Constituent Materials of Concrete
by Nick Gromicko and Kenton Shepard
Concrete is a composite material consisting of a binder, which is typically cement, rough and fine aggregates, whic
are usually stone and sand, and water. These comprise the constituent materials of concrete. But because of the
many variables of the raw materials and how they are processed and combined, there are many opportunities forproblems to appear in concrete. Having a fundamental understanding of the different materials and manufacturing
processes may help those who inspect concrete to know what problems to look for, where to look for them, and
how to recognize them.
In simple terms:
cement + water = cement paste;
cement paste + sand = mortar; and
mortar + stone = concrete.
Admixtures may be included in the mix to control setting properties.
The chemical reactions that take place when different constituent materials are combined can vary depending on th
properties of the individual materials. The materials can vary in their chemical makeup and performance
characteristics, depending on where they were mined or quarried, and according to the manufacturing methods
used and conditions in the manufacturing plant.
Binders
Binders are fine, granular materials that form a paste when water is added to them. This paste hardens and
encapsulates aggregates and reinforcement steel. Immediately after water is added, cement paste begins to harden
through a chemical process called hydration. Hydration takes place at different rates according to the different
properties of the binders and admixtures used, the water-to-cement ratio, and the environmental conditions under
which the concrete is placed. The ways in which binders affect concrete, mortar and similar products can vary with
the chemical and physical properties of the source materials, the constituent materials, the mix design, and, to a
lesser extent, the variations in the cement manufacturing process.
Portland Cement
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
2/28
Portland cement
There are different types of cement, but Portland cement is the binder used most widely. Although Portland cemen
is named after an area in England where its use was originated, today it is manufactured all over the world.
ASTM International defines Portland cement as hydraulic cement (cement that forms a water-resistant product)
produced by pulverizing clinkers consisting essentially of hydraulic calcium silicates, usually containing one or more
of the forms of calcium sulfate as an inter-ground addition.
Portland cement is made by fusing calcium-bearing materials with aluminum-bearing materials. The calcium may
come from limestone, shells, chalk, or marl, which is a soft stone, or hard mud, sometimes called mudstone, that is
rich in lime.
The Cement Manufacturing Process
The basic operations of cement plants are roughly similar but may vary according to location. The manufacturing
process that follows describes what takes place in a quarry and cement plant in Colorado.
Quarry Operations
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
3/28
A limestone layer about 18 feet thick breaks the surface and slants away underground. Quarrying operations follo
it down to a level of about 200 feet before it is no longer profitable to pursue.
The dark-colored rock pictured above contains limestone and two kinds of shale, all of which are used in
producing cement. The light-colored material is called over-burden, which is not used in manufacturing, but is set
aside to be replaced later during reclamation after the quarry has reached the end of its permit period and is closed
The flat area in the quarry wall, called the lift or bench, is the depth to which holes are drilled before charges are s
for blasting. Here, it is about 80 feet. Because of Homeland Security requirements, most quarries subcontract theblasting operations.
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
4/28
After blasting, the waste stone is brought to the end of the quarry where quarrying first began. It will be the first
material to be filled back in as part of the reclamation process. Usable stone is hauled by truck and either dumped
into the primary crusher or piled nearby.
The roads and piles must be kept watered to reduce airborne dust.
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
5/28
Trucks back into this building to dump their loads into the primary crusher.
The primary crusher
After the stone is dumped into the feed chute from above, gravity moves it down through the crusher, which
reduces it to about 3 inches in diameter. A bag filter helps reduce airborne dust.
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
6/28
From the crusher, the stone moves onto a conveyor belt that carries it to the manufacturing plant about 2 miles
away.
Long conveyor belts must be kept adjusted to the proper tension. This is done by using steel cables to suspend
concrete weights inside the towers.
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
7/28
At each point where the conveyor changes height or direction, another bag filter helps to remove dust from the
crushed stone and from the air.
The limestone and shale are finally stockpiled at the far end of the production line.
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
8/28
The stone is loaded with a front-end loader one bucketful at a time onto a conveyor that carries it into the surge sil
(above left). From the surge silo, the stone can be conveyed into the system at a uniform rate. From the surge silo,
the stone is transported to a dryer that removes most of the moisture before returning it to the secondary crusher
(center silo), where it is reduced to about 3/8-inch in diameter. From this point, the stone is transported by high-
speed air instead of by roller-supported belts.
The dried, crushed stone is then moved to the ball mill, in which tumbling steel balls reduce it to a powder. The ba
mill is a spinning cylinder that has a sacrificial lining held in place by hundreds of bolts, the heads of which can be
seen in the photo above.
Different materials are combined in the ball mill, so this is also where initial blending takes place. Common material
are limestone, shale, sandstone and iron.
From the ball mill, the material moves to the pre-heat tower (at left), where it is heated to about 1,800 F before
moving to the horizontal, cylindrical, rotating kiln.
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
9/28
The kiln (dark grey) is tilted slightly so that the material moves through it as it rotates. The more steeply inclined
tube above the kiln (light grey) supplies combustion air, as does the U-shaped duct at the top of the pre-heat
tower. Inside the kiln, the material is heated to about 3,300 F. This process is called sintering. Chemical changes
take place that result in the formation of a marble-sized substance called clinker. Creating clinker means using heatto drive all carbon dioxide out of the material. Carbon dioxide is a major greenhouse gas.
The photo above shows the doors open at the lower end of the kiln, which is shut down for inspection and service
The 6-inch-diameter flexible pipe slanting down to the left is the gas supply for the burner that ignites the pulverized
coal fuel. The end of the 8-inch coal supply pipe can be seen just to the right of the feet of the worker.
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
10/28
Stockpiles of the pulverized coal used to fuel the kiln
Clinker is moved to a specially-shaped storage shed to control its moisture content.
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
11/28
Clinker is finely ground to create the final cement product. The photo above shows both the marble-sized clinker
before being ground, and the final product: cement.
The entire operation is monitored and controlled from a central control console that contains numerous monitorswith real-time digital readouts.
Variations
Although there are ASTM standards with which Portland cement may comply, there are a number of factors that
can cause its performance characteristics to vary.
Particle Size
The size of the particles is important because particles that are ground more finely offer more surface area against
which the chemical reactions take place, and these strongly influence the properties of the cement. Cement with
small particles will be more reactive and will gain strength sooner after the hydration process has begun. The total
surface area of the particles in a given volume of material is called its specific surface.
Portland cements have a specific surface of 1,500 to 2,000 square feet per pound of material (ft /lb), equal to
around 300 to 400 square meters per kilogram (m /kg), depending on type.
Gypsum and Sulfates
Gypsum, also in the form of ground particles, is mixed with the ground clinker to slow the hydration process
enough so that there will be time to place the concrete, screed it, and finish it before it sets. If gypsum or sulfate
materials are added to and ground with the clinker material, they may be reduced in size more quickly than theclinker. This preferential grinding can result in smaller particles, which increases their ratio of reactivity compared
to that of the clinker material.
For any particular cement, there is an optimum content for both gypsum and sulfate. The details of exactly how
sulfates affect the strength development of concrete are not well understood.
The optimum content of both gypsum and sulfates depends not only on the type of cement design mix, but also on
the:
chemical properties of both the calcium and aluminum source materials used for the clinker;
physical properties of the aluminates, such as crystal size;
2
2
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
12/28
varying solubility of the different sources of the sulfates;
particle size;
milling temperature; and
use of admixtures.
As if this werent complicated enough, the optimum sulfate content for one cement property, such as strength, may
be different from the optimum content for another property, such as drying shrinkage. Concrete and mortar can
have different optimum contents, which is why different types of cements are manufactured.
Materials are tested four times during the manufacturing process in an effort to prevent such problems. The rawmaterials are tested before they enter the manufacturing process, before entering the kiln, after leaving the kiln, and
before final storage in the main storage silos.
Cement wafers used in a portion of the testing process
Equipment used to test compressive strength
Cement Types
ASTM Specification C-150 provides standards for eight different types of Portland cement:
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
13/28
1. Type I is a general-purpose cement used in a wide variety of project types, including buildings, bridges, floors
pavements, and precast concrete projects.
2. Type IA is similar to type I but is used for projects requiring air-entrainment.
3. Type II generates less heat, generates heat at a slower rate, and has moderate resistance to sulfate attack.
4. Type IIA is identical to Type II but is used for projects requiring air-entrainment.
5. Type III is a high early-strength cement that causes concrete to set and gain strength quickly. Type III cement
is chemically and physically similar to Type I except that the particles are more finely ground.
6. Type IIIA is a high early-strength cement used for projects requiring air-entrainment.
7. Type IV develops strength at a slower rate than other cement types and produces lower levels of heat duringhydration. Its used for large-mass concrete structures from which there is little chance for heat to escape, suc
as dams.
8. Type V is used only in concrete structures that will be exposed to severe attack by sulfates, typically in places
where concrete is exposed to soil and groundwater with a high sulfate content.
ASTM C-1157 includes the following:
1. Type GU hydraulic cement is used for general construction.
2. Type HE is high early-strength cement.
3. Type MS is moderately resistant to attack from sulfates.
4. Type HS is highly resistant to attack from sulfates.
5. Type MH produces moderate levels of heat during hydration.
6. Type LH produces low levels of heat during hydration. This cement type can also be designed for low
reactivity (Option R) with alkali-reactive aggregates.
SUPPLEMENTARY CEMENTICOUS MATERIALS
Pozzolans
Other materials may be blended with Portland cement to meet special requirements and environmental
considerations. Some of these materials, called pozzolans, do not have cementicious properties until mixed with
Portland cement. When concrete is mixed, in order to improve its workability and flow characteristics, more water
is added beyond what is needed for hydration. This surplus water is then present in tiny capillary channels in the
hydrated (hardened) concrete. When a pozzolan material is substituted for a portion of the cement, a secondary
chemical reaction takes place after hydration. Chemicals released from the cement paste during hydration react
with chemicals in the pozzolan material to form a material that partially or fully fills these capillary channels. This
makes concrete more dense and increases its resistance to chemicals (such as those used for de-icing operations)
that can penetrate porous concrete and corrode reinforcement steel and cause surface deterioration or spalling.
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
14/28
Surface spalling caused by de-icing chemicals
When a portion of the cement is replaced with pozzolans, less heat is produced during hydration. This secondary
reaction produces some heat, but the peak temperatures are lower and spread out over a longer period of time.Since concrete contracts (shrinks) as it cools, less heat means less overall shrinkage. Since shrinkage creates
stresses that are relieved by cracking, less shrinkage means fewer cracks. This is especially important with high-
mass structures that cannot release heat easily, such as dams.
Fly Ash
Flay ash viewed at the microscopic level
Fly ash is an industrial by-product that is sometimes used as a partial replacement for Portland cement. Fly ash is
composed of the non-combustible particulates that are removed from the flue gas of coal-burning power plants. It
may form up to 65% of the mass of cementicious materials, depending on the performance requirements of the
concrete and the type of coal burned.
Reclaiming fly ash for industrial use is an environmentally sound practice, since fly ash is removed from flue gas to
improve air quality, and its use in cement means that what was once a waste product is now recycled as a useful
material. As of 2005, U.S. coal-fired power plants reported producing 71 million tons of fly ash, 29 million tons of
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
15/28
which were used in various applications. The remaining 42 million tons could cover an acre of land to a depth of
27,500 feet. This unused fly ash takes up space in landfills and contains toxins that can contaminate aquifers. In
December 2008, an embankment at a Tennessee Valley Authority fly ash storage facility in Kingston, Tennessee,
failed and released 5.4 million cubic yards of fly ash into the Emory River. Cleanup costs are approaching $1.2
billion.
Failure of a fly ash containment facility in Kingston, Tennessee
Here are some relevant facts about fly ash used in concrete:
Fly ash comes in types F and C. Type F fly ash is made by burning older, harder coal. It is a pozzolan and
when mixed with water, does not produce cementicious compounds unless the mix includes Portland cement.Type C is made by burning younger, softer coal and does have some cementicious compounds when its mixe
with water.
Very fine particles of fly ash can improve the flow characteristics of concrete, reduce costs by replacing
cement, require less water in the mix, and make concrete more dense. Coarse particles do not provide the
same benefits, and coarse and fine particles cannot always be separated effectively.
It may increase the setting time.
Fly ash does not accept pigments or acid stains as well as cement, so matching existing concrete made withou
fly ash can be a problem.
The performance characteristics of fly ash vary with particulate size, but also with the chemical composition of
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
16/28
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
17/28
Silica fume magnified 10,000 times
Silica fume is sometimes used to enhance certain properties of concrete. It is a very fine, glass- like powder
collected from the flue gases of electric arc furnaces during the process of manufacturing silicon metals. Before the
implementation of tougher environmental laws in the mid-1970s, silica fume was not collected. It has now become
one of the most valuable and versatile concrete admixtures in the world. Unlike sand its chemically similar
counterpart particles of silica fume are water-soluble, which means that they can react chemically as part of the
hydration process.
When the amounts of two granular materials are equal, materials with smaller particles expose more surface area
against which reactions can take place. Silica fume is approximately 100 times smaller than Portland cement
particles, and so its small size, along with its relatively high silica content, make it a very highly reactive pozzolan.
Their small particle size also allows silica fume to fill in the spaces between grains of cement, called particle-
packing, making concrete more dense and less porous or permeable to moisture. It also improves compressivestrength, the bonding strength between particulates, aggregates and embedded steel, and improves resistance to
abrasion.
Silica fume may form up to 12% of the mass of cementicious materials. Silica fume has a specific surface of 63,000
to 150,000 ft /lb (13,000 to30,000 m /kg).
The uniformity of silica fume can vary according to the chemical characteristics of the metal alloys being
manufactured. Silica fume from up to four different furnaces is sometimes mixed together in an effort to provide a
more uniform product. The effects on concrete of variations in the chemical properties of silica fumes from differen
furnaces are not well understood. The properties of silica fume concrete also vary with the different properties andamounts of the various water-reducing agents (plasticizers) that are typically used when silica fume is added to
concrete. Because the huge surface area of silica fume uses more water and reduces workability, plasticizers and
super-plasticizers are added to make concrete more fluid so that it can be placed and worked more easily.
Concrete is typically mixed at local batch plants before being trucked to a job site. Batch plants commonly have
silos containing fly ash and often have GGBFS on hand. Permanent storage facilities for silica fume are less
common.
2 2
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
18/28
A concrete batch plant with two fly ash silos
AGGREGATES
Aggregates are granular materials that include sand, gravel, crushed stone, river stone, and lightweight
manufactured aggregates, and may occupy up to 75% of the concretes total volume. Since aggregates are less
expensive than cement paste, they are added to concrete to help reduce costs. The properties of aggregates can
have a significant effect on the workability of concrete in its plastic state, as well as the durability, strength, density,
and thermal properties of the hardened concrete.
Where do aggregates come from?
Aggregates are heavy. Quarrying them in a central region and trucking them long distances is cost-prohibitive, so
aggregates are generally quarried locally. This means that the mineral, chemical and physical properties are likely t
be different in different areas, depending on the local geology. Minerals with different properties can react
differently to chemical processes or conditions in concrete, so aggregates are one more constituent material of
concrete that can have properties that vary.
Quarrying Aggregate
Aggregate quarry operations are similar to those used for quarrying stone for cement. The quarry pictured below,
also located in Colorado, provides primarily granite aggregate for the asphalt paving and concrete industries.
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
19/28
The photo above shows a relatively new quarry being worked. The drilling rig is shown drilling the holes in which
explosive charges will be set, while a truck is loaded with stone loosened by previous blasting. The truck will haul
the stone to Crusher #1.
Older quarries have been worked longer, so they are deeper. This operation blasts in holes drilled 35 feet deep, as
opposed to 80 feet at the limestone quarry. Here, too, blasting is performed by a subcontractor. This operation
contains several quarries in addition to the processing area, so it is a large operation.
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
20/28
Above, a truck feeds Crusher #1, the first in a series of crushers that the stone passes through. This quarry
produces 18 different aggregate products that vary in size from boulders to sand.
Looking directly down into Crusher #1, the size of the stone before it enters the crusher is visible. The stone is
moving from left to right.
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
21/28
Crushing and sorting operations are monitored from a central control tower overlooking the operations area. The
conveyor nearest the camera is moving the stone after processing by Crusher #1.
The photo above shows the view overlooking the operations area, and the controls and monitors.
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
22/28
This overview photo shows two additional crushers near the center. Despite massive amounts of stone being
crushed, transported, pushed and dropped onto stockpiles, airborne dust was minimal.
Aggregate Size
Aggregates for concrete are generally divided into two categories: fine and coarse. Fine aggregates are generally
natural sand or crushed stone, with most particles passing through a 3/8-inch (9.5-mm) sieve. Coarse aggregates
generally range between 3/8- to 1-1/2 inches (9.5 mm to 37.5 mm) in diameter. Most coarse aggregate used in
concrete is crushed stone, although smooth river rock is also used.Inadequate amounts of fine aggregates can cause excessive bleeding, difficulties in pumping concrete, and
difficulties in achieving smooth troweled surfaces. The bond strength of fine aggregates is not affected much by the
shape or texture of the aggregate, since smaller particles offer a large amount of surface area at which bonding to
the cement paste can take place. The surface properties of fine aggregate can affect the amount of water required
to keep concrete workable. Bear in mind that excessive amounts of water can weaken concrete by increasing the
percentage of capillary structure left behind as excess water finds its way to the surface as bleed water and then
evaporates. The photos below show aggregates commonly stocked by concrete batch plants.
1-inch gravel
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
23/28
-inch gravel
Squeegee
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
24/28
Lightweight
Common sand
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
25/28
Double-washed sand
The maximum size of aggregate should be less than one-fifth of the narrowest dimension between the sides offorms, one-third the depth of slabs, or three-fourths of the minimum clear spacing between reinforcing bars.
Using the largest possible aggregate size is sometimes recommended to minimize the amount of cement required, a
well as to minimize drying shrinkage of the concrete. The disadvantage of using large, coarse aggregate is that it
increases the chances of bond failure between the aggregate surface and the surrounding cement paste, since the
stresses at the interface between the two materials are higher than with smaller aggregate. It also reduces the total
available surface-bonding area.
The rigidity/deformation characteristics of the aggregate are also important. Extreme differences in the properties o
aggregate and cement paste result in high stresses that create micro-cracks that can weaken concrete.
Grading Aggregate
Well-graded aggregate is the result of using many sizes of aggregate in the mix. This helps reduce the amount of
cement paste required to fill the spaces or voids between the individual aggregate pieces. Reducing the percentage
of cement paste in the mix helps reduce shrinkage and lowers the heat of hydration, both of which can crack
concrete. It also improves its durability. The amount of aggregate used in a mix is called its packing density. Well-
graded aggregate has better packing density than gap-graded aggregate. Gap-graded aggregate has no
intermediate-sized pieces, which makes the concrete more difficult to place and increases its cost, and both of
these factors can affect the final product.
Moisture Content
Different types of aggregate have different levels of porosity; that is, they can absorb different amounts of water.
Highly porous stone affects concrete differently, depending on whether it is water-saturated or dry before being
added to the mix. Dry stone will absorb more water from the mix, and this can make concrete stiffer and more
difficult to work, which may appear as visible problems in the finished concrete. Water in saturated stone has to b
considered when calculating the amount of water to be added to the mix or the water ratio may be too high,
resulting in weakened concrete.
There are four moisture levels:
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
26/28
1. Oven-dry (OD) means that all moisture has been removed.
2. Air-dry (AD) means that surface moisture has been removed and internal pores are partially full.
3. Saturated surface-dry (SSD) means that the surface moisture has been removed, and all internal pores are ful
4. Wet means that pores are full, and there is a surface film.
Of these four states, saturated surface-dry is considered the best moisture state. With SSD, the aggregate is in a
state of equilibrium, so the aggregate will not absorb or give water to the cement paste. However, this moisture
state can be difficult to obtain.
Lightweight Aggregates
A facility for manufacturing lightweight aggregate
Lightweight aggregates are typically man-made and are highly porous. Clay, shale and slate will expand when they
are heated, a little like popcorn. Since most are porous, they are also moisture-absorbent, which can affect theamount of water used in the mix. A few types develop a coating during the fusion process that reduces their
absorptive properties; however, if this coating is damaged during handling, the aggregate as a whole will regain
some of its ability to absorb water. Depending on the percentage of aggregate that has damaged coating, this
condition can affect the quality of the concrete if such a variation is not allowed for in designing the mix.
Heavyweight Aggregates
Heavyweight aggregates are usually used in buildings requiring radiation shielding and are not of concern to most
inspectors.
Waste Materials as Aggregate
Many ideas for re-purposing waste materials have been considered and some have been tried. Inspectors may
encounter concrete with problems caused by materials inappropriately substituted for aggregate.
Some of those waste materials include:
building rubble;
industrial waste; and
mine tailings.
Alkali-Aggregate Reaction (AAR)
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
27/28
ASR-damaged concrete
Some types of aggregate materials react badly with alkalis from sources in the concrete or from other sources, sucas de-icing salts, groundwater, or sea water. If the aggregates contain a large percentage of silica, the reaction is
called alkali-silica reaction (ASR). If the aggregate consists of dolomitic carbonate rocks, it is called alkali-
carbonate reaction (ACR).
During ASR, which is the more common of the two problems, soluble silica in the aggregate reacts with soluble
alkali to produce an alkali-silica gel. When this gel absorbs moisture, it expands, causing concrete to crack. It may
take a while after the concrete is placed for ASR to appear. Cracks in control joints, shrinkage cracks, or micro-
cracks in the surface that are enlarged by freezing may allow moisture to enter the concrete and be absorbed by th
gel. Some aggregates are non-reactive and others are reactive to varying degrees.
There is no cost-effective method for mitigation of concrete damaged by AAR. Correction requires removal and
replacement.
Other Aggregate-Related Problems
Some types of stone used for aggregates may cause problems by expanding and contracting during freeze-
thaw cycles due to moisture content.
Aggregates can vary in their resistance to wear.
Aggregate impurities consisting of fine, solid particles can interfere with the surface bonding between cement
and coarse aggregate.Aggregate impurities that are soluble may interfere chemically with alkaline cement pastes and affect setting
times.
Aggregate from quarries in coastal locations should be cleaned to avoid salt contamination that may affect the
concrete chemically or attack embedded steel.
Inspectors will not always be able to attribute problems they see to particular constituent materials. Taking the time
to learn about the types of raw materials used in their area and the typical problems that arise related to those
materials may help inspectors to better understand the seriousness of various defects they discover so that they can
make the appropriate recommendations.
-
8/12/2019 Constituent Materials of Concrete - InterNACHI
28/28
Tweet 0 2
************************
This article is part of a series to help InterNACHI inspectors understand the characteristics of and visually inspect
concrete.
(http://inspectorseek.com)
Take InterNACHI's free, online "Structural Issues for Home Inspectors" course.
(http://www.nachi.org/structuralcoursereleased2007.htm)
Take InterNACHI's free, online "Inspecting Foundation Walls and Piers" course.
(http://www.nachi.org/wallsandpierscoursereleased2008.htm)
Take InterNACHI's free, online "How to Perform Exterior Inspections" course.
(http://www.nachi.org/exteriorcourse.htm)
International Standards of Practice for Inspecting Commercial Properties. (http://www.nachi.org/comsop.htm)
The History of Concrete (http://www.nachi.org/history-of-concrete.htm)
Concrete for Exterior and Structural Walls (http://www.nachi.org/concrete-exterior-walls.htm)
Concrete Admixtures (http://www.nachi.org/concrete-admixtures.htm)
More inspection articles like this (http://www.nachi.org/articles.htm)
Inspectopedia (http://www.inspectopedia.com/)
The entire contents of this site 2006-2014 InterNACHI. All rights reserved.
InterNACHI is a registered trademark of the International Association of Certified Home Inspectors, Inc.
Terms of Use (/termsofuse.htm?PHPSESSID=834d3d61f020f9d5cdf6a3139415a031) | Find an Inspector
(http://www.inspectorseek.com)
http://www.inspectorseek.com/http://www.nachi.org/termsofuse.htm?PHPSESSID=834d3d61f020f9d5cdf6a3139415a031http://www.inspectopedia.com/http://www.nachi.org/articles.htmhttp://www.nachi.org/concrete-admixtures.htmhttp://www.nachi.org/concrete-exterior-walls.htmhttp://www.nachi.org/history-of-concrete.htmhttp://www.nachi.org/comsop.htmhttp://www.nachi.org/exteriorcourse.htmhttp://www.nachi.org/wallsandpierscoursereleased2008.htmhttp://www.nachi.org/structuralcoursereleased2007.htmhttp://inspectorseek.com/http://twitter.com/search?q=http%3A%2F%2Fwww.nachi.org%2Fconstituent-materials-concrete.htmhttps://twitter.com/intent/tweet?original_referer=http%3A%2F%2Fwww.nachi.org%2Fconstituent-materials-concrete.htm&text=Constituent%20Materials%20of%20Concrete%20-%20InterNACHI%3A&tw_p=tweetbutton&url=http%3A%2F%2Fwww.nachi.org%2Fconstituent-materials-concrete.htm%23.Uw9u7PGlicY.twitter