fenomena dynamic strain aging pada proses tempa panas

Download Fenomena Dynamic Strain Aging pada Proses Tempa Panas

Post on 19-Jan-2017

219 views

Category:

Documents

2 download

Embed Size (px)

TRANSCRIPT

  • Penanggung Jawab:

    Kapuslit Metalurgi LIPI

    Dewan Redaksi :

    Ketua Merangkap Anggota:

    Ir. Ronald Nasoetion, MT

    Anggota:

    Dr. Ir. Rudi Subagja

    Dr. Ir. F. Firdiyono

    Dr. Agung Imadudin

    Dr. Ika Kartika, MT

    Ir. Yusuf

    Ir. Adil Jamali, M.Sc (UPT BPM LIPI)

    Prof. Riset. Dr. Ir. Pramusanto

    (Puslitbang TEKMIRA)

    Prof. Dr. Ir. Johny Wahyuadi, DEA (UI)

    Dr. Ir. Sunara, M.Sc (ITB)

    Sekretariat Redaksi:

    Pius Sebleku, ST

    Tri Arini, ST

    Arif Nurhakim, S.Sos

    Lia Andriyah, ST

    Penerbit:

    Pusat Penelitian Metalurgi LIPI

    Kawasan PUSPIPTEK, Serpong,

    Gedung 470

    Telp: (021) 7560911, Fax: (021) 7560553

    Alamat Sekretariat:

    Pusat Penelitian Metalurgi LIPI

    Kawasan PUSPIPTEK, Serpong,

    Gedung 470

    Telp: (021) 7560911, Fax: (021) 7560553

    E-mail : metalurgi_magz@yahoo.com

    Majalah ilmu dan teknologi terbit

    berkala setiap tahun, satu volume

    terdiri atas 3 nomor.

    VOLUME 27 NOMOR 1, APRIL 2012 ISSN 0216 3188

    AKREDITASI : SK 187/AU1/P2MBI/08/2009

    Pengantar Redaksi.. iii

    Abstrak ...... v

    Pengaruh Waktu Pelindian pada

    Proses Pemurnian Silikon Tingkat

    Metalurgi Menggunakan Larutan

    HCl

    Bintang Adjiantoro dan Efendi Mabruri......1

    Aplikasi Severe Plastic Deformation

    (SPD) dan Heavy Cold Rolling pada

    Baja Tahan Karat Austenitik 316L

    Efendi Mabruri ....................... 7

    Percobaan Pendahuluan

    Perbandingan Daya Serap Unsur

    Minor dalam Larutan Natrium

    Silikat

    F. Firdiyono, dkk .15

    Fenomena Dynamic Strain Aging

    pada Proses Tempa Panas Paduan

    Co-33Ni-20Cr-10Mo

    Ika Kartika ........ 27

    Sifat Listrik Superkonduktor

    YBa2Cu3O7-x Hasil Proses Pelelehan

    dengan Dopant Ti

    Didin S.Winatapura, dkk .... 35

    Percobaan Pengisian-Pengeluaran

    Hidrogen Sebuah Tangki Simpan

    Hidrogen Padat

    Hadi Suwarno ..... 43

    Pembentukan Nanopartikel Paduan

    CoCrMo dengan Metoda Pemaduan

    Mekanik

    Sulistioso Giat S dan Wisnu Ari Adi . 51

    Indeks

    mailto:metalurgi_magz@yahoo.com

  • ii | Majalah Metalurgi, V 27.1.2012, ISSN 0216-3188

  • Pengantar Redaksi | iii

    PENGANTAR REDAKSI

    Syukur Alhamdulillah Majalah Metalurgi Volume 27 Nomor 1, April 2012 kali ini

    menampilkan 7 buah tulisan.

    Tulisan pertama hasil penelitian disampaikan oleh Bintang Adjiantoro dan Efendi

    Mabruri berjudul Pengaruh Waktu Pelindian pada Proses Pemurnian Silikon Tingkat

    Metalurgi Menggunakan Larutan HCl. Selanjutnya Efendi Mabruri tentang Aplikasi Severe

    Plastic Deformation (SPD) dan Heavy Cold Rolling pada Baja Tahan Karat Austenitik

    316L. F. Firdiyono dan Kawan-Kawan juga menulis tentang Percobaan Pendahuluan

    Perbandingan Daya Serap Unsur Minor dalam Larutan Natrium Silikat. Ika Kartika

    menulis tentang Fenomena Dynamic Strain Aging pada Proses Tempa Panas Paduan Co-

    33Ni-20Cr-10Mo. Didin S.Winatapura dan Kawan-Kawan menulis tentang Sifat Listrik

    Superkonduktor YBa2Cu3O7-x Hasil Proses Pelelehan dengan Dopant Ti dan Hadi Suwarno

    juga menulis tentang Percobaan Pengisian-Pengeluaran Hidrogen Sebuah Tangki Simpan

    Hidrogen Padat. Berikutnya Sulistioso Giat Sukaryo dan Wisnu Ari Adi menulis tentang

    Pembentukan Nanopartikel Paduan CoCrMo dengan Metoda Pemaduan Mekanik.

    Semoga penerbitan Majalah Metalurgi volume ini dapat bermanfaat bagi perkembangan

    dunia penelitian di Indonesia.

    REDAKSI

  • iv | Majalah Metalurgi, V 27.1.2012, ISSN 0216-3188

  • Abstrak | v

    METALURGI

    (Metallurgy) ISSN 0216 3188 Vol 27 No. 1 April 2012 Kata Kunci bersumber dari artikel. Lembar abstrak ini boleh diperbanyak tanpa izin dan biaya.

    UDC (OXDCF) 669.540

    Bintang Adjiantoro dan Efendi Mabruri (Pusat Penelitian Metalurgi LIPI)

    Pengaruh Waktu Pelindian pada Proses Pemurnian Silikon Tingkat Metalurgi Menggunakan Larutan HCl

    Metalurgi, Vol 27 No. 1 April 2012

    Proses pemurnian silikon tingkat metalurgi (MG-Si) dengan menggunakan metoda pelindian asam pada

    konsentrasi 2,45mol/L HCl telah dilakukan dengan memvariasikan waktu pelindian pada temperatur didih

    (100 C) dan gerakan pengadukan mekanik. Hasil penelitian menunjukkan bahwa proses pelindian MG-Si

    dengan HCl dapat digunakan untuk menghilangkan unsur pengotor logam. Persentase hasil efisiensi ekstraksi

    dari unsur pengotor yang terkandung di dalam MG-Si dengan pelarutan HCl masing-masing mencapai

    99,996 % untuk Al, 98,247 % untuk Ti dan 98,491 % untuk Fe pada waktu pelindian 120 jam. Sedangkan efisiensi larutan HCl terhadap unsur pengotor dengan gerakan pengadukan mekanik mencapai 99,04 %.

    Kata kunci : Silikon tingkat metalurgi, Pemurnian dengan proses kimia, Pelindian asam, Pengotor

    Effect of Leaching Time on Purification Process of Metallurgical Grade Silicon by Using Acid Solution

    The purification process of metallurgical grade silicon (MG-Si) using acid leaching method at a

    concentration of 2.45 mol/L HCl was performed by varying the leaching time at boiling temperature (100

    C) and with mechanical stirring. The results showed that the leaching process of MG-Si with HCl can be

    used to eliminate the element of metal impurities. The extraction efficiency of impurity elements contained

    in the MG-Si by HCl dissolution is 99.996 % for Al, 98.247 % for Ti and 98.491 % for Fe at leaching time

    of 120 hours. Whereas the leaching efficiency HCl solution on the impurities with mechanical stirring is

    99.04 %.

    Keywords : Metallurgical grade silicon, Chemical purification, Acid leaching , Impurities

  • vi | Majalah Metalurgi, V 27.1.2012, ISSN 0216-3188

    METALURGI

    (Metallurgy) ISSN 0216 3188 Vol 27 No. 1 April 2012 Kata Kunci bersumber dari artikel. Lembar abstrak ini boleh diperbanyak tanpa izin dan biaya.

    UDC (OXDCF) 660

    Efendi Mabruri (Pusat Penelitian Metalurgi LIPI)

    Aplikasi Severe Plastic Deformation (SPD) dan Heavy Cold Rolling pada Baja Tahan Karat Austenitik 316L

    Metalurgi, Vol 27 No. 1 April 2012

    Untuk meningkatkan kekuatan baja tahan karat austenitik, penghalusan butir sampai ukuran submikron (ultra

    fine grain) merupakan metoda yang efektif. Tulisan ini melaporkan aplikasi severe plastic deformation

    (SPD) menggunakan equal channel angular pressing (ECAP) dan aplikasi heavy cold rolling terhadap baja tahan karat austenitik SS 316L. Hasil percobaaan menunjukkan bahwa sifat mekanik baja tahan karat

    austenitik 316L dapat ditingkatkan secara signifikan masing-masing dengan kedua teknik tersebut. ECAP

    pass 1 (single pass) dengan regangan 0,65 dapat meningkatkan kekuatan tarik baja tahan karat austenitik

    316L menjadi 1,6 kali lipat, sedangkan heavy cold rolling 80 % dengan regangan 1,65 dapat meningkatkan

    kekuatan tarik menjadi 2,1 kali lipat. Pemanasan anil pada suhu 750 C menurunkan kekuatan tarik menjadi 1055,14 MPa tetapi nilai tersebut masih jauh lebih tinggi dari kekuatan tarik pada kondisi awal (solution

    treatment) sebesar 655,53 Mpa.

    Kata kunci : Baja tahan karat austenitik, Penghalusan butir, Severe plastic deformation, Equal channel

    angular pressing, Heavy cold rolling

    The Application of Severe Plastic Deformation (SPD) and Heavy Cold Rolling of Austenitic Stainless Steel

    316L

    The grain refinement down to ultrafine sizes is the efective method for strengthening of austenitic stainless

    steel. This paper reports the application of severe plastic deformation (SPD) using equal channel angular pressing (ECAP) and the application of heavy cold rolling on the austenitic stainless steel (SS) 316L. The

    experimental results showed that the mechanical properties of SS 316L can be increased significantly by

    these two techniques. The single pass-ECAP with 0.65 strain increased tensile strength of SS 316L by 1.6

    times, whereas heavy cold rolling with 80 % reduction and 1.65 strain increased tensile strength by 2.1 times.

    The annealing treatment at 750 C decreased tensile strength of 80 % cold rolled-SS 316L down to 1055.14

    Mpa, however this value is still much larger compared to that of solution treated ones of 655.53 Mpa.

    Keywords : Austenitic stainless steel, Grain refinement, Severe plastic deformation, Equal channel angular

    pressing, Heavy cold rolling

  • Abstrak | vii

    METALURGI

    (Metallurgy) ISSN 0216 3188 Vol 27 No. 1 April 2012 Kata Kunci bersumber dari artikel. Lembar abstrak ini boleh diperbanyak tanpa izin dan biaya.

    UDC (OXDCF) 540

    F. Firdiyono, Murni Handayani, Eko Sulistiyono, Iwan Dwi Antoro (Pusat Penelitian Metalurgi LIPI)

    Percobaan Pendahuluan Perbandingan Daya Serap Unsur Minor dalam Larutan Natrium Silikat

    Metalurgi, Vol 27 No. 1 April 2012

    Penelitian tentang kemampuan penyerapan zeolit alam Karangnunggal dan karbon aktif sebagai adsorben

    dalam larutan natrium silikat telah dilakukan. Penelitian ini bertujuan untuk mengetahui efisiensi penyerapan

    zeolit dan karbon aktif terhadap unsur pengotor Ca, Mg, Fe, dan Al dalam larutan natrium silikat serta