scope of the mac d project - shte · supplier gerdau gerdau ovako ovako heat treatment quench &...
TRANSCRIPT
![Page 1: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/1.jpg)
1
![Page 2: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/2.jpg)
2
Scope of the MAC D project:
=> Investigate the feasibility of induction hardening of a few demonstrators.
=> Compare rough turning, hob milling and hard turning machining, carburizing steel
vs induction hardening steels.
=> Compare mechanical properties of samples and demonstrators of the two
hardening treatments.
=> Actually manufacture some 20-50 demonstrator parts, w induction hardening.
=> Make comparison of manufacturing costs.
To replace carburizing with induction hardening of transmission components
Method:
![Page 3: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/3.jpg)
3
The use of automotive steels
Heat treatments:
All gears are
carburized
Most shafts as well
Some shafts are
induction hardened
![Page 4: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/4.jpg)
The MAC D project is about:
…moving from here …to here
…as heat treatment route of transmission components
4
![Page 5: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/5.jpg)
5
Consortium
Project facts
Duration: 2011-2014
Budget: GT=1.9 M€
![Page 6: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/6.jpg)
Materials
wt% ppm
Steel
grade
MAC D
Name
C Mn Si S Cr Ni Mo O Ca
18CrMo4 C 0,19 0,81 0,29 0,024 1,06 0,12 0,16 10 7
35CrMo4 QL 0,34 0,81 0,31 0,026 1,12 0,11 0,18 12 8
50CrMo4 QH 0,50 0,68 0,23 0,035 0,98 0,21 0,19 8 2
100Cr6 B 0,97 0,31 0,28 0,012 1,41 0,20 0,06 5 3
6
![Page 7: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/7.jpg)
As-delivered conditions
7
Steel grade 18CrMo4 35CrMo4 50CrMo4 100Cr6
Short name C QL QH B
Supplier Gerdau Gerdau Ovako Ovako
Heat treatment
Quench & tempering I
QL-T1
240 HB
■ QH-T1
350 HB
Quench & tempering II
QL-T2
287 HB
■ QH-T2
315 HB
Annealing**
▲ C-IA
160 HB
B-SA
200 HB
Reference Most attention of R&D
![Page 8: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/8.jpg)
The Basics | The Benefits | The Technology | The Products | The Services | The Applications
The necessity of high hardness prior to
induction hardening (TTA-diagrams)
50CrMo4 (1.7228) Source: Orlich J., Rose A.: Atlas zur Wärmebehandlung der Stähle, Band 3, ZTA-Schaubilder
Transformation-
temperature depends
of:
Heating time
Start structure
M Martensitic
Start structure: 2 4 0 0 1 0 0 0 3 0 0 1 0 0 3 0 1 0 3 1 K / s 0 , 2 2
A c c
A c 3 A c 1
700
800
900
1000
1100
1300
°C
0,1 1 10 100 1.000 10.000 s
P Pearlitic
W Soft annealed
Time
Tem
per
atu
re
![Page 9: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/9.jpg)
9
Steel grade 18CrMo4 35CrMo4 50CrMo4 100Cr6
Short name C QL QH B
Supplier Gerdau-Sidenor
Gerdau-Sidenor Ovako Ovako
Heat treatment
Induction hardening I ▲ C-H1 QL-H1
■ QH-H1
58 HRC
Induction hardening II QL-H2 ■ QH-H2
Through hardening
B-H1
61 HRC
Materials in the hardened state
• … was aimed at a 2nd gear shaft of
Fiat gear box
Reference
Most attention of R&D
![Page 10: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/10.jpg)
Demonstrator component
10
Gear module: 2.35
Outer diameter 168 mm
Helical angle 20°
Current steel 17CrMo7
![Page 11: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/11.jpg)
Rough machining
…was made up of:
- Tool life tests in rough turning
- Tool life tests in experimental gear hobbing
- Tool wear studies and chip study
- Fundamental studies of the intermittent cutting process
characteristics of gear hobbing.
11
![Page 12: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/12.jpg)
Tool life in rough turning
12
50% (!)
![Page 13: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/13.jpg)
Tool wear behaivour in rough turning
13
C-IA (18CrMo4) 160 HB QL-T2 (35CrMo4) 287 HB
![Page 14: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/14.jpg)
14
Gear cutting through experimental simulation
The test mimics:
- Realistic tool life
- Tool wear mechanisms of actual
gear hobs
- The variation in chip thickness
inherent in gear cutting.
![Page 15: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/15.jpg)
15
50%
5
0%
Tool life in gear cutting
![Page 16: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/16.jpg)
Chip breakability
16
C-IA
B-SA
QL-T1
QL-T2
QH-T1
QH-T2
0.1 0.40.3 0.60.2
Dep
tho
f cu
t a
p/ m
m
1
3
2
Feed f / mm0.5
Material: varying Cutting speed: vc = 225 m/min Grade: WC 4215
Tool holder: DCLNL 2525M12 Cooling: Dry Geometry: CNMG120408PM
![Page 17: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/17.jpg)
• Industrial cutting conditions
• Comparison of performance of a CC grade and PCBN
17
Hard part turning
![Page 18: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/18.jpg)
18
Tool life in hard part turning
The realistic steel and
hardness for a gear
application
![Page 19: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/19.jpg)
19
Conclusions green turning, gear hobbing &
hard part turning
• Roughly 50% loss of productivity in rough turning (in this comparison)
Significant improvement in productivity with harder carbide grade (P05).
• Roughly 50% loss of productivity in gear hobbing (in this comparison).
=> A solution is to implement carbide hobbing for sufficient productivity in
gear cutting of 350 HB
• Minimised distortion in induction hardening => Possibility to
minimise/eliminate the need of hard part turning (?)
![Page 20: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/20.jpg)
Mechanical properties and fatigue strength of
the induction hardened 50CrMo4
IMPORTANT: Induction hardening is very geometry dependent. => All
pre-tests should be made on the actually aimed component!
(Though very difficicult in a world that is used to evaluation that is
optimised more to the test geometry than to the heat treatment)
20
![Page 21: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/21.jpg)
Toughness
21
![Page 22: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/22.jpg)
Multiaxial fatigue strength
22
![Page 23: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/23.jpg)
Rotating beam fatigue tests
23
3%
![Page 24: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/24.jpg)
Root testing of actual gear
24
Impossible to line-up fatigue loads
of the helical demonstrator gear =>
spur gear was used in this task
0
5
10
15
20
25
Carburized18CrMo4
Inductionhardened50CrMo4
Fatigue limit [kN]
12%
S=0.025% S=0.035%
![Page 25: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/25.jpg)
Fatigue strength of induction hardened 50CrMo4
Summary
• Results very dependent on geometry!
• Fatigue strength of induction hardened 50CrMo4 is on par or (probably)
slightly better than that of carburized 18CrMo4.
• Important to compare steels of similar sulphur content!
(18CrMo4: S=0.025% 50CrMo4: S=0.035%)
25
![Page 26: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/26.jpg)
Demonstrator component
26
Gear module: 2.35
Outer diameter 168 mm
Helical angle 20°
Current steel 17CrMo7
![Page 27: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/27.jpg)
Manufacturing steps
27
No. Sequence Operation
1 Supply of steel as bar from the steel producer to
the forging company.
2 Blank forging & heat treatment
3 Arrival of gear blank at Fiat Powertrain.
4 Turning operations. (& dimensional check) OP10
5 Gear cutting. OP30
6 Chamfering and snagging. OP40
7 Washing. OP50
8 Drilling. OP60
9 Washing. OP70
10 Carburizing. OP80
11 Shot blasting of gear roots. OP80
12 Fine turning of end surfaces. OP100
13 Grinding of gear tooth flanks. OP110
![Page 28: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/28.jpg)
Manufacturing of demonstrator gears of
50CrMo4
1. Forging to gear blanks of Ovako 528E at Fomas HotRoll ( 70 pcs)
2. Heat treatment at HotRoll specified to 350 HB.
3. At RWTH WZL: Turning and hob milling ( 30 pcs)
4. At Fiat: Chamfering of gear teeth.
5. EFD Induction: Induction hardening trials & evaluation
28
![Page 29: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/29.jpg)
The induction hardening process and trials at
EFD Induction
29
Left edge Middle Right edge
Typical case contour
of carburized gear
![Page 30: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/30.jpg)
Comparison of the two heat treatment
processes: Carburizing vs Induction hardening
Based on a yearly production of 550 000 gears at the Mirafiori plant
of Fiat Powertrain
Aspects dealt with:
• Process time
• Energy consumption
• Cost of investment and maintenance
• => Total cost of heat treatment
Machining processes:
• Tooling
• Manpower
• Machine cost
• Machining engagement times
30
![Page 31: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/31.jpg)
Process time
31
Carburizing:
• Carburizing: 2.5 h
• Tempering time: 3 h
=> Total: 510 min
Induction hardening:
• Hardening cycle: <30 s
• Induction tempering: 60 s (in a parallel low power setup)
=> Total: 2 min
![Page 32: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/32.jpg)
32
Cost of heat treatment
Carburizing:
• Investment: 0.45 €
• Energy cost: 1.6 €
=> Total: 2.4 €
Induction hardening:
• Investment: 0.27 €
• Energy consumption: 0.3 €
=> Total: 0.6 €
![Page 33: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/33.jpg)
Machining costs
33
Operation Engagement time
[s] in today’s
production at Fiat
Internal facing 13
External facing 13
Finishing facing 8
Turning and facing 13
Turning and finishing facing 23
Finishing facing 13
Finishing facing 8
Hob milling 116
Chamfering 15
Snagging 15
Drilling 11
Boring 7
Hard part turning 26
Tooth grinding 125
We have considered the following machining operations:
![Page 34: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/34.jpg)
Introduced the following modifications of
cutting processes
34
![Page 35: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/35.jpg)
Spreadsheet to alter machining costs
35
Operation Tools [#]
Staff cost [€/h]
Tooling cost (€/tool)
Machine cost [€/h]
Sharpening [€]
Time in machine [h]
Set-up time [s]
Machining time [s/pc]
Cost (€)/year
Gre
e
n
turn
-
ing
Tooling 1000 10 10 000 Machine 40 16130 15 90,6 645 200 Staff 20 16130 15 90,6 322 600
Ho
bb
ing
Tooling new hobs
45 1000 45 000
Tooling sharpening
360 200 72 000
Machine 40 20070 15 116,4 802 800 Staff 20 20070 15 116,4 401 400
Ch
a
m-
feri
n
g
Tooling 50 500 25 000 Machine 40 4580 15 15 183 200 Staff 20 4580 15 15 91 600
Dri
ll-
ing
Tooling 200 50 10 000 Machine 40 7850 40 11,4 314 000 Staff 20 7850 40 11,4 157 000
Fin
is
hin
g
turn
-
ing
Tooling 550 100 55 000 Machine 40 6230 15 25,8 249 200 Staff 20 6230 15 25,8 124 600
Gri
n
din
g Tooling 50 200 10 000
Machine 40 22120 20 124,8 884 800 Staff 20 22120 20 124,8 442 400
Total cost/year (€)
4 846 k€
Total cost/pc
9 €
![Page 36: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/36.jpg)
Machining costs
Total machining costs
Carburizing 9 €
Induction hardening 12 €
36
![Page 37: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/37.jpg)
Major conclusions and thoughts of the project
• Induction hardening is a technical challenge to implement on helical gears due to the uneven
hardening profile of the tooth.
• Induction hardening is on par or better than carburizing, from the mechanical strength, toughness
and fatigue strength aspects.
• The component that was actually chosen as demonstrator makes lot of influence on the outcome
o this project. A shaft (or king pin) would have been much more viable and straightforward.
• Rule of thumb: The less machining of a component the higher the potential of induction
hardening.
• The process time of induction hardening is extremely short compared to carburizing => great
potential!!
• The process time and lead time are key aspects in this comparison. The complete shift from batch
process to in-line process showed too complex to evaluate in this project.
• The direct cost of IH is lower. (0.64 € vs 2.41€)
• The machining cost of carburizing is lower (9 € vs 12 €).
37
![Page 38: Scope of the MAC D project - SHTE · Supplier Gerdau Gerdau Ovako Ovako Heat treatment Quench & tempering I z QL-T1 240 HB v QH-T1 350 HB Quench & tempering II z QL-T2 287 HB v QH-T2](https://reader035.vdocuments.mx/reader035/viewer/2022071116/5ffe60c1a3965849b74608c1/html5/thumbnails/38.jpg)
38
Thanks for your attention!