INDIAN RUBBER INSTITUTEKarnataka Branch
PAPER- I POLYMER SCIENCE
OBJECTIVE QUESTIONS & ANSWERS
YEAR 1996
(a) Select appropriate answers:i) Fischer Tropsch process refers to
a) Stereo regular polymerization
b) Conversion of methanol to formaldehyde
c) Reaction between carbon monoxide and hydrogend) Dehydrogenation of ehtylbenzene to styrene
ii) Heptane is assigned an Octane number ofa) 100; b) 0; c) 42; d) none of these
iii) If the repeat units are joined in a 3-dimensional array, the resulting polymer will be
a) linear polymerb) branched polymer
c) cross linked polymer
d) none of the above
iv) The ratio of Mw and Mn for most of the synthetic polymer is
a) more than 1b) less than 1
c) equal to 1
d) none of the above
v) In polycondensation to prepare polyamides, the reaction takes place between
a) carboxyl and hydroxyl group
b) amino and hydroxyl groupc) amino and carboxyl group
d) none of the above
vi) The relation between degree of polymerization, molecular weight of a polymer and molecular
weight of monomer is given by Mn = DPn x m
vii) The chain carrier in case of anionic polymerization area) carbonium ions
b) hydroxyl ions
c) carbanions d) none of the above
-
7/30/2019 objective questions without.doc
2/94
viii) The Florys principal of equal reactivity states that---------------------
ix) In suspension polymerization technique the initiator used area) water soluble
b) monomer soluble
c) insoluble in either water or monomerd) soluble in both water and monomer
x) Critical micelle concentration refers toa) concentration of surfactant at which there exists complete molecular dispersion
b) a state of equilibrium between dissolved surfactant molecule and micelles
c) concentration beyond which only micelle formation is possible d) none of the above
10x1=10
1. (b) State whether the following statements are True or False:
i) In chain polymerization the normal mode of addition of the incoming monomer to thegrowing chain is always head to tail
ii) Atmospheric oxygen is a good inhibitor for polymerization
iii) Polymers produced by cationic polymerization technique is called living polymer
iv) Co-ordination polymerization is also known as insertion polymerization
v) Emulsion polymerization technique can be used to prepare high molecular weight
polymers
vi) Diene rubbers are susceptible to oxidation
vii) The ration Mn /Mw = 1+P (F)
viii) Glass transition temperature (Tg) of a polymer does not depend on flexibility of the chain
segments
ix) Copolymer of isobutylene and acrylonitrile is called nitrile rubber
x) Ultracentrifuge method is used to determine weight average molecular weight
10x1=10
-
7/30/2019 objective questions without.doc
3/94
PAPER - I POLYMER SCIENCE
YEAR 1997
1. a) Multiple choice questions. Select the right answer
i) Polyethylene, polypropylene and nylon are known as
a) Glassy polymers
b) Amorphous polymers
c) Crystalline polymers
d) None of these
ii) Fibers have molar cohesion per 5 A chain length in the range
a) less than 2 Kcal/gm. mole
b) 4-10 Kcal/gm mole
c) 2-5 Kcal/gm mole
d) none of these
iii) Azobisisobutyronitrile on thermal decomposition produces free radicals along with
a) CO2
b) NO
c) N2
d) None of these
iv) Polymer produced by anionic polymerization is called
a) Dead polymer
b) Living polymer
c) Ladder polymer
d) None of these
-
7/30/2019 objective questions without.doc
4/94
v) Mw/Mn value for synthetic polymers obtained by co-ordination polymerization technique is
a) between 2-3
b) greater than 10
c) between 8-10
d) none of these
vi) Glass transition temperature of polyvinyl chloride is
a) 1000C b) 800C c) +800C d) none of these
vii) Expandable polystyrene beads are produced by
a) bulk polymerization technique
b) solution polymerization technique
c) suspension polymerization technique
d) none of these
viii) Atactic polymers are
a) high melting and highly soluble
b) low melting and easily solublec) high melting and less soluble
d) none of these
ix) Weight-average molecular weight of a polymer can be determined bya) Osmometry
b) Viscometry
c) Light scatteringd) None of these
x) Most important criteria of a polymer to form strong fiber isa) partially crystalline
b) amorphous
c) highly crystallined) none of these
1x10=10
-
7/30/2019 objective questions without.doc
5/94
b) State whether the following statements are true or false
i) Ionic polymerizations are generally carried out in presence of water
ii) Cationic polymerization is normally done at high temperature
iii) Heat is essential to initiate free radical polymerization
iv) Inhibitors are added for storage of monomers
v) Copolymers are physical mixture of two polymers
vi) Elastomer have Tg above room temperature
vii) Nylons do not have many common organic solvents
viii) Polyethylene can be dissolved only at higher temperature
ix) All crystalline polymers are stereo regular
x) Step growth polymers show very high molecular weight.
1x10=10
-
7/30/2019 objective questions without.doc
6/94
PAPER- I POLYMER SCIENCE
YEAR 1998
1. a) Give one example each of the following and write down chemical structure of the repeat
unit in each case:
i) An amorphous polymer which is glassy at room temperature, but rubbery at
1450C - PC
ii) A crystalline polymer whose Tg is below room temperature PE (LDPE)
iii) An inorganic polymer which is useful as a rubber over a wide temperature
range - PDMS
iv) A rubber which is a terpolymer- EPDM
v) A rubber which is a block copolymer
b) State whether the following statements are true or false:
i) Ring-opening polymerization is a free radical reaction
ii) The effect of high temperature is to increase the tensile property of rubber
iii) Emulsion polymerization is nothing but a solution polymerization
iv) Polymers are polydispersity materials
v) Bezoyl peroxide is normally used in ionic reactions
c) Select the correct answer
i) Block polymers are mostly produced through
a) ionic polymerization
b) condensation polymerization
c) free radical polymerization
-
7/30/2019 objective questions without.doc
7/94
ii) A cross linked polymer is
a) always flexible
b) always rigid
c) may be made flexible or rigid
iii) A fiber forming polymer has
a) very regular repeating units
b) weak intermolecular forces
c) amorphous structure
iv) In step polymerization, each polymer formed can react further with
a) monomers only
b) polymers only
c) both monomers and polymers present
v) Tacticity in polymers is due to the presence of
a) double bond in polymer backbone
b) heterochain polymer backbone
c) asymmetric carbon atom
-
7/30/2019 objective questions without.doc
8/94
PAPER- I- POLYMER SCIENCE
YEAR 1999
1. A. State whether the following statements are correct or wrong:
i) High-pressure polymerization of ethylene gives high density polyethylene
ii) Free radical polymerization of propylene gives good yield of structural polypropylene
iii) Natural rubber is 1,4 Cis Polybutadiene
iv) Polybutadiene rubber has high resilience
v) Polymerization is accompanied by a decrease in the total number of molecules
vi) Polymers prepared from monomers with bifunctional groups always are branched in
structure
vii) Monomers with polar groups always give rise to polar polymers
viii) Isotactic structures facilitate crystallinity in polymers
ix) A monomer can be converted to polymer through reactions that create new bonds
x) Trans configuration in polymers results in high elongation and low modulus
xi) Atactic polymers usually have higher melting point than syndiotactic polymers
xii) Branched polymers are held by primary bonds in one direction and through secondary
bonds in other two directions
xiii) Bond energy of S-S bond is higher than that of C-C bond
xiv) Butyl rubber is produced by ionic polymerization
xv) Block copolymers are type of branched polymers
B. Select the correct term from the bracket
i) (Cellulose, cellulose acetate, Polybutadiene) is a natural polymer
ii) Rubbers are usually useful only after (cooling, heating, cross linking)
iii) Degradation of addition polymers commonly takes place by a (step, chain) mechanism
iv) Basic requirements of a fiber forming polymer is (low Tm, low Tg, high molecular
symmetry/molar cohesion)
v) Dissolution of polymer (precedes, follows) swelling
(15x1)+(5x1)=20
-
7/30/2019 objective questions without.doc
9/94
PAPER1 POLYMER SCIENCE
YEAR 2000
1. (a) Multiple choice questions. Select the right answer
i) Living polymers formed byA. Cationic polymerization
B. Anionic polymerization
C. PolycondensationD. None of these
ii) Number average molecular weight of a polymer can be determined byA. Viscometry
B. End group analysis
C. Osmometry
D. Light scattering
iii) For a Hookean material stress is directly proportional to
A. Shear rateB. Strain
C. Viscosity
D. Strain rateiv) The chain carrier in case of cationic polymerization are
A. Carbanions
B. Hydroxyl ionsC. Carbonium ions
D. None of these
v) Copolymer of isobutylene and acrylonitrile is calledA. Nitrile rubberB. Butyl rubber
C. Acrylic rubber
D. None of thesevi) Glass transition temperature of polystyrene is
A. 500C
B. -1000CC. 1000C
D. none of these
vii) Zeigler-Natta Catalysts are used to produceA. Condensation polymer
B. Block copolymers
C. Stereo regular polymersD. None of these
-
7/30/2019 objective questions without.doc
10/94
viii) For all the synthetic polymers MW/Mn value is
A. 1C. =1
D. =
ix) Glass transition temperature can be measured usingA. glass thermometer
B. capillary rheometer
C. DSCD. Osmometer
x) Benzoyl peroxide is a well known
A. Initiator
B. chain transfer agentC. inhibitor
D. short stop
(10x1=10)
(b) Give one example with structure of each of the following
i) A monomer which can be polymerized by radical, coordination, cationic and/or anionicmethod
ii) An inorganic polymer which is useful as a rubber over a wide range of temperature
Silicone rubberiii) A linear polymer which does not contain any hydrogen atom and useful for insulating
purpose CF2-CF2iv) A rubber which is resistance to both hydrocarbon oil and flame - PC
v) A polar rubber which is a copolymer and useful for light footwear(5x1-5)
(c) State whether the following statements are correct or wrong
i) Most of the elastomers after curing become thermoplastics (X)
ii) Gutta percha is same as cis-polyisoprene (X)
iii) If there are 1000 repeat units in a polymer molecule, DP of the polymer is 1000 (CH
iv) The structure of isoprene is CH2=CH-C=CH2 (X)
v) Solution polyemerization technique is recommended where the polymer is used in its
solution form ()(5x1=5)
-
7/30/2019 objective questions without.doc
11/94
PAPER- I POLYMER SCIENCE
YEAR 2001
1. (a) Give one example with structure of repeat unit for each of the following
i) A rubber which is excellent resistant to oxidation, ozone attack and also good heat ageing
resistance EPM/EPDM
ii) A rubber which is useful for light footwear
iii) A copolymer which is non oil resistant rubber - SBR
iv) A homopolymer which is non oil resistant rubber - PBD
v) A naturally occurring polymer which is not a rubber - Cellulose
vi) A condensation polymer which is useful in making tyres - PU
(6x2=12)
(b) State whether the following statements are correct or wrong
i) All crystalline polymers can be converted into a useful fibers
ii) Natural rubber is glassy at 00C
iii) Poly vinyl chloride can be made flexible even at room temperature
iv) All commercially useful rubbers are organic in nature
v) A thermoplastic material can be made rubbery through chemical modification
vi) Stress induced crystallization is not found in natural rubber
vii) Ionic polymerization are generally carried out in presence of water
viii) Diene rubbers are susceptible to oxidation
(1x8=8)
PAPER I POLYMER SCIENCE
YEAR 2002
-
7/30/2019 objective questions without.doc
12/94
1. (a) Give one example with structure of repeat unit for each of the following:
i) A linear polymer which does not contain any hydrogen atom and useful for insulating
purpose CF2-CF2
ii) A terpolymer, which is useful for making automotive window seal - EPDM
iii) A rubber having good oxidation resistance and highly impermeable to gases used mainly
in tyre inner tubes - Butyl
iv) A polar homopolymer, which is useful for making adhesives
PMMA/acrylic/PVAC/PAN/PVA
v) An inorganic polymer, which is useful as a rubber over a wide range of temperature -
Silicone
vi) A polymer, which can be prepared by radical, coordination, cationic and/or anionicmethod
vii) A rigid homopolymer, which can be made flexible even at room temperature and useful
in cable industry - PVC
viii) A highly crystalline polymer used very much in tyre industry - Nylon
ix) A homopolymer which is capable of crystallizing when stretched and does not exhibit as
high a gum tensile strength
x) A copolymer, which is used as a oil and solvent resistant rubber and does not crystallize
on stretching - NBR
(2x10=20)
PAPER I POLYMER SCIENCE
YEAR 2003
1. a) Multiple choice questions, select the right answer(s)
-
7/30/2019 objective questions without.doc
13/94
i) Polypropylene is known as
a) Glassy polymerb) Amorphous polymer
c) Crystalline polymer
d) Ionomer
ii) Glass transition temperature of polystyrene is
a) 1000Cb) 100C
c) 1000C
d) 1200C
iii) Within polymeric materials, localized mobility of the segments is called
a) Segmental motionb) Molecular motion
c) Brownian movement
d) Micro Brownian movement
iv) Weight average molecular weight of a polymer can be determined by
a) Viscometry
b) End group analysisc) Osmometry
d) Light scattering
v) Glass transition temperature of a polymer is determined by
a) Infrared spectrophotometry
b) Differential scanning calorimetry
c) Mass spectrometryd) Scanning Electron Microscopy
vi) Most important criteria of a polymer to form strong fiber isa) Partially crystalline
b) Amorphous
c) Highly crystallined) Should be branched
vii) Polymer produced by Anionic polymerization is calleda) Dead polymer
b) Living polymerc) Ladder polymer
d) None of theseviii) A crystalline polymer whose Tg is below 1000C
a) Polypropylene
b) Polystyrenec) Polyethylene
d) Polychloroprene
-
7/30/2019 objective questions without.doc
14/94
ix) Atactic polymers are
a) High melting and highly solubleb) Low melting and easily soluble
c) High melting and less soluble
d) None of these
x) Copolymer of Styrene and Butadiene, which is used in tire is
a) SBSb) SBR
c) SEBS
d) XSBR
1x10=10b) State whether the following statement is TRUE or FALSE
a) Plastics exhibit elongation at break ranging usually 200-500%
b) All crystalline polymers are stereo regularc) Elastomers have Tg above room temperature
d) Natural rubber is 1,4 cis polyisoprenee) Vinyl polymerization are highly exothermic
(1x5=5)
c) An example for inorganic polymer is Siliconei) A rubber, which is, manufactured both by radical and anionic polymerization
is Styrene
ii) Example for anionic polymerization initiator is Alkyl Li, Alkoxides
iii) Example for a polymer with a low Tg but not a rubber is PEiv) Molecular weight control is achieved using chain transfer agents
(1x5=5)
-
7/30/2019 objective questions without.doc
15/94
PAPER- I POLYMER SCIENCE
YEAR -2004
1. a) Choose the correct answer from the given alternatives.
i) The weight average molecular (MW) weight is determined by
a) End group analysis
b) Osmometry
c) Viscometryd) Light scattering
ii) The glass transition tempreture (Tg) of low density polyethylene is
a) -1200 C b) +1200C c) 00C d) does not have any (Tg)
iii) Name a polymer which can be prepared via anionic, free radical and co-ordinationpolymerization
a) Poly bytadiene
b) Polypropylenec) Polychloroprene
d) Polyethylene terephthalate
iv) For a Hooken region stress is directly proportional to
a) Viscosity b) strain rate c) strain d) Modulus
v) Name rubber(s) which is prepared by condensation polymerization
a) Butyl rubberb) Silicon rubber
c) Acrylic rubber (ACM)
d) Fluoroelastomer
vi) Indicate the firore that contains carbon Nitrogen linkage.
a) Jute b) Cotton c) Silk d) Polyester
vii) cellulose is a polymer
a) Natural b) Semi-synthetic c) Synthetic d) Artificial
viii) Aramids are high performance
a) Polyalkenes b) Polyehters c) Polyimides d) Polyamides
-
7/30/2019 objective questions without.doc
16/94
ix) SBR is a _______ copolymer of styrene and lutadine
a) Random b) Alternate c) Block d) Star shaped
x) Vulcanization is the processing step for rubbers
a) Initial b) Intermediate c) Final d) Penultimate
(1x10=10)
b) State whether the following statement are correct or wrong, correct the statement)
i) Dicumyl peroxide is a catisnic initiator False : Diamyl peroxide is radical initiator
ii) Among all the polymerization techniques emulsion polymerization is the most
useful method.
iii) GPC can be used to analyze all the molecular weights of polymer.
iv) Carthers Equation DP= 1/1 p CDP degree of polymerization, P = Extent of
reaction) is associated with anionic polymerization
V) The Mark Howwinx equation (n) = Km ~ (K and ~ are constant) is used to obtain
M2 (2 average molecular weight ) of a polymer.
vi) Cellulose nitrate is a good plastic.
vii) Back bone c-o-c linkage between repeat units renders a polymer more stiff.
viii) Incorporation of aromatic ring structure in repeat units renders a polymer more
rigid and stiff.
ix) Aromatic ring read rigidness and stiffness Natural rubber ceases to behave as
rubber below 800 c
x) Polystyrene assumes rubberly character at temprature > 1000 c
(1x10=10)
-
7/30/2019 objective questions without.doc
17/94
PAPER I POLYMER SCIENCE
YEAR 2005
1. Choose the correct answer from the given alternatives:
i. Hardening of plastics often involves cross-linking. This process is calleda) Curing b) Extrusion c) Compounding d) Plasticization
ii. Gutta percha is
a) Cis 1,4-polyisoprene b) Trans1,4-polyisoprene c) Vulcanised polyisoprene d) Ebonite
iii. The concentration of polymers in solution are often expressed as
a) g/dl b) Molarity c) Molality d) Volume %
iv. Which of the following is the initiator for suspension polymerization
a) Potassium persulphate b) Benzoyl peroxide c) AIBN d) Lewis acids
v. Which of the following is a branched chain polymer
a) HDPE b) Isotactic polypropylene c) LDPE d) Starch
vi. The value of in Mark-Houwink equation () = kM in theta solvent is
a) 1.0 b) 0 c) 0.5 d) 0.8
vii. Which of the following techniques yields a number average molecular weight
a) Viscometry b) Osmometry c) Light scattering d) Ultracentrifugation
viii. Shellac is a
a) Natural resin
b) Synthetic resin
c) Regenerated resin
d) Rubber
ix. Celluloid is
a) Unplasticised cellulose nitrate
b) Plasticised cellulose acetate
c) Plasticised ethyl cellulose
d) Plasticised cellulose nitrate
x. When the glass transition temperature (Tg) of a polymer is below the ambient temperature,
it is a
a) Plastic b) Fiber c) Rubber d) Dendrimer
-
7/30/2019 objective questions without.doc
18/94
xi. In the typical stress-strain curve, the stiffness is measured by calculating the
a) Total area under the curve till the point of rupture
b) Area within the Hookean region
c) Slope of straight portion within the Hookean region
d) Energy at break
xii. Polyethylene terephthalate is a
a) Polyamide
b) Polyimide
c) Polyether
d) Polyester
xiii. Mastication is the processing step for
a) Synthetic rubber
b) Natural rubber
c) Thermoplastic elastomer
d) Commodity plastics
xiv. EVA is
a) Homopolymer
b) Copolymer
c) Terpolymer
d) Non polymeric material
xv. Melamine-formaldehyde resin while in usable condition is
a) a thermoplastic
b) a thermosetting plastic
c) an engineering plastic
d) a pseudoplastic
(1x15=15)
-
7/30/2019 objective questions without.doc
19/94
(b) Write true or false and in case of false statements, correct it:
i. When more than two monomers are polymerized together, the process is called
copolymerization
ii. Cross-linked polymers do not form solutions and can undergo only limited swelling
iii. Emulsion polymerization produces polymers of the highest purity
iv. Atactic Polypropylene has the highest crystallinity of all the commercially available
polypropylene
Ans: Isotactic cyrstalline
v. SBS (Styrene butadiene- styrene) is an example of thermoplastic elastomer (T)
(1x5=5)
-
7/30/2019 objective questions without.doc
20/94
PAPER II RUBBER PROCESSING AND ENGINEERING
OBJECTIVE QUESTIONS
YEAR 1996
1. A) Mention only the right answers
i) The upside down mixing method is efficient and effective for those compounds
a) containing a large volume of liquid plasticizers and large particle size fillersb) containing low structure, small particle size carbon black
c) containing high loading of both soft mineral filler and oil together with an elastomer
of high Mooney viscosityd) none of the above
ii) While blending natural rubber with styrene butadiene rubber on a mixing milla) first natural rubber is to be masticated to a lower viscosity to form a band and then
SBR is addedb) natural rubber and SBR to be mixed simultaneously on the mill
c) SBR to be banded on the mill then NR addedd) None of the above
iii) A major disadvantage of mill mixing isa) it is time consuming and depends upon the skill of the operator
b) it is difficult to prevent rapid rise of stock temperature
c) it provides no shearing actiond) none of the above
iv) A common cause of poor dispersion and scorchiness in a mixer isa) sp gr. of the stock is too lowb) batch size too high
c) dump temperature too low
d) tensile strength of the stock too high
v) For better dispersion of filler on a mixing mill
a) Bank size should be very largeb) Bank size should be low
c) Bank size should be such that the material rolls constantly at the nip
d) None of the above
vi) Scorchiness of a rubber compound depends on
a) heat history of the compound on the process equipment
b) higher mastication timec) too much of plasticizer
d) none of the above
vii) A roller die consists ofa) a two roll calendar in combination with extruder feeding
-
7/30/2019 objective questions without.doc
21/94
b) a 3 roll vertical calendar in combination with a two roll calendar feeding
c) a 2 roll calendar in combination with open mill feeding
d) a 2 roll calendar in combination with internal mixer feeding
viii) The roll deflection in a calendar is mainly caused by
a) too much tension on the fabric being processedb) the excessive amount of feed material on the calendar
c) the force required in the nip to flatten the feed material
d) the high speed of taking away the calendared material
ix) Both side topping is usually done by a calendar with
b) 3-rolls
c) 2-rollsd) 4-rolls
e) none of the above
x) Frictioning on a calendar involvesa) coating a fabric with rubber stock at least 1/8 inch thick
b) depositing and coat of liquid cement on a fabric for better adhesionc) forcing the rubber into the interstices between fibers of a fabric through wiping with
roll pressure between the middle and bottom rolls
d) producing a surface design on sheet material
-
7/30/2019 objective questions without.doc
22/94
PAPER- II RUBBER PROCESSING AND ENGINEERING
YEAR 1997
1. A. Mention only the right answer/s:
i) Efficiency of Mastication is the lowest at around the temperature of
a) 500C b) 1100C c) 800C d) 2000C
ii) Dispersion of compounding ingredients can be improved by
a) Mixing at higher temperature
b) Mixing for longer period
c) Allow the compound to cool at least for a day and rework it again
d) None of the above
iii) Mixing in an internal mixer results in
a) Good quality of compound
b) Consistant quality of compound
c) Better dispersion than mixing in open mill
d) None of the above
iv) To achieve uniformity in color, the color has to be
a) Added at the beginning of the mixing cycle
b) Added at the middle of the mixing cycle
c) Added at the end of the mixing cycle
d) Partly added at the beginning and partly added at the end of the mixing
v) To get uniform (proper) blending of two polymers in a compound
a) the major polymer should have higher viscosity
b) the major polymer should have higher viscosity
c) the minor polymer should have lower viscosity
d) both the polymers should have viscosity nearest to each other
vi) To produce a thick rubber sheeting, it is preferable to use
a) a calender
b) an extruder
c) a combination of extruder and calender
d) an extruder with roller head
-
7/30/2019 objective questions without.doc
23/94
vii) Crows feet and Church mark are common processing problems associated with
a) the manufacture of tread compounds
b) the calendered sheets
c) the extruded profiles
d) mixing of compounds
viii) Continuous vulcanization of an extruded sponge profile can be done by
a) Rotocure
b) UHF cure
c) LCM cure
d) Fluidized bed cure
ix) Spreading operation is done
a) to achieve high thickness of coating
b) for long length coating on fabrics
c) for tyre cord coating
d) for short length fabric coatings
x) Injection moulding is preferable
a) to produce large volume of moulded articles
b) to vulcanize an extruded product
c) to produce small volume of big size rubber products
d) none of the above 1X10=
-
7/30/2019 objective questions without.doc
24/94
PAPER II- RUBBER PROCESSING AND ENGINEERING
YEAR 1998
1. Mention correct answers from the alternatives given against each question. More than one answer are
possible.
i) PVI (Cyclohexyl thiophthalimide) does not retard well when the acceleration system in the
compound is:
a) sulphenamide based
b) thiazoles based
c) thiuram based
d) both (b) & (c)ii) During winter seasons, compound surfaces on storage appear to be grey/white. This
phenomenon is called:
a) scorchb) high tack
c) crows feet
d) blooming
iii) Post cure inflation of tyres is not required for the following reinforcing materials:
a) Nylon-6
b) Rayonc) Polyester (high modulus low shrinkage)
Glass fiber
iv) Prewarming of polymer before using in compounds warranted, especially in cooler season forthe following:
a) Polybutadiene rubber
b) Butyl rubberc) Natural rubber
v) Screw Marks is a phenomenon associated with:
a) Calendaring operation
b) Vulcanization
c) Extrusion
vi) An Undercure/Laminated compound would result if following polymers get mixed:a) Natural rubber and chlorobutyl
b) Styrene butadiene rubber and IIR (Butyl)
c) Polybutadiene and Nitrile
vii) The most important criteria in selection of plasticizers are:
-
7/30/2019 objective questions without.doc
25/94
a) Elastomer compatibility
b) Viscosity and specific gravity
c) Odour and testd) None of the above
viii) From the point of view of ingredients, the following physical changes occur during a mixingcycle:
a) Entering, contacting, flowing and dumping
b) Incorporation, dispersion, distribution and plasticizationc) Contacting, squeezing and moving
d) None of the above
ix) Batch to batch variation in mixed compound is seldom caused by:a) Variation in initial loading temperature
b) Variation in flow and/or temperature of cooling water
c) Variation in Ram pressure
d) Variation in time and/or dump temperature
x) The length, to diameter ratio (L/D) of a cold feed extruder is:
a) 10:1 b) 15:1 c) 20:1 d) none of the above
xi) The amount of die swell in extrudate is dependent on:a) The Sp.Gr. of the compound
b) The T.S. and elongation of the compound
c) The shear rate of the extruder and the viscosity of the compound
d) None of the above
xii) When a 3-Roll calender is used for fractioning, the surface speed of the bottom roll isusually:a) Equal to middle roll
b) Slower than middle roll
c) Faster than middle rolld) None of the above
xiii) Shrinkage of cured products is not affected by:
a) Curing temperatureb) Amount and type of filler
c) Nature of mould materials and polymer
d) None of the abovexiv) With every 100C rise in vulcanization temperature, the vulcanization time will be reduced
by:
a) Half b) Doubled
c) Unaffected
d) None of the above
-
7/30/2019 objective questions without.doc
26/94
xv) Mastication is favoured by the presence of:
(give atleast two alternatives)
a) Oxygenb) Peptizers
c) Antioxidants
d) Sulphure) Electron withdrawing groups in the structure
f) Electron donating groups in the structure
xvi) Of the four widely used elastomers listed below, the only one with oil resistance property is:
a) SBR
b) NBR
c) CR d) EPDM
xvii) Vulcanizing agents are ingredients, which must be present in a compound to:
a) Reduce its viscosityb) Increase the speed of mixing
c) Cause chemical reaction resulting cross-linking elastomerd) None of the above
xviii) If the modulus of a compound is progressively increased, its elongation at break propertyhas a tendency to:
a) Increase
b) Decrease
c) Remain constant
xix) The maximum rebound height of a vulcanized compound is achieved when the polymer
used is:a) Polybutadiene
b) Butyl
c) Natural rubberd) Chloroprene
xx) In a pin extruder, the pins mounted in the barrel provide an effective way to:
a) Heat the stock inside the barrel
b) Improve homogenization of the stock in the barrelc) Increase head pressure
d) None of the above
20x1=20
-
7/30/2019 objective questions without.doc
27/94
PAPER- II RUBBER PROCESSING AND ENGINEERING
YEAR 1999
1. Mention correct answer from the alternatives given against each question. More than one
answers are possible. (20x1=20)
i) Because of its relatively poor processability, poly butadiene rubber is used primarily in blendswith other elastomers to improve
a) resistance to abrasion, cut growth, and flex cracking
b) resistance to oil and gasolinec) resistance to sunlight and ozone
d) none of above
ii) The properties and processability of a carbon black reinforced compound is greatly affected
bya) the specific gravity of the type of black it contains
b) the particle size and structure of the type of black it containsc) the cost of the carbon blacks used
d) none of above
iii) The maximum effect on masticating crude natural rubber for viscosity reduction is obtained
a) either at temperature, below 550C or at temperature above 1300C
b) at temperature between 90 and 1050Cc) only at temperature above 1300C
d) none of above
iv) The major disadvantage of mill mixing is
a) it is not only time-consuming, but also too dependent upon the skill of the operator
b) it is difficult to prevent rapid rise of stock temperature
c) it provides no shearing actiond) none of above
v) The major advantage of a screw extruder over a ram extruder is thata) it was invented earlier and its technology was perfect and well known
b) it is a continuous process instead of an intermittent process
c) it develops no frictional heat through the shearing action of the rotary screw
d) none of above
-
7/30/2019 objective questions without.doc
28/94
vi) The output rate of an extruder is not greatly affected by
a) the Mooney scorch and Mooney viscosity of the compound
b) the head pressurec) the resilience and tensile strength of the compound
d) the screw design
vii) In a two-roll mill operation the maximum pressure occurs at
a) point of bite
b) point of separation
c) nip point d) just before nip
viii) Reduction in the rate of flow of cooling water in an internal mixer will result ina) increase in the stock viscosity
b) decrease in the stock temperature
c) increase in the stock temperature
d) no change in the stock viscosity
ix) Increase in the rotor speed of an internal mixer will result in:a) increase in the temperature of cooling water
b) decrease in stock temperature
c) increase in the stock viscosityd) decrease in the shear rate
x) The deflection of calender rolls during processing is mainly caused by
a) too much tension on the fabric being processedb) the excessive amount of feed material on the calender
c) the force required in the nip to flatten the feed materiald) the high speed of taking a way the calendered material
xi) Off-gauge material processed by calendaring is not likely caused by
a) incorrect crowning of rollsb) improper use of roll-bending or roll-crossing devices
c) use of wrong rubber compound
d) excessive wear in roll journal bearings
xii) The cored roll cooling design for calender rolls is_____________ to the peripherally drilled
roll design
a) superiorb) inferior
c) equivalent
d) not at all related
xiii) Reversion behaviour can be visualized from testing in:
a) a high pressure capillary viscometer
b) universal tensile testing machine
-
7/30/2019 objective questions without.doc
29/94
c) Monsanto Rheometer
d) None of the above
xiv) The Mooney viscometer is the most effective in predicting behaviour of
a) RIM
b) Castingc) Injection molding
d) Compression molding
xv) Compared to transfer molding, compression molding has the advantage of
a) a wider tolerance for different rubber compositions
b) shorter molding cycles
c) better insert-to-rubber bondingd) ability to easily hold an insert in required position in mold cavity
xvi) Optimum cure time as calculated from a rheometer represents the time required to attain
a) 50% of the maximum torqueb) 70% of the maximum torque
c) 90% of the maximum torqued) none of the above
xvii) Rapid plastimeter is used to have an idea about:a) the flow behaviour
b) tensile strength
c) green strength
d) tack of raw rubber
xviii) L/D ratio of hot feed rubber extruder is in the range of:
a) 4 to 6b) 10 to 14
c) 15 to 18
d) 19 to 22
xix) In a horizontally placed single screw extruder the pitch of the screw is the:
a) horizontal distance between two flights
b) horizontal distance between three flightsc) vertical distance between flight and barrel
d) angular distance between two flights
xx) For preheating the rubber compound to produce bulky articles the preferred method of
heating is:
a) steam heatingb) electric heating
c) microwave heating
d) none of the above
-
7/30/2019 objective questions without.doc
30/94
PAPER- II RUBBER PROCESSING AND ENGINEERING
YEAR 2000
1. Mention the correct answer from the alternatives given against each questioni) Crows feet is a phenomenon associated with
a) calendaring operation
b) spreading operationc) extrusion
d) continuous vulcanization
ii) The material of the calender roll isa) carbon steel
b) alloy steel
c) chilled cast irond) stainless steel
iii) The deflection of calender rolls during processing is mainly caused bya) too much tension on the fabric being processed
b) the excessive amount of feed materialc) the force required in the nip to flatten the feed material
d) the high speed of taking away the calendaring material
iv) Microwave heating is effective for the followinga) non-polar rubber and curing agent
b) polar rubber and curing agent
c) rubber with metal insertsd) non-polar rubber with mineral fillers
v) Long cycle time is normally associated with the following molding method
a) transferb) injection
c) compression
d) RIM
vi) The viscosity of a fluid is the ratio of shear stress to shear rate. For most rubber the value ofis
a) greater than 1
b) less than 1
c) equal to 1d) none of these
vii) Calendar grain gives the rubber sheet which is
a) stronger across its lengthb) stronger along its length
c) having same strength at both directions
d) stronger at the diagonal directionviii) Generally in a hot feed extruder the L/D is
a) 10:1
b) 15:1
c) 5:1
-
7/30/2019 objective questions without.doc
31/94
d) none of the above
ix) Crows feet marks appear due toa) low processing temperature
b) high processing temperature
c) scorchyness of the compoundd) softness of the compound
x) Cast iron safety bushes are fixed at the roll journals of Two-roll mixing mills in order to
ensurea) safety of the operator
b) safety of the rolls
c) safety of the motor
d) none of the abovexi) For a thick moulded rubber product the curing should be done at
a) higher temperature with shorter time
b) higher temperature with longer time
c) lower temperature with shorter timed) lower temperature with longer time
xii) The content in the Liquid Curing Medium (LCM) continuous vulcanization process is aa) mixture of salts
b) mixture of salts with water
c) mixture of oilsd) mixture of salt and oil
xiii)The main objective to have a pin-barrel extruder is to
a) remove the porosity in the extrudate
b) reduce the scorch problem of the rubber compoundc) improve homogenization of rubber compound
d) reduce the die swell of the extrudate
xiv) Calendar machine having roll diameter of 20 inch, normally should have the roll length ofa) 40 inch
b) 54 inch
c) 64 inchd) 74 inch
xv) PCI (Post Cure Inflation) in manufacturing of nylon reinforced tyres is generally done by
circulating
a) hot waterb) hot air
c) steam
d) cold waterxvi) Both side frictioning of a fabric in one-pass is possible by using
a) a 4-roll type calender
b) a inverted L-type calenderc) a Z-type calender
d) two sets of 3 roll L-type calender
-
7/30/2019 objective questions without.doc
32/94
xvii) Mooney viscosity of a rubber compound is generally tested at
a) 800C
b) 1000Cc) 1500C
d) 500C
xviii) In mixing of Nitrile rubber compound, sulphur is added at the initial stage fora) increasing the scorch safety
b) improving the viscosity
c) better dispersiond) to improve oil resistance
xix) While moulding a rubber product in a hydraulic curing press bumping is required to
a) remove entrapped air
b) facilitate flow of compoundc) fill the mould cavity uniformly
d) reduce the curing time
xx) While mixing on a Two-roll mill, the problem of bagging is often experienced with
a) NR b) SBR
c) BR d) A blend of NR and SBR
(1X20=20)
-
7/30/2019 objective questions without.doc
33/94
PAPER- II RUBBER PROCESSING AND ENGINEERING
YEAR 2001
1. Give the correct answer from the alternatives given against each question
i) Torque is defined as a product ofa) Force and distance
b) Force and area
c) Pressure and distanced) Pressure and area
ii) The blends of polypropylene and EPDM area) Compatible
b) Incompatible
c) Mutually solubled) None of these
iii) S-B-S copolymers are
a) TPEb) TP
c) Rubbers
d) Thermosets
iv) The term Incorporation refers to
a) Bound rubberb) Wetting of the filler surface with rubber
c) Breaking down of the filler aggregates
d) None of these
v) For a highly shear sensitive rubber the filler dispersion in an internal mixer is
a) Very good
b) Goodc) Poor
d) None of these
vi) The flash or the mould spew occurs in different types of moulds in the order of
a) Injection moulds>Compression moulds
b) Injection moulds>Transfer moulds
c) Compression moulds>Injection mouldsd) None of these
vii) In an on-line vulcanization system the Shear head is fitted to a
a) Internal mixerb) Calender
c) Extruder
d) Transfer mould
-
7/30/2019 objective questions without.doc
34/94
viii) Salt bath vulcanizing method uses a mixture of molten potassium and sodium
a) Chloride
b) Sulfatesc) Bromides
d) Nitrates
ix) To measure the stock temperature inside a Banbury mixer, the device used is
a) A pyrometer
b) A mercury thermometerc) A thermocouple
d) A gas-thermometer
x) The rheo-curve of the SBR based rubber compound is ofa) Plateau type
b) Marching type
c) Reversion type
d) None of these
xi) Microwave heating is most effective for curing ofa) White rubber compounds
b) Textile reinforced rubber components
c) Black rubber compoundsd) Compounds made from non-polar rubbers
xii) Mould shrinkage increases with increase in
a) Rubber content of the compoundb) Filler content of the compound
c) Moulding pressure
d) None of the above
xiii) Calender grain effect is most pronounced when the compound is
a) Highly loaded with carbon blackb) Highly loaded with mineral fillers
c) Highly viscous in nature
d) Highly elastic in nature
xiv) Frictioning of both sides of textiles can be easily done in
a) A 4-roll calender of I type
b) A 4-roll calender of Z typec) A 4-roll calender of L type
d) Two nos. of 3-roll calendars of any configuration
xv) Variation in thickness of a calendered sheet between the centre and sides can be minimized
by
a) Increasing the compound viscosity
b) Decreasing the calendaring speed
-
7/30/2019 objective questions without.doc
35/94
c) Decreasing roll temperature
d) None of the above
xvi) Porosity cannot occur during vulcanization of an extrudate in curing chamber if cured in
a) Hot air without air pressure
b) Open steamc) Hot air without open steam
d) None of the above
xvii) A common cause of poor dispersion is
a) Specific gravity of the mix is too low
b) Dump temperature is too low
c) Batch size is too lowd) Ram pressure is too high
xviii) Die swell in extrusion is dependent upon
a) Specific gravity of compoundb) Specific heat of compound
c) Green strength of compoundd) Shear rate of the extrudate
xix) Generally in a mixing mill if the diameter is 22 inches then the roll length isa) 44 inches b) 60 inches c) 66 inches d) 22 inches
xx) When the material stops flowing through the extruder die even if the screw keeps rotating it
implies thata) Drag flow>Pressure flow
b) Drag flow
-
7/30/2019 objective questions without.doc
36/94
PAPER II RUBBER PROCESSING AND ENGINEERING
YEAR 2002
I. Give the correct answer from the alternatives given against each question
1. The modulus at 300% elongation as obtained from Universal Testing machine (UTM) refers to
a) Ratio of stress to strain at 300% elongation
b) Stress at 300% elongationc) Strain at 300% elongation
d) None of the above
2. The tensile strength of rubber vulcanizates as measured from an UTM refers to
a) Nominal stress at the point of failureb) True stress at the point of failure
c) Force required to break the sampled) None of the above
3. The unit of the viscosity obtained by Mooney Viscometer are equivalent to beinga) Dimensionless
b) Unit of torque
c) Unit of shear viscosityd) Unit of pressure
4. The dynamic characteristics of rubber matrix during vulcanization are measured by aa) Moving die rheometerb) Oscillating Disc rheometer
c) Universal Testing Machine
d) High pressure capillary viscometer
5. Mixing mill operated at smaller nip gap will exert in comparison to larger nip gap a
a) smaller shear forceb) higher shear force
c) identical shear force
d) none of the above
6. In the rubber processing terminology the terms like z-type, Inverse L-type are associated with
a) Mixing mills
b) Extrudersc) Compression mould
d) Calendars
7. As compared to Natural rubber Polybutadiene rubber has relativelya) Better processability
-
7/30/2019 objective questions without.doc
37/94
b) Identical processability
c) Poor processability
d) None of the above
8. The Rheometric curve of an SBR based rubber compound indicates predominantly
a) Fast Reversionb) Plateau Effect
c) Marching Modulus
d) None of the above
9. Reversion characteristics of a rubber compound can be easily visualized by testing the
compound in
a) a Monsanto Rheometerb) an Instron Tensile Tester
c) a DIN Abrader
d) a Dispergrader
10. The output rate of a given compound in an extruder can be significantly improved by
a) increased cooling water pressureb) increased barrel and head temperatures
c) increased screw R P M
d) reduced screw R P M
11. In an internal mixer, higher rotor speed provides
a) shorter mixing cycles
b) higher cooling water temperaturec) lower stock temperature build up
d) higher batch weights
12. Post cure inflation is essential for tires built with
a) Rayon cords
b) Nylon-6 cordsc) Steel cords
d) Cotton
13. Heat setting of nylon cords should be carried out at
a) Room temperatureb) Below room temperature
c) Temperature higher than the melting point of nylon
d) Temperature nearer to the melting point of nylon
14. L/D ratio of a pin barrel extruder isa) 4:1 to 6:1
b) 10:1 to 15:1c) 12:1 to 20:1
d) 10:1 to 40:1
-
7/30/2019 objective questions without.doc
38/94
15. Crows feet is a phenomenon associated with
a) Calendering operationb) Spreading operation
c) Extrusion
d) Continuous vulcanization
16. Microwave heating is effective for the following
a) Non polar rubber and ingredients
b) Polar rubber and ingredientsc) Rubber with metal inserts
d) Rubber with mineral filler
17. Long cycle time is normally associated with the following molding
a) Transfer
b) Injection
c) Compressiond) RIM
18. Improved resistance of reversion in case of NR is obtained by
a) Urethane cross-linking system
b) Semi efficient vulcanizationc) Soluble EV system
d) None of the above
19. In a calendaring operation maximum pressure occur on the roll at a height h equal toa) height of nip
b) half the height of nipc) 4/3 the height of nipd) the height of nip
20. The following rubber is not subjected to cracking by ozonea) SBR
b) BR
c) NBR
d) EPDM(20X1=20)
-
7/30/2019 objective questions without.doc
39/94
PAPER II RUBBER PROCESSING AND ENGINEERING
YEAR 2003
1. Give the correct answers from the alternatives given against each question
i) The viscosity of raw synthetic polyisoprene rubber as compared to raw natural rubber is
a) lower b) 1.5 times, higher c) equal d) 2 times, higher
ii) Excessive remilling of SBR compound may lead to
a) softening b) gelling c) high tac d) none of the above
iii) The ASTM series number for cold SBR gum rubber is
a) 1000 b) 1700 c) 1500 d) 2000
iv) Polybutadiene rubber containing 32-35% cis forms a tight elastic band on a two roll mill at
roll temperature range ofa) 200C-300C b) 400C-450C c) 1200C-1300C d) 650C-700C
v) Butyl rubber is generally compounded at higher temperature than NR due to its relatively
a) low level of unsaturationb) high unsaturation
c) low Mooney viscosity
d) none of the above
vi) Die swell is associated with
a) calendaring b) extrusion c) mixing d) spreading
vii) Optimum cure time is generally denoted as
a) Tc25 b) Tc50 c) Tc90 d) Tc98
viii) SI unit of viscosity of polymer is
a) Nm b) N/m2 c) PaS d) MPa
ix) In a rubber extruder a screen pack is used toa) Remove undesirable particles of higher size from rubber mix
b) Remove excess of plasticizer
c) Remove excess curatives
d) Protect the breaker platesx) Mastication is a process of
a) Curing rubber in sunlightb) Lowering of Mooney viscosity by adding process oil
c) Lowering of Mooney viscosity by mechanical shearing
d) Devulcanization of rubber compound
xi) The Rotor design of the Mooney Viscometer is of the type
-
7/30/2019 objective questions without.doc
40/94
a) A disk with smooth surface
b) A disk having serrated grid pattern
c) A disk having perforationd) A bi-conical disk
xii) The rapid rise in the temperature of the stock when the rubber is fed to the internal mixer isdue to
a) Circulation of water through the body of the mixer
b) Viscous dissipation of energy due to high stock viscosityc) Breakdown of the molecular chains
d) Disentanglement of rubber molecules
xiii) In an internal mixer the purpose of the rotor shaft seal isa) To prevent the escape of particulate material
b) To prevent the escape of cooling water
c) To maintain the temperature inside the mixer
d) None of the above
xiv) Blooming is a phenomenon wherea) Processability of a rubber compound is affected
b) Proper distribution of compounding ingredients are hampered
c) Blisters appear on the surface of the compoundd) Compounding ingredients move from bulk to the surface of a rubber compound
xv) An increase in Extruder Screw RPM will lead to
a) Decrease in output rateb) Increase in output rate
c) No change in output rate
d) None of the above
xvi) On a calender sheet the blisters appear due to
a) The calender roll temperature being too lowb) Feed stock temperature being too low
c) Calender rolls and/or feed stock being too hot
d) None of the above
xvii) During the moulding of a rubber component bumping and breathing operations are
performed to
a) Eliminate the trapped air and vapours from the mouldingb) Improve the surface finish
c) Reduce the thickness
d) None of the above
xviii) In an injection moulding system the sprew is the flow channel
a) Between runner and gate
b) Between runner and die
-
7/30/2019 objective questions without.doc
41/94
c) Between gate and mould cavity
d) Before the die
xix) For a flashless moulding of rubber articles the most suited moulding operation is
a) Compression moulding
b) Injection mouldingc) Blow moulding
d) None of the above
xx) Shear head is the device used for
a) Raising the temperature of the rubber compound
b) Mixing fillers with rubbers
c) Controlling the pressured) None of the above
(1x20)
-
7/30/2019 objective questions without.doc
42/94
PAPER II- RUBBER PROCESSING AND ENGINEERING
YEAR 2004
1. Give the most correct answer from the alternatives given against each questioni) The scorching tendency of a rubber compound is not
a) dependent upon its base elastomer
b) dependent upon curative systemc) dependent upon processing temperature
d) dependent upon its color
ii) Nitrile rubber is modified by PVC resins to improvea) oil resistance
b) tear strength
c) resistance to weather, ozone, and sunlightd) adhesion to fabric and metals
iii) The maximum effect on masticating crude NR for viscosity reduction is obtaineda) either at temperature below 550C or at temperature above 1300C
b) at temperature between 900C and 1500C
c) only at temperature above 1300C
d) none of above
iv) A common and often overlooked cause of poor dispersion and scorchiness is
a) Specific gravity of the stock too low
b) Batch size too largec) Dump temperature too low
d) Tensile strength of the stock too high
v) The amount of die swell in extrusion is dependent upon
a) the shear rate of the extruder and the viscosity of the compoundb) the specific gravity of the compound
c) the tensile strength and elongation of the compound
d) none of the above
vi) Surface roughness of the extrudate is not likely to be caused by
a) air entrapment or insufficient masticationb) improper temperature profilec) insufficient cooling at take away equipment
d) high screw speed
-
7/30/2019 objective questions without.doc
43/94
vii) The major causes of porosity problems are
a) use of high viscosity material and application of mold releaseb) moisture and trapped air
c) low molding temperature and along curing cycle
d) none of the above
viii) Sulfur is the most widely used vulcanizing agent. The second most popular vulcanizing
agent isa) Organic amines
b) Organic peroxides
c) Phenolic resins
d) Metallic oxides
ix) The major disadvantage of heated nitrogen over heated air as a source of thermal energy for
vulcanization is
a) it cannot be easily compressedb) it has no oxidizing effect on sensitive polymer composite being vulcanized
c) it is much more efficient in heat transferd) none of above
x) Molded good with irregular shape and complex configuration are most likely made bya) compression molding
b) transfer molding or injection molding
c) bladder molding
d) none of the above
xi) The Mooney viscometer gives the viscosity in equivalent units as
a) Forceb) Torque
c) Momentum
d) Acceleration
xii) The rotors of Mooney viscometer are designated as L and S, which stand respectively for
a) low and slow
b) long and shortc) large and small
d) none of the above
xiii) For a particular rubber compound the optimum cure time obtained using a moving die
rheometer as compared to oscillating disc rheometer is
a) sameb) lower
c) higher
d) none of the above
xiv) Increase in friction ratio of the two roll mill operation will
-
7/30/2019 objective questions without.doc
44/94
a) increase the temperature of stock
b) decrease the temperature of stock
c) increase the stock viscosityd) none of the above
xv) The friction ratio of a Banbury internal mixer is the consequence ofa) Tip diameters of the rotor wings
b) Root diameters of the rotors
c) Root diameter of one rotor and wing tip diameter of the otherd) None of the above
xvi) Cold feed extruder L/D ratio is higher than the hot feed extruder because it contains
a) Additional feeding arrangementb) High capacity drive motor
c) Additional preheating zone
d) None of the above
xvii) An extruder die invariably contains
a) Lead-in and land sectionsb) Melting section
c) Conveying section
d) Metering section
xviii) In an injection molding system the gate diameter is
a) Smaller than the runner diameter
b) Larger than the runner diameterc) Equal to the runner diameter
d) None of the above
xix) In a pin barrel extruder the pins are used to impart
a) A smooth flow
b) A cross flowc) High viscosity
d) None of the above
xx) The crows feet defect is observed normally in aa) A calendered sheet
b) An extrudate
c) A moulded productd) None of the above
(20x1=20)
-
7/30/2019 objective questions without.doc
45/94
PAPER II RUBBER PROCESSING AND ENGINEERING
YEAR 2005
1. a) Choose the correct answer from the given alternatives given against each question
i) A high value of die swell indicates
a) low viscosity b) high viscosity c) low elasticity d) high elasticity
ii) The fill factor in an internal mixer during curative mixing is
a) 50-55 b) 60-65 c) 70-75 d) 80-85
iii) In autoclave curing of rubber compounds an uncured surface layer is observed in the case of
a) sulfur curing b) peroxide curing c) metal oxide curing d) resin curing
iv) The advantage of a ram extruder over a screw extruder is
a) low heat development b) low operating cost c) metal oxide d) all of a,b & c
v) The Mooney viscometer measures the viscosity at a shear rate of.. s-1
a) 0-1 b) 1-2 c) 2-3 d) 3-4
vi) In a four roll calender the second and third rolls which apply coating to the fabric must be
of. speed, while the first and fourth rolls can be ..
a) even, even or uneven b) uneven, even c) uneven, even or uneven d) 1.0 and 1.25
vii) For friction coating in a three-roll calender the friction ratio is between
a) 1 and 1.5 b) 1.5 and 2.0 c) 1.25 and 1.5 d) 1.0 and 1.25viii) ML1+8 is related to
a) NR b) SBR c) IIR d) NBR
ix) Crows feet can be observed after
a) Extrusion b) Moulding c) calendaring d) Mixing on a two roll mill
x) Reversion is often shown by
a) NR b) SBR c) IIR d) NBR
xi) Typical mill friction ratio is
a) 1:1 b) 1.25:1 c) 2.5:1 d) 5:1
-
7/30/2019 objective questions without.doc
46/94
xii) In hot feed extruders, L/D ratio is
a) 2:1 b) 6:1 c) 15:1 d) 20:1
xiii) Eutectic mixture of inorganic salts is used as vulcanization medium for
a) Hot air cure b) LCM cure c) Radiation cure d) Fluidized bed cure
xiv) Bag-O-matic press is used for curing a
a) Seal b) Mount c) Cable d) Tyre
xv) Die swell is related to
a) Injection moulding b) Calendering c) Extrusion d) Mixing
xvi) Cure rate is generally obtained from a
a) Plastimeter b) Mooney viscometer c) Rheometer d) Processability tester
xvii) Typical operating roll temperature of highly loaded EPDM is
a) 10-200C b) 20-300C c) 30-500C d) 60-800C
xviii) Peroxide curing of rubber at 1600C shows rheometric rheological properties of a rubber
compound after the scorch time because
a) Marching modulus b) High scorch safety c) Reversion tendency d) Flat curing
xix) Mooney viscometer cannot be used for measuring Rheological properties of a rubber
compound after the scorch time because
a) test temperature is low
b) test shear is low
c) the rotors tear the cured rubber
d) temperature uniformity cannot be maintained
xx) Porosity in fluidized bed curing is avoided by
a) use of dessicant b) application of pressure c) use of dried filler d) all of a, b& c
(1x20=20)
-
7/30/2019 objective questions without.doc
47/94
PAPER - III- RUBBER MATERIALS
YEAR 1996
A) Select suitable curing system for following rubbers. Only write the answer against the
question number.i) NBR-EPDM blend requiring good compression set and heat resistant properties - EV
ii) Natural rubber for better heat resistant application Sulphur donor
iii) Neoprene W for general purpose application Ethylene thiourea
iv) NR-BIIR blend for tyre application S/Znov) Butyl rubber for maximum heat resistant application - Resilience
5x1=5
B) What is the effect of:
i) Increasing acrylonitrile content on heat resistance of NBR - Increases
ii) Increasing styrene content in SBR on rubbery characteristic - Decreasesiii) Introducing halogen group in IIR on compatibility with diene rubbers - Improves
iv) Increasing vinyl content in BR on the skid resistance Improves
v) Increasing butadiene content on oil resistance of NBR - Decreases
5x1=5C) Select suitable rubber/rubber blends for following applications:
Outer cover and inner tube of oil field hose
i) Aerotyre and cycle tyre NR/BR/RRii) Tread and inner liner for tubeless truck tyre NR/BR HIIR/NR
iii) Lining material for sulfuric acid tank - NR
iv) Artificial heart valve SILICONE5x1=5
D) What are the effects of increasing HAF black loading (upto 80 phr) on the following
properties of optimum cured NR based compound (Give only typical curve)?
i) Tensile strengthii) Elongation at break
iii) Rebound resilience
iv) Hardness
Hardness
T.S
E.BResilience
20 40 60 80
5x1=5
-
7/30/2019 objective questions without.doc
48/94
PAPER- III RUBBER MATERIALS
YEAR 1997
1.AWhy is Polybutadiene blended with other polymers, while butyl rubber is nearly used alone? ANS: Cure compatibility
i) What is understood by the term Plateau Effect in Cure Curves?
Tg plateau
Tm
ii) Place the following rubbers in order of increasing resistance to ozone attack: Natural
rubber, butyl rubber, acrylonitrile butadiene rubber and EPDM rubber. ANS:NR
-
7/30/2019 objective questions without.doc
49/94
C.
i) Why is DCBS more delayed action accelerator than CBS? ans: DCHA less than CHA
ii) Name one difunctional compound for curin rubber Quinane dioxin
iii) Name two ultra accelerators ZDC, TMTD
iv) Which of the following are accelerator activators: Zinc oxide , red lead, acetic acid,stearic acid , phenol
v) Which of the following are chemical plasticizers: Oil soluble sulfonic acid, pine tar,
pitch, xylyl mercaptan
D. What is the effect of?
i) Increasing nitrile content on the rubbery characteristics of nitrite rubber - Decreases
ii) Increasing trans content of polyisoprene on the processibility at room temperature -
Lowers
iii) Replacing natural rubber by butyl rubber on rolling loss of tyre tread compound -Increases
iv) Blending NBR with EPDM on heat resistance - Improves
v) Replacing sulfur donor compound by sulfur Heat resistance inferior
-
7/30/2019 objective questions without.doc
50/94
PAPER- III RUBBER MATERIALS
YEAR 1998
1. A. Write only the answer against the question number:
i) Zinc oxide is the cross linking agent for which rubber - CRii) Name at least three elastomers which can be cross linked by dicumyl peroxide EPDM,
HNBR, Siliconeiii) Which type of resin is used for vulcanizing butyl rubber? Ans: Modified PF
iv) Why is stearic acid used in diene rubbers? Ans: Activator
v) What is the dosage of sulphur required for curing SBR to ebonite stage? Ans: 305X1=5
B. Which type of oils or plasticizers are used.
i. For manufacturing oil-extended styrene butadiene rubbers - Aromaticii. For manufacturing oil-extended EPDM rubbers - Paraffinic
iii. As plasticizer for polychloroprene rubber Ester plasticizeriv. As softener for isobutylene isoprene rubber - Napthanicv. For imparting fire retardant properties chlorinated paraffin
5X1=5
C. Name one important application for each of the following polymer blends
i) NBR/PVC LPG tubing
ii) NR/BR Tyre headiii) IIR/EPDM Inner tube
iv) NR/BIIR (bromobutyl) Inner liner
v) NR/HSR (high styrene resin rubber masterbatch) shoe soles
5X1=5
D. Select the most appropriate filler for each of the following applications
i) White sport shoe sole precipitated silicaii) Passenger car tyre tread - ISAF
iii) Battery boxes made of ebonite (hard rubber) Ebonite part
iv) Green colored garden hose of EPDM china clayv) Hot water bottle Precipitated CaCO3
5X1=5
-
7/30/2019 objective questions without.doc
51/94
PAPER- III RUBBER MATERIALS
YEAR 1999
1. A. Write only the symbol of the correct answer/answers
i) Which rubber has the widest temperature range of application
a) NR b) EPDM c) Butyl (IIR) d) Silicone e) Polybutadiene (BR)ii) Select the most suitable elastomer for aerotyre
a) BR b) NR c) IIR d) EPDM e) SBRiii) Among the following rubbers the best heat resistant one is
a) SBR b) EVA c) EPDM d) NBR e) IIRiv) The best example of self-reinforcing elastomer is.
a) EPDM b) BR c) NBR d) SBR e) NRv) The Paraffinic oil is suitable plasticizer for
a) NBR b) SBR c) CR d) EPDM e) Siliconvi) Increasing acrylonitrile content the property which decreases is
a) heat resistance
b) oil resistance
c) resilience
d) air impermeability
e) modulusvii) Peroxide curing is not suitable for
a) IIR b) NBR c) BR d) SBR e) NRviii) Among the following the most delayed action accelerator is
a) MBT b) CBS d) TMTD d) ZDC e) ZMBTix) Among the following fillers the average particle size is the least for
a) Activated CaCO3 b) SAF c) ZnO d) HAF e) Fumed silica
x) Zinc salt of pentachlorothiophenol is used as
a) Curing agent b) Plasticizer c) Filler d) Peptizer e) Tackifier
-
7/30/2019 objective questions without.doc
52/94
B. Write only the answer against the question number:
ii) Which is the main monomer for butyl rubber?- ans: Isobutylene
iii) Name the feedstock for furnace blacks CBFS/Naptha
iv) Name the tree, which produces natural rubber Hevea brasiliensis
v) Which type of catalyst is used for manufacturing Polybutadiene rubber? Ans: No
vi) Name an oxygen containing elastomer - Silicone
C. Select a suitable polymer or polymer blend for
i) LPG tubing NBR/PVC
ii) Metereological balloon - CR
iii) Solvent based contact adhesives - CR
iv) Inner layer of steam hose - NBR
v) Tyre curing bag - IIR
10+5+5=20
-
7/30/2019 objective questions without.doc
53/94
PAPER- III RUBBER MATERIALS
YEAR 2000
1. Choose the correct answer (write the letter code in your answer):
i) Which property of Nitrile rubber is improved when it is modified with PVC resin?a) Oil resistance
b) Resistance to weather, ozone and sunlight
c) Tear strengthd) Adhesion to fabric and metals
ii) Fluorocarbon elastomers have excellent resistance to oils, fuels, acids and chemicals but haspoor resistance to
a) Hydraulic fluids
b) Oxygen, ozone, sunlight
c) Oxygenated solvents such as acetone, MEK
d) None of the above
iii) Which copolymer of ethylene and vinyl acetate exhibits rubbery behavioura) Copolymer with 12% vinyl acetate
b) Copolymer with 28% vinyl acetate
c) Copolymer with 45% vinyl acetated) Copolymer with 90% vinyl acetate
iv) What is the weight percent of chlorine in PVC?a) 15% b) 30% c) 45% d) 56%
v) Arrange in order of decreasing abrasion resistance of the following rubbersNR
-
7/30/2019 objective questions without.doc
54/94
a) EPDM
b) NR
c) PUd) BR
xi) Calcium oxide is used in EPDM microwave curing fora) Fast extrusion
b) Better shine on finished product
c) Absorbing moistured) Uniform dispersion of reinforcing materials
xii) Paraffin mineral oil is the most compatible with
a) Butyl rubberb) Silicone rubber
c) Natural rubber
d) Nitrile rubber
e) Polyacrylic rubber
xiii) Aniline point of a oil is 300C, if it is highlya) Paraffinic
b) Aromatic
c) Napthenicd) Linear molecules
e) Dark in color
xiv) Resin curing is the most suitable fora) NBR b) BR c) NR d) IIR
xv) Neither peroxide nor conventional sulfur curing system is recommended for
a) NR b) SBR c) CR d) BR
xvi) Increasing ethylene content in EPDM reducesa) Tensile strength
b) Compression set resistance
c) Ozone resistance
d) Filler loading capacityxvii) During reclaiming of a rubber vulcanizate unsaturation and molecular weight variations are
as follows
a) unsaturation of rubber increases, but molecular weight decreasesb) unsaturation of rubber reduces as well as molecular weight reduces
c) unsaturation increases and molecular weight increases
d) both remain sane as that of original compound
xviii) Sulfur, chlorine, oxygen containing rubber is
a) CR b) CIIR c) CSP d) CM
-
7/30/2019 objective questions without.doc
55/94
xix) The most suitable polymer for tyre curing bag is
a) IIR b) NBR c) SBR d) NR
xx) The most delayed action accelerator is
a) MBT b) MBTS c) TMTD d) MOZ
(1X20=20)
-
7/30/2019 objective questions without.doc
56/94
PAPER-III RUBBER MATERIALS
YEAR 2001
1. (a) Choose the correct answers from the following
i) What is the basis of grading of ISNR as ISNR 3, 5, 10, 20, 50 etc.?
a) Viscosity
b) Dirt contentc) Ash content
d) Nitrogen content
ii) At 23.5% bound system level, the Tg of SBR isa) 400C b) 500C c) 600C d) 700C
iii) A 100% hydrogenated NBR can be vulcanized bya) Sulfur and accelerator
b) Peroxides
c) Metal oxidesd) None of these
iv) Polychloroprene rubber is vulcanized by
a) ZnO b) ZnO and MgO c) S and Accelerator d) None of these
v) The Cis-content in Polychloroprene rubber of adhesive grade is
a) 70% b) 80% c) 85% d) 90%
vi) The significant characteristic of a thermoplastic elastomer is to
a) Behave like a thermoplastic at room temperatureb) Process like a thermoplastic at elevated temperature
c) Behaves like an elastomer at room temperature
d) Process like a rubber at room temperature
vii) Many specialty elastomers require Post curing for achieving best balance of properties.
Name from the listed below the one, which does not require post curing.
a) Acrylic b) Fluorocarbon c) Cross linked Polyethylene d) Vamac
viii) Name the rubber which has better air impermeability than butyl rubber
a) Acrylic b) Hypalon c) ENR d) Polyepichlorophydrin
ix) Fluorosilicone rubber has outstanding properties of
a) Good swelling resistance and low temperature flexibility
b) Long temperature heat resistance at elevated temperaturesc) Resistance to acids and bases
d) Good tear and wear properties
-
7/30/2019 objective questions without.doc
57/94
x) In latex processing the chemical used as gelling agent is
a) Ammonia b) ZnO c) Sodium silicofluoride d) Resorcinol
(1x10=10)
(b) Mention the function of the following compounding ingredients in rubber
1 Dioctyl phthalate - Plasticizer
2 Zinc salt of mercapto benzothiazole - Accelerator
3 Precipitated silica Reinforcing filler4 Dicumyl peroxide cross-linking agent
5 Triallyl isocyanurate peroxide activator
(5)(c) Select the most suitable filler for
1 Inner tube of tyres - FEF
2 EPDM steam hose - SRF3 Insulation compound for power cables - Talc
4 LPG tubing Precipitated CaCo35 Passenger tire tread OESBR/SBR
(5)
-
7/30/2019 objective questions without.doc
58/94
PAPER III RUBBER MATERIALS
YEAR 2002
1. (A) Choose the correct answer:
i) Polyurethane rubber has outstanding resistance to
a) acids and solvents b) hot water c) abrasion and tear d) none of the above
ii) Nitrile rubber modified with PVC resin improves its
a) oil resistance b) tear strength c) resistance to weather, ozone and sunlight d) adhesion to
fabric and metals
iii) Acrylic rubber has inferior resistance to
a) ozone and sunlight b) oxidation c) water and steam d) gasoline and similar hydrocarbon
solvents
iv) Fluorocarbon elastomer has very little resistance to
a) hydraulic fluids b) oxygen, ozone and sunlight c) oxygenated solvents such as MEK d) none
of the above
v) The mercaptan modified neoprene rubber (type W) has better
a) resistance to oil and gasoline b) more tackiness and faster cure c) superior resistance to heat
and compression d) none of the above
1x5=5(B) What these notations stand for and accordingly name the following types of black fillers
i) N 110 - SAF ii) N 242 - HSisAF iii) N 440 - iv) N 339 - HSHAF v) N 990 - SRF1x5=5
(C) Select most suitable rubber for the following applicationsi) Truck tyre tread - NR
ii) Weather strip - EPDM
iii) LPG tubing NBR/PVCiv) Air bag for tyre curing - IIR
v) Seals operating at 600C in hydrocarbon oil - NBR
1x5=5(D) Select the most suitable fillers (with grades) for the following applications:
i) Passenger radial tyre tread N326
ii) Green tyre tread (low rolling resistance environmentally friendly tyre tread) precipitated silica
iii) Acid resistance tank liner BaSo4iv) White sidewall for tyres CaCo3v) Automotive tube - FEF
1x5=5
-
7/30/2019 objective questions without.doc
59/94
PAPER III RUBBER MATERIALS
YEAR 2003
I. i) Which of the following rubber has maximum gas impermeabilitya) NR b) Butyl c) Polyethers d) EPDMii) The properties of Hypalon are similar to Neoprene. However, it is superior to Neoprene in:
a) Resilience
b) Resistance to acid, solvents, ozone and oxidationc) Resistance to compression set
d) None of the above
iii) Phynol formaldehyde resin can be used toa) Reduce hardness
b) Improve flex properties
c) Reduce heat built up or
d) Increase hardnessiv) Which of the following rubber can be used to get lowest resilinece
a) IIR b) BR c) FKM d) Siliconev) MST of latex should preferably bea) 5 secs. b) 600 secs c) 1000 secs d) 5000 secs
(1X5=5)
II. Name the type of accelerators and vulcanizing agents used in curing the following rubber
products
i) Butyl curing bags PF resin
ii) Disposable hand gloves made from NR latex ultra fast ZDBCiii) Aero tyre tread - Sulfenamulsiv) Cable jacket based on Neoprene rubber - Pbo
v) Truck tyre carcass - NBRS
vi) RTV silicone for automobile gasket DCP+TIAC
vii) Printing rolls from epichlorohydrin rubber Ethylene thiourea / Pb3O4viii) Cable sheathing compounds from Hypalon Pb3 O4+Terone A
ix) Crank shaft seals from Acrylate rubber - Diamines
x) Aircraft and rocket seals from fluorocarbon rubber Bisphenol/Metal oxide(1x10=10)
III. Give two examples of each of the following
i) Antioxidants 6PPD, TDCP
ii) Process aids Zinc salt of fatty acid
iii) Retarders CTP, NDPAiv) Extenders Whiting, Clay
v) Blowing agents ADC, TSH
(1x5=5)
-
7/30/2019 objective questions without.doc
60/94
PAPER III RUBBER MATERIALS
YEAR 2004
1. Choose the correct answer / write the letter code in your answer:
i) Select a cure system for the best flex life of the cured producta) Conventional b) Semi-EV c) EV d) Peroxide
ii) Amongst the following rubbers, which rubber can take maximum filler and oil loading
a) EPDM b) NR c) PU d) SBR
iii) Resin curing is the most suitable fora) NBR b) SBR c) NR d) IIR
iv) The most suitable polymer for tyre curing bag isa) IIR b) NBR c) SBR d) NR
v) A 100% hydrogenated NBR can be vulcanized by
a) Sulfur and accelerator b) Peroxides c) Metal oxides d) None of these
vi) In latex processing the chemical used as gelling agent is
a) Ammonia b) ZnO c) Sodium silicofluoride d) Resorcinol
vii) Lowest heat build up is observed for vulcanizate of
a) CR b) NR c) SBR d) IIR
viii) The highest air impermeability is shown by
a) NR b) CR c) NBR (50 ACN) d) IIR
ix) The best flame resistant rubber is
a) CIIR b) BIIR c) NBR d) CR
x) Arrange in increasing order of gum vulcanizate strength
SBR
-
7/30/2019 objective questions without.doc
61/94
xv) Which elastomer has highest fluorine content?
a) Fluorocarbon rubbers (FKM) b) Fluorosilicone rubbers (FVMQ)c) Polytetra fuluroethylene (PTFE)
xvi) The most compatible plasticizer for EPDM rubber isa) Aromatic mineral oil b) Paraffinic mineral oil c) DOP d) Caster oil
xvii) High voltage power cables are insulated witha) Butyl rubber b) Silicone rubber c) EPDM d) XLPE
xviii) Which of the following is a thermoplastic rubber?
a) SBR b) SBS c) ABS d) SAN
xix) Which of these polymers has the lowest Tg?
a) BR b) CR c) SBR d) NBR
xx) Field latex has the (rubber hydrocarbon content) of about
a) 25% b) 35% c) 50% d) 60%
(20x1=20)
-
7/30/2019 objective questions without.doc
62/94
PAPER III RUBBER MATERIALS
YEAR 2005
1. Select most suitable answer/answers from the given choices against each question
i) Only solution grade of-------------is exclusively used for tyre tread
a) IIR b) CR c) NBR d) BR e) SBR
ii) Peroxide curing is not technically recommended for---------
a) BIIR b) IIR c) CR d) NBR e) HNBR
iii) The best combination of heat and mineral oil resistance can be obtained from
a) CR b) NBR c) BIIR d) HNBR e) MQ
iv) The most suitable rubber for Aero tyre is-----------
a) HNBR b) BR c) SBR d) NR e) ENR
v) The rubber which has the highest abrasion resistance--------
a) SBR b) XNBR c) CR d) NBR e) BR
vi) For tyre curing bag the most suitable rubber is------------
a) CR b) NBR c) BIIR d) CIIR e) IIR
vii) The best combination of mechanical properties, oil resistance and flame resistance can be
obtained from -----------------
a) CR b) BIIR c) CIIR d) NBR e) VMQ
viii) The highest resilience is shown by the rubber----------
a) SBR b) IIR c) BR d) HNBR
ix) The rubber which requires production at lowest polymerization temperature
a) IR b) NBR c) CR d) SBR e) IIR
x) The most important property of oil seals and gasket
a) Tensile strength
b) Compression setc) Heat build up
d) Resilience
e) Modulus at 300% elongation
-
7/30/2019 objective questions without.doc
63/94
xi) Carbon black with higher surface area is
a) N550 b) N330 c) N110 d) N234
xii) Accelerator having highest scorch safety in conventional rubber compound
a) NOBS b) MBT c) DCBS d) CBS
xiii) Additive used for enhancing static ozone resistance properties of general purpose rubber
compound is
a) TMQ b) 6PPD c) Wax d) Aromatic oil
xiv) The most unsuitable filler for improving acid resistance properties of rubber compound is
a) Whiting b) Barytes c) Carbon black d) Clay
xv) The maximum limit of dirt content of TSR 10 is
a) 0.1% b) 0.2% c) 0.5% d) 0.01%
xvi) The material derived from petroleum source is
a) NR b) Silica c) Vegetables oil d) BR
xvii) The Recycle material used in rubber industry
a) WTR (Whole Tyre Reclaim) b) Sheet Rubber c) N330 d) ZnO
xviii) High pH of carbon black results in rheometric curve of rubber compound
a) increase in cure rate b) decrease in cure rate c) cure rate remain unchanged d) maximum
torque increases
xix) DRC of commercial NR latex isa) 40% b) 60% c) 30% d) 80%
xx) Preservative used for NR latex is
a) HCOOH b) Water c) Ammonia d) 6PPD
(20x1=20)
-
7/30/2019 objective questions without.doc
64/94
PAPER 4 RUBBER PRODUCT MANUFACTURING AND THEIR
EVALUATIONYEAR 1996
1. a) Select suitable answer from the given set:(Only write the answer for each question in the answer script not in the question paper)
i) Cycle tyre cord is mainly derived from..
a) Cottonb) nylon
c) rayon
d) polyester
ii) Tyre sidewalls are made thin because.a) For better heat dissipation
b) No abrasion is needed in side wallc) For better economy
d) None of these
iii) The most important property requirement for rubber compound in metal to rubber bonding is
a) tear resistance
b) elongation at breakc) tensile strength
d) heat build up
e) modulus
iv) Incorporation of .. improves metal-rubber bond strength
a) clay
b) plasticizerc) carbon black
d) dicumyl peroxide
v) Heat treatment is necessary for cord prior to be used in rubber product
a) rayon
b) carbon fiber
c) steeld) nylon
vi) For acid resistant tank lining the most suitable rubber is .a) Natural rubber
b) SBR
c) Nitriled) Hypalon
-
7/30/2019 objective questions without.doc
65/94
vii) For stabilization of latex the usual material is
a) NaCl, b) H2SO4, c) NH3 , d) CaCO3
viii) Dry bonding agent used for fabric-rubber adhesion is based on.
a) Chemlok
b) Hexa+resorcinol+silica
c) Desmodur
d) None of these
ix) Air craft tyre is based on ..
a) NR SBR blend
b) NR BR blend
c) Pure NR
d) SBR BR blend
x) The most widely used black for oil seal application is
a) HAF
b) SRF
c) ISAF
d) FEF
1x10=10
-
7/30/2019 objective questions without.doc
66/94
B)i) Bursting strength of braided hose is given by the following formula
a) 3N8RSin/DL
b) 0.2NSRSin/DL
c) 0.2N3RSin/D
d) 0.2N3RCos/DL, where each term has its usual meaning
Ans: 2NRSin/DL
ii) The breaking load of conveyor belt is equal to
a) Sum of tensile strength of top and bottom cover compound + sum of strengths of top
and bottom plies
b) Strength of individual ply x number of plies
c) Sum of strength of top and bottom rubber cover
d) None of these
iii) The usual formula for calculation of tensile strength of rubber compound is.
a) Breaking load/cross sectional area at the time of breaking
b) Breaking load/thickness of the sample
c) Breaking load/original cross sectional area of the sample
d) Load at 300% elongation/original cross sectional area
iv) Neutral angle in braided hose is
a) 450 b) 390 c) 600 d) 540
v) The width/height ratio in classical and wedge type V-belt are respectively
a) 1.6, 1.0; b) 2.6,1.6; c) 1.6,1.2; d) 1.2, 2.1
vi) Bias angle in bias ply and radial tyres are
a) 540, 900 b) 650, 450 c) 900, 450 d) 300, 900
-
7/30/2019 objective questions without.doc
67/94
vii) If the volume of the mould is V, then the volume of initial compound used for preparation of
micro cellular rubber should be roughly
a) 1.7V b) V c) 0.7V d) none of these
viii) For preparation of flexible high voltage cable for 15KV power line the suitable polymer willbe
a) Nitrile rubber b) Butyl rubber c) XLPE d) EPR/EPDM e) PVC
ix) The included angle in classical V-belt is
a) 600 b) 450 c) 400d) 540
x) Drum friction test is relevant to..
a) Tyre b) V-belt c) Hose d) Conveyor belt e) Shoe
1x10=10
-
7/30/2019 objective questions without.doc
68/94
PAPER- IV- RUBBER PRODUCTS MANUFACTURING AND THEIR
EVALUATION
YEAR 1997
1. From these multiple choice of answers select the most appropriate answer of the followings:
i) Best curing system for metal-rubber bonding should be based on:
2 Semi EV
3 EV
4 Conventional
5 Peroxide
ii) The most suitable cord material for V-belt reinforcement is:
2 Nylon
3 Polyester
4 Rayon
5 Cotton
iii) The tear strength is usually calculated for Crescent tear test using the formula:
2 Tearing load/thickness of the sample
3 Tearing load/original cross-sectional area of the sample
4 Tearing load/width of the sample
5 Tearing load/final cross-sectional area of the sample
iv) Hollography is the test to evaluate
2 Shoe
3 V-belt
4 Tyre
5 Hose
-
7/30/2019 objective questions without.doc
69/94
v) Peroxide vulcanization is not recommended for:
2 EPDM
3 Silicone
4 Butyl
5 Hypalon
vi) For coagulation of NR-latex the following material is used commercially
2 Sulfuric acid
3 Calcium nitrite
4 Acetic acid
5 Calcium carbonate
vii) Pressure sensitive adhesive can be derived from:
2 SBR
3 NBR
4 CR
5 Silicone rubber
viii) Thick rubber article should be cured for:
2 Longer time at elevated temperature
3 Shorter time at elevated temperature
4 Shorter time at lower temperature
5 Longer time at lower temperature
ix) LPG (domestic gas) tubing should be made from:
2 SBR
3 EPDM
4 Butyl
5 Polychloroprene rubber
-
7/30/2019 objective questions without.doc
70/94
x) The reason of porosity in tyre tread is mainly due to:
2 Improper polymer blends
3 Non-use of desiccant
4 Low boiling plasticizer
5 High dose of sulphur
xi)_ Ebonite bonding with metal is not suitable for high temperature application because:
2 It corrodes metal at high temperature
3 It gets aged for faster oxidation
4 Ebonite layer softens
5 Ebonite gets brittle
xii) For non-intercommunicating cell structure of a sponge the right-choice of blowing agent
should be
2 (NH4)3CO3
3 NaHCO3
4 Dinitroso pentamethylene tetramine (DNPT)
5 Hot air
xiii) In a braided hose, if the braid angle is less than the natural angle, the hose will
2 Increase in diameter
3 Increase in length
4 Elongate in the direction 450 to the hoop force
5 No change during service
xiv) If a latex foam collapse after vulcanization, necessary steps should be:
1 to reduce the gelling time
2 to increase gelling time
3 to increase foaming time
4 to increase vulcanization time
-
7/30/2019 objective questions without.doc
71/94
xv) Belt angle of a vulcanized radial tyre is:
1) 120-180 2) 850-900 3) 260-280 4)300-350
xvi) Hardness of ebonite is measured in the durometer scale of
2 Shore A
3 Shore B
4 Shore C
5 Shore D
xvii) For testing flex resistance of sole