engineering materials lecture #14
DESCRIPTION
ENGR 151 Professor Martinez. Engineering materials lecture #14. Simple fracture is the separation of a body into two or more pieces in response to an imposed constant stress and at temperatures relatively low as compared to the material’s melting point. Failure analysis (Chapter 8). - PowerPoint PPT PresentationTRANSCRIPT
![Page 1: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/1.jpg)
ENGR 151Professor Martinez
![Page 2: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/2.jpg)
Simple fracture is the separation of a body into two or more pieces in response to an imposed constant stress and at temperatures relatively low as compared to the material’s melting point
![Page 3: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/3.jpg)
Stress can be tensile, compressive, shear, or torsional
For uniaxial tensile loads: Ductile fracture mode (high plastic
deformation) Brittle fracture mode (little or no plastic
deformation)
![Page 4: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/4.jpg)
“ductile” and “brittle” are relative (ductility is based on percent elongation and percent reduction in area)
Fracture process involves two steps: Crack formation & propagation
Ductile fracture characterized by extensive plastic deformation in the vicinity of an advancing crack
Process proceeds slowly as crack length is extended.
![Page 5: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/5.jpg)
Stable crack: resists further extension unless there is increase in applied stress
Brittle fracture: cracks spread extremely rapidly with little accompanying plastic deformation (unstable)
Ductile fracture preferred over brittle fracture Brittle fracture occurs suddenly and
catastrophically without any warning Brittle (ceramics), ductile (metals)
![Page 6: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/6.jpg)
Figure 8.4 (differences between highly, moderately, and brittle fracture)
Common type of fracture occurs after a moderate amount of necking After necking commences, microvoids form Crack forms perpendicular to stress direction Fracture ensues by rapid propagation of crack around the
outer perimeter of the neck (45° angle) Cup-and-cone fracture
![Page 7: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/7.jpg)
Takes place without much deformation (rapid crack propagation)
Crack motion is nearly perpendicular to direction of tensile stress
Fracture surfaces differ: Lines/ridges that radiate from origin in fan-like pattern Ceramics: relatively shiny and smooth surface
![Page 8: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/8.jpg)
Crack propagation corresponds to the successive and repeated breaking of atomic bonds along specific crystallographic planes
Transgranular: fracture cracks pass through grains
Intergranular: crack propagation is along grain boundaries (only for processed materials)
![Page 9: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/9.jpg)
Quantification of the relationships between material properties, stress level, crack-producing flaws, and propagation mechanisms
![Page 10: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/10.jpg)
Fracture strengths for most brittle materials are significantly lower than those predicted by theoretical calculations based on atomic bonding energies. Due to microscopic flaws that exist at
surface and within the material (stress raisers)
![Page 11: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/11.jpg)
Assume that a crack is similar to an elliptical hole through a plate, oriented perpendicular to applied stress.
σm = 2σo(a/ρt)1/2
σo = applied tensile stress ρt = radius of curvature of crack tip a = represents the length of a surface crack
(pg. 167)
![Page 12: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/12.jpg)
Maximum stress at crack tip
![Page 13: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/13.jpg)
Kt = σm/σo=2(a/ρt)1/2
Measure of the degree to which an external stress is amplified at the tip of a crack
Stress amplification can also take place: Voids, sharp corners, notches Not just at fracture onset
![Page 14: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/14.jpg)
Critical stress required for crack propagation in a brittle material:
σc=(2Eγs/πa)1/2
E = modulus of elasticityγs = specific surface energya = one half the length of an internal crack
When magnitude of tensile stress at tip of flaw exceeds critical stress, fracture results
![Page 15: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/15.jpg)
A relatively large plate of glass is subjected to a tensile stress of 40 MPa. If the specific surface energy and modulus of elasticity for this glass are 0.3 J/m2 and 69 GPa, respectively, determine the maximum length of a surface flaw that is possible without fracture.
![Page 16: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/16.jpg)
The measure of a material’s resistance to brittle fracture when a crack is present
KIC = Yσc(πa)1/2
σc = critical stress for crack propagation
a = crack lengthY = parameter depending on both crack
and specimen sizes and geometries
![Page 17: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/17.jpg)
For thin specimens, KIC depends on specimen thickness
Example 8.2 Example 8.3
![Page 18: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/18.jpg)
Charpy V-notch (CVN) technique: Measure impact energy (notch toughness) Specimen is bar-shaped (square cross
section) with a V-notch High-velocity pendulum impacts specimen Original height is compared with height
reached after impact Izod Test
Used for polymers
![Page 19: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/19.jpg)
Form of failure that occurs in structures subjected to dynamic and fluctuating stresses.
Failure can occur at stress level considerably lower than tensile of yield strength
Occurs after repeated stress/strain cycling
Single largest cause of failure in metals
![Page 20: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/20.jpg)
Axial, flexural, or torsional Three modes
Symmetrical Asymmetrical Random
Mean stress:σm = (σmax + σmin)/2
![Page 21: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/21.jpg)
Range of stress:σr = σmax – σmin
Stress amplitudeσa = σr/2 = (σmax – σmin)/2
Stress ratioR = σmin / σmax
![Page 22: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/22.jpg)
Fatigue testing apparatus Simultaneous axial, flex, and twisting
forces S-N curve (stress v. number of cycles)
Fatigue limit Fatigue strength Fatigue life
![Page 23: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/23.jpg)
Evaluation of materials without impairing their usefulness X-radiography
Produces shadowgraph Ultrasonic testing
Pulse echo
![Page 24: Engineering materials lecture #14](https://reader035.vdocuments.mx/reader035/viewer/2022070404/56813ab6550346895da2b85b/html5/thumbnails/24.jpg)
Midterm #2 Tuesday, May 4th
Quiz on Thursday Creep