LAPORAN

PRAKTIKUM MATERIAL TEKNIK MELIPUTI :

PENGUJIAN TARIK (TENSILE TEST)

PENGUJIAN IMPAK (IMPACT TEST)

PENGUJIAN KEKERASAN (HARDNESS TEST)

Disusun oleh:

NAMA

: ARIF ROHMAN HAKIMNIM

: 1411053KELOMPOK: 23TEKNIK MESIN S-1

FAKULTAS TEKNOLOGI INDUSTRI

INSTITUT TEKNOLOGI NASIONAL MALANG

2014

LEMBAR PERSETUJUAN

LAPORAN PRAKTIKUM

PENGUJIAN MATERIAL/METALLOGRAFI

MELIPUTI:

1. UJI TARIK

2. UJI IMPAK

3. UJI KEKERASANDisusun oleh :

NAMA

: ARIF ROHMAN HAKIMNIM

: 1411053JURUSAN

: TEKNIK MESIN S-1

FAKULTAS

: TEKNOLOGI INDUSTRI

PERIODE

: 2014/2015TAHUN

: 2014

NILAI

: . . . . . .DIPERIKSA DAN DISETUJUI OLEH :

Mengetahui,

Diperiksa/disetujuiKa. Lab. Peng. Material/Metallografi

Dosen Pembimbing

Ir. Teguh Rahardjo, MT

Ir. Teguh Rahardjo, MT NIP. 1957061199202001

NIP. 1957061199202001DAFTAR ISI LAPORAN PRAKTIKUM

Daftar isi

: Lembar persetujuan ................................................................................ i

: Kata pengantar ....................................................................................... ii

: Daftar isi ................................................................................................ iii

: Daftar Gambar ....................................................................................... iv

: Daftar Tabel .......................................................................................... v

: Daftar Grafik .......................................................................................... viBAB I

PENDAHULUAN

1.1 Latar Belakang ..................................................................................11.2 Maksud dan Tujuan Praktikum .........................................................2BAB IIPENGUJIAN TARIK (TENSILE TEST)

2.1 Tujuan Pengujian ................................................................................42.2 Teori Dasar .........................................................................................42.3 Prosedur Pengujian ............................................................................122.4 Data pengujian ...................................................................................12BAB IIIPENGUJIAN IMPAK (IMPACT TEST)3.1 Tujuan Pengujian ................................................................................133.2 Teori Dasar .........................................................................................133.3 Prosedur Pengujian .............................................................................203.4 Struktur Makro Uji Impak ..................................................................213.5 Data pengujian ...................................................................................26BAB IVPENGUJIAN KEKERASAN (HARDNESS TEST)

4.1 Tujuan Pengujian ...............................................................................304.2 Teori Dasar ........................................................................................304.3 Prosedur Pengujian ............................................................................314.4 Data pengujian ...................................................................................37BAB VPENUTUP

4,1 Simpulan .............................................................................................40

4.2 Saran ...................................................................................................41Daftar GambarGambar 2.1 Mesin Uji Tarik .............................................................................................. 4Gambar 2.2 Benda Uji untuk Pengujian Tarik .................................................................. 11Gambar 3.2 Universal Impact Tester .................................................................................22Gambar 3.2 Mesin Uji Impact ............................................................................................24Gambar 3.3 Metode Pengujian Charpy ( v- notch) ........................................................... 25Gambar 3.4 Bentuk permukaan Patahan spesimen ........................................................... 26Gambar 3.5 Ukuran Spesimen Uji Impact ......................................................................... 27Gambar 3.6 Kurva Temperatur untuk 1 baja ...................................................................... 28Gambar 3.6 Spesiment (bahan ST42) ............................................................................... 29Daftar TabelTabel Data Pengujian Tarik .......................................................................................... 13Tabel Test Report ......................................................................................................... 14Tabel Data Pengujian Impak ......................................................................................... 30Tabel Data Rockwell .....................................................................................................32

Daftar GrafikGrafik 2.1 Kurva Tegangan Regangan .........................................................................7Grafik 2.2 Tegangan Renggangan Logam ....................................................................8Grafik Test Report ...........................................................................................................14Grafik Hubungan Tegangan dan Renggangan ................................................................19Grafik Hubungan Energi dan Temperatur ......................................................................29Grafik Hubungan Harga Impak dan Temperatur ............................................................29BAB VPENUTUP

5.1 Kesimpulana. Pengujian Tarik

Setiap logam yang di uji tarik mempunyai besar pertambahan panjang berbedabeda, kandungan unsurunsur paduan logam sangat mempengaruhi ketahananya terhadap beban puntir, tarik maupun tekan. Apabila logam tersebut dipakai dalam konstruksi yang mempengaruhi oleh besarnya beban tarik maka sebaliknya kandungan unsurunsur diperhatikan agar memperoleh harga kekerasan dan keuletan yang seimbang.

b. Pengujian ImpactSuatu logam yang di buat dengan unsurunsur yang sama akan mempunyai daya ketahanan terhadap beban yang di berikan bervariasi. Hal ini disebabkan oleh suhu pemanasan yang diberikan saat pengerjaan. Demikian pula temperatur pemanasan akan mempengaruhi sifatsifat permukaan patahan pada logam tersebut, seperti getas, kristal atau ulet (serat).c. Pengujian KekerasanSuatu logam yang mengalami proses Heat Treatment akan mempengaruhi sifatsifat mekanisnya, seperti proses pemanasan yang di berikan pada pengujian kekerasan, ini terlihat bahwa apabila suhu pemanasan pada logam dinaikan maka akan menurun. Disamping itu pula media pendingin juga ikut mnepengaruhi terbentuknya sifatsifat mekanisnya pada logam tersebut.

5.2 Saran1. Dalam bebrapa percobaan perlu ditingkatkan ketelitian dalam pengukuran untuk mendapatkan hasil pengujian yang benarbenar sesuai dengan teori tentang logam.

2. Untuk ini di setiap praktikum diharapkan sebelumnya sudah menguasai teoriteorinya agar dalam pelaksanaan pengujian bisa berjalan sesuai dengan yang diharapkan.

3. Agar menjamin kerja praktikum sebaiknya alatalat praktikum yang membutuhkan ketelitian tinggi perlu ditambah jumlahnya.

4. Pada proses pemanasan, hendak temperatur yang digunakan sesuai dengan benda kerja yang digunakan agar hasil praktikum yang diperoleh memenuhi syarat dari Heat Treatment.

5. Untuk memperoleh hasil percobaan yang memuaskan maka sesuatu percobaan hendaknya dilakukan berkalikali.