPR.
ENG APPR.
CHECKED
DRAWN
FINISH
MATERIAL
INTERPRET GEOMETRICTOLERANCING PER:
DIMENSIONS ARE IN INCHESTOLERANCES:FRACTIONALANGULAR: MACH BEND TWO PLACE DECIMAL THREE PLACE DECIMAL
APPLICATION
USED ONNEXT ASSY
PROPRIETARY AND CONFIDENTIALTHE INFORMATION CONTAINED IN THISDRAWING IS THE SOLE PROPERTY OF<INSERT COMPANY NAME HERE>. ANY REPRODUCTION IN PART OR AS A WHOLEWITHOUT THE WRITTEN PERMISSION OF<INSERT COMPANY NAME HERE> IS PROHIBITED.
5 4 3 2 1
8.664
45.000
6.250
6.0
00 1
2.00
0
6.75 22.25
22.75 38.25
45.00
2.6
0
R0.10Sym
45.000 0.5
00
+-0.005in
Attachment 2
DO NOT SCALE DRAWING
Shelf1SHEET 1 OF 1
UNLESS OTHERWISE SPECIFIED:
SCALE: 1:10 WEIGHT:
REVDWG. NO.
ASIZE
TITLE:
NAME DATE
COMMENTS:
Q.A.
MFG APPR.
ENG APPR.
CHECKED
DRAWN
FINISH
MATERIAL
INTERPRET GEOMETRICTOLERANCING PER:
DIMENSIONS ARE IN INCHESTOLERANCES:FRACTIONALANGULAR: MACH BEND TWO PLACE DECIMAL THREE PLACE DECIMAL
APPLICATION
USED ONNEXT ASSY
PROPRIETARY AND CONFIDENTIALTHE INFORMATION CONTAINED IN THISDRAWING IS THE SOLE PROPERTY OF<INSERT COMPANY NAME HERE>. ANY REPRODUCTION IN PART OR AS A WHOLEWITHOUT THE WRITTEN PERMISSION OF<INSERT COMPANY NAME HERE> IS PROHIBITED.
5 4 3 2 1
0.125 11.875 12.000
1.0
00
1.1
25
1.6
25
1.7
50
2.7
50
0.125
1.0
00
12.000
0.500
1.000
0.5
00 1.0
00
0.250Sym
0.500
1.000 0.5
00
1.1
25
1.6
25
2.2
50
2.7
50 2 X 0.250
+-0.005in
Attachment 3
DO NOT SCALE DRAWING
support 3SHEET 1 OF 1
UNLESS OTHERWISE SPECIFIED:
SCALE: 1:5 WEIGHT:
REVDWG. NO.
ASIZE
TITLE:
NAME DATE
COMMENTS:
Q.A.
MFG APPR.
ENG APPR.
CHECKED
DRAWN
FINISH
MATERIAL
INTERPRET GEOMETRICTOLERANCING PER:
DIMENSIONS ARE IN INCHESTOLERANCES:FRACTIONALANGULAR: MACH BEND TWO PLACE DECIMAL THREE PLACE DECIMAL
APPLICATION
USED ONNEXT ASSY
PROPRIETARY AND CONFIDENTIALTHE INFORMATION CONTAINED IN THISDRAWING IS THE SOLE PROPERTY OF<INSERT COMPANY NAME HERE>. ANY REPRODUCTION IN PART OR AS A WHOLEWITHOUT THE WRITTEN PERMISSION OF<INSERT COMPANY NAME HERE> IS PROHIBITED.
5 4 3 2 1
8.485sym
6.000sym
12.
000
6.0
00sy
m
45.000
11.
875S
ym
6.000
7.000 22.000 23.000
38.000 39.000
45.000 0
.125
0
.625
0.7
50
+-0.005in
Attachment 4
DO NOT SCALE DRAWING
Shelf 3SHEET 1 OF 1
UNLESS OTHERWISE SPECIFIED:
SCALE: 1:10 WEIGHT:
REVDWG. NO.
ASIZE
TITLE:
NAME DATE
COMMENTS:
Q.A.
MFG APPR.
ENG APPR.
CHECKED
DRAWN
FINISH
MATERIAL
INTERPRET GEOMETRICTOLERANCING PER:
DIMENSIONS ARE IN INCHESTOLERANCES:FRACTIONALANGULAR: MACH BEND TWO PLACE DECIMAL THREE PLACE DECIMAL
APPLICATION
USED ONNEXT ASSY
PROPRIETARY AND CONFIDENTIALTHE INFORMATION CONTAINED IN THISDRAWING IS THE SOLE PROPERTY OF<INSERT COMPANY NAME HERE>. ANY REPRODUCTION IN PART OR AS A WHOLEWITHOUT THE WRITTEN PERMISSION OF<INSERT COMPANY NAME HERE> IS PROHIBITED.
5 4 3 2 1
45.00
11.
50
0.1
3 1
1.18
11.
40
0.1
0 0
.60
0.7
0
0.15Sym
0.60Sym 0.75Sym
11.
50
R0.23Sym
0.7
5 0
.38
45.00
+-0.005in
Attachment 5
DO NOT SCALE DRAWING
Shelf 2SHEET 1 OF 1
UNLESS OTHERWISE SPECIFIED:
SCALE: 1:10 WEIGHT:
REVDWG. NO.
ASIZE
TITLE:
NAME DATE
COMMENTS:
Q.A.
MFG APPR.
ENG APPR.
CHECKED
DRAWN
FINISH
MATERIAL
INTERPRET GEOMETRICTOLERANCING PER:
DIMENSIONS ARE IN INCHESTOLERANCES:FRACTIONALANGULAR: MACH BEND TWO PLACE DECIMAL THREE PLACE DECIMAL
APPLICATION
USED ONNEXT ASSY
PROPRIETARY AND CONFIDENTIALTHE INFORMATION CONTAINED IN THISDRAWING IS THE SOLE PROPERTY OF<INSERT COMPANY NAME HERE>. ANY REPRODUCTION IN PART OR AS A WHOLEWITHOUT THE WRITTEN PERMISSION OF<INSERT COMPANY NAME HERE> IS PROHIBITED.
5 4 3 2 1
R0.075 R0.075
0.17
TRUE R0.08Sym
R0.23
R0.23 R0.30
R0.30
1.57°
0.17
0.4
5
0.6
6
0.5
6
0.7
3 0
.89
3.3
4 3
.37
3.4
1 3
.76
3.8
1
3.9
2
1.85
1.55
+-0.005"
InchesAttachment 6
Drawing represents an example of pertinent parameters for injection molding process
DO NOT SCALE DRAWING
Support 2SHEET 1 OF 1
UNLESS OTHERWISE SPECIFIED:
SCALE: 1:5 WEIGHT:
REVDWG. NO.
ASIZE
TITLE:
NAME DATE
COMMENTS:
Q.A.
MFG APPR.
ENG APPR.
CHECKED
DRAWN
FINISH
MATERIAL
INTERPRET GEOMETRICTOLERANCING PER:
DIMENSIONS ARE IN INCHESTOLERANCES:FRACTIONALANGULAR: MACH BEND TWO PLACE DECIMAL THREE PLACE DECIMAL
APPLICATION
USED ONNEXT ASSY
PROPRIETARY AND CONFIDENTIALTHE INFORMATION CONTAINED IN THISDRAWING IS THE SOLE PROPERTY OF<INSERT COMPANY NAME HERE>. ANY REPRODUCTION IN PART OR AS A WHOLEWITHOUT THE WRITTEN PERMISSION OF<INSERT COMPANY NAME HERE> IS PROHIBITED.
5 4 3 2 1
35.00
11.
50
11.
50
0.60
11.
46
11.
41
11.
33
4.20
4.28 8.00 36.70
Attachment 7
+-0.005"
This design cannot be plastic machined, however an example of parametersare shown here.
DO NOT SCALE DRAWING
Shelf 4SHEET 1 OF 1
UNLESS OTHERWISE SPECIFIED:
SCALE: 1:10 WEIGHT:
REVDWG. NO.
ASIZE
TITLE:
NAME DATE
COMMENTS:
Q.A.
MFG APPR.
ENG APPR.
CHECKED
DRAWN
FINISH
MATERIAL
INTERPRET GEOMETRICTOLERANCING PER:
DIMENSIONS ARE IN INCHESTOLERANCES:FRACTIONALANGULAR: MACH BEND TWO PLACE DECIMAL THREE PLACE DECIMAL
APPLICATION
USED ONNEXT ASSY
PROPRIETARY AND CONFIDENTIALTHE INFORMATION CONTAINED IN THISDRAWING IS THE SOLE PROPERTY OF<INSERT COMPANY NAME HERE>. ANY REPRODUCTION IN PART OR AS A WHOLEWITHOUT THE WRITTEN PERMISSION OF<INSERT COMPANY NAME HERE> IS PROHIBITED.
5 4 3 2 1
3D Printed Conceptual Prototype Summary Team PolymerWorks
Advisors: Dr. Gipson and Dr. Prins
Team members:
Mick Blackwell, Ben Condro, Mark Dufresne, Brenton Lester, and Matt Lewis
Page 2 of 3
Overview
In order to demonstrate practicality for the proposed design (displayed below in Figure 1), a 3D prototype was fabricated using the MakerBot Replicator 2 (MR2).
Figure 1. The selected design for shelving unit fabrication. For a complete description of parameters, refer to Attachment 6 and 7 within the SUCP documentation.
Note the documentation and thought process to conceive the concept above is shown in the SUCP.
Process
The Makerbot Replicator 2 was made available through the in-house 3D Printing Lab. According to the Lab-Ops, the MR2 can print 3D components up to Length = 11”, Width = 6”, and Height = 6”. Material used for printing components was PLA (poly-lactic acid). Furthermore, the individual components of the shelf were printed in order to better replicate the actual system.
Thus, a total of five components were printed including: four supports and one shelf. The scaling ratio was determine based on the largest parameter of the shelving system to ensure the largest model would be created. The largest parameter of the shelving system was the required shelf length of 45”.
Simple math yields the maximum scaling ratio stated below.
0.244 0.24 (Eq. 1)
Where was the length of the maker bot printing tray and was the length of the shelf.
As shown in Eq. 1, a printing ratio of 0.24 was derived and used for all components to obtain appropriate interfacing during assembly. Each shelving support was printed at a rate of one support a session due to recommendations from Lab-Ops. Figure 2 below displays the shelf being printed.
Page 3 of 3
Figure 2. The shelf being 3D printed on the MR2.
Note nearly the maximum length of the printing tray was utilized during printing as shown in Figure 2. Furthermore, the shelf was printed support face down in order for the print to not require any supporting material.
Results
The 3D printing techniques utilized allowed for an appropriate demonstration of shelf practicality. Figure 3 below displays the assembled shelving system.
Figure 3. The shelving system used for demonstrative purposes.
Note the shelving unit was attached to a metal brace only for display.
Future work involves producing a 1:1 scale ratio shelving system to fully demonstrate feasibility.
Assembly Instructions Team PolymerWorks
Advisors: Dr. Gipson and Dr. Prins
Team members:
Mick Blackwell, Ben Condro, Mark Dufresne, Brenton Lester, and Matt Lewis
Page 2 of 7
The following documentation provides a step-by-step tabulated and figurative assembly process. Assembly begins with acquiring needed tools. The consumer, before purchase, would need to read the packaging of the shelving unit to find the stud spacing requirement of 16”. If the consumer does not live in a home constructed using the 16” stud spacing convention, then the consumer cannot properly mount the 16” support-span shelving model. Hereafter, the actual assembly instruction template will begin (Text enlarged to portray actual assembly text).
Congratulations on your purchase of the PolymerWorks Shelving System! We appreciate your business and we will guide you through the installation process in a timely fashion.
In order to begin the assembly of your shelving unit, please acquire the following tools.
1. One Stud Finder 2. One Level 3. One Drill with Appropriate Drill Bit for a #10 Screw 4. One Tape Measure
A general overview of the shelving process is shown below and figurative instructions follow.
Page 3 of 7
Step 1: Locate the wall studs using the required stud finder. Be sure the studs are located 16” apart as shown in the figure below.
Step 2: Mark the stud located farthest left. This will be the stud used to mount the first support.
Page 4 of 7
Step 3: Drill two screw holes into the wall stud spaced 1.50” apart vertically using the required tape measure, drill, and standard drill bit for a #10 screw.
Step 4: Drill two more screw holes (using the same drill bit as before) 16” to the right (horizontally) of the screw holes drilled in Step 3.
Page 5 of 7
Step 5: Drill two more screw holes (using the same drill bit as before) 16” to the right (horizontally) of the screw holes drilled in Step 4.
Step 6: Insert the screw and washer combination included in the packaging into the supports as shown below. Screw the screws into the previously drilled holes until all three supports are mounted.
Page 6 of 7
Step 7: Lay the shelf onto the supports in the orientation shown below. Be shown supports rest in the slots on the Bottom-Side of the shelf.
Final Step: Once the shelving unit has been assembled, use the required level to check that the shelf is level. If the shelf is level, then you have successfully assembled your new PolymerWorks Shelving System.
Page 7 of 7
Disclaimer: PolymerWorks is not responsible for any injuries or product malfunctions due to improper installation. PolymerWorks is also not responsible for any injuries acquired when using required equipment. PolymerWorks recommends professional installation when the consumer is unsure of how to assemble the shelving system. As stated on the packaging, the maximum weight supported by the shelving unit is 60 pounds. Product failure may occur if the weight exceeds the recommended maximum limit of 60 pounds. If bending can be seen while examining the shelf or supports, consider removing all supported objects and check the assembly to be sure the shelving system was properly assembled.
Bill of Materials Team PolymerWorks
Advisors: Dr. Gipson and Dr. Prins
Team members:
Mick Blackwell, Ben Condro, Mark Dufresne, Brenton Lester, and Matt Lewis
Page 2 of 2
Overview
In order to test different material properties, samples were bought through select manufactures. The team budget was 100USD and the samples were purchased through Mr. John Wild of the James Madison Engineering Department.
Bill of Materials
Materials were purchased through US Plastics and McMaster. The list of materials purchased was separated by manufacturer and is shown below in Table 1.
US Plastics
ROD Stock 3/8" Diameter Quantity
Price, USD
Total, USD
PC (Clear) 2.25 USD/ft 8 18 29.72
HDPE 5.84 USD/ 8ft 1 5.84
PP 5.88 USD/ 8ft 1 5.88
McMaster
ROD Stock 1/4" Diameter Quantity
Price, USD
Total, USD
PC (Clear) 1.22 USD/ft 8 9.76 21.84
HDPE 0.67 USD/ ft 8 5.36 Sum
PP 0.84 USD/ft 8 6.72 51.56
Thus, team PolymerWorks stayed within the 100USD budget during the project timeline.
Statistical Analysis of Polycarbonate and
Copper
Submitted to:
Dr. Kyle Gipson
Prepared by:
Mick Blackwell
Ben Condro
Mark Dufresne
Brenton Lester
Matthew Lewis
1.0 Introduction
The materials polycarbonate and copper were mechanically tested in order to statistically prove that the
two materials were different. The mechanical test performed was a three‐point bend test that required
the use of an Instron machine. The flexural strength of each material was the property calculated in order
to determine that the two materials were different. A total of 60 trials were performed during this test;
30 three‐point bend tests for copper and 30 three‐point bend tests for polycarbonate. This number was
used in order to statistically prove with a 95% confidence that the two materials were different.
1.1 Scope
These stated tests and calculations were performed in order to statistically prove that the two chosen
materials are different. It is known that polycarbonate and copper are not the same material, but
statistical analysis was needed in order to prove with 95% that the two materials belong in different
families. By researching known flexural strengths values using CES ® software, each material tested was
comparatively quantified according to standard and known flexural strength. This helped to prove that
the procedure used and data obtained was accurate. The values obtained in this testing were entirely
quantitative and included no qualitative observations. The experiment took place in a laboratory where
an Instron machine is located.
1.2 Significance and Use
The outcomes of these experiments can in be used in order to statistically show that polycarbonate and
copper do not belong in the same material family. The three‐point bend tests can also be used to further
investigate the flexural strength of both polycarbonate and copper. Although these tests have already
been performed, the tests that were run can better indicate with statistical accuracy the flexural strength
of each material.
1.3 Apparatus
As mentioned, the apparatus used for the three‐point bend test was the Instron machine. This machine
induces a point load on a specimen that sits atop two supports. The supports used for this test were 2
inches apart and the load was place directly in the middle of the two supports. Below, Figure 1.3.1 displays
a schematic of the test performed.
Figure 1.3.1‐‐Schematic of three‐point bend test
As seen in Figure 1.3.1 the specimen was atop two supports that were 2 inches apart from one another.
The load was then placed in the middle of the supports as well as in the middle of the specimen and the
Instron machine put increasing pressure on the specimen until the point at which the specimen broke or
was bent beyond repair.
2.0 Three‐point Bend Testing
2.1 Test Specifications and Procedure
The testing procedures to determine the flexural strength of both the copper and polycarbonate followed
the steps of ASTM D790 – Standard Test Methods for Flexural Properties of Unreinforced and Reinforced
Plastics. The steps within this ASTM test were the exact same for the three‐point bend testing of metals.
The only difference within this testing standard is that it is recommended that a four‐point bend test be
run for materials that do not fail by the maximum strain.
This standard includes taking a specimen that is roughly, but no less than, 2 inches in length and placing
it atop the supports. Refer back to Figure 1.3.1 for the schematic of the setup. The load arm was then
touched to the specimen and the “Balance Load” tab was pushed on the Instron control panel. Once the
load was balanced the “Start Test” tab on the control interface was pushed in order to begin the test. The
Instron placed would then place an increasing load (pressure or force) on the specimen until it failed.
Failure took place when the specimen broke or was deformed beyond repair.
The data obtained during testing was stored on an accompanying computer using BlueHill Software and
then later transferred to a personal computer for data analysis.
Specimen
3.0 Tests Results
3.1 Flexural Strength and Statistical Analysis Results
After the testing was completed, the flexural strength of each trial was calculated. Table 3.1.1 describes
the average flexural strength for polycarbonate and copper along with the statistical data calculated for
the trials. A total of 30 trials were performed for each material family resulting in 60 trials overall. The
value of 30 was chosen for the trial amount because that it the minimum amount needed in order to
calculate statistical values. To view data for all 60 trials refer to the Appendix in sections 5.1 and 5.2.
Note that the determination for these values can be found in section 3.2 below.
Table 3.1.1: Summary of average flexural strength and calculated statistical values
The above table summarizes the average flexural strength of copper and polycarbonate calculated from
the three‐point bend test. The statistical values calculated from the 60 trials are also displayed. These
values were calculated using a 95% confidence interval. It can be seen that copper has a higher average
flexural strength than polycarbonate. One may assume from the average values that they are different,
but statistical analysis must first be performed in order to make that statement. To better illustrate the
results described above, the average flexural strength of each material along with their margins of error
were inserted into a bar graph. This is shown in Figure 3.1.1 below.
Figure 3.1.1: Bar graph of average flexural strength for copper and polycarbonate along with error bars
and display of the dmin value.
From the above data, the following determinations can be drawn:
1) Copper has a higher flexural strength than polycarbonate
2) With 95% confidence it can be determined that copper and polycarbonate are statistically
different. This can be stated because the average difference between the flexural strength of
copper and polycarbonate is greater than the calculated dmin value.
3.2 Analysis of Test Data
To calculate the flexural strength from the obtained data, the following equation was utilized:
(3.2.1)
where:
Ff = max load applied to specimen during trial, L = span length (for these tests it was 2 inches), R = radius of test specimen. The average flexural strength was calculated using the following equation:
∑
(3.2.2)
where:
53171
18443
0
10000
20000
30000
40000
50000
60000
Flexural Stress (psi)
Copper
Polycarbonate
95% 1318 psi
n = the number of trials performed.
The critical t value (tcrit) was determined using the degrees of freedom (DF) and Student’s t‐value
distribution table. The DF value was calculated using the equation below:
1 (3.2.3)
where n is the same variable as in Equation 3.2.2. Next, the standard deviation was calculated using
Equation 3.3.4 below:
∑
(3.2.4)
where:
= the flexural strength of that particular trial, = average flexural strength. The margin of error was calculated using the equation below:
√
(3.2.5)
In order to calculate the dmin value, an intermediate variable had to be calculated. This is the sp value which
was calculated using Equation 3.2.6 below:
(3.2.6)
where:
s1 = the standard deviation of the copper trials, s2 = the standard deviation of the polycarbonate trials.
Last, dmin was calculated using the equation below:
∗ ∗ (3.2.7)
4.0 Summary
Using ASTM D790 – Standard Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics,
it can be concluded with 95% confidence that polycarbonate and copper are statistically different in
regards to flexural strength. After the 60 trials were performed (30 trials for polycarbonate and 30 trials
for copper), the test results showed that the average difference between the two materials was 34,727
psi which is much greater than the calculated dmin value of 1,318 psi. This proves that the two materials
tested are statistically different.
5.0 Appendix
5.1 Flexural Strength of Copper
The flexural strength calculated for each copper trial is described in the table below.
Table 5.1.1: Flexural strength for the 30 trials of copper
5.2 Flexural Strength of Polycarbonate
The flexural strength calculated for each polycarbonate trial is described in the table below.
Table 5.2.1: Flexural strength for the 30 trials of polycarbonate
Mechanical Analysis of Polypropylene,
Polycarbonate, and Polyethylene
Submitted to:
Dr. Kyle Gipson
Prepared by:
Mick Blackwell
Ben Condro
Mark Dufresne
Brenton Lester
Matthew Lewis
Page 2 of 6
1.0 Introduction
The polymers polypropylene, polycarbonate, and polyethylene will be mechanically tested in order to
compare experimental mechanical properties to mechanical values found using CES Edupack 2013
software (CES) as well as compare all three polymers to one another. The mechanical test to be
performed is a three-point bend test that makes use of an Instron 5966 machine.
1.1 Scope
The mechanical testing on the above polymers quantitatively describes mechanical properties of each
polymer. The test method being performed is a three-point bend test. From this test the flexural
strength of each polymer can be determined. Through finding the flexural strength experimentally, a
comparison can be made between polymers and also against the accepted values found using CES
Edupack 2013 software. The testing was performed on an Instron 5966 machine under laboratory
settings.
1.2 Significance and Use
The outcomes of this experiment can be used to compare the flexural strength of polypropylene,
polycarbonate, and polyethylene. The values obtained can also be used to compare mechanical
properties found through experimental analysis to those listed in CES as accepted values. The tests will
better indicate as to what flexural strength the polymers can handle.
1.3 Apparatus
The three-point bend test was performed using an Instron 5966 machine. This machine has an accessory
which allows for three-point bend testing where a material sample rests across two supports. The
Instron 5966 has a load arm which applies a force on the material at the mid-span of the supports.
Below, a schematic of the setup can be seen in Figure 1.3.1.
Figure 1.3.1--Schematic of three-point bend test
As seen in Figure 1.3.1 the material sample sets atop the two supports. The load arm applies a force
until the sample broke or ruptured on the outer surface.
Material
Sample
Page 3 of 6
2.0 Three-point Bend Testing
2.1 Test Specifications and Procedure
The three-point bend testing performed was in accordance with ASTM D790, Standard Test Methods for
Flexural Properties of Unreinforced and Reinforced Plastics, procedure A. This testing procedure includes
using a support span of two inches as well as use supports and a load arm that has a cylindrical surface.
Note that ASTM D790 allows for materials that have been cut from sheets, plates, or molded shapes, or
may be molded to the desired finished dimensions. The procedure also indicates that a minimum of five
trials must be run on each material.
The procedure of testing on the Instron 5966 machine is as follows. The Instron 5966 machine was
turned on in addition to the computer connected with it. On the computer, BlueHill software was
initiated in order to use the testing apparatus. The polypropylene, polycarbonate, and polyethylene
samples were measured and cut to a length of approximately (but no less than) two inches. These pieces
were placed onto the center of the support spans. The load arm was lowered until first contact with the
sample was made and then the load and extension of the Instron 5966 were both balanced. The “Start
Test” button was pressed to initiate the machine where the load arm was lowered (applying a force to
the sample) until the sample failed or ruptured on the outer surface. Once the test was complete, a new
sample was cut and the above steps repeated.
The BlueHill software recorded the applied load and the downward extension of the load arm. This data
was saved and transferred to a personal computer so that it may analyzed further.
For reference, a picture of the testing apparatus can be seen blow in Figure 2.1.1.
Figure 2.1.1: Testing apparatus
Page 4 of 6
3.0 Tests Results
3.1 Flexural Strength
The data obtained from testing was used to calculate the flexural strength of each sample. Five tests
were performed on each type of polymer so that a total of fifteen tests took place. The data from all
fifteen tests in addition to the average flexural strength for each polymer can be found below in Tables
3.1.1, 3.1.2, and 3.1.3. Note that the derivations of flexural strength can be found below in section 3.2.
Table 3.1.1: Polypropylene flexural strength properties
Polypropylene
Specimen # Flexural Strength, psi
1 14947.8
2 14987.8
3 14915.9
4 14947.3
5 14799.2
Average: 14919.6
Table 3.1.2: Polycarbonate flexural strength properties
Polycarbonate
Specimen # Flexural Strength, psi
1 21972.1
2 21838.0
3 21915.7
4 21889.5
5 21777.0
Average: 21878.4
Table 3.1.3: Polyethylene flexural strength properties
Polyethylene
Specimen # Flexural Strength, psi
1 10989.7
2 11025.1
3 11023.5
4 10996.9
5 11042.0
Average: 11015.4
Page 5 of 6
The above tables summarize the flexural strength of each polymer from testing. In order to compare
these values to the accepted ones in CES, Table 3.1.4 below shows both the average values from
experimental testing and those found using CES. Note that CES does not list flexural strength, but
flexural strength can be equated to the lower of tensile or compression strength and as such the values
below represent the average of the range given for the lower of tensile or compression strength.
Table 3.1.4: Summary of Flexural Strength
Flexural Strength, Psi
Material: Experimental CES
Polypropylene 14919.6 5000
Polycarbonate 21878.4 9600
Polyethylene 11015.4 3745
The above table summarizes both the flexural strength from the experiment as well as the flexural
strength obtained from CES. Using this information the following conclusions may be formed:
1) The experimental flexural strength values do not represent the accepted values
from CES; however the hierarchy among the three polymers is the same.
2) Polycarbonate is shown to have a larger flexural strength than polypropylene and
polyethylene.
3.2 Analysis of Test Data
To calculate the flexural strength from the obtained data, the following equation was utilized:
𝐹𝑙𝑒𝑥𝑢𝑟𝑎𝑙 𝑆𝑡𝑟𝑎𝑖𝑛 = 𝜎𝑓𝑠 =𝐹𝑓𝐿
𝜋𝑅3 (3.2.1)
Where sigma represents the flexural stress in psi (lbf/in2), Ff is the force load (lbf) applied to the material,
L is the gauge length or length of the testing specimen (in), and R is the radius of the polymer rod. Note
that the flexural strength is the max flexural strain achieved while testing.
4.0 Summary
Using ASTM D790, Standard Test Methods for Flexural Properties of Unreinforced and Reinforced
Plastics, procedure A the flexural strength amongst different materials can be compared. It was found
that polycarbonate has a higher flexural strength at 21878.4 psi than polypropylene or polyethylene at
14919.6 psi and 11015.4 psi respectively. These experimental values did not agree with the accepted
values found using CES Edupack 2013 software. The experimental values were larger at 14919.6 psi,
21878.4 psi, and 11015.4 psi for polypropylene, polycarbonate, and polyethylene respectively while in
CES values (respectively) were found to be 5000 psi, 9600 psi, and 3745 psi.
Page 6 of 6
5.0 References
1. ASTM Standard D790, 2002, “Standard Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics,” ASMT International, West Conshohocken, PA, 2002, DOI: 10.1520/D0790-10, www.astm.org.
Chemical Resistance Testing in
accordance with ATSM D543
Submitted to:
Dr. Kyle Gipson
Prepared by:
Mark Dufresne
Mick Blackwell
Ben Condro
Brenton Lester
Matt Lewis
1.0 Introduction
The polymers Polycarbonate, Polyethylene, and Polypropylene will be subjected to a discrete list of
aqueous solutions and weak acids. This chemical reagent test is performed in order to determine the listed
polymers resistance to a given set of solutions and acids. Once the polymers have been subjected to the
listed reagents, their mechanical properties will be evaluated using three-point bend tests. If the polymers
properties differ from standard and known properties, then resistance to the given reagent can be
determined.
1.1 Scope
The chemical reagent testing on the described polymers quantitatively describe resistance in relation to a
given reagent. By performing preliminary mechanical property testing, each material can be quantified
according to standard and un-changed mechanical properties. This preliminary property analysis is
performed via three-point bend testing. This method is utilized to characterize the material mechanical
property: Flexural Strength or Flexural Stress. After material subjection to various chemical reagents,
testing is again performed to measure the described material property. This new set of material
properties—after chemical testing—is comparatively analyzed to the preliminary set of material
properties to assess material resistance, and to quantify material degradation in the form of change in
material properties. This testing procedure ultimately labels the given set of polymers resistance and level
of degradation to the described aqueous solutions and weak acid.
1.2 Significance and Use
The outcomes of this experiment effectively characterize the polymers ability to withstand normal
subjection to the variety of aqueous solutions and weak acids. This essentially details possible limitations
of the given materials resistance to reagents. In other words, this experiment produces an end-user or
manufacturer caution/discretion list to reagents not to be used on a given polymer. For and end-user, this
clarifies the reagents that should be used with caution around a given polymer. An example would include
cautionary use of cleaning products that include some of the reagents described; as the material could
degrade if continuous use persists. For a manufacturer, this clarifies cautionary reagent use with
processing, preparation, cleaning, etc. techniques for producing the listed polymers.
2.0 Chemical Resistance Testing
2.1 Test Specifications and Procedure
ASTM D543 - 95, Standard Test Methods for Evaluating Resistance of Plastics to Chemical Reagents,
Practice B, describes the chemical testing procedures for determining resistance—in this case for
polymers—to various chemical reagents. Utilizing the described immersion procedure, the materials will
be characterized in terms of chemical resistance according to mechanical properties after an immersion
period. Note, ASTM D543 does not clarify: the types, concentrations, or amount of reagents, the duration
of the immersion period, or the mechanical properties to be reported.
The testing procedure consisted of soaking three sets of each polymer, for a duration period of one day
(24 hours), in the following chemical reagents:
1) Water – Control
2) 5% Acetic Acid – Vinegar
3) <1% Malic/Tartaric Acid - Red Wine
Following immersion, three-point bends are to be performed on each specimen ultimately to calculate
flexural strength.
ASTM D543, Practice B – Mechanical Stress and reagent Exposure, is utilized for this test and describes
the reagent impact on each material in terms of flexural stress. More details following the testing
procedures can be found in the remaining report sections.
3.0 ASTM D543 Practice B – Mechanical Stress & Reagent Exposure
3.1 Test Specifications and Procedures
Testing comprised of soaking three material specimens, of each polymer, in each chemical reagent for an
agreed upon duration of one day; then mechanically testing the material strength by means of three-point
bending tests. Material properties following immersion and testing will be compared to the control, un-
immersed polymers. Any differences from the control shall be considered material degradation to the
given reagent and material resistance to that reagent will be labeled.
3.2 Test Specimens
The material specimens for the ASTM D543 Practice B test, following Practice A (Procedure A) methods
were cut from 0.25 inch, 8 foot long rods. Two inch cuts were made on each polymer rod yielding nine
specimens per material. A total of 27 polymer rods were tested, these consisted of: three polymer rods for
each reagent being tested.
3.3 Test Equipment
The chemical reagents utilized for testing were held in sealable Tupperware containers at room
temperature in a controlled environment. Three specimens, for each polymer, are completely immersed in
the sealed containers at a depth of approximately 1 inch. The figure below illustrates the testing set-up:
Figure 3.3.1 ASTM D543 Immersion Testing Set-Up for Practice B
The setup in Figure 3.3.1 shows the sealed containers holding three testing specimens for each polymer.
Following the 24 hour immersion period, the test specimens are removed from their respective baths,
dried, and then immediately subjected to three-point bend testing. Figure 3.3.2 below shows the test
specimens following soaking for 24 hours:
Figure 3.3.2 ASTM D543 Immersion Specimens
Each specimen shown in Figure 3.3.2 was then subjected to three-point bending tests. The strain fixture
utilized during testing is the Instron 5966 apparatus. The Instron three-point bend setup includes a gauge
length of 2 inches. The resulting data and analysis can be found presented in the remaining report
sections.
3.4 Test Results
Following a soaking period of 24 hours in the reagent baths, a total of 27 specimens were tested using
three-point bending. Tables 3.4.1, 3.4.2, and 3.4.3 describe the calculated flexural strengths for
polycarbonate, polypropylene, and polyethylene respectively; under each bath condition. Figures 3.4.1,
3.4.2, and 3.4.3 illustrate the average flexural strengths for polycarbonate, polypropylene, and
polyethylene shown with respect to the given reagent bath.
Note, the determination for these values and the methods utilized can be found in section 3.5 below.
Table 3.4.1: Summary of flexural strength results from three-point bending of polycarbonate after reagent
exposure.
Table 3.4.2: Summary of flexural strength results from three-point bending of polypropylene after reagent
exposure.
Table 3.4.3: Summary of flexural strength results from three-point bending of polycarbonate after reagent
exposure.
The above tables show the calculated flexural strength values for each polymer, for each reagent bath. To
illustrate the effects each reagent had on each polymer, the average flexural strength values for the three
Chemical Specimen # σfs Max [psi] σfs Avg. [psi]
#1 18532.797
#2 18716.659
#3 18765.388
#1 18250.978
#2 18262.853
#3 18231.731
#1 18783.765
#2 18737.934
#3 18904.813
Wine
Water
Vinegar
18671.615
18248.521
18808.837
Chemical Specimen # σfs Max [psi] σfs Avg. [psi]
#1 13574.873
#2 13784.579
#3 13723.223
#1 9326.544
#2 9297.659
#3 9163.576
#1 9464.604
#2 9345.378
#3 9405.718
Wine 13694.225
Water 9262.593
Vinegar 9405.233
Chemical Specimen # σfs Max [psi] σfs Avg. [psi]
#1 9533.115
#2 9362.656
#3 9305.589
#1 9326.544
#2 9297.659
#3 9163.576
#1 9464.604
#2 9345.378
#3 9405.718
Wine 9400.453
Water 9262.593
Vinegar 9405.233
polymers tested under each bath condition are assembled into bar charts; according to the specified
polymer.
Figure 3.4.1: Average flexural strength (psi) values for polycarbonate rods after 24 hour reagent exposure.
Figure 3.4.2: Average flexural strength (psi) values for polypropylene rods after 24 hour reagent
exposure.
18671.615
18248.521
18808.837
18443
17900
18000
18100
18200
18300
18400
18500
18600
18700
18800
18900
Flex
ura
l Str
ess,
[p
si]
Polycarbonate
Wine
Water
Vinegar
Control
13694.225
9262.593 9405.233
14919.6
0
2000
4000
6000
8000
10000
12000
14000
16000
Flex
ura
l Str
ess,
[p
si]
Polypropylene
Wine
Water
Vinegar
Control
Figure 3.4.3: Average flexural strength (psi) values for polyethylene rods after 24 hour reagent exposure.
From the above data, the following determinations can be drawn:
1) The chemical reagents, Wine and Vinegar suggest to increase—correlating no
effect—to the flexural strength of Polycarbonate. However, degradation in flexural
strength exists for exposer to water by roughly 1%.
2) All chemical reagents (from the experimental data) suggest to decrease the flexural
strength of Polypropylene. Degradation in percentage by reagent bath are as follows:
a. 10% appears for exposure to Wine
b. 37% appears for exposure to Water
c. 36% for exposure to Vinegar (5% Acetic Acid)
3) All chemical reagents (from the experimental data) suggest to decrease the flexural
strength of Polyethylene. Degradation in percentage by reagent bath are as follows:
a. 15% appears for exposure to Wine
b. 16% appears for exposure to Water
c. 15% for exposure to Vinegar (5% Acetic Acid)
3.5 Analysis of Test Data
To calculate the flexural stress (strength) from the three-point bend data set, the following equation is
utilized:
9400.453 9262.593
9405.233
11015.4
8000
8500
9000
9500
10000
10500
11000
11500Fl
exu
ral S
tres
s, [
psi
]
Polyethylene
Wine
Water
Vinegar
Control
Where sigma represents the flexural stress in psi (lbf/in2), Ff is the force load (lbf) applied to the material,
L is the gauge length or length of the testing specimen (in), and R is the radius of the polymer rod.
The above data tables represent the maximum flexural strength calculated for that given material, per
trial; where the maximum flexural strength values for each specimen, under the described bath condition
are used.
4.0 Summary
ASTM D543 Practice B - Mechanical Stress & Reagent Exposure, test results indicate that all chemicals
appear to reduce the flexural stress for the Polypropylene and Polyethylene specimens, however, for
Polycarbonate, this trend showed only with exposure to water. Aside from the differing material
properties of each polymer, the reagent baths suggest material degradation, in terms of flexural strength
for both Polypropylene and Polyethylene. In regards to the data obtained for Polycarbonate, the
determinations follow that water is the most degrading solution; whereas weak acids such as Vinegar and
Red Wine appear to increase flexural strength. It should be noted that while determinations can be drawn
from the small batch of testing data, further evidence from testing needs to be performed in order to
accurately describe the effects each reagent had on the materials.
5.0 References
1. American Society for Testing and Materials Committee D-20 on plastics (1999). ASTM D543 -
99: Standard Test Methods for Evaluating the Resistance of Plastics to Chemical Reagents.
Philadelphia, Pennsylvania: American Society for Testing and Materials.
Thermal Conductivity Testing of various
Polymers
Submitted to:
Dr. Kyle Gipson
Prepared by:
Mark Dufresne
Mick Blackwell
Ben Condro
Brenton Lester
Matt Lewis
1.0 Introduction
The polymers Polycarbonate, Polyethylene, and Polypropylene will be tested to derive experimental
values for thermal conductivity. This thermal test is performed in order to determine the listed polymers
resistance to a heat transfer and the flow of heat through the material. The polymers will be subjected to
boiling water for a short duration, then the temperature differential that exists on a given side of the
material will be evaluated. This differential is then used to approximate the thermal conductivity or
resistivity of the material. If the polymers thermal properties differ from standard and known properties,
then resistance to the given reagent can be accurately compared and validated as either a thermal
conductor or insulator.
1.1 Scope
The thermal testing on the described polymers quantitatively describe resistance in relation to a given
temperature differential. By researching known conductivity values using CES ® software, each material
tested can be comparatively quantified according to standard and known thermal properties. This method
is utilized to characterize the material as either a thermal insulator or conductor. Using this testing
procedure ultimately labels the given set of polymers resistance and level of degradation to the described
thermal source—boiling water.
1.2 Significance and Use
The outcomes of this experiment effectively characterize the polymers ability to withstand subjection to a
normal thermal heat source. This essentially details possible limitations of the given materials resistance
to heat transfer. In other words, this experiment produces an end-user caution/discretion concern as to the
thermal limitations of a given polymer. Essentially this test clarifies the given polymer, in a given product
for example, can or cannot resist heat well; therefore large heat sources—dependent of the testing
results—should be used with caution around the polymer type product. An example would include
cautionary use of hot liquids like coffee, tea, or hot chocolate. Or, cautionary use of hot objects placed on
or around the polymer; as the material could degrade if continuous use persists.
2.0 Thermal Resistance Testing
2.1 Test Specifications and Procedure
Thermal testing procedures for determining thermal conductivity/resistance—in this case for polymers—
utilized a slightly altered version of ASTM E2584-14 – Standard Practice for Thermal Conductivity of
Materials Using Thermal Capacitance (Slug) Calorimeter. This standard includes utilizing a slug of a
given material, impregnated with a thermocouple situated about the middle of the slug, with the slug
incorporated in a standard laboratory calorimeter setup. In coating the slug with insulation, deposited
materials, etc. then measuring the temperature differential from the calorimeter fluid to the center of the
slug radially, the thermal conductivity of the slug’s material can be approximated. The ASTM standard
setup can be shown (approximately) by Figure 2.1.1 located below. The modified testing procedures
utilized for this test, however, follows methods that include Type K thermocouples fitted atop the
polymer slugs, then fitted with insulation atop the thermocouples to ensure proper thermal readings.
Rather than radial heat transfer, the measured temperature differentials are recorded by vertical (linear)
methods with thermocouples located atop the polymer slugs.
Once the materials are fitted with the appropriate thermocouples, they are immersed in a similar
calorimeter described by the ASTM standards including boiling water as the calorimeter fluid.
Figure 2.1.1 ASTM E2584 - 14 approximate experimental setup for testing the thermal conductivity of
various materials using radial temperature differential methods [2]
.
The above figure shows the heat flux q from the calorimeter to the slug. Because this setup includes
heat flux as a constant from the calorimeter, the same methods can be followed for this testing procedure.
It follows that the amount of heat transfer q to the slug pictured above—in accordance with the
conservation of energy laws—is the same heat transfer to the calorimeter fluid resulting from the
temperature differential until boiling occurs; where the amount of heat transfer to the water (utilized in
this setup) is the same heat transfer to the slug, neglecting any miscellaneous heat transfer to the
surroundings. Following similar setups in Figure 2.2.1, the experimental setup utilized for this procedure
can be illustrated in Figure 2.2.2 below:
Figure 2.1.2 Experimental setup for testing the thermal conductivity of various materials using vertical
temperature differential methods.
The slugs remain in the boiling water for a duration period of four minutes; temperature readings are
performed at intervals of 15 seconds for the described duration of four minutes. The linear temperature
differential between the slug’s surface temperature and the temperature of the calorimeter are then utilized
to approximate the thermal conductivity of the polymer slugs. More description on the conductivity
calculations can be found in section 2.5 below.
The testing procedure consisted of soaking three sets of each polymer, for a duration period of four
minutes, in the boiling water calorimeter. Following immersion, calorimeter (surrounding) temperatures
as well as surface temperatures on each specimen are performed in fifteen second intervals, ultimately to
calculate the material thermal conductivity.
Note, ASTM E2584 – 14 has been utilized as an experimental reference. Also, this standard uses radial
heat transfer to calculate thermal conductivity values. The described alternate method above is again used
as a reference and is noted as a modified testing procedure.
2.2 Test Specimens
The material specimens for the described thermal testing were cut from 0.25 inch, 8 foot long rods. Half
inch cuts were made on each polymer rod yielding nine specimens per material. A total of nine polymer
rods were tested, these consisted of: three polymer rods for each boiling bath immersion:
2.3 Test Equipment
The following laboratory equipment utilized during this testing procedure are outlined below:
Standard laboratory hot plate
Stopwatch
Two calibrated type k thermocouples wired to digital multimeters
Three 0.5 in. polymer slugs for each material tested
0.5 in diameter Styrofoam ring disks (insulation)
500ml beaker
Mass balance
The laboratory hot plate is used to eat the 500 ml. beaker (simulating the calorimeter) to boil water, the
mass balance records the mass of the water, both thermocouples are utilized to record the surface
temperature of the polymer slugs and the calorimeter fluid respectively, and the stopwatch is incorporated
to delegate the time to record the temperature measurements. The resulting data and analysis can be found
presented in the remaining report sections.
2.4 Test Results
During the soaking period of four minutes in the calorimeter bath, a total of nine specimens were tested
and temperature differentials were recorded. Tables 2.4.1, 2.4.2, and 2.4.3 describe the recorded
experimental data, and calculated (averaged) thermal conductivity values for three slugs of polycarbonate,
polyethylene, and polypropylene respectively. Figure 2.4.1, illustrates the average temperature profile—
increasing temperature with time—for each polymer specimen, and the calculated average thermal
conductivity values with uncertainty that are associated. Note, the determination for these values and the
methods utilized can be found in section 2.5 below.
Table 2.4.1 Summary of experimental data and calculated thermal conductivities of polycarbonate after
calorimeter bath.
Table 2.4.2 Summary of experimental data and calculated thermal conductivities of polyethylene after
calorimeter bath.
Time (s) ΔT Temp. PC ΔT Temp. PC ΔT Temp. PC
0 74.7 25.3 74.9 25.1 74.4 25.6 25.3
15 73.8 26.2 74.6 25.4 73.5 26.5 26.0
30 72.7 27.3 73.5 26.5 72.4 27.6 27.1
45 71.9 28.1 72.7 27.3 71.6 28.4 27.9
60 70.8 29.2 71.7 28.3 70.5 29.5 29.0
75 70 30.0 70.9 29.1 69.7 30.3 29.8
90 68.9 31.1 69.8 30.2 68.6 31.4 30.9
105 67.6 32.4 68.6 31.4 67.3 32.7 32.2
120 66 34.0 67.0 33.0 65.7 34.3 33.8
135 64.2 35.8 65.3 34.7 63.8 36.2 35.6
150 62.7 37.3 63.8 36.2 62.3 37.7 37.1
165 61.4 38.6 62.6 37.4 61.0 39.0 38.3
180 60.1 39.9 61.3 38.7 59.7 40.3 39.6
195 59 41.0 60.2 39.8 58.6 41.4 40.7
210 57.3 42.7 58.6 41.4 56.9 43.1 42.4
225 56.4 43.6 57.7 42.3 56.0 44.0 43.3
240 55.2 44.8 56.5 43.5 54.8 45.2 44.5
Average 65.5 66.5 65.1 65.671
Thermal Cond. 0.197 0.194 0.198 0.196
Trial #1 Trial #2 Trial #3Average
Time (s) ΔT Temp. PW ΔT Temp. PW ΔT Temp. PW
0 74.8 25.2 74.3 25.7 74 26 25.6
15 73.7 26.3 74.226 25.8 73.174 26.8 26.3
30 72.9 27.1 73.442 26.6 72.358 27.6 27.1
45 71.4 28.6 71.972 28.0 70.828 29.2 28.6
60 69.7 30.3 70.306 29.7 69.094 30.9 30.3
75 68.4 31.6 69.032 31.0 67.768 32.2 31.6
90 67 33 67.66 32.3 66.34 33.7 33.0
105 64.1 35.9 64.818 35.2 63.382 36.6 35.9
120 62.5 37.5 63.25 36.8 61.75 38.3 37.5
135 60.7 39.3 61.486 38.5 59.914 40.1 39.3
150 59 41 59.82 40.2 58.18 41.8 41.0
165 56.2 43.8 57.076 42.9 55.324 44.7 43.8
180 54.7 45.3 55.606 44.4 53.794 46.2 45.3
195 51.9 48.1 52.862 47.1 50.938 49.1 48.1
210 49.1 50.9 50.118 49.9 48.082 51.9 50.9
225 46.6 53.4 47.668 52.3 45.532 54.5 53.4
240 44.1 55.9 45.218 54.8 42.982 57.0 55.9
Average 61.6 62.3 60.8 61.551
Thermal Cond. 0.197 0.195 0.199 0.197
AverageTrial #1 Trial #2 Trial #3
Table 2.4.3 Summary of experimental data and calculated thermal conductivities of polypropylene after
calorimeter bath.
Table 2.4.4 Summary of calculated average and known thermal conductivity values for each polymer
tested.
The above tables show the calculated average thermal conductivity values for each polymer, for the
calorimeter bath. Note, the resulting values (with uncertainty) for both Polycarbonate and Polypropylene
are reasonably accurate values; however, they fail to be considered comparably and experimentally
accurate due to falling outside uncertainty limits to known values.
To illustrate the effects the boiling water bath had on each polymer, the average temperature gradient—
temperature recordings for the interval at fifteen seconds—for the three polymers tested have been
plotted; according to Temperature (°C) vs. Time (s).
Time (s) ΔT Temp. P0 ΔT Temp. P0 ΔT Temp. P0
0 72.7 27.3 73.5 26.5 74.6 25.4 26.4
15 72.6 27.4 73.4 26.6 74.5 25.5 26.5
30 72.4 27.6 73.2 26.8 74.4 25.6 26.7
45 72.3 27.7 73.2 26.8 74.3 25.7 26.7
60 72.2 27.8 73.1 26.9 74.2 25.8 26.8
75 72.1 27.9 73.0 27.0 74.1 25.9 26.9
90 72 28 72.9 27.1 74.0 26.0 27.0
105 71.9 28.1 72.8 27.2 73.9 26.1 27.1
120 71.9 28.1 72.7 27.3 73.8 26.2 27.2
135 71.8 28.2 72.6 27.4 73.7 26.3 27.3
150 71.8 28.2 72.6 27.4 73.7 26.3 27.3
165 71.7 28.3 72.5 27.5 73.6 26.4 27.4
180 71.7 28.3 72.5 27.5 73.5 26.5 27.4
195 71.7 28.3 72.4 27.6 73.5 26.5 27.5
210 71.6 28.4 72.4 27.6 73.4 26.6 27.5
225 71.6 28.4 72.4 27.6 73.4 26.6 27.5
240 71.6 28.4 72.3 27.7 73.4 26.6 27.6
Average 72.0 72.8 73.9 72.889
Thermal Cond. 0.168 0.166 0.164 0.166
AverageTrial #2 Trial #3Trial #1
Material Experimental Avg. (W/m.K) Known Avg. (W/m.K)
Polycarbonate 0.196 ± 0.034 0.204
Polyethylene 0.197 ± 0.034 0.419
Polypropylene 0.166 ± 0.029 0.140
Figure 2.4.1 Average temperature profiles and thermal conductivity values for each polymer slug in the
boiling water calorimeter.
The described uncertainty values found in the above figure and Table 2.4.4 were performed using the
Engineering Equation Solver (EES ®) uncertainty propagation function. This propagation can be found in
the appendix.
From the above data, the following determinations can be drawn:
1) The experimentally determined average thermal conductivity values for
Polycarbonate fall within 5% of known averages, however, fail to be considered
comparably accurate due to uncertainty limits.
2) The experimentally determined average thermal conductivity values for
Polypropylene fall approximately within 15% of known averages, however, fail to be
considered comparably accurate due to uncertainty limits.
3) Further thermal testing conforming to ASTM standards needs to be performed in
order to validate results and also to explain lower Polyethylene thermal conductivity
values recorded
2.5 Analysis of Test Data
To calculate the average thermal conductivity values from the recorded data set, first the amount of heat
transfer from the hot plate to the boiling water needs to be determined:
( ) ( ) ( )
Where Qdot represents the heat transfer or flux from the water to the polymer slug (W), m is the mass of
the water in the calorimeter (kg), CP is the specific heat of water (kJ/kg.K), Tinf. is the temperature of the
water bath (°C), and TS is the surface temperature of the polymer slug (°C).
Using this approximation, we are neglected any heat transfer from convection from the boiling water to
the atmosphere, and also suggesting that the total energy transferred to the calorimeter bath is then
transferred to the polymer slug. Also, any mass boiled off from the calorimeter during constant heating is
considered negligible.
Once the amount of heat transfer (considered relatively constant) to the calorimeter bath is determined,
the average thermal conductivities can be calculated using Fourier’s Law of heat transfer:
( ) ( )
( )
Where k is the thermal conductivity of the material (W/m.K), AS is the polymer rods surface area (m2) and
L is the length of the testing specimen (in).
Note, the above equations utilize the same heat transfer approximation; where energy is conserved by the
assumed total heat transfer from the calorimeter bath to the polymer slugs. Also, the surface areas of the
slugs are approximated as perfect cylinders, neglecting the top surface or circle covered by the thermal
insulation.
Equation 2.5.2 can then be manipulated to solve for the experimental variable k to find the thermal
conductivity:
( ) ( )
By substituting the total heat transfer Qdot, slug surface area, and averaged temperature differentials for
the given polymer, the thermal conductivity can be calculated.
3.0 Summary
The referenced ASTM E2584 - 14 - Standard Practice for Thermal Conductivity of Materials Using a
Thermal Capacitance (Slug) Calorimeter, modified test results indicate fairly accurate thermal
conductivity values for both polymers Polycarbonate and Polypropylene. Values that failed to fall within
comparably accurate uncertainty limits to known averages; but resulted in percentages of those known
averages by approximately 5% and 15% respectively. However, the experimentally determined data for
Polyethylene failed to resemble accurate values when compared to known averages. In regards to the
modified testing procedure, many assumptions were made including those related to the conservation of
energy, yet procedures followed were in fact closely related to those stated in the ASTM standard. Minor
differences include: approximating constant heat transfer (using energy conservation laws) linearly by
vertical means, and fixing the thermocouple to the top surface of the polymer slug with insulation rather
than the described embedment. It should be noted that while determinations can be drawn from the small
batch of testing data, further evidence from testing needs to be performed in order to accurately describe
the effects the calorimeter bath had on the materials.
4.0 Appendix: EES Uncertainty Propagation
Figure 4.1EES Uncertainty propagation for the experimentally calculated thermal conductivity values
5.0 References
1. ASTM E2584-14, Standard Practice for Thermal Conductivity of Materials Using a
Thermal Capacitance (Slug) Calorimeter, ASTM International, West Conshohocken, PA, 2007
2. Efim Litovsky, Jacob I. Kleiman, Michael Shagalov, Robert B. Heimann, “Measurement of the
thermal conductivity of cold gas dynamically sprayed alumina-reinforced aluminum coatings
between -150;°C and +150°C. New test method and experimental results”. Surface and Coatings
Technology, Volume 242, 15 March 2014, Pages 141-145, ISSN 0257-8972,
http://dx.doi.org/10.1016/j.surfcoat.2014.01.033.
(http://www.sciencedirect.com/science/article/pii/S0257897214000498)
Optical Testing of Various Polymers
Submitted to:
Dr. Kyle Gipson
Prepared by:
Mick Blackwell
Benjamin Condro
Mark Dufresne
Brenton Lester
Matthew Lewis
1.0 Introduction The polymers Polycarbonate, Polyethylene, and Polypropylene will be tested for optical properties when exposed to natural light. This optical test was performed in order to determine the aforementioned polymer properties of transmission, reflection, and absorption. The polymers will be subjected to natural light in order to measure the transmission of light through the material and measure the reflection of light off the material. The absorption measurement will be calculated using equation 2.5.1 located in section 2.5. 1.1 Scope The optical testing of the described polymers display different properties for transmission, reflection, and absorption due to the makeup of the material. Each material is comprised of optical properties that either allow light to pass through, reflect off the surface, or absorb in the material. Polycarbonate, polyethylene, and polypropylene each respond differently to light exposure and thus need to be quantified. 1.2 Significance and Use The outcomes of this experiment effectively characterize the polymer properties of transmission, reflection, and absorption when exposed to natural light. These properties will be utilizedd to determine how the materials can be used and the affects it will have when exposed to natural light. 2.0 Optical Testing 2.1 Test specifications and Procedure Testing was comprised of cutting the three materials to the proper length and measuring the optical properties for the materials using a Universal Arc lamp that illuminates natural light 15 inches from the material. The material was placed in front of the radiometer and measured transmission. Once the transmission tests were complete, the radiometer was moved in front of the material location and angled 45 degrees and 10 inches away from the material. The material location remained the same as well as the location of the Universal Arc lamp. The measurements from the tests are displayed in section 2.4. It should be known that ASTM E971 has been utilized as an experimental reference. 2.2 Test Specimens The material specimens for the described optical testing were cut from 1/4 inch thick, 12 x 12 inch long sheets. Each material had protective tape over both faces of the sheet to ensure no scratches or dust was on the material. A total of 9 sheets were cut to dimensions of 4 x 12 inches for each of the three materials. 2.3 Test Equipment The following laboratory equipment utilized during this testing procedure are outlined below:
Universal Arc lamp-Newport Orical Product Line 500 watt Family Radiometer Measuring tape protractor Black back stop-black sheet
The Universal Arc lamp was used to simulate natural light and the radiometer measured how much light was able to penetrate through and/or reflect off the material. Figure 2.3.1 displays the setup to measure the transmission through the material while Figure 2.3.2 displays the testing scenario for measuring the reflection. The resulting data and analysis can be found presented in the remaining report sections.
Figure 2.3.1 Transmission testing setup at approximately 15 inches.
Figure 2.3.2 Reflection testing setup at 45 degrees and 10 inches from material.
The displayed figures represent how the tests were conducted for each material. These tests were performed in the lab under no light. Therefore, no outside light could influence the tests such as overhead lights and hallway lights. It should be noted that in the figures themselves, the overhead lights were on to provide a clear picture of the experiment but where turned off during testing. 2.4 Test Results Following the optical testing, a total of nine trials for each of the three materials, Table 2.4.1 displays the results from measuring the transmission and the reflection. The measurement units are Watts/m^2 which is a measurement of the power over the area. The angle at which reflection was measured is 45 degrees relative to the material location. Table 2.4.1: Data recorded from the transmission and reflection test trials.
Trial Transmission Reflection (45°)Polycarbonate Watts/m^2 Watts/m^2
1 1800 100 2 1800 98 3 1800 100
Polypropylene 1 400 3 2 400 3 3 400 2.8
Polyethylene 1 120 10 2 140 11 3 120 10
Table 2.4.1 shows the measurements for each material trial in terms of transmission and reflection. The initial reading taken before the transmission test and reflection test was recorded at 2000 Watts/m^2 and 0.5 Watts/m^2 respectively. The measurement of absorption could not be tested due to the limited availability of equipment. However, this test can be excluded due to the already collected data and the use of equation 2.5.1 which can calculate the absorption of each material. 2.5 Analysis of Test Data An initial measurement of the Universal Arc lamp natural light admittance was recorded before placing each material in front of the radiometer. During the testing period, each material specimen was placed directly in front of the radiometer which had a 1 inch diameter lens to capture light. When placed directly behind the material, the radiometer measured the transmission of natural light through the material. Thus, revealing how much light will pass
through the material and into the radiometer. Using equation 2.5.1, the optical properties are used for calculations
1 (2.5.1) where Po is the initial light, T is transmission, R is reflection, and A is absorption. All three variables are equal to 1 or 100% of the natural light that originates from the light source. The reflection was measured by moving the radiometer 45 degrees and 10 inches in front of the material being tested. Knowing both the transmission and reflection, the absorption can be calculated. It should be known that each test is a measure of the fractional rate of which light is being transmitted. Thus, the transmission, reflection, and absorption being measured is the fractional percentage of light that originates from the source. Table 2.5.1 displays the average percentage of light transmitted and reflected for each material. Table 2.5.1: Data calculated from the transmission and reflection test trials as a percentage.
Material Transmission Reflection (45°) Polycarbonate 90% 5% Polypropylene 20% 0.1% Polyethylene 6% 0.5%
From the results displayed in table 2.5.1, it can be known that the absorption for each material can be calculated by rearranging equation 2.5.1. The new equation for absorption is displayed in equation 2.5.2.
(2.5.2) From this equation, table 2.5.2 displays the calculated average absorption for each material as a percentage and a numerical value. Table 2.5.2: Calculated values for absorption as a percentage and numerical value.
Material Absorption Watts/m^2 Polycarbonate 5% 200 Polypropylene 79.9% 1599.8 Polyethylene 93.5% 1870
From the table 2.5.2 and table 2.4.1, all values equal the initial reading of 2000 watts/m^2. Thus concluding that all three optical properties have been measured and/or calculated for each material.
3.0 Summary The referenced ASTM E971 - 11 - Standard Practice for Calculations of Photometric Transmittance and Reflectance of Materials to Solar Radiation, tailored test results indicate high transmission for polycarbonate and high absorption for both polymers polypropylene and polypropylene. Polycarbonate allowed 90% transmission of natural light while polypropylene and polyethylene allowed 20% and 6% transmission respectively. The reflection for polycarbonate, polypropylene, and polyethylene was 5%, 0.1%, and 0.5% respectively. The absorption for these materials is calculated to be 5%, 79.9%, and 93.5% for polycarbonate, polypropylene, and polyethylene respectively. In regards to the data obtained for polycarbonate, this material has higher transmission and reflection properties compared to the other two materials. These factors do not degrade the integrity of the material but is considered when determining the type of material to use for specific functions. 4.0 References
1. ASTM E971 - 11, Standard Practice for Calculation of Photometric Transmittance and Reflectance of Materials to Solar Radiation, ASTM International, West Conshohocken, PA, 2007
Magnetic Analysis of Polypropylene,
Polycarbonate, and Polyethylene
Submitted to:
Dr. Kyle Gipson
Prepared by:
Mick Blackwell
Ben Condro
Mark Dufresne
Brenton Lester
Matthew Lewis
1.0 Introduction
The polymers polypropylene, polycarbonate, and polyethylene will be tested in order to derive experimental
magnetic properties. The magnetic test will be performed in order to determine if the polymers facilitate or
impede a magnetic field. The polymers will be placed on a magnet and the intensity of the magnetic field
will be measured. Comparing the magnetic field intensity when a polymer is present against when only air
is present will allow a conjecture to be made as to whether the polymers facilitate or impede magnetic
fields.
1.1 Scope
The magnetic testing on the described polymers quantitatively describe the magnetic field intensity through
each polymer. Through researching magnetic properties of the polymers using CES Edupack 2013 software
there were no listed magnetic properties. Since there were no properties listed, the purpose of this test was
to make a conjecture as to whether the polymers facilitated or impeded magnetic fields between magnets.
1.2 Significance and Use
The conjectures made from this experiment can be used to characterize how the polymers may interact with
surrounding magnetic fields. This is to say that the polymers may or may not be used with a relative, when
compared to air, safety when around magnetic fields.
2.0 Magnetic Testing
2.1 Test Specifications and Procedure
When performing the test, the material specimens (see section 2.2 for elaboration) were placed on top of
the magnet then the gauss meter was used to measure the magnetic field intensity, which is also known as
the magnetic flux density, produced by the magnet. Figure 2.1.1 shows a picture of this procedure. The
gauss meter was also used to record the magnetic flux density through only air at the same height as the
sample. This procedure was repeated for all nine samples.
Figure 2.1.1 Testing apparatus
2.2 Test Specimens
The material specimens used for the described magnetic testing were cut from 0.25 inch diameter, 8 foot
long rods. For each material the specimens were cut in varying lengths from 2 centimeter to 7 centimeter,
exact lengths cut are listed further on. Three specimens from each polymer were cut for a total of nine
samples.
2.3 Test Equipment
The laboratory equipment utilized during this testing procedure included a gauss meter, a caliper, a magnet,
and the material samples. The gauss meter was used to measure the magnetic flux density (in units of gauss,
G) produced by the magnet when either a polymer sample was present or only air was present. The caliper
was used to measure the samples and height for which the gauss meter’s measuring device was placed. The
resulting data and analyzing can be found in the remaining section of the report.
3.0 Tests Results
3.1 Magnetic Testing Results
Through performing the above testing set up the magnetic flux densities from a magnet through
polypropylene, polycarbonate, polyethylene, and air at varying heights was known. These values, which
can be seen in Tables 3.1.1, 3.1.2, and 3.1.3, allow a conjecture to be made as to whether the polymer
facilitated or impeded the magnetic field of the magnet when compared to air.
Table 3.1.1: Magnetic flux density for polypropylene
Polypropylene
Sample Height, ± 0.001
cm
Sample, ± 0.1 gauss Air, ± 0.1
gauss
2.944 56.0 60.0
4.059 19.1 22.0
6.627 5.5 6.6
Table 3.1.2: Magnetic flux density for polycarbonate
Polycarbonate
Sample Height, ± 0.001
cm
Sample, ± 0.1 gauss Air, ± 0.1
gauss
3.637 26.0 30.0
4.884 15.0 17.5
6.795 5.0 6.0
Table 3.1.3: Magnetic flux density for polyethylene
Polyethylene
Sample Height, ± 0.001
cm
Sample, ± 0.1 gauss Air, ± 0.1
gauss
2.314 86.0 110.0
3.396 36.0 40.0
6.304 4.0 4.5
The above tables represent a summary of the data obtained through the magnetic testing performed. Note
that the gauss reading for all polymer samples is lower than the corresponding gauss reading for air.
From these results the following conjectures can be made:
1) Polypropylene impedes magnetic fields relative to air since there is a larger gauss
reading for air at the same heights.
2) Polycarbonate impedes magnetic fields relative to air since there is a larger gauss
reading for air at the same heights.
3) Polyethylene impedes magnetic fields relative to air since there is a larger gauss
reading for air at the same heights.
3.0 Summary
Through performing the magnetic testing described above the magnetic flux density could be measured and
compared to that of air. Through measurements made at similar heights it was conjectured that each
polypropylene, polycarbonate, and polyethylene impede magnetic fields relative to air.
Resistivity Analysis of Polypropylene, Polycarbonate, and Polyethylene
Submitted to:
Dr. Kyle Gipson
Prepared by:
Mick Blackwell
Ben Condro
Mark Dufresne
Brenton Lester
Matthew Lewis
1.0 Introduction
The polymers polypropylene, polycarbonate, and polyethylene were tested in order to derive experimental electrical properties. The resistivity test was performed in order to determine if the polymers facilitate or impede an electrical current. Polymer samples were cut, parameterized, and each sample resistance measured with a Fluke 287 multimeter. By utilizing the relationship between resistance, length, and cross sectional area, an approximate resistivity value was determined for each sample.
1.1 Scope
The electrical testing on the described polymers gave an approximate resistivity value. However, due to the limitations of the Fluke 287 multimeter, conclusive results could not be obtained. In this case, the Fluke 287 could only measure a resistance up to 500 . The samples used during experimentation each exceeded the resistance limit, thus all resistance values used in resistivity calculations were the same (500 . Although the ASTM D257-07 standard states the proper format for resistivity testing, the testing equipment could not meet requirements, therefore the standard was not referenced.
1.2 Significance and Use
Accurate resistivity values were unable to be obtained; the testing provided a minimum bound on resistivity values. The creation of the minimum bound was due to resistivity being directly proportional to resistance. If the multimeter did not max out at 500 , the resistivity value would be higher. Polymers are known to inherently maintain high resistivity values, thus can be used as insulators.
2.0 Electrical Testing
2.1 Test Specifications and Procedure
The test was performed using a Fluke multimeter to measure resistance across a parameterized specimen. Figure 2.1.1 shows a picture of this procedure. The setup, displayed in Figure 2.1.1, shows a polymer specimen attached to the negative and positive terminals of the multimeter.
Figure 2.1.1 Testing apparatus
Note the resistance limit was reached according to the multimeter output screen.
Resistivity was determined from the equation that follows.
∗ (2.1.1)
Where R was resistance, A was the cross section area of each sample, and L was the length of each sample.
2.2 Test Specimens
The material specimens used for the described electrical testing were cut from 0.25 inch diameter, 8 foot long rods. For testing purposes, relatively small samples were cut ranging in size from 0.001m to 0.002m in length.
2.3 Test Equipment
The laboratory equipment utilized during this testing procedure included a Fluke 287 multimeter, a caliper, and the material samples. The multimeter was used to measure the resistance (in units of ohms, ) produced by the polymer sample The caliper was used to measure the samples girth and length. The resulting data and analysis can be found in the remaining section of the report.
3.0 Tests Results
3.1 Electrical Testing Results
Through performing the above testing set up, the resistivity of polypropylene, polycarbonate, polyethylene, was determined. Shown below are the derived sample parameters and resistivity values.
Table 3.1.1: The parameters of each sample tabulated for all trials, resistance for each sample, and calculated resistivity values.
Polypropylene R, MΩ A, m^2 L, m , ohm/m
Trial 1 500 2.58E‐05 0.002 6597403
Trial 2 500 4.03E‐05 0.002 10583333
Trial 3 500 2.85E‐05 0.002 7089494
Polyethylene R, MΩ A, m^2 L, m , ohm/m
Trial 1 500 1.09E‐05 0.0016 3302000
Trial 2 500 4.7E‐05 0.002 11869615
Trial 3 500 1.26E‐05 0.0024 2620211
Polycarbonate R, MΩ A, m^2 L, m , ohm/m
Trial 1 500 8.24E‐06 0.002 2052738
Trial 2 500 1.36E‐05 0.0013 5038066
Trial 3 500 1.69E‐05 0.0021 3967843
Note the relatively dispersed results for each resistivity trial.
For comparison, the average resistivity values for each polymer are shown below with error bars.
Figure 3.1.1: The average resistivity values for each polymer tested with error bars.
Figure 3.1.1 was found to display a large range of values via error bars. Thus, the materials tested were not statistically different. No conclusive results were drawn from the methods used during experimentation, except the fact that polymers do indeed behave as insulators.
3.0 Summary
Although testing results were inconclusive, the overall concept that polymers behave as insulators was proven to be correct. The resistivity values determined were in the ranges appropriate for insulating materials, however skewed drastically. More testing with improved equipment is necessary to further confirm findings.
8090000
5900000
3700000
2.50E+06
3.50E+06
4.50E+06
5.50E+06
6.50E+06
7.50E+06
8.50E+06
9.50E+06
Volume Resistivity,
Ohm/m
Polypropylene High DensityPolyethylene
Polycarbonate
Memorandum
To: Dr. Gipson and Dr. Prins From: Team PolymerWorks
The problem has been answered to the fullest potential based on the teams’ abilities. In regards to the teams’ thoughts, a polymer shelving system has potential to be fabricated on a large scale. Selection of more environmentally friendly plastics should be researched and tradeoffs with standard shelving systems analyzed.
Thank you for the opportunity to approach this problem.
To Those Who Supported Us
We wanted to thank all those who played a part in providing support and advice during project work.
Special Thanks to:
1. Dr. Gipson 2. Dr. Prins 3. Dr. R. Nagel 4. John Wild 5. Lab-Ops
END