EAGLE CHEMICALS is the leading producer of resins in Africa and Middle-East. Our state-of-the-art car coatings center underpins EAGLE CHEMICALS as the superior supplier of resins for automo-tive re�nish, especially solvent based resins.
We are ensuring high quality raw materials, excellent technical formulations and stringent Q.C. protocol.
EAGLE CHEMICALS fully computerized production lines, assistance of international chemical expertises and highly equipped labs helped us to exceed our customer expectations.
As our customers are our “success partner”, we provide the know-how and technology to modify resins upon our custom-ers’ request to facilitate the optimall use of our products.
EAGLE CHEMICALS o�ers starting guide formulas for each appli-cation based on recommended resins and followed by its technical results and conclusion.
Our resins technology
1‐ Resins for unsaturated polyester putty.2‐ Resins for primer �ller.3‐ Resins for base coat.4‐ Resins for clear coat.5‐ Resins for solid colour.
1
2
Car Coatings
Primer Filler
AC-EAGLE(OH66-20BA50)60%
AC-EAGLE(OH66-28X60)60%
AC-EAGLE(OH60-20X55)55%
SDA-EAGLE(SFX27-25/60)60%
Putty Filler
USP-EAGLE(BF3.7/65)
USP-EAGLE(BF4/68)
Metallic Base Coat
AC‐EAGLE(TS‐10XB50)50%
Clear Coat and Solid Color
AC-EAGLE(OH138-40BA65)65%
AC-EAGLE(OH132-20X50)50%
AC-EAGLE(OH138-40M65)65%
AC-EAGLE(OH148-27M60)60%
AC-EAGLE(OH100-40BA70)70%
AC-EAGLE(OH90-30X60)60%
AC-EAGLE(OH138-30M60)60%
AC-EAGLE(OH100-18BA60)60%
AC-EAGLE(OH138-90BA70)70%
AC-EAGLE(OH148-95BA70)70%
1. Resins for Putty Filler
1.1 Rigid Unsaturated Polyester :
Styrene
Xylene
20
25
Dispersing agent
Rigid USP
Thickener
Rheology modi�er
Coarse particle size
Rheology modi�er
Remarks
Fine particle size
Fine particle size200Talcum powder
TiO2
Luvothix R‐RC
18
Raw Materials Weight by %
USP‐EAGLE(BF‐3.7/65)65% 300
BYK‐W969 6
Aerosil ‐200 5
Benton paste 34 20
6
Talcum powder 200
CaCO3 200
Guide formula 1.1Body �ller based on hard unsaturated polyester
Recommended Resins
USP-EAGLE(BF-3.7/65)
0
5
10
15
20
25
30
35
1-Hr 2-Hr 3-Hr 4-Hr
Hardness of body �ller based on hard unsaturated polyester
AdhesionThe adhesion after one day on metal panel (120µm wet) at 25°C by cross cut tester is 5B (Excellent)
SandabilityThe sandability after 1/2 Hr on metal panel (120µm wet) at 25°Cby abrasive AA ‐120 (Excellent)
chart 1.1
Hour
Hardness
3
1. Resins for Putty Filler
1.2 Flexible Unsaturated Polyester :
Dispersing agent
Flexible USP
Thickener
Rheology modi�er
Coarse particle size
Coarse particle size
Hollow glass microsphere
Remarks
200Talcum powder
Glass bubbles K1
Styrene
18
Raw Materials Weight by %
USP-EAGLE(BF-4/68)68% 300
BYK-W980 6
Aerosil -200 5
Thixin R 20
6
CaCO3 200
TiO2 200
Guide formula 1.2Body �ller based on �exible unsaturated polyester
Recommended Resins
USP-EAGLE(BF-4/68)
Hardness of body �ller based on �exible unsaturated polyester
chart 1.2
AdhesionThe adhesion after one day on metal panel (120µm wet) at 25°C by cross cut tester is 5B (Excellent)
SandabilityThe sandability after 1/2 Hr on metal panel (120µm wet) at 25˚Cby abrasive AA -120 (Good)
9
9.5
10
10.5
11
11.5
12
12.5
1-Hr 2-Hr 3-Hr 4-Hr
4
Hour
Hardness
1. Resins for Putty Filler
5
USP-EAGLE (BF-4/68)
USP-EAGLE (BF-3.7/65)
68%
65%
8 max.
8 max.
3-6 min
5-8 min
11-15 min
14-18 min
110 ± 10 0C
170 ± 10 0C
••••
•••••
•••••
•••••
••
•••••
•••••
••
•••••
•••••
••••
•••••
Application Product
Properties
Performance
Flexible body �ller
Semi rigid body �ller
Amine accelerated USP with excellent �exibility
and very good sandability by machine.
Amine accelerated USP with excellent hardness
and excellent sandability.
Styrene Monomer
Styrene Monomer
Solid%
Type ofSolvent
ColourG ardner Gel Time Cure TIme Peak
exothermic 0C Flexabilit
y
Hardness
Sandability
Adhesion
Filling
Properti
esFast
curin
g time
••••• Exce llent •••• Very Good ••• Good •• Fair • Poor N/A Not Applied
2. Resins for Primer Filler
Hardness of primer �ller basedon hydroxy resins
chart 2.1
Guide formula 2.1Primer �ller 2K based on hydroxy acrylic or alkyd resins
Dispersing agent
Rheology modi�er
Fine particle size
35µ particle size
Coarse particle size
Hardener
CaCO3 100
Talcum powder
Hardener Solution
Butyl Acetate 49.15
Xylene 24.57
Thinner
Butyl Acetate : Xylene 2 : 1
100
Mix well
Desmodur L75 73.72
Xylene
BYK110
Bentone paste 34
TiO2
2
10
180
Raw Materials Weight by grams
Hydroxy resin 60% (OH 2%) 250
Remarks
CaCO3 180
158
Butyl Acetate 20
Recommended Resins
AC-EAGLE(OH66-20BA50)60%
AC-EAGLE(OH66-28X60)60%
AC-EAGLE(OH60-20X55)55%
SDA-EAGLE(SFX27-25/60)60%
Har
dnes
s
1020304050607080
After 1 Day
After 3 Days
After 1 Week
6
2. Resins for Primer Filler
0
1
2
3
4
5
6
Adhesion 1-week
0
20
40
60
80
100
120
Impact 1-week
chart 2.2
chart 2.3
Adhesion of primer �ller based on hydroxy resins
Impact of primer �ller based on hydroxy resins
7
Adhesion
Impact
2. Resins for Primer Filler
Properties
8
Properties
AC‐EAGLE(OH66‐28X60)
AC‐EAGLE(OH66‐20BA50)
AC‐EAGLE(OH60‐20X55)
SDA‐EAGLE(SFX27‐25/60)
2%
2%
1.8%
1.3% 60% Z‐Z23 max byGardner
60 %
60 %
55 %
X-Z
X-Z
Y-Z
≤ 50 Hazen
≤ 50 Hazen
≤ 50 Hazen
•••••
•••••
•••••
•••••
•••••
•••••
••••
••••
••••
••••
••••
••••
•••••
•••••
•••••
•••• •••••••••• ••••••••
Application Product Performance
Economical primer �ller & car repair
High chemical resistance primer �ller & car repair
Economical primer �ller & car repair
Low cost primer �ller
Excellent adhesion, mechanical properties and
very good drying time
Compatible with CAB,excellent adhesion &
excellent resins for primer �ller
Excellent adhesion, mechanical properties and
very good drying time
Excellent adhesion, very good mechanical properties
and drying time
Xylene
Butyl acetate
Xylene
Xylene
OH % Solid %Type ofSolvent
Visc. Colour Hardness Flexibility Impact Adhesion Curing time
Hydroxy acrylic resin
Short oil alkyd resin
••••• Exce llent •••• Very Good ••• Good •• Fair • Poor N/A Not Applied
3. Resins for Metallic Base Coat
Recommended Resins
AC‐EAGLE(TS‐10XB50)50%
Melamine formaldehyde resin
Wax dispersion
100
230
Raw Materials RemarksWeight by %
Butyl Acetate : Xylene
AC-EAGLE(TS-10XB50)50% 95
Butyl Acetate 100
CAB-531 (20% in Butyl Acetate)
Uramex MF822 B 16
Solvesso 100 70
Xylene 359
2 : 1
Cerafac 106(10% in xylene) 30
Sparkle Silver 3334 AR
Guide formula 3.1Base coat based on thermosetting hydroxy acrylic resin
After 1 Day After 3 Days After 1 Week
Hardness of base coat based on thermosetting hydroxy acrylic resin
chart 3.1
9
AC‐EAGLE(TS‐10XB50) 2% 50 % W-X ≤ 150 Hazen •••••••••••••••••• ••••••••••
Application Product Performance
Automotive metalicbase coat
Excellent weathering resistance, scratch
resistance, �exibility & compatible with CAB
Xylene/Butanol 3/1
OH % Solid %Type ofSolvent
Visc. Colour Gloss Hardness Flexibility Impact Adhesion Curing time
••••• Exce llent •••• Very Good ••• Good •• Fair • Poor N/A Not Applied
Properties
4. Resins for Clear Coat
Recommended Resins
AC-EAGLE(OH138-40BA65)65%
AC-EAGLE(OH132-20X50)50%
AC-EAGLE(OH138-40M65)65%
AC-EAGLE(OH148-27M60)60%
AC-EAGLE(OH100-40BA70)70%
AC-EAGLE(OH90-30X60)60%
AC-EAGLE(OH138-30M60)60%
AC-EAGLE(OH100-18BA60)60%
AC-EAGLE(OH138-90BA70)70%
AC-EAGLE(OH148-95BA70)70%
Substrate wetting
Hardener
Hydroxy acrylic 65% (OH% 4.2) 835
Butyl Acetate 54.6
Byk 331 (10% in Xylene)
Raw Materials Weight by grams Remarks
1.1
Butyl Acetate : Xylene 2 : 1
Solvesso 100 159
Butyl Acetate 159
Desmodur N75 BA/X 455
Xylene 109.3
Hardener Solution
Xylene 80
Thinner
Clear coat based on hydroxy acrylic Guide formula 4.1Clear coat based on hydroxy acrylic resin
10
4. Resins for Clear Coat
020406080
100120140160180200
After 1 DayAfter 3 DaysAfter 1 Week
Hardness of clear varnish basedon hydroxy acrylic resins
chart 4.1
Gloss of clear varnish basedon hydroxy acrylic resins
chart 4.2
Impact of clear varnish basedon hydroxy acrylic resins
chart 4.3
Adhesion of clear varnish basedon hydroxy acrylic resins
chart 4.4
7678808284868890929496
After 1 DayAfter 3 DaysAfter 1 Week
020406080
100120
Impact After 1 Week
0
1
2
3
4
5
6
Adhesion After 1 Week
11
4. Resins for Clear Coat
12
AC-EAGLE(OH148-27M60)
AC-EAGLE(OH148-95BA70)
AC-EAGLE(OH138-90BA70)
AC-EAGLE(OH138-40BA65)
AC-EAGLE(OH138-40M65)
AC-EAGLE(OH138-30M60)
AC-EAGLE(OH132-20X50)
AC-EAGLE(OH100-40BA70)
AC-EAGLE(OH100-18BA60)
AC-EAGLE(OH90-30X60)
4.5%
4.5%
4.2%
4.2%
4.2%
4.2%
4%
3%
3%
3%
Mix. solvent
Butyl acetate
Butyl acetate
Butyl acetate
Mix.solvent
Xylene
Xylene
Butyl acetate
Butyl acetate
Xylene
60%
70%
70%
65%
65%
60%
50%
70%
60%
60%
Z-Z1
Z4-Z6
Z4-Z6
Z-Z3
Z-Z3
Z1-Z3
W-Y
Z1-Z3
X-Z
Z1-Z2
≤ 50 Hazen
≤ 50 Hazen
≤ 50 Hazen
≤ 50 Hazen
≤ 50 Hazen
≤ 50 Hazen
≤ 50 Hazen
≤ 50 Hazen
≤ 50 Hazen
≤ 50 Hazen
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
••••
••••
••••
••••
•••••
•••••
•••••
••••
••••
••••
•••••
•••••
•••••
•••••
••••
••••
•••••
•••••
••••
•••
•••
•••••
•••••
••••
•••
•••••
••••
••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
Application Product Performance
High hydroxyl %, excellent hardness, very good gloss and weathering resistance
High solid with excellent gloss, very good hardness and weathering resistance
High solid with excellent gloss, very good hardness and weathering resistance
Excellent gloss, very good hardness and weathering
resistance
Excellent gloss, very good hardness and weathering
resistance
Excellent gloss, very good hardness and weathering
resistance
Very good gloss, excellent hardness and weathering
resistance
High solid with excellent hardness, excellent gloss
and weathering resistance
Very good hardness, excellent gloss and
weathering resistance
Very good hardness, very good gloss and weathering
resistance
High solid, high quality with mirror e�ect for
automotive re�nish clear coat
High solid automotive re�nish clear coat
High solid automotive re�nish clear coat
Medium solid automotive re�nish clear coat
Medium solid automotive re�nish clear coat
Medium solid automotive re�nish clear coat
Medium solid automotive re�nish clear coat
Economic high solid automotive re�nish clear
coat
Economic medium solid automotive re�nish clear
coat
Economic medium solid automotive re�nish clear
coat
OH % Solid %Type ofSolvent
Visc. Colour Gloss Hardness Flexibility Impact Adhesion Curing time
••••• Exce llent •••• Very Good ••• Good •• Fair • Poor N/A Not Applied
Properties
5. Resins for Solid Colour
Recommended Resins
AC-EAGLE(OH138-40BA65)65%
AC-EAGLE(OH132-20X50)50%
AC-EAGLE(OH138-40M65)65%
AC-EAGLE(OH148-27M60)60%
AC-EAGLE(OH100-40BA70)70%
AC-EAGLE(OH90-30X60)60%
AC-EAGLE(OH138-30M60)60%
AC-EAGLE(OH100-18BA60)60%
AC-EAGLE(OH138-90BA70)70%
AC-EAGLE(OH148-95BA70)70%
Guide formula 5.1Solid colour based on hydroxy acrylic resins
Tinstab BL 277 (1% in Xylene)
Rheology modi�er
Levelling agent
Catalyst
Hardener
Solvesso 100 100.1
Butyl Acetate 100.1
Xylene 50.4
Thinner
Butyl Acetate : Xylene 2 : 1
9.5
Hardener Solution
Desmodur N75 BA/X 288
Grind well then add
Hydroxy Acrylic 65% (OH% 4.2) 355.4
BYK 358N (50% in BA) 4.1
Xylene 157.14
Hydroxy Acrylic 65% (OH% 4.2) 168.46
TiO2 303
Bentone 38 2.4
Raw Materials Weight by grams Remarks
Solid color based on hydroxy acrylic
020406080
100120140160180
After 1 DayAfter 3 DaysAfter 1 Week
Hardness of solid colour basedon hydroxy acrylic resins
chart 5.1
13
Gloss of solid colour basedon hydroxy acrylic resins
chart 5.2
Whiteness of solid colour basedon hydroxy acrylic resins
chart 5.3
Impact of solid colour basedon hydroxy acrylic resins
chart 5.4
Adhesion of solid colour basedon hydroxy acrylic resins
chart 5.5
5. Resins for Solid Colour
82
84
86
88
90
92
94
After 1 DayAfter 3 DaysAfter 1 Week
79808182838485868788
After 1 DayAfter 3 DaysAfter 1 Week
0
20
40
60
80
100
120
Impact After 1 Week
0
1
2
3
4
5
6
Adhesion After 1 Week
14
5. Resins for Solid Colour
00.010.020.030.040.050.060.070.08
∆G*
∆W*
∆G*
∆W* 00.020.040.060.08
0.10.120.14
00.020.040.060.08
0.10.120.140.160.18
∆G*
∆W*
0
0.05
0.1
0.15
0.2
0.25
0.3
∆G*
∆W*
Effect of weathering on gloss and whiteness after 240 hr
chart 5.6
Effect of weathering ongloss and whiteness after 500 hr
chart 5.7
Effect of weathering ongloss and whiteness after 750 hr
chart 5.8
Effect of weathering ongloss and whiteness after 1000 hr
chart 5.9
15
5. Resins for Solid Colour
AC-EAGLE(OH148-27M60)
AC-EAGLE(OH148-95BA70)
AC-EAGLE(OH138-90BA70)
AC-EAGLE(OH138-40BA65)
AC-EAGLE(OH138-40M65)
AC-EAGLE(OH138-30M60)
AC-EAGLE(OH132-20X50)
AC-EAGLE(OH100-40BA70)
AC-EAGLE(OH100-18BA60)
"AC-EAGLE(OH90-30X60)"
4.5%
4.5%
4.2%
4.2%
4.2%
4.2%
4%
3%
3%
2.7%
Mix. solvent
Butyl acetate
Butyl acetate
Butyl acetate
Mix.solvent
Xylene
Xylene
Butyl acetate
Butyl acetate
Xylene
60%
70%
70%
65%
65%
60%
50%
70%
60%
60%
Z-Z1
Z4-Z6
Z4-Z6
Z-Z3
Z-Z3
Z1-Z3
W-Y
Z1-Z3
X-Z
Z1-Z2
≤ 50 Hazen
≤ 50 Hazen
≤ 50 Hazen
≤ 50 Hazen
≤ 50 Hazen
≤ 50 Hazen
≤ 50 Hazen
≤ 50 Hazen
≤ 50 Hazen
≤ 50 Hazen
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
••••
••••
••••
••••
••••
•••••
•••••
••••
••••
•••••
•••••
•••••
•••••
•••••
•••••
••••
•••••
•••••
••••
•••
•••
•••••
•••••
••••
•••
•••••
••••
••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
•••••
Application Product Performance
High hydroxyl %, excellent hardness, very good gloss and weathering resistance
High solid with excellent gloss, very good hardness and weathering resistance
High solid with excellent gloss, very good hardness and weathering resistance
Excellent gloss, very good hardness and weathering
resistance
Excellent gloss, very good hardness and weathering
resistance
Excellent gloss, very good hardness and weathering
resistance
Very good gloss, excellent hardness and weathering
resistance
High solid with excellent hardness, excellent gloss
and weathering resistance
Very good hardness, excellent gloss and
weathering resistance
Very good hardness, very good gloss and weathering
resistance
Medium solid automotive pigmented top coat- best for expensive black colour
High solid automotive pigmented top coat
High solid automotive pigmented top coat
High solid automotive pigmented top coat
High solid automotive pigmented top coat
Medium solid automotive pigmented top coat
Low cost automotive pigmented top coat
Low cost high solid automotive pigmented top
coat
Low cost medium solid automotive pigmented top
coat
Low cost medium solid automotive pigmented top
coat
OH % Solid %Type ofSolvent
Visc. Colour Gloss Hardness Flexibility Impact Adhesion Curing time
••••• Exce llent •••• Very Good ••• Good •• Fair • Poor N/A Not Applied
Properties
16