BOPP-FILMSTECHNICAL DATA SHEETS
TRANSPARENT FILMS . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .4
HGPL Heat sealable transparent film with – standard coefficient of friction . . . 4HGHL Heat sealable transparent film with low coefficient of friction . . . . . . . . . 6HGFL Heat sealable transparent film with high coefficient of friction
for special purposes . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 8HASL Antifog . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 10PGR Transparent release film . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 12HGSL Heat sealable transparent film for hot climate . . . . . . . . . . . . . . . . . . . . 14
METALLIZED FILMS . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .16
HMPL .M Metallized heat sealable film for general purposes . . . . . . . . . . . . . . . . 16HMPLB .M Metallized heat sealable film with improved barrier properties . . . . . . . 18HOHMLB .M Metallized white pearlised heat sealable film with improved
barrier properties . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 20HMIL .M Metallized heat sealable for printing and lamination . . . . . . . . . . . . . . . 22PMD .M Metallized non heat sealable film for the production
of decorative packaging . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 24HMPLA .M Heat sealable with low sealing threshold and with barrier properties . . 26
NON-FOOD FILMS . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .28
PGA Transparent non heat sealable film for general purposes and production of adhesive tapes . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 28
PGD Transparent non heat sealable film for general purposes and decorative packaging . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 30
PGT Transparent non heat sealable for general purposes and decorative overwrapping . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 32
PWA White none heat sealable opaque for general purposes and production of adhesive tapes . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 34
MATT FILMS . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .36
MGS One side matt non heat sealable film . . . . . . . . . . . . . . . . . . . . . . . . . . . 36
MGD Both side matt non heat sealable film . . . . . . . . . . . . . . . . . . . . . . . . . . 38MGPL Matt heat sealable film with low seal initiation temperature . . . . . . . . . 40MGR Matte release film . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 42
OPAQUE FILMS . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .44
HOHL Heat sealable white-pearlised film with low seal initiation temperature 44HWHL White heat sealable film with low seal-initiation temperature . . . . . . . . 46HOHW White Pearlised film with wide heatsealing range . . . . . . . . . . . . . . . . . 48HOHG White Pearlised film both side corona treated with a standard
coefficient of friction . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 50HWHW White heat sealable film with low seal intention temperature . . . . . . . . 52HOSL Heat sealable White Pearlised high antistatic film with low seal
intention temperature . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 54
LABEL FILMS . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .56
LGBA Transparent film for labels . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 56LOBA White Pearlised film for full-wrap label . . . . . . . . . . . . . . . . . . . . . . . . . 58LOBB White Pearlised film for full-wrap label with improved gloss . . . . . . . . . 60LOBC White Pearlised film for full-wrap label with high yield . . . . . . . . . . . . . 62LOHM .M White pearlised metallized film for bottle labeling . . . . . . . . . . . . . . . . . 64LOMB Matt White Pearlised microporous film . . . . . . . . . . . . . . . . . . . . . . . . . . 66
TOBACCO FILMS . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .68
TSHL Heat shrinkable non treated-film for «rigid» carton pack overwrapping 68TGHL Non heat shrinkable non treated – film for «soft» and «rigid»
carton pack overwrapping . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 70TSHD Heat shrinkable – non treated film for «rigid» carton pack
overwrapping for ultra high speed machines . . . . . . . . . . . . . . . . . . . . . 72TSHT Heat shrinkable treated film «rigid» carton pack overwrapping . . . . . . . 74
STORAGE AND HANDLING
Rolls should be stored In their original wrapping on pallets in dry closed sun protected place minimum 1 meter from heating units.
Storage conditions should eliminate any risk of wrapping deterioration. If stored in unheated area Biaxplen films should be placed at room temperature and humidity at least for 48 hours before converting.
It’ is recommended to corona pre treat fi lm before printing Guaranteed storage life is 6 months from the date of production.
SURFACE TREATMENT
Metallized film surface energy Is affected by temperature and storage life. Biaxplen guarantees surface treatment level of metallized films higher than 36 dynes within 15 days after metallization. In order to minimize the deterioration of surface energy it is recommended to store film below 30°C and to convert it asap. Should film be used for specific application, it is advisable to measure surface energy in order to prove if it suits. Standard roll- outside corona treated web. Metallized film is advised to be primer covered before printing. Metallized film can be laminated with a number of materials.
It’s highly recommended that the film should be used according to the application recommended by the Producer.
Information given in Techical data sheets is based on typical values checked in standard production. Techical data sheet has not to be considered a product specification.
* 500 kg
DIMENSIONS
ApplicationMax outer
diameter, mm
Corediameter,
mm
Tolerance
Width, mm Order weight
For tobaccofilms
50076 120 152
± 0,5± 10%*450
400300 < 2000 kg ± 20%
For allpackaging
films
98076
152
± 3 mm> 2000 kg ± 10%
780 > 5000 kg ± 5%
580 ± 2 mm >10000 kg ± 2%
4
TRANSPARENT FILMS
Biaхplen HGPL
B Treated modified heat sealable copolymer skin layer
C Transparent oriented polypropylene core layer
D Heat sealable, non treated skin layer with low seal intention temperature and standard coefficient of friction
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for vertical VFFS and horizontal HFFS packaging machines;• production of decorative packaging for flowers, gift wrap and etc.;• for cold seal glue frame coating onto UT film side (if necessary).
MAIN PROPERTIES:• A wide range of heat sealing;• contains slip-antistatic and antiblocking additives;• excellent optical properties;• good physical and mechanical properties;• intended for contact with food;• standard coefficient of friction;• without coatings and primers.
DESCRIPTION:Heat sealable transparent BOPP film with a standard coefficient of friction and low heat sealing threshold for packaging machines.For high quality rotogravure and flexographic printing and lamination.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit HGPL
Thickness, ± 5%
BIAXPLEN
mkm 15 18 20 25 30 35 40 48
Density* g/cm3 0,91
Weight, ± 5% g/m2 13,65 16,38 18,20 22,75 27,30 31,85 36,40 43,68
Yield, ± 5% m2/kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47 22,89
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa
130 140
TD 230 250
Elongation at break, not moreMD
%220 200
TD 80 70
Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,3
+ 0,10
- 0,15
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %
5 4
TD 3 2
Heat sealing strength at 130 °C, 1 bar, 1 sec, not less UT/UT GOST 27319 ISO 527
ASTM D 882,
ASTM F 88N/15 mm 2,0 2,2 2,3 2,5 2,8
Haze, not more GOST 15875 ISO 14782 ASTM D 1003 % 2,5 3,0 3,2
Gloss at 45 °, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 85
Heat sealing range at 1 bar, 1 sec .* UT/UT BIAXPLEN °C 105–140
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578
Dyne/cm, mN/m 38
6
TRANSPARENT FILMS
Biaхplen HGHL
B Treated modified heat sealable copolymer skin layer
C Transparent oriented polypropylene core layer
D Heat sealable, non treated skin layer with low seal intention temperature and low coefficient of friction
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for high-speed vertical VFFS and horizontal HFFS packaging machines.
MAIN PROPERTIES:• A wide range of heat sealing;• contains slip-antistatic and antiblocking additives;• excellent optical properties;• good mechanical properties;• intended for contact with food;• both side low coefficient of friction;• without coatings and primers.
DESCRIPTION:Heat sealable transparent BOPP film with low coefficient of friction and low heat sealing threshold for high-speed packaging machines.For high quality rotogravure and flexographic printing and lamination.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit HGHL
Thickness, ± 5%
BIAXPLEN
mkm 15 18 20 25 30 35 40 48
Density* g/cm3 0,91
Weight, ± 5% g/m2 13,65 16,38 18,20 22,75 27,30 31,85 36,40 43,68
Yield, ± 5% m2/kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47 22,89
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa
130 140
TD 230 250
Elongation at break, not moreMD
%220 200
TD 80 70
Kinetic coefficient of friction UT/UT
GOST 27492 ISO 8295 ASTM D 1894 —
0,2 +0,05
Т/Т -0,1
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %
5 4
TD 3 2
Heat sealing strength at 130 °C, 1 bar, 1 sec, not less UT/UT GOST 27319 ISO 527
ASTM D 882,
ASTM F 88N/15 mm 2,0 2,2 2,3 2,5 2,8
Haze, not more GOST 15875 ISO 14782 ASTM D 1003 % 2,5 3,0 3,2
Gloss at 45 °, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 85
Heat sealing range at 1 bar, 1 sec .* UT/UT BIAXPLEN °C 105 - 140
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578
Dyne/cm, mN/m 38
8
TRANSPARENT FILMS
Biaхplen HGFL
B Treated modified heat sealable copolymer skin layer
C Transparent oriented polypropylene core layer
D Heat sealable, non treated skin layer with low seal intention temperature and high coefficient of friction
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for vertical VFFS and horizontal HFFS packaging machines;• laminating with PE and CPP films with a high content of slipping additives;• to reduce the impact of slip additives transition from PE or CPP film to the BOPP film side,
which leads to a significant coefficient of friction reduction. The high coefficient of friction of the HGFL film, provides a certain margin in this case;
• for a case in which the bondage process of packed products is present, for example, in pasta packaging;
• to save the packed packages in a single group without sliding over each other (if necessary);
• in the other cases, when slip reduction on BOPP side of the flexible packaging is necessary;
• for cold seal glue frame coating onto UT film side (if necessary).
MAIN PROPERTIES:• A wide range of heat sealing;• contains antistatic and antiblocking additives;• excellent optical properties;• good mechanical properties;• intended for contact with food;• high coefficient of friction stable in time;• without coatings and primers.
DESCRIPTION:Heat-sealing transparent BOPP film with a low threshold of welding, with high coefficient of friction for a special purposes, for high quality rotogravure and flexographic printing and lamination.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit HGFL
Thickness, ± 5%
BIAXPLEN
mkm 15 18 20 25 30 35 40 48
Density* g/cm3 0,91
Weight, ± 5% g/m2 13,65 16,38 18,20 22,75 27,30 31,85 36,40 43,68
Yield, ± 5% m2/kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47 22,89
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa
130 140
TD 230 250
Elongation at break, not moreMD
%220 200
TD 80 70
Kinetic coefficient of friction UT/UT
GOST 27492 ISO 8295 ASTM D 1894 — 0,45
+ 0,20
- 0,05
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %
5 4
TD 3 2
Heat sealing strength at 130 °C, 1 bar, 1 sec, not less UT/UT GOST 27319 ISO 527
ASTM D 882,
ASTM F 88N/15 mm 2,0 2,2 2,3 2,5 2,8
Haze, not more GOST 15875 ISO 14782 ASTM D 1003 % 2,5 3,0 3,2
Gloss at 45 °, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 85
Heat sealing range at 1 bar, 1 sec .* UT/UT BIAXPLEN °C 105 - 140
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578
Dyne/cm, mN/m 38
10
TRANSPARENT FILMS
Biaхplen HASL
B Corona treated, heat sealable skin layer with low coefficient of friction, designed for printing (OUT)
C Transparent oriented polypropylene tie layer
D Transparent, specially designed, oriented polypropylene core layer
E Transparent, specially designed, oriented polypropylene tie layer
F Antifog, corona treated, heat sealable skin layer with low coefficient of friction (IN)
APPLICATION:• High quality rotogravure and flexographic solvent based printing;• production of flexible packaging, requiring no fogging during packed product storage;• packing lettuce, shredded vegetables, herbs, etc.;• packaging for vertical VFFS and horizontal HFFS packaging machines;• application temperature not below + 5 C.
MAIN PROPERTIES:• IN side has an antifog properties;• OUT side is the printable;• antifog properties for 6 month;• low coefficient of friction on both sides;• both side heat sealable;• high optical and physical-mechanical properties;• contains a slip-antiblock and special additives;• intended for contact with food;• without blocking in unwinding;• without coatings or primer.
DESCRIPTION:Transparent, antifog, both side corona treated BOPP film, for high quality rotogravure and flexographic printing, for the production of packaging for salads and vegetables.
MD – Machine, longitudinal direction OUT – the outside of the roll TD – Transverse direction IN – The inside of the roll GOST – Russian Federation standards * Typical values
Properties Methods Unit HASL
Thickness, ± 5%
BIAXPLEN
mkm 20 25 30 35 40
Density* g/cm3 0,91
Weight, ± 5% g/m2 18,20 22,75 27,30 31,85 36,4
Yield, ± 5% m2/kg 54,95 43,96 36,63 31,40 27,47
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa130 140
TD 230 250
Elongation at break, not moreMD
%220 200
TD 80 70
Kinetic coefficient of friction OUT/OUT
GOST 27492 ISO 8295 ASTM D 1894 — 0,2+ 0,1
IN/IN - 0,1
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %5 4
TD 2 2
Heat sealing strength at 130 °C, 1 bar, 1 sec, not lessOUT/IN
GOST 27319 ISO 527 ASTM D 882, ASTM F 88 N/15 mm
2,3 2,8
Haze, not more GOST 15875 ISO 14782 ASTM D 1003 % 3 3,2
Gloss at 45 °, not less OUT BIAXPLEN ISO 2813 ASTM D 2457 % 85
Heat sealing range at 1 bar, 1 sec .* OUT/IN BIAXPLEN °C 120 - 140
Treatment level, not less OUT — ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
Water vapour transmission rate at 38 °C, 90% rel .humidity, 24 h* BIAXPLEN — ASTM F 1249 g/m2/24 h 6,5 5,2 4,3 3,7 3,3
Oxygen transmission rate at 23 °С, 0% rel .humidity 24 h* BIAXPLEN — ASTM D 3985 cm3/m2/24 h 2650 2100 1750 1500 1300
IN OUT
12
TRANSPARENT FILMS
Biaхplen PGR
B Treated modified copolymer skin layer
C Transparent oriented polypropylene core layer
D Non heat sealable, untreated release skin layer with low coefficient of friction
APPLICATION:• High quality rotogravure and flexographic solvent printing;• solvent or solventless polyurethane laminating adhesives;• for the production of flexible packaging (typically duplex) with frame cold seal glue.
MAIN PROPERTIES:• UT side has a release properties to the latex cold seal glue;• high optical: transparency and gloss and high physical and mechanical
properties;• low coefficient of friction, including hot surfaces, specially for HFFS machines;• contains antistatic, slip-antiblocking and release additives;• intended for contact with food;• chemically resistant to oils, fats and chemicals.
DESCRIPTION:Transparent release BOPP film for high quality rotogravure and flexographic printing and lamination; for the production of flexible packaging with frame cold seal glue.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit PGR
Thickness, ± 5%
BIAXPLEN
mkm 15 20 25 30 35
Density* g/cm3 0,91
Weight, ± 5% g/m2 13,65 18,20 22,75 27,30 31,85
Yield, ± 5% m2/kg 73,26 54,95 43,96 36,63 31,40
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa150 140
TD 250
Elongation at break, not moreMD
%200
TD 70
Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,25+0,10
-0,15
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %5 4
TD 2 2
Haze, not more GOST 15875 ISO 14782 ASTM D 1003 % 2
Gloss at 45 °, not less UT — ISO 2813 ASTM D 2457 % 85
Treatment level, not less T — ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
14
TRANSPARENT FILMS
Biaхplen HGSL
B Treated modified heat sealable copolymer skin layer
C Transparent oriented polypropylene core layer
D Heat sealable, non treated skin layer with low seal intention temperature and standard coefficient of friction
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for vertical VFFS packaging machines as film in laminate, turned to pulling belts;• for horizontal HFFS packaging machines as internal film in laminate (turned to the
product);• production of decorative packaging for flowers, gift wrap and etc.;• for cold seal glue frame coating onto UT film side (if necessary).
MAIN PROPERTIES:• A wide range of heat sealing;• contains low speed migratory slip-antistatic additives;• less slippery surface in comparison with HGPL film;• contains an antiblock additives;• stable optical properties;• good physical and mechanical properties;• intended for contact with food;• standard coefficient of friction;• without coatings and primers.
DESCRIPTION:Heat sealable transparent BOPP film for hot climate with a standard coefficient of friction and low heat sealing threshold for packaging machines.For high quality rotogravure and flexographic printing and lamination.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit HGSL
Thickness, ± 5%
BIAXPLEN
mkm 15 18 20 25 30 35 40 48
Density* g/cm3 0,91
Weight, ± 5% g/m2 13,65 16,38 18,20 22,75 27,30 31,85 36,40 43,68
Yield, ± 5% m2/kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47 22,89
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa
130 140
TD 230 250
Elongation at break, not moreMD
%220 200
TD 80 70
Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,35
+ 0,10
- 0,15
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %
5 4
TD 3 2
Heat sealing strength at 130 °C, 1 bar, 1 sec, not less UT/UT GOST 27319 ISO 527
ASTM D 882,
ASTM F 88N/15 mm 2,0 2,2 2,3 2,5 2,8
Haze, not more GOST 15875 ISO 14782 ASTM D 1003 % 2,3 2,8 3,0
Gloss at 45 °, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 85
Heat sealing range at 1 bar, 1 sec .* UT/UT BIAXPLEN °C 105–140
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578
Dyne/cm, mN/m 38
16
METALLIZED FILMS
Biaхplen HMPL .M
B Aluminum layer
C Treated modified copolymer layer for aluminum adhesion
D Transparent oriented polypropylene core layer
E Heat sealable non treated, skin layer with standard coefficient of friction
APPLICATION:• High quality rotogravure and flexographic solvent based printing;• for lamination with solvent based or solventless polyurethane adhesives;• manufacture of flexible packaging for food products;• packaging for vertical VFFS and horizontal HFFS packaging machines;• for production of fully wrapped labels for bottles;• UT side can be coated by frame cold seal glue.
MAIN PROPERTIES:• Good adhesion of the aluminum layer;• excellent optical and barrier properties of the metallized films;• low threshold for welding, high adhesion of aluminum, good mechanical
properties;• stable standard coefficient of friction;• contains slip-antiblock additives;• intended for contact with food;• without coatings and primers;• UT side is allowed to accept activation inline on the printing press or laminator
(if necessary).
DESCRIPTION:Metallized heat sealable BOPP film with a low sealing intention temperature and standard coefficient of friction for printing and lamination.
MD – Machine, longitudinal direction T – Metallized side TD – Transverse direction UT – Untreated, non metallized film side GOST – Russian Federation standards * Typical value ** Garanteed shelf life of the activation of the metallized side is 15 days from the date of manufacture indicated on roll label
Properties Methods Unit HMPL .M
Thickness, ± 5%
BIAXPLEN
mkm 15 18 20 25 30 35 40
Density* g/cm3 0,91
Weight, ± 5% g/m2 13,65 16,38 18,20 22,75 27,30 31,85 36,40
Yield, ± 5% m2/kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa
130 140
TD 230 250
Elongation at break, not moreMD
%220 200
TD 80 70
Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,3
+ 0,15
- 0,15
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %
5 4
TD 3 2
Heat sealing strength at 130 °C, 1 bar, 1 sec, not less UT/UT GOST 27319 ISO 527
ASTM D 882,
ASTM F 88N/15 mm 2,0 2,2 2,3 2,5 2,8
Heat sealing range at 1 bar, 1 sec .* UT/UT BIAXPLEN °С 105 - 140
Optical density, not less — 1,8
Treatment level, not less** T BIAXPLEN ISO 8296 ASTM D 2578
Dyne/cm, mN/m 36
18
METALLIZED FILMS
Biaхplen HMPLB .M
B Aluminum layer with increased thickness
C Treated modified layer for high adhesion to aluminum
D Transparent oriented polypropylene core layer
E Heat sealable, non treated skin layer with standard coefficient of friction
APPLICATION:• High quality rotogravure and flexographic solvent based printing;• for lamination with solvent based or solventless polyurethane adhesives;• manufacture of flexible packaging for the food with long shelf life: cakes, sunflower seeds,
candies, chips and the like;• for vertical VFFS and horizontal HFFS packaging machines;• for cold seal glue frame coating onto UT film side (if necessary).
MAIN PROPERTIES:• More thick coating of aluminium is firmly bound to the film• high barrier properties to oxygen and water vapor;• low threshold for heat sealing, high adhesion of aluminum, good mechanical
properties;• permanent standard coefficient of friction;• contains no migratory antiblock and slip additives;• intended for contact with food;• without coating or primer.
DESCRIPTION:Metallized heatsealable BOPP film with low sealing threshold and standard coefficient of friction, with barrier properties, for printing and lamination.
MD – Machine, longitudinal direction T – Metallized side TD – Transverse direction UT – Untreated, non metallized film side GOST – Russian Federation standards * Typical value ** Garanteed shelf life of the activation of the metallized side is 30 days from the date of manufacture indicated on roll label
Properties Methods Unit HMPLB .M
Thickness, ± 5%
BIAXPLEN
mkm 18 20 30 35 40
Density* g/cm3 0,91
Weight, ± 5% g/m2 16,38 18,20 27,30 31,85 36,40
Yield, ± 5% m2/kg 61,05 54,95 36,63 31,40 27,47
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa130 140
TD 230 250
Elongation at break, not moreMD
%220 200
TD 80 70
Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,3+ 0,10
- 0,10
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %5 4
TD 3 2
Heat sealing strength at 130 °C, 1 bar, 1 sec, not less UT/UT GOST 27319 ISO 527 ASTM D 882, ASTM F 88 N/15 mm 2,0 2,3
Heat sealing range at 1 bar, 1 sec .* UT/UT BIAXPLEN °С 105 - 140
Optical density, not less — 2,3
Treatment level, not less** T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 36
Water vapour transmission rate at 38 °C, 90% rel .humidity, 24 h, not more
BIAXPLEN — ASTM F 1249 g/m2/24 h 1,0
Oxygen transmission rate at 23 °С, 24 h, not more BIAXPLEN — ASTM D 3985 cm3/m2/24 h 50
20
METALLIZED FILMS
Biaхplen HOHMLB .M
B Aluminum layer with increased thickness
C Treated modified layer for high adhesion to aluminum
D Oriented polypropylene tie layer
E White Pearl cavitated core layer of orinted polypropylene
F Oriented polypropylene tie layer
G White pearl heat sealable, non treated skin layer with standard coefficient of friction
APPLICATION:• High quality rotogravure and flexographic solvent based printing;• for both side printing or in center of triplex lamination;• for lamination with solvent based or solventless polyurethane adhesives;• production of flexible packaging with frame cold glue;• manufacture of flexible packaging for products with high shelf life;• manufacture of lid for trays with food, typically in center of triplex;• production of flexible packaging for the bouillon cubes.
MAIN PROPERTIES:• Metallized side with high adhesion to the film;• low threshold for heat welding, increased barrier properties and stable
coefficient of friction;• contains mineral fillers as calcium carbonate and titanium dioxide;• good protection from UV and sunlight;• intended for contact with food;• pearl side (UT) easily takes an activation, at 200 m/min corona
power 4 KW is enough for proper printing or lamination;• without coating or primer.
DESCRIPTION:Metallized white pearl microporous heatsealable BOPP film with increased barrier properties for printing and laminations for production of flexible packaging for products with long shelf life.
MD – Machine, longitudinal direction T – Metallized side TD – Transverse direction UT – White pearl side, untreated side GOST – Russian Federation standards * Typical value ** Garanteed shelf life of the activation of the metallized side is 15 days from the date of manufacture indicated on roll label
Properties Methods Unit HOHMLB .M
Thickness, ± 5%
BIAXPLEN
mkm 30 35 40
Density* g/cm3 0,7
Weight, ± 5% g/m2 21,0 24,5 28,0
Yield, ± 5% m2/kg 47,6 40,8 35,7
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa70
TD 140
Elongation at break, not moreMD
%200
TD 60
Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295 ASTM D 1894 —0,4 +0,1
-0,1
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Heat sealing strength at 130 °C, 1 bar, 1 sec, not less UT/UT GOST 27319 ISO 527 ASTM D 882, ASTM F 88 N/15 mm 2,5
Heat sealing range at 1 bar, 1 sec* UT/UT BIAXPLEN °С 105 - 140
Optical density, not less BIAXPLEN — 2,5
Treatment level, not less** T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 36
Water vapour transmission rate at 38 °C, 90% rel .humidity, 24 h, not more
BIAXPLEN — ASTM F 1249 g/m2/24 h 1
Oxygen transmission rate at 23 °С, 24 h, not more BIAXPLEN — ASTM D 3985 cm3/m2/24 h 90
22
METALLIZED FILMS
Biaхplen HMIL .M
B Aluminum layer
C Treated modified copolymer layer for aluminum adhesion
D Transparent oriented polypropylene core layer
E Heat sealable non treated, skin layer with standard coefficient of friction
APPLICATION:• High quality rotogravure and flexographic solvent based printing;• for lamination with solvent based or solventless polyurethane adhesives;• manufacture of flexible packaging for food products;• packaging for vertical VFFS and horizontal HFFS packaging machines;• for production of fully wrapped labels for bottles;• UT side can be coated by frame cold seal glue.
MAIN PROPERTIES:• Excellent adhesion of the aluminum layer;• long time surface tension shelf life;• good optical and barrier properties of the metallized films;• low threshold for welding, high adhesion of aluminum, good mechanical
properties;• stable standard coefficient of friction;• contains slip-antiblock additives;• intended for contact with food;• without coatings and primers;• UT side is allowed to accept activation inline on the printing press or laminator
(if necessary).
DESCRIPTION:Metallized heat sealable BOPP film with a low sealing intention temperature, long time surface tension shelf life and standard coefficient of friction for printing and lamination.
MD – Machine, longitudinal direction T – Metallized side TD – Transverse direction UT – Untreated, non metallized film side GOST – Russian Federation standards * Typical value ** Garanteed shelf life of the activation of the metallized side is 30 days from the date of manufacture indicated on roll label
Properties Methods Unit HMIL .M
Thickness, ± 5%
BIAXPLEN
mkm 15 18 20 25 30 35 40
Density* g/cm3 0,91
Weight, ± 5% g/m2 13,65 16,38 18,20 22,75 27,30 31,85 36,40
Yield, ± 5% m2/kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa
130 140
TD 230 250
Elongation at break, not moreMD
%220 200
TD 80 70
Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,3
+ 0,15
- 0,15
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %
5 4
TD 3 2
Heat sealing strength at 130 °C, 1 bar, 1 sec, not less UT/UT GOST 27319 ISO 527
ASTM D 882,
ASTM F 88N/15 mm 2,0 2,2 2,3 2,5 2,8
Heat sealing range at 1 bar, 1 sec .* UT/UT BIAXPLEN °С 105 - 140
Optical density, not less — 1,8
Treatment level, not less** T BIAXPLEN ISO 8296 ASTM D 2578
Dyne/cm, mN/m 36
Water vapour transmission rate at 38 °C, 90% rel .humidity, 24 h*
BIAXPLEN — ASTM F 1249 g/m2/24 h 1
Oxygen transmission rate at 23 °С, 0% rel .humidity 24 h*
BIAXPLEN — ASTM D 3985
cm3/m2/24 h 90
24
B Aluminum layer
C Treated modified copolymer layer for aluminum adhesion
D Transparent oriented polypropylene core layer
E Non heat sealable skin layer with high coefficient of friction, without treatment (by default)
APPLICATION:• High quality rotogravure and flexographic solvent based printing; • for lamination with solvent based or solventless polyurethane adhesives; • production of decorative packaging for flowers, gift wrap and etc.; • heat sealing by string is possible;• lamination with films, paper and cardboard;• in case of both side corona treatment:• - lamination as middle of triplex or both side printing;• - cold seal glue coating onto non metalized film side.
MAIN PROPERTIES:• Standard barrier properties of metallized films; • contains antiblock additives; • mechanical properties are good; • high adhesion of the aluminum layer; • intended for contact with food;• without coating or primer.
DESCRIPTION:None heat sealable metallized BOPP film for the production of decorative packaging. With increased coefficient of friction. for printing and lamination and for decorative packaging.
Biaxplen PMD .M
METALLIZED FILMS
Properties Methods Unit PMD .M
Thickness, ± 5%
BIAXPLEN
mkm 20 25 30 35 40
Density * g/cm3 0,91
Weight, ± 5% g/m2 18,2 22,8 27,3 31,9 36,4
Yield, ± 5% m2/kg 54,9 44,0 36,6 31,4 27,5
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa140
TD 280
Elongation at break, not moreMD
%200
TD 70
Kinetic coefficient of friction UT / UT GOST 27492 ISO 8295 ASTM D 1894 — 0,3+ 0,1
- 0,1
Thermal shrinkage at 120˚C, 5 min, not more
MDGOST 18616 ISO 11501 ASTM D1204 %
4
TD 2
Treatment level, not less ** T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 36 / 36 ***
Optical density, not less BIAXPLEN — 1,8
MD – Machine, longitudinal direction T – Metallized sideTD – Transverse direction UT – Untreated, non metallized film sideGOST – Russian Federation standards.* Typical value** Garanteed shelf life of the activation of the metallized side is 30 days from the date of manufacture indicated on roll label.*** When the order is placed for both side corona treatment. Shelf life of activation for non metallized film side is 6 months.
26
B Aluminum layer with increased thickness (T)
C Treated modified layer for aluminum coating, with increased heat resistance
D Transparent oriented polypropylene core layer
E Heat sealable, non treated skin layer with standard coefficient of friction (UT)
APPLICATION:• High quality rotogravure and flexographic solvent based printing;• hot melt lanination; • for lamination with solvent based or solventless polyurethane adhesives; • manufacture of flexible packaging for the food with long shelf life: cakes, sunflower seeds,
candies, chips and the like;• for vertical VFFS and horizontal HFFS packaging machines;• for cold seal glue frame coating onto UT film side (if necessary).
MAIN PROPERTIES:• Thick coating of aluminium;• increased heat resistance for metallized layer; • long time surface tension shelf life; • high barrier properties to oxygen and water vapor; • increased stiffness;• low threshold for heat sealing, high adhesion of aluminum, good mechanical
properties;• permanent standard coefficient of friction;• contains no migratory antiblock and slip additives; • intended for contact with food;• without coating or primer.
DESCRIPTION:Metallized heatsealable BOPP film with low sealing threshold and standard coefficient of friction, with barrier properties for printing and lamination with glue or hot melt.
Biaxplen HMPLA .M
METALLIZED FILMS
Properties Methods Unit HMPLA .M
Thickness, ± 5%
BIAXPLEN
mkm 18 20 30 35 40
Density * g/cm3 0,91
Weight, ± 5% g/m2 16,38 18,20 27,30 31,85 36,40
Yield, ± 5% m2/kg 61,05 54,95 36,63 31,40 27,47
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa130 140
TD 230 250
Elongation at break, not moreMD
%220 200
TD 80 70
Kinetic coefficient of friction UT / UT GOST 27492 ISO 8295 ASTM D 1894 — 0,3+ 0,10
- 0,10
Thermal shrinkage at 120˚C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %5 4
TD 3 2
Heat sealing strength at 130°C, 1bar, 1 sec, not less UT/UT GOST 27319 ISO 527 ASTM D 882,
ASTM F 88 N/15mm 2,0 2,3
Heat sealing range at 1bar, 1sec .* UT / UTBIAXPLEN
°С 105 - 140
Optical density, not less — 2,5
Treatment level, not less ** T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 36
Water vapour transmission rate at 38°C, 90% rel .humidity, 24h, not more
BIAXPLEN — ASTM F 1249 g/m2/24h 0,1
Oxygen transmission rate at 23°С, 24h, not more BIAXPLEN — ASTM D 3985 cm3/m2/24h 15
MD – Machine, longitudinal direction T – Metallized sideTD – Transverse direction UT – Untreated, non metallized film sideGOST – Russian Federation standards.* Typical value** Garanteed shelf life of the activation of the metallized side is 90 days from the date of manufacture indicated on roll label.
28
NON-FOOD FILMS
Biaхplen PGA
B Glossy, treated, none heat sealable skin layer
C Transparent biaxially oriented polypropylene
D Glossy, non treated (by default), none heat sealable skin layer
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• production of adhesive tapes (skotch) with hot melt and water based adhesives;• solvent based and solvent free lamination with polyurethane adhesives (if necessary).
MAIN PROPERTIES:• Contains antiblocking additives;• very high optical properties: transparency and gloss;• high mechanical properties;• good flatness of the film;• intended for contact with food (if necessary);• low thermo shrinkage to save print sizes in glue drying process;• without coatings and primers.
DESCRIPTION:Transparent BOPP film for general purposes for the production of adhesive tapes.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value ** In case of corona treatment *** In case of flame treatment
Properties Methods Unit PGA
Thickness, ± 5%
BIAXPLEN
mkm 20 23 25 26 28 32 40
Density* g/cm3 0,91
Weight, ± 5% g/m2 18,20 20,93 22,75 23,66 25,48 29,12 36,40
Yield, ± 5% m2/kg 54,95 47,78 43,96 42,27 39,25 34,34 27,47
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa
150 140
TD 250
Elongation at break, not moreMD
%180
TD 70
Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,5
+ 0,1
- 0,1
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %
4
TD 2
Heat sealing strength at 130 °C, 1 bar, 1 sec, not less UT/UT GOST 27319 ISO 527
ASTM D 882,
ASTM F 88N/15 mm Non heat sealable
Haze, not more GOST 15875 ISO 14782 ASTM D 1003 % 2
Gloss at 45 °, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 90
Heat sealing range at 1 bar, 1 sec .* UT/UT BIAXPLEN °C None heat sealable
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578
Dyne/cm, mN/m 38**/44 ***
30
NON-FOOD FILMS
Biaхplen PGD
B Glossy, treated, none heat sealable polypropylene skin layer
C Transparent biaxially oriented polypropylene
D Glossy, none treated, none heat sealable polypropylene skin layer
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• production of decorative packaging for flowers, gift wrap and etc.;• solvent based and solvent free lamination with polyurethane adhesives (if necessary);• in cases in which the exception of heat sealability is required.
MAIN PROPERTIES:• Contains slip-antistatic and antiblocking additives;• very high optical properties: transparency and gloss;• good physical and mechanical properties;• intended for contact with food;• without coatings and primers.
DESCRIPTION:Transparent non heat sealable BOPP film for general purposes and decorative packaging.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit PGD
Thickness, ± 5%
BIAXPLEN
mkm 20 25 30 35 40 48
Density* g/cm3 0,91
Weight, ± 5% g/m2 18,2 22,75 27,30 31,85 36,40 43,68
Yield, ± 5% m2/kg 54,95 43,96 36,63 31,40 27,47 22,89
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa140
TD 250
Elongation at break, not moreMD
%200
TD 70
Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,45+ 0,1
- 0,1
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Heat sealing strength at 130 °C, 1 bar, 1 sec, not less UT/UT GOST 27319 ISO 527 ASTM D 882, ASTM F 88 N/15 mm Non heat sealable
Haze, not more GOST 15875 ISO 14782 ASTM D 1003 % 2
Gloss at 45 °, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 90
Heat sealing range at 1 bar, 1 sec .* UT/UT BIAXPLEN °C Non heat sealable
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
32
NON-FOOD FILMS
Biaхplen PGT
B Corona treated, copolymer skin layer
C Transparent biaxially oriented polypropylene with antistatic
D Glossy, none treated, none heat sealable polypropylene skin layer
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• for textiles packaging, production of decorative and flowers packagings, gift wrapping and
etc.;• for heat sealing by hot wire or knife (sealing and cutting simultaneously);• solvent based and solvent free lamination with polyurethane adhesives (if necessary);• in cases in which the exception of heat sealability and/or stickiness is required at the
increased temperatures.
MAIN PROPERTIES:• Contains efficient antistatic and antiblocking additives;• corona treated film;• very high optical properties: transparency and gloss;• good physical and mechanical properties;• high antistatic properties;• intended for contact with food;• without coatings and primers.
DESCRIPTION:Transparent non heat sealable BOPP film for textile packaging, general purposes and decorative overwrapping with high antistatic properties.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit PGT
Thickness, ± 5%
BIAXPLEN
mkm 20 25 28 30 35 40
Density* g/cm3 0,91
Weight, ± 5% g/m2 18,20 22,75 25,48 27,30 31,85 36,40
Yield, ± 5% m2/kg 54,95 43,96 39,25 36,63 31,40 27,47
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa140
TD 250
Elongation at break, not moreMD
%200
TD 70
Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,4+ 0,1
-0,1
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Heat sealing strength at 130 °C, 1 bar, 1 sec, not less UT/UT GOST 27319 ISO 527 ASTM D 882, ASTM F 88 N/15 mm Non heat sealable
Haze, not more GOST 15875 ISO 14782 ASTM D 1003 % 2
Gloss at 45 °, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 90
Heat sealing range at 1 bar, 1 sec .* UT/UT BIAXPLEN °C Non heat sealable
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
34
NON-FOOD FILMS
Biaхplen PWA
B Glossy, treated, none heat sealable skin layer
C Solid – white opaque oriented polypropylene core layer
D Glossy, non treated (by default), none heat sealable skin layer
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• production of adhesive tapes (sktoch) with hot melt and water based adhesives;• decorative wrapping or other packaging with protection from UV light;• white appearance allows to exclude white inks from printing or/and exclude white
adhesives;• solvent based and solvent free lamination with polyurethane adhesives (if necessary).
MAIN PROPERTIES:• White appearance;• high opacity;• good mechanical properties;• high protection from UV light;• contains antiblocking and mineral filler as titanium dioxide;• does not contain migratory additives;• intended for contact with food (if necessary);• without coatings and primers.
DESCRIPTION:White none heat sealable opaque BOPP film for general purposes and production of adhesive tapes.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value ** In case of corona treatment *** In case of flame treatment
Properties Methods Unit PWA
Thickness, ± 5%
BIAXPLEN
mkm 23 25 28 32
Density* g/cm3 0,96
Weight, ± 5% g/m2 22,08 24,00 26,88 30,72
Yield, ± 5% m2/kg 45,29 41,67 37,20 32,55
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa120 140
TD 240 250
Elongation at break, not moreMD
%200
TD 70
Coefficient of friction, kinetic UT/UT GOST 27492 ISO 8295 ASTM D 1894 —0,5 + 0,1
- 0,1
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Heat sealing strength at 130 °С, 1 bar, 1 sec UT/UT GOST 27319 ISO 527 ASTM F 88; ASTM D882 N/15 mm None heat sealable
Light transmission, not more GOST 15875 ISO 14782 ASTM D 1003 % 45
Gloss at 45 °, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 50
Heat sealing range at 1 bar, 1 sec* UT/UT BIAXPLEN °C None heat sealable
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38 **/42 ***
36
MATT FILMS
Biaхplen MGS
B Matt not treated side
C Transparent oriented polypropylene core layer
D Treated modified heat sealable copolymer skin layer
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for vertical VFFS and horizontal HFFS packaging machines;• for production of decorative packaging for flowers, gift wrap and etc.;• for production of fully wrapped labels for bottles;• to make the flexible packaging or labels matte (paper like) appearance.
MAIN PROPERTIES:• Matte appearance;• contains slip-antistatic and anti-blocking additives;• good ink adhesion;• good mechanical properties;• low coefficient of friction;• intended for contact with food;• without coatings and primers.
DESCRIPTION:One side matt BOPP film for general purposes, for high quality rotogravure and flexographic printing and lamination for flexible packaging and labels.
MD – Machine, longitudinal direction T – Treated glossy side of the film TD – Transverse direction UT – Untreated matt side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit MGS
Thickness, ± 5%
BIAXPLEN
mkm 15 20 35
Density* g/cm3 0,91
Weight, ± 5% g/m2 13,65 18,2 31,85
Yield, ± 5% m2/kg 73,26 54,95 31,40
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa125
TD 240
Elongation at break, not moreMD
%220
TD 80
Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,25+0,15
-0,15
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Heat sealing strength at 130 °C, 1 bar, 1 sec, not less UT/UT GOST 27319 ISO 527 ASTM D 882, ASTM F 88 N/15 mm 2,0 2,3 2,5
Haze, not less GOST 15875 ISO 14782 ASTM D 1003 % 70
Gloss at 45 °, not more T BIAXPLEN ISO 2813 ASTM D 2457 % 12
Heat sealing range at 1 bar, 1 sec .* UT/UT BIAXPLEN °C 130 - 140
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
38
MATT FILMS
Biaхplen MGD
B Matt not treated side
C Transparent oriented polypropylene core layer
D Matt treated side
APPLICATION:• Solvent based flexographic printing;• for production of decorative packaging for flowers, gift wrap and etc.;• heat sealing by string is possible;• to make the flexible packaging or labels matte (paper like) appearance.
MAIN PROPERTIES:• Both side matte appearance;• contains slip-antistatic additives;• good mechanical properties;• standard coefficient of friction;• intended for contact with food;• without coatings and primers.
DESCRIPTION:Both side matt film for general purposes, for flexographic printing, for decorative packaging.
MD – Machine, longitudinal direction T – Treated matt side of the film TD – Transverse direction UT – Untreated matt side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit MGD
Thickness, ± 5%
BIAXPLEN
mkm 20 30 35
Density* g/cm3 0,91
Weight, ± 5% g/m2 18,2 27,3 31,85
Yield, ± 5% m2/kg 54,95 36,63 31,40
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa125
TD 240
Elongation at break, not moreMD
%220
TD 80
Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,35+0,10
-0,15
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Heat sealing strength at 130 °C, 1 bar, 1 sec, not less UT/UT GOST 27319 ISO 527 ASTM D 882, ASTM F 88 N/15 mm 2,3 2,4 2,5
Haze, not less GOST 15875 ISO 14782 ASTM D 1003 % 70
Gloss at 45 °, not more T BIAXPLEN ISO 2813 ASTM D 2457 % 12
Heat sealing range at 1 bar, 1 sec .* UT/UT BIAXPLEN °C 130 - 140
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
40
MATT FILMS
Biaхplen MGPL
B Matt heat sealable, non treated skin layer with low seal intention temperature
C Transparent oriented polypropylene core layer
D Treated modified heat sealable copolymer skin layer
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for vertical VFFS and horizontal HFFS packaging machines;• for vertical packaging machine with tamping of the film;• for production of decorative packaging for flowers, gift wrap and etc.;• for production of fully wrapped labels for bottles;• to make the flexible packaging or labels matte (paper like) appearance.
MAIN PROPERTIES:• Matte appearance;• contains slip-antistatic and antiblocking additives;• wide heat sealing range;• good ink adhesion;• good mechanical properties;• standard coefficient of friction;• intended for contact with food;• without coatings and primers.
DESCRIPTION:One side matt heat sealable BOPP film for general purposes, for high quality rotogravure and flexographic printing and lamination for flexible packaging and labels.
MD – Machine, longitudinal direction T – Treated glossy side of the film TD – Transverse direction UT – Untreated matt side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit MGPL
Thickness, ± 5%
BIAXPLEN
mkm 15 18 20 35
Density* g/cm3 0,91
Weight, ± 5% g/m2 13,65 16,38 18,2 31,85
Yield, ± 5% m2/kg 73,26 61,05 54,95 31,40
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa125
TD 240
Elongation at break, not moreMD
%220
TD 80
Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,35+0,10
-0,15
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Heat sealing strength at 130 °C, 1 bar, 1 sec, not less UT/UT GOST 27319 ISO 527 ASTM D 882, ASTM F 88 N/15 mm 2,0 2,3 2,5
Haze, not less GOST 15875 ISO 14782 ASTM D 1003 % 70
Gloss at 45 °, not more T BIAXPLEN ISO 2813 ASTM D 2457 % 12
Heat sealing range at 1 bar, 1 sec .* UT/UT BIAXPLEN °C 105 - 140
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
42
MATT FILMS
Biaхplen MGR
B Matte not treated release skin layer with low coefficent of friction
C Transparent oriented polypropylene core layer
D Treated smooth modified copolymer skin layer
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• for the production of “flow-pack” flexible packaging with frame cold seal glue;• to make the flexible packaging with matte (paper like) appearance;• for vertical VFFS, and mainly for horizontal high speed HFFS packaging machines.
MAIN PROPERTIES:• Matte UT side has a release properties to the latex cold seal glue;• low coefficient of friction, including hot surfaces, specially for high speed HFFS
machines;• good ink adhesion;• good mechanical properties;• contains antistatic, slip-antiblocking and release additives;• chemically resistant to oils, fats and chemicals;• intended for contact with food;• without coating or primer.
DESCRIPTION:Matte release BOPP film for high quality rotogravure, flexographic printing and lamination; for the production of flexible packaging with frame cold seal glue.
MD – Machine, longitudinal direction T – Treated glossy side of the film TD – Transverse direction UT – Untreated matt side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit MGR
Thickness, ± 5%
BIAXPLEN
mkm 15 18 20
Density* g/cm3 0,91
Weight, ± 5% g/m2 13,65 16,38 18,2
Yield, ± 5% m2/kg 73,26 61,05 54,95
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa125
TD 240
Elongation at break, not moreMD
%220
TD 80
Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,2+ 0,1
-0,1
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Haze, not less GOST 15875 ISO 14782 ASTM D 1003 % 70
Gloss at 45 °, not more T BIAXPLEN ISO 2813 ASTM D 2457 % 12
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
44
OPAQUE FILMS
Biaхplen HOHL
B Treated, heatsealable copolymer skin layer
C Transparent oriented polypropylene tie layer
D White Pearl cavitated core layer of oriented polypropylene
E Transparent oriented polypropylene tie layer
F Heat sealable, non treated skin layer with standard coefficient of friction
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for vertical VFFS and horizontal HFFS packaging machines;• production of flexible packaging with frame cold seal adhesives;• for cold seal glue frame coating onto UT film side (if necessary);• packaging of ice cream, chocolate bars, candy, etc. which requires protection from
UV light.
MAIN PROPERTIES:• A wide temperature range of heat sealing;• high opacity and good whiteness;• good protection from UV light;• low density and high yield;• contains slip-antistatic and antiblocking additives;• contains mineral fillers as calcium carbonate and titanium dioxide;• intended for contact with food;• stable standard coefficient of friction;• without coatings and primers.
DESCRIPTION:Heat sealable White Pearlised BOPP film with low seal intention temperature and standard coefficint of friction for packaging machines. For high quality rotogravure and flexographic printing and lamination.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit НOHL
Thickness, ± 5%
BIAXPLEN
mkm 30 35 40 45
Density* g/cm3 0,72
Weight, ± 5% g/m2 21,60 25,20 28,80 32,40
Yield, ± 5% m2/kg 46,30 39,68 34,72 30,86
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa70
TD 140
Elongation at break, not moreMD
%200
TD 60
Coefficient of friction, kinetic UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,35+ 0,10
- 0,15
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Heat sealing strength at 130 °С, 1 bar, 1 sec UT/UT GOST 27319 ISO 527 ASTM F 88; ASTM D882 N/15 mm 2,5
Light transmission, not more GOST 15875 ISO 14782 ASTM D 1003 % 40 35 30
Gloss at 45 °, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 80
Heat sealing range at 1 bar, 1 sec* UT/UT BIAXPLEN °C 105 - 140
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
46
OPAQUE FILMS
Biaхplen HWHL
B Treated, heatsealable copolymer skin layer
C White opaque oriented polypropylene core layer
D Heat sealable, non treated skin layer with low seal intention temperature and standard coefficient of friction
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for vertical VFFS and horizontal HFFS packaging machines;• production of flexible packaging with frame cold seal adhesives;• for cold seal glue frame coating onto UT film side (if necessary);• packaging of ice cream, chocolate bars, candy, etc. which requires protection from
UV light;• for production of fully wrapped labels for bottles in the original form of the film
or in laminate.
MAIN PROPERTIES:• A wide range of heat sealing;• completely white appearance, high opacity;• very high protection from UV light;• white appearance allows to exclude white paint using from printing process;• contains slip-antistatic, antiblocking and mineral filler as titanium dioxide;• stable standard coefficient of friction;• good physical and mechanical properties;• intended for contact with food;• without coatings and primers.
DESCRIPTION:White heat sealable BOPP film with low seal intention temperature and standard coefficint of friction for packaging machines. For high quality rotogravure and flexographic printing and lamination.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit HWHL
Thickness, ± 5%
BIAXPLEN
mkm 15 20 30 35
Density* g/cm3 0,96
Weight, ± 5% g/m2 14,40 19,20 28,80 33,60
Yield, ± 5% m2/kg 69,44 52,08 34,72 29,76
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa110 120
TD 210 220 230
Elongation at break, not moreMD
%200
TD 70
Coefficient of friction, kinetic UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,25+ 0,10
- 0,10
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Heat sealing strength at 130 °С, 1 bar, 1 sec UT/UT GOST 27319 ISO 527 ASTM F 88; ASTM D882 N/15 mm 2,5
Light transmission, not more GOST 15875 ISO 14782 ASTM D 1003 % 60 50 40 35
Gloss at 45 °, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 45
Heat sealing range at 1 bar, 1 sec* UT/UT BIAXPLEN °C 105 - 140
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
48
OPAQUE FILMS
Biaхplen HOHW
B Treated, heatsealable copolymer skin layer (T)
C Transparent oriented polypropylene tie layer
D White Pearl cavitated core layer of oriented polypropylene
E Transparent oriented polypropylene tie layer
F Non treated skin layer, with standard coefficient of friction and very broad heat sealing range (UT)
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for high speed heat sealing 130–250 packs/min. (depends from packaging thickness and
machine);• low sealing temperature in ice-cream packaging process;• for vertical VFFS and high speed horizontal HFFS packaging machines;• packaging of ice cream, chocolate bars, candy, etc. which requires protection from
UV light;• not for the application of the framework cold glue on UT-side.
MAIN PROPERTIES:• A wide range and high speed of heat sealing;• high opacity and good whiteness;• good protection from UV light;• low density and high yield;• contains slip-antistatic and antiblocking additives;• contains mineral fillers as calcium carbonate and titanium dioxide;• intended for contact with food;• standard coefficient of friction;• without coatings and primers.
DESCRIPTION:White Pearlised BOPP film with very wide heatsealing range and standard coefficient of friction for packaging machines.For high quality rotogravure and flexographic printing and lamination.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit НOHW
Thickness, ± 5%
BIAXPLEN
mkm 30 35 40 45
Density* g/cm3 0,72
Weight, ± 5% g/m2 21,60 25,20 28,80 32,40
Yield, ± 5% m2/kg 46,30 39,68 34,72 30,86
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa70
TD 140
Elongation at break, not moreMD
%200
TD 60
Coefficient of friction, kinetic UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,2+ 0,10
- 0,10
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Heat sealing strength at 130 °С, 1 bar, 1 sec UT/UT GOST 27319 ISO 527 ASTM F 88; ASTM D882 N/15 mm 2,5
Light transmission, not more GOST 15875 ISO 14782 ASTM D 1003 % 40 35 30
Gloss at 45 °, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 50
Heat sealing range at 1 bar, 1 sec* UT/UT BIAXPLEN °C 75 - 140
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
50
OPAQUE FILMS
Biaхplen HOHG
B Corona treated copolymer skin layer (OUT)
C White polypropylene oriented tie layer
D White Pearl cavitated core layer of oriented polypropylene
E Transparent oriented polypropylene tie layer
F Corona treated, glossy, copolymer skin layer with a standard coefficient of friction (IN)
APPLICATION:• High quality solvent based rotogravure and flexographic printing onto OUT side;• solvent based and solvent free lamination with polyurethane adhesives within IN, OUT
sides;• for cold seal glue frame coating onto IN film side SIBUR_cat_films_eng.indd;• for lamination in the center of the triplex (if necessary);• for flexible packaging with frame cold seal adhesives of single and multiple opening;• the production of flexible packaging “flowpack” for food;• production of both side printed labels for full round wrapping bottles;• production of self adhesive labels;• packaging of ice cream, chocolate bars, candy, etc.;• as the heat-sealing film is not always suitable.
MAIN PROPERTIES:• High gloss, whiteness and good opacity;• low density and high yield;• contains antistatic and antiblocking additives;• both side corona treated;• OUT side for the main printing and lamination;• IN side for a minor printing, lamination and cold seal glue coating;• without delamination of the foam layer during repeated opening of the
packaging;• contains white fillers;• intended for contact with food;• standard coefficient of friction;• without coatings and primers.
DESCRIPTION:White Pearlised both side corona treated BOPP film with a standard coefficient of friction for both side printing, lamination and for “flowpack” packaging with cold seal glue coating.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical, background values
Properties Methods Unit НOHG
Thickness, ± 5%
BIAXPLEN
mkm 30 35 40 45
Density* g/cm3 0,73
Weight, ± 5% g/m2 21,90 25,55 29,20 32,85
Yield, ± 5% m2/kg 45,66 39,14 34,25 30,44
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa90
TD 180
Elongation at break, not moreMD
%200
TD 70
Coefficient of friction, kinetic IN/IN GOST 27492 ISO 8295 ASTM D 1894 — 0,35+ 0,10
- 0,15
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Heat sealing strength at 130 °С, 1 bar, 1 sec .*IN/IN
GOST 27319 ISO 527 ASTM F 88; ASTM D882 N/15 mm 2 3
Light transmission, not more GOST 15875 ISO 14782 ASTM D 1003 % 40 35
Gloss at 45 °, not lessIN
BIAXPLEN ISO 2813 ASTM D 2457 %70
OUT 85
Heat sealing range at 1 bar, 1 sec*IN/IN
BIAXPLEN °C115 - 140
OUT/OUT 125 - 140
Treatment level, not less OUT
BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m38
IN 36
IN OUT
52
OPAQUE FILMS
Biaхplen HWHW
B Treated, heatsealable copolymer skin layer
C White opaque oriented polypropylene core layer
D Heat sealable, non treated skin layer with low seal intention temperature and standard coefficient of friction
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• white appearance allows to exclude white paint using from printing process;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• in some cases, instead of using packaging with frame glue cold welding;• for vertical VFFS and horizontal HFFS packaging machines;• for applications requiring temperature decrease or increase the speed of heat sealing;• packaging of ice cream, chocolate bars, candy, etc. which requires protection from
UV light;• not for corona treatment of UT side and not for cold seal coating for UT side.
MAIN PROPERTIES:• A wide range of heat sealing;• completely white appearance, high opacity;• very high protection from UV light;• contains slip-antistatic, antiblocking and mineral filler as titanium dioxide;• sufficiently low coefficient of friction, including the heated surfaces for high-
speed packaging machines;• good physical and mechanical properties;• intended for contact with food;• without coatings and primers.
DESCRIPTION:White heat sealable BOPP film with low seal intention temperature and standard coefficint of friction for packaging machines. For high quality rotogravure and flexographic printing and lamination.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit HWHW
Thickness, ± 5%
BIAXPLEN
mkm 15 20 30 35
Density* g/cm3 0,96
Weight, ± 5% g/m2 14,40 19,20 28,80 33,60
Yield, ± 5% m2/kg 69,44 52,08 34,72 29,76
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa110 120
TD 210 230
Elongation at break, not moreMD
%200
TD 70
Coefficient of friction, kinetic UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,25+ 0,10
- 0,10
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Heat sealing strength at 130 °С, 1 bar, 1 sec UT/UT GOST 27319 ISO 527 ASTM F 88; ASTM D882 N/15 mm 2,5
Light transmission, not more GOST 15875 ISO 14782 ASTM D 1003 % 60 50 40 35
Gloss at 45 °, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 45
Heat sealing range at 1 bar, 1 sec* UT/UT BIAXPLEN °C 75 - 140
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
54
OPAQUE FILMS
Biaхplen HOSL
B Treated, heatsealable copolymer skin layer
C Transparent oriented polypropylene tie layer
D White Pearl cavitated core layer of oriented polypropylene
E Transparent oriented polypropylene tie layer
F Heat sealable, non treated skin layer with standard coefficient of friction
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• in the range of temperatures (~ 150 °C) for hot melt adhesive coatings onto UT film side;• for cold seal glue frame coating onto UT film side (if necessary);• manufacture of flexible packaging for food products;• specially for high speed cubes overwrapping;• for vertical VFFS and horizontal HFFS packaging machines;• packaging of ice cream, chocolate bars, candy, etc. which requires protection from
UV light.
MAIN PROPERTIES:• High opacity and good whiteness;• a wide temperature range of heat sealing;• high antistatic properties;• good protection from UV light;• low density and high yield;• contains slip-antistatic and antiblocking additives;• contains mineral fillers as calcium carbonate and titanium dioxide;• intended for contact with food;• stable standard coefficient of friction;• without coatings and primers.
DESCRIPTION:Heat sealable White Pearlised BOPP film with low seal intention temperature, standard coefficint of friction and high antistatic properties for packaging machines. For high quality rotogravure and flexographic printing and lamination.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit НOSL
Thickness, ± 5%
BIAXPLEN
mkm 30 35 40 45
Density* g/cm3 0,72
Weight, ± 5% g/m2 21,60 25,20 28,80 32,40
Yield, ± 5% m2/kg 46,30 39,68 34,72 30,86
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa70
TD 140
Elongation at break, not moreMD
%200
TD 60
Coefficient of friction, kinetic UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,35+ 0,10
- 0,15
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Heat sealing strength at 130 °С, 1 bar, 1 sec UT/UT GOST 27319 ISO 527 ASTM F 88; ASTM D882 N/15 mm 2,5
Light transmission, not more GOST 15875 ISO 14782 ASTM D 1003 % 40 35 30
Gloss at 45 °, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 50
Heat sealing range at 1 bar, 1 sec* UT/UT BIAXPLEN °C 105 - 140
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
Water vapour transmission rate at 38 °C, 90% rel .humidity, 24 h*
BIAXPLEN — ASTM F 1249 g/m2/24 h 4,3 3,7 3,3 2,9
Oxygen transmission rate at 23 °С, 0% rel .humidi-ty 24 h*
BIAXPLEN — ASTM D 3985 cm3/m2/24 h 1750 1500 1300 1170
56
LABEL FILMS
Biaхplen LGBA
B Treated side of modified copolymer skin layer
C Transparent biaxially oriented polypropylene
D Glossy, none treated, none heat sealable polypropylene skin layer with standard coefficient of friction
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• for production of fully wrapped labels for bottles;• for labeling with cold and hot melt glue;• solvent based and solvent free lamination with polyurethane adhesives (if necessary).
MAIN PROPERTIES:• Improved ink adhesion;• contains antistatic and slip- antiblocking agents;• excellent optical properties: transparency and gloss;• good mechanical properties;• permanent coefficient of friction;• without coating or primer.
DESCRIPTION:Transparent BOPP film for labels and for general applications for bonding by cold and hot melt adhesives when labelling with improved ink adhesion for printing.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit LGBA
Thickness, ± 5%
BIAXPLEN
mkm 30 35 40 48
Density* g/cm3 0,91
Weight, ± 5% g/m2 27,30 31,85 36,40 43,68
Yield, ± 5% m2/kg 36,63 31,40 27,47 22,89
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa140
TD 280
Elongation at break, not moreMD
%200
TD 70
Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,3+ 0,1
- 0,1
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Haze, not more GOST 15875 ISO 14782 ASTM D 1003 % 2
Gloss at 45 °, not less UT BIAXPLEN ISO 2813 ASTM D 2457 % 90
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
58
LABEL FILMS
B Modified copolymer corona treated skin layer
C White opaque oriented polypropylene tie layer
D White Pearl cavitated core layer of oriented polypropylene
E Oriented polypropylene tie layer
F Glossy non heat sealable, non treated skin layer with standard coefficient of friction
APPLICATION:• High quality solvent rotogravure and flexographic direct printing;• for production of fully wrapped labels for bottles;• for labeling with cold and hot melt glue.
MAIN PROPERTIES:• High adhesion of solvent based inks: flexo and rotogravure for direct printing;• both side glossy film;• good opacity and whiteness;• contains slip, antistatic and antiblock additives;• contains mineral fillers such as calcium carbonate and titanium dioxide;• low coefficient of friction, stable in time; • without coating or primer.
DESCRIPTION:White Pearl microporous BOPP film for fully wrapped labeling of bottles for cold and hot melt glue application while labeling with good gloss and ink adhesion
Biaxplen LOBA
Properties Methods Unit LOBA
Thickness, ± 5%
BIAXPLEN
mkm 35 38 47
Density * g/cm3 0,68
Weight, ± 5% g/m2 23,80 25,84 31,96
Yield, ± 5% m2/kg 42,02 38,70 31,29
Tensile strength, not lessMD
N/mm2, MPa80
TD GOST 14236 ISO 527 ASTM D882 150
Elongation at break, not moreMD
GOST 27492 ISO 8295 ASTM D 1894
%200
TD 70
Coefficient of friction, kinetic UT / UT — 0,3+0,10
- 0,10
Thermal shrinkage at 120˚C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Light transmission, not more GOST 15875 ISO 14782 ASTM D 1003 % 30 25 20
Gloss at 45°, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 85
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
MD – Machine, longitudinal direction T – Treated side of the filmTD – Transverse direction UT – Untreated side of the filmGOST – Russian Federation standards.* Typical value
60
LABEL FILMS
Biaхplen LOBB
B Modified copolymer corona treated glossy skin layer
C Oriented polypropylene tie layer
D White Pearl cavitated core layer of oriented polypropylene
E Oriented polypropylene tie layer
F Glossy non heat sealable, non corona treated skin layer with standard coefficient of friction
APPLICATION:• High quality solvent rotogravure and flexographic printing;• for production of fully wrapped labels for bottles;• for labeling with cold and hot melt glue.
MAIN PROPERTIES:• Both side excellent gloss;• high adhesion of solvent based inks: flexo and rotogravure for direct printing;• excellent opacity and whiteness;• with increased yield;• contains slip, antistatic and antiblock additives;• contains mineral fillers such as calcium carbonate and titanium dioxide;• low coefficient of friction, stable in time;• without coating or primer.
DESCRIPTION:White Pearlised microporous glossy BOPP film for fully wrapped labeling of bottles for cold and hot melt glue application while labeling with excellent gloss and high ink adhesion.
MD – Machine direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit LOBB
Thickness, ± 5%
BIAXPLEN
mkm 38 47
Density* g/cm3 0,65
Weight, ± 5% g/m2 24,70 30,55
Yield, ± 5% m2/kg 40,49 32,73
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa75
TD 145
Elongation at break, not moreMD
%190
TD 65
Coefficient of friction, kinetic UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,3+0,10
-0,15
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Light transmission, not more GOST 15875 ISO 14782 ASTM D 1003 % 25
Gloss at 45 °, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 85
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
62
LABEL FILMS
Biaхplen LOBC
B Modified copolymer corona treated skin layer
C White opaque oriented polypropylene tie layer
D White Pearl cavitated core layer of oriented polypropylene
E Oriented polypropylene tie layer
F Glossy non heat sealable, non corona treated skin layer with standard coefficient of friction
APPLICATION:• High quality solvent based rotogravure and flexographic printing;• for production of fully wrapped labels for bottles;• for labeling with cold and hot melt glue.
MAIN PROPERTIES:• Very low density and very high yield;• high adhesion of solvent based inks: flexo and rotogravure for printing;• both side glossy film;• good opacity and whiteness;• contains mineral fillers such as calcium carbonate and titanium dioxide;• contains slip, antistatic and antiblock additives;• low coefficient of friction, stable in time;• without coating or primer.
DESCRIPTION:White Pearlised microporous BOPP film for fully wrapped labeling of bottles for cold and hot melt glue application while labeling with very high yield good gloss and good ink adhesion.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit LOBC
Thickness, ± 5%
BIAXPLEN
mkm 38 47
Density* g/cm3 0,60
Weight, ± 5% g/m2 22,80 28,20
Yield, ± 5% m2/kg 43,86 35,46
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa70
TD 140
Elongation at break, not moreMD
%180
TD 60
Coefficient of friction, kinetic UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,3+0,10
-0,15
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Light transmission, not more GOST 15875 ISO 14782 ASTM D 1003 % 35
Gloss at 45 °, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 65
Treatment level, not less Т BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
64
LABEL FILMS
Biaхplen LOHM .M
B High glossy aluminum layer
C Modified layer for aluminum adhesion
D Oriented polypropylene tie layer
E White Pearl cavitated core layer of orinted polypropylene
F Oriented polypropylene tie layer
G Glossy non heat sealable, non treated skin layer with standard coefficient of friction
APPLICATION:• High quality solvent based rotogravure and flexographic direct printing;• for production of fully wrapped labels for bottles;• for labeling with cold and hot melt glue.
MAIN PROPERTIES:• Very smoth surface and high gloss metallized side;• excellent adhesion of the aluminum layer;• lower density, high opacity and good whiteness;• permanent coefficient of friction and good mechanical properties;• contains an organic dye pearl and non-migratory slip additives;• intended for contact with food;• without coating and primer.
DESCRIPTION:White Pearlised metallized microporous BOPP film for labeling of bottles, for cold and hot melt glue application while labeling.
MD – Machine, longitudinal direction T – Metallized side TD – Transverse direction UT – White pearl, non treated side GOST – Russian Federation standards * Typical value ** Garanteed shelf life of the activation of the metallized side is 15 days from the date of manufacture indicated on roll label
Properties Methods Unit LOHM .М
Thickness, ± 5%
BIAXPLEN
mkm 35 38
Density* g/cm3 0,71
Weight, ± 5% g/m2 24,85 26,98
Yield, ± 5% m2/kg 40,24 37,06
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa90
TD 180
Elongation at break, not moreMD
%200
TD 70
Coefficient of friction, kinetic UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,3+0,15
-0,15
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Optical density, not less BIAXPLEN О .D . 1,8
Treatment level, not less** Т BIAXPLEN ISO 8296 ASTM D2578 Dyne/cm, mN/m 36
66
LABEL FILMS
Biaхplen LOMB
B Matt white corona treated skin layer
C White opaque oriented polypropylene tie layer
D White Pearl cavitated core layer of oriented polypropylene
E Oriented polypropylene tie layer
F Glossy non heat sealable, non treated skin layer with standard coefficient of friction
APPLICATION:• High quality solvent based printing;• for production of fully wrapped labels of bottles;• for labeling with cold and hot melt glue.
MAIN PROPERTIES:• Matt white, paper appearance;• high adhesion printing;• good opacity and whiteness;• contains slip, antistatic and antiblock additives;• contains mineral fillers such as calcium carbonate and titanium dioxide;• low coefficient of friction, stable in time;• without coating or primer.
DESCRIPTION:Matt White Pearlised microporous BOPP film for fully wrapped labeling of bottles.
MD – Machine, longitudinal direction T – Treated side of the film TD – Transverse direction UT – Untreated side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit LOMB
Thickness, ± 5%
BIAXPLEN
mkm 35 38 47
Density* g/cm3 0,68
Weight, ± 5% g/m2 23,80 25,84 31,96
Yield, ± 5% m2/kg 42,02 38,70 31,29
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa80
TD 150
Elongation at break, not moreMD
%200
TD 70
Coefficient of friction, kinetic UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,3+0,10
-0,15
Thermal shrinkage at 120 °C, 5 min, not moreMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Light transmission, not more GOST 15875 ISO 14782 ASTM D 1003 % 35
Gloss at 45 °, not more T BIAXPLEN ISO 2813 ASTM D 2457 % 13
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
68
TOBACCO FILMS
Biaхplen TSHL
B Non treated skin layer (OUT) with a low coefficient of friction and low heat sealingt threshold
C Transparent oriented modified polypropylene
D Non treated skin layer (IN) with a bit higher coefficient of friction and low heat sealing threshold
APPLICATION:• Overwrapping of the “rigid” cardboard packs on the horizontal high speed machines;• for tight carton packs overwrapping due to shrinkability of the film;• wrapping cardboard packs of tea, zephyr, cigarette cardboard blocks, etc.;• mainly for machines with heat tunnel;• also for machines without a heat tunnel in which the shrinkage of the film occurs due
to heating of the weld;• for tight overwrapping of small and medium-sized carton packs.
MAIN PROPERTIES:• Contains antistatic and slip-antilock additives;• non symmetric coefficient of friction of the film for packs tight overwrapping;• stable low coefficient of friction, including the heated surfaces;• medium shrinkage film;• excellent optical properties;• good physical and mechanical properties and increased stiffness;• intended for contact with food;• without coating.
DESCRIPTION:Thermo shrinkable transparent BOPP film for general purposes with a wide heat sealing range and low coefficient of friction for “rigid” carton pack overwrapping on high speed machines.
MD – Machine, longitudinal direction of the film IN – Internal film side of the reel TD – Transverse direction of the film OUT- external film side of the reel GOST – Russian Federation standards * Typical value
Properties Methods Unit TSHL
Thickness, ± 5%
BIAXPLEN
mkm 16 18 20
Density* g/cm3 0,91
Weight, ± 5% g/m2 14,56 16,38 18,2
Yield, ± 5% m2/kg 68,68 61,05 54,95
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, Mpa150
TD 260
Elongation at break, not moreMD
%180
TD 65
Kinetic coefficient of frictionIN/IN
GOST 27492 ISO 8295 ASTM D 1894 — 0,30 + 0,05
OUT/OUT 0,25 -0,10
Thermal shrinkage at 120 °C, 5 minMD
GOST 18616 ISO 11501 ASTM D1204 %6,5 - 9,0
TD 6,5 - 9,0
Heat Seal strength at 1 bar, 1 sec, 130 °C, not less IN/OUT GOST 27319 ISO 527 ASTM D 882, ASTM F 88 N/15 mm 2,5
Haze, no more GOST 15875 ISO 14782 ASTM D 1003 % 2,5
Gloss at 45 °, not less OUT BIAXPLEN ISO 2813 ASTM D 2457 % 85
Heat sealing range at 1 bar, 1 sec .* OUT/OUT BIAXPLEN °C 105 - 140
70
TOBACCO FILMS
Biaхplen TGHL
B Non treated skin layer (OUT) with a low coefficient of friction and a low heat sealingt threshold
C Transparent biaxially oriented polypropylene
D Non treated skin layer (IN) with a bit higher coefficient of friction and a low heat sealing threshold
APPLICATION:• For overwrapping of the “soft” and “rigid” cardboard packs and boxes on the horizontal
high speed machines;• for overwrapping cardboard packs with tea, zephyr, candies, cigarette cardboard blocks,
etc.• basically for the machines without heat tunnel.
MAIN PROPERTIES:• Contains antistatic and slip-antilock additives;• non symmetric coefficient of friction of the film for packs tight overwrapping;• contains antistatic and slip-antilock additives;• stable low coefficient of friction, including the heated surfaces;• small shrinkable film;• excellent optical properties;• good physical and mechanical properties;• intended for contact with food;• without coating.
DESCRIPTION:Tobacco transparent non heat shrinkable BOPP film for general purposes with a wide heat sealing range and low coefficient of friction for “soft” and “rigid” carton pack overwrapping.
MD – Machine, longitudinal direction of the film IN – Internal film side of the reel TD – Transverse direction of the film OUT- external film side of the reel * Typical value
Properties Methods Unit TGHL
Thickness, ± 5%
BIAXPLEN
mkm 16 18 20 25 30
Density* g/cm3 0,91
Weight, ± 5% g/m2 14,56 16,38 18,2 22,75 27,3
Yield, ± 5% m2/kg 68,68 61,05 54,95 43,96 36,63
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa130 140
TD 230 250
Elongation at break, not moreMD
%220 200
TD 80 80
Kinetic coefficient of frictionIN/IN
GOST 27492 ISO 8295 ASTM D 1894 — 0,3 +0,05
OUT/OUT 0,2 -0,05
Thermal shrinkage at 120 °C, 5 minMD
GOST 18616 ISO 11501 ASTM D1204 %4
TD 2
Heat Seal strength at 1 bar, 1 sec, 130 °C, not less IN/OUT GOST 27319 ISO 527 ASTM D 882, ASTM F 88 N/15 mm 2,5
Haze, no more GOST 15875 ISO 14782 ASTM D 1003 % 2,5
Gloss at 45 °, not less OUT BIAXPLEN ISO 2813 ASTM D 2457 % 85
Heat sealing range at 1 bar, 1 sec .* OUT/OUT BIAXPLEN °C 105 - 140
72
TOBACCO FILMS
Biaхplen TSHD
B Non treated skin layer (OUT) with very low coefficient of friction and low heat sealingt threshold
C Transparent oriented modified polypropylene
D Non treated skin layer (IN) with a bit higher coefficient of friction and low heat sealing threshold
APPLICATION:• For carton cigarette packs overwrapping, including on ultra high speed machines with
speed up to 1000 p/min;• overwrapping of the “rigid” cardboard packs on the horizontal high speed machines;• for tight carton packs overwrapping due to shrinkability of the film;• wrapping cardboard packs of tea, zephyr, cigarette cardboard blocks, etc.;• mainly for machines with heat tunnel;• also for machines without a heat tunnel in which the shrinkage of the film occurs due
to heating of the weld;• for tight overwrapping of small and medium-sized carton packs.
MAIN PROPERTIES:• Scratch and abrasion resistant;• contains antistatic and slip-antilock additives;• non symmetric coefficient of friction of the film for packs tight overwrapping;• stable low coefficient of friction, including the heated surfaces;• medium shrinkage film;• excellent optical properties;• good physical and mechanical properties and high stiffness;• intended for contact with food;• without coating.
DESCRIPTION:Transparent heat shrinkable BOPP film with a wide heat sealing range and low coefficient of friction specially designed for cigarette and tea carton packs overwrapping in high speed machines.
MD – Machine, longitudinal direction of the film IN – Internal film side of the reel TD – Transverse direction of the film OUT- external film side of the reel GOST – Russian Federation standards * Typical value
Properties Methods Unit TSHD
Thickness, ± 5%
BIAXPLEN
mkm 16 18 20 25
Density* g/cm3 0,91
Weight, ± 5% g/m2 14,56 16,38 18,2 22,75
Yield, ± 5% m2/kg 68,68 61,05 54,95 43,96
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, MPa140
TD 260
Elongation at break, not moreMD
%180
TD 70
Flexural modulus*MD
N/mm2, MPa2700
TD 4500
Kinetic coefficient of frictionIN/IN
GOST 27492 ISO 8295 ASTM D 1894 — 0,20
± 0,05OUT/OUT 0,15
Thermal shrinkage at 120 °C, 5 min*MD
GOST 18616 ISO 11501 ASTM D1204 %
8,5± 1,0
TD 6,5
Thermal shrinkage at 130 °C, 15 min*MD 13
± 2,0TD 13
Heat Seal strength at 1 bar, 1 sec, 130 °C, not less IN/OUT GOST 27319 ISO 527 ASTM D 882, ASTM F 88 N/15 mm 2,5
Haze, no more GOST 15875 ISO 14782 ASTM D 1003 % 2,5
Gloss at 45 °, not less OUT BIAXPLEN ISO 2813 ASTM D 2457 % 85
Heat sealing range at 1 bar, 1 sec .* OUT/OUT BIAXPLEN °C 105 - 140
74
TOBACCO FILMS
Biaхplen TSHT
B Non treated skin layer with very low coefficient of friction and low heat sealing threshold (UT)
C Transparent oriented modified polypropylene
D Corona treated skin layer with a higher coefficient of friction and low heat sealing threshold (T)
APPLICATION:• For carton cigarette packs overwrapping, including on ultra high speed machines with
speed up to 1000 p/min;• for solvent based flexographic and rotogravure printing with special inks;• overwrapping of the “rigid” cardboard packs on the horizontal high speed machines;• for tight carton packs overwrapping due to shrinkability of the film;• wrapping cardboard packs of tea, zephyr, cigarette cardboard blocks, etc.;• mainly for machines with heat tunnel;• also for machines without a heat tunnel in which the shrinkage of the film occurs due
to heating of the weld;• for tight overwrapping of small and medium-sized carton packs.
MAIN PROPERTIES:• Scratch and abrasion resistant;• treated for printing;• contains antistatic and slip-antilock additives;• non symmetric coefficient of friction of the film for packs tight overwrapping;• stable low coefficient of friction, including the heated surfaces;• medium shrinkage film;• excellent optical properties;• good physical and mechanical properties and high stiffness;• intended for contact with food;• without coating or primer;• when the shipment is for the printing, activation is OUT (specify in order);• when the shipment is for the packaging wrapping, activation is IN (specify
in order).
DESCRIPTION:Heat shrinkable transparent corona treated BOPP film with a wide heat sealing range and low coefficient of friction designed for printing for cigarette and other carton packs overwrapping in high speed machines.
MD – Machine, longitudinal direction of the film T – Treated side of the film TD – Transverse direction of the film UT – Untreated side of the film GOST – Russian Federation standards * Typical value
Properties Methods Unit TSHT
Thickness, ± 5%
BIAXPLEN
mkm 16 18 20 25
Density* g/cm3 0,91
Weight, ± 5% g/m2 14,56 16,38 18,2 22,75
Yield, ± 5% m2/kg 68,68 61,05 54,95 43,96
Tensile strength, not lessMD
GOST 14236 ISO 527 ASTM D882
N/mm2, Mpa150
TD 260
Elongation at break, not moreMD
%180
TD 70
Flexural modulus*MD
N/mm2, MPa2700
TD 4500
Kinetic coefficient of frictionT/T
GOST 27492 ISO 8295 ASTM D 1894 — 0,25
± 0,05UT/UT 0,15
Thermal shrinkage at 120 °C, 5 min*MD
GOST 18616 ISO 11501 ASTM D1204 %
8,5± 1,0
TD 6,5
Thermal shrinkage at 130 °C, 15 min*MD 12
± 2,0TD 12
Heat Seal strength at 1 bar, 1 sec, 130 °C, not less T/UT GOST 27319 ISO 527 ASTM D 882, ASTM F 88 N/15 mm 2,5
Haze, no more GOST 15875 ISO 14782 ASTM D 1003 % 2,5
Gloss at 45 °, not less UT BIAXPLEN ISO 2813 ASTM D 2457 % 85
Heat sealing range at 1 bar, 1 sec .* UT/UT BIAXPLEN °C 105 - 140
Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38
BIAXPLEN LTD16/1 Krzhizhanovskogo st., Moscow Russia 117997 +7 (495) 777 55 00
CHIEF OF MARKETING DEPARTMENTMatveev Dmitry +7 (495) 777 55 00 ext. 25-08 matveevdy@sibur.ru
EXPERTVinogradova Maria +7 (495) 777 55 00 ext. 26-31 vinogradovamv@ sibur.ru
CUSTOMER SERVICESmirnova Nadezhda +7 (495) 777 55 00 ext. 26-09 ClientService@biaxplen.sibur.ru
CUSTOMER TECHNICAL SUPPORTMaksim Fedorov +7 (495) 527 97 84, ext. 12-40 +7 (916) 033 28 81 FedorovMB@biaxplen.sibur.ru
SALESTatyana Mironenko +43 1 370 8000 ext. 819 +43 664 887 392 98 MironenkoTV@sibur-int.com
CHIEF OF MULTINATIONAL SALES Natalya Malkova +7 (495) 733 93 18 ext. 26-04 +7 (916) 531 27 32 malkovanv@sibur.ru
www.sibur.ru/biaxplen
top related