Transistor Spring& Gull Wing Clips

MSC Series

Spring Clips - Compared to the conventional nut, boltand insulating bush method spring clips offer a low costand fast way of mounting plastic case transistors compared to the conventional nut, bolt and insulatingbush method. Contact is made with the middle of the transistor whichprovides an even pressure and good thermal contact.Clips allow transistors to operate at higher voltages.Gull Wing Clips - Offer an easy way of mounting one ortwo plastic case transistors in a small place. Gull wingclips deliver high mounting pressure to the centre ofthe transistor case providing maximum heat transfer.

Material Specifications

Manufactured fromCarbon Steel Strip CS70Ann. Sp.St. to BS1449

Parts are heat treated to400 – 430vpn

Finish is eitherDelta Tone

Silver, Zinc plated andclear passivated or Black

Nylon Coated

© 2008 XtronicTel: +44(0) 1883 717243 | Fax: +44(0) 1883 717038 | Email: info@xtronic.co.uk | WWW: www.xtronic.co.uk

Transistor Spring& Gull Wing Clips

MSC Series

MSC607T0-220 DOUBLESuitable for use with any panel or pad thickness. Maximum force is7.5kg per transistor. Screws are not supplied. Zinc plated with clear finish. Additional version with Nylon coating for high voltage applications.Part No. MSC607-ZPPart No. MSC607-NY Nylon coating breakdown voltage750v givingup to 3500v isolation from transistor tab, depending on application.

MSC209T0-220Suitable for use with any panel. Maximum force 12kg. Screws arenot supplied. Zinc plated with clear finish.Part No. MSC209-ZP

MSC506T0-3P T0-218 T0-247 DOUBLESuitable for use with any panel or pad thickness. Maximum force is11kg per transistor. Screws are not supplied. Zinc pated with clearfinish.Additional version with Nylon coating for high voltage applications.Part No. MSC506-ZPPart No. MSC506-NY Nylon coating breakdown voltage750v givingup to 3500v isolation from transistor tab, depending on application.

© 2008 XtronicTel: +44(0) 1883 717243 | Fax: +44(0) 1883 717038 | Email: info@xtronic.co.uk | WWW: www.xtronic.co.uk

Transistor Spring& Gull Wing Clips

MSC Series

MSC405T0-3P T0-218 T0-247 SINGLESuitable for use with any panel. Maximum force 15kg. Screws arenot supplied. Zinc plated with clear finish.Part No. MSC405-ZP (Maximum 1000 volts isolation from tab)

MSC802T0-220Suitable for use with panels up to 1.2mm thick and pads up to0.18mm thick. Maximum force5.5kg. Zinc plated with clear finish.Part No. MSC802

MSC704T0-220Suitable for use with panels up to 2.0mm thick and pads up to0.2mm thick. Maximum force 5.5kg. Zinc plated with clear finish.Part No. MSC704

MSC903T0-3P (T0-218 T0-247 S0T-93)Suitable for use with panels up to 2.0mm thick and pads up to0.2mm thick. Maximum force 10kg. Zinc plated with clear finish.Part No. MSC903