G-CEM LinkAce is stronger Now offering comparative physical properties to current adhesive resin cements, G-CEM LinkAce is the next evolution in easy-to-use, versatile, self-adhesive resin cements.
Designed with a highly efficient self-cure polymerisation reaction, G-CEM LinkAce always delivers high bond strengths and exceptional physical properties, even without light activation.
G-CEM LinkAce is suitable for bonding and cementation of indirect metal, PFM, composite, zirconia, alumina and all-ceramic restorations (including posts), and retains the simple-to-use handling characteristics popularised by the previous generation of self-adhesive resin cements.
The transmission of light has never been a certainty… This experiment was designed to simulate a clinical situation. The light intensity of a LED curing unit was measured following its transmission through different restorative materials. Light intensity reduces drastically in each case, showing the importance of an efficient self-cure polymerisation.
1100 mW/cm²
Metal 1-mm thick metal disc.
0 mW/cm²
Zirconia 0.4-mm thick zirconia disc with ceramic layering up to 1.6 mm.
50 mW/cm²
Ceramic 0.5-mm thick ceramic disc (lithium disilicate) with ceramic layering up to 1.5 mm.
50 mW/cm²
Transparent disc
Source: Pereira et al., Sao Paulo University, Brazil
2
G-CEM LinkAce
G-CEM LinkAce Innovation Advanced resin polymerisation initiation systems;
patented self-cure initiation technology gives surety of a complete cure, high strength and strong adhesion even without light activation. As the majority of indirect restorations significantly limit transmission of curing light, a strong dark cure reaction offers security to ensure clinical durability of the cement. The new initiation system technology also introduces a high level of chemical stability to give G-CEM LinkAce a 2-year shelf life without refrigeration.
Finer glass fillers; used to improve flow characteristics, physical properties and cement wear resistance while decreasing cement film thickness to just 3 microns.
Higher polymerisation conversion; gives superior colour stability and stain resistance, as well as helping achieve more durable adhesion over time.
Proprietary phosphate ester monomer; enhances the level of adhesion to a variety of substrate surfaces.
Higher strength: self cure or light cure
G-CEM LinkAce
Maxcem Elite*
Unicem2 Automix*
Clearfil SA Cement*
SpeedCEM *
Unicem Aplicap*
G-CEM Capsule
Multilink Automix*
Variolink II*
Panavia F2.0*
Self-cure
Light-cure
Flexural Strength (MPa) GC R&D
0 20 40 60 80 100 120 140 160
Self-
adhe
sive
res
in c
emen
tsA
dhe
sive
res
in
cem
ents
* Not trademarks of GC Corporation
3
G-CEM LinkAce Simplicity
G-CEM LinkAce VersatilityStrong chemical bonding and self-curing capabilities are essential for durable bonding of indirect metal, zirconia and opaque ceramic restorations.
ChallengeIn many clinical cases, light simply doesn’t penetrate through indirect restorations, compromising polymerisation and leading to poor bonding and poor physical properties with self-adhesive resin cements.
SolutionG-CEM LinkAce achieves strong chemical bonding and provides exceptionally reliable self-curing capabilities with all materials, thanks to its unique initiator system. Even without light activation, G-CEM LinkAce will provide strong durable adhesion.
No need for etching or bonding steps. Clean the prepared tooth with pumice and water, rinse and gently dry.
One step automix dispensing. Where required, pretreat the internal surfaces of the restoration, then extrude cement directly without over filling
Stronger bonding to dentine: Self-cure tensile bond strength, before and after thermocycling
G-CEM LinkAce
Maxcem Elite*
Unicem 2 Automix*
SpeedCEM*
Unicem Aplicap*
G-CEM Capsule
1 Day
5000 TC
Tensile Bond Strength (MPa)0 2 4 6 8 10 12 14
GC R&D
Low film thickness (3 µm) and effortless seating. Seat the restoration and maintain moderate pressure.
* Not trademarks of GC Corporation
4
G-CEM LinkAce
Ideal consistency for easy excess removal. To remove excess cement, either light cure for 1 second or allow the cement to self cure. Remove excess when the cement feels rubbery.
Guaranteed stability, 2-year shelf life. No refrigeration needed.
Fluoride release and aesthetic results. Light cure for 20 seconds each surface or wait 4 minutes for self cure set before final finishing.
Images by Dr. Javier Tapia Guadix, Madrid, Spain
A chemical bond to zirconiaChallengeZirconia restorations offer many advantages but bonding to zirconia remains challenging.
SolutionG-CEM LinkAce contains a proprietary phosphate ester monomer that chemically bonds to zirconia for a strong and stable bond. Combined with the enhanced physical properties and higher degree of conversion, this results in a stronger and more durable bond to zirconia without the need for a separate primer.
Zirconia: Tensile bond strength before and after thermocycling
G-CEM LinkAce
Maxcem Elite*
Unicem 2 Automix*
SpeedCEM*
Rely X Ultimate*
Multilink Automix*
Variolink II*
1 Day
5000 TC
Tensile Bond Strength (MPa)
0 10 20 30 40 50 60
GC R&DSe
lf-ad
hesi
ve
resi
n ce
men
tsA
dhe
sive
re
sin
cem
ents
* Not trademarks of GC Corporation
5
G-CEM LinkAce ReliabilityG-CEM LinkAce gives you a consistently high degree of polymerisation – ensuring optimal colour stability, bond strengths and aesthetics for all ceramic restorations.
ChallengeCementation of all-ceramic crowns requires a material with extra bonding efficacy and high colour stability for a superior aesthetic result.
SolutionG-CEM LinkAce high polymer conversion gives increased durability and high bond strengths, preventing loss of retention. G-CEM LinkAce exhibits minimal water uptake, is HEMA-free and delivers reliable colour stability.
G-CEM LinkAce high polymer conversion is important for colour stability when bonding highly aesthetic restorations.
Images by Dr. Emmanuel D’Incau, France
1 Day
5000 TC
Tensile Bond Strength (MPa)
G-CEM LinkAce
Maxcem Elite*
Unicem 2 Automix*
SpeedCEM*
Rely X Ultimate*
Multilink Automix*
Variolink II*
0 10 20 30 40 50 60
7.445913488 10.05982824
GC R&D
Lithium disilicate: Tensile bond strength with manufacturer’s silane before and after thermocycling
Before After
Self-
adhe
sive
re
sin
cem
ents
Ad
hesi
ve
resi
n ce
men
ts
Images by Dr. Emmanuel D’Incau, France
* Not trademarks of GC Corporation
6
G-CEM LinkAce
Unsurpassed wear resistanceChallengeExposed cement at margins wears over time and can lead to chipping of ceramic restorations.
SolutionG-CEM LinkAce offers high wear resistance due to its small and homogeneously-distributed filler particles, minimal water uptake and highly-polymerised resin matrix.
Replica image of self- adhesive resin cement degradation after 4 years.
Images by Prof. Dr. Marleen Peumans, Belgium
Three-body wear test
0 100 200 300
Light-cure
Self-cure
Depth of Wear (µm)
G-CEM LinkAce
Maxcem Elite*
Unicem 2 Automix*
Clearfil SA cement*
Variolink II*
Multilink Automix*
GC R&D
G-CEM LinkAce Unicem 2 Automix Maxcem Elite
Self-
adhe
sive
re
sin
cem
ents
Adh
esiv
e
resi
n ce
men
ts
SEM images of cement fillers identify the reason for improved wear resistance.
* Not trademarks of GC Corporation
30 µm30 µm30 µm
7
GC Australasia Dental Pty Ltd 1753 Botany Road, Banksmeadow NSW 2019, Australia
T: +61 2 9316 4499 F: +61 2 9316 4196
www.gcasia.info
GC Luting Navigation Chart
Cementation indications Surface pre-treatment† G-CEM LinkAce
G-CEM Capsule Fuji PLUS FujiCEM Fuji I
Sandblast or etch Ceramic primerSelf-adhesive resin cement
Self-adhesive resin cement
Resin-reinforced glass ionomer cement
Resin-reinforced glass ionomer cement
Conventional glassionomer cement
Metal, PFM- Inlays, Onlays ✔ Y Y Y Y Y- Crowns ✔ Y Y Y Y Y- Bridges ✔ Y Y Y Y Y- Endodontic Posts ✔ Y Y Y Y Y
Ceramics eg. lithium disilicate (less than 600 MPa flexural strength)- Inlays, Onlays ✔ ✔ Y Y Y Y- Crowns ✔ ✔ Y Y- Bridges ✔ ✔ Y Y
High Strength Ceramics eg. zirconia (greater than 600 MPa flexural strength)- Crowns ✔ Y Y Y Y Y- Bridges ✔ Y Y Y Y Y- Endodontic Posts ✔ Y Y Y Y
Shades: Translucent, A2, BO1, AO3
Package: 2 x G-CEM LinkAce Syringes (4.6gm, 2.7ml each)
15 x Automix Tip Regular
5 x Automix Tips for endo (with 5x Extension Tips)