THERMOSETRESINS FOR COMPOSITES
HELIOS RESINS FOR COMPOSITES OFFER FLEXIBLE HIGH-QUALITY RELIABLE COMPOSITE SOLUTIONS.
RESINS SUPPLIER SINCE 1908Composite resins since 1964
GOLDEN RESINS
Helios Resins is a separate business unit of the HeliosGroup producing the highest quality liquid resins foradvanced coating and composite manufacturers globally.Today, Helios Resins produces over 60,000 tons of liquidresins annually, including coating resins, composite resins,and polyester polyols for PU flexible foams. In addition to our coating resin brands, the composite resin brands - COLPOLY and COLVINYL - have achieved a strong market position and are trusted for their quality and reliable service. We currently serve over 50 countries worldwide, including Germany, Italy,France, Poland, Switzerland, Russia, the South African Republic, Morocco, Turkey, the UAE, Saudi Arabia, Thailand, and many others.
QUALITY OF SERVICE
We are committed to providing flexible and reliable servicewhile satisfying your specific requests. Helios Resins ensures quality, stability and reproducibility of every delivery. With the know-how, resulting from over 100 years of experience in synthetic resins and over 50 years in composite resins, together as partners we can solve your challenges. Our experts produce tailor-made resins for your particular needs and offer support in developing your applications.
DEVELOPED BY ADVANCED TECHNOLOGY
Our laboratories and production facilities are fully equipped with the most advanced technology enabling the development and production of resins. Our R&D has advanced skills as well as equipment for polyester and acrylic chemistry, including synthesis under pressure. Our production lines were upgraded in 2014 with a new pilot and large-scale reactor, resulting in new types of environmentally-friendly resins, as well as increased production capacities.
OUR STRENGTHS
•FLExIbILITY TO MEET CUSTOMER'S REqUIREMENTS
•ON-TIME DELIVERY
•HIGH qUALITY OF EVERY ORDER
COLPOLYUnsaturatedpolyesters
COLVINYLVinyl
esters
3
PRODUCT CHEMICAL NATURE
REACTIVE MONOMER CONTENT (%)
VISCOSITY AT 25°C (Brookfield, #2/10 rpm)
(mPa.s)
GEL TIME AT 25°C (MIN)CURING SYSTEM (% Co Acc.
1%/%MEKP-50)
ELONGATION AT BREAK (%)
TENSILE STRENGTH (MPa)
HDT (°C) REMARKS
COLPOLY 7233 DCPD 38 900 30 (0/1) 1.5 55 80 Preaccelerated, thixotropic, (possible LSE version on request)
COLPOLY 7243 OPA 42 1100 30 (0/1) 1.5 60 65 Preaccelerated, thixotropic, LSE, low peak temperature, promoted
COLPOLY 7246 OPA 43 1800 28 (0/2) 1.5 60 65 Preaccelerated, thixotropic, LSE, low peak temperature, Lloyd's approval
COLPOLY 733-10 DCPD 38 1000 30 (0/1) 2.5 65 65 Preaccelerated, thixotropic, LSE, low peak temperature, Lloyd's approval (without LSE additive version COLPOLY 733-15)
COLPOLY 738-95 Hybrid VE/DCPD 39 1200 40 (0/1) 3.0 70 105 Preaccelerated, thixotropic, barrier coat
COLPOLY 7528 OPA 42 1000 20 (0/2) 2.5 85 105 Preaccelerated, thixotropic, LSE, low peak temperature, promoted
COLPOLY 7805 IPA 44 900 Various (0/1.5) 3.5 85 85 Preaccelerated, thixotropic, medium thix index, chemical resistant, (possible LSE version on request), Lloyd's approval
COLVINYL VE 101 AT VE 46 1200 18 (0/2) 4.5 80 105 Preaccelerated, thixotropic, barrier coat
I. GENERAL PURPOSE RESINS GENERAL PURPOSE LAMINATING RESINS FOR HAND LAY-UP AND SPRAY-UP APPLICATIONS
HIGH PERFORMANCE LAMINATING RESINS FOR HAND LAY-UP AND SPRAY-UP APPLICATIONS
PRODUCT CHEMICAL NATURE
REACTIVE MONOMER CONTENT (%)
VISCOSITY AT 25°C (Brookfield, #2/10 rpm)
(mPa.s)
GEL TIME AT 25°C (MIN)CURING SYSTEM (% Co Acc.
1%/%MEKP-50)
ELONGATION AT BREAK (%)
TENSILE STRENGTH (MPa)
HDT (°C) REMARKS
COLPOLY 7227 OPA 43 1450 35 (0/1) 2.5 70 75 Preaccelerated, thixotropic, LSE, low peak temperature, Lloyd's approval
COLPOLY 7815 IPA/NPG 41 1400 15 (0/2) 3.0 65 80 Preaccelerated, thixotropic, LSE, low peak temperature, Lloyd's approval
4 5
PRODUCT CHEMICAL NATURE
REACTIVE MONOMER CONTENT (%)
VISCOSITY AT 25°C (Brookfield, #2/10 rpm)
(mPa.s)
GEL TIME AT 25°C (MIN)CURING SYSTEM (% Co Acc.
1%/%MEKP-50)
ELONGATION AT BREAK (%)
TENSILE STRENGTH (MPa)
HDT (°C) REMARKS
COLPOLY 7321 DCPD 27 1400 45 (1/1) 3.0 70 80 Artificial marble and onyx
COLPOLY 732-D3 DCPD 35 380 15 (1/1) 3.0 70 80 Artificial marble and onyx
COLPOLY 733-90 M DCPD 34 420 20 (1/1) 2.5 60 100 Artificial marble and onyx
COLPOLY 733-90 DCPD 32 320 8 (0.5/2) 2.5 60 100 Polymer concrete, low viscosity, high reactivity
COLPOLY 7525 OPA 34 420 8 (0.5/2) 2.5 80 105 Polymer concrete, high reactivity
COLPOLY 7524 AM-GS OPA 36 400 14 (0/1)* 3.5 75 90Resin is designed and recommended for use with Gruber Systems’ composites manufacturing equipment, where quartz filler is utilised to manufacture cast polymer sanitaryware, kitchen sinks and other architectural surfacing products, * AAP curing
COLPOLY 7167 IPA/NPG 33 1100 10 (1/2) 2.0 90 105 Solid surface, contain acrylic (possible preaccelerated and different viscosity)
II. CASTING AND CLOSED MOULDING RESINS CASTING RESINS
RESIN TRANSFER MOULDING (RTM)
PRODUCT CHEMICAL NATURE
REACTIVE MONOMER CONTENT (%)
VISCOSITY AT 25°C (Brookfield, #2/10 rpm)
(mPa.s)
GEL TIME AT 25°C (MIN)CURING SYSTEM (% Co Acc.
1%/%MEKP-50)
ELONGATION AT BREAK (%)
TENSILE STRENGTH (MPa)
HDT (°C) REMARKS
COLPOLY 7524-03 DCPD 37 220 9 (0.8/1)* 4.0 75 85 Excellent impregnation * AAP curing
COLPOLY 7524/8 OPA 37 220 9 (0.8/1)* 3.5 80 90 Excellent impregnation * AAP curing
COLPOLY 7608 DCPD 32 300 15 (0/2) 3.0 70 75 Fire retardant, halogenated
PRODUCT CHEMICAL NATURE
REACTIVE MONOMER CONTENT (%)
VISCOSITY AT 25°C (Brookfield, #2/10 rpm)
(mPa.s)
GEL TIME AT 25°C (MIN)CURING SYSTEM (% Co Acc.
1%/%MEKP-50)
ELONGATION AT BREAK (%)
TENSILE STRENGTH (MPa)
HDT (°C) REMARKS
COLPOLY 757 OPA 36 1200 n.m. 2.0 40 115 High resistance to heat deformation, compatible with LP additives
COLPOLY 768 Maleic 32 3000 n.m. 1.5 60 120 Low shrink SMC/BMC application
COLPOLY 783-02 IPA 33 3800 n.m. 3.0 70 105 High crack resistance, high resistance to heat deformation, high viscosity and high reactivity
COLPOLY 7572 OPA 35 1400 n.m. 1.5 70 120 High resistance to heat deformation, compatible with LP additives
COLPOLY 7795 Maleic 35 180 n.m. 2.0 40 130 Basic resin for LS formulation
COLPOLY LPA 2600 Saturated polyester 30 1400 n.m. n.m. n.m. n.m. LPA additive
SHEET MOULDING COMPOUND (SMC), BULK MOULDING COMPOUND (BMC)
6 7
PRODUCT CHEMICAL NATURE
REACTIVE MONOMER CONTENT (%)
VISCOSITY AT 25°C (Brookfield, #2/10 rpm)
(mPa.s)
GEL TIME AT 25°C (MIN)CURING SYSTEM (% Co Acc.
1%/%MEKP-50)
ELONGATION AT BREAK (%)
TENSILE STRENGTH (MPa)
HDT (°C) REMARKS
COLPOLY 724 A LSE DCPD 40 200 10 (0/2) 1.5 55 70 Formulated to be filled with mineral fillers, preaccelerated, LSE (possible non LSE version on request), good adhesion on ABS
COLPOLY 7331 LV DCPD 37 150 8 (0/2) 2.5 65 70 Formulated to be filled with mineral fillers, preaccelerated, LSE (possible non LSE version on request), good adhesion on PMMA
COLPOLY 736 WAT DCPD 38 200 14 (0/2) 2.5 60 85 White pigmented, accelerated, thixotropic, LSE, formulated to be filled with mineral fillers, good adhesion on ABS and PMMA
PRODUCT CHEMICAL NATURE
REACTIVE MONOMER CONTENT (%)
VISCOSITY AT 25°C (Brookfield, #2/10 rpm)
(mPa.s)
GEL TIME AT 25°C (MIN)CURING SYSTEM (% Co Acc.
1%/%MEKP-50)
ELONGATION AT BREAK (%)
TENSILE STRENGTH (MPa)
HDT (°C) REMARKS
COLPOLY 721 S DCPD 36 250 18 (1/1) 3.5 60 80 Low viscosity, UV stabilised, good glass wetting, continuous sheet curing with MIBK, discontinuous laminating with MEKP or AAP
COLPOLY 736 S DCPD 30 280 18 (1/1) 2.5 65 85Low viscosity, low styrene contain, UV stabilised, good glass wetting, continuous sheet curing with MIBK, discontinuous laminating with MEKP or AAP
COLPOLY 739 S DCPD 32 240 18 (1/1) 2.5 60 95 Low viscosity, UV stabilised, good glass wetting, continuous sheet curing with MIBK, discontinuous laminating with MEKP or AAP
PRODUCT CHEMICAL NATURE
REACTIVE MONOMER CONTENT (%)
VISCOSITY AT 25°C (Brookfield, #2/10 rpm)
(mPa.s)
GEL TIME AT 25°C (MIN)CURING SYSTEM (% Co Acc.
1%/%MEKP-50)
ELONGATION AT BREAK (%)
TENSILE STRENGTH (MPa)
HDT (°C) REMARKS
COLPOLY RP 7015/8 DCPD 35 350 8 (2 BP) 2.5 60 95 Medium reactive resin, good mechanical properties, good glass wetting
COLPOLY 7558-02 OPA 35 700 9 (2 BP) 3.0 70 100 Excellent mechanical properties, high impact strength, high HDT
COLPOLY 779 Maleic 36 1800 8 1.5 35 130 High resistance to heat deformation, high reactivity
COLPOLY 7800 IPA 35 950 (2 BP) Various 4.5 90 100 Fast through cure (possible different viscosity and solids content modified with LS additives etc.)
COLVINYL VE 105 LV VE 34 500 10 (2 BP) 5.5 85 105 Optimal wetting of the glass fiber, good mechanical properties and excellent corrosion resistant, high HDT
PRODUCT CHEMICAL NATURE
REACTIVE MONOMER CONTENT (%)
VISCOSITY AT 25°C (Brookfield, #2/10 rpm)
(mPa.s)
GEL TIME AT 25°C (MIN)CURING SYSTEM (% Co Acc.
1%/%MEKP-50)
ELONGATION AT BREAK (%)
TENSILE STRENGTH (MPa)
HDT (°C) REMARKS
COLPOLY 7810 AI IPA/NPG 41 250 90 (0/1.5) 3.0 65 80 Rapid fill times, resistance to print-through, preaccelerated, Lloyd's approval
PRODUCT CHEMICAL NATURE
REACTIVE MONOMER CONTENT (%)
VISCOSITY AT 25°C (Brookfield, #2/10 rpm)
(mPa.s)
GEL TIME AT 25°C (MIN)CURING SYSTEM (% Co Acc.
1%/%MEKP-50)
ELONGATION AT BREAK (%)
TENSILE STRENGTH (MPa)
HDT (°C) REMARKS
COLPOLY RP 7015/9 DCPD 30 430 Various 2.5 70 85 Chemical resistance, low styrene content
COLPOLY 7166 IPA/NPG 40 600 Various 4.5 60 90 Excellent mechanical properties, high HDT, liner, adhesion on PVC
COLPOLY 7524 OPA 35 750 14 (0.8/1) 2.5 80 105 Chemical resistance
COLPOLY 7543 OPA 35 850 10 (1.5/2) 3.5 75 90 Excellent mechanical properties, outstanding durability, chemical resistance
COLPOLY 7854 IPA/TPA 40 400 Various 4.0 90 100 Chemical resistance
III. RESINS ARRANGING FOR TYPICAL APPLICATIONS SPRAY-UP LAMINATING RESINS FOR ACRYLICS AND/OR ABS
CONTINUOUS LAMINATING
PULTRUSION
VACUUM INFUSION
FILAMENT WINDING
8 9
PRODUCT CHEMICAL NATURE
REACTIVE MONOMER CONTENT (%)
VISCOSITY AT 25°C (Brookfield, #2/10 rpm)
(mPa.s)
GEL TIME AT 25°C (MIN)CURING SYSTEM (% Co Acc.
1%/%MEKP-50)
ELONGATION AT BREAK (%)
TENSILE STRENGTH (MPa)
HDT (°C) REMARKS
COLPOLY 7100 Maleic free 350 Grinding medium for pigment concentrates
COLPOLY 7220 OPA 36 500 10 (1/2) 2.5 70 80 Base resin for gel coats, Lloyd's approval
COLPOLY 7160 IPA/NPG 40 550 6 (1/2) 4.0 85 100 Base resin for gel coats, UV stabilised, Lloyd's approval
COLPOLY 7172 IPA 33 1250 8 (1/2) 5.0 85 95 Base resin for gel coats, Lloyd's approval
IV. SPECIALITY RESINS BASE RESINS FOR GEL COATS, TOP COATS AND PIGMENT CONCENTRATES
PRODUCT CHEMICAL NATURE
REACTIVE MONOMER CONTENT (%)
VISCOSITY AT 25°C (Brookfield, #2/10 rpm)
(mPa.s)
GEL TIME AT 25°C (MIN)CURING SYSTEM (% Co Acc.
1%/%MEKP-50)
ELONGATION AT BREAK (%)
TENSILE STRENGTH (MPa)
HDT (°C) REMARKS
COLPOLY 7281 DCPD 37 380 8.5 (2 BP) n.m. n.m. n.m. Pre-accelerated with amines, for use in the manufacture of car body fillers and putties for BPO cure
COLPOLY 7284 DCPD 35 550 8 (2 BP) n.m. n.m. n.m. Pre-accelerated with amines, for use in the manufacture of car body fillers and putties for BPO cure
COLPOLY 7291 DCPD 35 750 12 (2 BP) n.m. n.m. n.m. Pre-accelerated with amines, for use in the manufacture of car body fillers and putties for BPO cure, high flexibility
COLPOLY 7294 THPA 36 800 5 (2 BP) n.m. n.m. n.m.Pre-accelerated with amines, for use in the manufacture of car body fillers and putties for BPO cure, can be combined with other Colpoly grades (7281, 7284, 7291, 7296) to increase their hardness
COLPOLY 7296 THPA 33 700 8.5 (2 BP) n.m. n.m. n.m. Pre-accelerated with amines, for use in the manufacture of car body fillers and putties for BPO cure
RESINS FOR PUTTIES
10 11
Helios TBLUS d.o.o.Količevo 65, 1230 Domžale, Slovenia
T +386 1 722 40 71T +386 1 722 43 94 [email protected] www.resinshelios.com
A member of the European Helios Group.
European company Global delivery
Pub
lishe
r: H
elio
s T
BLU
S, d
.o.o
.
392
400
– G
B
2
015