FLUXES, STRIPS & WIRESFor ELECTROSLAG and SUBMERGED ARC WELD OVERLAY
Doc FLUXES, STRIPS & WIRESS2011EN
-
I INTRODUCTION
I STRIP CLADDING PROCESS
I CHARACTERISTICS
I PRODUCTS
I DEPOSIT TYPES
1. ComPany PAGE 2 - 32. oUR bRandS PAGE 3
1. SUbmERGEd aRC STRIP CLaddInG I SaW PAGE 42. ELECTRoSLaG STRIP CLaddInG I ESW PAGE 4
1. dEPoSITIon RaTES PAGE 5
1. WELdInG STRIP: SoUdoTaPE PAGE 6 - 72. WELdInG FLUXES: RECoRd PAGE 8 - 9
1. LoW aLLoy & maRTEnSITIC A I (rebuilding & hardfacing) B I (overlaying) PAGE 10 - 152. STaInLESS STEEL PAGE 16 - 193. SPECIaL STaInLESS STEEL PAGE 20 - 214. nICKEL aLLoyS PAGE 22 - 255. CobaLT aLLoyS PAGE 26 - 276. CoPPER aLLoyS PAGE 26 - 27
1. In PETRoCHEmICaLS & CHEmICaLS PAGE 282. In oFFSHoRE PAGE 28 - 293. FoR maInTEnanCE & REPaIR PAGE 294. In nUCLEaR PoWER IndUSTRy PAGE 305. SoUdoKay Q5 nUCLEaR PRodUCTS PAGE 30
1. STRIP CLaddInG oF WELdEd JoInTS oF RoLL bondEd CLad PLaTES PAGE 31
1. TyPES oF STRIP CLaddInG noZZLES PAGE 32 - 332. maGnETIC STEERInG dEVICE PAGE 33
1. FLUXES FoR oVERLayInG WITH SoLId WIRES PAGE 34 - 352. FLUXES FoR SURFaCInG WITH CoREd WIRES PAGE 34 - 35
I WIRE CLADDING FLUXES
I STRIP CLADDING APPLICATIONS
I CLAD PLATES
I CLADDING NOZZLES
ConTEnTS
-
WIDTH & THICKNESS WIDTH & COIL15 x 0,5mm (0,59 x 0,020inch) 15 - 20kg (33, 1-44, 1 lbs)20 x 0,5mm (0,59 x 0,020inch) 20 - 25kg (44, 1-55, 1 lbs)30 x 0,5mm (0,59 x 0,020inch) 25 - 30kg (55, 1-66, 1 lbs)60 x 0,5mm (0,59 x 0,020inch) 55 - 60kg (121, 2-132, 3 lbs)90 x 0,5mm (0,59 x 0,020inch) 75 - 90kg (165, 3-198, 4 lbs)
other widths and coil weights available on requestBAGS METALIC DRUMS
25kg (55,1 lbs) 25kg (55,1 lbs)
I RECORD I FLUXES
I oUR bRandS2
I ComPany1
I Based in Seneffe, Belgium, SOUDOKAY is well-positioned to meet the chal-lenges and expectations of increasingly-competitive and demanding markets. The network of Bhler Welding Group subsidiaries, independent distributors and agents deliver SOUDOKAYs surfacing problem solutions, worldwide.
The certificates and approvals which we are able to offer, are both aguarantee for our clients and proof that we reach the most demanding of technical markets. In particular, ISO-9001, SOUDOKAY being one of the first to benefit from this, is a simple demonstration that our system of quality responds in every way to international demand.
I Because of the size of this document, we have not been able to show all the technical data we have available, so please contact our Sales Department for any additional information you might require or any help you may need in selecting welding products or processes. We are at your services, whatever the problem. Call us and we will help you to find the solution that will make sure your project is successful.
I Wire diameters from 0,9mm to 4mm,for open-arc, gas shielded, arc spraying andsubmerged arc applications.Diameters and packaging weightson request.
I SOUDOTAPE I STRIPS
I Our SOUDOTAPE welding strips are now clearly identified by a colouraccording to their base material ( ).We tried in this catalogue to use the same colours a those appliedon our strip labels.
A B
I SK I WIRESC
I Our RECORD fluxes.
InTRodUCTIon
2 I 3
-
STRIP CLaddInG PRoCESSI SUbmERGEd aRC STRIP CLaddInG I SaW1
I Both Electroslag and submerged arc strip cladding processes offer a very wide range of overlaying possibilities with many types of alloys, which are presented to you in the following pages, each of them being clearly represented by a colour ( ). We tried to be as much complete as possible.
I Nevertheless, please always keep in mind that the possibilities are not limited to the alloys listed in this catalogue and that we can offer you new solutions adapted to your specific needs, such as the already long list ofcustomized products we propose for serveral areas(P fluxes for pipes, Q5 products for the nuclear field, etc.).
I ELECTRoSLaG STRIP CLaddInG I ESW2
High deposition rates
High quality weld metal
Easy slag removal
Lower penetration
Lower dilution (down to 7%)
High current density resulting to higher deposition rate (up to 50kg/h)
Open weld pool
Special high speed fluxes (up to 45cm/min)
High deposition rate (up to 1,2m2/h)
Perfect overlap and very flat bead surface with magnetic steering
Low flux consumtion
Base metal
Solified slag Liquid slag
Flux feed hopper
30 mm stick-out
Strip feed & regulation
Direction of cladding
Flux feed hopper
5 mm 5 mm 1 > 1,5 mm
Strip feed & regulation
Flux feed hopper
Base metal
Direction of cladding
5 mm 5 mm 0,3 > 0,4 mm
Liquid slag Solidified slag
30 mm stick-out
-
400
300
600
700
500
200
100
010 15 20 25 30 35 40
WELDING SPEED [cm/min]
EXECUTION TIME to cover 100m2 as a function of the welding speedand the number of layers required [60x0,5mm strip]
EXEC
UTIO
N TI
ME [h
]
Two layers standard speed
Two layers high speed
One single layer standard speed One single layer high speed
40
30
60
50
20
10
0200 700 1200 1700 2200 2700
WELDING CURRENT [A]
DEPOSITION RATE IN kg/h as a function of the welding current and the strip width
DEPO
SITIO
N RA
TE [k
g/ho
ur]
30mm
60mm
90mm
120mm
kg/hour
Manual Metal ArcSubmerged Arc Singlewire
Submerged Arc Double WireFlux Cored Wire Open Arc
Plasma Transfered Arc PowderPlasma Mig
SUBMERGED ARC - Strip 30mm [SAW]Mig
SUBMERGED ARC - Strip 60mm [SAW]SUBMERGED ARC - Strip 90mm [SAW]
SUBMERGED ARC - Strip 120mm [SAW]ELECTROSLAG - Strip 30mm [ESW]
ELECTROSLAG - Strip 60mm [ESW]ELECTROSLAG - Strip 90mm [ESW]
ELECTROSLAG - Strip 120mm [SAW]
0 2 4 6 8 10 12 14 16 18 20 22 24 26 28 30 32 34 36 38 40 42 44 46 50 5248
STRIP WIDTH AvERAGE CURRENT CABLE SECTION BEAD WIDTH BEACH THICKNESS*15 mm (0,59 inch) 350 A 1 x 95 mm2 18-19 mm (0,7-0,74 Inch) 3-5 mm (0,12-0,19 inch)20 mm (0,78 inch) 400 A 1 x 95 mm2 23-24 mm (0,9-0,94 inch) 3-5 mm (0,12-0,19 inch)30 mm (1,18 inch) 600 A 2 x 95 mm2 32-37 mm (1,26-1,45 inch) 3-5 mm (0,12-0,19 inch)60 mm (2,36 inch) 1200 A 4 x 95 mm2 63-68 mm (2,48-2,68 inch) 3-5 mm (0,12-0,19 inch)90 mm (3,54 inch) 1800 A 5 x 95 mm2 93-99 mm (3,66-3,90 inch) 3-5 mm (0,12-0,19 inch)120 mm (4,72 inch) 2400 A 5 x 120 mm2 124-128 mm (4,88-5,04 inch) 3-5 mm (0,12-0,19 inch)
* On request according to specifications and application
PROCESS: SAW ESWELECTRIC ARC YES NO
MAGNETIC STEERING DEvICE NO YESDILUTION 18% 7%
DEPOSITION RATE 14kg/h (30,9 lbs/h) 23 kg (50,7 lbs/h)C 1ste LAYER on 0,18C STEEL 0,045 0,03
I DEPOSITION RATE I WELDING CURRENT [kg/h] I DEPOSITION RATE I WELDING SPEED [m2/h]
I ESW STRIP CLADDING I WELDING CURRENT
CHaRaCTERISTICSI dEPoSITIon RaTES1
I ComPaRISon: SaW - ESW STRIP CLaddInG2
I DEPOSITION RATE
I SAW I ESW
4 I 5
-
ALLOYWELDING STRIP STANDARDS CHEMICAL ANALYSIS (TYPICAL) (WEIGHT -%)
SOUDOTAPE ASME II C EN ISO 14343-A EN ISO 14343-B EN ISO 18274 EN 14640 EN 14700 W.-NR. C Mn Si Cr Ni Mo Cu N Nb Fe Co Other elements
LOW ALLOY & MARTENSITIC
SOUDOTAPE A 0,025 0,2 0,01 bal.SOUDOTAPE S 258 0,33 1,1 0,4 6,8 0,4 1,7 bal. 1,7 WSOUDOTAPE 410 L SFA 5.9:EQ 410 B 13 L ZBS410L 1.4009 0,025 0,4 0,4 12,7 bal.SOUDOTAPE 420 SFA 5.9:EQ 420 BS420 0,33 0,4 0,4 13,6 bal.SOUDOTAPE 430 SFA 5.9:EQ 430 B 17 BS430 1.4015 0,045 0,4 0,3 16,2 0,038 bal.SOUDOTAPE 430 L SFA 5.9:EQ 430 ZB 17 L ZBS430L 1.4015 0,015 0,4 0,3 16,4 0,015 bal.
STAINLESS STEEL
SOUDOTAPE 308 L SFA 5.9:EQ 308 L B 19 9 L BS308L 1.4316 0,013 1,7 0,4 20,3 10,4 0,1 0,04 bal.SOUDOTAPE 309 L SFA 5.9:EQ 309 L B 23 12 L BS309L 1.4332 0,012 1,8 0,4 23,7 13,3 0,1 0,048 bal.SOUDOTAPE 22.11 L ZB 22 11 L 1.4829 0,010 1,8 0,3 21,2 11,3 0,1 0,035 bal.SOUDOTAPE 316 L SFA 5.9:EQ 316 L B 19 12 3 L BS316L 1.4430 0,014 1,7 0,4 18,3 12,6 2,9 0,045 bal.SOUDOTAPE 317 L SFA 5.9:EQ 317 L B 19 13 4 L BS317L 0,016 1,5 0,4 18,8 13,6 3,5 0,045 bal.SOUDOTAPE 21.13.3 L ZB 21 13 3 L 0,014 1,7 0,3 20,3 14,2 2,9 0,033 bal.SOUDOTAPE 24.12 LNb B 23 12 Nb BS309LNb 1.4556 0,017 2,1 0,4 23,7 12,5 0,2 0,05 0,7 bal.SOUDOTAPE 347 SFA 5.9:EQ 347 B 19 9 Nb BS347 1.4551 0,016 1,7 0,4 19,7 10,5 0,1 0,046 0,5 bal.SOUDOTAPE 21.11 LNb ZB 21 11 Nb L 0,016 1,8 0,3 21,4 11,3 0,036 0,7 bal.SOUDOTAPE 410 L SFA 5.9:EQ 410 B 13 L ZBS410L 1.4009 0,025 0,4 0,4 12,7 bal.SOUDOTAPE 420 SFA 5.9:EQ 420 BS420 0,33 0,4 0,4 13,6 bal.SOUDOTAPE 430 SFA 5.9:EQ 430 B 17 BS430 1.4015 0,045 0,4 0,3 16,2 0,038 bal.SOUDOTAPE 430 L SFA 5.9:EQ 430 ZB 17 L ZBS430L 1.4015 0,015 0,4 0,3 16,4 0,015 bal.
SPECIALSTAINLESS STEEL
SOUDOTAPE 310 MM B 25 22 2 N L 0,012 4,5 0,2 25,1 22 2,2 0,13 bal.SOUDOTAPE 22.6.3 L ZB 22 6 3 N L 0,022 1,4 0,3 22,5 5,5 3,2 0,16 bal.SOUDOTAPE 20.25.5 LCu SFA 5.9:EQ 385 B 20 25 5 Cu L BS385 1.4519 0,012 1,6 0,3 19,9 24,3 4,3 1,5 0,05 bal.SOUDOTAPE 254SMo 1.4547 0,013 0,5 0,4 20 17,8 6 0,6 0,208 bal.SOUDOTAPE S 307 SFA 5.9:EQ 307 BS307 0,09 4,4 0,4 21 10 0,04 bal.SOUDOTAPE SCrNi32.27Mn ZB 32 27 Mn H 0,17 7,3 0,2 31,8 27 bal.
NICKEL BASE
SOUDOTAPE 825 SFA 5.14:EQ NiFeCr-1 B Ni 8065 (NiFe30Cr21Mo3Cu3) 0,01 0,8 0,3 22,5 bal. 3,1 2,4 30,5 0,75TiSOUDOTAPE 625 SFA 5.14:EQ NiCrMo3 B Ni 6625 (NiCr22Mo9Nb) 2.4831 0,015 0,1 0,1 22 bal. 9 3,6 0,3 0,23TiSOUDOTAPE NiCr3 SFA 5.14:EQ NiCr3 B Ni 6082 (NiCr20Mn3Nb) 2.4806 0,015 3,2 0,2 20,6 bal. 2,7 0,3 0,35TiSOUDOTAPE NiCu7 SFA 5.14:EQ NiCu-7 B Ni 4060 (NiCu30Mn3Ti) 2.4377 0,02 3,5 0,2 bal. 29,4 0,3 2,3TiSOUDOTAPE NiTi +/- SFA 5.14:EQ Ni-1 +/- B Ni 2061 (NiTi3) +/- 2.4155 0,023 0,3 0,1 bal. 0,1 3,9TiSOUDOTAPE 690 +/- SFA 5.14:EQ NiCrFe-7A B Ni Z (NiCr30Fe9Mn3Nb) 0,017 2,8 0,2 30,5 bal. 0,1 1,8 8,8 0,35TiSOUDOTAPE NiCrMo22 SFA 5.14:EQ NiCrMo-10 B Ni 6022 (NiCr21Mo13Fe4W3) 0,005 0,2 0,03 21,4 bal. 13,5 2,4 2,8WSOUDOTAPE NiCrMo59 SFA 5.14:EQ NiCrMo-13 B Ni 6059 (NiCr23Mo16) 0,005 0,2 0,04 22,7 bal. 15,5 0,7SOUDOTAPE NiCrMo4 SFA 5.14:EQ NiCrMo-4 B Ni 6276 (NiMo16Cr15Fe6W4) 2.4886 0,005 0,5 0,03 16 bal. 15,8 0,1 5,5 3,5WSOUDOTAPE NiCrMo7 SFA 5.14:EQ NiCrMo-7 B Ni 6455 (NiCr16Mo16Ti) 2.4611 0,006 0,1 0,03 15,5 bal. 15 0,5 0,35TiSOUDOTAPE NiCr3H SFA 5.14:EQ NiCr3 B Ni 6082 (NiCr20Mn3Nb) 2.4806 0,025 3,2 0,2 20,6 bal. 2,7 1 0,3 TiSOUDOTAPE NiMo7 0,03 0,2 0,02 bal. 27,8 0,1
COBALT BASESOUDOTAPE SCoCr6 +/- SFA 5.21:EQ CoCr A C Co2 1,1 0,6 0,1 31,5 2,1 0,8 bal. 5 WSOUDOTAPE SCoCr21 C Co1 0,25 0,4 0,5 27,2 3,3 5,5 bal.
COPPER BASE SOUDOTAPE CuNi30 SFA 5.7:EQ CuNi (B) Cu 7158 (CuNi30) 2.0837 0,025 0,8 0,1 30,7 bal. 0,7 0,45 Ti
PRod
UCTS
SoUd
oTaP
E
I WELdInG STRIP:1PRodUCTS
SOUDOTAPE
-
ALLOYWELDING STRIP STANDARDS CHEMICAL ANALYSIS (TYPICAL) (WEIGHT -%)
SOUDOTAPE ASME II C EN ISO 14343-A EN ISO 14343-B EN ISO 18274 EN 14640 EN 14700 W.-NR. C Mn Si Cr Ni Mo Cu N Nb Fe Co Other elements
LOW ALLOY & MARTENSITIC
SOUDOTAPE A 0,025 0,2 0,01 bal.SOUDOTAPE S 258 0,33 1,1 0,4 6,8 0,4 1,7 bal. 1,7 WSOUDOTAPE 410 L SFA 5.9:EQ 410 B 13 L ZBS410L 1.4009 0,025 0,4 0,4 12,7 bal.SOUDOTAPE 420 SFA 5.9:EQ 420 BS420 0,33 0,4 0,4 13,6 bal.SOUDOTAPE 430 SFA 5.9:EQ 430 B 17 BS430 1.4015 0,045 0,4 0,3 16,2 0,038 bal.SOUDOTAPE 430 L SFA 5.9:EQ 430 ZB 17 L ZBS430L 1.4015 0,015 0,4 0,3 16,4 0,015 bal.
STAINLESS STEEL
SOUDOTAPE 308 L SFA 5.9:EQ 308 L B 19 9 L BS308L 1.4316 0,013 1,7 0,4 20,3 10,4 0,1 0,04 bal.SOUDOTAPE 309 L SFA 5.9:EQ 309 L B 23 12 L BS309L 1.4332 0,012 1,8 0,4 23,7 13,3 0,1 0,048 bal.SOUDOTAPE 22.11 L ZB 22 11 L 1.4829 0,010 1,8 0,3 21,2 11,3 0,1 0,035 bal.SOUDOTAPE 316 L SFA 5.9:EQ 316 L B 19 12 3 L BS316L 1.4430 0,014 1,7 0,4 18,3 12,6 2,9 0,045 bal.SOUDOTAPE 317 L SFA 5.9:EQ 317 L B 19 13 4 L BS317L 0,016 1,5 0,4 18,8 13,6 3,5 0,045 bal.SOUDOTAPE 21.13.3 L ZB 21 13 3 L 0,014 1,7 0,3 20,3 14,2 2,9 0,033 bal.SOUDOTAPE 24.12 LNb B 23 12 Nb BS309LNb 1.4556 0,017 2,1 0,4 23,7 12,5 0,2 0,05 0,7 bal.SOUDOTAPE 347 SFA 5.9:EQ 347 B 19 9 Nb BS347 1.4551 0,016 1,7 0,4 19,7 10,5 0,1 0,046 0,5 bal.SOUDOTAPE 21.11 LNb ZB 21 11 Nb L 0,016 1,8 0,3 21,4 11,3 0,036 0,7 bal.SOUDOTAPE 410 L SFA 5.9:EQ 410 B 13 L ZBS410L 1.4009 0,025 0,4 0,4 12,7 bal.SOUDOTAPE 420 SFA 5.9:EQ 420 BS420 0,33 0,4 0,4 13,6 bal.SOUDOTAPE 430 SFA 5.9:EQ 430 B 17 BS430 1.4015 0,045 0,4 0,3 16,2 0,038 bal.SOUDOTAPE 430 L SFA 5.9:EQ 430 ZB 17 L ZBS430L 1.4015 0,015 0,4 0,3 16,4 0,015 bal.
SPECIALSTAINLESS STEEL
SOUDOTAPE 310 MM B 25 22 2 N L 0,012 4,5 0,2 25,1 22 2,2 0,13 bal.SOUDOTAPE 22.6.3 L ZB 22 6 3 N L 0,022 1,4 0,3 22,5 5,5 3,2 0,16 bal.SOUDOTAPE 20.25.5 LCu SFA 5.9:EQ 385 B 20 25 5 Cu L BS385 1.4519 0,012 1,6 0,3 19,9 24,3 4,3 1,5 0,05 bal.SOUDOTAPE 254SMo 1.4547 0,013 0,5 0,4 20 17,8 6 0,6 0,208 bal.SOUDOTAPE S 307 SFA 5.9:EQ 307 BS307 0,09 4,4 0,4 21 10 0,04 bal.SOUDOTAPE SCrNi32.27Mn ZB 32 27 Mn H 0,17 7,3 0,2 31,8 27 bal.
NICKEL BASE
SOUDOTAPE 825 SFA 5.14:EQ NiFeCr-1 B Ni 8065 (NiFe30Cr21Mo3Cu3) 0,01 0,8 0,3 22,5 bal. 3,1 2,4 30,5 0,75TiSOUDOTAPE 625 SFA 5.14:EQ NiCrMo3 B Ni 6625 (NiCr22Mo9Nb) 2.4831 0,015 0,1 0,1 22 bal. 9 3,6 0,3 0,23TiSOUDOTAPE NiCr3 SFA 5.14:EQ NiCr3 B Ni 6082 (NiCr20Mn3Nb) 2.4806 0,015 3,2 0,2 20,6 bal. 2,7 0,3 0,35TiSOUDOTAPE NiCu7 SFA 5.14:EQ NiCu-7 B Ni 4060 (NiCu30Mn3Ti) 2.4377 0,02 3,5 0,2 bal. 29,4 0,3 2,3TiSOUDOTAPE NiTi +/- SFA 5.14:EQ Ni-1 +/- B Ni 2061 (NiTi3) +/- 2.4155 0,023 0,3 0,1 bal. 0,1 3,9TiSOUDOTAPE 690 +/- SFA 5.14:EQ NiCrFe-7A B Ni Z (NiCr30Fe9Mn3Nb) 0,017 2,8 0,2 30,5 bal. 0,1 1,8 8,8 0,35TiSOUDOTAPE NiCrMo22 SFA 5.14:EQ NiCrMo-10 B Ni 6022 (NiCr21Mo13Fe4W3) 0,005 0,2 0,03 21,4 bal. 13,5 2,4 2,8WSOUDOTAPE NiCrMo59 SFA 5.14:EQ NiCrMo-13 B Ni 6059 (NiCr23Mo16) 0,005 0,2 0,04 22,7 bal. 15,5 0,7SOUDOTAPE NiCrMo4 SFA 5.14:EQ NiCrMo-4 B Ni 6276 (NiMo16Cr15Fe6W4) 2.4886 0,005 0,5 0,03 16 bal. 15,8 0,1 5,5 3,5WSOUDOTAPE NiCrMo7 SFA 5.14:EQ NiCrMo-7 B Ni 6455 (NiCr16Mo16Ti) 2.4611 0,006 0,1 0,03 15,5 bal. 15 0,5 0,35TiSOUDOTAPE NiCr3H SFA 5.14:EQ NiCr3 B Ni 6082 (NiCr20Mn3Nb) 2.4806 0,025 3,2 0,2 20,6 bal. 2,7 1 0,3 TiSOUDOTAPE NiMo7 0,03 0,2 0,02 bal. 27,8 0,1
COBALT BASESOUDOTAPE SCoCr6 +/- SFA 5.21:EQ CoCr A C Co2 1,1 0,6 0,1 31,5 2,1 0,8 bal. 5 WSOUDOTAPE SCoCr21 C Co1 0,25 0,4 0,5 27,2 3,3 5,5 bal.
COPPER BASE SOUDOTAPE CuNi30 SFA 5.7:EQ CuNi (B) Cu 7158 (CuNi30) 2.0837 0,025 0,8 0,1 30,7 bal. 0,7 0,45 Ti
6 I 7
-
WELDING FLUXESPROCESS STANDARDS EN 760
WELDING FLUXESPROCESS STANDARDS EN 760
WELDING FLUXESPROCESS STANDARDS EN 760
RECORD RECORD RECORD
RECORD 13 BLFT SAW SA AB 2 RECORD EST 310MM-SP ESW (E) SA FB 2 Cr Ni Mo RECORD NiCrW SAW SA FB 2
RECORD 8B308T2 Q5 SAW SA AB 2 Cr RECORD EST 316-1 ESW (E) SA FB 2 Cr Ni Mo RECORD NiCuT SAW SA CS 2
RECORD 9v308T1 Q5 SAW SA CS 2 Cr RECORD EST 317-1 ESW (E) SA FB 2 Cr Ni Mo RECORD NiCuW SAW SA CS 2
RECORD CrMo 15TW SAW SA AB 3 Cr Mo RECORD EST 320 ESW (E) SA FB 2 Cr Ni Mo Cu RECORD NiMo 15T SAW SA AB 3 Ni Mo
RECORD CrMo 21LC-TW SAW SA CS 3 C Cr Mo RECORD EST 347-1 ESW (E) SA FB 2 Cr Ni RECORD NiT SAW SA AB 2
RECORD CrMo 21TW SAW SA CS 3 C Cr Mo RECORD EST 347-1 HS ESW (E) SA FB 2 Cr Ni Nb RECORD R 250 SAW SA MS 3 Cr Mo
RECORD CrMo25TW SAW SA AB 3 Cr Mo RECORD EST 385-1 ESW (E) SA FB 2 Cr Ni Mo Cu RECORD R 400S SAW SA MS 3 C Cr Mo
RECORD CuAlW SAW SA AB 2 RECORD EST 400 ESW (E) SA FB 2 Cu RECORD RT 146 SAW SA AB 1
RECORD CuNi 30 T SAW SA AB 2 RECORD EST 423 ESW (E) SA FB 3 Mo RECORD RT 152 SAW SA CS 3 Ni Mo
RECORD CuNiW SAW SA AB 2 RECORD EST 426 ESW (E) SA FB 3 RECORD RT 155 SAW SA CS 3
RECORD EST 115P ESW (E) SA FB 2 RECORD EST 4462-1 ESW (E) SA FB 2 Cr Ni Mo RECORD RT 157 SAW SA CS 3 C Cr Ni Mo Nb v
RECORD EST 122 ESW (E) SA FB 2 RECORD EST 452 ESW (E) SA FB 3 Ni Mo RECORD RT 159 SAW SA CS 3
RECORD EST 126 ESW (E) SA FB 2 RECORD EST 453 ESW (E) SA FB 3 Ni Mo RECORD RT 161 SAW SA CS 3 Ni Mo
RECORD EST 129 ESW (E) SA FB 2 RECORD EST 625-1 ESW (E) SA FB 2 Cr Mo Nb RECORD RT 162 SAW SA CS 3 Cr Ni Mo
RECORD EST 130 ESW (E) SA FB 2 Nb RECORD EST 690 ESW (E) SA FB 2 Cr Nb RECORD RT 168 SAW SA CS 3 Ni Mo
RECORD EST 136 ESW (E) SA FB 2 RECORD EST 743 ESW (E) SA FB 3 Ni Mo Nb v C RECORD RT 177 SAW SA CS 3 C Cr Ni Mo Nb v
RECORD EST 136Mo ESW (E) SA FB 2 Mo RECORD EST 904Mo-1 ESW (E) SA FB 2 Cr Ni Mo Cu RECORD RT 179 SAW SA CS 3 Cr
RECORD EST 138 ESW (E) SA FB 2 Cr Ni Mo RECORD IN SAW SA AB 2 Cr RECORD RT 184 SAW SA CS 3 Ni Mo
RECORD EST 200 ESW (E) SA FB 2 RECORD INC SAW SA FB 2 Ni C RECORD RT 250 SAW SA MS 3 Cr Mo
RECORD EST 201 ESW (E) SA FB 2 RECORD IND 24 SAW SA FB 2 RECORD RT 350 SAW SA AB 3 Cr Mo
RECORD EST 201-B ESW (E) SA FB 2 RECORD IND 27 SAW SA FB 2 Cr RECORD RT 356 SAW SA CS 3 Cr
RECORD EST 225P ESW (E) SA FB 2 RECORD IND 45 SAW SA AB 2 RECORD RT 400 D SAW SA AB 3 C Cr Mo
RECORD EST 229 ESW (E) SA FB 2 RECORD INT 101 SAW SA AB 2 Cr RECORD RT 500 SAW SA CS 3 Cr Ni C
RECORD EST 236 ESW (E) SA FB 2 RECORD INT 101 Mo SAW SA AB 2 Cr Mo RECORD RT 505 SAW SA CS 3 Cr Ni Mo v
RECORD EST 236 ESW (E) SA FB 2 RECORD INT 102 SAW SA AB 2 RECORD RT 600 SAW SA AB 3 C Cr Mo
RECORD EST 237 ESW (E) SA FB 2 Cr RECORD INT 109 SAW SA CS 2 RECORD RT 742 SAW SA CS 3 Ni Mo Nb v
RECORD EST 2584 ESW (E) SA FB 2 Cr Ni Mo RECORD INT 110 SAW SA CS 2 Cr Ni Mo RECORD S Mo TW SAW SA AB 3 Mo
RECORD EST 259 ESW (E) SA FB 2 RECORD NFT 690 SAW SA AF 2 RECORD S46T SAW SA AB 1
RECORD EST 307 ESW (E) SA FB 3 Cr Mn RECORD NFT201 SAW SA AB 2 RECORD SA SAW SA FB 3
RECORD EST 308-1 ESW (E) SA FB 2 Cr Ni RECORD NiCr3T SAW SA AB 2 Cr Nb RECORD SK SAW SA FB 3
RECORD EST 310MM ESW (E) SA FB 2 Cr Ni Mo RECORD NiCrT SAW SA AB 2 RECORD SO SAW SA FB 157
PRod
UCTS
RECo
Rd
I WELdInG FLUXES:2PRodUCTS
RECORD
-
WELDING FLUXESPROCESS STANDARDS EN 760
WELDING FLUXESPROCESS STANDARDS EN 760
WELDING FLUXESPROCESS STANDARDS EN 760
RECORD RECORD RECORD
RECORD 13 BLFT SAW SA AB 2 RECORD EST 310MM-SP ESW (E) SA FB 2 Cr Ni Mo RECORD NiCrW SAW SA FB 2
RECORD 8B308T2 Q5 SAW SA AB 2 Cr RECORD EST 316-1 ESW (E) SA FB 2 Cr Ni Mo RECORD NiCuT SAW SA CS 2
RECORD 9v308T1 Q5 SAW SA CS 2 Cr RECORD EST 317-1 ESW (E) SA FB 2 Cr Ni Mo RECORD NiCuW SAW SA CS 2
RECORD CrMo 15TW SAW SA AB 3 Cr Mo RECORD EST 320 ESW (E) SA FB 2 Cr Ni Mo Cu RECORD NiMo 15T SAW SA AB 3 Ni Mo
RECORD CrMo 21LC-TW SAW SA CS 3 C Cr Mo RECORD EST 347-1 ESW (E) SA FB 2 Cr Ni RECORD NiT SAW SA AB 2
RECORD CrMo 21TW SAW SA CS 3 C Cr Mo RECORD EST 347-1 HS ESW (E) SA FB 2 Cr Ni Nb RECORD R 250 SAW SA MS 3 Cr Mo
RECORD CrMo25TW SAW SA AB 3 Cr Mo RECORD EST 385-1 ESW (E) SA FB 2 Cr Ni Mo Cu RECORD R 400S SAW SA MS 3 C Cr Mo
RECORD CuAlW SAW SA AB 2 RECORD EST 400 ESW (E) SA FB 2 Cu RECORD RT 146 SAW SA AB 1
RECORD CuNi 30 T SAW SA AB 2 RECORD EST 423 ESW (E) SA FB 3 Mo RECORD RT 152 SAW SA CS 3 Ni Mo
RECORD CuNiW SAW SA AB 2 RECORD EST 426 ESW (E) SA FB 3 RECORD RT 155 SAW SA CS 3
RECORD EST 115P ESW (E) SA FB 2 RECORD EST 4462-1 ESW (E) SA FB 2 Cr Ni Mo RECORD RT 157 SAW SA CS 3 C Cr Ni Mo Nb v
RECORD EST 122 ESW (E) SA FB 2 RECORD EST 452 ESW (E) SA FB 3 Ni Mo RECORD RT 159 SAW SA CS 3
RECORD EST 126 ESW (E) SA FB 2 RECORD EST 453 ESW (E) SA FB 3 Ni Mo RECORD RT 161 SAW SA CS 3 Ni Mo
RECORD EST 129 ESW (E) SA FB 2 RECORD EST 625-1 ESW (E) SA FB 2 Cr Mo Nb RECORD RT 162 SAW SA CS 3 Cr Ni Mo
RECORD EST 130 ESW (E) SA FB 2 Nb RECORD EST 690 ESW (E) SA FB 2 Cr Nb RECORD RT 168 SAW SA CS 3 Ni Mo
RECORD EST 136 ESW (E) SA FB 2 RECORD EST 743 ESW (E) SA FB 3 Ni Mo Nb v C RECORD RT 177 SAW SA CS 3 C Cr Ni Mo Nb v
RECORD EST 136Mo ESW (E) SA FB 2 Mo RECORD EST 904Mo-1 ESW (E) SA FB 2 Cr Ni Mo Cu RECORD RT 179 SAW SA CS 3 Cr
RECORD EST 138 ESW (E) SA FB 2 Cr Ni Mo RECORD IN SAW SA AB 2 Cr RECORD RT 184 SAW SA CS 3 Ni Mo
RECORD EST 200 ESW (E) SA FB 2 RECORD INC SAW SA FB 2 Ni C RECORD RT 250 SAW SA MS 3 Cr Mo
RECORD EST 201 ESW (E) SA FB 2 RECORD IND 24 SAW SA FB 2 RECORD RT 350 SAW SA AB 3 Cr Mo
RECORD EST 201-B ESW (E) SA FB 2 RECORD IND 27 SAW SA FB 2 Cr RECORD RT 356 SAW SA CS 3 Cr
RECORD EST 225P ESW (E) SA FB 2 RECORD IND 45 SAW SA AB 2 RECORD RT 400 D SAW SA AB 3 C Cr Mo
RECORD EST 229 ESW (E) SA FB 2 RECORD INT 101 SAW SA AB 2 Cr RECORD RT 500 SAW SA CS 3 Cr Ni C
RECORD EST 236 ESW (E) SA FB 2 RECORD INT 101 Mo SAW SA AB 2 Cr Mo RECORD RT 505 SAW SA CS 3 Cr Ni Mo v
RECORD EST 236 ESW (E) SA FB 2 RECORD INT 102 SAW SA AB 2 RECORD RT 600 SAW SA AB 3 C Cr Mo
RECORD EST 237 ESW (E) SA FB 2 Cr RECORD INT 109 SAW SA CS 2 RECORD RT 742 SAW SA CS 3 Ni Mo Nb v
RECORD EST 2584 ESW (E) SA FB 2 Cr Ni Mo RECORD INT 110 SAW SA CS 2 Cr Ni Mo RECORD S Mo TW SAW SA AB 3 Mo
RECORD EST 259 ESW (E) SA FB 2 RECORD NFT 690 SAW SA AF 2 RECORD S46T SAW SA AB 1
RECORD EST 307 ESW (E) SA FB 3 Cr Mn RECORD NFT201 SAW SA AB 2 RECORD SA SAW SA FB 3
RECORD EST 308-1 ESW (E) SA FB 2 Cr Ni RECORD NiCr3T SAW SA AB 2 Cr Nb RECORD SK SAW SA FB 3
RECORD EST 310MM ESW (E) SA FB 2 Cr Ni Mo RECORD NiCrT SAW SA AB 2 RECORD SO SAW SA FB 157
8 I 9
-
@TYPE OFDEPOSITED ALLOY
WELDINGPROCESS LAYER
TYPE OF STRIP (60 x 0,5 mm) TYPE OF FLUX
CHEMICAL ANALYSES on a 0,2% C plate(typical) (weight - %)
WELDING PARAMETERS (60 x 0,5 mm)
LAYER THICKNESS DEPOSITION RATE
SOUDOTAPE + RECORD C Mn Si Cr Ni Mo N Nb Fe Others Hardness A V cm/min inch/min mm inch kg/h lbs/h m/h inch/h
Unalloyed steel SAW
1st+2nd L:strip2nd L:deposit
SOUDOTAPE ASOUDOTAPE A
+0,0250,055
0,21,0
0,010,5
bal.bal.RECORD S 46 T 150HB 1150 28 15 5,9 4,4 0,17 22,0 48,6 0,63 971
1st+2nd L:strip2nd L:deposit
SOUDOTAPE ASOUDOTAPE A
+0,0250,055
0,21,0
0,010,5
bal.bal.RECORD RT 146 150HB 1150 28 15 5,9 4,4 0,17 22,0 48,6 0,63 971
0,5Mo SAW1st+2nd L:strip2 nd L: deposit
SOUDOTAPE ASOUDOTAPE A
+0,0250,042
0,21,0
0,010,6
bal.bal.RECORD SMoTW 0,6 900 26 18 7,1 3,0 0,12 17,3 38,0 0,72 1114
1Ni - 0,5Mo SAW1st+2nd L:strip2nd L:deposit
SOUDOTAPE ASOUDOTAPE A
+0,0250,116
0,20,7
0,010,5
bal.bal.RECORD NiMo15T 0,9 0,5 210HB 1100 25 13 5,1 4,2 0,17 21,1 46,5 0,63 973
1,5Cr - 0,5Mo SAW1st+2nd+3rd L:strip2nd L:deposit3rd L:deposit
SOUDOTAPE ASOUDOTAPE ASOUDOTAPE A
0,0250,0600,036
0,20,40,5
0,010,30,3
bal.bal.bal.
++
RECORD CrMo15TWRECORD CrMo15TW
1,31,3
0,60,6
240HB235HB
800800
2424
1717
6,76,7
3,53,5
0,140,14
15,315,3
33,833,8
0,550,55
849849
1,5Cr - 2Ni - 0,5Mo SAW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE ASOUDOTAPE ASOUDOTAPE ASOUDOTAPE A
0,0250,2400,2600,260
0,20,50,30,3
0,010,50,50,5
bal.bal.bal.bal.
+++
RECORD RT 505RECORD RT 505RECORD RT 505
1,11,41,4
1,62,02,1
0,40,50,6
0,09v0,110v0,120v
285HB320HB340HB
100010001000
282828
151515
5,95,95,9
43,83,8
0,160,150,15
19,219,219,2
42,342,342,3
0,600,630,63
928977977
2,0Cr - 1,0 Mo SAW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE ASOUDOTAPE ASOUDOTAPE ASOUDOTAPE A
0,0250,1000,0900,090
0,20,30,20,1
0,010,40,40,4
bal.bal.bal.bal.
+++
RECORD CrMo21TWRECORD CrMo21TWRECORD CrMo21TW
1,72,22,3
0,70,91,0
260HB275HB275HB
650650650
282828
131313
5,15,15,1
444
0,160,160,16
12,512,512,5
27,527,527,5
0,390,390,39
603603603
1st+2nd+3rd+4th+5th L:strip5th L:deposit
SOUDOTAPE ASOUDOTAPE A
0,025 0,2 0,01 bal.bal.+ RECORD CrMo21 LC TW 0,060 0,1 0,3 2,4 1,0 230HB 900 28 13 5,1 4,3 0,17 17,3 38 0,5 777
2Cr - 0,5 Mo SAW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE ASOUDOTAPE ASOUDOTAPE ASOUDOTAPE A
0,0250,1400,1100,080
0,20,60,70,6
0,010,40,50,5
bal.bal.bal.bal.
+++
RECORD CrMo25TWRECORD CrMo25TWRECORD CrMo25TW
1,41,71,9
0,50,60,6
240HB240HB240HB
650650650
282828
131313
5,15,15,1
444
0,160,160,16
12,512,512,5
27,527,527,5
0,390,390,39
603603603
3Cr - 0,5 Mo SAW1st+2nd+3rd L:strip3rd L:deposit
SOUDOTAPE ASOUDOTAPE A
0,0250,080
0,20,7
0,010,7
bal.bal.+ RECORD RT 250 3,0 0,4 290HB 1275 24 15 5,9 4,4 0,17 24,4 53,9 0,69 1076
5Cr - 0,9Mo SAW1st+2nd+3rd L:strip2nd L:deposit3rd L:deposit
SOUDOTAPE ASOUDOTAPE ASOUDOTAPE A
0,0250,0700,080
0,20,30,3
0,010,30,3
bal.bal.bal.
++
RECORD RT 350RECORD RT 350
4,65,0
0,80,9
325HB325HB
900900
2828
1313
5,15,1
3,83,8
0,150,15
17,317,3
38,038,0
0,570,57
879879
0,15C - 6Cr - 1Mo SAW1st+2nd+3rd+4th L:strip3rd L:deposit4th L:deposit
SOUDOTAPE ASOUDOTAPE ASOUDOTAPE A
0,0250,1200,120
0,20,30,3
0,010,40,4
bal.bal.bal.
++
RECORD RT 400 DRECORD RT 400 D
5,55,8
0,90,9
40HRc40HRc
12001200
2828
2121
8,38,3
3,13
0,120,12
23,023,0
50,750,7
0,930,96
14371485
0,35C - 6Cr - 3Mo SAW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE ASOUDOTAPE ASOUDOTAPE ASOUDOTAPE A
0,0250,3000,3200,340
0,20,50,30,3
0,010,40,30,3
bal.bal.bal.bal.
+++
RECORD RT 500RECORD RT 500RECORD RT 500
4,55,66,0
2,22,83,0
45 HRc45 HRc50 HRc
100010001000
282828
151515
5,95,95,9
43,83,8
0,160,150,15
19,219,219,2
42,342,342,3
0,600,630,63
928977977
0,4C - 6Cr - 0,7Mo SAW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE ASOUDOTAPE ASOUDOTAPE ASOUDOTAPE A
0,0250,2900,3300,340
0,20,60,40,3
0,010,70,80,9
bal.bal.bal.bal.
+++
RECORD RT 600RECORD RT 600RECORD RT 600
3,44,65,3
0,50,60,7
45HRc50HRc55HRc
950950950
272727
171717
6,76,76,7
444
0,160,160,16
18,218,218,2
40,140,140,1
0,570,570,57
882882882
258(C-Cr-Mo 50HRc)
SAW1st+2nd+3rd L:strip2nd L:deposit3rd L:deposit
SOUDOTAPE 258SOUDOTAPE 258SOUDOTAPE 258
0,3300,2500,250
1,11,01,0
0,40,50,5
6,86,46,6
0,40,30,3
1,71,31,6
bal.bal.bal.
1,7W1,55W1,6W
++
RECORD RT 159RECORD RT 159
45HRc50HRc
750750
2828
1212
4,74,7
3,23,2
0,130,13
14,414,4
31,731,7
0,560,56
870870
ESW1st+2nd L:strip1st L:deposit2nd L:deposit
SOUDOTAPE 258SOUDOTAPE 258SOUDOTAPE 258
0,3300,2500,250
1,11,01,0
0,40,50,6
6,85,46,4
0,40,20,3
1,71,31,5
bal.bal.bal.
1,7W1,35W1,55W
++
RECORD EST 122RECORD EST 122
45HRc45HRc
12501250
2424
1616
6,36,3
54,8
0,200,19
24,024,0
52,852,8
0,600,62
928967
258 NiMo1st+2nd+3rd L:strip2nd L:deposit3rd L:deposit
SOUDOTAPE 258SOUDOTAPE 258SOUDOTAPE 258
0,3300,2500,250
1,10,90,9
0,41,00,9
6,86,46,5
0,41,91,9
1,72,22,2
bal.bal.bal.
1,7W0,23v, 1,55W0,23v, 1,55W
++
RECORD RT 157RECORD RT 157
0,30,3
45HRc50HRc
900900
2626
1313
5,15,1
4,34,3
0,170,17
17,317,3
38,038,0
0,500,50
777777
All given values are typical
dEPo
SIT TyP
ESLo
W aL
Loy & ma
RTEn
SITIC
dEPoSIT TyPES1 AI LoW aLLoy & maRTEnSITIC I Rebuilding & Hardfacing
-
@TYPE OFDEPOSITED ALLOY
WELDINGPROCESS LAYER
TYPE OF STRIP (60 x 0,5 mm) TYPE OF FLUX
CHEMICAL ANALYSES on a 0,2% C plate(typical) (weight - %)
WELDING PARAMETERS (60 x 0,5 mm)
LAYER THICKNESS DEPOSITION RATE
SOUDOTAPE + RECORD C Mn Si Cr Ni Mo N Nb Fe Others Hardness A V cm/min inch/min mm inch kg/h lbs/h m/h inch/h
Unalloyed steel SAW
1st+2nd L:strip2nd L:deposit
SOUDOTAPE ASOUDOTAPE A
+0,0250,055
0,21,0
0,010,5
bal.bal.RECORD S 46 T 150HB 1150 28 15 5,9 4,4 0,17 22,0 48,6 0,63 971
1st+2nd L:strip2nd L:deposit
SOUDOTAPE ASOUDOTAPE A
+0,0250,055
0,21,0
0,010,5
bal.bal.RECORD RT 146 150HB 1150 28 15 5,9 4,4 0,17 22,0 48,6 0,63 971
0,5Mo SAW1st+2nd L:strip2 nd L: deposit
SOUDOTAPE ASOUDOTAPE A
+0,0250,042
0,21,0
0,010,6
bal.bal.RECORD SMoTW 0,6 900 26 18 7,1 3,0 0,12 17,3 38,0 0,72 1114
1Ni - 0,5Mo SAW1st+2nd L:strip2nd L:deposit
SOUDOTAPE ASOUDOTAPE A
+0,0250,116
0,20,7
0,010,5
bal.bal.RECORD NiMo15T 0,9 0,5 210HB 1100 25 13 5,1 4,2 0,17 21,1 46,5 0,63 973
1,5Cr - 0,5Mo SAW1st+2nd+3rd L:strip2nd L:deposit3rd L:deposit
SOUDOTAPE ASOUDOTAPE ASOUDOTAPE A
0,0250,0600,036
0,20,40,5
0,010,30,3
bal.bal.bal.
++
RECORD CrMo15TWRECORD CrMo15TW
1,31,3
0,60,6
240HB235HB
800800
2424
1717
6,76,7
3,53,5
0,140,14
15,315,3
33,833,8
0,550,55
849849
1,5Cr - 2Ni - 0,5Mo SAW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE ASOUDOTAPE ASOUDOTAPE ASOUDOTAPE A
0,0250,2400,2600,260
0,20,50,30,3
0,010,50,50,5
bal.bal.bal.bal.
+++
RECORD RT 505RECORD RT 505RECORD RT 505
1,11,41,4
1,62,02,1
0,40,50,6
0,09v0,110v0,120v
285HB320HB340HB
100010001000
282828
151515
5,95,95,9
43,83,8
0,160,150,15
19,219,219,2
42,342,342,3
0,600,630,63
928977977
2,0Cr - 1,0 Mo SAW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE ASOUDOTAPE ASOUDOTAPE ASOUDOTAPE A
0,0250,1000,0900,090
0,20,30,20,1
0,010,40,40,4
bal.bal.bal.bal.
+++
RECORD CrMo21TWRECORD CrMo21TWRECORD CrMo21TW
1,72,22,3
0,70,91,0
260HB275HB275HB
650650650
282828
131313
5,15,15,1
444
0,160,160,16
12,512,512,5
27,527,527,5
0,390,390,39
603603603
1st+2nd+3rd+4th+5th L:strip5th L:deposit
SOUDOTAPE ASOUDOTAPE A
0,025 0,2 0,01 bal.bal.+ RECORD CrMo21 LC TW 0,060 0,1 0,3 2,4 1,0 230HB 900 28 13 5,1 4,3 0,17 17,3 38 0,5 777
2Cr - 0,5 Mo SAW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE ASOUDOTAPE ASOUDOTAPE ASOUDOTAPE A
0,0250,1400,1100,080
0,20,60,70,6
0,010,40,50,5
bal.bal.bal.bal.
+++
RECORD CrMo25TWRECORD CrMo25TWRECORD CrMo25TW
1,41,71,9
0,50,60,6
240HB240HB240HB
650650650
282828
131313
5,15,15,1
444
0,160,160,16
12,512,512,5
27,527,527,5
0,390,390,39
603603603
3Cr - 0,5 Mo SAW1st+2nd+3rd L:strip3rd L:deposit
SOUDOTAPE ASOUDOTAPE A
0,0250,080
0,20,7
0,010,7
bal.bal.+ RECORD RT 250 3,0 0,4 290HB 1275 24 15 5,9 4,4 0,17 24,4 53,9 0,69 1076
5Cr - 0,9Mo SAW1st+2nd+3rd L:strip2nd L:deposit3rd L:deposit
SOUDOTAPE ASOUDOTAPE ASOUDOTAPE A
0,0250,0700,080
0,20,30,3
0,010,30,3
bal.bal.bal.
++
RECORD RT 350RECORD RT 350
4,65,0
0,80,9
325HB325HB
900900
2828
1313
5,15,1
3,83,8
0,150,15
17,317,3
38,038,0
0,570,57
879879
0,15C - 6Cr - 1Mo SAW1st+2nd+3rd+4th L:strip3rd L:deposit4th L:deposit
SOUDOTAPE ASOUDOTAPE ASOUDOTAPE A
0,0250,1200,120
0,20,30,3
0,010,40,4
bal.bal.bal.
++
RECORD RT 400 DRECORD RT 400 D
5,55,8
0,90,9
40HRc40HRc
12001200
2828
2121
8,38,3
3,13
0,120,12
23,023,0
50,750,7
0,930,96
14371485
0,35C - 6Cr - 3Mo SAW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE ASOUDOTAPE ASOUDOTAPE ASOUDOTAPE A
0,0250,3000,3200,340
0,20,50,30,3
0,010,40,30,3
bal.bal.bal.bal.
+++
RECORD RT 500RECORD RT 500RECORD RT 500
4,55,66,0
2,22,83,0
45 HRc45 HRc50 HRc
100010001000
282828
151515
5,95,95,9
43,83,8
0,160,150,15
19,219,219,2
42,342,342,3
0,600,630,63
928977977
0,4C - 6Cr - 0,7Mo SAW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE ASOUDOTAPE ASOUDOTAPE ASOUDOTAPE A
0,0250,2900,3300,340
0,20,60,40,3
0,010,70,80,9
bal.bal.bal.bal.
+++
RECORD RT 600RECORD RT 600RECORD RT 600
3,44,65,3
0,50,60,7
45HRc50HRc55HRc
950950950
272727
171717
6,76,76,7
444
0,160,160,16
18,218,218,2
40,140,140,1
0,570,570,57
882882882
258(C-Cr-Mo 50HRc)
SAW1st+2nd+3rd L:strip2nd L:deposit3rd L:deposit
SOUDOTAPE 258SOUDOTAPE 258SOUDOTAPE 258
0,3300,2500,250
1,11,01,0
0,40,50,5
6,86,46,6
0,40,30,3
1,71,31,6
bal.bal.bal.
1,7W1,55W1,6W
++
RECORD RT 159RECORD RT 159
45HRc50HRc
750750
2828
1212
4,74,7
3,23,2
0,130,13
14,414,4
31,731,7
0,560,56
870870
ESW1st+2nd L:strip1st L:deposit2nd L:deposit
SOUDOTAPE 258SOUDOTAPE 258SOUDOTAPE 258
0,3300,2500,250
1,11,01,0
0,40,50,6
6,85,46,4
0,40,20,3
1,71,31,5
bal.bal.bal.
1,7W1,35W1,55W
++
RECORD EST 122RECORD EST 122
45HRc45HRc
12501250
2424
1616
6,36,3
54,8
0,200,19
24,024,0
52,852,8
0,600,62
928967
258 NiMo1st+2nd+3rd L:strip2nd L:deposit3rd L:deposit
SOUDOTAPE 258SOUDOTAPE 258SOUDOTAPE 258
0,3300,2500,250
1,10,90,9
0,41,00,9
6,86,46,5
0,41,91,9
1,72,22,2
bal.bal.bal.
1,7W0,23v, 1,55W0,23v, 1,55W
++
RECORD RT 157RECORD RT 157
0,30,3
45HRc50HRc
900900
2626
1313
5,15,1
4,34,3
0,170,17
17,317,3
38,038,0
0,500,50
777777
All given values are typical
dEPo
SIT TyP
ESLo
W aL
Loy & ma
RTEn
SITIC
10 I 11
-
All given values are typical(4) 30mm strip
dEPo
SIT TyP
ESLo
W aL
Loy & ma
RTEn
SITIC
@
TYPE OFDEPOSITED ALLOY
WELDINGPROCESS LAYER
TYPE OF STRIP (60 x 0,5 mm) TYPE OF FLUX
CHEMICAL ANALYSES on a 0,2% C plate(typical) (weight - %)
WELDING PARAMETERS (60 x 0,5 mm)
LAYER THICKNESS DEPOSITION RATE
SOUDOTAPE + RECORD C Mn Si Cr Ni Mo N Nb Fe Others Hardness A V cm/min inch/min mm inch kg/h lbs/h m/h inch/h
410
SAW
1st+2nd+3rd L:strip
1st L:deposit
2nd L:deposit
SOUDOTAPE 430
SOUDOTAPE 430
SOUDOTAPE 430
+
+
RECORD RT 155
RECORD RT 155
0,045
0,083
0,075
0,4
0,5
0,4
0,3
0,7
0,8
16,2
10,8
13,4
0,1 bal.
bal.
bal.
340HB
260HB
900
900
26
26
12
12
4,7
4,7
4,1
3,8
1,61
0,15
17
17
38,0
38,0
0,53
0,57
815
879
ESW1st L:strip
1st L:deposit
SOUDOTAPE 430
SOUDOTAPE 430 + RECORD EST 122
0,045
0,055
0,4
0,4
0,3
0,5
16,2
12,9
0,1 bal.
bal. 280HB 1250 24 20 7,9 4,5 0,18 24 52,8 0,67 1031
410HC SAW
1st+2nd L:strip
1st L:deposit
2nd L: deposit
SOUDOTAPE 420
SOUDOTAPE 420
SOUDOTAPE 420
+
+
RECORD RT 356
RECORD RT 356
0,330
0,290
0,310
0,4
0,7
0,6
0,4
0,7
0,7
13,6
11,0
12,6
bal.
bal.
bal.
50HRc
55HRc
1100
1100
26
26
12
14
4,7
5,5
5,0
4,4
0,20
0,17
21,1
21,1
46,5
46,5
0,53
0,60
817
928
420
SAW
1st+2nd+3rd L:strip
1st L:deposit
2nd L:deposit
3rd L:deposit
SOUDOTAPE 420
SOUDOTAPE 420
SOUDOTAPE 420
SOUDOTAPE 420
+
+
+
RECORD RT 159
RECORD RT 159
RECORD RT 159
0,330 0,4 0,4 13,6 bal.
0,190 0,2 0,7 9,2 bal. 45HRc 750 28 12 4,7 3,8 0,15 14 31,7 0,47 733
0,200
0,200
0,2
0,2
0,8
0,8
11,6
12,2
bal.
bal.
45HRc 750 28 12 4,7 3,6 0,14 14 31,7 0,50 774
50HRc 750 28 12 4,7 3,5 0,14 14 31,7 0,51 796
1st+2nd+3rd L:strip
1st L:deposit
2nd L:deposit
3rd L:deposit
SOUDOTAPE 420
SOUDOTAPE 420
SOUDOTAPE 420
SOUDOTAPE 420
+
+
+
RECORD RT 155
RECORD RT 155
RECORD RT 155
0,330
0,220
0,230
0,230
0,4
0,5
0,3
0,2
0,4
0,8
0,9
1,0
13,6 bal.
bal.
bal.
bal.
8,8 50HRc 900 26 12 4,7 4,1 0,16 17 38,0 0,53 815
11,9
12,9
50HRc
50HRc
900
900
26
26
12
12
4,7
4,7
3,8
3,8
0,15
0,15
17
17
38,0
38,0
0,57
0,57
879
879
ESW
1st+2nd L:strip
1st L:deposit
2nd L:deposit
SOUDOTAPE 420
SOUDOTAPE 420
SOUDOTAPE 420
+
+
RECORD EST 426
RECORD EST 426
0,330
0,290
0,310
0,4
0,4
0,3
0,4
0,4
0,2
13,6
10,6
12,6
bal.
bal.
bal.
50HRc
50HRc
1400
1400
24
24
24
24
9,4
9,4
4,4
4,2
0,17
0,17
27
27
59,2
59,2
0,76
0,80
1182
1238
420 Mo ESW
1st+2nd+3rd L:strip
1st L:deposit
2nd L:deposit
3rd L:deposit
SOUDOTAPE 420
SOUDOTAPE 420
SOUDOTAPE 420
SOUDOTAPE 420
+
+
+
RECORD EST 423
RECORD EST 423
RECORD EST 423
0,330
0,270
0,280
0,290
0,4
0,4
0,2
0,3
0,4
0,2
0,1
0,1
13,6
10,5
12,8
12,9
1,4
1,8
1,8
bal.
bal.
bal.
bal.
50HRc
50HRc
50HRc
1250
1250
1250
24
24
24
17
17
17
6,7
6,7
6,7
4,3
4,2
4,2
0,17
0,17
0,17
24
24
24
52,8
52,8
52,8
0,70
0,71
0,71
1079
1105
1105
14Cr2Ni1MoNb
ESW1st L:strip
1st L:deposit
SOUDOTAPE 430 (4)
SOUDOTAPE 430 (4) + RECORD EST 743
0,045
0,140
0,4
0,2
0,3
0,2
16,2
13,0
0,1
2,2
0,02
0,8 0,2
bal.
bal. 0,33 v 45HRc 600 26 18 7,1 4,0 0,16 11,5 25,4 0,36 557
SAW
1st+2nd+3rd L:strip
1st L:deposit
2nd L:deposit
3rd L:deposit
SOUDOTAPE 430 0,045 0,4 0,3 16,2 0,1 0,02 bal.
SOUDOTAPE 430 + RECORD RT 177 0,180 0,6 0,5 11,1 2,0 1,0 0,3 bal. 0,31 v 45HRc 650 27 13 5,1 3,5 0,14 12,5 27,5 0,44 690
SOUDOTAPE 430 + RECORD RT 177 0,170 0,5 0,6 13,3 2,3 1,1 0,3 bal. 0,32 v 45HRc 650 27 13 5,1 3,5 0,14 12,5 27,5 0,44 690
SOUDOTAPE 430 + RECORD RT 177 0,175 0,6 0,5 13,8 2,4 1,2 0,3 bal. 0,33 v 45HRc 650 27 13 5,1 3,5 0,14 12,5 27,5 0,44 690
dEPoSIT TyPES1 BI LoW aLLoy & maRTEnSITIC I overlaying
-
LoW
aLLo
y & ma
RTEn
SITIC
dEPo
SIT TyP
ES
@
TYPE OFDEPOSITED ALLOY
WELDINGPROCESS LAYER
TYPE OF STRIP (60 x 0,5 mm) TYPE OF FLUX
CHEMICAL ANALYSES on a 0,2% C plate(typical) (weight - %)
WELDING PARAMETERS (60 x 0,5 mm)
LAYER THICKNESS DEPOSITION RATE
SOUDOTAPE + RECORD C Mn Si Cr Ni Mo N Nb Fe Others Hardness A V cm/min inch/min mm inch kg/h lbs/h m/h inch/h
410
SAW
1st+2nd+3rd L:strip
1st L:deposit
2nd L:deposit
SOUDOTAPE 430
SOUDOTAPE 430
SOUDOTAPE 430
+
+
RECORD RT 155
RECORD RT 155
0,045
0,083
0,075
0,4
0,5
0,4
0,3
0,7
0,8
16,2
10,8
13,4
0,1 bal.
bal.
bal.
340HB
260HB
900
900
26
26
12
12
4,7
4,7
4,1
3,8
1,61
0,15
17
17
38,0
38,0
0,53
0,57
815
879
ESW1st L:strip
1st L:deposit
SOUDOTAPE 430
SOUDOTAPE 430 + RECORD EST 122
0,045
0,055
0,4
0,4
0,3
0,5
16,2
12,9
0,1 bal.
bal. 280HB 1250 24 20 7,9 4,5 0,18 24 52,8 0,67 1031
410HC SAW
1st+2nd L:strip
1st L:deposit
2nd L: deposit
SOUDOTAPE 420
SOUDOTAPE 420
SOUDOTAPE 420
+
+
RECORD RT 356
RECORD RT 356
0,330
0,290
0,310
0,4
0,7
0,6
0,4
0,7
0,7
13,6
11,0
12,6
bal.
bal.
bal.
50HRc
55HRc
1100
1100
26
26
12
14
4,7
5,5
5,0
4,4
0,20
0,17
21,1
21,1
46,5
46,5
0,53
0,60
817
928
420
SAW
1st+2nd+3rd L:strip
1st L:deposit
2nd L:deposit
3rd L:deposit
SOUDOTAPE 420
SOUDOTAPE 420
SOUDOTAPE 420
SOUDOTAPE 420
+
+
+
RECORD RT 159
RECORD RT 159
RECORD RT 159
0,330 0,4 0,4 13,6 bal.
0,190 0,2 0,7 9,2 bal. 45HRc 750 28 12 4,7 3,8 0,15 14 31,7 0,47 733
0,200
0,200
0,2
0,2
0,8
0,8
11,6
12,2
bal.
bal.
45HRc 750 28 12 4,7 3,6 0,14 14 31,7 0,50 774
50HRc 750 28 12 4,7 3,5 0,14 14 31,7 0,51 796
1st+2nd+3rd L:strip
1st L:deposit
2nd L:deposit
3rd L:deposit
SOUDOTAPE 420
SOUDOTAPE 420
SOUDOTAPE 420
SOUDOTAPE 420
+
+
+
RECORD RT 155
RECORD RT 155
RECORD RT 155
0,330
0,220
0,230
0,230
0,4
0,5
0,3
0,2
0,4
0,8
0,9
1,0
13,6 bal.
bal.
bal.
bal.
8,8 50HRc 900 26 12 4,7 4,1 0,16 17 38,0 0,53 815
11,9
12,9
50HRc
50HRc
900
900
26
26
12
12
4,7
4,7
3,8
3,8
0,15
0,15
17
17
38,0
38,0
0,57
0,57
879
879
ESW
1st+2nd L:strip
1st L:deposit
2nd L:deposit
SOUDOTAPE 420
SOUDOTAPE 420
SOUDOTAPE 420
+
+
RECORD EST 426
RECORD EST 426
0,330
0,290
0,310
0,4
0,4
0,3
0,4
0,4
0,2
13,6
10,6
12,6
bal.
bal.
bal.
50HRc
50HRc
1400
1400
24
24
24
24
9,4
9,4
4,4
4,2
0,17
0,17
27
27
59,2
59,2
0,76
0,80
1182
1238
420 Mo ESW
1st+2nd+3rd L:strip
1st L:deposit
2nd L:deposit
3rd L:deposit
SOUDOTAPE 420
SOUDOTAPE 420
SOUDOTAPE 420
SOUDOTAPE 420
+
+
+
RECORD EST 423
RECORD EST 423
RECORD EST 423
0,330
0,270
0,280
0,290
0,4
0,4
0,2
0,3
0,4
0,2
0,1
0,1
13,6
10,5
12,8
12,9
1,4
1,8
1,8
bal.
bal.
bal.
bal.
50HRc
50HRc
50HRc
1250
1250
1250
24
24
24
17
17
17
6,7
6,7
6,7
4,3
4,2
4,2
0,17
0,17
0,17
24
24
24
52,8
52,8
52,8
0,70
0,71
0,71
1079
1105
1105
14Cr2Ni1MoNb
ESW1st L:strip
1st L:deposit
SOUDOTAPE 430 (4)
SOUDOTAPE 430 (4) + RECORD EST 743
0,045
0,140
0,4
0,2
0,3
0,2
16,2
13,0
0,1
2,2
0,02
0,8 0,2
bal.
bal. 0,33 v 45HRc 600 26 18 7,1 4,0 0,16 11,5 25,4 0,36 557
SAW
1st+2nd+3rd L:strip
1st L:deposit
2nd L:deposit
3rd L:deposit
SOUDOTAPE 430 0,045 0,4 0,3 16,2 0,1 0,02 bal.
SOUDOTAPE 430 + RECORD RT 177 0,180 0,6 0,5 11,1 2,0 1,0 0,3 bal. 0,31 v 45HRc 650 27 13 5,1 3,5 0,14 12,5 27,5 0,44 690
SOUDOTAPE 430 + RECORD RT 177 0,170 0,5 0,6 13,3 2,3 1,1 0,3 bal. 0,32 v 45HRc 650 27 13 5,1 3,5 0,14 12,5 27,5 0,44 690
SOUDOTAPE 430 + RECORD RT 177 0,175 0,6 0,5 13,8 2,4 1,2 0,3 bal. 0,33 v 45HRc 650 27 13 5,1 3,5 0,14 12,5 27,5 0,44 690
12 I 13
-
All given values are typical
dEPo
SIT TyP
ESLo
W aL
Loy & ma
RTEn
SITIC
@
TYPE OFDEPOSITED ALLOY
WELDINGPROCESS LAYER
TYPE OF STRIP (60 x 0,5 mm) TYPE OF FLUX
CHEMICAL ANALYSES on a 0,2% C plate(typical) (weight - %)
WELDING PARAMETERS (60 x 0,5 mm)
LAYER THICKNESS DEPOSITION RATE
SOUDOTAPE + RECORD C Mn Si Cr Ni Mo N Nb Fe Others Hardness A V cm/min inch/min mm inch kg/h lbs/h m/h inch/h
14Cr2Ni1Mo
SAW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
+++
RECORD RT 152RECORD RT 152RECORD RT 152
0,0450,0680,0370,033
0,40,60,50,5
0,30,60,90,9
16,212,213,914,0
0,12,93,83,8
0,020,70,90,9
bal.bal.bal.bal.
405HB390HB385HB
650650650
272727
131313
5,15,15,1
3,53,53,5
0,140,140,14
121212
27,527,527,5
0,440,440,44
690690690
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
+++
RECORD RT 161RECORD RT 161RECORD RT 161
0,0450,1420,1490,137
0,40,60,50,5
0,30,81,01,0
16,211,613,614,3
0,11,11,51,5
0,020,40,50,5
bal.bal.bal.bal.
45 HRc45 HRc45 HRc
700700700
272727
131313
5,15,15,1
3,83,83,8
0,150,150,15
131313
29,629,629,6
0,440,440,44
684684684
ESW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
+++
RECORD EST 452RECORD EST 452RECORD EST 452
0,0450,0620,0520,045
0,40,50,30,3
0,30,40,40,4
16,211,714,114,8
0,13,03,33,6
0,020,40,40,5
bal.bal.bal.bal.
40 HRc40 HRc40 HRc
110011001100
242424
161616
6,36,36,3
43,53,5
0,160,140,14
212121
46,546,546,5
0,660,750,75
102111671167
14Cr4Ni1Mo
SAW1st+2nd L:strip1st L:deposit2nd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
++
RECORD RT 162RECORD RT 162
0,0450,0540,039
0,40,60,5
0,31,01,1
16,213,116,2
0,14,05,3
0,020,70,9
bal.bal.bal.
40 HRc35 HRc
650650
2727
1313
5,15,1
33
0,120,12
1212
27,527,5
0,520,52
805805
ESW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
+++
RECORD EST 453RECORD EST 453RECORD EST 453
0,0450,0580,0450,041
0,40,30,20,2
0,30,30,30,3
16,212,514,314,6
0,13,34,54,6
0,020,81,01,1
bal.bal.bal.bal.
40 HRc40 HRc40 HRc
900900900
242424
161616
6,36,36,3
444
0,160,160,16
171717
38,038,038,0
0,540,540,54
835835835
13Cr3Ni1MoNbv SAW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
+++
RECORD RT 742RECORD RT 742RECORD RT 742
0,0450,0850,0900,090
0,40,40,30,3
0,30,80,90,9
16,212,013,013,5
0,12,02,32,4
0,020,91,01,0
0,10,10,2
bal.bal.bal.bal.
0,10v0,13v0,15v
40HRc40HRc40HRc
800800800
272727
131313
5,15,15,1
333
0,120,120,12
151515
33,833,833,8
0,640,640,64
990990990
1st+2nd+3rd L:strip2nd L:deposit3rd L:deposit
SOUDOTAPE 410LSOUDOTAPE 410LSOUDOTAPE 410L
++
RECORD RT 157RECORD RT 157
0,0250,1400,140
0,40,30,3
0,40,80,9
12,711,812,0
2,62,5
1,41,3
0,30,3
bal.bal.bal.
0,27W0,27W
40HRc45HRc
900900
2626
1313
5,15,1
3,83,5
0,150,14
1717
38,038,0
0,570,62
879955
13Cr6Ni2Mo SAW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE 430LSOUDOTAPE 430LSOUDOTAPE 430LSOUDOTAPE 430L
+++
RECORD RT 168RECORD RT 168RECORD RT 168
0,0150,0750,0270,017
0,40,40,30,2
0,30,60,70,8
16,49,512,112,9
0,13,94,75,2
0,022,02,52,6
bal.bal.bal.bal. 35 HRc
800800800
262626
161616
6,36,36,3
2,82,82,8
0,110,110,11
15,315,315,3
33,833,833,8
0,680,680,68
106110611061
430
SAW1st+2nd L:strip2nd L:deposit3rd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
++
RECORD RT 159RECORD RT 159
0,0450,0600,053
0,40,30,2
0,30,60,9
16,214,115,0
0,1 bal.bal.bal.
21HRC20HRC
750750
2828
1212
4,74,7
3,93,9
0,150,15
14,414,4
31,731,7
0,460,46
714714
ESW1st+2nd L:strip2nd L:deposit
SOUDOTAPE 430SOUDOTAPE 430 + RECORD EST 122
0,0450,067
0,40,4
0,30,5
16,215,3
0,10,1
bal.bal. 22HRC 1250 24 17 6,7 4,5 0,18 24,0 52,8 0,67 1031
17 Cr
SAW1st+2nd L:strip1st L:deposit2nd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
++
RECORD RT 179RECORD RT 179
0,0450,0600,071
0,40,40,5
0,31,01,1
16,215,017,3
0,1 bal.bal.bal.
900900
2424
1515
5,95,9
4,14,1
0,160,16
17,317,3
38,038,0
0,530,53
815815
ESW1st+2nd L:strip1st L:deposit2nd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
++
RECORD EST 127RECORD EST 127
0,0450,0550,050
0,40,40,4
0,30,50,6
16,214,517,2
0,1 bal.bal.bal.
12501250
2424
2020
7,97,9
4,54,5
0,180,18
2424
52,852,8
0,670,67
10311031
dEPoSIT TyPES1 BI LoW aLLoy & maRTEnSITIC I overlaying (continuation)
-
LoW
aLLo
y & ma
RTEn
SITIC
dEPo
SIT TyP
ES
@
TYPE OFDEPOSITED ALLOY
WELDINGPROCESS LAYER
TYPE OF STRIP (60 x 0,5 mm) TYPE OF FLUX
CHEMICAL ANALYSES on a 0,2% C plate(typical) (weight - %)
WELDING PARAMETERS (60 x 0,5 mm)
LAYER THICKNESS DEPOSITION RATE
SOUDOTAPE + RECORD C Mn Si Cr Ni Mo N Nb Fe Others Hardness A V cm/min inch/min mm inch kg/h lbs/h m/h inch/h
14Cr2Ni1Mo
SAW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
+++
RECORD RT 152RECORD RT 152RECORD RT 152
0,0450,0680,0370,033
0,40,60,50,5
0,30,60,90,9
16,212,213,914,0
0,12,93,83,8
0,020,70,90,9
bal.bal.bal.bal.
405HB390HB385HB
650650650
272727
131313
5,15,15,1
3,53,53,5
0,140,140,14
121212
27,527,527,5
0,440,440,44
690690690
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
+++
RECORD RT 161RECORD RT 161RECORD RT 161
0,0450,1420,1490,137
0,40,60,50,5
0,30,81,01,0
16,211,613,614,3
0,11,11,51,5
0,020,40,50,5
bal.bal.bal.bal.
45 HRc45 HRc45 HRc
700700700
272727
131313
5,15,15,1
3,83,83,8
0,150,150,15
131313
29,629,629,6
0,440,440,44
684684684
ESW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
+++
RECORD EST 452RECORD EST 452RECORD EST 452
0,0450,0620,0520,045
0,40,50,30,3
0,30,40,40,4
16,211,714,114,8
0,13,03,33,6
0,020,40,40,5
bal.bal.bal.bal.
40 HRc40 HRc40 HRc
110011001100
242424
161616
6,36,36,3
43,53,5
0,160,140,14
212121
46,546,546,5
0,660,750,75
102111671167
14Cr4Ni1Mo
SAW1st+2nd L:strip1st L:deposit2nd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
++
RECORD RT 162RECORD RT 162
0,0450,0540,039
0,40,60,5
0,31,01,1
16,213,116,2
0,14,05,3
0,020,70,9
bal.bal.bal.
40 HRc35 HRc
650650
2727
1313
5,15,1
33
0,120,12
1212
27,527,5
0,520,52
805805
ESW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
+++
RECORD EST 453RECORD EST 453RECORD EST 453
0,0450,0580,0450,041
0,40,30,20,2
0,30,30,30,3
16,212,514,314,6
0,13,34,54,6
0,020,81,01,1
bal.bal.bal.bal.
40 HRc40 HRc40 HRc
900900900
242424
161616
6,36,36,3
444
0,160,160,16
171717
38,038,038,0
0,540,540,54
835835835
13Cr3Ni1MoNbv SAW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
+++
RECORD RT 742RECORD RT 742RECORD RT 742
0,0450,0850,0900,090
0,40,40,30,3
0,30,80,90,9
16,212,013,013,5
0,12,02,32,4
0,020,91,01,0
0,10,10,2
bal.bal.bal.bal.
0,10v0,13v0,15v
40HRc40HRc40HRc
800800800
272727
131313
5,15,15,1
333
0,120,120,12
151515
33,833,833,8
0,640,640,64
990990990
1st+2nd+3rd L:strip2nd L:deposit3rd L:deposit
SOUDOTAPE 410LSOUDOTAPE 410LSOUDOTAPE 410L
++
RECORD RT 157RECORD RT 157
0,0250,1400,140
0,40,30,3
0,40,80,9
12,711,812,0
2,62,5
1,41,3
0,30,3
bal.bal.bal.
0,27W0,27W
40HRc45HRc
900900
2626
1313
5,15,1
3,83,5
0,150,14
1717
38,038,0
0,570,62
879955
13Cr6Ni2Mo SAW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE 430LSOUDOTAPE 430LSOUDOTAPE 430LSOUDOTAPE 430L
+++
RECORD RT 168RECORD RT 168RECORD RT 168
0,0150,0750,0270,017
0,40,40,30,2
0,30,60,70,8
16,49,512,112,9
0,13,94,75,2
0,022,02,52,6
bal.bal.bal.bal. 35 HRc
800800800
262626
161616
6,36,36,3
2,82,82,8
0,110,110,11
15,315,315,3
33,833,833,8
0,680,680,68
106110611061
430
SAW1st+2nd L:strip2nd L:deposit3rd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
++
RECORD RT 159RECORD RT 159
0,0450,0600,053
0,40,30,2
0,30,60,9
16,214,115,0
0,1 bal.bal.bal.
21HRC20HRC
750750
2828
1212
4,74,7
3,93,9
0,150,15
14,414,4
31,731,7
0,460,46
714714
ESW1st+2nd L:strip2nd L:deposit
SOUDOTAPE 430SOUDOTAPE 430 + RECORD EST 122
0,0450,067
0,40,4
0,30,5
16,215,3
0,10,1
bal.bal. 22HRC 1250 24 17 6,7 4,5 0,18 24,0 52,8 0,67 1031
17 Cr
SAW1st+2nd L:strip1st L:deposit2nd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
++
RECORD RT 179RECORD RT 179
0,0450,0600,071
0,40,40,5
0,31,01,1
16,215,017,3
0,1 bal.bal.bal.
900900
2424
1515
5,95,9
4,14,1
0,160,16
17,317,3
38,038,0
0,530,53
815815
ESW1st+2nd L:strip1st L:deposit2nd L:deposit
SOUDOTAPE 430SOUDOTAPE 430SOUDOTAPE 430
++
RECORD EST 127RECORD EST 127
0,0450,0550,050
0,40,40,4
0,30,50,6
16,214,517,2
0,1 bal.bal.bal.
12501250
2424
2020
7,97,9
4,54,5
0,180,18
2424
52,852,8
0,670,67
10311031
14 I 15
-
TYPE OFDEPOSITED ALLOY
WELDINGPROCESS LAYER
TYPE OF STRIP (60 x 0,5 mm) TYPE OF FLUX
CHEMICAL ANALYSES on a 0,2% C plate(typical) (weight - %)
WELDING PARAMETERS (60 x 0,5 mm) LAYER THICKNESS DEPOSITION RATE
SOUDOTAPE + RECORD C Mn Si Cr Ni Mo N Nb Fe FN* A V cm/min inch/min mm inch kg/h lbs/h m/h inch/h
307 ESW1st+2nd L:strip1st L:deposit2nd L:deposit
SOUDOTAPE 308 L 0,013 1,7 0,4 20,3 10,4 bal.SOUDOTAPE 308 L + RECORD EST 307 0,079 4,9 0,5 17,7 8,8 bal. 1250 24 17 6,7 4,5 0,18 24 52,8 0,67 1031SOUDOTAPE 308 L + RECORD EST 307 0,071 5,3 0,6 18,6 9,2 bal. 1250 24 17 6,7 4,5 0,18 24 52,8 0,67 1031
308 L
SAW
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 L SOUDOTAPE 308 LSOUDOTAPE 308 L
0,0120,0370,0130,022
1,81,61,71,6
0,40,80,40,8
23,719,720,319,7
13,310,710,410,2
0,1 0,048 bal.bal.bal.bal.
+ RECORD INT 101 6 750 27 12 4,7 4,2 0,17 14,4 31,7 0,43 6630,1 0,040
+ RECORD INT 101 7 750 27 12 4,7 4,1 0,16 14,4 31,7 0,44 6791st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 308 LSOUDOTAPE 308 L
0,0120,0450,0130,030
1,80,91,71,0
0,40,80,40,8
23,719,320,319,5
13,310,610,410,2
0,1 0,048 bal.bal.bal.bal.
+ RECORD INT 109 4 900 28 12 4,7 4,5 0,18 17,3 38,0 0,48 7430,1 0,040
+ RECORD INT 109 6 900 28 12 4,7 4,2 0,17 17,3 38,0 0,51 7961st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 L Q5SOUDOTAPE 309 L Q5SOUDOTAPE 308 L Q5SOUDOTAPE 308 L Q5
0,0120,0530,0130,030
1,81,51,71,5
0,40,70,40,9
23,718,020,319,3
13,39,510,49,9
0,1 0,048 bal.bal.bal.
+ RECORD 9v308T1 Q5 2,4 750 26 14 5,5 4,1 0,16 14,4 31,7 0,44 6790,1 0,040
+ RECORD 8B308T2 Q5 bal. 8 750 26 12 4,7 3,9 0,15 14,4 31,7 0,46 714
ESW
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309LSOUDOTAPE 308 LSOUDOTAPE 308 L
0,0120,0350,0130,020
1,81,31,71,4
0,40,60,40,6
23,719,220,319,3
13,310,610,410,2
0,1 0,048 bal.bal.bal.bal.
+ RECORD EST 122 6 1250 24 16 6,3 4,9 0,19 24,0 52,8 0,61 9470,1 0,040
+ RECORD EST 122 8 1250 24 16 6,3 4,5 0,18 24,0 52,8 0,67 10311st L:strip1st L:deposit
SOUDOTAPE 22.11 LSOUDOTAPE 22.11 L
0,0100,029
1,81,1
0,30,5
21,218,5
11,39,7
0,1 0,0350,028
bal.bal.+ RECORD EST 122 5 1250 24 15 5,9 5 0,20 24,0 52,8 0,60 928
ESWSingle layer
1st L:strip1st L:deposit
SOUDOTAPE 308 LSOUDOTAPE 308 L
0,0130,024
1,71,3
0,40,4
20,319,8
10,410,0
0,1 0,040 bal.bal.+ RECORD EST 308-1 7 1250 24 18 7,1 4 0,16 24,0 52,8 0,75 1160
ESW High speed
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 308 LSOUDOTAPE 308 L
0,0120,0500,0130,025
1,81,51,71,3
0,40,50,40,4
23,718,420,319,2
13,310,210,410,1
0,1 0,048 bal.bal.bal.bal.
+ RECORD EST 136 2 1450 24 35 13,8 3,1 0,12 27,8 61,3 1,12 17370,1 0,040
+ RECORD EST 136 6 1450 24 35 13,8 3 0,12 27,8 61,3 1,16 1795
316 L
SAW
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 316 LSOUDOTAPE 316 L
0,0120,0400,0140,025
1,81,61,71,5
0,40,90,40,5
23,719,818,318,3
13,311,012,612,2
0,1 0,048 bal.bal.bal.bal.
+ RECORD INT 101 4 750 26 14 5,5 4,2 0,17 14,4 31,7 0,43 6632,92,4
0,045+ RECORD INT 101 7 750 26 14 5,5 3,7 0,15 14,4 31,7 0,49 753
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 316 LSOUDOTAPE 316 L
0,0120,0580,0140,029
1,80,81,70,7
0,40,80,40,9
23,718,318,318,6
13,39,612,611,7
0,10,12,92,0
0,048 bal.bal.bal.bal.
+ RECORD INT 109 2 750 28 13 5,1 3,5 0,14 14,4 31,7 0,51 7960,045
+ RECORD INT 109 5 750 28 13 5,1 3,5 0,14 14,4 31,7 0,51 796
ESW
1st L:strip1st L:deposit
SOUDOTAPE 21.13.3 LSOUDOTAPE 21.13.3 L
0,0140,030
1,71,4
0,30,4
20,318,5
14,212,4
2,92,5
0,033 bal.bal.+ RECORD EST 115P 5 1250 24 16 6,3 5 0,20 24,0 52,8 0,60 928
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 316 LSOUDOTAPE 316 L
0,0120,0460,0140,021
1,81,41,71,5
0,40,50,40,6
23,720,618,318,8
13,310,812,612,2
0,10,22,92,4
0,048 bal.bal.bal.bal.
+ RECORD EST 122 7,5 1250 24 20 7,9 3,6 0,14 24,0 52,8 0,83 12890,0450,046+ RECORD EST 122 7 1250 24 20 7,9 3,6 0,14 24,0 52,8 0,83 1289
1st L:strip1st L:deposit
SOUDOTAPE 21.13.3 LSOUDOTAPE 21.13.3 L
0,0140,025
1,71,3
0,30,4
20,318,2
14,212,6
2,92,6
0,033 bal.bal.+ RECORD EST 122 6 1250 24 16 6,3 5 0,20 24,0 52,8 0,60 928
ESWSingle layer
1st L:strip1st L:deposit
SOUDOTAPE 316 LSOUDOTAPE 316 L
0,0140,020
1,71,2
0,40,3
18,319,4
12,612,8
2,92,6
0,0450,058
bal.bal.+ RECORD EST 316-1 6,5 1250 24 16 6,3 4,8 0,19 24,0 52,8 0,62 967
ESWHigh speed
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 316 LSOUDOTAPE 316 L
0,0120,0500,0140,025
1,81,51,71,4
0,40,50,40,4
23,718,418,318,2
13,310,212,612,0
0,1 0,048 bal.bal.bal.bal.
+ RECORD EST 136 2 1450 24 35 13,8 3,1 0,12 27,8 61,3 1,12 17372,92,3
0,0450,046+ RECORD EST 136 5 1450 24 35 13,8 3 0,12 27,8 61,3 1,16 1795
All given values are typical*Ferrite measurement with Fischer Ferritescope according to AWS A4.2
dEPo
SIT TyP
ESSTaInL
ESS STEEL
I STaInLESS STEEL2dEPoSIT TyPES
-
TYPE OFDEPOSITED ALLOY
WELDINGPROCESS LAYER
TYPE OF STRIP (60 x 0,5 mm) TYPE OF FLUX
CHEMICAL ANALYSES on a 0,2% C plate(typical) (weight - %)
WELDING PARAMETERS (60 x 0,5 mm) LAYER THICKNESS DEPOSITION RATE
SOUDOTAPE + RECORD C Mn Si Cr Ni Mo N Nb Fe FN* A V cm/min inch/min mm inch kg/h lbs/h m/h inch/h
307 ESW1st+2nd L:strip1st L:deposit2nd L:deposit
SOUDOTAPE 308 L 0,013 1,7 0,4 20,3 10,4 bal.SOUDOTAPE 308 L + RECORD EST 307 0,079 4,9 0,5 17,7 8,8 bal. 1250 24 17 6,7 4,5 0,18 24 52,8 0,67 1031SOUDOTAPE 308 L + RECORD EST 307 0,071 5,3 0,6 18,6 9,2 bal. 1250 24 17 6,7 4,5 0,18 24 52,8 0,67 1031
308 L
SAW
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 L SOUDOTAPE 308 LSOUDOTAPE 308 L
0,0120,0370,0130,022
1,81,61,71,6
0,40,80,40,8
23,719,720,319,7
13,310,710,410,2
0,1 0,048 bal.bal.bal.bal.
+ RECORD INT 101 6 750 27 12 4,7 4,2 0,17 14,4 31,7 0,43 6630,1 0,040
+ RECORD INT 101 7 750 27 12 4,7 4,1 0,16 14,4 31,7 0,44 6791st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 308 LSOUDOTAPE 308 L
0,0120,0450,0130,030
1,80,91,71,0
0,40,80,40,8
23,719,320,319,5
13,310,610,410,2
0,1 0,048 bal.bal.bal.bal.
+ RECORD INT 109 4 900 28 12 4,7 4,5 0,18 17,3 38,0 0,48 7430,1 0,040
+ RECORD INT 109 6 900 28 12 4,7 4,2 0,17 17,3 38,0 0,51 7961st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 L Q5SOUDOTAPE 309 L Q5SOUDOTAPE 308 L Q5SOUDOTAPE 308 L Q5
0,0120,0530,0130,030
1,81,51,71,5
0,40,70,40,9
23,718,020,319,3
13,39,510,49,9
0,1 0,048 bal.bal.bal.
+ RECORD 9v308T1 Q5 2,4 750 26 14 5,5 4,1 0,16 14,4 31,7 0,44 6790,1 0,040
+ RECORD 8B308T2 Q5 bal. 8 750 26 12 4,7 3,9 0,15 14,4 31,7 0,46 714
ESW
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309LSOUDOTAPE 308 LSOUDOTAPE 308 L
0,0120,0350,0130,020
1,81,31,71,4
0,40,60,40,6
23,719,220,319,3
13,310,610,410,2
0,1 0,048 bal.bal.bal.bal.
+ RECORD EST 122 6 1250 24 16 6,3 4,9 0,19 24,0 52,8 0,61 9470,1 0,040
+ RECORD EST 122 8 1250 24 16 6,3 4,5 0,18 24,0 52,8 0,67 10311st L:strip1st L:deposit
SOUDOTAPE 22.11 LSOUDOTAPE 22.11 L
0,0100,029
1,81,1
0,30,5
21,218,5
11,39,7
0,1 0,0350,028
bal.bal.+ RECORD EST 122 5 1250 24 15 5,9 5 0,20 24,0 52,8 0,60 928
ESWSingle layer
1st L:strip1st L:deposit
SOUDOTAPE 308 LSOUDOTAPE 308 L
0,0130,024
1,71,3
0,40,4
20,319,8
10,410,0
0,1 0,040 bal.bal.+ RECORD EST 308-1 7 1250 24 18 7,1 4 0,16 24,0 52,8 0,75 1160
ESW High speed
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 308 LSOUDOTAPE 308 L
0,0120,0500,0130,025
1,81,51,71,3
0,40,50,40,4
23,718,420,319,2
13,310,210,410,1
0,1 0,048 bal.bal.bal.bal.
+ RECORD EST 136 2 1450 24 35 13,8 3,1 0,12 27,8 61,3 1,12 17370,1 0,040
+ RECORD EST 136 6 1450 24 35 13,8 3 0,12 27,8 61,3 1,16 1795
316 L
SAW
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 316 LSOUDOTAPE 316 L
0,0120,0400,0140,025
1,81,61,71,5
0,40,90,40,5
23,719,818,318,3
13,311,012,612,2
0,1 0,048 bal.bal.bal.bal.
+ RECORD INT 101 4 750 26 14 5,5 4,2 0,17 14,4 31,7 0,43 6632,92,4
0,045+ RECORD INT 101 7 750 26 14 5,5 3,7 0,15 14,4 31,7 0,49 753
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 316 LSOUDOTAPE 316 L
0,0120,0580,0140,029
1,80,81,70,7
0,40,80,40,9
23,718,318,318,6
13,39,612,611,7
0,10,12,92,0
0,048 bal.bal.bal.bal.
+ RECORD INT 109 2 750 28 13 5,1 3,5 0,14 14,4 31,7 0,51 7960,045
+ RECORD INT 109 5 750 28 13 5,1 3,5 0,14 14,4 31,7 0,51 796
ESW
1st L:strip1st L:deposit
SOUDOTAPE 21.13.3 LSOUDOTAPE 21.13.3 L
0,0140,030
1,71,4
0,30,4
20,318,5
14,212,4
2,92,5
0,033 bal.bal.+ RECORD EST 115P 5 1250 24 16 6,3 5 0,20 24,0 52,8 0,60 928
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 316 LSOUDOTAPE 316 L
0,0120,0460,0140,021
1,81,41,71,5
0,40,50,40,6
23,720,618,318,8
13,310,812,612,2
0,10,22,92,4
0,048 bal.bal.bal.bal.
+ RECORD EST 122 7,5 1250 24 20 7,9 3,6 0,14 24,0 52,8 0,83 12890,0450,046+ RECORD EST 122 7 1250 24 20 7,9 3,6 0,14 24,0 52,8 0,83 1289
1st L:strip1st L:deposit
SOUDOTAPE 21.13.3 LSOUDOTAPE 21.13.3 L
0,0140,025
1,71,3
0,30,4
20,318,2
14,212,6
2,92,6
0,033 bal.bal.+ RECORD EST 122 6 1250 24 16 6,3 5 0,20 24,0 52,8 0,60 928
ESWSingle layer
1st L:strip1st L:deposit
SOUDOTAPE 316 LSOUDOTAPE 316 L
0,0140,020
1,71,2
0,40,3
18,319,4
12,612,8
2,92,6
0,0450,058
bal.bal.+ RECORD EST 316-1 6,5 1250 24 16 6,3 4,8 0,19 24,0 52,8 0,62 967
ESWHigh speed
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 316 LSOUDOTAPE 316 L
0,0120,0500,0140,025
1,81,51,71,4
0,40,50,40,4
23,718,418,318,2
13,310,212,612,0
0,1 0,048 bal.bal.bal.bal.
+ RECORD EST 136 2 1450 24 35 13,8 3,1 0,12 27,8 61,3 1,12 17372,92,3
0,0450,046+ RECORD EST 136 5 1450 24 35 13,8 3 0,12 27,8 61,3 1,16 1795
All given values are typical*Ferrite measurement with Fischer Ferritescope according to AWS A4.2
STaInL
ESS STEEL
dEPo
SIT TyP
ES
16 I 17
-
dEPo
SIT TyP
ESSTaInL
ESS STEEL
TYPE OFDEPOSITED ALLOY
WELDINGPROCESS LAYER
TYPE OF STRIP (60 x 0,5 mm) TYPE OF FLUX
CHEMICAL ANALYSES on a 0,2% C plate(typical) (weight - %)
WELDING PARAMETERS (60 x 0,5 mm) LAYER THICKNESS DEPOSITION RATE
SOUDOTAPE + RECORD C Mn Si Cr Ni Mo N Nb Fe FN* A V cm/min inch/min mm inch kg/h lbs/h m/h inch/h
347
SAW
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 24.12 LNbSOUDOTAPE 24.12 LNbSOUDOTAPE 347SOUDOTAPE 347
+
+
RECORD INT 109
RECORD INT 109
0,0170,0500,0160,035
2,10,81,70,8
0,40,80,40,9
23,718,619,719,2
12,510,010,510,0
0,2
0,1
0,0500,0400,0460,040
0,70,30,50,4
bal.bal.bal.bal.
4
6
750
750
28
28
15
13
5,9
5,1
3,3
3,8
0,13
0,15
14,4
14,4
31,7
31,7
0,58
0,50
899
779
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 347SOUDOTAPE 347
+
+
RECORD INT 109
RECORD INT 109
0,0120,0450,0160,035
1,80,91,70,8
0,40,80,40,9
23,718,219,719,3
13,39,710,510,0
0,1
0,1
0,048
0,046 0,50,4
bal.bal.bal.bal.
2
6
750
750
28
28
15
15
5,9
5,9
3,3
3,1
0,13
0,12
14,4
14,4
31,7
31,7
0,54
0,58
844
898
ESW1st L:strip1st L:deposit
SOUDOTAPE 21.11 LNbSOUDOTAPE 21.11 LNb RECORD EST 122
0,0160,030
1,81,4
0,30,4
21,419,0
11,310,1
0,03 0,036 0,70,5
bal.bal. 7 1250 24 17 6,7 4,8 0,19 24,0 52,8 0,62 967+
ESW
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 347SOUDOTAPE 347
+
+
RECORD EST 122
RECORD EST 122
0,0120,0330,0160,015
1,81,21,71,3
0,40,40,40,4
23,719,319,719,1
13,310,610,510,5
0,1
0,1
0,0480,0340,0460,030
0,50,4
bal.bal.bal.bal. 5
1250
1250
24
24
17
17
7
7
5
5
0,20
0,20
24
24
52,8
52,8
0,60
0,60
928
928ESW
Single layer1st L:strip1st L:deposit
SOUDOTAPE 347SOUDOTAPE 347
+
RECORD EST 347-1
0,0160,025
1,71,2
0,40,4
19,718,4
10,59,7
0,1 0,046 0,50,3
bal.bal.
6
1250
24
18
7,1
4
0,16
24,0
52,8
0,75
1160
ESW High speed
1st L:strip1st L:deposit
SOUDOTAPE 21.11 LNbSOUDOTAPE 21.11 LNb
+
RECORD EST 129
0,0160,035
1,81,4
0,30,3
21,418,4
11,39,5
0,03 0,0360,030
0,70,5
bal.bal.
4
1350
24
22
8,7
4,2
0,17
25,9
57,0
0,77
1194
1st L:strip1st L:deposit
SOUDOTAPE 24.12 LNBSOUDOTAPE 24.12 LNB
+
RECORD EST 129
0,0170,040
2,11,3
0,40,4
23,718,9
12,510,4
0,2 0,0500,040
0,70,5
bal.bal.
4
1350
24
30
11,8
3,5
0,14
25,9
57,0
0,92
1432
1st L:strip1st L:deposit
SOUDOTAPE 24.12 LNBSOUDOTAPE 24.12 LNB
+
RECORD EST 136
0,0170,045
2,11,4
0,40,4
23,719,3
12,510,5
0,2 0,0500,040
0,70,5
bal.bal.
5
1450
24
35
13,8
3,1
0,12
27,8
61,3
1,12
1737
1st L:strip1st L:deposit
SOUDOTAPE 21.11 LNBSOUDOTAPE 21.11 LNB
+
RECORD 347-1 HS
0,0160,039
1,81,2
0,30,4
21,418,3
11,39,3
0,03 0,036 0,70,5
bal.bal.
5
1650
24
35
13,8
2,8
0,11
31,6
69,7
1,41
2188
317 L
SAW
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 21.13.3 LSOUDOTAPE 21.13.3 LSOUDOTAPE 316 LSOUDOTAPE 316 L
RECORD INT 101 MO
RECORD INT 101 MO
0,0140,0410,0140,025
1,71,41,71,4
0,30,70,40,7
20,317,918,318,6
14,211,512,612,6
2,92,82,93,1
0,033
0,0450,047
bal.bal.bal.bal.
7,3
7,1
750
750
26
26
11
12
4,3
4,7
4,7
4,2
0,19
0,17
14,4
14,4
31,7
31,7
0,38
0,43
593
663
+
+
ESW
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 21.13.3 LSOUDOTAPE 21.13.3 LSOUDOTAPE 317 LSOUDOTAPE 317 L
+
+
RECORD EST 122
RECORD EST 122
0,0140,0270,0160,015
1,71,31,51,2
0,30,40,40,5
20,318,318,818,5
14,212,713,613,4
2,92,53,53,2
0,0330,0310,045
bal.bal.bal.bal.
4,3
6,3
1250
1250
24
24
18
18
7,1
7,1
4,3
4
0,17
0,16
24,0
24,0
52,8
52,8
0,70
0,75
1079
1160
1st L:strip1st L:deposit2nd L:deposit
SOUDOTAPE 316 LSOUDOTAPE 316 LSOUDOTAPE 316 L
++
RECORD EST 317-2RECORD EST 317-2
0,0140,0220,016
1,71,31,3
0,40,40,4
18,317,019,0
12,612,413,9
2,92,93,3
0,0450,0330,035
bal.bal.bal. 4,7
12501250
2424
1818
7,17,1
4,54,2
0,180,17
25,925,9
57,057,0
0,770,77
11941194
ESWSingle layer
1st L:strip1st L:deposit
SOUDOTAPE 21.13.3 LSOUDOTAPE 21.13.3 L RECORD EST 317-1
0,0140,022
1,71,1
0,30,2
20,318,5
14,213,4
2,93,2
0,0330,030
bal.bal. 7 1350 24 25 9,8 4 0,16 25,9 57,0 0,81 1253+
ESWHigh speed
1st L+2nd L:strip1st L:deposit 2nd L:deposit
SOUDOTAPE 21.13.3 LSOUDOTAPE 21.13.3 LSOUDOTAPE 21.13.3 L
++
RECORD EST 136 MORECORD EST 136 MO
0,0140,0420,021
1,71,21,3
0,30,30,3
20,315,318,2
14,211,013,3
2,92,73,3
0,0330,0310,037
bal.bal.bal.
2,66,6
14001400
2424
3535
13,813,8
3,83,8
0,150,15
26,826,8
59,259,2
0,880,88
13681368
318ESW
1st L: strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 21.11 LNbSOUDOTAPE 21.11 LNbSOUDOTAPE 316 LSOUDOTAPE 316 L
+
+
RECORD EST 130
RECORD EST 130
0,0160,0300,0140,020
1,81,21,71,2
0,30,40,40,6
21,419,018,318,5
11,310,312,612,2
0,032,92,4
0,0360,0450,034
0,70,50,3
bal.bal.bal.bal.
2
5
1250
1250
24
24
17
17
6,7
6,7
5
4,5
0,20
0,18
24,0
24,0
52,8
52,8
0,60
0,67
928
1031
ESWSingle layer
1st L:strip1st L:deposit
SOUDOTAPE 21.13.3 LSOUDOTAPE 21.13.3 L + RECORD EST 130
0,0140,030
1,71,3
0,30,3
20,318,0
14,212,2
2,92,6
0,0330,030
0,3bal.bal. 5,8 1250 24 17 6,7 4,7 0,19 24,0 52,8 0,64 988
All given values are typical*Ferrite measurement with Fischer Ferritescope according to AWS A4.2
(continuation)I STaInLESS STEEL2dEPoSIT TyPES
-
TYPE OFDEPOSITED ALLOY
WELDINGPROCESS LAYER
TYPE OF STRIP (60 x 0,5 mm) TYPE OF FLUX
CHEMICAL ANALYSES on a 0,2% C plate(typical) (weight - %)
WELDING PARAMETERS (60 x 0,5 mm) LAYER THICKNESS DEPOSITION RATE
SOUDOTAPE + RECORD C Mn Si Cr Ni Mo N Nb Fe FN* A V cm/min inch/min mm inch kg/h lbs/h m/h inch/h
347
SAW
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 24.12 LNbSOUDOTAPE 24.12 LNbSOUDOTAPE 347SOUDOTAPE 347
+
+
RECORD INT 109
RECORD INT 109
0,0170,0500,0160,035
2,10,81,70,8
0,40,80,40,9
23,718,619,719,2
12,510,010,510,0
0,2
0,1
0,0500,0400,0460,040
0,70,30,50,4
bal.bal.bal.bal.
4
6
750
750
28
28
15
13
5,9
5,1
3,3
3,8
0,13
0,15
14,4
14,4
31,7
31,7
0,58
0,50
899
779
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 347SOUDOTAPE 347
+
+
RECORD INT 109
RECORD INT 109
0,0120,0450,0160,035
1,80,91,70,8
0,40,80,40,9
23,718,219,719,3
13,39,710,510,0
0,1
0,1
0,048
0,046 0,50,4
bal.bal.bal.bal.
2
6
750
750
28
28
15
15
5,9
5,9
3,3
3,1
0,13
0,12
14,4
14,4
31,7
31,7
0,54
0,58
844
898
ESW1st L:strip1st L:deposit
SOUDOTAPE 21.11 LNbSOUDOTAPE 21.11 LNb RECORD EST 122
0,0160,030
1,81,4
0,30,4
21,419,0
11,310,1
0,03 0,036 0,70,5
bal.bal. 7 1250 24 17 6,7 4,8 0,19 24,0 52,8 0,62 967+
ESW
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 347SOUDOTAPE 347
+
+
RECORD EST 122
RECORD EST 122
0,0120,0330,0160,015
1,81,21,71,3
0,40,40,40,4
23,719,319,719,1
13,310,610,510,5
0,1
0,1
0,0480,0340,0460,030
0,50,4
bal.bal.bal.bal. 5
1250
1250
24
24
17
17
7
7
5
5
0,20
0,20
24
24
52,8
52,8
0,60
0,60
928
928ESW
Single layer1st L:strip1st L:deposit
SOUDOTAPE 347SOUDOTAPE 347
+
RECORD EST 347-1
0,0160,025
1,71,2
0,40,4
19,718,4
10,59,7
0,1 0,046 0,50,3
bal.bal.
6
1250
24
18
7,1
4
0,16
24,0
52,8
0,75
1160
ESW High speed
1st L:strip1st L:deposit
SOUDOTAPE 21.11 LNbSOUDOTAPE 21.11 LNb
+
RECORD EST 129
0,0160,035
1,81,4
0,30,3
21,418,4
11,39,5
0,03 0,0360,030
0,70,5
bal.bal.
4
1350
24
22
8,7
4,2
0,17
25,9
57,0
0,77
1194
1st L:strip1st L:deposit
SOUDOTAPE 24.12 LNBSOUDOTAPE 24.12 LNB
+
RECORD EST 129
0,0170,040
2,11,3
0,40,4
23,718,9
12,510,4
0,2 0,0500,040
0,70,5
bal.bal.
4
1350
24
30
11,8
3,5
0,14
25,9
57,0
0,92
1432
1st L:strip1st L:deposit
SOUDOTAPE 24.12 LNBSOUDOTAPE 24.12 LNB
+
RECORD EST 136
0,0170,045
2,11,4
0,40,4
23,719,3
12,510,5
0,2 0,0500,040
0,70,5
bal.bal.
5
1450
24
35
13,8
3,1
0,12
27,8
61,3
1,12
1737
1st L:strip1st L:deposit
SOUDOTAPE 21.11 LNBSOUDOTAPE 21.11 LNB
+
RECORD 347-1 HS
0,0160,039
1,81,2
0,30,4
21,418,3
11,39,3
0,03 0,036 0,70,5
bal.bal.
5
1650
24
35
13,8
2,8
0,11
31,6
69,7
1,41
2188
317 L
SAW
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 21.13.3 LSOUDOTAPE 21.13.3 LSOUDOTAPE 316 LSOUDOTAPE 316 L
RECORD INT 101 MO
RECORD INT 101 MO
0,0140,0410,0140,025
1,71,41,71,4
0,30,70,40,7
20,317,918,318,6
14,211,512,612,6
2,92,82,93,1
0,033
0,0450,047
bal.bal.bal.bal.
7,3
7,1
750
750
26
26
11
12
4,3
4,7
4,7
4,2
0,19
0,17
14,4
14,4
31,7
31,7
0,38
0,43
593
663
+
+
ESW
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 21.13.3 LSOUDOTAPE 21.13.3 LSOUDOTAPE 317 LSOUDOTAPE 317 L
+
+
RECORD EST 122
RECORD EST 122
0,0140,0270,0160,015
1,71,31,51,2
0,30,40,40,5
20,318,318,818,5
14,212,713,613,4
2,92,53,53,2
0,0330,0310,045
bal.bal.bal.bal.
4,3
6,3
1250
1250
24
24
18
18
7,1
7,1
4,3
4
0,17
0,16
24,0
24,0
52,8
52,8
0,70
0,75
1079
1160
1st L:strip1st L:deposit2nd L:deposit
SOUDOTAPE 316 LSOUDOTAPE 316 LSOUDOTAPE 316 L
++
RECORD EST 317-2RECORD EST 317-2
0,0140,0220,016
1,71,31,3
0,40,40,4
18,317,019,0
12,612,413,9
2,92,93,3
0,0450,0330,035
bal.bal.bal. 4,7
12501250
2424
1818
7,17,1
4,54,2
0,180,17
25,925,9
57,057,0
0,770,77
11941194
ESWSingle layer
1st L:strip1st L:deposit
SOUDOTAPE 21.13.3 LSOUDOTAPE 21.13.3 L RECORD EST 317-1
0,0140,022
1,71,1
0,30,2
20,318,5
14,213,4
2,93,2
0,0330,030
bal.bal. 7 1350 24 25 9,8 4 0,16 25,9 57,0 0,81 1253+
ESWHigh speed
1st L+2nd L:strip1st L:deposit 2nd L:deposit
SOUDOTAPE 21.13.3 LSOUDOTAPE 21.13.3 LSOUDOTAPE 21.13.3 L
++
RECORD EST 136 MORECORD EST 136 MO
0,0140,0420,021
1,71,21,3
0,30,30,3
20,315,318,2
14,211,013,3
2,92,73,3
0,0330,0310,037
bal.bal.bal.
2,66,6
14001400
2424
3535
13,813,8
3,83,8
0,150,15
26,826,8
59,259,2
0,880,88
13681368
318ESW
1st L: strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 21.11 LNbSOUDOTAPE 21.11 LNbSOUDOTAPE 316 LSOUDOTAPE 316 L
+
+
RECORD EST 130
RECORD EST 130
0,0160,0300,0140,020
1,81,21,71,2
0,30,40,40,6
21,419,018,318,5
11,310,312,612,2
0,032,92,4
0,0360,0450,034
0,70,50,3
bal.bal.bal.bal.
2
5
1250
1250
24
24
17
17
6,7
6,7
5
4,5
0,20
0,18
24,0
24,0
52,8
52,8
0,60
0,67
928
1031
ESWSingle layer
1st L:strip1st L:deposit
SOUDOTAPE 21.13.3 LSOUDOTAPE 21.13.3 L + RECORD EST 130
0,0140,030
1,71,3
0,30,3
20,318,0
14,212,2
2,92,6
0,0330,030
0,3bal.bal. 5,8 1250 24 17 6,7 4,7 0,19 24,0 52,8 0,64 988
All given values are typical*Ferrite measurement with Fischer Ferritescope according to AWS A4.2
STaInL
ESS STEEL
dEPo
SIT TyP
ES
18 I 19
-
dEPo
SIT TyP
ESSP
ECIaLSTa
InLESS
STEEL
TYPE OFDEPOSITED ALLOY
WELDINGPROCESS LAYER
TYPE OF STRIP (60 x 0,5 mm) TYPE OF FLUX
CHEMICAL ANALYSES on a 0,2% C plate(typical) (weight - %)
WELDING PARAMETERS (60 x 0,5 mm) LAYER THICKNESS DEPOSITION RATE
SOUDOTAPE + RECORD C Mn Si Cr Ni Mo N Fe Others FN* A V cm/min inch/min mm inch kg/h lbs/h m/h inch/h
310 MM
SAW
1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit
SOUDOTAPE 310 MMSOUDOTAPE 310 MMSOUDOTAPE 310 MMSOUDOTAPE 310 MM
0,0120,0400,0330,025
4,5
3,53,63,7
0,20,60,60,6
25,12123
24,5
2219,821,322,2
2,21,92,02,1
0,130,130,120,12
bal.bal.bal.bal.
+ RECORD 13 BLFTRECORD 13 BLFTRECORD 13 BLFT
750750750
282828
121212
4,74,74,7
4,5
4,14,1
0,180,160,16
14,414,414,4
31,731,731,7
0,40,440,44
619679679
+
+
ESW
1st+2nd L:strip1st L:deposit2nd L:deposit
SOUDOTAPE 310 MMSOUDOTAPE 310 MMSOUDOTAPE 310 MM
0,0120,0450,030
4,5
3,63,8
0,20,40,4
25,121,524
2220
22,5
2,21,82,0
0,130,130,15
bal.bal.bal.
+ RECORD EST 122RECORD EST 122
12001200
2424
1818
7,17,1
4,74,5
0,190,18
23,023,0
50,750,7
0,610,64
948990+
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 310 MMSOUDOTAPE 310 MM
0,0120,0390,0120,014
1,81,34,5
2,8
0,40,50,20,3
23,718,925,127,4
13,310,722
22,7
0,10,02,22,7
0,0480,0530,130,131
bal.bal.bal.bal.
+ RECORD EST 122 1250 24 18 7,1 4 0,16 24,0 52,8 0,75 1160
+ RECORD EST 310 MM-SP 1000 24 16 6,3 4 0,16 19,2 42,3 0,6 928
ESWHigh speed
1st+2nd L:strip1st L:deposit2nd L:deposit
SOUDOTAPE 310 MMSOUDOTAPE 310 MMSOUDOTAPE 310 MM
0,0120,0450,029
4,5
3,33,8
0,20,30,3
25,122,324,3
2220,522,5
2,22,02,3
0,130,110,12
bal.bal.bal.
+ RECORD EST 310 MMRECORD EST 310 MM
15001450
2424
3524
13,89,4
34,5
0,120,18
28,827,8
63,461,3
1,20,77
18571197+
28.23.3 L ESW
1st L:strip1st L:deposit2nd L:strip2nd L:deposit
SOUDOTAPE 309 LSOUDOTAPE 309 LSOUDOTAPE 310 MMSOUDOTAPE 310 MM
0,0120,0340,0120,017
1,81
4,5
3
0,40,40,20,3
23,724,425,128,1
13,314,822
23,4
0,11,12,22,9
0,0480,0530,13
0,096
bal.bal.bal.bal.
+ RECORD EST 310 MM-SP 1000 24 16 6,3 4 0,16 19,2 42,3 0,6 928
+ RECORD EST 310 MM-SP 1000 24 16 6,3 4 0,16 19,2 42,3 0,6 928
Duplex
SAW1st+2nd+3rd L:strip2nd