development of high temperature cathodic disbondment test
TRANSCRIPT
![Page 1: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/1.jpg)
Amal Al-Borno, Ph.D.
Charter Coating Service (2000) Ltd.
Calgary, AB
Canada
Development of High Temperature Cathodic
Disbondment Test Methods
![Page 2: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/2.jpg)
Presentation Outline ● Project Background and Summary
● Technical Background
● Technical Objectives
● Design of Prototype Pressure Apparatus
● Test Results from Pressure Apparatus
● Design of Low Pressure Apparatus
● Further Test Results
● Conclusions
![Page 3: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/3.jpg)
Project Background
● Increasing temperatures in oil industry means more testing needed at elevated temperatures.
● Many pipelines are now operating at service temperatures above 100oC/212oF.
● Cathodic disbondment (CD) tests evaluate protective coatings used on cathodically protected systems.
● Many current CD test methods are not for use at high temperatures (above 80oC/176oF)
![Page 4: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/4.jpg)
Project Summary ● Both end users and coating suppliers expressed
interest in CD testing above 100oC/212oF.
● Current test methodologies are limited since test solutions must be below boiling point.
● This project includes design, building, testing and validation of a CD test apparatus for
> 100oC/212oF.
● Subsequent work includes the design, build and testing of a cooling jacketed test cell that allows for high temperature CD tests at ambient pressure.
![Page 5: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/5.jpg)
Technical Background
● A combination of a protective coating and
cathodic protection (CP) is used to
suppress corrosion.
● Coating defects (holidays) can occur due
to poor application or damage.
● While protecting the steel, CP can be
detrimental to coatings by producing an
aggressive, caustic environment at
holidays.
![Page 6: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/6.jpg)
Cathodic Protection – How does it work?
- COM
Pipe
Reference Electrode
Pipe Test Lead
Digital Volt Meter
SOIL
+ -
Ground Bed Anode
DC Power Supply
Current
+ VOLT
-0.850 V
![Page 7: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/7.jpg)
Technical Objectives ● To design, build and test a high-temperature
and high-pressure (HT-HP) CD test
apparatus for > 100oC/212oF.
● To investigate possible alternative reference
electrodes.
● To develop a new test procedure by
modification of currently used CD standard
test methods.
![Page 8: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/8.jpg)
Technical Objectives ● To investigate effect of increased pressure on
the adjusted potential and the disbondment of
different coating.
● To compare results from the HT-HP apparatus
and tests conducted at ambient pressure.
● To examine coating performance at
temperatures above 100oC/212oF.
● To examine the influence of Oxygen content.
● To develop a test cell that would allow for
testing up to at least 150°C/302°F.
![Page 9: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/9.jpg)
Design of HT-HP Prototype
Operating Condition Maximum
Temperature (0C) 150
Pressure (MPa) 1.4
Liquid Phase Salt Water
Primary Gas Phase Air and Steam
Potential Gaseous
Reactants
Hydrogen and Chlorine
Operating Conditions for the HT-HP Prototype
![Page 10: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/10.jpg)
Design of HT-HP Prototype
Body and Head Material 316L Stainless Steel
Internal Diameter (mm) 178
Wall Thickness (mm) 25.4
Height (cm) 25
Shell Bolt Grade 1
Shell Bolt Ultimate
Tensile Strength (MPa)
248
Number of Shell Bolts 8
Construction Materials and Dimensions
![Page 11: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/11.jpg)
Schematic of HT-HP Cell
0.635 cm NPT Port
1.27 cm NPT Port
1.905 cm NPT Port
Thermocouple
Reference electrode
Electrochemical Bulkhead
Electrochemical Bulkhead
316L SS Head
Luggin Probe
Pressure
316L SS Body 17.78 cm
25 cm
![Page 12: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/12.jpg)
Schematic of Electrochemical Monitoring Equipment on HT-HP Cell
+ –
+
+
–
–
Sample
Pt. Electrode Luggin Probe Ag / AgCl Reference Electrode.
DC Power Supply
Voltmeter (V-Ag / AgCl )
Voltmeter (V-Cu/CuSO4)
Cu/CuSO4 reference electrode Thermometer TOC
Brine Displacer
Heat Source
Thermometer
Needle valve
Coolant Luggin Probe Reservoir
Test Cell (pressurized)
![Page 13: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/13.jpg)
HT-HP Apparatus Note that different set ups are required for pressurizing, adding electrolyte, and taking electrical readings
![Page 14: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/14.jpg)
● Two reference
electrodes were
examined:
● Internally a Ag/AgCl
electrode was used
● Externally a Luggin
probe assembly was
used with a
Cu/CuSO4 (CSE)
Reference electrodes and Luggin Probe
Luggin Capillary
Cu/CuSO4 Reference electrode
Working electrode
![Page 15: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/15.jpg)
Reference electrode selection Testing showed the internal Ag/AgCl electrode to be instable,
probably related to effects of pressure and temperature in
the test cell and so the external CSE in the Luggin probe was
selected for all future tests
![Page 16: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/16.jpg)
Comparative Tests for Study ● To evaluate the HT-HP test procedure it was
compared with two standard CD tests that can
be run at high temperature with suitable
modifications:
● ASTM G42: sample in electrolyte bath; usually
the bath is heated but for this study the pipe
sample was heated internally.
● ASTM G95: sample heated on a sand bath to
achieve the appropriate sample temperature.
![Page 17: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/17.jpg)
ASTM G42
Mg anode Heater Unit
Sample (cathode)
Test electrolyte
Iron filings used in sample for heating
![Page 18: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/18.jpg)
ASTM G95
Sample (cathode)
Sand bath – heats sample to set temperature
Pt anodes
![Page 19: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/19.jpg)
Comparative Tests
● Identical samples, same sample temperatures
● 80°C, 120°C and 150°C sample temperatures
● Two novolac coatings rated for immersion
conditions up to 150°C / 302°F
● -1.5 V (versus CSA)
● 6 days
● 3% NaCl electrolyte
● Electrolyte temperature and other factors vary
![Page 20: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/20.jpg)
Results 6 Day Cathodic Disbondment Results
for the Three Test Procedures
25
10 10
45 5
34 4
0
5
10
15
20
25
30
Tests at 80ºC Tests at 120ºC Tests at 150ºC
Dis
bond
men
t (m
m)
HT/HP Test ASTM G42 ASTM G95
![Page 21: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/21.jpg)
Results Water Temperature for the Three Test
Methods
72
109
128
5357
67
54
70
83
0
20
40
60
80
100
120
140
Tests at 80ºC Tests at 120ºC Tests at 150ºC
Tem
pera
ture
(ºC
)
HT/HP PrototypeASTM G42ASTM G95
![Page 22: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/22.jpg)
24.61
6.28
4.4 4.953.98
4.98
22.81
5.69
0
5
10
15
20
25
30
Prototype 700 kPa Air-1.5V
Prototype Atm.-1.5V
Prototype 700 kPa-N2-1.5V
G95 Atm.-1.5V G95 Atm.-2.0V G95 Atm.-2.5V
Dis
bond
men
t Rad
ius
(mm
)Results (80°C)
CD Disbondment Results Under Various Pressure, Gas and Potential Conditions
HT-HP 700kPa
Air -1.5V
HT-HP Atmos.
Air -1.5V
HT-HP 700kPa N2 -1.5V
G95 Atmos. -1.5V
G95 Atmos. -2.0V
G95 Atmos. -2.5V
![Page 23: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/23.jpg)
Results Theoretical Dissolved Oxygen Levels
35.4
28.8
24.2
5.3 4.9 4.15.23.8 2.6
0.0
10.0
20.0
30.0
40.0
50.0
60.0
70.0
80ºC 120ºC 150ºC
Dis
solv
ed O
xyge
n (p
pm)
Test Temperature (Celsius)
HT/HP Test ASTM G42 ASTM G95
72ºC
109ºC
54ºC 53ºC 57ºC 70ºC
128ºC
67ºC 82ºC
![Page 24: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/24.jpg)
Results 6 Day Cathodic Disbondment Results
for the Three Test Procedures
25
10 10
45 5
34 4
0
5
10
15
20
25
30
Tests at 80ºC Tests at 120ºC Tests at 150ºC
Dis
bond
men
t (m
m) HT/HP Test ASTM G42 ASTM G95
![Page 25: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/25.jpg)
Results 30 Day Cathodic Disbondment Results
for the Three Methods at 120°C
18.19
4.93
8.499.83
3.594.64
0
2
4
6
8
10
12
14
16
18
20
HT-HP Procedure ASTM G95 Modified ASTM G42 Modified
Dis
bond
men
t(mm
)
Liquid Epoxy 1 Liquid Epoxy 2
![Page 26: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/26.jpg)
Design of High Temperature Low Pressure Test Apparatus
Concerns from use of the high pressure test apparatus :
● Multiple tests require multiple test set ups
● HT/HP results significantly accelerated and severe
● Electrolyte temperature is not representative of fluids
in normal service since:
●> 100°C would result in boiling and so a dry pipe
●fluids around a pipeline are cooled by the
environment
● Test pressure is not reproducing actual field conditions
● Test apparatus is complicated and expensive
![Page 27: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/27.jpg)
Coolant in
Coolant out
Pt anode
Cooling jacket
Cathodic connection
Sample
Heated sand bath
High Temperature Low Pressure CD Test Apparatus
![Page 28: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/28.jpg)
Low Pressure CD Test – Oxygen Level Effect
4.1 4.1
3
0
1
2
3
4
Oxygen: 2.0-3.5 mg/L Bubbling Air: Oxygen: 2.0-3.5 mg/L
Bubbling Oygen: Oxygen: 5.0-6.5 mg/L
Dis
bond
men
t, m
m
![Page 29: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/29.jpg)
High Temperature Low Pressure CD Test Apparatus for Undersea Simulation
Electrolyte temperature
Sample temperature
Silicone oil in
Silicone oil out
Thermo-statically controlled cooler
Insulation on test vessel and tubing to maintain
Silicone temperature
Heated Sand Bath
![Page 30: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/30.jpg)
CD Results: 3-Layer PP Coating, 28 days, 108°C, -1.5 V
PP, No pre-treatment PP, With pre-treatment
The thick top PP layer and some of a middle red adhesive layer were removed using a powered steel brush and the base blue FBE coating was rated for disbondment. The average of duplicate samples was 4.3 and 3.2 mm for the two different substrate pre-treatment methods.
![Page 31: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/31.jpg)
Conclusions – HT/HP Apparatus ● Successful design, construction and
commission of HT-HP Apparatus
● Safe and reliable method
● Luggin Probe and CSE found to be best for
measuring and controling the potential
● Accelerated disbondment observed and more
severe than other CD test set ups; especially
when air is used for pressurization
● Severity related to higher electrolyte temp. and
dissolved oxygen concentration
![Page 32: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/32.jpg)
● Better simulation of actual service conditions
● Control of both sample and electrolyte
temperatures
● Reaction of sample (blistering etc.) is always
visible
● Relatively low cost apparatus/equipment
● Can be used to very high temperatures (we
have worked to 180°C / 356°F )
● Potential for subsea environment simulation
Conclusions - Low Pressure CD Test Apparatus
![Page 33: Development of High Temperature Cathodic Disbondment Test](https://reader031.vdocuments.mx/reader031/viewer/2022012300/61e131187f28ff786d580fe0/html5/thumbnails/33.jpg)
Thank You