Textile adhesives
First class bonding
Jowat AG · Ernst-Hilker-Straße 10-14 · 32758 Detmold · Germany · Phone: +49 (0)5231 749-0 · Fax: +49 (0)5231 749-105 · [email protected] · www.jowat.de
JN-E052 05/2010
Textile adhesives
First class bonding
Jowat AG · Ernst-Hilker-Straße 10-14 · 32758 Detmold · Germany · Phone: +49 (0)5231 749-0 · Fax: +49 (0)5231 749-105 · [email protected] · www.jowat.de
Whenever adhesives
are used to manufac-
ture textiles, Jowat is
the right partner: We
offer a wide range of
innovative products to
our customers, for the
most diverse require-
ments. The PUR
products which are
specifi cally certifi ed
meet the high de-
mands of the „Oeko-
Tex Standard 100“ for
extremely low emis-
sion risks in textiles.
PUR hot melt adhesivesPOR hot melt adhesives
Jowatherm-Reaktant®
Jowacoll®/Jowapur®
Dispersion adhesives
Jowatherm®
EVA hot meltPSA hot melt
Jowat-Hightherm®
APAO hot melt
Jowat-Toptherm®
PO hot melt
le industry
Ourproductskeepwhatwe promise!
Jowat adh
obs/Adam Opel GmbH
HEADQUATERS:
Jowat AGPostfach 1953D-32709 DetmoldPhone +49(0)5231 749-0Fax +49(0)5231 749-105Internet: www.jowat.deE-Mail: [email protected]
AFFILIATED COMPANIES:E U R O P E
GermanyJowat Klebstoffe GmbHD-06729 Elsteraue / OT GöbitzPhone +49 (0)3441 5382-0E-Mail:[email protected]
FranceJowat France sarlF-67810 HoltzheimPhone +33 388 101676E-Mail: [email protected]
Great BritainJowat (UK) Ltd.Staffordshire Technology ParkGB - Stafford, ST18 0WPPhone +44 (0)17 8571 6565E-Mail: [email protected]
ItalyJowat Italia s.r.l.I-20017 Mazzo di Rho (MI)Phone +39 02 9390 4504E-Mail: [email protected]
NetherlandsJowat Nederland B.V.NL-7666 NB FleringenPhone +31 541 670629E-Mail: [email protected]
PolandJowat Polska Sp.z.o.o.PL-62-080 Sady k. PoznaniaPhone +48 618 147287E-Mail: [email protected]
RussiaOOO JowatRU-143000 Moscow Region / OdintsovoPhone +7 495 941-9092 / -9094E-Mail: [email protected]
SwedenJowat-Lundquist ABSE-24562 HjärupPhone +46 40 461190E-Mail:[email protected]
SwitzerlandJowat Swiss AGCH-6033 Buchrain (LU)Phone +41 41 4451111E-Mail: [email protected]
A S I A
China / Hong KongJowat (Beijing) Adhesives Co. Ltd..Room B2009, Intelli CenterNo. 18 Zhongguancun East RoadHaidian District, 100083 BeijingPhone +86 10 8260 0725E-Mail: [email protected]
Malaysia / SingapurJowat (Malaysia) Sdn. Bhd.Jowat Manufacturing (SEA) Sdn. Bhd.MY-43300 BalakongSelangor Darul EhsanPhone +603 89 622800E-Mail: [email protected]
U.A.E.Jowat Middle East FZE Sharjah Airport Int‘ Free Zone P.O. Box 120801, Sharjah - U.A.E.E-Mail: [email protected]
A M E R I C A
BrasilJowat do Brasil Ltda.BR-93352-000Novo Hamburgo-RS-BrasilPhone 011 55 51 35941404E-Mail: [email protected]
CanadaJowat Canada Ltd.CA-Mississauga, ON L5M 2B7Phone +1 336 434 9150E-Mail: [email protected]
MexicoJowat de Mexico, S. de R.L. de C.V.,MX-Cuahtemoc, Mexico D.F., 06700Phone 011 525 552117514E-Mail: [email protected]
USAJowat CorporationHigh Point, NC 27261, USAPhone +1 336 434-9000E-Mail: [email protected]
Novamelt-Jowat LLCHigh Point, NC 27261, USAPhone +1 336 434-9500www.novameltjowat.com
JN-E052 05_2010.indd 1JN-E052 05_2010.indd 1 11.05.2010 11:32:5111.05.2010 11:32:51
Textile adhesives Textile adhesives
The fi ve application systems illustrated below aresuitable for the hot melt adhesives listed.They are used for the production of:
· double and triple laminates
· air-permeable laminates
· soft textile feel of the laminated fabrics
Wide slot nozzle coating systems:
· closed application system (no contact with oxygen and humidity)
· high production speeds
· above all suitable for full cover coating
· open coating structure (O.C.S.) possible
Gravure roller coating systems:
· precise adhesive pattern control
· adhesive application only in the area of contact
· open coating structure (O.C.S.)
· clean application
Spray nozzle coating systems:
· closed application system (no contact with oxygen and humiditiy)
· high production speeds
· open coating structure (O.C.S.)
Multiple roller coating systems:
· high fl exibility - easy switch of adhesives
· above all suitable for full cover coating
· open coating structure (O.C.S.) possible
Screen print coating systems:
· precise adhesive pattern control
· adhesive application only in the area of contact
· open coating structure (O.C.S.)
· clean application
Dispersion coating systems:
· Self-adhesive products
· full cover or air-permeable coating and lamination
· precoating
Scatter coating systems:
· Assembly of double and triple laminates
· air-permeable laminates
· reverse coating of carpets
· precoating of foam and textiles
Jowat adhesives for the textile industry
Coating of 3D parts:
· Adhesive application with spray nozzle manually or by robot
· Drying of the adhesive fi lm
· Reactivation of the adhesive fi lm by radiator or hot air
· Pressing or evacuation of the compound
· Cooling-down followed by removal
INFO Selection of 2K PU solvent based adhesives, water-based 2K laminating adhesives
Examples of application
157.70Bonding of textiles w. or w.-out foam backing to variousfibre-based supports
157.60 Textiles to various fibre based substrates, also for highlymolded shapes and absorbent materials
Spray pattern
rough
rough
Crosslinkers
197.43
197.43
Viscosityin mPas
approx. 400
approx. 500
Solid contend(%)
approx. 55
approx. 57
Colour
158.01 Bonding of PVC and TPO foils + textiles to ABS substrates fine197.43 approx. 300 approx. 50white
clear
clear
493.25Bonding of PVC and TPO foils, carpet and textiles to ABS andwood-fibreboard substrates
493.60 Hemming, contact and assembly adhesive
fine
rough
498.07
498.07
approx. 200
approx. 3500
approx. 16
approx. 19
blue
clear
INFO Selection of hot melt adhesives
Jowatherm®
262.16
EVA hot melt
299.75
Jowat-Hightherm
®
221.00
APAO hot melt
230.00
Jowatherm-Reaktant
®
628.30
POR hot melt
628.80
628.90
Jowatherm-Reaktant
®
630.00
PUR hot melt
634.17
637.00
637.10
639.00
Characteristics Examples of application Softeningrange in °C
Viscosityat 180 °C
Translucent,short open time,high heat resistance
High hot tack andseam resistance,medium viscosity, elastic,no blocking, translucent
Lamination of textile to textileand to foil and structure foil
approx. 2,500mPas
approx. 95
Lamination of textiles,textiles to plastic foilsand to leather; precoatingof toecap materials
approx. 45,000mPas
approx. 75
299.65High hot tack andseam resistance,medium viscosity, elastic,no blocking, translucent
Lamination of textiles,textiles to plastic foilsand to leather; precoatingof toecap materials
approxmPas
. 24,000approx. 75
Characteristics Examples of application Softeningrange in °C
Viscosityat 180 °C
Medium viscosity, long open time, good adhesion,elastic, high heat resistance
Low viscosity, very long opentime, very high hot tack,good adhesion, highly elastic,high heat resistance
Lamination of textile totextile, to plastic foils, to foam and to fleece
approxmPas
. 35,000 approx. 115
Lamination of textile totextile, to plastic foils, to foam and to fleece
approxmPas
. 6,000 approx. 105
263.40
263.50
Low viscosity,medium open time,good adhesion,high heat resistance
Lamination of textile totextile, to plastic foils and to foam, fleece to plastic foils andmetal or plastic surfaces
approxmPas
. 9,000 approx. 75
approx. 12approxmPas
. 10,000
Characteristics Examples of application ProcessingTemp. in °C
Viscosityin mPas
Low viscosity,good adhesion,high initial strength
High viscosity,very high initial strength,good adhesion toresinated papers
Automotive andTextile industries
approx. 9,000at 140 °C
approx. 140
Sanding materials industry approxat 140 °C
. 22,000 approx. 140
Low viscosity,high resistance to hydrolysis,very low processingtemperature
Automitive andTextile industry(e.g. medical applications)
approxat 100 °C
. 9,000 approx. 100
approxat 100 °C
. 15,000 approx. 100
approx. 110approxat 110 °C
. 8,000Low viscosity, good adhesion,low processing temperature
Automotive andTextile industriesexcellent adhesion property(difficult to bond substrates)
Low viscosity,good adhesion,low processing temperature,special rheology
Automitive andTextile industry(e.g. medical applications)
Characteristics Examples of application ProcessingTemp. in °C
Viscosityat 180 °C
Low viscosity,long open time,suitable for spray application
Medium viscosity,very short open time,high initial strength
General-purpose usein the Automotive andTextile industries.
excellent adhesionproperties especially topolyolefine substrates.
approxmPas
. 3,500 approx. 140 - 180
approxmPas
. 16,000 approx. 160 - 190
Medium viscosity,medium open time,good initial strength
approxmPas
. 10,000 approx. 160 - 190
238.50Elastic, no blocking,good adhesion, low melt viscosity
Coating of filtersAssembly approx
mPas. 15,000 approx. 115
299.35High hot tack andseam resistance,medium viscosity, elastic,no blocking, translucent
Precoatingof toecap materials approx
mPas. 17,000
approx. 75
Jowat-Toptherm
® Characteristics Examples of application Softeningrange in °C
Viscosityat 180 °C
239.65Elastic, no blocking,good adhesion, low melt viscosity
Coating of fabrics and for reinforcing purposes approx
mPas. 7,000 approx. 105
INFO Selection of dispersion adhesives
Jowacoll®
766.00
763.40
Examples of application Solid contentin %
Densityin g/cm³
Viscosityin mPas
Self-adhesive coating of protectivefoils, good peel performance approx. 500 approx. 1.05
approx. 16,600 approx. 1.05Excellent tack,high cohesion and heat resistance
pH valueHot Shear Testin °C
approx. 7.5
approx. 4.0
-
approx. 115
approx. 50
approx. 64
762.35 approx. 17,000 approx. 1.02high tack
,high cohesion and heat resistanceapprox. 4.5approx. 165approx. 68
INFO Selection of hot melt adhesives
Jowatherm®
PSA hot melt
245.00
244.85
Characteristics Examples of application SAFT in °C100g/10min
Viscosityat 160 °C
High surface tack,very good adhesion
Precoating of fleece andnonwoven materials,self-adhesive coatings
approxmPas
. 18,000 approx. 60 - 70
Excellent tack,very high heat resistance
Precoating of insulating parts for the automotive industry
approxmPas at 180°C
. 26,000 approx. 100 - 110
JN-E052 05_2010.indd 2JN-E052 05_2010.indd 2 11.05.2010 11:33:0011.05.2010 11:33:00