Elements Required Required
ASTM A 564 Type 630 10088-3 Mat. 1.4542
Carbon 0.07 0.07 0.07
Manganese 1.00 1.50 1.00
Phosphorus 0.04 0.04 0.04
Sulfur 0.03 0.03 0.03
Silicon 1.00 0.70 0.70
Chromium 15.0017.50 15.0017.00 15.0017.00
Nickel 3.00-5.00 3.00-5.00 3.00-5.00
Aluminium ---- ----
Molybdenum ---- 0.60 0.60
Titanium ---- ----
Copper 3.00-5.00 3.00-5.00 3.00-5.00
Columbium +Tantalum 0.15 - 0.45 ----
Niobium 5 x C to 0.45 5 x C to 0.45
Required Required
ASTM A 564 Type 630 10088-3 Mat. 1.4542 (+P930)
Homogenization
Temperature Min Not defined. Not defined. 1040C +/-15C
Holding for a minimum Not defined. Not defined. 1.5 Hrs.
Quenching Media Not defined. Not defined. Air
Solution annealing
Temperature 1040C +/-15C 1030C-1050C 1050C +/-15C
Holding for a minimum Not defined Not defined. 30 Min / Inch
Quenching Media Not defined Oil / Air Water
Precipitation Hardening H1150
Temperature 620 C 620 C 620 C
Holding for a minimum 4 Hrs. 4 Hrs. 4 Hrs.
Quenching Media Air cool Air cool Air cool
Required Required
Heat No. ASTM A 564 Type 630 10088-3 Mat. 1.4542 (+P930)
Impact Testing @room
Temperature.41 40 30
Required Required
ASTM A 564 Type 630 10088-3 Mat. 1.4542 (+P930)
Yield Strength 0.2 %
Offset, min Mpa725 720 725
Tensile Strength,
Mpa930 930-1100 930-1100
Elongation in 2
in. [51 mm],
min, %
16.00 16.00 16.00
Reduction in Area. % 50 Not defined. -----
Rockwell C 28 Not defined. -----
Brinell 277 Not defined. -----
Hardness Min
Proposal
Proposal
Chemical Analysis
Heat Treatment Details
Impact Testing
Mechanical Analysis
ElementsProposal
Proposal