DRISEAM REINFORCEMENT TAPE

• Ultimate breathability

• Integrated moisture transport system using Bemis FlowfreeTM in partnership with drirelease fabrics

• Use for construction or aesthetic

• Reduces seam weight

• Strengthens seams

• Soft hand feel

• Withstands high heat wash

Why It’s Worth a Look

Engineered with

DRISEAM REINFORCEMENT TAPE

/ CORE COLORS

Snow

Pantone 11-0601 TPX

Navy

Pantone 19-4024 TPX

Black

Pantone 19-4006 TPX

Red

Pantone 18-1763 TPX

Radiation

Pantone 388C

DSRT / 1

DRISEAM REINFORCEMENT TAPE

/ CORE COLORS

Heather Cool Grey

Heather Black

Heather Gold

Heather Red

Heather Purple

DSRT / 2

TECHNICAL INFORMATION

DRISEAM REINFORCEMENT TAPE DSRT1000

MATERIALS Polyester/Cotton/Spandex Knit Lightweight Fabric/Polyurethane Adhesive

STOCKED WIDTH 1372 mm

ADHESIVE SOFTENING POINT 83°C (181°F)

TOTAL THICKNESS 0.014” (0.36 mm)

ADHESIVE THICKNESS 0.004” (0.10 mm)

MATERIAL WEIGHT 2.15 g/m at 10 mm

MODULUS @ 50% ELONGATION1 10 mm

SERVICE TEMPERATURE −30°C to 60°C (−22°F to 140°F)

WASH Excellent up to 60°C water temperature

INITIAL BONDING CONDITIONS2

FLAT PRESS

TEMPERATURE 110°C to 150°C

TIME 15 to 25 seconds

PRESSURE 2.8 to 4.2 bar (40 to 60 psi)

1Modulus: The force required to pull a 12 mm (0.47”) wide sample by specified gauge to 50% elongation at 508 mm (20”) per minute after 3 cycles.2Recommended bonding conditions will vary between different machinery and fabrics. The recommended conditions stated are a starting point only. Optimal bonding conditions should be established by the factory of the specific application.

NOTE: Seller hereby excludes any express warranties and the implied warranties of merchantability and fitness for a particular purpose. The following is made in lieu of any such “warranties.” Bemis Associates, Inc. believes the information and specification supplied are reliable, but does not guarantee that any results shown or claimed will be obtained. Before using, the user shall determine the suitability and fitness of the product for its intended use. The user assumes all risks and liability whatever in connection with its own tests and use. Neither seller nor manufacturer shall be liable for any injury, loss or damage, direct or consequential, arising out of the use, or misuse or inability to use this product.

KNITSEAM REINFORCEMENT TAPE

• Incorporates knit fabric for differentiated look and hand feel

• High stretch

• Use for construction or aesthetic

• Reduces seam weight

• Strengthens seams

• Withstands high heat wash

Why It’s Worth a Look

KNIT SEAM REINFORCEMENT TAPE

/ CORE COLORS

Snow

Pantone 11-0601 TPX

Cool Grey

Pantone 428C

Ash

Pantone 19-4104 TPX

Navy

Pantone 19-4024 TPX

Black

Pantone 19-4006 TPX

KSRT / 1

KNIT SEAM REINFORCEMENT TAPE

/ CORE COLORS

Red

Pantone 18-1763 TPX

Radiation

Pantone 388C

KSRT / 2

TECHNICAL INFORMATION

KNIT SEAM REINFORCEMENT TAPE SRT4000

MATERIAL Nylon/Spandex Knit Fabric/Polyurethane Adhesive

STOCKED WIDTH 10 mm, 1372 mm

WEIGHT 3.23 g/m at 10 mm

HAND Soft

WASH Excellent up to 60°C

MODULUS1 1.3 lbf (0.6 kgf)

SOFTENING POINT 95°C (203°F)

TOTAL THICKNESS 0.020” (0.51 mm)

ADHESIVE THICKNESS 0.004” (0.10 mm)

SERVICE TEMPERATURE −30°C to 60°C (−22°F to 140°F)

INITIAL BONDING CONDITIONS2

HOT AIR

NOZZLE POSITION Same as a standard 2-layer seam tape

NOZZLE AIR TEMPERATURE 550°C to 650°C

NOZZLE PRESSURE 0.09 mpa

ROLLER PRESSURE 0.4 mpa

LINE SPEED 4 m/min

FLAT PRESS

TEMPERATURE 115°C to 170°C

TIME 15 to 25 seconds

PRESSURE 2.8 to 4.2 bar (40 to 60 psi)

Self fabric lamination is available. Contact Bemis for details.

1Modulus: The force required to pull a 12 mm (0.47”) wide sample by specified gauge to 50% elongation at 508 mm (20”) per minute after 3 cycles.2Recommended bonding conditions will vary between different machinery and fabrics. The recommended conditions stated are a starting point only. Optimal bonding conditions should be established by the factory of the specific application.

NOTE: Seller hereby excludes any express warranties and the implied warranties of merchantability and fitness for a particular purpose. The following is made in lieu of any such “warranties.” Bemis Associates, Inc. believes the information and specification supplied are reliable, but does not guarantee that any results shown or claimed will be obtained. Before using, the user shall determine the suitability and fitness of the product for its intended use. The user assumes all risks and liability whatever in connection with its own tests and use. Neither seller nor manufacturer shall be liable for any injury, loss or damage, direct or consequential, arising out of the use, or misuse or inability to use this product.

CertificationOeko Tek, Standard 100 Class 1 (Test No. 6187)REACH compliant, European Union (EU) legislation concerning the Registration, Evaluation, Authorization and Restriction of Chemicals (REACH)

WOVENSEAM REINFORCEMENT TAPE

• Incorporates woven fabric for differentiated look and hand feel

• High stretch

• Use for construction or aesthetic

• Reduces seam weight

• Strengthens seams

• Withstands high heat wash

Why It’s Worth a Look

WOVEN SEAM REINFORCEMENT TAPE

/ CORE COLORS

Cool Grey

Pantone 428C

Ash

Pantone 19-4104 TPX

Navy

Pantone 19-4024 TPX

Snow

Pantone 11-0601 TPX

Black

Pantone 19-4006 TPX

WSRT / 1

WOVEN SEAM REINFORCEMENT TAPE

/ CORE COLORS

Red

Pantone 18-1763 TPX

Radiation

Pantone 388C

WSRT / 2

TECHNICAL INFORMATION

WOVEN SEAM REINFORCEMENT TAPE SRT5000

MATERIAL Polyester/Spandex Woven Fabric/Polyurethane Adhesive

STOCKED WIDTH 10 mm, 1372 mm

WEIGHT 2.88 g/m at 10 mm

HAND Soft

WASH Excellent up to 60°C

MODULUS1 4.5 lbf (2.0 kgf)

SOFTENING POINT 95°C (203°F)

TOTAL THICKNESS 0.012” (0.31 mm)

ADHESIVE THICKNESS 0.004” (0.10 mm)

SERVICE TEMPERATURE −30°C to 60°C (−22°F to 140°F)

INITIAL BONDING CONDITIONS2

HOT AIR

NOZZLE POSITION Same as a standard 2-layer seam tape

NOZZLE AIR TEMPERATURE 550°C to 650°C

NOZZLE PRESSURE 0.09 mpa

ROLLER PRESSURE 0.4 mpa

LINE SPEED 4 m/min

FLAT PRESS

TEMPERATURE 115°C to 170°C

TIME 15 to 25 seconds

PRESSURE 2.8 to 4.2 bar (40 to 60 psi)

Self fabric lamination is available. Contact Bemis for details.

1Modulus: The force required to pull a 12 mm (0.47”) wide sample by specified gauge to 50% elongation at 508 mm (20”) per minute after 3 cycles.2Recommended bonding conditions will vary between different machinery and fabrics. The recommended conditions stated are a starting point only. Optimal bonding conditions should be established by the factory of the specific application.

NOTE: Seller hereby excludes any express warranties and the implied warranties of merchantability and fitness for a particular purpose. The following is made in lieu of any such “warranties.” Bemis Associates, Inc. believes the information and specification supplied are reliable, but does not guarantee that any results shown or claimed will be obtained. Before using, the user shall determine the suitability and fitness of the product for its intended use. The user assumes all risks and liability whatever in connection with its own tests and use. Neither seller nor manufacturer shall be liable for any injury, loss or damage, direct or consequential, arising out of the use, or misuse or inability to use this product.

CertificationOeko Tek, Standard 100 Class 1 (Test No. 6187)REACH compliant, European Union (EU) legislation concerning the Registration, Evaluation, Authorization and Restriction of Chemicals (REACH)

HEATHERSEAM REINFORCEMENT TAPE

• Incorporates a heather look for a classic sportswear feel

• High stretch

• Use for construction or aesthetic

• Reduces seam weight

• Strengthens seams

• Soft hand feel

• Withstands high heat wash

Why It’s Worth a Look

WHY IT’S WORTH A LOOK

HEATHER SEAM REINFORCEMENT TAPE

Grey

*Stocked in slit width of 10 mm

Navy

Black

Gold

Red

/ CORE COLORS

HSRT / 1

TECHNICAL INFORMATION

HEATHER SEAM REINFORCEMENT TAPE HSRT4000

MATERIAL Polyester/Spandex Knit Heather Fabric/Polyurethane Adhesive

STOCKED WIDTH 1372 mm

WEIGHT 3.75 g/m

HAND Soft

WASH Excellent at 60°C

MODULUS @ 50% ELONGATION1 2.0 lbf (0.9 kgf)

ADHESIVE SOFTENING POINT 95°C (203°F)

TOTAL THICKNESS 0.024” (0.61 mm)

ADHESIVE THICKNESS 0.004” (0.10 mm)

SERVICE TEMPERATURE −30°C to 60°C (−22°F to 140°F)

INITIAL BONDING CONDITIONS2

FLAT PRESS

TEMPERATURE 115°C to 170°C

TIME 15 to 25 seconds

PRESSURE 2.8 to 4.2 bar (40 to 60 psi)

1Modulus: The force required to pull a 12 mm (0.47”) wide sample by specified gauge to 50% elongation at 508 mm (20”) per minute after 3 cycles.2Recommended bonding conditions will vary between different machinery and fabrics. The recommended conditions stated are a starting point only. Optimal bonding conditions should be established by the factory of the specific application.

NOTE: Seller hereby excludes any express warranties and the implied warranties of merchantability and fitness for a particular purpose. The following is made in lieu of any such “warranties.” Bemis Associates, Inc. believes the information and specification supplied are reliable, but does not guarantee that any results shown or claimed will be obtained. Before using, the user shall determine the suitability and fitness of the product for its intended use. The user assumes all risks and liability whatever in connection with its own tests and use. Neither seller nor manufacturer shall be liable for any injury, loss or damage, direct or consequential, arising out of the use, or misuse or inability to use this product.

REFLECTIVESEAM REINFORCEMENT TAPE

• Reflective properties

• High stretch

• Use for construction or aesthetic

• Reduces seam weight

• Strengthens seams

• Withstands high heat wash

Why It’s Worth a Look

REFLECTIVE SEAM REINFORCEMENT TAPE

/ CORE COLORS

Snow

Pantone 11-0601 TPX

Silver

~400 Cd/Lux

Gold

Pantone 871C

Navy

Pantone 19-4024 TPX

Black

Pantone 19-4006 TPX

RSRT / 1

REFLECTIVE SEAM REINFORCEMENT TAPE

/ CORE COLORS

Red

Pantone 18-1763 TPX

Radiation

Pantone 388C

Spray Tan

Pantone 1505C

RSRT / 2

TECHNICAL INFORMATION

REFLECTIVE SEAM REINFORCEMENT TAPE RSRT3000

MATERIAL Reflective Film/Polyester Spandex Knit Fabric/Polyurethane Adhesive

STOCKED WIDTH 10 mm, 1250 mm

WEIGHT 4.7 g/m

HAND Medium

WASH Excellent at 60°C

MODULUS @ 50% ELONGATION1 3.3 lbf (1.5 kgf)

CANDLEPOWER2 ~20 Cd/Lux (varies by color)

ADHESIVE SOFTENING POINT 95°C (203°F)

TOTAL THICKNESS 0.017” (0.43 mm)

ADHESIVE THICKNESS 0.004” (0.10 mm)

SERVICE TEMPERATURE −30°C to 60°C (−22°F to 140°F)

INITIAL BONDING CONDITIONS3

FLAT PRESS

TEMPERATURE 115°C to 170°C

TIME 15 to 25 seconds

PRESSURE 2.8 to 4.2 bar (40 to 60 psi)

1Modulus: The force required to pull a 12 mm (0.47”) wide sample by specified gauge to 50% elongation at 508 mm (20”) per minute after 3 cycles.2Candlepower: Varies by color and/or graphic. Contact Bemis for exact specifications.3Recommended bonding conditions will vary between different machinery and fabrics. The recommended conditions stated are a starting point only. Optimal bonding conditions should be established by the factory of the specific application.

NOTE: Seller hereby excludes any express warranties and the implied warranties of merchantability and fitness for a particular purpose. The following is made in lieu of any such “warranties.” Bemis Associates, Inc. believes the information and specification supplied are reliable, but does not guarantee that any results shown or claimed will be obtained. Before using, the user shall determine the suitability and fitness of the product for its intended use. The user assumes all risks and liability whatever in connection with its own tests and use. Neither seller nor manufacturer shall be liable for any injury, loss or damage, direct or consequential, arising out of the use, or misuse or inability to use this product.

NARROWSEAM REINFORCEMENT TAPE

• Ultimate stretch

• Reduces seam weight

• Use for construction or aesthetic

• Strengthens seams

• Soft hand feel

• Withstands high heat wash

Why It’s Worth a Look

NARROW SEAM REINFORCEMENT TAPE

/ CORE COLORS

Snow

Pantone 11-0601 TPX

*Stocked in slit width of 15 mm

Grey

Pantone 17-1501 TPX

*Stocked in slit width of 15 mm

Ash

Pantone 19-4104 TPX

Navy

Pantone 19-4024 TPX

Pitch

Pantone 19-4006 TPX

*Stocked in slit width of 15 mm

NSRT / 1

NARROW SEAM REINFORCEMENT TAPE

/ CORE COLORS

Red

Pantone 18-1763 TPX

Orange

Pantone 17-1464 TPX

Electric

Pantone 285C

Radiant

Pantone 803C

Luminous

Pantone 804C

NSRT / 2

NARROW SEAM REINFORCEMENT TAPE

/ CORE COLORS

Jolt

Pantone 802C

Blazing

Pantone 801C

Intense

Pantone 806C

Flashy

Pantone 807C

NSRT / 3

TECHNICAL INFORMATION

NARROW SEAM REINFORCEMENT TAPE NSRT3900

MATERIAL Nylon/Spandex Knit Narrow Width Ribbon/Polyurethane Adhesive

STOCKED WIDTH 10 mm

WEIGHT 3.15 g/m

HAND Medium

WASH Excellent at 60°C

MODULUS @ 50% ELONGATION1 1.3 lbf (0.6 kgf)

ADHESIVE SOFTENING POINT 95°C (203°F)

TOTAL THICKNESS 0.021” (0.53 mm)

ADHESIVE THICKNESS 0.004” (0.10 mm)

SERVICE TEMPERATURE −30°C to 60°C (−22°F to 140°F)

INITIAL BONDING CONDITIONS2

FLAT PRESS

TEMPERATURE 115°C to 170°C

TIME 15 to 25 seconds

PRESSURE 2.8 to 4.2 bar (40 to 60 psi)

1Modulus: The force required to pull a 12 mm (0.47”) wide sample by specified gauge to 50% elongation at 508 mm (20”) per minute after 3 cycles.2Recommended bonding conditions will vary between different machinery and fabrics. The recommended conditions stated are a starting point only. Optimal bonding conditions should be established by the factory of the specific application.

NOTE: Seller hereby excludes any express warranties and the implied warranties of merchantability and fitness for a particular purpose. The following is made in lieu of any such “warranties.” Bemis Associates, Inc. believes the information and specification supplied are reliable, but does not guarantee that any results shown or claimed will be obtained. Before using, the user shall determine the suitability and fitness of the product for its intended use. The user assumes all risks and liability whatever in connection with its own tests and use. Neither seller nor manufacturer shall be liable for any injury, loss or damage, direct or consequential, arising out of the use, or misuse or inability to use this product.

GRAPHICSEAM REINFORCEMENT TAPE

• Customizable in up to 8 colors using a proprietary digital print process

• High stretch

• Use for construction or aesthetic

• Reduces seam weight

• Strengthens seams

• Soft hand feel

• Withstands high heat wash

Why It’s Worth a Look

GRAPHIC SEAM REINFORCEMENT TAPE

/ CORE COLORS

Example A

Example B

Example C

GSRT / 1

TECHNICAL INFORMATION

GRAPHIC SEAM REINFORCEMENT TAPE GSRT1000

MATERIAL Digital Print Pigment: Nylon/Spandex Knit Narrow Width Ribbon/ Polyurethane Adhesive

STOCKED WIDTH 10 mm

WEIGHT 3.15 g/m

HAND Medium

WASH Excellent at 60°C

MODULUS @ 50% ELONGATION1 1.5 lbf (0.7 kgf)

ADHESIVE SOFTENING POINT 95°C (203°F)

TOTAL THICKNESS 0.020” (0.51 mm)

ADHESIVE THICKNESS 0.004” (0.10 mm)

SERVICE TEMPERATURE −30°C to 60°C (−22°F to 140°F)

INITIAL BONDING CONDITIONS2

FLAT PRESS

TEMPERATURE 115°C to 170°C

TIME 15 to 25 seconds

PRESSURE 2.8 to 4.2 bar (40 to 60 psi)

1Modulus: The force required to pull a 12 mm (0.47”) wide sample by specified gauge to 50% elongation at 508 mm (20”) per minute after 3 cycles.2Recommended bonding conditions will vary between different machinery and fabrics. The recommended conditions stated are a starting point only. Optimal bonding conditions should be established by the factory of the specific application.

NOTE: Seller hereby excludes any express warranties and the implied warranties of merchantability and fitness for a particular purpose. The following is made in lieu of any such “warranties.” Bemis Associates, Inc. believes the information and specification supplied are reliable, but does not guarantee that any results shown or claimed will be obtained. Before using, the user shall determine the suitability and fitness of the product for its intended use. The user assumes all risks and liability whatever in connection with its own tests and use. Neither seller nor manufacturer shall be liable for any injury, loss or damage, direct or consequential, arising out of the use, or misuse or inability to use this product.