mix design of foamed bitumen mixtures
TRANSCRIPT
-
8/21/2019 Mix design of foamed bitumen mixtures
1/40
Table of Contents1 Introduction .................................................................................................................................... 1
1.1 Problem statement .................................................................................................................1
1.2 Aims and objectives ......................................................................................................................1
2 Study on mix design parameters ....................................................................................................3
2.1 Introduction ............................................................................................................................ 3
2.2 Mix design considerations ......................................................................................................3
2.2.1 Bitumen type................................................................................................................... 3
2.2.2 Foaming conditions.........................................................................................................4
2.2.3 Foam characteristics .......................................................................................................4
2.2.4 Aggregate properties ......................................................................................................4
2.2.5 Mixing..............................................................................................................................5
2.2.6 Mixing and Compaction water content .......................................................................... 5
2.2.7 Compaction..................................................................................................................... 6
2.2.8 Curing ..............................................................................................................................7
2.2.9 Materials .........................................................................................................................8
2.3 Methodology.........................................................................................................................10
2.3.1 Introduction ..................................................................................................................10
2.4 Results and Discussion..........................................................................................................14
2.4.1 Optimum foam characteristics......................................................................................14
2.4.2 Design gradation ...........................................................................................................15
2.4.3 Optimum mixing water content (pre wet water content)............................................ 18
2.4.4 Optimum compaction effort ......................................................................................... 20
2.4.5 Mixture volumetric composition ..................................................................................23
2.4.6 Selection of Foamed Bitumen content (Mechanical tests)...........................................25
2.5 Conclusions ...........................................................................................................................28
3 Study on accelerated curing..........................................................................................................30
3.1 Scope of the study ................................................................................................................30
3.2 Effect of time and temperature on water loss .....................................................................30
3.3 Effect of time and temperature on stiffness.........................................................................31
3.4 Effect of water content on stiffness...................................................................................... 33
3.5 Effect of RAP and Cement on stiffness .................................................................................33
3.6 Conclusions ...........................................................................................................................34
-
8/21/2019 Mix design of foamed bitumen mixtures
2/40
3.7 Further curing study..............................................................................................................34
4 Further study................................................................................................................................. 35
4.1 Generating inputs for Pavement analysis and design (June 2013 August 2013)...............35
4.1.1 Specimen Fabrication.................................................................................................... 35
4.1.2 MEPDG inputs frequency sweep test.........................................................................35
4.1.3 Material constants generation for non-linear elastic analysis...................................... 36
4.2 Analysis and design (September 2013 January 2013)........................................................36
4.2.1 Non-linear elastic analysis using KENLAYER.................................................................. 36
4.2.2 Sensitivity analysis of distress types to FBM inputs......................................................36
4.3 Fatigue and durability study (February 2014-June 2014).....................................................36
5 References .................................................................................................................................... 37
-
8/21/2019 Mix design of foamed bitumen mixtures
3/40
1
1 Introduction
1.1 Problem statement
Unlike Hot Mix Asphalt (HMA) in which bitumen and aggregate are primary components, in foamed
bitumen (FB) treated mixtures, water and, often, active fillers are the additional ingredients.
Therefore, FB mixtures involve more variables, have a less controllable mixing procedure, and are
expected to exhibit more complex behaviour than HMA. It is a very common practice to add
cementitious additives in FB treated mixtures (FBM) for various reasons such as; to achieve early
strength, accelerated curing. Moreover, this technique of bitumen foaming has commonly been
used for recycling, which means mixtures including Reclaimed Asphalt Pavement (RAP) material.
From the literature review it was understood that the permanent deformation behaviour of FBM
with cementitious and RAP addition is well documented (Halles and Thenoux, 2009,Jenkins, 2000).
However, fatigue behaviour of these mixtures with these additives has not been studied so
extensively. It is a well-known fact that FB mixtures are neither fully bound (like HMA) nor unboundmixtures. The presence of mastic (fines + bitumen) brings a difference in these mixtures in which
aggregates are bonded with this mastic. Therefore, water susceptibility of these mixtures is much
more important than in the case of HMA. Usually, therefore, tests on FBMs are mostly accompanied
by water susceptibility tests. FBMs gain strength with time after compaction. This is due to loss of
mixing water in the mix over the time. This process of gaining strength of FBM with expulsion of
water is called curing. With reduction of water in FBM strength (compressive and tensile) and
stiffness increase (Asphalt academy, 2009). Maturity functions can potentially be used to convert the
actual curing temperature to an equivalent temperature. This concept of a time-temperature factor
can be used to quantify the strength development of FB mixtures.
It has been learned that stress and strain signals occur in the pavement under traffic loading. The
magnitude of the stress varies from one location to the other. HMA exhibits stress independent
behaviour at least to a certain level of stress. So, it has been a common practice to analyse HMA
layers using linear elastic theory. Due to the un-bound nature of the FB mixtures, applicability of
linear (stress dependency) behaviour is questionable. In order to obtain reliable stress and strain
data from analysis, an experimental program with varying stress levels has to be carried out.
After detailed literature review, the following aim and objectives are considered.
1.2 Aims and objectivesThe primary aim of this research is to understand the behaviour of FB mixtures with cementitious
additives and RAP material and to design pavements with FBM layers with some confidence.
The objectives of the research are as follows;
1. Detailed literature review of mix design and structural design procedures that are being
followed by different agencies.
2. Identifying critical mix design parameters and studying their influence on mechanical
properties.
3. Understanding curing (water loss and strength gain) mechanisms in FBM.
4. Developing strength-maturity relationships for FB mixtures.
-
8/21/2019 Mix design of foamed bitumen mixtures
4/40
2
5. Studying fatigue behaviour and durability of FB mixtures with cement and RAP material.
6. Understanding the stress dependency behaviour FB mixtures.
7. Conducting mechanistic (non-linear elastic) analysis of pavements with FB layers by using
the results obtained in 4.
8. Designing pavements (structural design) using the Mechanistic Empirical Design Guide
(MEPDG AASHTO design guide).
-
8/21/2019 Mix design of foamed bitumen mixtures
5/40
3
2 Study on mix design parameters
2.1 Introduction
Unlike HMA (Hot mix asphalt), there is no universally accepted mix design method for FBM. Most of
the agencies Asphalt Academy, 2009 and 2002, Wirtgen 2004 and 2010 which use FBM have their
own mix design procedures which are the result of numerous efforts over decades (Jenkins, 2000,
Ebels and Jenkins, 2007, Jenkins and vanderVen, 2001, Jenkins et al., 1999, Muthen, 1998, Acott,
1979,Bowering and Martin, 1976,Castedo et al., 1982,Gui-Ping and Wing-Gun, 2008, Kim and Lee,
2006,Ramanujam and Jones, 2007,Saleh, 2003) for improving the mix design guidelines for FBM. In
spite of all these efforts, Foamed Bitumen application in cold recycling suffers from lack of a
standardised mix design procedure and as a result the mix design parameters such as Foam
characteristics, mixing, compaction, curing and testing that are being adopted are far from being
standardised. To overcome this, a research was undertaken at the University of
Nottingham(Sunarjono, 2008) to develop a mix design procedure by identifying critical mix design
parameters. The mix design parameters identified were
Type of bitumen
Foaming conditions- Foaming water content (FWC) and Foaming temperature
Foam characteristics- Maximum expansion ratio (ERm) and Half-life(HL)
Type of mixer
Aggregate gradation
Foamed Bitumen content
Secondary binder (Cement, lime etc)
Mixing and compaction water content
Compaction effort
Conditioning of compacted specimens (Curing)
The research by Sunarjono, 2008was focussed on the influence of the bitumen type, the foaming
conditions, foam characteristics and mixer type on the mechanical properties of FBM. The major
outcomes of the work were recommendations for producing an optimised FA mixture in terms mixer
type and usage, selection of binder type, bitumen temperature, foam characteristics. Therefore the
present study focussed on other mix design parameters such as aggregate gradation, FB content,
mixing and compaction water content, compaction effort and curing conditions. Thus, the primary
objective of the present study is to propose a practical and consistent mix design procedure.
2.2 Mix design considerations
2.2.1 Bitumen type
In HMA mix design, the expected traffic and the regional climate influence the selection of the
bitumen type. However in FBM mix design, fomability (foaming potential) of the bitumen and the
mixture compactability has to be considered during selection of the bitumen type. Harder bitumen
was avoided in past as it produces poorer quality foam leading to poorer dispersion of fines.
However, it was found that FBM with harder bitumen had a positive effect on mixture stiffness due
to high stiffness of the bitumen (Sunarjono, 2008). However, a FBM with hard binders has to be
mixed in a high speed mixture to ensure good dispersion of mastic.
-
8/21/2019 Mix design of foamed bitumen mixtures
6/40
4
2.2.2 Foaming conditions
Temperatures of the bitumen during foaming and Foaming water content (FWC) are considered as
important parameters during the bitumen foaming process (Jenkins et al., 1999,Sunarjono, 2008,
Kim and Lee, 2006). In general the higher the bitumen temperature the higher the ERm and lower
the HL. FWC also has similar effect on the foam characteristics (Muthen, 1998, Brennan, 1983,
Maccarrone et al., 1994). Efforts were made to propose a range of foaming temperature and
FWC(Sunarjono, 2008). However, it was understood from the results that the range depends on the
bitumen type. For the type of binder used in this work which is 70/100 (90 pen) a range of 150C -
180C and a FWC of 2.5% - 5% was recommended. However, sensitivity analysis of these
characteristics with FWC and temperature was conducted to verify these values.
2.2.3 Foam characteristics
The first qualitative characterisation of FB was the result of a Mobil Australia study ( Mobil Oil
Austrailia Ltd, 1971) in Australia. In their work quality of bitumen foam was characterised by ERm
and HL. Since then along with ERm and HL, FB has been characterised by other characteristics such
as Foam Index (FI)(Jenkins et al., 1999) and minimum viscosity (Saleh, 2006b) and quantitative
recommendations for these foam characteristics were made by some studies (Bowering and Martin,
1976, Ruckel et al., 1982, Muthen, 1998). Attempts by researchers to apply ERm and HL for
optimising foam characteristics have (Maccarone et al., 1995, Acott and Myburgh, 1983,Fu et al.,
2011) been successful. But, optimising FI for FBM was not successful as no optimum point could be
achieved (Sunarjono, 2008) and measuring foam viscosity was found to be difficult because of foam
distortion and this may lead to unreliable results (Namutebi et al., 2011). Consequently in this study
it was decided to study ERm and HL as foam characteristics to be optimised.
2.2.4 Aggregate properties
Many researchers have showed that a wide range of aggregates can be used with FB ranging from
crushed stone (Ruckel et al., 1982,Saleh, 2006a) to sand (Acott and Myburgh, 1983,Bissada, 1987).
Research has showed that aggregate properties such as aggregate type (Ruckel et al., 1982,Saleh,
2006a, Acott and Myburgh, 1983, Bissada, 1987 ), aggregate gradation (Akeroyd and Hicks, 1988,
Saleh, 2006a,Al-Abdul Wahhab et al., 2012,Namutebi et al., 2011), amount of fines (Bowering and
Martin, 1976,Lee, 1981,Csanyi, 1960,Castedo et al., 1982,Sakr and Manke, 1985,Abel, 1978,Acott,
1979) have significant effect of strength and deformation characteristics of FBM. Alongside these,
angularity of aggregate, Plasticity Index (PI) have also been considered (Sakr and Manke, 1985).
The importance of fines (< 63 (or) 75 micron) has been well documented. It has been argued that the
higher the amount of the fines the more promising the mix (Ruckel et al., 1982,Roberts et al., 1984,
Bissada, 1987, Maccarrone et al., 1994). This argument seems to be true, because foam bonds with
fines to form mastic; more mastic will be formed if more fines are available and the mastic enhances
the FBM properties. However, this was not found to be true in all the findings. Mixtures with higher
amount of fines found to have lower soaked strength (Fu et al., 2011). In addition, the amount of
fines suggested to be in mix ranged from 3% (Sakr and Manke, 1985) to 40% (Lee, 1981) which is a
very wider range. Hence, efforts were made in this study to understand the effect of fines in the
FBM by the use of strength and stiffness characteristics of the mixture. However, work was limited
to a single aggregate type (limestone), four different gradations out of which two are fuller curve
-
8/21/2019 Mix design of foamed bitumen mixtures
7/40
5
gradations with 20mm and 32mm nominal maximum size and the other two are gradations with
more fines than fuller gradations.
2.2.5 Mixing
Foamed Bitumen begins to collapse rapidly once it comes into contact with relatively cold
aggregates. Therefore, the mixing process should be a dynamic one. Consequently FB is most often
applied directly from the laboratory foaming plant to the aggregate as it is being agitated in the
mixer. As different mixers can produce up to 25% difference in strength (Academy, 2009) selection
of an appropriate mixer is very important in production of FB mix. It is always recommended to
utilise a mixer that simulates site mixing. From the literature it was found that most of the research
was carried out using a Hobart type mixer (blender type) (Sakr and Manke, 1985,Lee, 1981). Pug mill
drum mixers and milling-drum mixers are the most commonly used mixers on site for the production
of FB mixtures. These mixers provide sufficient volumes in the mixing chamber and energy of
agitation to ensure better mixing (Jenkins, 2000). A pug mill type mixer is therefore recommended
for production of FB mix that is representative of the field (Long et al., 2004). Hence, a twin shaft
pug mill is adopted in this work.
Mixing time should be in accordance with the time required by the bitumen foam to collapse.
Therefore, half-life is an important factor to be considered in the mixing process. The greater the
half -life the better the mixture is predicted to ge. A Half-life of more than 60 seconds can be
achieved with addition of foamant (Maccarone et al., 1995); but this approach is seldom used. In the
laboratory a mixing time of 60 seconds is recommended (Bissada, 1987)which is longer than in situ
mixing but simulates the difference in the energy of the laboratory mixer and field plant and the
same was adopted in this study.
2.2.6 Mixing and Compaction water content
The water content during mixing and compaction is considered as one of the most important mix
design parameter in FBM(Bowering, 1971, Ltd, 1973, Xu et al., 2012). The mixing water content
(MWC) of FBM is defined as the water content in the aggregate when the FB is injected (Fu, 2009).
The MWC helps in dispersion of the mastic in the mix (Brennan, 1983,Jenkins, 2000). However, too
much water causes granular agglomerations which do not yield optimum dispersion of the mastic in
the mix (Ruckel et al., 1982,Fu et al., 2010). It has been considered as best to mix when the water
content of the material is at fluff point; i.e, the water content that gives the material its maximum
loose volume (Sakr and Manke, 1985, Bowering and Martin, 1976, Brennan, 1983). This is
approximately 65% to 85% of OMC as determined by the modified Proctor test (Ruckel, 1978,Abel
and Hines, 1979,Academy, 2009). This range was also validated by Fu et al., 2010 by investigating
the mixng phenomenon by combined micromechanics observations and mechanical testing. In this
study the MWC was always in this range with some exceptions where 65% of OMC has also needed
to consider. It should be noted that, in the present study the mixing and compaction water contents
are the same as the specimens are compacted directly after mixing and therefore it is assumed that
there is no loss of the water content during compaction.
In view of this fact many studies have been focussed on the optimisation of compaction water
content (CWC). (Lee, 1981)) and (Bissada, 1987) optimised CWC with reference to Marshall stability
and found that the optimum CWC was very much dependent on other mix design variable such as
amount of fines and bitumen content. (Sakr and Manke, 1985)), related the CWC to the mix design
-
8/21/2019 Mix design of foamed bitumen mixtures
8/40
6
variable and recommended a linear relationship among them to obtain optimum CWC. However, the
work was performed on a FB stabilised sand mixture which did not have any coarser fraction of
aggregate. Moreover, the work was based on optimising the density, without considering any
mechanical properties. The concept of optimum fluid content was later borrowed from emulsion mix
design in which the sum of the water and bitumen content should be close to OWC (Castedo-Franco
and Wood, 1983, Muthen, 1998). This concept considers the lubricating action of the binder in
addition to that of water. Thus the actual water content of the mix for optimum compaction is
reduced in proportion to the amount of binder incorporated. However, the works of ( Kim and Lee,
2006) and (Xu et al., 2012); which optimised CWC based on both density criteria and fundamental
tests (ITS and tri-axial tests) on Marshall specimens, question the lubricating action of bitumen in the
mix. Although the above discussed works are very informative, they have their limitations as
discussed and little attention has been paid to optimising CWC with the gyratory compactor.
Therefore, the present work aims at obtaining a rational range of CWC for mix design and to study
the lubricating action of the bitumen during the gyratory compaction with the help of fundamental
tests such as ITS, ITSM and the volumetric composition of FBM.
2.2.7 Compaction
As density achieved is crucial to the ultimate performance of the mix, special attention needs to be
paid to the compaction phase of mix design. Because of the presence of the water phase in FBM,
this makes the compaction mechanism different from that of HMA. Various laboratory compaction
methods such as Marshall compaction(Brennan, 1983,Muthen, 1998,Kim and Lee, 2006,Xu et al.,
2012), vibratory compactor (Shackel et al., 1974, Bowering and Martin, 1976, Jenkins, 2000),
gyratory compactor (Brennan, 1983,Maccarrone et al., 1994,Jenkins et al., 2004,Saleh, 2006b) in
the past. There are very well established guidelines for Marshall compaction (Wirtgen, 2004) and
vibratory compaction (Wirtgen, 2010,Academy, 2009). However, there are no established guidelinesfor gyratory compaction of FBM in terms of compaction effort (number of gyrations and compaction
conditions (gyratory angle and gyratory pressure). Past studies have evaluated the feasibility of using
the laboratory gyratory compaction on FBM. In these studies efforts were made to obtain the design
compaction effort in terms of compaction pressure, compaction angle and number of gyrations
(Table 2-1). The compaction pressure recommended by Australian guidelines (0.24kPa) and 1.38kPa
from Table 2-1 were given earlier to SHRP work on HMA and seems to require major adjustments.
(Jenkins et al., 2004) tabulated conditions were based on by single water content and single FB
content. From preliminary trials it was found that 30 gyrations (recommended Kim and Lee, 2006)
were too few to achieve modified Proctor densities. The ideal compaction effort has to produce mix
densities that are achieved in the field. However, this is not possible in laboratory compaction as the
field densities are very much mixture specific. Therefore modified Proctor density, which is used
worldwide for monitoring laboratory densities, is used as reference in the present study.
http://c/Users/evxkkk/AppData/Local/Microsoft/Windows/Temporary%20Internet%20Files/Content.MSO/19757928.xlsxhttp://c/Users/evxkkk/AppData/Local/Microsoft/Windows/Temporary%20Internet%20Files/Content.MSO/19757928.xlsx -
8/21/2019 Mix design of foamed bitumen mixtures
9/40
7
Table 2-1 Gyratory compaction effort on FBM by different researchers
Summary of gyratory compaction effort on FBM by different researchers
Number of
gyrations
(N)
Compaction
pressure
(kPa)
Compaction
angle
(degrees) reference density
Brennan, 1983 20 1.38 - 2.25kg/m3
Maccarrone et al.1994 85 0.24 2 field density
Jenkins et al., 2004 150 0.6 1.25 Modified proctor density
Kim and Lee, 2006 30 0.6 1.25 Marshall density (75 blows)
Saleh, 2006b 80 0.24 2 Australian guidelines for HMA
The literature review indicates that the past studies although informative still had some limitations
warranting additional study and the mix design compaction effort needs to be established. The
present work aimed at determining the mix design compaction effort with gyratory compactor
required to match practical field densities obtainable.
2.2.8 Curing
Curing is the process in which FBMs lose their water content at elevated temperatures. ( Bowering,
1970) found that FBMs gain their full strength only if they expel a large amount of their mixing water
content. From the literature (Bowering and Martin, 1976,Acott, 1979) it was found that pavements
with FB treated layers exhibited premature distress in days rather than in weeks or months after
construction indicating the need for expulsion of water for performance of pavements with FBM.
Ruckel et al., 1982 , concluded that the sample water content was the most important parameter
affecting mix strength. Therefore, a laboratory mix design procedure needs to simulate the field
curing process in order to correlate the properties of laboratory prepared mixtures with those of
field mixtures. An accelerated laboratory curing procedure which is curing at elevated temperature
is the best available option. From the literature it was found that an elevated temperatures of 40C
or 60C have usually been used to accelerate the laboratory curing mechanism. Most of the previous
researchers (Acott, 1979, Maccarone et al., 1995, Muthen, 1998, Lane and Kazmierowski, 2003)
adopted 60C curing temperature which was proposed by Bowering, 1970. However, Ruckel et al.,
1982 expressed his concern over a curing temperature of 60C which is above the softening point of
many bitumen grades used for foaming. This high temperature may cause a change in mix
properties, which is not desirable. Ruckel et al., 1982 recommended curing at 40C for 3 days which
is for long term curing. Jenkins et al., (2004), (Marquis et al., 2003) adopted this method of
laboratory curing at 40C for 3 days. The present study has also adopted this curing regime of for
mixture design purposes.
http://c/Users/evxkkk/AppData/Local/Microsoft/Windows/Temporary%20Internet%20Files/Content.MSO/19757928.xlsxhttp://c/Users/evxkkk/AppData/Local/Microsoft/Windows/Temporary%20Internet%20Files/Content.MSO/19757928.xlsxhttp://c/Users/evxkkk/AppData/Local/Microsoft/Windows/Temporary%20Internet%20Files/Content.MSO/19757928.xlsxhttp://c/Users/evxkkk/AppData/Local/Microsoft/Windows/Temporary%20Internet%20Files/Content.MSO/19757928.xlsxhttp://c/Users/evxkkk/AppData/Local/Microsoft/Windows/Temporary%20Internet%20Files/Content.MSO/19757928.xlsxhttp://c/Users/evxkkk/AppData/Local/Microsoft/Windows/Temporary%20Internet%20Files/Content.MSO/19757928.xlsxhttp://c/Users/evxkkk/AppData/Local/Microsoft/Windows/Temporary%20Internet%20Files/Content.MSO/19757928.xlsxhttp://c/Users/evxkkk/AppData/Local/Microsoft/Windows/Temporary%20Internet%20Files/Content.MSO/19757928.xlsx -
8/21/2019 Mix design of foamed bitumen mixtures
10/40
8
2.2.9 Materials
2.2.9.1 Bitumen
Penetration grade 70/100 supplied by Shell was used in this study. The properties of the bitumen are
tabulated in Table 2-2.
Table 2-2 Properties of 70/100 bitumen used in the study
70/100 grade bitumen properties
Specific gravity 1.03
Penetration Index at 25C 90
Softening Point (C) 45
Viscosity at 135C(mPa-s) 321
2.2.9.2 Virgin aggregates
The virgin mineral aggregate used in this study is limestone from Dene quarry, Derbyshire, UK. It has
been stored separately in stockpiles of size fractions31.5mm, 20mm, 14mm, 10mm, 6mm, dust and
filler (
-
8/21/2019 Mix design of foamed bitumen mixtures
11/40
9
2.2.9.3 Reclaimed Asphalt Pavement (RAP)
The RAP material used in this study was supplied by Lafarge Aggregates Limited obtained from
Elstow Asphalt Plant in Bedfordshire. A visual inspection of the material as supplied indicated
that the RAP aggregate material included particles comprising of slate, broken glass, wood and
tiny plastic components. The RAP aggregate material from the quarry was initially air dried at
room temperature in the laboratory at 205C for 24 hours and then placed in a
thermostatically controlled oven at a temperature of 40C for 24 hours and stored in sealed
containers for the further use. A composition analysis of the RAP aggregate material was also
conducted in order to determine the properties of the RAP and its extracted components. The
composition analysis conducted conformed with BS 598-102:2003, BS 598-101:2004 and BS EN
933-1:2012. The results of the composition analysis and the gradation of the RAP after binder
extraction are stated in Table 2-4 and Table 2-4,whileFigure 2-2 Gradation of RAP and recovered
aggregateshows the gradations of both the RAP aggregate material as obtained from the quarry
and the RAP aggregate material after binder extraction.
Table 2-4 Physical properties of RAP used in the study Table 2-5 Properties of recovered bitumen from RAP
Particle Density (kg/m3) and Water
Absorption (%) (BS EN1097-6:2000)
Size (mm) 20mm-4mm
-
8/21/2019 Mix design of foamed bitumen mixtures
12/40
10
2.3 Methodology
2.3.1 Introduction
This section discusses the methodology adopted in the study to develop practical FBM mix design
methodology. A detailed and careful experimental design was prepared for the study and is
tabulated in table. The factors were selected considering the findings of previous work done at the
University of Nottingham. Figure shows a flow chart that illustrates the methodology that was
adopted in this laboratory experimental study. For optimising MWC/CWC only 100%VA mixture was
considered. Whereas for optimising compaction effort and bitumen content 50%RAP and 75%RAP
mixtures were also considered.
Table 2-6 Experimental design for mix design study.
Mix design
parameter factorial levels Remarks
Bitumen type 90pen (70/100 grade)
constant throughout the
experiment
Foam Characteristics Erm = 10 Recommended by Sunarjono, 2008
for 70/100 bitumenHL (seconds) = 6
Foaming conditions
Temperature
(C):150,160,170 Recommended range by
Sunarjono, 2008FWC(%): 1,2,3,4,5
Mixer type Pug mill type mixer
constant throughout the
experiment
Aggregate type lime stone
constant throughout the
experiment
Aggregate gradation
31.5 fuller, 31.5 finer, 20mm
fuller, 20mm finer to study the effect of fines
MWC/CWC % of OMC: 65,75,85,95 variable to be optimised
FB content % of total mix: 2,3,4,5 variable to be optimised
Volumetrics dry density, % air voidsto study bitumen-water interaction
Mechanical tests ITS-dry, ITS-wet, ITCY to obtain design binder content
Step 1
Foamed bitumen was produced using a laboratory mobile foaming plant type Wirtgen WLB 10 in
which the bitumen was foamed at a water pressure of 6 bars and an air pressure of 5 bars. As seen
in Table 2-6 Experimental design for mix design study., the present study is limited to single grade
70/100 (90pen) bitumen. The characteristics of foamed bitumen (ERm and HL) were obtained by
applying different foaming water contents (FWC) (1% to 5% of the amount of bitumen by weight)
and temperatures (150C, 160C and 170C). The magnitude of these foam characteristics were
obtained by collecting foam produced by 500 grams of bitumen in a 275mm diameter steel bucket. A
Wirtgen measuring instrument (dipstick), which is calibrated to measure the ERm if 500 grams of
bitumen is sprayed into the bucket, was used to record ERm and HL. A stopwatch was used to find
out the time the foamed bitumen took to collapse to half of its maximum volume. The Figure 2-4,
Figure 2-5 and Figure 2-6 show the effect of FWC on expansion ratio and half-life respectively. A
minimum half-life of 6 seconds and expansion ratio of 10 were adopted as selection criteria. The
-
8/21/2019 Mix design of foamed bitumen mixtures
13/40
11
optimum foam characteristics were obtained by plotting ERm and HL versus FWC. The procedure
recommended by Asphalt Academy, (2009) was adapted to obtain optimum FWC and the findings
are discussed in section 2.4.1.
Step 2
The maximum dry density (MDD) and optimum water content (OWC) of each mixture gradation(Figure 2-8) that was studied were determined using modified Proctor in accordance with BS EN
13286-2: 2004. Obtain Npre, the number of gyrations required to compact the aggregate and water
mixture to attain densities that were obtained, by compacting mixture with gyratory compactor.
Compaction was carried out on the aggregate in the gyratory compactor at different water contents
(95%, 85%, 75%, 65% of OWC). The densities were optimised to obtain optimum trial mixing water
content (MMC-trial). The MMC-trial determination for a mixture is shown in Figure 2-8. The Npre,
MDD, OWC, MWC-trail are tabulated in Table 2-7.
Step 3
In this step each graded aggregate was mixed at a water content of MWC-trial and a FB content of
3% and compacted to the optimised density obtained in Step2. Mixing was carried out in laboratory
scale mixing unit, WLS 30, which is a twin shaft mixer. The mixer was positioned in such a way that
the foamed bitumen can be sprayed directly on the mixture in the mixer and mixing was carried out
for 60 seconds. Before foamed bitumen was sprayed, the aggregate and water were mixed for 60
seconds. After mixing the mixture was riffled and transferred into gyratory compactor moulds. The
gyratory compaction was carried out on the mixture targeting the optimised density that was
obtained in Step 2.
Step 4
The moulds were placed in a forced draft oven at 40C for 24 hours before samples were extracted.
The extracted specimens were cured for 3 days at 40C in oven. The cured specimens were then
tested for indirect tensile stiffness modulus (ITSM) and indirect tensile strength (ITS). The results are
as plotted in Figure 2-9 and Figure 2-10 and are discussed in section 2.4.2. An aggregate gradation
was selected based on ITSM and ITS results.
Step 5
Mixing and compaction was carried out on the aggregate of each selected gradation with varying
water content (95%,85%,75% and 65% of OWC) and varying foamed bitumen content (2%, 3%, 4%,
5% by weight of aggregate) to study the interaction of water and bitumen and to optimise the
mixing water content (MWC). The two compaction methods, modified Proctor compaction andgyratory compaction, were studied. After mixing the mixed material was compacted in using
modified Proctor equipment and densities were obtained. This was done for all possible
combinations and the results are as plotted in Figure 2-11. The same mixtures were also compacted
using the gyratory compactor to Npre gyrations.
Step 6
In this stage, all possible combinations of mixtures were mixed and compacted to the modified
Proctor densities that were obtained in Step 5. Gyratory compacted moulds after compaction were
kept at room temperature for 24 hours and then specimens were extracted. The extracted
specimens were cured at 40C and water content of the mix was monitored. The mechanical tests
-
8/21/2019 Mix design of foamed bitumen mixtures
14/40
12
were carried out on the cured specimens after 3 to 5 days depending on the amount water in the
specimen. The tests were carried out on all specimens at the same water content (in between 0.6%
and 0.65%) to eliminate the effect of the factor, water content in the mix, on the measured
mechanical properties. The effect of mixing water content on the mechanical properties can be seen
in plots in the figures 2.12-2.15. The findings of optimisation of MWC with respect to mechanical
properties are discussed in section 2.4.3.
Step 7
Plots of wet densities from gyratory compaction from Step 5 versus number of gyrations were
plotted (figures 2.17 2.20) and number of gyrations required to reach the modified Proctor
densities were identified using these plots. Ndesign was identified from the range of gyrations that
were obtained.
Step 8
Mechanical test (ITSM, ITS-dry, ITS-wet) were performed on the specimens compacted to N designgyrations and an OMWC obtained. The tests were performed on all mixture types (100%VA.,
50%RAP and 75% RAP mixtures).
-
8/21/2019 Mix design of foamed bitumen mixtures
15/40
13
Obtain FB characteristics (ERm and HL)
@T (C): 150, 160, 170
@FWC(%):1,2,3,4,5 (Section 3.2 and figure)
Step1 and Figure 2-4 and Figure 2-5
Determine of Optimum FWC from ERm and
HL data (Step1 and Figure 2-6)
Obtain OMC and MDD for selected four
gradations ( BS 13286-2: 2004) (Step2,
Figure 2-8 and Table 2-7)
Obtain Nprefor all gradations by compacting
the aggregate at OWC to MDD (Step2,
Figure 2-8 and table 2-7)
Optimise densities for all four gradations
and obtain MWC-trial in terms of %OWC
(Step2 and Figure 2-8
Compact aggregates of all four gradations
@MWC-trial and trial FB content of 3% and
cure the specimens at 40C for 3days (Step3)
Test the specimens for ITSM (BS EN 12697-
26:2012) and ITS (BS EN 12697-23:2003)
(Step4, Figure 2-9and Figure 2-10)
Select
deign
gradation
Mix the aggregates
@FB content(%): 2,3,4,5 and
@MWC(%OWC):65,75,85,95,105
(Step5)
Compact the mix using gyratory compactor
to Npre gyrations (Step7)
Obtain densities at all combinations using
Modified Proctor compaction (Step5 and
Figure 2-11)
Obtain Ndesign using gyratory compaction
data and densities obtained by Modified
Proctor compaction (Step7 and Figure 2-16-
2-20)
Compact using gyratory compactor to
modified Proctor densities obtained in Step5
(Step6)
Test the specimens for ITSM, ITS-dry and
ITS-wet (Mechanical tests) (Step6)
Optimise mechanical properties obtain
OMWC (Step6 and Figure 2-12-2-15)
Mix the aggregate at OMWC and compact to
Ndesign at varying FB content of 2%,3%, 4%
and 5%
Test for mechanical properties and
obtain design FB content (Step8 and
Figure 2-24-2-28)
Figure 2-3 Flowchart of methodology implemented in mix design study
-
8/21/2019 Mix design of foamed bitumen mixtures
16/40
14
2.4 Results and Discussion
2.4.1 Optimum foam characteristics
The results of the foaming experiment that was conducted on 70/100 grade bitumen are shown in
Figure 2-4 and Figure 2-5. The experiment was conducted varying FWC and temperature and
keeping all other factors constant. It can be observed from the plots that as foaming temperature
increased from 150C to 170C, the expansion ratio increased while the half-life decreased. This
trend in expansion ratio and half-life is because of increasing thermal energy available to convert
water to steam at higher temperatures. This leads to formation of foam bubbles of large volume and
hence higher ERm. The trend could also be attributed to the viscosity of bitumen at higher
temperatures. As the viscosity of bitumen has an inverse relation to temperature; its viscosity
decreases and hence the bigger size of the bubbles at higher temperatures. The reason for the trend
of half-life is as the foam temperature increases, the temperature of the foam increases and leads to
less stable foam.
The ERm value increased with increase in FWC while the HL decreased. This trend is because of lack
of enough thermal energy to convert larger volume amount of water available into steam. It has to
be noted that HL values decreased with increase FWC and at higher FWC, HL values tends to be
constant.
Figure 2-4 Sensitivity study on ERm with FWC
0
5
10
15
20
25
30
35
0 1 2 3 4 5 6
ExpansionRatio
FWC(%)
Expansion Ratio vs FWC (70/100 grade)
150C
160C
170C
-
8/21/2019 Mix design of foamed bitumen mixtures
17/40
15
Figure 2-5 Sensitivity study on HL with FWC
Figure 2-6 Optimising foam characteristics
2.4.2 Design gradation
As discussed in Section 2.2.4, the gradations were selected in such a way that the study should
understand the importance of the amount the fines (63m passing) and their interaction with the
available surface area of the coarser fraction of aggregate. It is a known fact that smaller the
maximum size of aggregate the more the surface area. The results of mechanical tests that were
performed in step 4 are plotted and can be seen in Figure 2-9 and Figure 2-10. For FB operations, it is
recommended that the minimum amount of aggregate passing 63m or 75m sieve size should be
5% and it can be seen from Figure 2-7 that the amount of fines in the aggregate gradation studied
was always greater than 5%. The results of ITSM and ITS tests that were performed on specimens
compacted at OMWC-trial (Table 2-1) and 3% FB and to N pregyrations are presented in Figure 2-9and Figure 2-10. Both ITSM and ITS values on the mixtures with 31.5mm-finer and 20mm-finer
0
5
10
15
20
25
0 1 2 3 4 5 6
Half-life(seconds)
FWC (%)
Half-Life vs FWC (70/100 grade)
150C
160C
170C
0
5
10
15
20
0
5
10
15
20
25
30
35
0 1 2 3 4 5 6
Half-life(seconds)
ER
and
FWC (%)
Foam Characteristics at 170C
ER
HL
-
8/21/2019 Mix design of foamed bitumen mixtures
18/40
16
gradations were found to be higher than those of mixtures with the fuller gradation. This result
shows the importance of fines in the mixture. However, it has to be noted that though 31.5 mm-
finer and 20mm-fuller have the same amount of fines, their mechanical properties differ
significantly, this can be seen especially ITS values. The reason for this is that the amount of mastic
produced was not enough to weld the coarser fraction of 20mm gradation which has more surface
than 31.5mm gradation coarser fraction. Based on these observations it was understood that though
the amount of fines in the mixtures is a very important mix design parameter, it is not possible to
specify an optimum amount of fines for all gradations. This parameter very much depends on the
maximum size of the gradation.
Figure 2-7 Aggregate gradation considered in the study
Figure 2-8 Modified compaction and gyratory compaction comparison
0
10
20
30
40
50
60
70
80
90
100
0.0 0.1 1.0 10.0 100.0
%Passing
Sieve size(mm)
20mm finer
31.5mm finer
31.5 fuller
20mm fuller
45 55 65 75 85 95 105 115 125
2000
2050
2100
2150
2200
2250
2300
2350
3 4 5 6 7 8
% OMC
Drydensity
(kg/m3)
Moisture content (%)
Modified Proctor
Gyratory compactor-
Npre gyrations
20mm finer
Npre= 200gyrations
OWC = 6.5%
OMWC-trial= 85% of OWC
-
8/21/2019 Mix design of foamed bitumen mixtures
19/40
17
Table 2-7 Summary of modified Proctor compaction and gyratory compaction study
Gradation (% fines) modified Proctor compaction gyratory compaction
Parameter
OMC
(%) MDD(Kg/m3) Npre
OMMC-trial
(% of OMC) density (kg/m3)
31.5mm fuller (5%) 6.5 2170 190 75 2218
31.5mm finer (7.5%) 7 2210 230 80 224720mm fuller (7.5%) 6 2155 180 80 2178
20mm finer (10%) 6.5 2250 200 85 2298
Figure 2-9 ITSM results on FBM with different gradations
20mm-fuller20mm-finer31.5mm-fuller31.5mm-finer
2700
2600
2500
2400
2300
2200
ITSM(MPa)
Effect of gradation on ITSM
-
8/21/2019 Mix design of foamed bitumen mixtures
20/40
18
Figure 2-10 ITS-dry results on FBM with different gradations
Figure 2-11 Modified Proctor test results on FBM
2.4.3 Optimum mixing water content (pre wet water content)
The mechanical properties (ITSM, ITS-dry and ITS-wet) on gyratory compacted and cured specimens
were plotted against MWC in Figure 2-12, Figure 2-13,Figure 2-14 and Figure 2-15. Each ITSM valuein the plot is an average of tests on 8 specimens and ITS-dry and ITS-wet are averages of 4
20mm-fuller20mm-finer31.5mm-fuller31.5mm-finer
550
500
450
400
350
300
ITS(kPa)
Effect of gradation/amount of fines on ITS
4.25 4.75 5.25 5.75 6.25 6.75 7.25
2100
2150
2200
2250
2300
2350
2400
65 75 85 95 105
WetDensity(kg/m3)
Moisture content (% of OWC)
2%FB
3%FB
4%FB
0%FB
-
8/21/2019 Mix design of foamed bitumen mixtures
21/40
19
specimens. The properties were all measured at the same water content of the specimens (0.6-
0.65%). As can be seen from the figures, the peak ITSM values were 85% of OWC, except for 2%FBM.
When ITS-dry results were considered, the optimum MWC was seen at 85% of OWC for 2%FBM and
3%FBM; and for 4% FBM and 5% FBM the peak was at 75%. For ITS-wet values the optimum was
found at 85% except for 5% FBM. Over all, the optimum MWC for all mixtures was consistently
found between 75% and 85% of OWC of the mixture.
Figure 2-12 Optimisation MWC for 2% FBM
Figure 2-13 Optimisation MWC for 3% FBM
1000
1100
1200
1300
1400
1500
1600
1700
1800
1900
100
150
200
250
300
350
400
60 65 70 75 80 85 90 95 100
ITSM
(MP
a)
ITS(kPa)
% OMC
2 % FBM - Mechanical properties (100% VA)
ITS-dry(kPa)
ITS-wet(kPa)
ITSM (MPa)
1000
1200
1400
1600
1800
2000
2200
2400
100
150
200
250
300
350
400
450
500
60 65 70 75 80 85 90 95 100
ITSM(MPa)
ITS(kPa)
% OMC
3% FBM- Mechanical properties (100% VA)
ITS-dry(kPa)
ITS-wet(kPa)
ITSM (MPa)
-
8/21/2019 Mix design of foamed bitumen mixtures
22/40
20
Figure 2-14 Optimisation MWC for 4% FBM
Figure 2-15 Optimisation MWC for 5% FBM
2.4.4 Optimum compaction effort
To study the optimum compaction effort and to obtain the design number of gyrations (N design ), the
heights were obtained from the gyratory compactor during compaction. From the height data
density was calculated and plotted against number of gyrations (Figure 2-17, Figure 2-18,Figure 2-19
and Figure 2-20). The marks on the curves are the target densities that were obtained from modified
Proctor data (Figure 2-8). It can be seen from the plots that, though the target densities were
different, the number of gyrations that were required to compact to those target densities are in a
similar range. That means, a design number of gyrations that are required to compact modified
Proctor densities can be established. Ndesignfor all FBMs considered were in the range of 120-160
gyrations. An average of 140 gyrations was adopted as Ndesign.
0
500
1000
1500
2000
2500
3000
0
100
200
300
400
500
600
60 65 70 75 80 85 90 95 100
ITSM(MPa)
ITS(kPa)
%OMC
4% FBM- Mechanical properties (100% VA)
ITS-dry(kPa)
ITS-wet(kPa)
ITSM (MPa)
0
500
1000
1500
2000
2500
3000
0
100
200
300
400
500
600
60 65 70 75 80 85 90 95 100
ITSM
(MPa)
ITS(kPa)
% OMC
ITS-dry(kPa)
ITS-wet(kPa)
ITSM (MPa)
-
8/21/2019 Mix design of foamed bitumen mixtures
23/40
21
Figure 2-16 Modified proctor test results on mixtures considered in the study
Figure 2-17 Obtaining Ndesignfor mixture with 100%VA and 0% FB at OM WC
2000
2050
2100
2150
2200
2250
2300
3 4 5 6 7 8 9
DryDensity(kg/m3)
Water Content (%)
0%RAP
50%RAP
75%RAP
1800
1900
2000
2100
2200
2300
2400
0 40 80 120 160 200
Wetdensity(kg/m3)
Number of gyrations
0%FB - 100%VA
Target density = 2330kg/m3)
MWC = 80% of OWC = 5.2%
-
8/21/2019 Mix design of foamed bitumen mixtures
24/40
22
Figure 2-18 Obtaining Ndesignfor mixture with 100%VA and 2% FB at OMWC
Figure 2-19 Obtaining Ndesignfor mixture with 100%VA and 3% FB at OMWC
1800
1900
2000
2100
2200
2300
2400
0 40 80 120 160 200
WetDensity(kg/m3)
Number of gyrations
2%FB - 100%VA
target density
Target density = 2280kg/m3
MMC = 80% OMC = 5.2%
1800
1900
2000
2100
2200
2300
2400
0 40 80 120 160 200
Wetdewnsity(kg/m3)
Number of Gyrations
3%FB - 0%RAP
target density
Target density = 2260kg/m3
MMC = 80% OMC = 5.2%
Ndeg= 120 - 160gyrations
-
8/21/2019 Mix design of foamed bitumen mixtures
25/40
23
Figure 2-20 Obtaining Ndesignfor mixture with 75%RAP FBM at OMWC
2.4.5 Mixture volumetric composition
The effect of MWC and bitumen on mixture volumetrics was studied by means of two compaction
methods; modified Proctor compaction and gyratory compaction. Bulk densities of specimens that
were compacted to 140 gyrations (Ndesig) for mixtures with different bitumen content were plotted
against MWC. The densities of the specimens increased as the foamed bitumen content increased.
This result indicates that FB increases the compactability of the mixture. The magnitude of this
behaviour can only be studied from water-bitumen interaction curves. This phenomenon was
supported by a shift in peak of the curves towards the left from 100% OWC. However, this shift was
not considerable, and was negligible from 4% FB to 5% FB. Thus replacing water in the mixture with
bitumen doesnt give required level of compactability. Air voids of specimens after curing were
plotted against FB content (Figure 2-22). The theoretical maximum densities were mathematically
calculated from the aggregate and bitumen densities data. Overall, the air voids decreased gradually
as FB content increased.
1800
1900
2000
2100
2200
2300
2400
0 40 80 120 160 200 240 280
WetDensity(kg/m3)
Number of gyrations
75% RAP
0% FB
3% FB
Target density for 0% FBM = 2230kg/m3
Target density for 3% FBM = 2200 /m3
OMMC = 80% OMC = 4.8%
Ndeg= 80 - 120gyrations
-
8/21/2019 Mix design of foamed bitumen mixtures
26/40
24
Figure 2-21 Influence of FB content on densities
Figure 2-22 Influence of FB content on air voids
2000
2050
2100
2150
2200
2250
60 65 70 75 80 85 90 95 100
drydensity(k
g/m3)
% OWC
2%FB
3%FB
4%FB
5%FB
12.00
13.00
14.0015.00
16.00
17.00
18.00
19.00
20.00
21.00
22.00
60 65 70 75 80 85 90 95 100
Va(%)
% OWC
2%FB
3%FB
4%FB
5%FB
-
8/21/2019 Mix design of foamed bitumen mixtures
27/40
25
Figure 2-23 Influence of FB content on VMA
2.4.6 Selection of Foamed Bitumen content (Mechanical tests)
The results of mechanical tests on the mixtures that were compacted at optimum MWC which is
80% of OWC and to Ndesign, and varying FB content were plotted in Figure 2-24, Figure 2-25,Figure
2-26, Figure 2-27 and Figure 2-28. As can be seen in the plots there is a clear optimum ITSM value for
all mixtures. For 100%VA mixtures, the optimum was found at 4% FB content. Similarly, the optimum
ITSM values for 50%RAP and 75% RAP mixtures were found at 3.5% and 3% FB content respectively.
It has to be noted that, though the mixing and compaction was carried at room temperature, themixtures with RAP have optimum ITSM values at lower FB content than 100%VA mixture. This
indicates that in FBM design it is not correct to treat RAP just as fresh aggregate, which means that a
separate mix design for mixtures with RAP is imperative.
If ITS-dry values are considered, there was not any optimum for 100%VA mixtures. ITS-dry values for
these mixtures increase with increased in FB content without any optimum value. However, an
optimum could be located for both the mixtures with RAP (50% RAP and 75% RAP mixtures). The
optimum values were found at 3% FB for both mixtures. When ITS-wet results are considered, the
optimum ITS-wet was found only for 75% RAP mixtures, which is at 3% FB content. There was not
any optimum for any mixtures if ITSR was considered. However, it can be noted that, though ITS-dry
values were higher for 100%VA mixture than for mixtures with RAP, the ITS-wet and ITSR values
were found to be superior for mixtures with RAP. This indicates that the mixtures with RAP have
better resistance against water than mixtures without any RAP. This could be attributed to the
presence of fully bitumen coated RAP aggregates in the mixture. Overall, from the results, at 4% and
3% FB contents, optimum mechanical properties were found for 100%VA and 75% RAP mixtures
respectively. However, optimum FB content was not very clear for 50% RAP mixtures. So, a value
between 3.5% and 3%; which is 3.25% was finally adopted as the design FB content for 50% RAP
mixtures. Though UCS tests were performed on all the mixtures, the results (Figure 2-28) were not
considered for the selection of optimum FB content.
18.00
20.00
22.00
24.00
26.00
28.00
30.00
60 65 70 75 80 85 90 95 100
VMA(%)
% OWC
2%FB
3%FB
4%FB
5%FB
-
8/21/2019 Mix design of foamed bitumen mixtures
28/40
26
Figure 2-24 Effect of Foamed bitumen content on ITSM
Figure 2-25 Effect of Foamed bitumen content on ITS-dry
1500
1700
1900
2100
2300
2500
2700
2900
2 2.5 3 3.5 4 4.5 5
ITSM(MPa)
% Foamed Bitumen
100%VA
50% RAP
75%RAP
300
350
400
450
500
550
2 2.5 3 3.5 4 4.5 5
ITS
-dry(kPa)
% Foamed Bitumen
100%VA50% RAP
75%RAP
-
8/21/2019 Mix design of foamed bitumen mixtures
29/40
27
Figure 2-26 Effect of Foamed bitumen content on ITS-wet
Figure 2-27 Effect of Foamed bitumen content on ITSR
100
150
200
250
300
350
400
2 2.5 3 3.5 4 4.5 5
ITS-wet(kPa)
% Foamed Bitumen Contnet
100%VA
50% RAP
75% RAP
30
35
40
45
50
55
60
65
70
2 2.5 3 3.5 4 4.5 5
ITSR(%
)
% Foamed Bitumen
100%VA
75% RAP
50% RAP
-
8/21/2019 Mix design of foamed bitumen mixtures
30/40
28
Figure 2-28 Effect of Foamed bitumen content on UCS
2.5 Conclusions
The conclusions that were drawn in accordance to the mix design parameters that were considered
in the study are:
1. The limited study on the gradation of aggregate with two different amounts of fines showed
the importance of fines in the mixture and dependence of its amount on maximum size of
the aggregate (surface area available). From the detailed literature review in conjunction
with the results of this study, it was understood that for a good FBM, the amount of fines inthe mixture should be more than in an HMA mixture and also even more than in bitumen-
emulsion cold mixtures. However, there is an optimum to this amount as well; where
beyond this optimum the mechanical properties deteriorate. However, finding an optimum
amount of fines is not in the scope of this study.
2. The role of the bitumen during compaction was studied. The study showed that the
bitumen helps in compaction of the mixture but not as effective as water. The bitumen-
water interaction studies also revealed that total fluid (water + bitumen) is not a valid
parameter in mix design of FBM.
3. A rational range of optimum mixing water content (OMWC) was suggested; which is 75-85%
of OWC obtained by modified Proctor test.
4. It was found that a unique design number of gyrations (Ndesign ); the compaction effort
equalling modified Proctor compaction can be established for FBM with a specific aggregate
gradation.
In addition to the above findings, the following conclusions can also be drawn from the present
study on mix design parameters.
5. The study showed that gyratory compaction resulted in higher unit weights and lower
optimum water contents than those obtained by the modified Proctor compaction test.
2.00
2.50
3.00
3.50
4.00
2 2.5 3 3.5 4 4.5 5
UCS(MPa)
% Foamed Bitumen
100%VA
50% RAP
75%RAP
-
8/21/2019 Mix design of foamed bitumen mixtures
31/40
29
6. The parameter MWC needs to be addressed with reference to OWC obtained from the
modified Proctor test, as this is a parameter obtained from modified Proctor test whose
parameters depends on amount of fines; which an important mix design parameter.
7. It was found that stiffness measure (ITSM) was more sensitive to FB content with clear
optimum than other mechanical properties such as ITS-dry and ITSR.
8. The mixtures with RAP showed more resistance to water than mixtures without RAP.
9. It was observed that the presence of RAP influenced the design FB content; which means
treating RAP as black rock in FBM mix design is not appropriate.
-
8/21/2019 Mix design of foamed bitumen mixtures
32/40
30
3 Study on accelerated curingFoamed bitumen mixtures gain strength with time after compaction. This is due to loss of mixing
water in the mix over time. This process of gaining strength of FB mixtures with expulsion of water is
called curing. With the reduction of water in the FB mixtures strength (compressive and tensile) and
stiffness increase (Academy, 2009). It is obvious that the laboratory samples used for mix design andto determine engineering properties should be representative samples of field placed mixtures.
Hence, the aim of this study is to develop a standard laboratory curing regime(s) at which it is
sensible to conduct performance tests that represents conditions in the field.
To fulfil this aim the following objectives were considered on FBM.
1. To study influence of curing temperature and time on stiffness and water loss in the mix.
2. To study influence of cement and RAP on curing (stiffness gain and water loss).
3. To develop stiffness maturity (time-temperature factor) relationships.
4. To study performance in terms of permanent deformation of mixtures at the different curing
conditions those are being followed by different agencies.
The need for development of a curing regime protocol and maturity concept was discussed in the
year 1 report and is not repeated here. The specimen fabrication method was discussed was
discussed in Chapter 2. In this method after the specimen was compacted, the specimen was left in
the mould at room temperature for 24hours and then extracted at which time the average water
content was 4.72%. The water content in the specimen was monitored for 30 days. (It is planned to
monitor for a longer period, however, in this report only the first 30 days period is presented) by
observing the change in the specimens weight over time.
3.1 Scope of the study1. In order to avoid ageing of bitumen, it was recommended to cure the specimens below
softening point of the bitumen used in the mixture, which is 45C for the 70/100 grade
bitumen used in this study. Hence, curing temperatures of 40C, 30C, 20C and 5C were
considered. Though curing at 20C and 5C are not to be considered as accelerated curing,
these temperatures were included to study the effect of this temperature on curing.
2. To study the effect of RAP and cement, the following mixtures were considered (a) 100% VA
(b) 100%VA+1%Cement (c) 50% RAP (d) 50%RAP+1% Cement (e) 75% RAP+1% Cement
3. The Non-destructive stiffness (ITSM) test was selected for assessing curing of the specimen.
This is in order to carry out the test on the same set of specimens to nullify variability in the
mixtures and to derive reliable trends for curing evaluation.
3.2 Effect of time and temperature on water loss
The water content in the specimen which was monitored over time is plotted in Figure 3-1. A trend
line which is a power curve is also included. The initial water content in the mixture during
compaction was 5.2% (80% of OWC). The plots showed that water content in the specimen reached
about 25% of the initial amount after 24 hours of curing at both 30C and 40C. Similarly, water
content reached to about 50% of initial amount when specimens were cured at 20C and 5C. The
trend suggests that the rate of water loss is proportional to the amount of water present in the
mixture. In other words, the rate of water loss decreased with time. It is clear from the plot and alsoobvious that the water loss is dependent on curing temperature. The higher the curing temperature
-
8/21/2019 Mix design of foamed bitumen mixtures
33/40
31
the faster was the water loss. However, all curves, except the 5C curves, seem to reach a constant
amount after which the loss is negligible.
Figure 3-1 Effect of time and temperature on water loss
3.3 Effect of time and temperature on stiffness
The stiffness (ITSM) values that were measured over time on the specimens that were cured at
different temperatures are plotted in Figure 3-2. The plot shows a stiffness monitored for a period of30 days and at curing temperatures of 40C, 30C, 20C and 5C. Trend lines were also included in
the plot. The trend line is a logarithmic with positive tangential slope. As can be seen from the
figure, for all conditions, stiffness increased with time of curing. However, this gain was most rapid
for specimens cured at higher temperatures. This is because rapid curing takes place at higher
temperature; the rapid loss of water yields higher stiffness values with time. This phenomenon can
be seen in Figure 3-3 in which, water loss and stiffness gain of specimens cured at 20C is presented.
0
0.5
1
1.5
2
2.5
3
0 5 10 15 20 25 30 35
Moisturecontent(%)
Number of days
40C
30C
20C
5C
Power (40C)
Power (30C)
Power (20C)
Power (5C)
-
8/21/2019 Mix design of foamed bitumen mixtures
34/40
32
Figure 3-2 Effect of time and temperature on stiffness
Figure 3-3 Effect of time on curing
0
500
1000
1500
2000
2500
3000
3500
4000
0 5 10 15 20 25 30 35
ITSM
(MPa)
Number of days
40C
30C
20C
5C
Log. (40C)
Log. (30C)
Log. (20C)
Log. (5C)
0
0.5
1
1.5
2
2.5
3
0
500
1000
1500
2000
2500
3000
0 5 10 15 20 25 30 35
WaterContent(%)
ITSM(MPa)
Number of days
ITSM
m/c
Log. (ITSM)
Power (m/c)
-
8/21/2019 Mix design of foamed bitumen mixtures
35/40
33
3.4 Effect of water content on stiffness
Figure 3-4 shows the plots of stiffness (ITSM) versus water content for the specimens that were
cured at different temperatures. As a general trend, with decrease in water content the stiffness was
increased. However, as can be seen from the figure when individual temperatures were considered
it was found that temperature has a significant additional impact on the stiffness of the mixture. For
example, the specimens which were cured at 40C having water content around 1% showed better
stiffness (ITSM) than the specimens cured at other lower temperatures at same water content in the
specimen.
Figure 3-4 Effect of water content on stiffness
3.5 Effect of RAP and Cement on stiffness
Figure 3-5 shows ITSM results for two curing conditions, 20C for 3 days (early stage of curing) and
40C for 3 days (long term curing). The Figure 3-5shows the importance of cement in FBM especially
during early stages of as construction of FBM layer. The presence of RAP has positive influence on
the stiffness values in early stages of curing. It has to be noted that during early stages of curing,
mixtures with RAP showed better stiffness than mixtures with 100%VA. This could be because of
presence of fully bitumen coated aggregates which provide some deformation resistance. However,
for fully curing regime, 100% VA mixtures showed better stiffness values. This could be because
slower water loss in the mixture with RAP.
500
1000
1500
2000
2500
3000
3500
00.511.522.5
ITSM
(MPa)
moisture content in mix (%)
40C
20C
30C
5C
Log. (40C)
Log. (20C)
Log. (30C)
Log. (5C)
-
8/21/2019 Mix design of foamed bitumen mixtures
36/40
34
Figure 3-5 Effect of RAP and Cement on ITSM
3.6 Conclusions
The following conclusions can be drawn based the work so far
1. The effect of curing temperature and curing period on water loss and stiffness gain was
studied.
2. It was found from the experimental results that temperature and time both have a
significant influence on stiffness and water content in the mixture.
3. The presence of cement enhances the mechanical properties (ITSM); its presence is
especially important during early stage of curing.
3.7 Further curing studyThe further study in the present curing study includes (May2013 July 2013)
1. A curing study on mixtures with cement and RAP is in progress.
2. The possibility of Stiffness-maturity relationship development will be studied.
3. Curing study in terms of performance (permanent deformation) and strength (ITS-dry and
ITS-wet) characteristics will be studied. As these are destructive tests only the following
conditions will be considered.
Table 3-1 Curing regimes considered for destructive testing
TemperatureFullyWrapped Unwrapped combination
5C 28 days n/a n/a
20C 28 days 3days
7days (unwrapped) + 21
days(fully wrapped)
40C
28 and 3
days
28 and 3
days n/a
0
500
1000
1500
2000
2500
3000
3500
4000
100%VA 1%Cement 50% RAP 100%VA 1%Cement 50% RAP
20C 40C
ITSM(MPa)after3
dayscuring
-
8/21/2019 Mix design of foamed bitumen mixtures
37/40
35
4 Further studyThe further work that has to be done includes
4.1 Generating inputs for Pavement analysis and design (June 2013
August 2013)The structural design of pavement ensures that it serves its purpose structurally and functionally in
an economically viable manner with in estimated design life. Such design can be achieved by
empirical method or mechanistic method or mechanistic-empirical method. The mechanistic-
empirical method of design of pavements will be considered. Huang (2004) reported that the
mechanistic-empirical method is based on the mechanics of materials that relates an input, such as a
wheel load, to an output or pavement response such as strain or stress. The response values are
subsequently used to predict distress from laboratory-test and field performance data. The main
objective of this study is to evaluate the sensitivity of pavement distresses; permanent deformation
on subgrade and fatigue in FBM base layer. For this, two mechanistic analysis tools namely
KENLAYER and MEPDG (Mechanistic-Empirical Pavement Design Guide) will be considered.
The MEPDG is an improved pavement design method adopted by AASHTO (American Association of
State Highway and Transportation). This methodology depends on the pavement material
characterisation of the fundamental engineering parameters. The design method is an iterative
process using the analytical results based on the trial designs postulated by the designer. A trial
design is analysed for adequacy against user input data.
KENLAYER is a flexible pavement response analysis application in KENPAVE computer program
developed by Huang (2004) will be for analysis. Unlike MEPDG, this gives only the response of the
pavement to a given load. Distress models in KENLAYER are fatigue cracking and permanentdeformation. From the preliminary studies and from literature it was understood that FBMs exhibit
non-linear behaviour. Hence, non-linear elastic analysis is considered. For this type of analysis using
KENLAYER, the K- model and its parameters are used. In KENLAYER for non-linear analysis, three
methods were recommended. Out of these three first method which is sub dividing the stress
dependent layers is considered in this study.
4.1.1 Specimen Fabrication
The mixture data consists of dynamic modulus frequency sweep tests on specimens for five
temperatures and four rates of loading. The specimens should have a diameter of 100 mm and a
height-to-diameter ratio of 1.5.
4.1.2 MEPDG inputs frequency sweep test
The MEPDG software uses the material properties to calculate incremental and accumulated
pavement damage based on the expected variation in environmental and traffic loading. This
process, as defined by the user-selected reliability, allows the designer to judge whether or not the
input design thickness and/or materials meet the expected performance during the design period. In
the current version of the MEPDG procedure, three input levels can be used based on the availability
of materials characterization data. The site-specific laboratory-measured values of the material
properties are used as Level 1 input parameters. Predicted values determined from basic volumetric
properties of as constructed mixtures are considered Level 2 input parameters. Level 3 inputparameters are provided as default values in the software based on mixture gradation and the
https://www.google.co.uk/url?sa=t&rct=j&q=&esrc=s&source=web&cd=1&cad=rja&ved=0CDIQFjAA&url=http%3A%2F%2Fwww.trb.org%2Fmepdg%2F&ei=qjywUd24DYGn0QWYvoGAAg&usg=AFQjCNFd1brpUWBQa_G6er6Qw_grXKVAVQ&sig2=FT1VUbZs-JiXZ30C6EtIcQ&bvm=bv.47534661,d.d2khttp://en.wikipedia.org/wiki/American_Association_of_State_Highway_and_Transportation_Officialshttp://en.wikipedia.org/wiki/American_Association_of_State_Highway_and_Transportation_Officialshttp://en.wikipedia.org/wiki/American_Association_of_State_Highway_and_Transportation_Officialshttp://en.wikipedia.org/wiki/American_Association_of_State_Highway_and_Transportation_Officialshttps://www.google.co.uk/url?sa=t&rct=j&q=&esrc=s&source=web&cd=1&cad=rja&ved=0CDIQFjAA&url=http%3A%2F%2Fwww.trb.org%2Fmepdg%2F&ei=qjywUd24DYGn0QWYvoGAAg&usg=AFQjCNFd1brpUWBQa_G6er6Qw_grXKVAVQ&sig2=FT1VUbZs-JiXZ30C6EtIcQ&bvm=bv.47534661,d.d2k -
8/21/2019 Mix design of foamed bitumen mixtures
38/40
36
performance grade (PG) of the binder. In the present study the dynamic modulus (|E*|) which is
Level 1 input will be measured by frequency sweep tests at different temperatures.
|E*| tests will be performed with the NU14 testing machine in accordance with AASHTO TP 62
(AASHTO, 2007a). Tests were performed on 150 mm tall by 100 mm diameter specimens as
previously mentioned. Four testing temperatures ranging from 5C to 50C will be used. Six testing
frequencies ranging from 0.1 Hz to 25 Hz will be used. To measure against damage to the test
samples, the tests will be conducted starting from the coldest temperatures to the warmest
temperatures. In addition, at each test temperature, the tests will be performed starting from the
highest to the lowest frequency. Each sample will be conditioned at the testing temperature for a
minimum period of 3 hr before the test was started. Load levels were selected in such a way that at
each temperature-frequency combination, the applied strain was in the range that ensure testing
will conducted in the linear viscoelastic range of mixture, a necessary requirement for a valid |E*|
test. All tests will be conducted in the uniaxial mode without confinement in line with current
standard AASHTO specifications.
4.1.3 Material constants generation for non-linear elastic analysis
The inputs will be generated in accordance to BS EN 13286-7:2004 which is cyclic load triaxial test for
resilient modulus. The K1 and K2 values obtained from this resilient modulus test.
4.2 Analysis and design (September 2013 January 2013)
4.2.1 Non-linear elastic analysis using KENLAYER
Since, one of the objectives of the present study is to evaluate the performance of FBMs, the
structural analysis will be studied by examining the stress and strain responses distribution inpavement with FBM base layer using non-linear elastic analysis using the parameters obtained in
resilient modulus test. This response data will be used to obtain the life of the pavements with FBM
layer.
4.2.2 Sensitivity analysis of distress types to FBM inputs
For sensitivity analysis on input parameters of MEPDG, the sensitivities of five MEPDG performance
measures to inputs will be studied by varying one input parameter per trial using the MEPDG. The
distresses that will be studied during this analysis are alligator cracking, longitudinal cracking,
thermal cracking, rutting and smoothness for flexible pavements. While for sensitivity analysis using
KENLAYER only fatigue cracking in base layer and permanent deformation on subgrade will only beconsidered.
4.3 Fatigue and durability study (February 2014-June 2014)
For comparing the fatigue resistance of different mixes, and to understand the effect of cement and
RAP addition on fatigue behaviour, a plot of number of cycles (N) against N divided by vertical
deformation (VD) will be used. The N value at which N/VD reaches its maximum value will be
considered as N critical. The N value at which the specimen fails will be considered as N failure. This
method of representing fatigue behaviour was actually used by Read (1996) to define the initiation
and propagation phase of fatigue. It was understood from literature that durability (water
sensitivity) of FB mix is an important factor to be considered for better field performance. The testmethod for durability that will be employed in this research is testing strength parameter (ITS and
-
8/21/2019 Mix design of foamed bitumen mixtures
39/40
37
UCS) before and after vacuum saturation conditioning. This permits the calculation of a ratio that
gives an indication of the water sensitivity of the FB mix. The lower the ratio, the more sensitive is
the mix to the effect of water.
5 ReferencesABEL, F. Year. Foamed asphalt base stabilisation In: 6th Annual Asphalt Paving Seminar, 1978 Colorado
State University.
ABEL, F. & HINES, C. R. 1979. Base Stabilisation with Foamed Asphalt. Colorodo Division of Highways.
ACADEMY, A. 2009. A Guideline for the Design and Construction of Bitumen Emulsion and Foamed Bitumen
Stabilised Materials.
ACOTT, S. M. Year. Sand stabilization using foamed bitumen. In: 3rd Conf. on Asphalt Pavements for South
Africa, 1979 Durban. 155172.
ACOTT, S. M. & MYBURGH, P. A. 1983. Design and Performance Study of Sand Bases Treated with Foamed
Asphalt. Transportation Research Record 290-296.
AKEROYD, F. M. L. & HICKS, B. J. 1988. Foamed Bitumen Road Recycling. Highways 56, 42- 45.AL-ABDUL WAHHAB, H. I., BAIG, M. G., MAHMOUD, I. A. & KATTAN, H. M. 2012. Study of road bases
construction in Saudi Arabia using foam asphalt. Construction and Building Materials, 26, 113-121.
BISSADA, A. F. 1987 Structural Response of Foamed-Asphalt-Sand Mixtures in Hot Environments.
Transportation Research Record, 134-149.
BOWERING, R. H. Year. Properties and Behaviour of Foamed Bitumen Mixtures for Road Building. In: 5th
Australian Road Research Board Conference, 1970 Canberra, Australia. 38-57.
BOWERING, R. H. 1971. Soil Stabilisation with Foamed Bitumen. Highway Engineering in Australia.
BOWERING, R. H. & MARTIN, C. L. Year. Foamed Bitumen Production and Application of Mixtures Evaluation
and Performance of Pavements. In: Association of Asphalt Paving Technologists, 1976. 453-477.
BRENNAN, M. 1983. A Laboratory Investigation on the Use of Foamed Asphalt for Recycled Pavements Joint
Transportation Research Program Technical Report. Purdue University.
CASTEDO-FRANCO, L. H. & WOOD, L. E. Year. Stabilisation with Foamed Asphalt of Aggregate Commonly
Used in Low Volume Road. In: Low volume road: 3rd International Conference., 1983 Washington,
DC. Transportation Research Board., 297-302.
CASTEDO, F. L., WOOD, L. E. & ALTSCHAEFFL, A. G. 1982. Laboratory mix design procedure for foamed
asphalt mixtures Indiana Department of Highways,Indianapolis.
CSANYI, L. H. 1960. Bituminous Mixes Prepared with Foamed Asphalt. Iowa Engineering Experiments Station
Bulletin No 189. Iowa State University.
EBELS, L. J. & JENKINS, K. J. Year. Mix design of bitumen stabilised material: best practices and
considerations for classification. In: 9th conference of Asphalt Pavements for South Africa, 2007.
FU, P. 2009. Micromechanics for Foamed Asphalt Stabilized Materials. PhD, University of California.
FU, P., JONES, D. & HARVEY, J. T. 2011. The effects of asphalt binder and granular material characteristics on
foamed asphalt mix strength. Construction and Building Materials, 25, 10931101.
FU, P., JONES, D., HARVEY, J. T. & HALLES, F. A. 2010. Investigation of the Curing Mechanism of Foamed
Asphalt Mixes Based on Micromechanics Principles. Journal of Materials in Civil Engineering, 22,29-38.
GUI-PING, H. & WING-GUN, W. 2008 Effects of moisture on strength and permanent deformation of foamed
asphalt mix incorporating RAP materials. Construction and Building Materials, 22, 3040.
HALLES, F. A. & THENOUX, G. Z. 2009. Degree of Influence of Active Fillers on Properties of Recycled Mixes
with Foamed Asphalt. Transportation Research Board, 13,127-135.
JENKINS, VANDEVEN, M. & GROOT, J. D. Year. Characterisation of foamed bitumen. In: 7th conference on
asphalt pavements for South Africa, 1999.
JENKINS, K. & VANDERVEN, M. Year. GUIDELINES FOR THE MIX DESIGN AND PERFORMANCE PREDICTION
OF FOAMED BITUMEN MIXES. In: 20th South African Transport Conference South Africa, Meeting
the Transport Challenges in Southern Africa, 2001.
JENKINS, K. J. 2000. Mix Design Considerations for Cold and Half-warm Bituminous Mixes with Emphasis on
Foamed Bitumen. PhD, University of Stellenbosch, South Africa.
-
8/21/2019 Mix design of foamed bitumen mixtures
40/40
JENKINS, K. J., ROBROCH, S., HENDERSON, M. G., WILKINSON, J. & MOLENAAR, A. Year. Advanced Testing for
Cold Recycling Treatment Selection on N7 Near Cape Town. . In: 8th Conference on Asphalt
Pavements for Southern Africa (CAPSA 04), 2004 Sun City, South Africa.
KIM, Y. & LEE, H. 2006. Development of mix design procedure for cold in-place recycling with foamed
asphalt. Journal of Materials in Civil Engineering, 18, 116-124.
LANE, B. & KAZMIEROWSKI, T. Year. Expanded asphalt stabilization on the Trans-Canada Highway In:
Transportation Research Board (TRB) 82nd Annual Meeting, 2003 Washington, DC.LEE, D. Y. Year. Treating marginal aggregates and soil with foamed asphalt. In: Association of Asphalt
Paving Technologists, 1981. 211-150.
LONG, F. M., THEYSE, H. L. & VENTURA, D. F. C. 2004. Characterization of Foamed Bitumen Treated
Materials from HVS Test Sections. Pretoria, South Africa: CSIR Transportek.
LTD, M. O. A. 1973. Foamed Bitumen - Cold Dustless Mixtures. Technical Bulletin, Bitumen, 5.
MACCARONE, S., HOLLERAN, G. & KY, A. Year. Cold Asphalt System as an Alternative to Hot Mix. In: 9th
AAPA International Asphalt Conference., 1995.
MACCARRONE, S., HOLLERAN, G., LEONARD, D. J. & HEY, S. Year. Pavement Recycling Using Foamed
Bitumen. In: 17th ARRB conference, 1994 Queensland. 349-65.
MARQUIS, B., BRADBURY, R. L., COLSON, S., MALLICK, R. B., NANAGIRI, Y. V., GOULD, J. S. & MARSHALL, M.
Year. Design, construction and early performance of foamed asphalt full depth reclaimed FDR
pavement in Maine. In: TRB 82nd Annual Meeting, 2003 Washington, D.C.
MOBIL OIL AUSTRAILIA LTD 1971. Foamed bitumen: A new development. Technical Bulletin.
MUTHEN, K. M. 1998. Foamed Asphalt Mixes:Mix Design Procedure. CSIR TRANSPORTEK.
NAMUTEBI, M., BIRGISSON, B. & BAGAMPADDE, U. 2011. Foaming Effects on Binder Chemistry and
Aggregate Coatability using Foamed Bitumen. Road Materials and Pavement Design, 12, 821-847.
RAMANUJAM, J. M. & JONES, J. D. 2007. Characterization of foamed-bitumen stabilization. International
Journal of Pavement Engineering, 8, 111-122.
ROBERTS, F. L., ENGELBRECHT, J. C. & KENNEDY, T. W. 1984. Evaluation of Recycled Mixtures Using Foamed
Asphalt. Transportation Research Board, 78-85.
RUCKEL, P. J. Year. Foammix Asphalt- An Alternative Mixing Method. In: 22nd Annual Kansas Asphalt Paving
Conference, 1978 The University of Kansas.
RUCKEL, P. J., ACOTT, S. M. & BOWERING, R. H. 1982. Foamed - asphalt paving mixture: Preperation of
Design mixes and treatment of test specimens. Transportation Research Board, 88-95.
SAKR, H. A. & MANKE, P. G. 1985. Innovations in Oklahoma Foamix Design Procedures. TransportationResearch Board, 1034,26-34.
SALEH, M. F. 2003. New Zealand experience with foam bitumen stabilization. Transportation Research
Board, 40-49.
SALEH, M. F. 2006a. Effect of aggregate gradation, mineral fillers, bitumen grade, and source an mechanical
properties of foamed bitumen-stabilized mixes. Geomaterials 2006.
SALEH, M. F. 2006b. Effect of Rheology on The Bitumen Foamability and Mechanical Properties of Foam
Bitumen Stabilised Mixes. The International Journal of Pavement Engineering 8.
SHACKEL, B., MAKHIUCHI, K. & DERBYSHIRE, J. R. Year. The Response of a Foamed Bitumen Stabilised Soil to
Repeated Triaxial Loading In: ARRB, 1974. 74-87.
SUNARJONO, S. 2008. The Influence Foamed Bitumen Characteristics on Cold Mix Asphalt Properties. PhD,
University of Nottingham.
WIRTGEN 2004. Cold Recycling Manual.
WIRTGEN 2010. Cold Recycling Technology.XU, J. Z., HAO, P. W., MA, Y. F. & LIU, N. 2012. Study on the optimization design of mixing moisture content in
foamed asphalt mix. Materials and Structures, 45, 1071-1085.