more wood, less plastic - doil ecotec

More wood, Less plastic

ⓒ

Doill Wood plastic – the alternative to plastic

What’s special about our Wood plastic

■ Doill Wood Plastic is : · Suitable for extrusion, co-extrusion, injection and blow molding. · Stable quality. · 100% human friendly. · 100% recyclable.

■ Doill Wood Plastic has : · Outstanding physical properties. · No formaldehyde, chlorine or phenol and is odorless. · Weather-resistance, water-proof, durability, flame-resistance, impact-resistance, etc.

Make your own Wood plastic.

Here are steps to get your own Wood plastic

· 100% recyclable. · Contains no formaldehyde, chlorine or phenol, and is odorless. · Weather-resistance, water-proof, durability, impact-resistance. · Stable under temperature changes. · It is perfect to use in Extrusion, Co-extrusion, Injection and blow molding.

Wood Plastic

1 molding type · Extrusion · Co-extrusion · Injection · Blow molding

Additives · Bonding agent · Impact strength modifier · Flame retardant · UV stabilizer · Thermal stabilizer · Flow improver · Processing improver · And others

1 color · Natural · Cherry · Walnut · Dark brown · Beige · Gray · And others

1 plastic · PE · PP · PLA · TPE

· ABS · ASA · PS

1 natural ingredient · Wood flour

Extrusion molding Applications

Technical data sheet (for Extrusion molding, wood 60% and PE based)Properties Unit Test Method Result

Density g/cm³ ISO 1183 1.28

Melt Index Flow (230°C/10kg) g/10min ISO 1133 1.6

Flexural Strength MPa ISO 178 34

Flexural Modulus GPa ISO 178 3.71

Charpy Impact (notched 23℃) KJ/m² ISO 179 3.5

HDT (4.6Kgf/cm² unannealed) ℃ ISO 75-2/B 90

Linear Thermal Expansion 10-5/℃ ISO 11359-2 4.5

Screw Retention N ASTM D1761 990

Flammability UL94 HB

Formaldehyde Emission mg/L ASTM E1333 Less Than 1.5

Contents ofHarmful Materials

As mg/L ISO 17294-2 Less Than 0.1

Cd mg/L ISO 17294-2 Less Than 0.1

Cr mg/L ISO 17294-2 Less Than 0.1

Pb mg/L ISO 17294-2 Less Than 0.1

Hg mg/L ISO 17294-2 Less Than 0.005

Injection molding Applications

Technical data sheet (for injection molding, wood 30% and PP based)Properties Unit Test Method Result


Melt Index Flow (230°C/10kg) g/10min ISO 1133 8.22

Flexural Strength MPa ISO 178 30.6

Flexural Modulus GPa ISO 178 2.94

Charpy Impact (notched 23℃) KJ/m² ISO 179 3.2


Mold Shrinkage % ISO 11359-2 1.0








Blow-molding Applications

Technical data sheet (for blow molding, wood 15% and PE based)Properties Unit Test Method Result


Melt Index Flow (190°C/2.16kg) g/10min ISO 1133 0.3

Tensile Strength MPa ISO 178 18.4

Elongation % ISO 178 N/A


Flammability UL94 N/A

Mold Shrinkage % ISO 294-4 1.5








3D Printing Filament from WPC

Wood pattern Master batch is a functional solid additive for plastic products to express wood pattern. It is perfect to use in extrusion, co-extrusion and injection molding products, it is a concentrated mixture of synthetic resins (PVC, ABS, ASA, PS, PE, etc), pigments and other additives in pellet type.

· Use : Window frame, Door, Decking board, Automobile parts, Furniture, Stationery Consumer goods, etc.

· Effect : Wood pattern effect.

Wood pattern M/B

WOOD

CHERRYWALNUT

MAPLE

Basic colors for Wood Plastic Composites

Natural

Cherry (Reddish Brown)

Walnut (Brown)

Dark Brown

Beige

Gray

Colors After Extrusion Molding After Sanding Treatment

http:// www.doillecotec.com

CUSTOMER SERVICEJason LeeInternational business directorMobile : +82-10-3924-2710Tel : +82-70-7010-8981E-mail : [email protected]