1.- Properties of materials
Part II
Grau Superior de Disseny en Fabricaci
MecnicaM08 Materials (MATFA)UF1 Propietats dels materials
Professor: Llus Claps i Badia
-
8/8/2019 M8.UF1.2 Properties of Materials 2
2/29
UF Index
1.1. Preliminary knowledgePreliminary knowledge2.2. Physical and chemical propertiesPhysical and chemical properties
3.3. Mechanical propertiesMechanical properties
1.1. Quick summaryQuick summary2.2. Understanding stress and strainUnderstanding stress and strain
3.3. The tensile testThe tensile test
4.4. PropertiesProperties
4.4. Manufacturing propertiesManufacturing properties
5.5. Other: cost, environmental, non tangibleOther: cost, environmental, non tangible
6.6. Material selection processMaterial selection process
-
8/8/2019 M8.UF1.2 Properties of Materials 2
3/29
3.1 Quick summary
Mechanical properties:Mechanical properties: Strength
tensile1.Yield strength (Re)2.Ultimate strength (Rm)
compressive strength flexural strength torsional, shear
Stiffness - Elasticity (E) Elongation (ductility) (A) Hardness (H) Resilience & toughness (KV) DBTT Fatigue limit Creep
Fracture toughness (Kic)
...
Tests:Tests: Tensile test Compressive test Beaming or flexural test Shear test, bending test, torsional, .
Hardness test Rockwell Brinell Vickers Shore, knoop
Impact test Charpy (V-notch test) Izod
Fatigue test
Creep test ...
-
8/8/2019 M8.UF1.2 Properties of Materials 2
4/29
3.2 Understanding
stress and strain
Types of mechanical load (when external forcesare applied to pieces):
TENSILE
(i.e. a cable)
TORSION(i.e. a screw driver)SHEAR(i.e. a pin or a key)
BENDING OR FLEXURAL
(i.e. a beam)
COMPRESSIVE
(i.e. a column)
-
8/8/2019 M8.UF1.2 Properties of Materials 2
5/29
3.2 Understanding
stress and strain
Suppose a mechanicalcomponent
Load this componentapplying a 20.000 N (2tones) external force aspicture shows.
In this case, thecomponent is mainlysubjected to a tensile load(also bending and shearload exist).
2 tones
18 12
-
8/8/2019 M8.UF1.2 Properties of Materials 2
6/29
3.2 Understanding
stress and strain
MPamm
N
mmmm
N
A
F
93216
000.20
1812
000.20
2===
=
WHAT WILL HAPPEN?:
Each particle of material issubjected to STRESS (tensi).
Engineering units are MPa
(N/mm). In the past Kg/mm (). 10 MPa ~ 1 Kg/mm
Knowing the loads, engineerscan calculate the stress:
-
8/8/2019 M8.UF1.2 Properties of Materials 2
7/29
3.2 Understanding
stress and strain
WHAT WILL HAPPEN?:
The load deform the piece.Strain is the measure of thedeformation.
As much stress, as muchstrain.
The strain can be:
ELASTIC: if material returns toto the original form when theload disapears.
PLASTIC: if strain remainswhen the load disapears.
VISCOELASTIC,VISCOPLSTIC: when a lot oftime is needed for strainhappens.
-
8/8/2019 M8.UF1.2 Properties of Materials 2
8/29
3.2 Understanding
stress and strain
Elasticdeformation
Plasticdeformation
-
8/8/2019 M8.UF1.2 Properties of Materials 2
9/29
3.3 The tensile test
The most fundamental mechanicaltest you can perform on a material
A standard specimen is stretchedslowly and progressively until itbreaks.
Load (force) and strain ismeasured and recordedcontinuously during the test.
Its a destructive test
The specimen is only subjected totensile load.
Standards: UNE-EN 10.002-1(metals at ambient T), UNE-EN-ISO 527(plastics), ...
SPECIMEN
-
8/8/2019 M8.UF1.2 Properties of Materials 2
10/29
3.3 The tensile test
Test will be done in a specialhydraulic machine (tensile oruniversal testing machine).
Force is measured with a load cell.
Strain is measured with aextensometer gauge. Usually will beenough measuring the strain whenspecimen is already broken.
Virtual test:http://www.engsc.ac.uk/an/mini_projects/tensile/tensile_laboratory.html
http://www.engsc.ac.uk/an/mini_projects/tensile/tensile_laboratory.htmlhttp://www.engsc.ac.uk/an/mini_projects/tensile/tensile_laboratory.html -
8/8/2019 M8.UF1.2 Properties of Materials 2
11/29
3.3 The tensile test
1. The machine has recorded, a great number ofdates:
FLOAD FORCE (N) lDEFORMATION (mm)
1. With calculation, we must change load to stressand deformation to strain.
1. And finally, draw a graphics thaty (vertical): STRESS (MPa)x (horiz.): ,A STRAIN (-, %)
100
0
0
=
=
=
Al
l
A
F
A0is the section of the specimen
l0 is the measuring lenght of the specimen.
-
8/8/2019 M8.UF1.2 Properties of Materials 2
12/29
3.3 The tensile test
(MPa)
(%)
Breaking point
PLASTIC ZONE
ELASTIC
ZONEA strain
Re yield strength
Rm tensile strength
Corba real
Striction zone
Stress-strain curve
E Young modulus
0,2%
-
8/8/2019 M8.UF1.2 Properties of Materials 2
13/29
3.4 Mechanical propertiesTensile strength, yield strength
RRmm TENSILE STRENGTH TENSILE STRENGTH ororUTSUTS (MPa)(MPa) (Resistncia a tracci)The highest stress in the stress-strain curve
RRee YIELD STRENTH YIELD STRENTH (MPa)(MPa) (Lmit elstic)The stress applied to a material at which plastic deformation starts to occur
Sometime is called proof stress Rp0,2 when offset method is used The most important property in structural materials. In brittle materials Rm = Re
Steel for cables
Re=Rm= 1.800 MPaStructural steel
Re = 275 MPa
Rm = 420 MPa
Nanotubes of carbon
Re=Rm~ 50.000 MPaCarbon fibres
Re=Rm~ 3.500 MPa
-
8/8/2019 M8.UF1.2 Properties of Materials 2
14/29
STEEL
3.4 Mechanical propertiesYoung modulus
E YOUNGS MODULUS or ELASTIC MODULUSE YOUNGS MODULUS or ELASTIC MODULUS (MPa)(MPa)
It shows if a material is elastic or stiff.
The value of E is the slope of the stress-strain curve in the elastic zone.Its also the stress necessary to double the length of the specimen
stretching in elastic zone.
1.100.000 MPaRUBBER
+
-
DIAMOND
10 MPa
210.000 MPa
PP
1.500 MPa
-
8/8/2019 M8.UF1.2 Properties of Materials 2
15/29
3. Propietats mecniques
3.6 Allargament
When this happened, the willow said to itself, I wish Iwas as strong as the Oak, instead of bending overwith every breeze then one day a large windstormwhipped through the field.
When the storm passed, and the darkness lifted, the
willow looked across the field, and was shocked todiscover that the oak was laying on the ground,broken. When the Gardener came into the field, thewillow said, Oh sir, what happened to the Oak? Howis it that I survived the storm, weak as I am, and theOak fell?
The Gardener said, Oh little willow-tree, do you not
understand what happened? When the winds blow,you bend with them, while the oak remains still. Sowhen a really powerful wind comes along, you canbend with the wind, and survive it. But the Oak cannotbend, and so if the wind is strong enough, it will break.For the Oak had a secret, a weakness within that noone looking at the outside could see. And the
Gardener went on his way, leaving the willow toponder what he said.
Moral: Strength within and strength without are not thesame, and one should cultivate strength within first.Also, when the winds of life blow, bend, and you maysurvive the real storms when they come. Try andresist them, and when the real storms come, you may
break instead.
In a field, there was an oak at one end, and awillow-tree at the other.
Whenever a wind moved through the field, thewillow swayed in the wind, while the oak remainedunmoved.
-
8/8/2019 M8.UF1.2 Properties of Materials 2
16/29
3.4 Mechanical propertiesStrain
A STRAINA STRAIN (%)(%) (allargament)The ratio of the elongation to the original length (usually in %).
It shows if a material is ductile or brittle. Ductile materials can be shaped bydeformation processes.
-
8/8/2019 M8.UF1.2 Properties of Materials 2
17/29
3.4 Mechanical propertiesCompressive strength, bending s.
In addition to the tensile test /tensile strength, there are othertests. Each type of load we saw(compressive, bending, torsionand shear) has its own test.
COMPRESSIVE TEST: speciallyused in ceramic materials forconstruction.
FLEXURAL TEST: We uses it forbrittle materials (we cant test itsby tensile test). With the flexuraltest results, its possible tocalculate the tensile strength.
-
8/8/2019 M8.UF1.2 Properties of Materials 2
18/29
3.4 Mechanical propertiesToughness, resilience
RESILIENCE & KV - TOUGHNESSRESILIENCE & KV - TOUGHNESS (J/m(J/m)) (tenacitat)They show the capacity of a material to withstand impacts.RESILIENCE is the maximum amount ofenergy per area unit with only elasticdeformation. TOUGHNESS is the amount of energy per area unit necessary to break thematerial.Theoretically they are the area under the stress-strain curve (only the elastic zone inresilience and all the graphic in toughness case).
In practice, toughness is tested mainly with Charpy impact test (UNE 7475) or with Izodimpact test (less usual).
E
RRU
e
ee
2
2
12
==
-
8/8/2019 M8.UF1.2 Properties of Materials 2
19/29
3.4 Mechanical propertiesToughness and temperature
DBTT (Ductile BrittleDBTT (Ductile BrittleTransition Temperature)Transition Temperature)
Many of the ductile materials(metals and plastics) turns tobrittle at low temperatures.
We can know the transitiontemperature testing a set ofspecimens at differenttemperatures with a Charpyimpact test.
-
8/8/2019 M8.UF1.2 Properties of Materials 2
20/29
3.4 Mechanical propertiesHardness
H - HARDNESSH - HARDNESS (duresa)The resistance of a material to be penetrated or scratched.
The value depends of the type of test. Most usually tests and scalesare:
-HB, HBW (Brinell,
UNE-EN-ISO 6506-1)- HV (Vickers, UNE-EN-ISO 6507-1)
- HR_(Rockwell, UNE-EN-ISO 6508-1)
- HS_(Shore)
- HK (Knopp, microhardness)
Advantages of hardness test:1. Usually is a non-destructive test (although little traces rest in
material)
2. Testing machines are cheap and we can perform the tests veryquickly.
3. Tensile strength can be approached from hardness value.
-
8/8/2019 M8.UF1.2 Properties of Materials 2
21/29
3.4 Mechanical propertiesHardness
HARDNESS TESTS
Hardnesstester
BRINELL TEST(HB): Uses a carbide ball as penetrator.Shape is measured with a microscope..
VICKERS TEST(HV): Uses a diamond pyramidal penetrator.The shape is measured with a microscope. The most
universal hardness test (metals, ceramics, ).ROCKWELL TEST: Uses a steel or carbide ball (HRB) odiamond cone (HRC). The device measures the distancepenetrated. More quick and cheap than others.
SHORE TEST: It measures the bounce of a diamond-tipped
hammer. Applied mainly to rubber and plastic materials. Thedevice is known as scleroscope.
KNOOP TEST (HK): Microhardness, it can measure thinplates or coatings. Similar to Vickers.
FILE PENETRATION: Its a workshop quick test. If filepenetrates or not, material is more or less to 60 HRC
-
8/8/2019 M8.UF1.2 Properties of Materials 2
22/29
3.4 Mechanical propertiesHardness
CONVERSION
TABLESF
OR
STEELS
Quenche
d,tempered
Nottempered
-
8/8/2019 M8.UF1.2 Properties of Materials 2
23/29
3.4 Mechanical propertiesFatigue resistance
FATIGUE LIFEFATIGUE LIFE (N)andand FATIGUE STRESS LIMITFATIGUE STRESS LIMIT (MPa)Fatigue is a failure of a material due to cyclic loading. The maximum stress of every cycle isless than the yield strength of the material.Fatigue is a stochastic process. Dates are given for a specified probability.Fatigue stress limit is the stress value necessary to fatigue damage occurs with a specifiednumber of cycles.Fatigue life is the number of stress cycles (of a specified character) that a specimen sustains
before failure occurs.Material performance against fatigue are commonly characterized by an S-N curve.
-
8/8/2019 M8.UF1.2 Properties of Materials 2
24/29
3.4 Mechanical propertiesFatigue resistance
Example of fatigue collapsed shaft:
2) Lamelar tearing(beaches)
3) Final
fracture
1) Start point ornucleation
DAMAGE
COLLAPSE
-
8/8/2019 M8.UF1.2 Properties of Materials 2
25/29
3.4 Mechanical propertiesFatigue resistance
The Norwegian rigAlexander Kiellandcollapse at the North Sea in1980.Of the 212 people aboard,123 died.A fatigue failure of a steelbracing was the cause of thedisaster. Fissure starts at apoor profile of a hydrophonefillet weld.
-
8/8/2019 M8.UF1.2 Properties of Materials 2
26/29
3.4 Mechanical propertiesCreep
CREEPCREEP ((termoflunciatermofluncia)) Creep is a slow deformation of materials subjected to constant charges for long time,
even if stress is less than yield strength.
Creep depends on temperature. It occurs up to 30% of melting point in metals andup to 40-50% of melting point in ceramics.
Creep is evaluated with tests (1000 to 10.000 hours). The result of tests are drew ina graphic.
Larson-Miller graphic (stress-time-temperature)Strain versus time
-
8/8/2019 M8.UF1.2 Properties of Materials 2
27/29
3.4 Mechanical propertiesCreep
Jet turbine and steam turbine blades caneasily have a creep failure. They arecontinuously subjected to centrifugal forceand high temperatures.
The movement of ice in a glacier flow is anexample of creep.
Creep occur in many plastics at room
temperature. Results of this are notorious indaily objects: The wardrobe shelves (wood + plastic glues)
always increase deformation with time
Plastic cable ties (Unex) always come loosewith time
-
8/8/2019 M8.UF1.2 Properties of Materials 2
28/29
3.4 Mechanical propertiesToughness to fracture
KKITIT FRACTURE TOUGHNESSFRACTURE TOUGHNESS
Describes the ability of a material containing a crack, to resist the growing of thisfracture, avoiding a catastrophic failure in brittle fracture mode.
All the materials contain micro-fissures. There are a effect ofstress concentration inthis points.
Ceramics and very hardened metals, arent good structural materials in tensile loadbecause they present brittle fracture.
Ductile fracture:
Deformation + breakingBrittle fracture:
Only breaking
-
8/8/2019 M8.UF1.2 Properties of Materials 2
29/29
3.4 Mechanical propertiesToughness to fracture
1944, Portland.
Suddenly, the USS T-2Schenectady , cracked in half.
When the accident happened,the ship were in port, in calmweather, and not charged. Thewater was cold.
It was de first accident of nearly800, involving the Liberty,Victory and Tanker T-2 shipclasses.
The cause of the failure was notunderstood at the time. Really,low-grade steel of hull became
brittle in low-temperature.Since then, naval engineershave to consider the brittlefracture in hull structuralmaterials and their welds.