Lesson 25 IACS Repair Quality Standard for Existing ShipsPart II
![Page 2: Lesson 25 IACS Repair Quality Standard for Existing Ships Part II](https://reader033.vdocuments.mx/reader033/viewer/2022061516/56649e635503460f94b5f262/html5/thumbnails/2.jpg)
CONTENTS
1. Welding requirement
2. Repair quality standard
3. Doublers on plating
4. Renewal of internals/stiffeners
5. Renewal of internals/stiffeners -
transitions inverted angle/bulb profile
![Page 3: Lesson 25 IACS Repair Quality Standard for Existing Ships Part II](https://reader033.vdocuments.mx/reader033/viewer/2022061516/56649e635503460f94b5f262/html5/thumbnails/3.jpg)
1. Welding Requirement
A. Correlation of welding consumables with
hull structural steels
B. General requirements to preheating and
drying out
C. Dry welding on hull plating below the
waterline of vessels afloat
![Page 4: Lesson 25 IACS Repair Quality Standard for Existing Ships Part II](https://reader033.vdocuments.mx/reader033/viewer/2022061516/56649e635503460f94b5f262/html5/thumbnails/4.jpg)
Repair quality standardItem Standard Limit Remarks
Material Grade Same as original or higher See Section 4
Welding Consumables IACS UR-W17 (ref. 6) Approval according. to equivalent international standard
Groove / roughness See note and Fig. 22.1 d < Grind smooth
Pre-Heating See Table 22.1 Steel temperature not lower than
Welding with water on the outside See Section 5.3 Acceptable for normal and high strength steels
Moisture to be removed by a heating torch
Alignment As for new construction
Weld finish IACS guide for inspection of ship hull welds (ref. 10)
NDE IACS guide (ref. 10) At random with extent to be agreed with attending surveyors
NOTE: Slag, grease, loose mill scale, rust and paint, other than primer, to be removed.
![Page 5: Lesson 25 IACS Repair Quality Standard for Existing Ships Part II](https://reader033.vdocuments.mx/reader033/viewer/2022061516/56649e635503460f94b5f262/html5/thumbnails/5.jpg)
Doublers on plating
![Page 6: Lesson 25 IACS Repair Quality Standard for Existing Ships Part II](https://reader033.vdocuments.mx/reader033/viewer/2022061516/56649e635503460f94b5f262/html5/thumbnails/6.jpg)
Doublers on plating
![Page 7: Lesson 25 IACS Repair Quality Standard for Existing Ships Part II](https://reader033.vdocuments.mx/reader033/viewer/2022061516/56649e635503460f94b5f262/html5/thumbnails/7.jpg)
Renewal of internals/stiffeners
![Page 8: Lesson 25 IACS Repair Quality Standard for Existing Ships Part II](https://reader033.vdocuments.mx/reader033/viewer/2022061516/56649e635503460f94b5f262/html5/thumbnails/8.jpg)
Item Standard Limit Remarks
Size insert Min. Min.
Material grade Same as original or higher See Section 4.
Edge Preparation As for new construction. Fillet weld stiffener web/plate to be released over min. d =
Welding sequence See fig.22.4 . Weld sequence is 1→ 2 → 3
Alignment As for new construction
Weld finish IACS guide for inspection of ship hull welds (ref. 10)
NDE IACS guide (ref. 10)
![Page 9: Lesson 25 IACS Repair Quality Standard for Existing Ships Part II](https://reader033.vdocuments.mx/reader033/viewer/2022061516/56649e635503460f94b5f262/html5/thumbnails/9.jpg)
Renewal of internals/stiffeners - transitions inverted angle/bulb profile
![Page 10: Lesson 25 IACS Repair Quality Standard for Existing Ships Part II](https://reader033.vdocuments.mx/reader033/viewer/2022061516/56649e635503460f94b5f262/html5/thumbnails/10.jpg)
Termination of straps
![Page 11: Lesson 25 IACS Repair Quality Standard for Existing Ships Part II](https://reader033.vdocuments.mx/reader033/viewer/2022061516/56649e635503460f94b5f262/html5/thumbnails/11.jpg)
WORDS Ambient adj. 周围环境 Submerge v. 浸没 hydrogen n. 氢 alignment n. 找中、队中 compliance n. 符合 Insert n. 嵌补板 Pitch n. 波高 circumferencial adj. 圆周的 throat n. 焊喉 Internals n. (pl)内部构件 Transition n. 过渡 Taper v. 逐渐变细 /薄 Strap n. 带钢 Asymmetrical adj. 不对称的
![Page 12: Lesson 25 IACS Repair Quality Standard for Existing Ships Part II](https://reader033.vdocuments.mx/reader033/viewer/2022061516/56649e635503460f94b5f262/html5/thumbnails/12.jpg)
Phrases and Expressions ambient temperature 环境温度 submerged arc welding 埋弧焊 coated low-hydrogen electrode 碱氢焊条 manual metal arc welding 手工电弧焊 grind smooth 研磨平整 weld finish 焊缝处理 as for new construction 如同新结构(建造)
at random 随机(选择) rounded off corner 倒圆角 edge preparation (焊接 )接边加工 slot welding 槽焊 (长孔焊 ) step welding 分段焊接 fillet weld 角焊
![Page 13: Lesson 25 IACS Repair Quality Standard for Existing Ships Part II](https://reader033.vdocuments.mx/reader033/viewer/2022061516/56649e635503460f94b5f262/html5/thumbnails/13.jpg)
Assignment
1. Review the text.
2. Do the exercises on Page 249.