sheet metal processes. introduction sheet metal is simply metal formed into thin and flat pieces. it...

SHEET METAL PROCESSES

Introduction

Sheet metal is simply metal formed into thin and flat pieces. It is one of the fundamental forms used in

metalworking, and can be cut and bent into a variety of different shapes. Countless everyday objects are constructed of the material. Thicknesses can vary significantly, although extremely thin thicknesses are considered foil or leaf, and pieces thicker than 6 mm (0.25 in) are considered plate.

Sheet metal processing The raw material for sheet metal manufacturing

processes is the output of the rolling process. Typically, sheets of metal are sold as flat, rectangular sheets of standard size. If the sheets are thin and very long, they may be in the form of rolls. Therefore the first step in any sheet metal process is to cut the correct shape and sized ‘blank’ from larger sheet.

Sheet Metal Forming processes

Introduction

1. Sheet metal processes involve plane stress loadings and lower forces than bulk forming

2. Almost all sheet metal forming is considered to be secondary processing

3. The main categories of sheet metal forming are • Shearing• Bending• Drawing

Shearing

Shearing is a sheet metal cutting operation along a straight line between two cut-ting edges by means of a power shear.

Blanking and punching

Blanking and punching are similar sheet metal cutting operations that involve cutting the sheet metal along a closed outline. If the part that is cut out is the desired product, the operation is called blanking and the product is called blank. If the remaining stock is the desired part, the operation is called punching. Both operations are illustrated on the example of producing a washer

Bending

Bending is defined as the straining of the sheet metal around a straight edge

Bending force :

Maximum bending force, P = KYLT2

W

K – constant ranges from 0.3(wiping die) – 0.7(u-die)-1.3(V-die)Y – yield stressL- length of the bendT- thickness of sheet

For a V-dieMax bending force, P = (UTS)LT 2

WUTS – Ultimate tensile strength

Drawing

Drawing is a sheet-metal operation to make hollow-shaped parts from a sheet blank

Dies and Punches

Simple- single operation with a single stroke

Compound- two operations with a single stroke

Combination- two operations at two stations

Progressive- two or more operations at two or more stations with each press stroke, creates what is called a strip development

COMPOUND DIES

Several operations on the same strip performed in one stroke at one station with a compound dies

Schematic illustrations: (a) before and (b) after blanking a common washer in a compound die.note the separate movements of the die(or blanking) and the punch

Progressive dies

Merits

•High strength•Good dimensional accuracy and surface finish•Relatively low cost

Demerits•Wrinkling and tearing are typical limits to drawing operations•Trimming may be used to reach final dimensions

Applications

•Roofing•Ducting•Vehicles body buildings like 3 wheelers, 4 wheelers, ships, aircrafts etc.•Furniture, House hold articles and Railway equipment

ROLL FORMING

Process where sheet metal strips are passed through consecutive set of rolls and bent in consecutive stages and then sheared into specific lengths and stacked continuously.

Forming speed: below 1.5 m/s (300 ft/min) Examples: Door panels, picture frame, and gutters.

Stretch Forming

Process where a sheet metal is clamped along it’s edges and stretched over a male die (form die or form punch).

Examples: aircraft wing-skin panels, fuselages, and boat hulls.

Rubber Forming One of the dies in the set is made of polyurethane

membrane, which is a type of flexible material. Polyurethane is resistant to abrasion, cutting or tearing by

the metal, and has a long fatigue life.

SPINNING

Process where a circular piece of sheet metal is placed and held against a mandrel and rotated while a rigid tool deforms and shapes the material over the mandrel.

May be performed at room temperature or at higher temperature for thicker metal.

Shear spinning :

Known as power spinning, flow turning, hydro-spinning, and spin forging

Produces axisymmetric conical or curvilinear shape Single rollers and two rollers can be used It has less wastage of material Typical products are rocket- motor casing and missile nose cones.

Tube spinning

Thickness of cylindrical parts are reduced by spinning them on a cylindrical mandrel rollers

Parts can be spun in either direction Large tensile elongation up to 2000 % are obtained within certain

temperature ranges and at low strain rates.

Super Plastic FormingTypes of structures made by diffusion bonding and superplastic forming of sheet metal. Such structures have a high stiffness-to-weight ratio.

EXPLOSIVE FORMING

First used to form metals in the 1900’s. A sheet metal blank is clamped over a die, and the entire assembly is lowered into a tank filled with water. The air in the cavity is evacuated, and an explosive is detonated at a certain height above.

MAGNETIC-PULSE FORMING

Also called electromagnetic forming. Energy stored in a capacitor bank is discharged rapidly through a magnetic coil. Magnetic field crosses metal tube (conductor) creating eddy currents which have an opposing magnetic field.(a)

(b)

Figure 16.45 (a) Schematic illustration of the magnetic-pulse forming process used to form a tube over a plug. (b) Aluminum tube collapsed over a hexagonal plug by the magnetic-pulse forming process.