li-ion battery use copper foil - multi channel inc chun/ccp- copper foil.pdf · ・copper foil...

Product Characteristics Major Applications

・Both shiny side Copper Foil with equal roughness on the two sides.

・Anode material for secondary Li-ion battery.

Product Specification

CBFLI-ION BATTERY USE COPPER FOIL

Items Unit Value Testing method

Nominal Thickness μm 8 10 12 IPC-TM-650

Thickness by weight g/m2 75 ±10% 85 ±10% 105 ±10% IPC-TM-650

Tensile Strength

at 23℃ kg/mm2 ＞40 ＞40 ＞40IPC-TM-650

at 180℃ kg/mm2 ＞8 ＞10 ＞10

Elongationat 23℃ % ＞2 ＞2 ＞2

IPC-TM-650at 180℃ % ＞3 ＞5 ＞8

Roughness of Shiny side (Rz) μm ＜1.6 ＜1.6 ＜1.6IPC-TM-650

Roughness of Matte side (Rz) μm ＜1.6 ＜1.6 ＜1.6

Matte side SEM image

CHANG CHUN PETROCHEMICAL CO., LTD.H.Q.: 301 SONGKIANG RD., 7TH FL., TAIPEI 104, TAIWANTEL: 886-2-2500-1800FAX: 886-2-2501-8018WEB SITE: www.ccp.com.tw

CCP長春

COPPER FOIL

Drum side SEM image

HTEHIGH TEMPERATURE ELONGATION COPPER FOIL



・Single side treated Copper Foil following IPC-4562 class 3.

・Surface plated with Zn/Cr.

・Glass Fiber Copper Clad Laminates ( FR-4, CEM-1, CEM-3, High Tg, HF )・Multi-layer Printed Circuit Board.


Nominal Thicknessμm 12 18 35 70

IPC-TM-650oz 1/3 1/2 1 2

Thickness by weight g/m2 107±10% 153±10% 305±10% 610±10% IPC-TM-650

Purity % ＞99.8 ＞99.8 ＞99.8 ＞99.8 IPC-TM-650

Tensile Strength

at 23℃ kg/mm2 ＞21 ＞21 ＞28 ＞28IPC-TM-650

at 180℃ kg/mm2 ＞15 ＞15 ＞15 ＞15

Elongationat 23℃ % ＞3 ＞4 ＞5 ＞5

IPC-TM-650at 180℃ % ＞2 ＞3 ＞3 ＞3

Roughness of Shiny side (Ra) μm ＜0.43 ＜0.43 ＜0.43 ＜0.43 IPC-TM-650

Roughness of Matte side (Rz) μm ＜7 ＜8 ＜10 ＜14 IPC-TM-650

Peel Strengthkg/cm ＞1.1 ＞1.3 ＞1.7 ＞1.9

IPC-TM-650lb/in ＞6.0 ＞7.3 ＞9.5 ＞10.6

COPPER FOIL


CCP長春

Peel Strength Tested with Standard FR-4 material(6 sheets 7628P Prepreg)

Matte side SEM image Shiny side SEM image

DSTFD R U M S I D E T R E A T E D F O I L

Major ApplicationsProduct Characteristics・Copper Foil with treatment on

Drum side.・Inner layer application using low

profile foils・Suitable for fine patterns.



Nominal Thicknessμm 18 35 70

IPC-TM-650oz 1/2 1 2

Thickness by weight g/m2 153±10% 305±10% 610±10% IPC-TM-650

Purity % ＞99.8 ＞99.8 ＞99.8 IPC-TM-650

Tensile Strength

at 23℃ kg/mm2 ＞21 ＞28 ＞28IPC-TM-650

at 180℃ kg/mm2 ＞15 ＞15 ＞15

Elongationat 23℃ % ＞4 ＞5 ＞5

IPC-TM-650at 180℃ % ＞3 ＞3 ＞3

Roughness of treated side (Rz) μm ＜5.0 ＜5.0 ＜5.0 IPC-TM-650

Roughness of Matte side (Rz) μm ＜6.0 ＜8.0 ＜10.0 IPC-TM-650

Peel Strengthkg/cm ＞0.8 ＞0.8 ＞0.9

IPC-TM-650lb/in ＞4.5 ＞4.5 ＞5.0

COPPER FOIL


CCP長春

Peel Strength Tested with Standard FR-4 material(6 sheets 7628P Prepreg)

Matte side SEM image Treated side SEM image


・High Flexibility・High tensile strength・Very low profile・High peel strength

・Specialized for 2-Layers and 3-Layers Flexible Copper Clad Laminate(FCCL).

VLPV E R Y L O W P R O F I L E C O P P E R F O I L


Nominal Thickness μm 9 12 18 IPC-TM-650

Thickness by weight g/m2 79 ±10% 107 ±10% 153 ±10% IPC-TM-650

Tensile Strength

at 23℃ kg/mm2 ＞40 ＞40 ＞40 IPC-TM-650

at 180℃ kg/mm2 ＞10 ＞10 ＞10 IPC-TM-650

Elongationat 23℃ % ＞2 ＞2 ＞2 IPC-TM-650

at 180℃ % ＞3 ＞5 ＞8 IPC-TM-650

Roughness of Matte side (Rz) μm ＜3.0 ＜3.0 ＜3.0 IPC-TM-650

COPPER FOIL



CCP長春

Matte side SEM imageDrum side SEM image

Product Characteristics

Major Applications

・Copper foil containing Phenolic resin Adhesive.

・Paper Phenolic Copper Clad Laminates(FR-1, FR-2, HB).

・Single side Printed Circuit Boards.

LTLC O P P E R F O I L W I T H A D H E S I V E


Nominal Thicknessμm 18 35 70 IPC-TM-650

oz 1/2 1 2 IPC-TM-650

Thickness by weight g/m2 153±10% 305 ±10% 610 ±10% IPC-TM-650

Purity % ＞99.8 ＞99.8 ＞99.8 IPC-TM-650

Tensile Strength at 23℃ kg/mm2 ＞21 ＞28 ＞28 IPC-TM-650

Elongation at 23℃ % ＞2 ＞3 ＞3 IPC-TM-650

Roughness of Shiny side (Ra) μm ＜0.43 ＜0.43 ＜0.43 IPC-TM-650

Peel Strength kg/cm ＞1.2 ＞1.7 ＞1.9 IPC-TM-650

Adhesive content g/m2 24~29 24~29 30~35 JIS-C-6481

Volatile content % 1.5~4.0 1.5~4.0 1.5~4.0 JIS-C-6481

Surface resistance

C-96/20/65 Ω 1 x 1010 1 x 1010 1 x 1010 JIS-C-6481C-96/20/65+C-96/40/90 Ω 1 x 1010 1 x 1010 1 x 1010 JIS-C-6481

COPPER FOIL



CCP長春

Shiny side SEM image

Product Characteristics

Major Applications

・Copper foil containing Anti-Tracking Adhesive.

・Paper Phenolic Copper Clad Laminates(FR-1, FR-2)

・Single side Printed Circuit Boards.

LTCC O P P E R F O I L W I T H A D H E S I V E


Nominal Thicknessμm 18 35 70 IPC-TM-650

oz 1/2 1 2 IPC-TM-650

Thickness by weight g/m2 153±10% 305 ±10% 610 ±10% IPC-TM-650

Purity % ＞99.8 ＞99.8 ＞99.8 IPC-TM-650

Tensile Strength at 23℃ kg/mm2 ＞21 ＞28 ＞28 IPC-TM-650

Elongation at 23℃ % ＞2 ＞3 ＞3 IPC-TM-650

Roughness of Shiny side (Ra) μm ＜0.43 ＜0.43 ＜0.43 IPC-TM-650

Peel Strength kg/cm ＞1.2 ＞1.7 ＞1.9 IPC-TM-650

Adhesive content g/m2 30~34 30~34 33~37 JIS-C-6481

Volatile content % 1.0~3.5 1.0~3.5 1.0~3.5 JIS-C-6481

Surface resistance

C-96/20/65 Ω 1 x 1010 1 x 1010 1 x 1010 JIS-C-6481C-96/20/65+C-96/40/90 Ω 1 x 1010 1 x 1010 1 x 1010 JIS-C-6481

Tracking resistance drops ＞50 ＞50 ＞50 JIS-C-6481

COPPER FOIL



CCP長春

Shiny side SEM image