![Page 1: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/1.jpg)
CERAMICS
Chapter 3
1
![Page 2: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/2.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
Structures & Properties of Ceramics
2
• How do the crystal structures of ceramic materials differ from those for metals?
• How do point defects in ceramics differ from those defects found in metals?
• How are the mechanical properties of ceramics measured, and how do they differ from those for metals?
• In what ways are ceramic phase diagrams different from phase diagrams for metals?
The Porsche Carrera GT's carbon-ceramic (silicon carbide) disc brake
![Page 3: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/3.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering 3
Mid‐16th century ceramic tilework on the Dome of the Rock, Jerusalem
A ceramic is an inorganic, nonmetallic solid materialcomprising metal, nonmetal or metalloid atomsprimarily held in ionic and covalent bonds.
The word "ceramic comes from the Greek wordκεραμικός (keramikos), "of pottery" or "for pottery“.
The crystallinity of ceramic materials ranges fromhighly oriented to semi‐crystalline, and oftencompletely amorphous (e.g., glasses).
Varying crystallinity and electron consumption in theionic and covalent bonds cause most ceramicmaterials to be good thermal and electrical insulatorsand extensively researched in ceramic engineering.
Generalities such as high melting temperature, highhardness, poor conductivity, high moduli of elasticity,chemical resistance and low ductility are the norm,with known exceptions to each of these rules (e.g.piezoelectric ceramics, glass transition temperature,superconductive ceramics, etc.).
Many composites, such as fiberglass and carbon fiber,while containing ceramic materials, are notconsidered to be part of the ceramic family.
![Page 4: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/4.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
Spectrum of Ceramics Uses
4
![Page 5: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/5.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
Most frequently silicates, oxides, nitrides and carbides Typically insulative to the passage of electricity andheat
More resistant to high temperatures and harshenvironments than metals and polymers.
Hard but very brittle.
5
![Page 6: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/6.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
General Comparison of Materials
6
Property Ceramic Metal PolymerHardness Very High Low Very LowElastic modulus Very High High Low
Thermal expansion High Low Very Low
Ductility Low High High
Corrosion resistance High Low Low
Wear resistance High Low Low
Electrical conductivity Depends on material High Low
Density Low High Very Low
Thermal conductivity Depends on material High Low
Magnetic Depends on material High Very Low
![Page 7: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/7.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering 7
CeramTec Medical Engineering (2013)CeramTec – The Ceramic Experts
Ceramic Engineering 1
![Page 8: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/8.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering 8
Ceramic Engineering 2
![Page 9: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/9.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
Structure of Ceramics
9
• Bonding:-- Can be ionic and/or covalent in character.-- % ionic character increases with difference in
electronegativity of atoms.
Adapted from Fig. 2.7, Callister & Rethwisch 8e. (Fig. 2.7 is adapted from Linus Pauling, The Nature of the Chemical Bond, 3rd edition, Copyright 1939 and 1940, 3rd edition. Copyright 1960 byCornell University.)
• Degree of ionic character may be large or small:
SiC: small
CaF2: large
![Page 10: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/10.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
Periodic table with ceramics compounds indicated by acombination of one or more metallic elements (in lightcolor) with one or more nonmetallic elements (in darkcolor).
10
![Page 11: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/11.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering 11
![Page 12: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/12.jpg)
Example of Crystal Structure
Fluorite structure(AX2)(CaF2)
Barium titanate structure(ABX3)(BaTiO3)
Spinel structure(AB2X4)(MgAl2O4)
12http://www.eng.uwo.ca/es021/ES021b_2007/Lecture%20Notes/Chap%2012-13%20SN%20-%20Ceramics.pdf
Rock salt structure NaCl
![Page 13: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/13.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
VMSE: Ceramic Crystal Structures
13
http://www.wiley.com/college/callister/0470125373/vmse/xtalp.htm
![Page 14: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/14.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
Silicate CeramicsMost common elements on earth are Si & O2
SiO2 (silica) polymorphic forms are quartz, crystobalite, &tridymite
The strong Si‐O bonds lead to a high melting temperature(1710ºC) for this material
14
Si4+
O2-
Adapted from Figs. 12.9-10, Callister & Rethwisch 8e crystobalite
![Page 15: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/15.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
SilicatesBonding of adjacent SiO4
4‐ accomplished by the sharing ofcommon corners, edges, or faces
15
Mg2SiO4 Ca2MgSi2O7
Adapted from Fig. 12.12, Callister & Rethwisch 8e.
Presence of cations such as Ca2+, Mg2+, & Al3+
1. maintain charge neutrality, and2. ionically bond SiO4
4- to one another
VARIOUS COMBINATIONS
For example, Forsterite (Mg2SiO4)
![Page 16: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/16.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering 16
One of the most common clay minerals, kaolinite, has a relatively simple twolayersilicate sheet structure. Kaolinite clay has the formula Al2(Si2O5)(OH)4 inwhich the silica tetrahedral layer, represented by (Si2O5)-2.
The structure of kaoliniteclay. (Adapted from W. E. Hauth,“Crystal Chemistry of Ceramics,”American Ceramic Society Bulletin,Vol. 30, No. 4, 1951, p. 140.)
![Page 17: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/17.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
Glass Structure
17
• Quartz is crystallineSiO2:
• Basic Unit: Glass is noncrystalline (amorphous)• Fused silica is SiO2 to which no
impurities have been added• Other common glasses contain
impurity ions such as Na+, Ca2+, Al3+, and B3+
(soda glass)Adapted from Fig. 12.11, Callister & Rethwisch 8e.
Si04 tetrahedron4-
Si4+
O2-
Si4+Na+
O2-
![Page 18: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/18.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
Ceramic Phase DiagramsMgO‐Al2O3diagram (Spinel):
18
Adapted from Fig. 12.25, Callister & Rethwisch 8e.
Two eutectics are found, one on either side of the spinel phase field, and stoichiometric spinel melts congruently at about 2100o.
Spinel
These diagrams are especially useful in assessing the high temperatureperformance of ceramic materials.
![Page 19: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/19.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
STRESS–STRAIN BEHAVIOR
19
Adapted from Figs. Callister & Rethwisch 8e
![Page 20: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/20.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering 20
Single-walled carbon nanotube: 1,000 GPaDiamond:1,050 – 1210 GPaCarbyne: 32,100 GPa
![Page 21: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/21.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering 21
Adapted from Figs. Callister & Rethwisch 8e
![Page 22: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/22.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
Applications and Processing of Ceramics It is important for the engineer to realize how theapplications and processing of ceramic materials areinfluenced by their mechanical and thermalproperties, such as hardness, brittleness, and highmelting temperatures.
ceramic pieces normally cannot be fabricated usingconventional metal forming techniques.
22
![Page 23: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/23.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
Classification of ceramics
23
![Page 24: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/24.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering 24
![Page 25: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/25.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
High‐performance ceramics drive the world of theautomobile
25
https://www.ceramtec.com/news/archive/year/2007/id/41/
![Page 26: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/26.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
Ceramics Applications: Cutting Tools
26
• Tools:-- for grinding glass, tungsten,
carbide, ceramics-- for cutting Si wafers-- for oil drilling
bladesoil drill bits
Single crystal diamonds
polycrystallinediamonds in a resinmatrix.
Photos courtesy Martin Deakins,GE Superabrasives, Worthington,OH. Used with permission.
• Materials:-- manufactured single crystal
or polycrystalline diamondsin a metal or resin matrix.
-- polycrystalline diamondsresharpen by microfracturingalong cleavage planes.
![Page 27: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/27.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
The glasses are a familiar group of ceramics;containers, lenses, and fiberglass represent typicalapplications.
They are noncrystalline silicates containing otheroxides, notably CaO, Na2O, K2O, and Al2O3, whichinfluence the glass properties. A typical soda–limeglass consists of approximately 70 wt% SiO2, thebalance being mainly Na2O (soda) and CaO (lime).
27
Ceramics Applications: GLASSES
![Page 28: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/28.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering 28
![Page 29: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/29.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
One of the most widely used ceramic raw materials is clay.This inexpensive ingredient, found naturally in greatabundance, often is used as mined without any upgradingof quality.
Most of the clay‐based products fall within two broadclassifications: the structural clay products and thewhitewares.
Structural clay products include building bricks, tiles, andsewer pipes—applications in which structural integrity isimportant. The whiteware ceramics become white after thehigh‐temperature firing. Included in this group areporcelain, pottery, tableware, and plumbing fixtures(sanitary ware).
29
Ceramics Applications: CLAY PRODUCTS
![Page 30: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/30.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
Refractories
30
• Materials to be used at high temperatures (e.g., in high temperature furnaces).
• Consider the Silica (SiO2) - Alumina (Al2O3) system.• Silica refractories - silica rich - small additions of alumina
depress melting temperature (phase diagram):
Fig. 12.27, Callister & Rethwisch 8e. (Fig. 12.27 adapted from F.J. Klug and R.H. Doremus, J. Am. Cer. Soc. 70(10), p. 758, 1987.)
Composition (wt% alumina)
T(ºC)
1400
1600
1800
2000
2200
20 40 60 80 1000
alumina+
mullite
mullite + L
mulliteLiquid
(L)
mullite+ crystobalite
crystobalite + L
alumina + L
3Al2O3-2SiO2
![Page 31: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/31.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering 31
Ceramic as Refractories
https://www.youtube.com/watch?v=JcFixNVnjgs&index=2&list=PL1AE198B26227EC62
![Page 32: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/32.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
Advanced Ceramics: Materials for Engines Advantages:
Operate at high temperatures – high efficiencies Low frictional losses Operate without a cooling system Lower weights than current engines
32
• Disadvantages: – Ceramic materials are
brittle– Difficult to remove internal
voids (that weaken structures)
– Ceramic parts are difficult to form and machine
• Potential candidate materials: Si3N4, SiC, & ZrO2
• Possible engine parts: engine block & piston coatings
![Page 33: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/33.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering 33
CERAMIC JET‐ENGINE PARTS TAKING OVER THE AVIATION INDUSTRY
Source: https://jsetceramics.wordpress.com/
![Page 34: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/34.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering 34
Source: https://jsetceramics.wordpress.com/
![Page 35: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/35.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering 35
Advanced Ceramics: Microelectromechanical Systems (MEMS
Microelectromechanical systems (abbreviated MEMS) areminiature “smart” systems consisting of a multitude ofmechanical devices that are integrated with large numbers ofelectrical elements on a substrate of silicon.
The mechanical components are microsensors and microactuators.
One example of a practical MEMSapplication is an accelerometer (accelerator/decelerator sensor) that is used in thedeployment of air‐bag systems inautomobile crashes.
![Page 36: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/36.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering 36
![Page 37: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/37.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering
Manufacturing process of ceramic products
37
![Page 38: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/38.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering 38
![Page 39: Advanced Materials 20151 Ch3.ppt - site.iugaza.edu.pssite.iugaza.edu.ps/aabuzarifa/files/Advanced-Materials-20151_Ch3.pdf · Rethwisch 8e crystobalite. Dr. Anwar Abu-Zarifa . Islamic](https://reader030.vdocuments.mx/reader030/viewer/2022021717/5b4f9d0e7f8b9a256e8cab85/html5/thumbnails/39.jpg)
Dr. Anwar Abu-Zarifa . Islamic University Gaza . Department of Industrial Engineering 39
Manufacturing of ceramics