polymer & nanocomposites...
TRANSCRIPT
POLYMER & NANOCOMPOSITES
SYMPOSIUM
Multi-Scale Self-Healing Nanocomposite Shielding Material
Abstract Book
21-22 February, 2018
supported by TUBITAK 1001 Project No-115R017
Editor: Prof. Dr. Nilgun BAYDOGAN
Co-Editors: Assoc. Prof. Nesrin KOKEN, Assoc. Prof. Dr. Birgul BENLI,
Dr. Tayfun BEL, Assist.Prof.Dr. Utku CANCI MATUR, PhD-Candidate Osman URPER
http://innovationorbit1.itu.edu.tr
978-975-561-501-1
Polymer & nanocomposites symposium, multi-scale self-healing nanocomposite shielding material abstract book
E – Published at Istanbul Technical University, Ayazaga Campus,
Maslak, Sariyer, 34469, Istanbul, TURKEY
on November 27, 2018
e-ISBN
POLYMER & NANOCOMPOSITES
SYMPOSIUM
Multi-Scale Self-Healing Nanocomposite Shielding Material
http://innovationorbit1.itu.edu.tr
Istanbul Technical University,
Energy Institute, Ayazaga Campus,
Maslak, 34469, Istanbul Turkey
February 21-22, 2018
Dear Colleagues,
International POLYMER & NANOCOMPOSITES SYMPOSIUM, Multi-Scale
Self-Healing Nanocomposite Shielding Material supported by TÜBİTAK 1001
Project with number 115R017 (Kendini Çok Yönlü Onarabilen
Nanokompozitlerin Geliştirilmesi ve Zırh Malzemesi Olarak Mekanik
Davranışlarının İncelenmesi) was held in Istanbul Technical University, Energy
Institute in February 21-22, 2018. This symposium aimed to bring together
academicians, researchers and engineers working in industrial companies.
The high profile delegates tried to exchange and discuss the original ideas,
research results, practical development experiences and technological
advancements of future applications in the symposium providing a common
platform from various disciplines and sectors.
This symposium was provided a privilege to participants and to discuss the
advantages and opportunities involved in sustainability of innovation in
Polymers and Nanocomposites with respect to current industrial and
academically researches.
We thank you for allowing us to partner with you in that effort for
International POLYMER & NANOCOMPOSITES SYMPOSIUM.
Prof. Dr. Nilgun BAYDOGAN
Symposium Chair
v
Executive Committee
Abdulehad ÖZDEMİR, PhD. Candidate, TUBITAK MAM, Kocaeli, TURKEY
Ayça KARAİL, ASELSAN, Electronics Industry and Trade, Inc., Ankara, TURKEY
Beril TUĞRUL, Prof.Dr., Istanbul Technical University, Energy Institute, Istanbul,
TURKEY
Birgül BENLİ, Associate Prof.Dr., Istanbul Technical University, Faculty of Mines,
Istanbul TURKEY
Cüneyt ARSLAN, Prof.Dr., Istanbul Technical University, Faculty of Chemical and
Metallurgical Engineering, Istanbul TURKEY
Fahir ARISOY, Assist. Prof.Dr., Istanbul Technical University, Faculty of Chemical
and Metallurgical Engineering, Istanbul TURKEY
Görkem MEMİŞOĞLU, PhD., Vestel Electronics, Manisa, TURKEY
Hande SESİGÜR, ŞİŞECAM, Çayırova, Kocaeli, TURKEY
Hüseyin ÇİMENOĞLU, Prof.Dr., Istanbul Technical University, Faculty of Chemical
and Metallurgical Engineering, Istanbul TURKEY
Murat CELEP, TÜBİTAK, MAM
Mustafa Serdar ŞALCI, GERSAN Elektrik Tic. ve San. A.Ş. Istanbul TURKEY
Namık Serkan TAŞKIRAN, TÜBİTAK MAM
Nedim TÜRKMEN, Dr. TAI- Turkish Aerospace Industries, Inc.
Nesrin KÖKEN, Associate. Dr., Istanbul Technical University, Faculty of Arts and
Sciences, Istanbul TURKEY
Nilgün BAYDOĞAN, Prof.Dr., Istanbul Technical University, Energy Institute,
Istanbul TURKEY
Nilgün KIZILCAN, Prof.Dr., Istanbul Technical University, Faculty of Arts and
Sciences Istanbul TURKEY
Noorhana YAHYA, Prof.Dr., Universiti Teknologi PETRONAS, MALAYSIA
Osman ÜRPER, PhD-Candidate, Istanbul Technical University, Energy Institute
Istanbul TURKEY
Tayfun BEL, PhD, Istanbul Technical University, Prof.Dr. Adnan Tekin Materials
Science and Production Technologies Applied Research Center (ATARC) Istanbul
TURKEY
vi
Scientific Committee
ADNANE MOHAMED, Département de Technologie des Matériaux, Faculté de physique,
Université des Sciences et de la Technologie d’Oran Mohamed Boudiaf, El M’naouar BP
1505 Bir El Djir 31000 Oran, ALGÉRIE
Afza SHAFIE, PhD., Universiti Teknologi PETRONAS, MALAYSIA
Ahmet Togo GIZ, Prof.Dr., Istanbul Technical University, Faculty of Arts and Sciences
Istanbul TURKEY
Andy AUGOUSTI, Prof.Dr., Kingston University, London, UNITED KINGDOM
Ayben KİLİSLİOĞLU, Prof.Dr., Istanbul University, Engineering Faculty Istanbul
TURKEY
Aylin KARAHAN TOPRAKÇI, Assist. Prof.Dr., Yalova University Engineering Faculty,
Yalova, TURKEY
Barbara PIERSCIONEK, Prof. Dr., Nottingham Trent University, Nottingham,
UNITED KINGDOM
Beril TUĞRUL, Prof.Dr., Istanbul Technical University, Energy Institute, Istanbul,
TURKEY
Birgül BENLİ, Associate Prof.Dr., Istanbul Technical University, Faculty of Mines,
Istanbul TURKEY
Burak BARUTÇU, Assist. Prof.Dr.Istanbul Technical University, Energy Institute,
Istanbul TURKEY
Cevza CANDAN, Prof.Dr., Istanbul Technical University Faculty of Textile Technologies
and Design, Istanbul TURKEY
Denis CHAUMONT Prof.Dr., ICB, Université de Bourgogne Franche-Comté UBFC, BP 47 870,
21078 Dijon, FRANCE
Cihat TAŞALTIN, PhD.,TÜBİTAK MAM, , Kocaeli, TURKEY
Cüneyt ARSLAN, Prof.Dr., Istanbul Technical University, Faculty of Chemical and
Metallurgical Engineering, Istanbul TURKEY
vii
Esra GENCELİ, Assist. Prof.Dr., Istanbul Technical University,, Civil Engineering
Faculty Istanbul TURKEY
Esra ÖZKAN ZAYİM, Prof.Dr., Istanbul Technical University,, Faculty of Arts and
Sciences Istanbul TURKEY
Elif ARICI BOGNER, Associate Prof.Dr., Istanbul Technical University, Energy
Institute, Istanbul, TURKEY
Emel ÖNDER KARAOĞLU, Prof.Dr., Istanbul Technical University Faculty of Textile
Technologies and Design, Istanbul TURKEY
Emine TEKİN, Associate Prof.Dr., TÜBİTAK MAM, Kocaeli, Turkey
Emine ÇOKGÖR, Prof.Dr., Istanbul Technical University, Civil Engineering Faculty
Istanbul TURKEY
Fahir ARISOY, Assist. Prof.Dr., Istanbul Technical University, Faculty of Chemical and
Metallurgical Engineering, Istanbul TURKEY
Filiz PİROĞLU, Associate Prof.Dr., Istanbul Technical University,, Civil Engineering
Faculty, Istanbul TURKEY
Fried MİKLOS, PhD., Eötvös Loránd University, Budapeşte, HUNGARY
Hande SESİGÜR, PhD., ŞİŞECAM, Çayırova, Kocaeli, TURKEY
Hassan SOLEIMANI, Dr. Universiti Teknologi PETRONAS, MALAYSIA
Hülya CEBECİ, Associate Prof.Dr., Istanbul Technical University, Faculty of Aeronautics
and Astronautics Istanbul TURKEY
Hüseyin ÇİMENOĞLU, Prof.Dr., Istanbul Technical University, Faculty of Chemical and
Metallurgical Engineering Istanbul TURKEY
Hüseyin KIZIL, Associate Prof.Dr., Istanbul Technical University, Faculty of Chemical
and Metallurgical Engineering Istanbul TURKEY
İskender REYHANCAN, Prof.Dr., Istanbul Technical University, Energy Institute,
Istanbul TURKEY
Kaiying WANG, Prof. Dr., University College of South East, NORWAY
Levent TRABZON, Prof.Dr., Istanbul Technical University, Engineering Faculty Istanbul
TURKEY
viii
Lütfü ÖVEÇOĞLU, Prof.Dr., Istanbul Technical University, Faculty of Chemical and
Metallurgical Engineering Istanbul TURKEY
Mehmet Ali GÜRKAYNAK, Prof.Dr., İÜ Mühendislik Fakültesi, Istanbul TURKEY
Murat CELEP, PhD., TUBITAK MAM, Kocaeli, TURKEY
Mustafa BAKKAL, Associate Prof.Dr., Istanbul Technical University, Engineering
Faculty Istanbul TURKEY
Namık Serkan TAŞKIRAN, PhD., TUBITAK MAM, Kocaeli, TURKEY
Neslihan YUCA, PhD., ENWAIR Energy Technology Company, Istanbul TURKEY
Nesrin ALTINSOY, Prof.Dr., Istanbul Technical University, Energy Institute, Istanbul
TURKEY
Nesrin KOKEN, Associate Prof.Dr., Istanbul Technical University, Faculty of Arts and
Sciences Istanbul TURKEY
Nevin TAŞALTIN, Associate Prof.Dr., TÜBİTAK MAM, Kocaeli, TURKEY
Nilgün Baydoğan, Prof.Dr., Istanbul Technical University, Energy Institute Istanbul
TURKEY
Nilgün KIZILCAN, Prof.Dr., Istanbul Technical University, Faculty of Arts and Sciences
Istanbul TURKEY
Nilgün YAVUZ, Prof.Dr., Istanbul Technical University, Energy Institute, Istanbul
TURKEY
Noorhana YAHYA, Prof. Dr., Universiti Teknologi Petronas, MALAYSIA
Nuray UÇAR, Prof.Dr., University Faculty of Textile Technologies and Design, Istanbul
TURKEY
Ömer Berk BERKALP, Prof. Dr. Istanbul Technical University Faculty of Textile
Technologies and Design, Istanbul TURKEY
Ömer Suat TAŞKIN, Assist. Prof.Dr., Istanbul University, Marine Sciences and
Management Institute, Istanbul TURKEY
Pelin SARITEPE OTANSEV, Assist. Prof.Dr., Istanbul University,Science Faculty
Istanbul TURKEY
ix
Rüstem ARSLAN, Prof. Dr. Istanbul Technical University, Faculty of Aeronautics and
Astronautics, Istanbul TURKEY
Said SABBAGH, PhD., Istanbul Technical University, Energy Institute, Istanbul,
TURKEY
Sema AKYIL ERENTÜRK, Prof.Dr., Istanbul Technical University, Energy Institute,
Istanbul TURKEY
Sema MEMİŞ, Dr. TUBITAK MAM, Kocaeli, TURKEY
Senem ŞENTÜRK LÜLE, Assist. Prof.Dr., Istanbul Technical University, Energy
Institute, Istanbul TURKEY
Serço Serkis YEŞİLKAYA, Associate Prof. Dr., Yıldız Technical University, Faculty of
Arts and Sciences, Istanbul TURKEY
Sevilay HACIYAKUPOĞLU, Associate Prof.Dr., Istanbul Technical University, Energy
Institute, Istanbul TURKEY
Svetlana M. DANİLOVA-TRETİAK, PhD., A.V. Luikov Heat and Mass Transfer
Institute, the National Academy of Sciences of Belarus, Minsk,
REPUBLIC OF BELARUS
Şafak Nur ERTÜRK BOZKURTOĞLU, Assist. Prof.Dr, Faculty of Naval Architecture
and Ocean Engineering, Istanbul TURKEY
Şinasi EKİNCİ, Associate Prof. Dr., Çekmece Nuclear Research and Training Center,
TAEK, Istanbul TURKEY
Tuğrul HAKİOĞLU, Prof. Dr., Istanbul Technical University, Energy Institute, Istanbul,
TURKEY, Istanbul TURKEY
Utku Canci Matur, Assist. Prof.Dr., İstanbul Gedik University, Istanbul TURKEY
Üner ÇOLAK, Prof.Dr., Istanbul Technical University, Energy Institute, Istanbul
TURKEY
Liu ZIYUAN, PhD., Tokyo University, Tokyo, JAPAN
Zuhal ER, Assist. Prof.Dr. Istanbul Technical University, Faculty of Arts and Sciences,
Istanbul TURKEY
x
Organizing Committee
Abdulehad ÖZDEMİR, PhD. Candidate , TUBITAK MAM, Kocaeli, TURKEY
Ahmet GÜLTEKİN, Research Assistant, PhD. Candidate Istanbul Technical University,
Energy Institute, , Istanbul TURKEY
Birgül BENLİ, Associate Prof.Dr., Istanbul Technical University, Faculty of Mines,
Istanbul TURKEY
Bülent BÜYÜK, PhD, Istanbul Technical University, Energy Institute, Istanbul TURKEY
C.Fahir ARISOY, Associate Prof.Dr., Istanbul Technical University, Faculty of Chemical
and Metallurgical Engineering, Istanbul TURKEY
Cihat TAŞALTIN, PhD., TUBITAK MAM, Kocaeli, TURKEY
Cüneyt ARSLAN, Prof.Dr., Istanbul Technical University, Faculty of Chemical and
Metallurgical Engineering, Istanbul TURKEY
Doğukan ÇETİNER, Research Assistant, PhD Candidate Istanbul Technical University,
Faculty of Chemical and Metallurgical Engineering, Istanbul TURKEY
Emre YILMAZ, Research Assistant PhD. Candidate Istanbul Technical University,
Faculty of Chemical and Metallurgical Engineering, Istanbul TURKEY
Erkan BOZKURTOĞLU, Associate Prof.Dr., Istanbul Technical University, Faculty of
Mines, Istanbul TURKEY
Faiz MUHAFFEL, Research Assistant PhD. Candidate, Istanbul Technical University,
Faculty of Chemical and Metallurgical Engineering, Istanbul TURKEY
Filiz PİROĞLU, Associate Prof., Istanbul Technical University, Civil Engineering
Faculty, Istanbul TURKEY
Görkem MEMİŞOĞLU, PhD., VESTEL Electronics, İstanbul, TURKEY
Hande SESİGÜR, PhD., ŞİŞECAM, Çayırova, Kocaeli, TURKEY
Hasan GÖKÇE, PhD., Istanbul Technical University, Prof.Dr. Adnan Tekin Materials
Science and Production Technologies Applied Research Center (ATARC), Istanbul,
TURKEY
M. Sahip KIZILTAŞ, Specialist, PhD.. Candidate., Istanbul Technical University, Energy
Institute, Istanbul TURKEY
Maihemuti MAIMAITITUERSUN, PhD. Candidate, Istanbul Technical University,
Graduate School of Science Engineering and Technology, Istanbul TURKEY
Melis TÜRKER, East Marmara Development Agency, Kocaeli Support Office, Value
Chain Analyst, Istanbul TURKEY
Mustafa Serdar ŞALCI, GERSAN Elektrik Tic. ve San. A.Ş., Istanbul TURKEY
xi
Murat CELEP, PhD., TÜBİTAK MAM Kocaeli, TURKEY
Namık Serkan TAŞKIRAN, TÜBİTAK MAM, Kocaeli, TURKEY
Nedim TÜRKMEN, PhD., TAI Turkish Aerospace Industries, Inc.
Neslihan YUCA, PhD., ENWAIR Energy Technology Company, Istanbul TURKEY
Nesrin KÖKEN, Associate Prof. Dr., Istanbul Technical University, Faculty of Arts and Sciences, Istanbul TURKEY
Nilgün BAYDOĞAN, Prof. Dr., Istanbul Technical University, Energy Institute, Istanbul TURKEY
Nilgün KIZILCAN, Prof.Dr., Istanbul Technical University, Faculty of Arts and Sciences, Istanbul TURKEY
Nursev ERDOĞAN, PhD. TAI - Turkish Aerospace Industries, Inc., Ankara, TURKEY
Onur TAZEGÜL, Research Assistant PhD. Candidate, Istanbul Technical
University, Faculty of Chemical and Metallurgical Engineering Istanbul
TURKEY
Osman ÜRPER, Research Assistant PhD. Candidate, Istanbul Technical University, Energy Institute, Istanbul TURKEY
Pelin SARITEPE OTANSEV, Assist. Prof.Dr., Istanbul University, Science Faculty, Istanbul TURKEY
Selim ERTÜRK, PhD., Istanbul Technical University, Prof.Dr. Adnan Tekin
Materials Science and Production Technologies Applied Research Center
(ATARC), Istanbul TURKEY
Sema MEMİŞ, PhD, TÜBİTAK MAM, Kocaeli, TURKEY
Serço Serkis YEŞİLKAYA, Assoc. Prof. Dr., Yıldız Technical University, Faculty of Arts and Sciences, Istanbul TURKEY
Songül ULAĞ, PhD. Candidate, Marmara University, Institute of Pure and Applied Sciences, Istanbul TURKEY
Şafak Nur ERTÜRK BOZKURTOĞLU, Assist. Prof.Dr. İTÜ Gemi İnşaatı ve Deniz Bilimleri Fakültesi, Istanbul TURKEY
Tayfun BEL, PhD., Istanbul Technical University, Prof.Dr. Adnan Tekin Materials
Science and Production Technologies Applied Research Center (ATARC), Istanbul TURKEY
Türkan DOĞAN, PhD. Candidate, Istanbul Technical University, Energy Institute, Istanbul TURKEY
Utku CANCİ MATUR, PhD., Assis.Prof., İstanbul Gedik Üniversitesi, Istanbul TURKEY
Yakup YÜREKTÜRK, Research Assistant PhD. Candidate, Istanbul Technical University, Faculty of Chemical and Metallurgical Engineering, Istanbul TURKEY
Yunus Emre DOĞAN, BSc. Candidate, Istanbul University, Science Faculty, Istanbul TURKEY
Zeynep CAMTAKAN, Specialist, PhD. Candidate., Istanbul Technical University, Energy Institute, Istanbul TURKEY
xii
Participant List
Abdulrahman ABDUL-HADI, PhD., University of Damascus, Damascus, SYRIA
Abdulehad ÖZDEMİR, PhD. Candidate, TUBITAK MAM, Kocaeli, TURKEY
Afza SHAFIE, PhD., Universiti Teknologi PETRONAS, MALAYSIA
Ahmet GÜLTEKİN, Research Assistant, PhD. Candidate Istanbul Technical
University, Energy Institute, Istanbul TURKEY
Ahmet Togo GIZ, Prof.Dr., Istanbul Technical University, Faculty of Arts and
Sciences Istanbul TURKEY
Ali BAYGELDİ, Head of Satellite Design and Integration Department, Republic of
Turkey Ministry of Transport Maritime Affairs and Communications, Directorate
General of Aeronautics and Space Technologies, Ankara, TURKEY
Ali Erdem EKEN PhD., ASELSAN, Electronics Industry and Trade, Inc., Ankara,
TURKEY
Andy AUGOUSTI, Prof.Dr., Kingston University, London, UNITED KINGDOM
Aref CEVAHİR, PhD., ŞİŞECAM, Research Center, ÇAYIROVA, KOCAELİ,
TURKEY
Ayben KİLİSLİOĞLU, Prof.Dr., Istanbul University, Engineering Faculty Istanbul
TURKEY
Ayça KARAİL, ASELSAN, Electronics Industry and Trade, Inc., Ankara, TURKEY
Aylin KARAHAN TOPRAKÇI, Assist. Prof.Dr., Yalova University Engineering
Faculty, Yalova, TURKEY
Barbara PIERSCIONEK, Prof. Dr., Nottingham Trent University, Nottingham,
UNITED KINGDOM
Beril TUĞRUL, Prof.Dr., Istanbul Technical University, Energy Institute, Istanbul,
TURKEY
Birgül BENLİ, Associate Prof.Dr., Istanbul Technical University, Faculty of Mines,
Istanbul TURKEY
Burak BARUTÇU, Assist. Prof.Dr. Istanbul Technical University, Energy Institute,
Istanbul TURKEY
Bülent BÜYÜK, PhD, Istanbul Technical University, Energy Institute
C.Fahir ARISOY, Associate Prof.Dr., Istanbul Technical University, Faculty of
Chemical and Metallurgical Engineering, Istanbul, TURKEY
Cevza CANDAN, Prof.Dr., Istanbul Technical University Faculty of Textile
Technologies and Design, Istanbul TURKEY
xiii
Cihat TAŞALTIN, PhD., TÜBİTAK MAM, , Kocaeli, TURKEY
Cüneyt ARSLAN, Prof.Dr., Istanbul Technical University, Faculty of Chemical and
Metallurgical Engineering Istanbul, TURKEY
Doğukan ÇETİNER, Research Assistant, PhD Candidate Istanbul Technical
University, Faculty of Chemical and Metallurgical Engineering Istanbul, TURKEY
Elif ARICI BOGNER, Associate Prof.Dr., Istanbul Technical University, Energy
Institute, Istanbul, TURKEY
Emel ÖNDER KARAOĞLU, Prof.Dr., Istanbul Technical University Faculty of
Textile Technologies and Design, Istanbul TURKEY
Emine ÇOKGÖR, Prof.Dr., Istanbul Technical University, Civil Engineering Faculty
Istanbul TURKEY
Emine TEKİN, Associate Prof.Dr., TÜBİTAK MAM, Kocaeli, Turkey
Emre YILMAZ, Research Assistant PhD. Candidate Istanbul Technical University,
Faculty of Chemical and Metallurgical Engineering Istanbul, TURKEY
Erkan BOZKURTOĞLU, Associate Prof.Dr., Istanbul Technical University, Faculty
of Mines Istanbul, TURKEY
Esra GENCELİ, Assist. Prof.Dr., Istanbul Technical University, Civil Engineering
Faculty Istanbul TURKEY
Esra ÖZKAN ZAYİM, Prof.Dr., Istanbul Technical University, Faculty of Arts and
Sciences Istanbul TURKEY
Faiz MUHAFFEL, Research Assistant PhD. Candidate, Istanbul Technical University,
Faculty of Chemical and Metallurgical Engineering Istanbul, TURKEY
Filiz PİROĞLU, Associate Prof.Dr., Istanbul Technical University, Civil Engineering
Faculty Istanbul TURKEY
Fried MİKLOS, PhD., Eötvös Loránd University, Budapest, HUNGARY
Furkan YAZICI, BSc. Candidate, ENWAIR Energy Technology Company, Kocaeli
University, Engineering Faculty, Kocaeli, Turkey
Görkem MEMİŞOĞLU, PhD., VESTEL Electronics, Manisa, TURKEY
xiv
Gülşah KAHRAMAN, PhD., ŞİŞECAM, Research Center, Çayırova,
Kocaeli, TURKEY
Hande SESİGÜR, PhD., ŞİŞECAM, Research Center, Çayırova,
Kocaeli, TURKEY
Hasan GÖKÇE, PhD., Istanbul Technical University, Prof.Dr. Adnan Tekin Materials
Science and Production Technologies Applied Research Center (ATARC) Istanbul
TURKEY
Hassan SOLEIMANI, Dr. Universiti Teknologi PETRONAS, MALAYSIA
Hülya CEBECİ, Associate Prof.Dr., Istanbul Technical University, Faculty of
Aeronautics and Astronautics Istanbul TURKEY
Hüseyin ÇİMENOĞLU, Prof.Dr., Istanbul Technical University, Faculty of Chemical
and Metallurgical Engineering Istanbul TURKEY
Hüseyin KIZIL, Associate Prof.Dr., Istanbul Technical University, Faculty of
Chemical and Metallurgical Engineering Istanbul TURKEY
İskender REYHANCAN, Prof.Dr., Istanbul Technical University, Energy Institute,
Istanbul, TURKEY Istanbul TURKEY
Kaiying WANG, Prof. Dr., University College of Southeast, NORWAY
Levent TRABZON, Prof.Dr., Istanbul Technical University, Engineering Faculty
Istanbul TURKEY
Liu ZIYUAN, PhD., Tokyo University, Tokyo, JAPAN
Lütfü ÖVEÇOĞLU, Prof.Dr., Istanbul Technical University, Faculty of Chemical and
Metallurgical Engineering Istanbul TURKEY
M. Sahip KIZILTAŞ, Specialist, PhD. Candidate., Istanbul Technical University,
Energy Institute Istanbul, TURKEY
Mahmut MUHEMMETTURSUN, PhD. Candidate, Istanbul Technical University,
Graduate School of Science Engineering and Technology, Istanbul, TURKEY
Mehmet Ali GÜRKAYNAK, Prof.Dr., İÜ Mühendislik Fakültesi, Istanbul TURKEY
Melis TÜRKER, East Marmara Development Agency, Kocaeli Support Office, Value
Chain Analyst KOCAELİ, TURKEY
xv
Murat CELEP, PhD., TUBITAK MAM, Kocaeli, TURKEY
Murat Ferhat DOĞDU, PhD. Candidate, ENWAIR Energy Technology Company,
Istanbul Technical University, Energy Institute, Istanbul, TURKEY
Mustafa BAKKAL, Associate Prof.Dr., Istanbul Technical University, Engineering
Faculty Istanbul TURKEY
Mustafa Serdar ŞALCI, GERSAN Elektrik Tic. ve San. A.Ş. Istanbul, TURKEY
Namık Serkan TAŞKIRAN, PhD., TUBITAK MAM, Kocaeli, TURKEY
Nedim TÜRKMEN, PhD., TAI Turkish Aerospace Industries, Inc.
Neslihan YUCA, PhD., ENWAIR Energy Technology Company,
Nesrin ALTINSOY, Prof.Dr., Istanbul Technical University, Energy Institute,
Istanbul, TURKEY, Istanbul TURKEY
Nesrin KOKEN, Associate Prof.Dr., Istanbul Technical University, Faculty of Arts
and Sciences Istanbul TURKEY
Nevin TAŞALTIN, Associate Prof.Dr., TÜBİTAK MAM, Kocaeli, TURKEY
Nilgün BAYDOĞAN, Prof.Dr., Istanbul Technical University, Energy Institute,
Istanbul, TURKEY
Nilgün KIZILCAN, Prof.Dr., Istanbul Technical University, Faculty of Arts and
Sciences Istanbul TURKEY
Nilgün YAVUZ, Prof.Dr., Istanbul Technical University, Energy Institute, Istanbul,
TURKEY Istanbul TURKEY
Noorhana YAHYA, Prof.Dr., Universiti Teknologi PETRONAS, MALAYSIA
Nuray UÇAR, Prof.Dr., University Faculty of Textile Technologies and Design,
Istanbul TURKEY
Nursev ERDOĞAN, PhD. TAI-Turkish Aerospace Industries, Inc., Ankara, TURKEY
Onur TAZEGÜL, Research Assistant PhD. Candidate, Istanbul Technical University,
Faculty of Chemical and Metallurgical Engineering Istanbul, TURKEY
Osman ÜRPER, Research Assistant PhD. Candidate, Istanbul Technical University,
Energy Institute Istanbul, TURKEY
xvi
Ömer Berk BERKALP, Prof. Dr. Istanbul Technical University Faculty of Textile
Technologies and Design, Istanbul TURKEY
Ömer Suat TAŞKIN, Assist. Prof.Dr., Istanbul University, Marine Sciences and
Management Institute, Istanbul TURKEY
Pelin SARITEPE OTANSEV, Assist. Prof.Dr., Istanbul University, Science Faculty
Istanbul TURKEY
Rüstem ARSLAN, Prof. Dr. Istanbul Technical University, Faculty of Aeronautics
and Astronautics, Istanbul TURKEY
Said SABBAGH, PhD., Istanbul Technical University, Energy Institute, Istanbul,
TURKEY
Selim Dinçer, TAI - Turkish Aerospace Industries, Inc., Ankara, TURKEY
Selim ERTÜRK, PhD., Istanbul Technical University, Prof.Dr. Adnan Tekin Materials
Science and Production Technologies Applied Research Center (ATARC) Istanbul,
TURKEY
Sema AKYIL ERENTÜRK, Prof.Dr., Istanbul Technical University, Energy Institute,
Istanbul TURKEY
Sema MEMİŞ, PhD, TUBITAK MAM, Kocaeli, TURKEY
Senem ŞENTÜRK LÜLE, Assist. Prof.Dr., Istanbul Technical University, Energy
Institute, Istanbul, TURKEY Istanbul TURKEY
Serço Serkis YEŞİLKAYA, Associate Prof. Dr., Yıldız Technical University, Faculty
of Arts and Sciences, Istanbul TURKEY
Sevilay HACIYAKUPOĞLU, Associate Prof.Dr., Istanbul Technical University,
Energy Institute, Istanbul, TURKEY Istanbul TURKEY
Songül ULAĞ, PhD. Candidate, Marmara University, Institute of Pure and Applied
Sciences Istanbul, TURKEY
Svetlana M. DANİLOVA-TRETİAK, PhD., A.V. Luikov Heat and Mass Transfer
Institute, the National Academy of Sciences of Belarus, Minsk,
REPUBLIC OF BELARUS
xvii
Şafak Nur ERTÜRK BOZKURTOĞLU, Assist. Prof.Dr, Faculty of Naval
Architecture and Ocean Engineering, Istanbul TURKEY
Tayfun BEL, PhD, Istanbul Technical University, Prof.Dr. Adnan Tekin Materials
Science and Production Technologies Applied Research Center (ATARC) Istanbul,
TURKEY
Tuğçe Köröğlu, MSc, Istanbul Technical University, Graduate School of Science
Engineering and Technology. Istanbul TURKEY
Tuğrul HAKİOĞLU, Prof. Dr., Istanbul Technical University, Energy Institute,
Istanbul TURKEY
Türkan DOĞAN, PhD. Candidate, Istanbul Technical University, Energy Institute
Istanbul, TURKEY
Utku CANCİ MATUR, Lecturer, PhD., İstanbul Gedik Üniversitesi
Üner ÇOLAK, Prof.Dr., Istanbul Technical University, Energy Institute, Istanbul
TURKEY
Yakup YÜREKTÜRK, Research Assistant PhD. Candidate, Istanbul Technical
University, Faculty of Chemical and Metallurgical Engineering Istanbul, TURKEY
Yunus Emre DOĞAN, BSc. Candidate, Istanbul University, Science Faculty Istanbul
TURKEY
Zeynep CAMTAKAN, Specialist, PhD. Candidate., Istanbul Technical University,
Energy Institute Istanbul, TURKEY
Zineb BENZAIT, PhD. Candidate, Istanbul Technical University, Graduate School of
Science Engineering and Technology, Istanbul, TURKEY
Zuhal ER, Assist. Prof.Dr. Istanbul Technical University, Faculty of Arts and Sciences
Istanbul TURKEY
xviii
CONTENTS
PROGRAMME.........................................................................................................................1
ABSTRACTS............................................................................................................................6
LIST OF ORAL ABSTRACTS................................................................................................7
LIST OF POSTER ABSTRACTS...............................................................................10
O01
POLYMERIC NANOCOMPOSITES AND SONOCHEMISTRY...................................11 Prof. Dr. Ayben KİLİSLİOĞLU
O02
LIGHT INDUCED SYNTHESIS OF NANOCOMPOSIT..............................................12 Prof. Dr. Yusuf YAĞCI
O03
NANOPARTIKÜL (GÜMÜŞ, TİTANYUM), CNT VE İLETKEN POLIMER (PANI)
KATKILI NANOLİF, MİKROLİF VE UYGULAMA ALANLARI……………………....13 Prof. Dr. Nuray UÇAR
O04
COMPOSITE & HYBRID LIGHTWEIGHT DESIGN SOLUTIONS IN AUTOMOTIVE
INDUSTRY.............................................................................................................................14 Prof. Dr. Mustafa BAKKAL
O05
KOMPOZİT MALZEMELER VE UYGULAMALARI........................................................15 Dr. Ali Erdem EKEN
O06
BİYOMALZEME, BİYOMEKANİK VE BİYOELEKTRONİK MÜKEMMELİYET
MERKEZİ...............................................................................................................................16 Dr. CihatTAŞALTIN
O07
RADYASYON ZIRHI AMAÇLI NANOKOMPOZİTLER..................................................17 Prof.Dr. Beril TUĞRUL
O08
ELEKTRODÖNDÜRME YÖNTEMİYLE HAZIRLANMIŞ ALOE VERA KATKILI
TİTANYUM OKSİT NANOLİFLERİN ANTİBAKTERİYEL ETKİLERİ..........................18 Osman ÜRPER, Tuğçe KÖROĞLU, Prof. Dr. Esra ÖZKAN ZAYİM
O09
EFFECT OF POROSITY IN SNO2 NANOFIBERS AS ANODE MATERIALS FOR
SODIUM-ION BATTERIES……………………………………………………………..…19 Doç. Dr. Hüseyin KIZIL
xix
O10
IMPROVING GLASS FIBER-POLYMER INTERFACIAL BOND STRENGTH USING
NANO-CLAY PLATELETS..................................................................................................20 Gülşah KAHRAMAN
*, Dr. Aref CEVAHİR, Şener YILMAZ, Prof. Selim KUSEFOĞLU
Dr. Vedat SEDİROĞLU
O11
NANOTECHNOLOGY IN AEROSPACE APPLICATIONS……………………...……....22 Dr. Nursev ERDOĞAN, Selim DİNÇER
O12
MECHANICAL PROPERTIES OF NANO-PARTICLES REINFORCED
POLYURETHANE NANO-COMPOSITES..........................................................................23 Zineb BENZAIT MSc., Prof. Dr. Levent TRABZON
O13
SYNTHESIS OF POLYANILINE-DOPED BORIC ACID /CARBON NANOTUBE
COMPOSITES AND ITS THERMAL PROPERTIES…………………………………….25 Ayşenur Örs, Prof. Dr. Nilgün YAVUZ
O14
FABRICATION AND CHARACTERIZATION OF ULTRA-HIGH PERFORMANCE
CONDUCTIVE NANOCOMPOSITE FILAMENTS FOR ADDITIVE
MANUFACTURING..............................................................................................................27 Özge KAYNAN, Alptekin YILDIZ, Elif ÖZDEN-YENİGÜN, Prof. Dr. Hülya CEBECİ
O15
APPLICATIONS OF POLYMER AND COMPOSITE MATERIALS IN CONSUMER
ELECTRONICS....……………………………………………………….………………….28 Dr. Gorkem MEMISOGLU, Burhan GULBAHAR
O16
YİYECEK ENDÜSTRİSİ ATIK/ATIKSULARINDAN MİKROBİYAL BİYOPOLİMER
VE BİYOPLASTİK ÜRETİMİ...............................................................................................29 Prof. Dr. Emine ÇOKGÖR
O17
A BRIEF OVERVIEW TO SELF HEALING MATERIALS WITH THE
CONCEPTUAL AND THE ORETICAL PHYSICS ASPECTS …………………………...31 Prof. Dr. Tugrul HAKIOGLU
O18
İLETKEN POLİMER KOMPOZİTLER VE UYGULAMALARI……………………....…32 Yard.Doç.Dr. Hatice Aylin KARAHAN TOPRAKÇI, Yard.Doç.Dr. Ozan TOPRAKÇI
O19
NANOKOMPOZİTLERİN KULLANIM ALANLARI.........................................................33 Yard.Doç.Dr. Pelin SARITEPE OTANSEV
xx
O20
CLAY MODIFIED NANO COMPOSITE KETONIC RESINS AS FIRE RETARDANT
POLYOL FOR FOAM POLYURETHANE…………………………………………...…....34 Prof. Dr. Nilgün KIZILCAN
O21
PREPARATION OF POROUS POLYMERIC MATERIALS AND THEIR SELF
HEALING AND ENVIRONMENTAL APPLICATIONS…………………….…….….….36 Assist.Prof.Dr. Ömer Suat TAŞKIN
O22
KENDİNİ ÇOK YÖNLÜ ONARABİLEN NANOKOMPOZİTLER…………….………...38 Dr. Tayfun BEL, Prof.Dr. Cüneyt ARSLAN, Prof.Dr. Nilgün BAYDOĞAN
O23
ZnO NANO-PARÇACIKLARI VE NANO-KOMPOSİTLERİNİN OLED
UYGULAMALARI................................................................................................................39 Doç. Dr. Emine Tekin, Rifat KAÇAR, Dr. Selin P. MUCUR, Dr. Tülay Aslı TUMAY, Dr. Salih DABAK
O24
MARMARA BÖLGESİ KOMPOZİT MALZEME DEĞER ZİNCİRİ ANALİZİ................41 Melis TÜRKER
O25
ELECTRICAL PROPERTIES OF A SINGLE NANOFIBER OF SEPIOLITE CLAY BY
ATOMIC FORCE MICROSCOPY CONDUCTIVY MODE……………………...……….42 Assoc.Prof.Dr. Birgül BENLİ
O26
KOMPOZİT MALZEMELER İLE TASARIM, ANALİZ, OPTİMİZASYON
İMALAT VE KALİTE KONTROL İÇİN GÜNCEL YAZILIM PROGRAMLARINA
BAKIŞ.....................................................................................................................................43 Assist.Prof.Dr. Zuhal ER
O27
POLİMER VE NANOKOMPOZİTLERDE POZİTRON ANNİHİLASYON
SPEKTROSKOPİSİ VE ANİ GAMA AKTİVASYON ANALİZİ........................................44
Doç.Dr. Sevilay HACIYAKUPOĞLU
O28
USABILITY OF POLYMERIC NANOCOMPOSITE ADSORBENTS IN NUCLEAR
WASTE MANAGEMENT………………………………………………………………….45 Prof. Dr. Sema AKYIL ERENTÜRK
O29
İNCE FİLM NANOKOMPOZİT İNCE BOŞLUKLU (HOLLOW FİBER)
NANOFİLTRASYON MEMBRANLARIN ÜRETİMİ VE İÇME SUYU ARITIMI
AÇISINDA DEĞERLENDİRİLMESİ....................................................................................47 Yard.Doç.Dr. Esra ATEŞ GENCELİ, Araş.Gör. Reyhan ŞENGÜR-TAŞDEMİR,
Araş.Gör. Melike ÜRPER, Araş.Gör. Türker TÜRKEN, Prof.Dr. İsmail Koyuncu
xxi
O30
Lİ-İYON BATARYA UYGULAMALARİNDA Sİ/C NANOKOMPOZİTLERİN
KULLANİMİ..........................................................................................................................49 Dr. Neslihan YUCA
O31
PROPERTIES OF THE IRRADIATED GREEN PVC AND ITSAPPLICATIONS in
INDUSTRY ANDENVIRONMENT......................................................................................50 Dr. Said SABBAGH
O32
NANOSELÜLOZİK ELYAF TAKVİYESİ İLE YENİLENEBİLİR KAYNAKLI POLİMER
NANOKOMPOZİTLERİN GELİŞTİRİLMESİ..................................................51 Dr. Aysun EKİNCİ, Yard.Doç.Dr. Gülay BAYRAMOĞLU
O33
NÜKLEER GÜVENLİK VE EMNİYET AÇISINDAN NANOKOMPOZİTLERİN
OPERASYONEL UYGULAMALARI..................................................................................53 Yük.Müh. Zeynep CAMTAKAN
O34
MEKANOKİMYASAL SENTEZLEME VE MEKANİK ALAŞIMLAMA YÖNTEMLERİ
İLE DÜŞÜK SICAKLIK KOŞULLARINDA HİBRİT KOMPOZİTLERİN
ÜRETİMİ................................................................................................................................54 Dr. Hasan GÖKÇE
O35
İNCE FILM GÜNEŞ HÜCRELERI VE POLIMER NANOKOMPOZIT TAŞIYICILAR.......................................................................................................................55
Dr. Öğretim Üyesi Utku CANCİ MATUR, Prof.Dr. Nilgün BAYDOĞAN
O36
KÖPÜK POLİÜRETANDA YANMAZLIK ÖZELLİĞİ SAĞLAYACAK MİKRO
KÜRELERİN SENTEZİ VE KULLANIMI...........................................................................57
Doç.Dr. Nesrin KÖKEN, Görkem ÜLKÜ
O37
POLİMER VE NANOKOMPOZİT MALZEMELERİN İTÜ TRIGA MARK-II
REAKTÖRÜ UYGULAMALARI..........................................................................................59
Yük.Müh. M. Sahip KIZILTAŞ
xxii
P01
CU2ZNSNS4 THIN FILMS DEPOSITED BY DIP COATING TECHNIQUE FOR SOLAR
CELLS CONTAINING POLYMER SUBSTRATES............................................................61
MSc. Charif TAMIN, Prof.Dr.Mohamed ADNANE, Prof.Dr.Nilgun BAYDOGAN,
Prof.Dr.Denis CHAUMONT
P02
GRAPHENE NANOPLATELETS FOR POLYMER NANOCOMPOSITES………….….62
MSc. Maihemuti MAIMAITITUERSUN, Prof.Dr.Ahmet Togo GIZ, Prof.Dr.Nilgun BAYDOGAN
P03
SYNTHESIS OF FLEXIBLE POLY (IMIDE SILOXANE) BLOCK
COPOLYMERS………………………………………………………………………...…...63
Turkan DOGAN, Assoc.Prof.Dr. Nesrin KOKEN, Prof.Dr.Nilgun BAYDOGAN
P04
HYDROPHOBIC PROPERTIES OF ZnO COATED NANOCOMPOSITES......................64
Ar.Gör. Osman URPER, Prof.Dr.Nilgun BAYDOGAN
P05
THE EFFECT OF BUBBLES ON POLY(METHYLMETHACRYLATE)
POLYMER..............................................................................................................................66
H. CAKAR, Dr. T. BEL, Prof.Dr. N. YAHYA, Prof.Dr. C. ARSLAN, Prof.Dr. N. BAYDOGAN
P06
POLİMER KOMPOZİT MALZEMER; BOR VE BORÜR ESASLI POLİMER KOMPOZİT
MALZEMELER......................................................................................................................67
Dr. Selim ERTÜRK
P07
APPLICATIONS OF MULTIWALL CARBON NANOTUBES AT POLYMER
MATRIX....................................................................................................................... .........68
MSc. Songul ULAG, Prof.Dr. Nilgun BAYDOGAN
1
Programme
Location: Istanbul Technical University (ITU) ARI 6 Seminar Hall
February 21, 2018; Wednesday PROGRAM
SEMINAR: 9:00-9:25
Presentation on MULTI-SCALE SELF-HEALING NANOCOMPOSITE SHIELDING
MATERIAL, TÜBİTAK 1001 Project with No:115R017
Prof.Dr. Nilgün Baydoğan, Project Coordinator
Istanbul Technical University (ITU), Energy Institute,
SYMPOSIUM
Symposium Program – 1. Day Opening Statement: 9:25-9:30
Chair: Prof.Dr. Sema AKYIL ERENTÜRK, Istanbul Technical University, Energy Institute
Ayben KİLİSLİOĞLU,
Prof. Dr.
Istanbul University,
Engineering Faculty 9:30 – 9:45
Yusuf YAĞCI
Prof. Dr.
Istanbul Technical University,
Faculty of Arts and Sciences 9:45-10:00
Nuray UÇAR,
Prof. Dr.
Istanbul Technical University Faculty of
Textile Technologies and Design 10:00 - 10:15
Mustafa BAKKAL,
Associate Prof.Dr.
Istanbul Technical University,
Engineering Faculty 10:15 - 10:30
Ali Erdem EKEN
PhD.
ASELSAN
Electronics Industry and Trade, Inc. 10:30 - 10:45
Cihat TAŞALTIN, PhD. TUBITAK MAM 10:45 - 11:00
Beril TUĞRUL,
Prof. Dr.
Istanbul Technical University,
Energy Institute 11:00 - 11:15
Coffee Break: 11.15 - 11.30
Chair: Prof. Dr. Hüseyin ÇİMENOĞLU, Istanbul Technical University, Faculty of
Chemical and Metallurgical Engineering
Esra ÖZKAN ZAYİM
Prof. Dr.
Istanbul Technical University,
Faculty of Arts and Sciences 11:30 - 11:45
Hüseyin KIZIL
Associate Prof. Dr.
Istanbul Technical University,
Faculty of Chemical and Metallurgical
Engineering
11:45 - 12:00
Gülşah KAHRAMAN ŞİŞECAM 12:00-12:15
Nursev ERDOĞAN,
PhD.
TAI- Turkish Aerospace Industries, Inc. 12:15-12:30
2
Location: ITU Energy Institute Prof. Dr. Nejat Aybers Seminar Hall
February 21, 2018; Wednesday
Lunch Time 12:30– 14:00
Chair: Prof.Dr. Nilgün BAYDOĞAN
Istanbul Technical University, Energy Institute
Levent TRABZON
Prof. Dr.
Istanbul Technical University,
Engineering Faculty 14:00 - 14:15
Nilgün YAVUZ
Prof.Dr.
Istanbul Technical University,
Energy Institute 14:15 - 14:30
Hülya CEBECİ
Associate Prof. Dr.
Istanbul Technical University,
Faculty of Aeronautics and Astronautics 14:30 - 14:45
Namık Serkan TAŞKIRAN
PhD. TÜBİTAK MAM 14:45 - 15:00
Görkem MEMİŞOĞLU,
PhD. VESTEL Electronics 15:00 - 15:15
Coffee Break: 15:15 - 15:45
Discussions & Think Tank Questions
16:45-17:30
Closing Symposium - Day One
Chair: Prof.Dr. Nilgün YAVUZ
Istanbul Technical University, Energy Institute
Emine ÇOKGÖR
Prof. Dr.
Istanbul Technical University,
Civil Engineering Faculty
15:45 - 16:00
Tuğrul HAKİOĞLU
Prof. Dr.
Istanbul Technical University,
Energy Institute
16:00 - 16:15
Aylin KARAHAN TOPRAKÇI
Assist. Prof. Dr.
Yalova University,
Engineering Faculty 16:15-16:30
Pelin SARITEPE OTANSEV
Assist. Prof. Dr.
Istanbul University,
Science Faculty 16:30-16:45
3
Location: Istanbul Technical University (ITU) ARI 6 Seminar Hall
Symposium Program – 2. Day
February 22, 2018; Thursday
Chair: Assoc. Prof. Dr. Sevilay HACIYAKUPOĞLU,
Istanbul Technical University, Energy Institute
Nilgün KIZILCAN
Prof. Dr.
Istanbul Technical University,
Faculty of Arts and Sciences
9:45 - 10:00
Ömer Suat TAŞKIN
Assist. Prof.Dr.
Istanbul University,
Marine Sciences and Management
Institute
10:00 - 10:15
Tayfun BEL
PhD.
Istanbul Technical University,
Prof.Dr. Adnan Tekin Materials Science
and Production Technologies Applied
Research Center (ATARC)
10:15 - 10:30
Emine TEKİN, Assoc. Prof.Dr TÜBİTAK MAM 10:30 - 10:45
Melis TÜRKER
East Marmara Development Agency,
Kocaeli Support Office, Value Chain
Analyst.
10:45-11:00
Coffee Break: 11.15 - 11.30
Chair: Prof. Dr. Beril TUĞRUL Istanbul Technical University, Energy Institute
Birgül BENLİ
Associate Prof. Dr.
Istanbul Technical University,
Faculty of Mines
11:30 -11:45
Zuhal ER
Assist. Prof. Dr.
Istanbul Technical University,
Faculty of Arts and Sciences
11:45 12:00
Sevilay HACIYAKUPOĞLU
Associate Prof. Dr.
Istanbul Technical University,
Energy Institute
12:00-12:15
Sema AKYIL ERENTÜRK
Prof. Dr.
Istanbul Technical University,
Energy Institute
12:15-12:30
Lunch Time 12:30– 14:00
Chair: Prof. Dr. İskender REYHANCAN, Istanbul Technical University, Energy Institute
Esra GENCELİ Assist. Prof. Dr. ITU, Civil Engineering Faculty 14:00-14:15
Neslihan YUCA, PhD. ENWAIR Energy Technology Company, 14:15-14:30
Said SABBAGH, Dr. Lecturer ITU, Energy Institute 14:30-14:45
Utku CANCİ MATUR,
Assist. Prof. Dr.
Istanbul Gedik University 14:45-15:00
Zeynep CAMTAKAN
Specialist, PhD. Candidate
ITU, Energy Institute 15:00-15:15
4
Location: Istanbul Technical University (ITU) ARI 6 Seminar Hall
Symposium Program – 2. Day, February 22, 2018; Thursday
Coffee Break: 15:15 - 15:45
Chair: Dr. Neslihan YUCA,
ENWAIR Energy Technology Company
Hasan GÖKÇE,
PhD.
Istanbul Technical University,
Prof.Dr. Adnan Tekin Materials Science and
Production Technologies Applied Research
Center (ATARC)
15:45 - 16:00
Selim ERTÜRK
PhD.
Istanbul Technical University,
Prof.Dr. Adnan Tekin Materials Science and
Production Technologies Applied Research
Center (ATARC)
16:00 - 16:15
Aysun EKİNCİ,
PhD. Candidate
Yalova University
Polymer Engineering 16:15-16:30
Nesrin KOKEN
Associate.Prof. Dr.
Istanbul Technical University,
Faculty of Arts and Sciences 16:30-16:45
M. Sahip KIZILTAŞ
Specialist, PhD. Candidate
Istanbul Technical University,
Energy Institute 16:45-17.00
Discussions & Think Tank Questions
17:00-17:30
Closing Symposium - Day Two
5
Poster Presentations February 21, 2018 Saat: 10:00-16:45
Charif TAMIN
PhD. Candidate
Université des Sciences et de la Technologie
d'Oran Mohamed Boudiaf, Oran, ALGERIA
Türkan DOGAN
PhD. Candidate
Istanbul Technical University, Energy Institute
Mahmut MUHEMMETTURSUN
PhD. Candidate
Istanbul Technical University, Graduate School of
Science Engineering and Technology
Songül ULAG
PhD. Candidate
Marmara University,
Institute of Pure and Applied Sciences
Hanife ÇAKAR
MSc.
Istanbul Technical University, Energy Institute
Osman URPER
Research Assistant, PhD. Candidate
Istanbul Technical University, Energy Institute
Selim ERTURK, PhD. Istanbul Technical University, Prof.Dr. Adnan Tekin
Materials Science and Production Technologies
Applied Research Center (ATARC)
6
ABSTRACTS
7
LIST of ORAL ABSTRACTS
O01
“Polimer Nanokompozitler ve Sonokimya”
O02
"Işık ve nanopolimerik malzemeler"
O03
“Nano gümüş, titanyum, CNT ve iletken polimer katkılı nanolif, mikrolif ve uygulama
alanları”
O04
"Otomotiv İçin Kompozit ve Hibrit Hafifletme Çözümleri"
O05
“Kompozit Malzemeler ve Uygulamaları”
O06
“Bioteknoloji Mükemmeliyet Merkezindeki Çalışmalar”
O07
“Radyasyon Zırhı Amaçlı Nanokompozitler”
O08
“Electrospun titanium dioxide nanofibers with natural material”
O09
“Na ion pilleri için SnO2 nanofiber anot malzemesi geliştirilmesi”
O10
“Improving Glass Fiber-Polymer Interfacial Bond Strength using Nano-Clay
Platelets”
O11
“Nanokompozitler ve Havacılık Uygulamaları”
O12
“Mechanical Properties of Nano-Particles Reinforced PU Polymer Nano-Composites”
O13
“Synthesis Of Polyaniline-Doped Boric Acid /Carbon Nanotube Composites and Its
Thermal Propertıes”
8
O14
“Fabrication and Characterization of Ultra-High Performance Conductive
Nanocomposite Filaments For Additive Manufacturing”
O15
“Tüketici Elektroniğinde Polimer ve Nanokompozit Malzemelerin Önemi ve Uygulama
Örnekleri”
O16
“Yiyecek Endüstrisi Atık/Atıksularından Mikrobiyal Biyopolimer ve Biyoplastik Üretimi
O17
“A Brief Overview to Self Healing Materials With the Conceptual and the Oretical
Physics Aspects”
O18
“İletken Polimer Kompozitler ve Uygulamaları”
O19
"Nanokompozitlerin kullanım alanları"
O20
"Clay Modified Nano Composite Ketonic Resins as Fire Feterdant Polyol for Foam
Polyurethane"
O21
“Gözenekli Polimerik Malzemelerin Hazırlanması ve Kendi Kendini Onarabilme ve
Çevre Uygulamaları”
O22
“Kendini Çok Yönlü Onarabilen Nanokompozitler”
O23
“ZnO Nanoparçacıkları ve Nanokompositlerinin OLED Uygulamaları”
O24
“Marmara Bölgesi Kompozit Malzeme Değer Zinciri Analizi”
O25
“Force - Distance spectroscopy, Nanoindentation, Conductive - AFM -
Electrostatic Force Microscopy (EFM)” - “AFM ile tek bir sepiyolit nanofiberinin yüzey
yükü, mekanik ve elektriksel özelliklerinin incelenmesi”
9
O26
“Design, Analysis, Optimization, Production With Composite Materials and
Overview of Current Software Programs for Quality Control”
"Kompozit malzemeler ile tasarım, analiz, optimizasyon, imalat ve kalite kontrol için
güncel yazılım programlarına bakış"
O27
“Polimer ve Nanokompozitlerde Pozitron Annihilasyon Spektroskopisi ve Ani Gama
Aktivasyon Analizi”
O28
"Nükleer Atık Yönetiminde Polimerik Nano-Kompozit Adsorbanların Kullanımı"
O29
“Membran Teknolojilerinin Çevre Mühendisliğindeki Uygulamalari”
O30
“Li-İyon Batarya Uygulamalarinda Si/C Nanokompozitlerin Kullanimi”
O31
“Properties of the irradiated green PVC and its applications in industry and
environment”
O32
“Nanoselülozik elyaf takviyesi ile yenilenebilir kaynaklı polimer nanokompozitlerin
geliştirilmesi”
O33
“Nükleer Güvenlik ve Emniyet Açısından Nanokompozitlerin Operasyonel
Uygulamaları”
O34
"Mekanokimyasal sentezleme ve mekanik alaşımlama yöntemleri ile düşük sıcaklık
koşullarında hibrit kompozitlerin üretimi"
O35
“İnce Film Güneş Hücreleri ve Polimer Nanokompozit Taşıyıcılar”
O36
“Köpük Poliüretanda Yanmazlık Özelliği Sağlayacak Mikro Kürelerin Sentezi ve
Kullanımı”
O37
“Polimer ve Nanokompozit Malzemelerin İTÜ TRIGA MarII Reaktörü Uygulamaları”
10
LIST of POSTER ABSTRACTS
P01
“Cu2ZnSnS4 thin films deposited by dip coating technique for solar cells containing
polymer substrates”
P02
“Graphene Nanoplatelets for Polymer Nanocomposites”
P03
“Synthesis of Flexible Poly(imide siloxane) Block Copolymers”
P04
“Hydrophobic Properties of ZnO Coated Nanocomposites
P05
“The Effect of Bubbles on Poly(Methylmethacrylate) Polymer”
P06
“Polimer Kompozit Malzemer; Bor ve Borür Esaslı Polimer Kompozit Malzemeler”
P07
“Applications of Multiwall Carbon Nanotubes at Polymer Matrix”
11
O01
POLYMERIC NANOCOMPOSITES AND SONOCHEMISTRY
Prof. Dr. Ayben KILISLIOGLU
Istanbul University, Engineering Faculty
ABSTRACT
Novel antibacterial nanomaterials were prepared under ultrasonic irradiation. In these
experimental studies we observed the triggering effect of acoustic energy that caused the
formation of new chemical products with the reactions that cannot be accomplished by
conventional methods.
• Preparation of active metals by reduction of metal salts
• Sonochemical synthesis of particles
• Modification of surface morphology and particle size with inter-particle collisions at
high velocity
12
O02
LIGHT INDUCED SYNTHESIS OF NANOCOMPOSITES
Prof. Dr. Yusuf YAGCI
Istanbul Technical University, Faculty of Arts and Sciences
ABSTRACT
Nano-structured materials can successfully be combined with polymers. Various mehods
including photoinduced electron transfer, polymerizations, click reaction and intercalation
processses allow in situ preparation. These materials exhibit enhanced or new properties.
They find applications in elecronics, biomaterials, high performance materials, etc.
13
O03
NANOPARTIKÜL (GÜMÜŞ, TİTANYUM), CNT VE İLETKEN POLIMER (PANI)
KATKILI NANOLİF, MİKROLİF VE UYGULAMA ALANLARI
Prof. Dr. Nuray UÇAR
İstanbul Teknik Üniversitesi, tekstil Mühendisliği Bölümü, Taksim, İstanbul, TÜRKİYE
ÖZET
Kompozit nanolif veya mikrolifler başta tekstil ve teknik tekstil olmak üzere pekçok kullanım
alanına sahiptir. Bu noktada pekçok nano partiküller ve fonksiyonel polimerler katkı maddesi
şeklinde yapı içerisine katılarak, mevcut matriks polimerin özelliği ve fonksiyonelliği
geliştirilmektedir. Nao veya mikro lifi, mukavemet ve modülüs yönünde güçlendirme, güç
tutuşur kılma, antistatik malzeme haline getirme, elektromanyetik kalkanlama özelliğini
kazandırma, antimikrobiyel özellik kazandırma, kendikendini temizleme özelliğini
kazandırma vb. ana hedeflerden birkaçını oluşturmaktadır. Bu makalede gümüş nitrat tuzu
(AgNO3), Titanyumdioksit (TiO2), Karbonnanotüp (CNT) nano partikülleri ve iletken
polimer polianilin (PANI) ile katkılanmış, fonksiyonelliği geliştirilmiş Poliakrilonitril (PAN)
nanolif ve mikro liflerin üretimi ve özellikleri üzerine çalışma sonuçları sunulacaktır
14
O04
COMPOSITE & HYBRID LIGHTWEIGHT DESIGN SOLUTIONS IN
AUTOMOTIVE INDUSTRY
Prof. Dr. Mustafa BAKKAL
Istanbul Technical University, Engineering Faculty
ABSTRACT
Informations about the researches:
Low Carbon Emission due to environmental issues
Lighter / Cheaper / Aesthetic / Easy Manufacturing
New Design-New Analysis Methods
Mercedes-Benz Turk Truck and Bus R&D Centers
15
O05
KOMPOZİT MALZEMELER VE UYGULAMALARI
Dr. Ali Erdem EKEN
ASELSAN A.Ş. Savunma Sistem Teknolojileri (SST) Sektör Başkanlığı, Mekanik
Teknolojileri Tasarım Müdürlüğü, Ankara,
ABSTRACT
Malzeme teknolojilerindeki gelişmelerin yeni endüstriler yarattığı ve yaşantımızı yeniden
tanımladığı bilinmektedir. Savunma sanayiinde daha yüksek performansta, maliyet etkin ve
güvenilirliği yüksek yeni malzemelere her zaman ihtiyaç duyulmaktadır. Bu çalışmada da
gelecekte savunma sanayiine yön verebilecek kompozit malzeme teknolojileri ve uygulama
alanları değerlendirilmiştir.
16
O06
BİYOMALZEME, BİYOMEKANİK VE BİYOELEKTRONİK
MÜKEMMELİYET MERKEZİ
Dr. Cihat TAŞALTIN
TÜBITAK MAM, Gebze, Kocaeli, TÜRKİYE
ÖZET
TUBITAK MAM Biyomalzeme, Biyomekanik ve Biyoelektronik Mükemmeliyet Merkezi’da
biyomalzeme, biyomekanik ve biyoelektronik konularında çeşitli araştırmalar ve deneyler
yapılmaktadır. Bu, araştırma ve çalışmalar,
Türkiye Sağlık harcamaları
Tıbbi Cihaz & malzeme Alanında Mevcut
Durum –TÜRKİYE-Dünya
3B Mükemmeliyet Merkezi
Mevcut durum
1003 -Erken Evre Akciğer Kanseri Tanısı ve Taramalarında Nefes Havasındaki Uçucu
Belirteçleri Tespit Edebilen Kimyasal Sensör Tabanlı Prototip Cihaz Geliştirilmesi
17
O07
RADYASYON ZIRHI AMAÇLI NANOKOMPOZİTLER
Prof.Dr. Beril TUĞRUL
İstanbul Teknik Üniversitesi – Enerji Enstitüsü Ayazağa Kampüsü – 34469, Maslak –
İSTANBUL
ÖZET
Nükleer enerjinin barışcıl amaçlı kullanımında önemli bir husus nükleer güvenlik olup,
çalışılan radyasyon tipine uygun ve radyasyon şiddetine karşı yeterli nitelikte radyasyon zırhı
kullanılarak ilgili nükleer uygulama faaliyetlerinin yapılması esas olmaktadır. Farklı
radyasyon tipleri için esas itibariyle farklı radyasyon zırhı elemanlarının kullanılması söz
konusu olmaktadır.
Bu çalışmada, öncelikle girici radyasyona karşı nanoteknoloji bağlamında geliştirilen
radyasyon zırhı elemanlar hakkında bilgi verilmektedir. Takiben, özgün bir çalışma
bağlamında geliştirilmiş özel bir kompozit malzeme olan mikro ve nano boyutlu TiB2 katkılı
B4C-SiC kompozit malzeme tanıtılmakta ve mikro ve nano boyutta katkı elemanın
kullanılmasıyla imal edilen ve ileri teknoloji nükleer reaktörlerde zırh elemanı olarak
kullanılabileceği düşünülen radyasyon zırh malzemesinin girici radyasyonu zırhlama özelliği
yapılan deneysel çalışmaların sonuçları verilerek irdelenmektedir.
Anahtar Kelimeler: Girici radyasyon, Kompozit malzemeler, Nanomalzemeler,
Radyasyon Zırh malzemesi,
18
O08
ELEKTRODÖNDÜRME YÖNTEMİYLE HAZIRLANMIŞ ALOE VERA
KATKILI TİTANYUM OKSİT NANOLİFLERİN
ANTİBAKTERİYEL ETKİLERİ
Osman ÜRPER1, Tuğçe KÖROĞLU
2, Prof. Dr. Esra ÖZKAN ZAYİM
3*
1Energy Institute, Istanbul Technical University, Maslak, Istanbul, 34469, Turkey
2Department of Nanoscience and Nanoengineering, Istanbul Technical University, Maslak,
Istanbul, 34469, Turkey
3Department of Physics, Faculty of Sciences and Letters, Istanbul Technical University,
Maslak, 80626 Istanbul Turkey
ÖZET
Titanium dioxide (TiO2) nanomalzemeler; toksik olmamaları, çevre dostu özellikleri,
fotokatalitik yapıları ve antibakteriyel gibi geniş yelpazedeki bu önemli özellikleri, onları
önemli bir araştırma konusu haline getirmiştir. Bu kadar avantajlı özelliklerine rağmen,
antibakteriyel uygulama halen çok geniş bir araştırma sahasına sahiptir. Bu çalışmada
özellikle TiO2’lerin anti bakteriyel özelliklerini daha aktif kullanmak ve geliştirmek amacıyla,
aloe vera jeli katkılaması yapıldı. Aloe Vera içerdiği çeşitli organik yapılar ve onların
iyileştiri özelliği sayesinde antibakteriyel etkiyi hem daha iyi bir seviyeye getirmiş hemde
iyileştirme sürecini hızlandırmıştır. Aloe Vera eklenmesi ile TiO2 yapılı nanolifler
uygulandıkları alandaki enfeksiyon oranını azaltmış, ayrıca çok önemli oranda antibakteriyel
etkiyi arttırmıştır. Aloe Vera eklenmiş TiO2 nanfiberlerin katkısız TiO2 nanoliflere göre 5 kat
daha etkin olduğu tespit edilmiştir
Anahtar Kelimeler: AloeVera, elektrodöndürme, TiO2, nanolif, PVP.
19
O09
EFFECT OF POROSITY IN SNO2 NANOFIBERS AS ANODE MATERIALS FOR
SODIUM-ION BATTERIES
Doç. Dr. Hüseyin KIZIL
Istanbul Technical University, Faculty of Chemical and Metallurgical Engineering
ABSTRACT
Informations about the researches:
Increasing the porosity proved to be beneficial for electrochemical performance.
Highly porous structure compensated the volume expansion and led to better capacity
retention.
Porosity enabled the electrolyte to diffuse better into the material due to increased
surface area.
However, cycling performances of NF-252 and NF-50 were very similar, indicating
that there is a saturation point for the improvement with increasing the porosity.
Increased surface area of nanotubes hindered its ability to perform as well as
nanofibers, due to large SEI formation on its surface.
20
O10
IMPROVING GLASS FIBER-POLYMER INTERFACIAL BOND STRENGTH
USING NANO-CLAY PLATELETS
Gülşah KAHRAMAN*, Dr. Aref CEVAHİR, Şener YILMAZ,
Prof. Selim KUSEFOĞLU, Dr. Vedat Sediroğlu
Atmospheric Coating Technologies Management, Türkiye Şişe ve Cam Fabrikaları A,Ş.
Science &Technology Center
Cumhuriyet Mah. Şişecam Yolu Sokak, No.2 41400 Gebze –Kocaeli Turkey
E-mail address: [email protected]
Phone: +90-850-2060468, Fax: +90-262-6782453
ABSTRACT
Glass-reinforced polymer composites made with thermoplastic polymers are prefered over
thermosets by virtue of their recyclability. The broader use of thermoplastics and the pressing
need for products with higher added value accelerated the development efforts for innovative
glass fiber products based on Polypropylene(PP) and Polyamide(PA) polymers.
Towards this goal, montmorillonite clay, which was intercalated with a suitable quaternary
ammonium salt was incorporated in a glass fiber sizing. This sizing was then used to prepare
glass fibers by the conventional process. The expectation is that the clay additives shall
exfoliate to form nano platelets, induced by the shear stress of the extruder when mixed with
21
PP or PA during the part manufacturing process. This way, clay platelets with 5-15 nm
thickness form a very thin nano-composite film at the thermoplastic/glass fiber interface.
While many examples of nanoclay reinforced thermoplastics can be found in the literature,
this is the first work that places the nano clay reinforcement specifically at the fiber-matrix
interface.
We provide evidence for improved mechanical strength due the extra surface area and bonds
established between the matrix and the fiber phases once nano-clay has been introduced. The
presence of nano-sized clay at the interface also serves to improve the flame retardancy
characteristics of the final composite.
Keywords: Nanoclay, composite, thermoplastics, glass fiber, glass-polymer interface
22
O11
NANOTECHNOLOGY IN AEROSPACE APPLICATIONS
Dr. Nursev ERDOĞAN, Selim DİNÇER
1Advanced Materials Process and Energy Technology Center, Innovation Department,
Turkish Aerospace Industries, Inc., Ankara, 06980, Turkey
ABSTRACT
Recently, micro and nanotechnologies are already being used in various fields of industry and
attracting much attention in defense and aerospace industries. One of the best motivation for
research and development in aerospace industry is decreasing weight and increasing strength
of components. In line with this objective, research for nanotechnology is accelerating.
Besides strength improvement, several functionalities may be introduced to aerospace
platforms using micro and nanotechnologies. Some of these added functionalities are
corrosion resistivity, low RF and IR observabilities, anti/de-icing properties, self-
inspection/healing ability, and providing EMI/EMC requirements. Furthermore, research in
micro- and nanoscale raises consciousness in materials science, characterization as well as
processing. However, the requirements for aerospace industry are quite strict. Numerous
qualification tests must be conducted before certification. Nanotechnology has already been
approved for proof of concept and increasing amount of collaborations between research
centers and companies will accelerate nanotechnology to reach maturity level in near future.
Key Words: Aerospace, nanotechnology, multi-functionality, technology readiness level.
*Corresponding Author: Nursev Erdoğan, PhD, email: [email protected], Tel: 90
312 811 1800, Fax: 90 312 811 1425.
23
O12
MECHANICAL PROPERTIES OF NANO-PARTICLES REINFORCED
POLYURETHANE NANO-COMPOSITES
Zineb BENZAIT MSc., Prof. Dr. Levent TRABZON
Istanbul Technical University, Engineering Faculty
ABSTRACT
Incorporation of nanoparticles can significantly improve the desired properties of the
polymeric nanocomposites. One-dimensional carbon nanotubes (CNTs) as an interesting
additive has demonstrated outstanding mechanical, thermal and electrical properties. SiO2
(silica) nanoparticles have been widely used with polymers to enhance the heat resistance,
radiation resistance, mechanical and electrical properties. Polymeric foams such as
Polyurethane (PU) are a group of lightweight materials, which are suitable for a wide range of
applications such as electrical and thermal insulation, shock and sound absorbents. PU foams
are obtained by the chemical reaction of a polyol or mix of polyol, water and other processing
additives with an isocyanate.
In this work, multi-walled carbon nanotubes (MWCNT) were functionalized by hydrogen
peroxide (H2O2). In the next step, MWCNTs or silica nanoparticles were added to polyol and
were mixed for 15 min. Then, Isocyanate was added to the composition, which was mixed
and poured into the wooden mold. Nanocomposites with various content of MWCNTs, silica
nanoparticles were fabricated up to 1 wt %. Molded nanocomposites were cut in
turningmachine with a thickness of 10 mm and test samples were prepared with CNC
24
machine according to ISO 1926 for tensile tests of rigid cellular plastics and ASTM 6110 for
Charpy impact tests.
The aim of this work is investigating mechanical properties of the nanocomposites with
various contents of MWCNTs and silica nanoparticles such as 0.25, 0.5, 0.75 and 1 wt %.
Tensile, Charpy and hardness tests were carried out and their results were discussed. In
addition, the morphology of the nanocomposites was investigated using scanning electron
microscopy (SEM). As result, the neat PU presents the lowest tensile strength, whereas the
highest strength can be seen in the nanocomposites containing 0.25 wt% Silica-A with 33wt%
improvement, but further Silica-A addition decreased the strength of the PU/Silica-A foam. In
addition, this phenomenon can be seen in adding of Silica-B and MWCNT into the polymer
matrix, which adding 0.25 wt% of Silica-B and MWCNT increased the tensile strength about
27% and 16%, respectively. In order to fabricate nanocomposites with higher CNT content
and prevent the appearance of large agglomerations, hybrid nanocomposites were fabricated,
which could lessen large agglomerations. Hybrid PU/SiO2/MWCNT nanocomposite with the
constant overall content of 0.75 wt% showed higher tensile strength and hardness than either
of nanoparticles at this content, which approves a synergistic effect between MWCNTs and
silica nanoparticles.
25
O13
SYNTHESIS OF POLYANILINE-DOPED BORIC ACID /CARBON NANOTUBE
COMPOSITES AND ITS THERMAL PROPERTIES
Ayşenur Örs, Prof. Dr. Nilgün YAVUZ*
Istanbul Technical University, Energy Institute, 34 469, Maslak, Istanbul, Turkey
ABSTRACT
Carbon nanotubes (CNTs) have been a focus of considerable research since the first
discovered by Lijima [1]. Their remarkable properties, such as mechanical strength,
flexibility, chemical stability, electrical and thermal conductivity behavior have made them
very promising nanomaterials for new applications in chemistry and physics, particularly for
the development of new nanotechnologies and devices [2]. In recent years, incorporating
CNTs into polymeric materials and delivering the properties of these materials to a
processable and synergistic effect have promoted a great interest in developing
multifunctional carbon nanotube composites with other materials [3]. These functional CNT
based composites show eminent prospects and opportunities for new applications in a variety
of areas. Although recent studies show a unique compatibility between polymers and CNT,
the nature of CNT composites remains unclear.
In this study, carbon nanotubes were synthesized by the fluidized-bed CVD synthesis of
acetylene (C2H2) on a magnesium oxide (MgO) powder impregnated with an iron nitrate
(Fe(NO3)3•9H2O) solution. The synthesis parameters were selected as: the synthesis
temperatures of 500 and 800°C, the iron content in the precursor of 5% and the synthesis time
of 30 min. The synthesized material was purified by using HCl and then characterized by
26
transmission electron microscopy, Raman spectroscopy and thermogravimetric analysis. The
purified samples which synthesized temperature of 500 and 800°C consist of mostly multi
walled and single walled carbon nanotubes, respectively. After synthesis of CNTs, the
polyaninine-doped boric acid (PANI-B)/CNT composites were prepared by coagulation
method. Fourier transform infrared (FT-IR) were used to characterize the PANI-B/CNTs
composites. Thermal stability and glass transition temperature (Tg) were measured by
thermogravimetry (TG) and differential scanning calorimetry (DSC), respectively. The TG
and derivative thermogravimetry (DTG) curves indicated that with augment of CNTs content,
the thermal stability of PANI-B/CNTs composites increased continuously. While, Tg
increased and then decreased with the CNTs content increasing from 0 to 20 mass %.
*Corresponding author
References
[1] S. Lijima: Nature 354 (1991) 56.
[2] J.N.R. Rao and A.K. Cheetham: J.Mater. Chem. 11 (2001) 2887.
[3] W. Khan, R. Sharma, P. Saini: In Book: Carbon Nanotubes Chapter 1 (2016) 45.
27
O14
FABRICATION AND CHARACTERIZATION OF ULTRA-HIGH PERFORMANCE
CONDUCTIVE NANOCOMPOSITE FILAMENTS FOR ADDITIVE
MANUFACTURING
MSc. Özge KAYNAN, Ph.D. Candidate. Alptekin YILDIZ,
Assist. Prof.Dr. Elif ÖZDEN-YENİGÜN, Prof. Dr. Hülya CEBECİ*
ITU Aerospace Research Center, Maslak, Istanbul
ABSTRACT
Additive manufacturing (AM), also known as three-dimensional printing (3DP), is a method
that creates parts by material extrusion from the bottom-up one cross-sectional layer at a time.
This manufacturing technology provides fast, flexible, easy production of 3D objects which
can be either simple or complex geometries where CNC may not be an option. Also, 3DP
eliminates the additional post-processes for finishing. Ultra-high performance thermoplastic
filaments are promising raw materials to produce proper structural and/or interior applications
for aerospace by using 3D Printers. In this study, nanocomposite filaments were fabricated by
high-performance thermoplastic matrix polyetherimide (PEI) with multi-walled carbon
nanotubes (MWNTs) at various weight fractions. The nanocomposite filaments are produced
by twin and single screw extrusion processes respectively without using any solvents or
additives. As a result, MWNTs/PEI filaments demonstrated two-fold improvement in tensile
strength and enhancement in electrical conductivity compared to neat PEI filaments. With this
multifunctionality, MWNTs/PEI nanocomposite filaments are a promising candidate for
challenging in aerospace applications.
28
O15
APPLICATIONS OF POLYMER AND COMPOSITE MATERIALS IN CONSUMER
ELECTRONICS
Dr. Gorkem MEMISOGLU1, Burhan GULBAHAR
2
1Vestel Electronics Inc., Organize Sanayi Bolgesi, 45030, Manisa, TurkeyE-mail:
2Department of Electrical and Electronics Engineering and Applied Research Center of
Technology Products, Ozyegin University, 34794, Istanbul, TurkeyE-mail:
ABSTRACT
At the beginning of the 1900's, modern synthetic plastics and in the middle of that century,
polymer composites began to be developed. Over the last few decades, advanced composite
materials have expanded their application areas, and their tendency to improve new product
development and manufacturing technology has increased. Depending on the application area,
polymer composites can be selected according to their properties, such as nanoscale or
microscale dimensions, strength, flexibility, lightness, resistance to environmental conditions
(such as; humidity, sun rays), impact resistance, hardness, thermal expansion coefficients,
cracking-, fracture-, tensile- or bending- strengths. Thanks to properties of composite
materials, they are utilized in diverse set of application areas. Today, engineering, space,
aerospace, automotive and consumer electronics sectors are the major shareholders in the use
of advanced engineering materials. In this study, basic fundamentals and application areas
related to the use of polymer matrix composites in consumer electronics are presented and
discussed.
29
O16
YİYECEK ENDÜSTRİSİ ATIK/ATIKSULARINDAN MİKROBİYAL
BİYOPOLİMER VE BİYOPLASTİK ÜRETİMİ
Prof. Dr. Emine ÇOKGÖR
Istanbul Teknik Üniversitesi, Çevre Mühendisliği Bölümü
ÖZET
Günümüzde sentetik polimer üretimi değerli kaynakların tüketilmesine neden olduğu gibi
ciddi çevresel ve sağlık problemlerini beraberinde getirmektedir. Son yıllarda üretimi ve
kullanımı yaygınlaşan biyobozunur karakterdeki biyoplastikler kimyasal sentez veya
mikrobiyal proseslerle üretilebilmektedir. Biyobozunur bir mikrobiyal biyopolimer olan
polihidroksialkanoatların (PHA) üretim maliyetinin önemli bir kısmını hammadde olarak
kullanılan sentetik organik madde oluşturmaktadır. Bu nedenle besi maddesi olarak ucuz
alternatif kaynakların (karbon içeriği yüksek evsel ve endüstriyel olan atıksular/atıklar)
kullanımı ön plana çıkmakta ve uluslararası ölçekte teşvik edilmektedir. Karbonca zengin
endüstriyel/evsel atıksulardan organik madde giderimini yenilikçi yaklaşımlar arasında
yeralan PHA üretimiyle birleştirmek, çevresel ve ekonomik açıdan sürdürülebilir olmaktadır.
İstanbul Kalkınma Ajansı 2015 yılı Yenilikçi İstanbul Mali Destek Programı kapsamında
desteklenen TR10/15/YNK/0045 kodlu “Uygulamalı Biyopolimer ve Biyoplastik Üretim
Teknolojileri Araştırma Merkezi (UBÜTAM)” İTÜ İnşaat Fakültesi’nde 2016 yılında
30
kurulmuştur. Kurulan merkez sayesinde gerçekleştirilen işbirlikleri vasıtasıyla 1003-KMY-
ANAK-2017-1 Çağrı Kodlu, Yenilikçi Mühendislik Plastiklerinin Endüstriyel Uygulamalar
İçin Geliştirilmesi ve Üretim Süreçlerinin İyileştirilmesi” başlıklı TÜBİTAK 1003 - Öncelikli
Alanlar Ar-Ge Projeleri Destekleme Programı’nda “Yüksek Tuzlulukta Endüstriyel
Fermentasyon Atıksularının Biyopolimer Üretim Potansiyelinin Değerlendirilmesi (2018-
2020)” isimli proje TÜBİTAK tarafından desteklenmiş olup, proje çalışmaları halihazırda
merkezimizde sürdürülmektedir.
31
O17
A BRIEF OVERVIEW TO SELF HEALING MATERIALS WITH
THE CONCEPTUAL AND THE ORETICAL PHYSICS ASPECTS
KENDİNİ İYİLEŞTİREN YAPILARA KAVRAMSAL VE KURAMSAL FİZİK
BOYUTUNDAN KISA BİR BAKIŞ
Prof. Dr. Tuğrul HAKİOĞLU
Istanbul Technical University, Energy Institute
ABSTRACT
The physics of fractal growth provides a great leverage of understanding the microscopic
phenomena taking place in the nanocomposite and self healing materials. In this talk, we
concentrated on the determination of the fractal dimensions in such systems. The knowledge
of the fractal dimension is extremely important during the engineering of these systems since
it provides an estimation of the self healing volume that internal fractures cause. This
information can then be used in the distribution of the nanoparticle size and shape.
32
O18
İLETKEN POLİMER KOMPOZİTLER VE UYGULAMALARI
Dr. Öğr. Üyesi Hatice Aylin KARAHAN TOPRAKÇI*,
Dr. Öğr. Üyesi Ozan TOPRAKÇI
Yalova Üniversitesi Polimer Mühendisliği Bölümü
ÖZET
Polimerler; hafif ve buna rağmen güçlü bir yapıya sahip olması, dayanıklılığı, tokluğunun iyi
olması, uygun maliyet ve bakım giderlerine sahip olması, ısıl izolasyon özelliklerinin yüksek
olması gibi birçok özelliklerinden dolayı yaygın bir şekilde kullanılmaktadır. Tüm bu olumlu
özelliklerinin yanında polimerler elektrik akımını iletmemektedir. Polimerlerin iletken hale
getirilmesi için bazı seçenekler mevcuttur. Bunlardan en yaygını iletken dolgu maddesi
içeren polimer kompozitlerin hazırlanmasıdır. Bu kompozitler elektriksel iletkenlik gerektiren
her türlü elektronik parçada, esnek elektrotlarda, giyilebilir elektroniklerde, iletken
kaplamalarda,, elektromanyetik kalkanlama uygulamalarında, enerji depolama sistemlerinde
ve sensörlerde (biosensörler, kimyasal sensörler, kapasitif sensörler, piezorezistif sensörler
v.s). kullanılmaktadır. Bu çalışmada karbon nanolifi içeren poli(vinil klorür) esaslı
kompozitlerin morfolojik, elektriksel ve elektro-mekenik özellikleri incelenmiştir. Elde
ediilen sonuçlara göre kullanılan polimer, dolgu özellikleri ve test koşullarının elektro-
mekanik özelliklere etkisi olduğu gözlenmiştir.
Anahtar Kelimeler: Esnek iletken kompozitler, karbon nanolifleri, piezorezistif sensörler
33
O19
NANOKOMPOZİTLERİN KULLANIM ALANLARI
Dr. Öğr. Üyesi Pelin SARITEPE OTANSEV
Istanbul University, Science Faculty
ÖZET
20. yüzyılın ikinci yarısından itibaren tekniklerin hızla gelişmesi sonucu, yeryüzünde mevcut
olan ana malzemelerin özellikleri ihtiyaçları karşılamaya yeterli olmamış ve farklı arayışlar
başlamıştır. Bu nedenle hem ekonomik hem daha yüksek mukavemetli ve hem de çok hafif
malzemelerin oluşturulması için çalışmalar yapılmış ve kompozit malzemeler geliştirilmiştir.
Kompozit malzemeler uçak sanayi, savunma sanayi, enerji sektörü, elektronik sanayi, inşaat,
maden, tıp, ilaç sanayi, bio mühendislik, nükleer tıp olmak üzere pek çok alanda yaygın
olarak kullanılmaktadır.
34
O20
CLAY MODIFIED NANO COMPOSITE KETONIC RESINS AS FIRE RETARDANT
POLYOL FOR FOAM POLYURETHANE
Prof. Dr. Nilgün KIZILCAN
Istanbul Technical University, Faculty of Science, Department of Chemistry, 34469-Maslak,
Istanbul, Turkey
ABSTRACT
In this study, in situ modified cyclohexanone formaldehyde resin (CFR) was prepared from
clay (montmorillonite/MMT) and sepiolite in the presence of base catalyst. Different clay
contents (from 0,5 to 5 wt%) were used to produce clay modified nanocomposite ketonic
resins (MM-CFR and Sep.-CFR). The polymeric nanocomposite material prepared by this
method is directly synthesised in one step. These nanocomposites were characterized with
Fourier Transform Infrared Spectroscopy (FTIR-ATR), Nuclear Magnetic Resonance
Spectroscopy (NMR), X-ray Diffractometer (XRD) for structural analysis, Differential
Scanning Calorimetry (DSC) and Thermogravimetric Analyzer (TGA) for thermal analysis.
The obtained samples were also characterised morphologically by Scanning Electron
Microscope (SEM). Then, clay modified nanocomposite resins were used for the synthesis of
fire resistant polyurethane foam.
35
References
1. Kızılcan, N.; Akar, A. J. Appl. Polym Sci. 2005, 98, 97.
2. Kızılcan, N. and Mermutlu, M. J. Appl. Polym.Sci., 2014, 131(6), 2506-2517.
36
O21
PREPARATION OF POROUS POLYMERIC MATERIALS AND
THEIR SELF HEALING AND ENVIRONMENTAL APPLICATIONS
GÖZENEKLİ POLİMERİK MALZEMELERİN HAZIRLANMASI VE
KENDİ KENDİNİ ONARABİLME VE ÇEVRE UYGULAMALARI
Assist.Prof.Dr. Omer Suat TAŞKIN
Istanbul University, Marine Sciences and Management Institute
ABSTRACT
Many solid and powder materials both natural (stones, soils, minerals, etc.) and manufactured
(catalysts, cement, pharmaceuticals, metal oxides, ceramics, carbons, zeolites, etc.) contain a
certain void volume of empty space. This is distributed within the solid mass in the form of
pores, cavities, and cracks of various shapes and sizes. The total sum of the void volume is
called the POROSITY. This study presents some information on natural and manufactured
materials with porosity.
In this study, we investigated the ability of microporous polymers as adsorbent for removal of
heavy metal salts from aqueous solutions. The designed Schiff based network (SNW) with
high specific surface area was synthesized at 180°C for 3 days followed by freeze-drying
process. The porous structure of the material was confirmed by SEM analysis and CO2
37
adsorption/desorption studies at 77.3 K. The role of pH and contact time was examined and
the highest adsorption capacities. Reusability of the system was also demonstrated by
applying four cycles without any significant loss of activity.
38
O22
KENDİNİ ÇOK YÖNLÜ ONARABİLEN NANOKOMPOZİTLER
1 Dr. Tayfun BEL,
1Prof.Dr. Cüneyt ARSLAN,
2Prof.Dr. Nilgün BAYDOĞAN
1 İstanbul Teknik Üniversitesi, Prof.Dr. Adnan Tekin Malzeme Bilimleri ve Üretim
Teknolojileri Uygulama Araştırma Merkezi 34469 Maslak, İstanbul.
2 İstanbul Teknik Üniversitesi, Enerji Enstitüsü Ayazağa Kampüsü, 34469, Maslak, İstanbul
ÖZET
Atom Transfer Radikal Polimerizasyonu (ATRP) yöntemi kullanılarak canlı PMMA yapı elde
edilmesi amaçlanmıştır. PMMA (Polimetil metakrilat) polimere kendini onarma özelliği
kazandırmak amacıyla, polimer solisyonu içine mikro küreler eklenmiştir. Formaldehyd
reçine duvarlı mikro kürelerlerin içi, kendini onarma sıvısı olarak kullanılan, glycidyl
methacrylate dolu olarak üretilmiştir. PMMA solüsyonuna eklenerek, kompozitin mekanik
özellikleri değerlendirilmiştir. Mekanik hasar ardından oluşan, kendini onarma işlemi
sonrasında, yapının mekanik performansındaki değişim incelenmiştir. PMMA yapıya glycidyl
methacrylate dolu mikrokürelerin eklenmesinin polimer kompozit yapının mekanik
özelliklerini geliştirdiği tespit edilmiştir.
39
O23
ZnO NANO-PARÇACIKLARI VE NANO-KOMPOSİTLERİNİN
OLED UYGULAMALARI
Doç. Dr. Emine Tekin*, Rifat KAÇAR, Dr. Selin P. MUCUR,
Dr. Tülay Aslı TUMAY, Dr. Salih DABAK
TÜBİTAK MAM Malzeme Enstitüsü, Gebze, Kocaeli
ÖZET
OLED genel olarak Ca, Al gibi düşük iş fonksiyonu olan metal katot tabakası ve şeffaf anot
tabakası (ITO) arasına organik katmanların kaplanmasıyla elde edilen ve elektrotlar arasına
voltaj uygulandığında ışık veren aygıtlardır. OLED ekran uygulamalarında genelde evrik
OLED yapısı kullanılır. Evrik OLED yapısında Ca, PEDOT:PSS gibi kararlılığa olumsuz
etkileyen malzemeler kullanılmaz. ITO katot olarak, metal elektrot (Au, Ag, Al) anot olarak
görev yapar. Yani yük hareketi tersine dönmektedir. Bu nedenle e- enjeksiyonunu arttırmak
için genelde ZnO elektron iletim katmanı olarak kullanılır. Bu çalışmada ZnO
nanoparçacıklarının sentezinde öncelikle farklı çözücülerin etkisi araştırılmıştır. Yapılan
deneylerde, kullanılan çözücülerin hem ZnO yapısı hem de OLED performansı üzerine
etkileri olduğunu görülmüştür.
Daha sonra ZnO nanoparçacıklarının stabilitesini arttırmak ve film morfolojisini iyileştirmek
amacıyla dallanmış Polietilenimin (PEI) polimeri ile nanokompositler (NC) hazırlanmış ve
elektron iletim tabakası olarak kullanılmıştır. Eloktrostatik kuvvetlerle ZnO yüzeyine tutunan
PEI polimerinin oluşturduğu dipol etkileşimler neticesinde parçacıklar kümeleşmiyor ve daha
40
kararlı olabiliyorlar. Kırmızı, mavi, yeşil ışık veren polimerler seçilerek evrik NC katmanı
içeren OLED üretimi gerçekleştirilmiş ve aygıt performansı üzerindeki etkilerinin
incelenmiştir. Sonuç olarak film oluşturabilme kabiliyeti artması, etkili e- iletimi ve boşluk
engelleme karakteristiği sayesinde yüksek OLED verim ve parıltı değerleri elde edilmiştir.
(Yürütülen çalışmaların bir kısmı TÜBİTAK 1007 (113G035), proje desteğiyle
gerçekleştirilmiştir)
41
O24
MARMARA BÖLGESİ KOMPOZİT MALZEME DEĞER ZİNCİRİ ANALİZİ
Melis TÜRKER
East Marmara Development Agency, Kocaeli Support Office, Value Chain Analyst
ÖZET
“Marmara Bölgesi Kompozit Malzeme Değer Zinciri Analizi” başlıklı çalışmada
Micheal Porter’ın metodolojisi kullanılarak Marmara Bölgesi’nde kompozit malzeme değer
zinciri analizi yapılmıştır. Bu kapsamda değer zincirinin önemli sayılan aktörlerinden
20 tanesi ile mülakatlar gerçekleştirilmiştir. Derinlemesine mülakatlardan, ulusal ve
uluslararası raporlardan, resmi internet sitelerinden elde edilen veriler Porter’ın
“Küme Haritası, Stratejik Segmentasyon, 5 Güç Analizi ve Elmas Modeli” kullanılarak
sentezlenmiştir. Kompozit malzeme aktörlerinden oluşan çalışma grupları ile tespit edilen
sorunlara yönelik ortaya çıkarılan yeni ve rekabetçi segmentler uyarınca projeler
hazırlanmıştır. Yapılan araştırmalar neticesinde “Marmara Bölgesi Kompozit Malzeme Küme
Raporu ve Endüstri Raporu” oluşturulmuştur.
42
O25
ELECTRICAL PROPERTIES OF A SINGLE NANOFIBER OF SEPIOLITE CLAY
BY ATOMIC FORCE MICROSCOPY CONDUCTIVY MODE
Assoc.Prof.Dr. Birgül BENLİ
aIstanbul Technical University, Mining Faculty, Mineral Processing Engineering, Maslak,
34469, Istanbul, Turkey
ABSTRACT
Sepiolite is a fibrous type of clay consists of hydrated magnesium silicates. After sufficiently
liberated and modified with metal ions such as Ag+ and Cu
2+, sepiolite can be used for the
potential of producing antimicrobial and conducting fillers for several applications such as
medicals, next-generation drugs, sensor and active implantable devices. In this study,
electrical conductivity measurements on a single sepiolite nanofiber are investigated by AFM
conductivity modes (I-AFM) and electrostatic force microscopy (EFM). According to their
adsorption isotherms, optimum metal uptakes of the beneficiated fibers were determined as 50
mg/g of Ag+ and 80 mg/g of Cu
2+. The results show that the electrons were transferred rapidly
to the surface of silver loaded fibers compared to the copper ones. However, there are no
electrical properties seen on raw sepiolite which is expected. Finally, we compared the
electrical properties with antibacterial properties of the fibers and provide comparative
understandings of how antibacterial fillers behave in biodegradable innovative clay thin films,
coatings and their applications.
Keywords: AFM, electrical conductivity, antibacterial clay, sepiolite
43
O26
OVERVIEW of CURRENT SOFTWARE PROGRAMS for
DESIGN, ANALYSIS, OPTIMIZATION, PRODUCTION and
QUALITY CONTROL with COMPOSITE MATERIALS
KOMPOZİT MALZEMELER İLE
TASARIM, ANALİZ, OPTİMİZASYON, İMALAT VE KALİTE KONTROL İÇİN
GÜNCEL YAZILIM PROGRAMLARINA BAKIŞ
Assist.Prof.Dr. Zuhal ER
Istanbul Technical University, Faculty of Arts and Sciences, Maslak,34469, Istanbul, Turkey
ABSTRACT
There are several software programs and tools for the analysis of composites. These computer
programs and tools service the several opportunities to understand and precious of
composites’ behaviour. All the computer opportunities are constructed via programming
languages. Comparison of software opportunities and the languages were held in this study.
Furthermore, results of my own code for the user interface application in windows O/S were
presented.
44
O27
POLİMER VE NANOKOMPOZİTLERDE
POZİTRON ANNİHİLASYON SPEKTROSKOPİSİ VE
ANİ GAMA AKTİVASYON ANALİZİ
Doç.Dr. Sevilay HACIYAKUPOĞLU
Istanbul Technical University, Energy Institute Maslak,34469, Istanbul, Turkey
ÖZET
Ani Gama Aktivasyon Analizi (Prompt Gama Activation Analysis, PGAA) , Bilimsel ve
teknolojik gelişmeler, yeni analitik yöntemlere duyulan gereksinim, Hızlı sonuç alınan,
elemental seçiciliği ve duyarlılığı yüksek olan nükleer yöntemlerin öne çıkması, Nükleer
yöntemlerde genellikle kullanılan girici radyasyonun yalnızca yüzeylerin değil, tüm
malzemenin incelenmesine olanak vermesi nedenleri ile önemli bir analiz yöntemidir.
PGAA yöntemi, nötron aktivasyon analiz yöntemine ilaveten kimyasal analiz için elverişli
olan nükleer yöntemlerden biridir. PGAA nötron kaynakları kullanılarak geliştirilmiş olsa da,
genellikle nükleer reaktör tesislerinde yer alır. PGAA malzemelerin incelenmesinde, tıpta
teşhiste, jeolojik araştırmalarda yerinde analizde kullanılır. Bu bildiride, polimer ve
nanokompozitde PGAA uygulamaları belirtilmiştir.
45
O28
USABILITY OF POLYMERIC NANOCOMPOSITE ADSORBENTS IN NUCLEAR
WASTE MANAGEMENT
Prof. Dr. Sema AKYIL ERENTÜRK
Istanbul Technical University, Energy Institute, 34469 Maslak-Istanbul / TURKEY
ABSTRACT
The long-lived radionuclides in radioactive waste have been considered to be dangerous
pollutants, and their migration with groundwater is strongly affected by adsorption on the
geologic materials. Many inorganic and organic adsorbents have been used for the treatment
of radioactive and industrial wastes, even though they have some limits for extensive
application. The composite adsorbents are a special class of adsorbents developed to improve
processes of separation, concentration or removal of metal ions from solutions. They have
attracted attention as adsorbent materials in recent years.
This work aims to investigate the ability of the polymeric nanocomposite adsorbent prepared
by mixing of polyacrylonitrile (PAN) and clinoptilolite to remove UO2, Th, 226
Ra and 210
Po
from aqueous solutions testing the influence of specific process parameters such as initial
concentration, pH, contact time and temperature. The composite adsorbent has been prepared
from inorganic adsorbent, a natural zeolite clinoptilolite, as an active component and
polyacrylonitrile (PAN) as a binding polymer. The adsorption behaviour of uranium,
46
thorium, radium and polonium from aqueous solutions by polymeric nanocomposite
adsorbent has been investigated by a column technique. The uranium and thorium were
determined spectrophotometrically using Arsenazo III method as complexing agent at 665 nm
against reagent blank, employing Shimadzu UV–vis 260 Spectrophotometer. 226
Ra and 210
Po
were counted using ZnS(Ag) scintillation alpha counter (Eberline, SAC-4 model). The rapid
removal of U, Th, 210
Po and 226
Ra from aqueous solutions with quite high adsorption yield
above 90% using an efficient composite adsorbent was performed in a very short span of
time. The thermodynamic parameters such as free energy (G), enthalpy of adsorption (H)
and entropy (S) were found for each radionuclides. These parameters indicate that
adsorption is exothermic and spontaneous for 210
Po and 226
Ra and endothermic for U(VI),
Th(IV) ions. Change in activation enthalpy (H), free energy of adsorption (G) and entropy
(S) reveals the spontaneous and endothermic nature of adsorption process.
47
O29
İNCE FİLM NANOKOMPOZİT İNCE BOŞLUKLU (HOLLOW FİBER)
NANOFİLTRASYON MEMBRANLARIN ÜRETİMİ VE İÇME SUYU
ARITIMI AÇISINDA DEĞERLENDİRİLMESİ
Dr. Öğr. Üyesi Esra ATEŞ GENCELİb,c*
, Ar. Gör. Reyhan ŞENGÜR-TAŞDEMİRa,b
,
Ar.Gör. Melike ÜRPERb,c
, Türker TÜRKENb,c
, Prof.Dr. İsmail Koyuncub,c
aİstanbul Teknik Üniversitesi, Nanobilim Nanomühendislik Programı, 34469, Maslak,
İstanbul, Türkiye
bProf. Dr. Dincer Topacık Ulusal Membran Teknolojileri Araştırma Merkezi, MEMTEK,
İstanbul Teknik Üniversitesi, 34469, İstanbul, Türkiye
cİstanbul Teknik Üniversitesi, Çevre Mühendisliği Bölümü, 34469, Maslak, İstanbul, Türkiye
ÖZET
Nanofiltrasyon membranların içme ve atıksu arıtımında kullanımı gün geçtikçe
yaygınlaşmaktadır. Bunun nedeni standartlara getirilen sınırlamaların artması ile
konvansiyonel sistemlerin bu sınırlamaları sağlamakta zorlanması ve membran prosesler ile
elde edilen suyunyüksek çıkış suyu kalitesine sahip olmasıdır. Nanoteknolojideki gelişmeler
ile nanokompozit malzemelerin membran üretiminde kullanılması, membranların geçirgenlik,
seçicilik ve mekanik dayanım özelliklerinde olumlu gelişmeler yaşanmasına neden olmuştur.
Nanofiltrasyon membranlar, ultrafiltrasyon membranlar ile ters osmoz membranlar arasında
yer almaktadır. Nanofiltrasyon membranlar düşük enerji tüketimi ve yüksek akılar nedeni ile
48
su arıtımında tercih edilmektedirler. Bu çalışmanın amacı arayüzey polimerizasyonu ile
üretilen nanokompozit katkılı ince film kaplama (İFNK) ince boşluklu (hollow fiber)
nanofiltrasyon membranların üretimi, karakterizasyonu ve organik madde giderim
performansının belirlenmesidir. İnce film nanokompozit kaplama çalışmalarında
nanoparçacık olarak 3 farklı konsantrasyonda (0,01; 0,05; 0,2) TiO2 kullanılmıştır. Çalışma
sonucu nanoparçacık katkılı membranların akısında artış belirlenmiştir. Elde edilen sonuçlar
nanoparçacık katkısız membrana göre standardize edildiğinde, organik madde giderimi
açısından en iyi performansın %0,2 TiO2 nanoparçacık ile üretilen İFNK membranlarda elde
edildiği belirlenmiştir.
49
O30
Lİ-İYON BATARYA UYGULAMALARİNDA
Sİ/C NANOKOMPOZİTLERİN KULLANİMİ
Dr. Neslihan YUCA
ENWAIR Energy Technology Company, Istanbul, Turkey
ABSTRACT
Lityum iyon bataryalarda anot malzemesi olarak Si/C kompozitlerin kullanılması oldukça
önemli avantajlar sağlamaktadır. Silisyumun, grafit ile kıyaslandığında teorik olarak 10 kat
daha yüksek spesifik kapasitesini, karbonun iletkenlik ve mekanik dayanım sağlaması ile
birleştirmek, oldukça yüksek performanslı anot malzemeleri elde edilebilmesine imkan
vermektedir.
50
O31
PROPERTIES OF THE IRRADIATED GREEN PVC AND ITS
APPLICATIONS in INDUSTRY AND ENVIRONMENT
Dr. Said SABBAGH
Nuclear Researches Division, Energy Institute, Istanbul Technical University (ITU).
ABSTRACT
PVC free from the hazardous materials is the golden goal in the Plastic Business. The
future of the PolyVinyl Chloride PVC industry is under investigation, because of the
recycling problems, the heavy metals contamination, like Lead, Cadmium, Mercury, Arsenic,
Antimony, organochlorines, and the Lower-molecular-weight phthalates .
In this review, the use of Pb, Hg, Cd, Hexavalent chromium, As, Sb, and the phthalates
(PBB), (PBDE), (DEHP), (BBP), (DBP), and (DIBP) in PVC`s industry was analysed. The
restriction of DEHP, BBP, DBP and DIBP in the medical devices was also reviewed . In
addition, Influence of Gamma and Electron Beam Irradiation (X-rays) on The mechanical
properties of the new or green PVC is important for health and industry . The PVCs materials
used in the nuclear power plants (NPP) should be investigated in advance, and replaced after
certain time . The importance of knowledge about the heavy metals, for PVC producers is
vital for the future.
Keywords: Heavy metals, PVC, plastic, Industry, green products, phthalates, Enivronment.
51
O32
NANOSELÜLOZİK ELYAF TAKVİYESİ İLE YENİLENEBİLİR KAYNAKLI
POLİMER NANOKOMPOZİTLERİN GELİŞTİRİLMESİ
Dr. Aysun EKİNCİ, Dr. Öğr. Üyesi Gülay BAYRAMOĞLU1
1Polimer Mühendisliği Bölümü, Mühendislik Fakültesi, Yalova Üniversitesi, 77100, Yalova,
Türkiye
ÖZET
Son yıllarda, çevresel ve ekonomik kaygıların artış göstermesi nedeniyle yenilenebilir
kaynaklı malzemeler üzerine akademik ve endüstriyel alanda yapılan çalışmaların sayısında
önemli artışlar görülmektedir. Yenilenebilir kaynaklardan elde edilen polimerler, düşük
maliyet, çevre dostu ve kolay ulaşılabilir hammadde kaynağı olma gibi avantajlar
sağlamaktadır. Bu bağlamda bitkisel yağlar, kaynak bitki çeşitliliği ve bitkiye göre yapısal
çeşitlilik gibi avantajlarına bağlı olarak polimerlerin üretilmesinde büyük potansiyel
sergilemektedir. Bitkisel yağların yapısında yer alan çift bağların epoksidasyonu ile elde
edilen epokside bitkisel yağlar, oluşturulan oksiran halkalarının modifikasyonu ile doğrudan
kaplama malzemesi olarak kullanıldığı gibi polimer kompozitler/ nanokompozitler için matris
olarak kullanılabilmektedir. Epoksidasyon reaksiyonu sonucu epoksi fonksiyonu
kazandırılmış yağlar çeşitli polimerizasyon yöntemleri ile bitkisel yağ esaslı epoksi reçine,
poliüretan ve akrilik reçine olarak farklı uygulamalarda kullanılmaktadır. Bitkisel yağlara
benzer şekilde yenilenebilir kaynaklardan üretilen nanoselülozik elyaflar,
kompozit/nanokompozit uygulamalarında toksik olmaması, biyo-bozunur ve biyo-uyumlu
52
olması gibi üstün özellikleri sayesinde giderek daha çok tercih edilmektedir. Bu çalışmada,
sürdürülebilir kaynaklar kullanılarak yeni tür nanokompozitlerin üretilmesi hedeflenmiştir. Bu
amaçla takviyelendirici olarak tarımsal atıklardan nano selüloz elyaflar üretilirken bitkisel
yağlardan da polimerik matris olarak epokside yağlar sentezlenmiştir. Sentezlenen epokside
yağlar diizosiyanat bileşikleri kullanılarak kürlenmiş ve farklı nanokompozit formülasyonları
geliştirilmiştir. Hazırlanan nanokompozitlerin termal kararlılıkları TGA, morfolojileri SEM
ve kürlenme davranışları FTIR ile incelenmiştir.
Anahtar kelimeler: epokside yağ, nanokompozit, nanoselüloz
Teşekkür: TÜBİTAK tarafından 114M828 nolu proje kapsamında desteklenmiştir.
53
O33
NÜKLEER GÜVENLİK VE EMNİYET AÇISINDAN
NANOKOMPOZİTLERİN OPERASYONEL UYGULAMALARI
Yük.Müh. Zeynep CAMTAKAN
Istanbul Technical University, Energy Institute
ÖZET
Nanokompozitler ve polimer tabanlı nanokompozitler, başta uçak, otomotiv ve elektronik
sanayi olmak üzere bir çok uygulama alanında kullanılan ve geliştirilen malzemelerdir. Bu,
araştırma ve çalışma konularında yapılan çeşitli araştırma ve çalışmalara bu bildiride
değinilmiştir.
54
O34
MEKANOKİMYASAL SENTEZLEME VE MEKANİK ALAŞIMLAMA
YÖNTEMLERİ İLE DÜŞÜK SICAKLIK KOŞULLARINDA HİBRİT
KOMPOZİTLERİN ÜRETİMİ
Dr. Hasan GÖKÇE
İstanbul Teknik Üniversitesi, Prof.Dr. Adnan Tekin Malzeme Bilimleri ve Üretim
Teknolojileri Uygulama Araştırma Merkezi 34469 Maslak, İstanbul.
ÖZET
Mekanokimyasal sentezleme ve mekanik alaşımlama yöntemleri ile düşük sıcaklık
koşullarında hibrit kompozitlerin üretimi geliştirilmesi ve karakterizasyonu çalışmaları
hakkında bilgi verilmiştir.
55
O35
İNCE FİLM GÜNEŞ HÜCRELERİ VE POLİMER NANOKOMPOZİT TAŞIYICILAR
Dr. Öğr. Üyesi Utku CANCİ MATUR1,2*,
Prof.Dr. Nilgün BAYDOĞAN1
1Enerji Enstitüsü, Istanbul Teknik Üniversitesi, 34469, Istanbul, Türkiye
2Gedik Meslek Yüksekokulu, Gedik Universitesi, 34906, Istanbul, Türkiye
ÖZET
Teknolojinin gelişmesi ile beraber enerji ihtiyacının artışı, alternatif enerji kaynaklarına ilgiyi
artırmıştır. Alternatif enerji kaynaklarından olan güneş enerjisi, tükenmez, kirlilik içermeyen,
elektriksel verimliliği yüksek, gelecekteki enerji ihtiyacını, daha yaygın bir şekilde
karşılayabilecek düzeye ulaşabilecek, cazip bir kaynaktır. Güneş pili, güneş enerjisini
doğrudan elektrik enerjisine dönüştüren, yarıiletken bir diyot gibi çalışan, taşıma kayıpları ve
masrafı az olan yenilenebilir enerji kaynaklarımızdan biridir. Güneş pilleri, tek kristal ve çok
kristalli silisyum güneş pilleri, ince film güneş pilleri, yoğunlaştırıcı sistemli pilleri olmak
üzere üç farklı fotovoltaik teknoloji ile üretilirler. Kristal silisyum güneş pilleri birinci nesil
güneş pili teknolojisi olarak bilinmektedir. İkinci nesil güneş pilleri denildiğinde ise, amorf
silisyum (a-Si), kadmiyum tellür (CdTe), bakır indiyum galyum diselenit (CIGS) ve ince film
kristal silisyum gibi ince film güneş pilleri ifade edilmektedir. İnce film güneş pillerinin
üretimine başlanmasındaki en büyük sebep, daha düşük üretim maliyetleriydi. Silisyum güneş
pili panelleri 100 cm2 alana sahip bağımsız güneş gözelerinden meydana gelirken, ince film
güneş pilleri ise çok daha geniş alanlarda üretilebilmekte, bu da büyük ölçekli üretimler için
56
maliyeti düşüren bir faktördür. Bu çalışma kapsamında ince film güneş pillerinden, radyasyon
dayanımı ve soğurma katsayısı yüksek CIGS ince film güneş pilleri incelenmiştir.
İnce film güneş pilleri yapılarına ve kimyasal içeriklerine bağlı olarak farklı taşıyıcılar üzerine
kaplanabilmektedir. İnce film güneş pillerinde altlık olarak soda kireç cam (SLG), paslanmaz
çelik, titanyum (Ti), alüminyum (Al) ve poliimid malzemeler kullanılmaktadır. CIGS ince
film güneş pilleri esnek özelliğe sahip oldukları için SLG ve paslanmaz çelik altlıkların
yanısıra polimer folyo üzerine püskürtme, elektron demeti buharlaştırma ve sol-jel daldırma
tekniği gibi farklı metodlarala kaplanabilmektedirler. Esnek altlıklar, polimer ve metal levha
olmak üzere iki ayrı kategoride incelenmektedir. Altlık olarak kullanıcak olan polimer özel
olarak ısıya dayanıklı olabilecek şekilde seçilmelidir. Polimer altlıklar en yüksek 450° C-500°
C sıcaklık değerlerine kadar dayanabilmekte olup bu değer normal şartlarda sıklıkla
kullanılan cam altlıklar üzerine kaplama yöneteminden ~100 K kadar düşüktür. Altlık olarak
kullanılan metal levhalar herhangi bir bozulmaya uğramadan yüksek sıcaklıklara kadar
dayanabilmektedir fakat bu tip altlıklarda güneş pilinin fotovoltaik özelliklerini negatif yönde
etkileyen altlıktan soğurucu tabakaya kirliliklerin taşınması gibi problemler
gözlemlenebilmektedir.
Anahtar Kelimeler: İnce film güneş pilleri, CIGS ince film, Altlık.
57
O36
KÖPÜK POLİÜRETANDA YANMAZLIK ÖZELLİĞİ SAĞLAYACAK
MİKRO KÜRELERİN SENTEZİ VE KULLANIMI
Doç.Dr. Nesrin KÖKEN1, Görkem ÜLKÜ
2
1İstanbul Teknik Üniversitesi, Fen Edebiyat Fakültesi,Kimya Bölümü, Maslak, 34469,
İstanbul, Turkey
2İstanbul Teknik Üniversitesi, Fen Bilimleri Enstitüsü, Polimer Bilim ve Teknolojisi
Öğrencisi, Istanbul, 34469, Turkey
ÖZET
Polyüretanlar yapılarında üretan bağları içeren organik polimerlerdir. Poliüretanlar genellikle
bir poliolün bir diizosiyanatla reaksiyonuyla elde edilir. Mikrokapsülleme, çeşitli
kimyasallara küçük bir katı parçacık veya sıvı damlacığı mikron çapında kaplayarak
kapsülleme tekniğidir. Bu kaplanan madde; ilaç, protein, alev geciktirici, antimikrobiyal, boya
veya kozmetik gibi bir kimyasal madde olabilir. Kaplanan malzeme çekirdek kaplama
malzemesi kabuk veya duvar malzemesi olarak adlandırılır [1]. Tris-(2-kloropril)-fosfat
(TCPP) poliüretan köpükte alev geciktirici olarak çok kullanılan organofosfor esterlerinden
biridir [2]. Bu çalışmanın amacı, melamin formaldehit reçinesi ile kapsüllenmiş TCCP elde
etmek ve bunu poliüretan köpük yapımında kullanmaktır. Mikrokapsüller süspansiyon
polimerizasyonu ile sentezlendi [3].
58
SEM sonuçları, köpüğün morfolojisinin, mikrokapsüllerin eklenmesiyle önemli ölçüde
etkilenmediğini gösterdi. PU köpüğündeki mikrokapsüllerdeki TCPP'nin difüzyonunun,
kullanım sırasında mikrokapsüller içinde olmasından dolayı çok daha yavaş olması beklenir
ve mikrokapsüllerin kabuğunun ayrışmasıyla yangın sırasında yangın geciktirici olarak
hareket etmesi için serbest bırakılır. Ayrıca, Melamin kabuk yapısının da PU'nin yangın
geciktirici performansına olumlu etkisi vardır.
Kaynaklar
[1] Ghosh, S. K. (2006). Functional Coatings and Microencapsulation: A General (s.15-16).
Weinheim: WILEY- VCH Verlag GmbH & Co. KGaA.
[2] Meng, L. M. (2010). A dual mechanism single-component self-healing strategy for
polymers. Journal of Material Chemistry, 20(29), 5969-6196.
[3] W.Föllmann, J.Wober ‘’ Investigation of cytotoxic, genotoxic, mutagenic, and estrogenic
effects of the flame retardants tris-(2-chloroethyl)-phosphate (TCEP) and tris-(2-
chloropropyl)-phosphate (TCPP) in vitro ‘’ Toxicology Lett-ers,161 (2006) 124-134
59
O37
POLİMER VE NANOKOMPOZİT MALZEMELERİN
İTÜ TRIGA MARK-II REAKTÖRÜ UYGULAMALARI
Yük.Müh. M. Sahip KIZILTAŞ
Istanbul Technical University, Energy Institute
ÖZET
İ.T.Ü. TRiGA Mark-II Reaktörü, 11 Mart 1979 tarihinde kritik yapılmış ve TRIGA
Reaktörlerinin 54'üncüsü olarak işletmeye açılmıştır.
TRIGA adı “Training Research Isotope Production General Atomic” kelimelerinin ilk
harflerinden meydana gelmiştir. Mark-II ise, muhtelif TRIGA Reaktör tipleri arasında yer
seviyesi üstünde inşa edilen ve kalbi sabit bir tipin adıdır.
İ.T.Ü. TRIGA Mark-II Eğitim ve Araştırma Reaktörü; hafif su soğutuculu, grafit yansıtıcılı ve
zenginleştirilmiş uranyum yakıtın-zirkonyum hidrit yavaşlatıcı ile homojen bir şekilde
karıştırılmasıyla meydana gelen katı yakıt elemanları ile çalışan açık tank tipi bir reaktördür.
Sürekli (steady state) ve darbeli (pulsing) çalıştırılabilir. Sürekli çalışmada 250 kW ve darbeli
çalışmada ise çok kısa bir zaman aralığı için 1200 MW güç seviyelerine çıkmaktadır.
TRIGA Mark-II Reaktörünün yakıt elemanları, uranyum yakıt ile zirkonyum hidrit yavaş-
latıcının homojen bir karışımı olup, U-ZrH1.6 "ani negatif sıcaklık katsayısına sahiptirler.
Reaktörde meydana gelen herhangi bir ani güç artması, aynı anda yakıt-yavaş¬latıcının
sıcaklığının artmasına ve bunun neticesinde de yavaşlatıcının yavaşlatma özelliğinin
azalmasına, ani ola¬rak reaktivitenin düşmesine neden olmakta ve milisaniyeler mertebesinde
bir zaman süresinde reaktör gücü otomatik ola¬rak azalmaktadır. Bu özellik yalnız TRIGA
Reaktörlerinde vardır ve bu nedenle de "kendiliğinden emniyetli reaktörler" diye de
60
tanımlanmaktadırlar.
Nötron Kaynağı:
Reaktör kritik yapılabilmesi için Nötron kaynağı olarak özel muhafazası içinde 3 Ci
şiddetinde Amerisyum-Berilyum kullanılmaktadır.
Kontrol Çubukları:
Reaktörde üç adet kontrol çubuğu vardır.
1- Darbe Çubuğu (Transient Rod )
2- Güvenlik Çubuğu ( Safety Rod )
3- Ayar Çubuğu ( Regulation Rod )
Kontrol çubuklarının üçü de sinterlenmiş boron karbürden ( B10C4 ) yapılmıştır.
61
P01
CU2ZNSNS4 THIN FILMS DEPOSITED BY DIP COATING TECHNIQUE FOR
SOLAR CELLS CONTAINING POLYMER SUBSTRATES
Ph.D. Candiate Charif TAMIN1, Prof.Dr. Mohamed ADNANE
1, Prof.Dr. Nilgun BAYDOGAN
2,
Prof.Dr. Denis CHAUMONT3
1 Département de Technologie des Matériaux, Faculté de physique, Université des Sciences et de la
Technologie d’Oran Mohamed Boudiaf, El M’naouar BP 1505 Bir El Djir 31000 Oran, Algérie.
2 Istanbul Technical University, Energy Institute, 34469, Maslak, Istanbul, Turkey
3ICB, Université de Bourgogne Franche-Comté UBFC, BP 47 870, 21078 Dijon, France
ABSTRACT
The use of Cu2ZnSnS4 thin films deposıted by dip coating technique application was
evaluated for solar cells containing polymer substrates in this study. Hence, this work deals
with the elaboration and characterization of Cu2ZnSnS4 thin films (CZTS) by a simple and
economical technique using chemical processes. In this research, the CZTS thin films were
derived from sol-gel dip coating method. Then, we have studied the effect of annealing on the
optical properties of CZTS thin films using UV/Visible spectrophotometer. The SEM images
show a homogeneous zone with the presence of crack on the thin film surface for the use of
the solar cells containing polymer substrates.
Keywords: CZTS, Thin films, Sol-gel, Polymer
62
P02
GRAPHENE NANOPLATELETS FOR POLYMER NANOCOMPOSITES
1Ph.D. Candidate Maihemuti MAIMAITITUERSUN,
1Prof.Dr. Ahmet Togo GIZ,
2Prof.Dr. Nilgun BAYDOGAN
1Istanbul Technical University, Department of Physics, Istanbul Technical University
2Istanbul Technical University, Energy Institute, 34469, Maslak, Istanbul, Turkey
ABSTRACT
GNPs nanofiller homogeneously dispersed in the PMMA polymer matrix via in situ
polymerization method and their characterization was performed in this study.Because, GNPs
nanofiller with a big proportion of surface atoms have higher surface area to volume ratio.
Besides, GNPs have been considered as a potential alternative nanomaterial to Reduced
Graphene Oxide (RGO). Due to higher amount of surface, their interparticle forces such as
Vander Waals forces, electrostatic forces and magnetic attraction forces become stronger and
increase the surface energy of nanomaterials.
63
P03
SYNTHESIS OF FLEXIBLE POLY(IMIDE SILOXANE) BLOCK COPOLYMERS
Ph.D. Candidate Turkan DOGAN1*
,
Assoc.Prof.Dr. Nesrin KOKEN2, Prof.Dr. Nilgun BAYDOGAN
1
1Istanbul Technical University, Energy Institute, 34469, Maslak, Istanbul, Turkey
2Faculty of Arts and Science, Istanbul Technical University, Department of Chemistry,
34469, Istanbul, Turkey
ABSTRACT
Poly(imide siloxane) monomer blocks which are produced from the combination of
polysiloxane and polyimide has processable property [1]. Flexible block copolymers were
synthesized by using Benzophenone-3,3’,4,4’- tetracarboxylic dianhydride (BTDA),4,4’–
Oxydianiline (ODA) and Polydimethylsiloxane, bis(3– aminopropyl) (APPS). BTDA and
APPS composed soft block of the copolymer. The length of polysiloxane soft blocks
increased with increasing the length of polyimide hard block. These materials have a potential
usage as substrates in several industrial areas.
Keywords: Polysiloxane / Poly(imide siloxane)(PIS) / Copolymer
References
1. Turkan Dogan, , Nesrin Koken, Nilgun Baydogan, Production of Poly(imide siloxane)
Block Copolymers, Energy Systems and Management pp 209-215,
64
P04
HYDROPHOBIC PROPERTIES OF ZnO COATED NANOCOMPOSITES
Ar.Gör. Osman URPER, Prof.Dr.Nilgun BAYDOGAN
Istanbul Technical University, Energy Institute, Maslak, 34469, Istanbul, Turkey
ABSTRACT
Recent years, researchers have done various experiments on different geometrical shapes of
nanomaterials because of their different geometrical shapes have gained them significant
properties such as electrical, optical and water repellency. Due to the intensive demand for the
development of hydrophobic surfaces in applications, hydrophobic researches on ZnO
materials has exponentially grown at last decade. One of the main advantages of the ZnO
materials is relatively controllable and easiness to produce various surface morphologies on
wetting property. Although the various synthesis approaches of ZnO materials such as
thermal oxidization, hydrothermal method, chemical etching, spray coating technique, the
electrochemical method, and others, dip coating is the easiest and cheapest technique for ZnO
synthesis. this review is a representation of the recent achievement on ZnO superhydrophobic
surfaces.
Keywords: Hydrophobic, ZnO, nanocomposite, dip coating
Anahtar Kelimeler: ZnO, Nanomalzemeler, Hidrofobik
65
References
[1] X. Wang, C.J. Summers, Z.L. Wang, Nano Lett. 4 (2004) 423.
[2] C.S. Rout, C.N.R. Rao, Nanotechnology 19 (2008) 285203.
[3] K.X. Yao, H.C. Zeng, Langmuir 24 (24) (2008) 14234.
66
P05
THE EFFECT OF BUBBLES ON POLY(METHYLMETHACRYLATE) POLYMER
MSc. H. CAKAR1, Dr. T. BEL
2,
Prof.Dr. N. YAHYA3, Prof.Dr. C. ARSLAN
2, Prof.Dr. N.BAYDOGAN
1
1 Energy Institute, Istanbul Technical University, 34469, Istanbul, Turkey,
2 Department of Metallurgical and Materials Engineering, Istanbul Technical University,
Istanbul, Turkey
3 Universiti Teknologi PETRONAS, Department of Fundamental and Applied Science ,
Malaysia
ABSTRACT
The modification of PMMA materials was provided by the application of a suitable degass
process to obtain the porous structure. The application of a suitable of degass process has
enhanged the affordable weight reduction. Gamma transmission technique was used in order
to examine the details on high precision processing and fabrication of the modified PMMA
polymer as the affordable weight reduction of PMMA polymer supported for their use in
high-volume vehicles and components.
67
P06
POLİMER KOMPOZİT MALZEMER; BOR VE BORÜR ESASLI POLİMER
KOMPOZİT MALZEMELER
Dr. Selim ERTÜRK
İstanbul Teknik Üniversitesi, Prof.Dr. Adnan Tekin Malzeme Bilimleri ve Üretim
Teknolojileri Uygulama Araştırma Merkezi 34469 Maslak, İstanbul.
ÖZET
Bu çalışmada, polimer kompozit malzemer, bor ve borür esaslı polimer kompozit
malzemelerin yapısal karakteristik özellikleri karşılaştırılmıştır. Polimer kompozit
malzemerin, bor ve borür esaslı polimer kompozit malzemelerin, karakteristik özellikleri göz
önüne alınarak, kullanım alanları değerlendirilmiştir.
Anahtar Kelimeler: Bor, Bor Esaslı Malzemeler
68
P07
APPLICATIONS OF MULTIWALL CARBON NANOTUBES AT POLYMER
MATRIX
MSc. Songul ULAG, Prof.Dr. Nilgun BAYDOGAN
Istanbul Technical University, Energy Institute, 34469, Maslak, Istanbul, Turkey
ABSTRACT
Poly (methyl methacrylate) (PMMA) is a transparent thermoplastic material that shows good
mechanical properties, high resistance to abrasion and superior heat resistance. Mechanical,
thermal and radiation shielding properties of PMMA can be enhanced by addition of
multiwall carbon nanotubes (MWCNTs). Due to suitable structural properties of MWCNTs,
PMMA is an ideal candidate for some applications such as sensor, solar cell, electronic and
aerospace fields. PMMA was produced via ATRP technique. MWCNTs nanofiller was
dispersed by in situ polymerization method because it was the efficient method to disperse the
MWCNTs and the structural changes were examined in this study.