1.1 TEXTILES:The word textile encompasses anything that is associated with fibres, whether they be of animal, vegetable or mineral origin, manufactured or natural. Fibres can be spun together to form continuous filaments which can then be knotted, woven or felted. When fibres are spun and then woven, the result may be, or can be, a length of fabric (natural or synthetic). Fabrics can be further enhanced by controlled weaving to create textured patterns within the woven form, colouring of different spun fibres to create distinct pattern groupings and finally by adornment through such techniques as creative stitchery, appliqué or beading. Textiles are historically an integral part of many cultures. People have knotted woven, intertwined, felted, knitted, sewn for many reasons. To create functional objects was always the primary aim, but personal adornment and embellishment have grown into cultural traits over the years. People have knotted and intertwined continuous filaments to create everyday usable objects such as carry-bags. They have used the knotting technique to increase the strength of fibres so that their function and life span may be extended and, of course, people have woven fibres into continuous lengths of cloth for personal clothing and soft furnishing. The urge to adorn and beautify has led people to embellish these functional objects. Such embellishment has been handed down through generations so that today we can see and identify pattern and colour combinations in one culture uniquely different from those in another. Today, work with fibres encompasses not only functional forms but also non-functional sculptural and/or pictorial forms. When we look at the extensive range of textile products and techniques used to obtain these products it may all seem quite daunting and you may wonder where to start. However, by grouping according to technique it all begins to become a lot clearer. 1. Fibre to Fibre - spinning, weaving, tapestry, crochet, macramé, knitting, felting. 2. Colour to Fabric - tie dye, batik, gutta, dispersal dye, serigraphic printing (silkscreen) relief printing - lino, card, string, hand painting.3. Fabric to Fabric - patchwork, appliqué, quilting.4. Fibre to Fabric - creative stitchery.Each technique can be used by itself to create an end product, or they can be combined to create further exciting products.

1.2 Dyes & Fibre Polymer System

1.2.1 Wool Fibres:The wool fibre is composed of the protein keratin, which consists of long polypeptide chains built from eighteen different amino acids. Most of these acids have the general formula H2N.CHR.COOH, in which R is a side chain of varying character. The chain structure is of the type:

And at intervals bridges derived from the amino acid cystine connect the chains.

1

Some of the side chains end in amino groups and others in carboxyl groups; internal salts are therefore formed and the

Molecules are bound together by electrovalent linkages. The molecules of keratin are very large, with and average molecular weight estimated at about 60,000. The wool fibre is readily destroyed by alkali, but withstands acid conditions fairly well; some hydrolysis of peplide linkages occurs on prolonged boiling with acids, however. The carboxylic acid and amino groups in the keratin molecule confer affinity for basic and acid dyes. Basic dyes are now little used on wool since their fugitive properties render them unsuitable for such and expensive and durable fibre. Acid dyes, however, are extensively used, and the general characteristics of this large class and the related mordant and pre-metallised azo dyes are now described.

Since the bonds between dye anions and amino groups in the wool fibre are easily broken and re-formed, dyes attached in this way are liable to migrate. This property is advantageous, in that level dyeing is readily attained, but it leads to low fastness to wet treatments, and any undyed wool present during washing becomes stained. These characteristics are chiefly apparent in dyes of low molecular weight, and fastness to washing is in general much better in more complex dyes. The larger dye molecules are evidently attached the fibre by some means other than the ionic bonds mentioned above, and it is believed that6 they are held by non-polar Van-der Waals forces exerted between hydrophobic dye anions and hydrophobic regions of the wool fibre, their strength being proportional to the area of contact. From an application point of view acid dyes are classed as either Levelling or Milling types. The Levelling (sometimes called Equalizing) dyes have fairly simple chemical structures, migrate readily on wool, and are easily applied from strongly acid baths; their wet-fastness properties are low. The Milling dyes are structurally more complex, have high affinity, and must be applied form weakly acid baths for control of the rate of dyeing, but they show high fastness to milling and other wet treatments. Milling is a felting process applied to woolen cloth by squeezing or beating, usually in a soap solution. It sometimes follows dyeing, and the dyes used must then have high wet-fastness properties in order to withstand these severe conditions. The advantages of good levelling and high milling fastness cannot be fully combined in a single dye, but there are general purpose dyes with intermediate GTFVJ,./properties. The application classes can becorrelated roughly with chemical types, as shown for monoazo and disazo dyes in Table 4 – 1, which provides a few typical examples. As might be expected from the foregoing generalizations, trisazo and other polyazo dyes are of the milling class, but since shades are usually dull and uneven they are seldom of technical value on wool.1.2.2 Silk Fibres:Cultivated silk is a natural fibre produced by larvae of the silkworm Bombyxmori, and wild silk is produced similarly by silkdworms of various species. Raw silk consists of the protein fibroin surrounded by silk gum (sericin), and the latter is removed in the process of de-gumming or ‘boiling off’ which precedes dyeing.

2

Fibroin consists of long parallel chain containing about 400 amino acid residues with a structure of the general type

The residues are derived mainly from the amino acids glycine (R = H), alanine (R = CH3), serine (R=CH2OH) and tyrosine (R= --CH2--- OH), but there are numerous others in small quantities. Fibroin differs from keratin in that it contains no sulphur. Its chemical properties are similar to those of keratin, but it is more sensitive to acids than the latter and less sensitive to milk alkalis. Silk can be dyed with dyes of almost every class, but some restrictions arise from the common practice of weighting the fibre with tin salts, which is carried out in order to improve handling properties and reduce cost. So far as azo dyes are concerned the main classes applied to silk are the acid dyes and pre-metallised dyes already described as wool dyes, the direct dyes described in Chapter and the reactive dyes described in Chapter. Mordant dyes applied to silk are mainly of the anthraquinone type. It has never been necessary to develop dyes especially for silk.

1.2.3 Cellulosic Fibres:

The earliest cellulosic fibres were lines and cotton, both of which have been used since remote antiquity. Linen, or flax, is derived from ‘bast’ fibres of plants of the Linum family, especially Linum usitatissimum. After removal of glutinous and pectinous matter the fibre has cellulose content of 82 – 83%. Cotton, which is fine hair attached to seeds of various species of plants of the Gossypium genus, has a cellulose content which may reach 96%. Cellulose is a polymer of high molecular weight consisting of long chains of D-glucose units connected by B-1, 4- glucosidic bonds, and its structure may be represented asfollows:

Each glucose unit contains three alcoholic hydroxyl groups, of which two are secondary and one is primary. The degree of polymerisation of cellulose varies from a few hundred to 3500 or more.Regenerated cellulose fibres were introduced during the last two decades of the 19th century. The first process was that Chardonnet (1884), who produced a fibre by spinning a solution of nitrocellulose in a mixture of alcohol and ether and subsequently removing nitro groups. The cuprammonium process followed (1890), and in 1891 Cross and Bevan introduced the viscose process

3

whereby wood pulp cellulose is treated with caustic soda and carbon disulphide to form sodium cellulose xanthate, which, after a ‘ripening’ stage, is spun into an acid coagulating bath. The nitrocellulose process is now obsolete, but the cuprammonium process, which has the advantage of giving an exceptionally fine filament, is still used. The viscose process is of much greater importance, but it is declining in consequence of the development of the newer synthetic fibres. The dyeing properties of the various cellulosic fibres are broadly similar, but application conditions are affected by differences in physically properties. Thus lines, which has a harder structure than cotton, is less readily penetrated by dyes. There are also differences in dyeing properties between the several types of regenerated cellulose fibres; cuprammonium rayon, for example, having fine filaments, is more easily dyed than viscose. Dyes of many chemical classes are applied to cellulosic fibres. Azo dyes, which predominate numerically, are described here, and others are dealt with in the appropriate chapters. The first substantive or ‘direct’ dyes discovered in 1884 were diazo dyes obtained from tetrazotised benzidine, but other structure have since been found to confer affinity for cellulose. The azo group itself favours substantivity but for adequate effect either a second azao group or another favourable group must also be present in the dye molecule.The structures which are chiefly important in substantive dyes are as follows

All of the other groupings listed find used in conjunction with the azo chromophore to give a great variety of dyes for cellulosic fibres. Others of smaller importance, such as the residues of pyrazol-5-one, resorcinol and m-phenylenedianine, also confer a measure of cellulose affinity. Apart from the presence of one or more of the favourable components there are other structure requirements for substantivity. Typical substantive azo dyes of the various chemical classes are now described.

1.2.4 Monoazso Dyes:

4

About 35 monoazo direct dyes are in use, most of them containing either a thiazole or a J acid residue. Examples are CI Direct Yellow 8 (CI 13920), CI Direct Brown 30 (CI 17630) and CI Direct Red 118 (CI 17780) (diazotised and developed on the fibre with B-naphtol or 3- methy-1-phenylpyrazol-5-one), with the structures shown:

1.2.5 Dyes with Mixed Chromophores:

Polyazo dyes normally contain a single chromophoric system, and a conjugated chain runs through the whole molecule. It is possible, however, for a dye molecule to contain two or more independent chromophoric systems electronically insulated from each other. Such dyes were first introduced by CIBA, who utilized the triazinyl ring as a chromophoric block. This ring serves as a convenient link since it can be introduced

5

by reaction of cyanuric chloride with two or three aminocontaining dyes in succession. Substitution of the first chlorine atom takes place easily in presence of alkali at atmospheric temperature. The second chlorine atom is less easily removed, and reaction with an amino compound may require a temperature of 55o – 60oC, the optimum conditions varying with the basicity of the amine. Replacement of the clorine atom calls for still more vigorous conditions, and a temperature of 90o – 100oC may be suitable; much higher temperature are needed, however, in the case of weakly basic compounds. The progressive loss of activity at each stage enables condensation to be carried out with three different components to give a substantially homogeneous product. The residues of three dyes (Dye 1)-NH2, (Dye 2)-NH2 and (Dye 3)-NH2 may be linked by a series of reactions in alkaline medium, as shown:

In the resulting product each dye residue contributes its own absorption characteristics; by combining yellow and blue components, green dyes can therefore be obtained that are much brighter than normal polyazo greens. Dyes containing three inde; pendent chromophoric system is of limited interest and the third condensation is often carried out with a suitably reactive colourless compound such as aniline or phenol.An example of a commercial dye containing two electronically insulated chromophores is Chlorantine Fast Green BLL (CIBA) (CI Direct Green 26; CI 34045); it gives bluish green hue on cellulosic fibres. One of the aminoazo dye residues. A commercial dye containing both azo and anthraquinone residues is Chlorantine Fast 5 GLL (CIBA) (CI Direct Green 28; CI 14155), which has the structure (2) and gives bright yellowish green shades on cellulosic fibres.

6

1.2.6 Cellulose Acetate Fibres:

The D-glucose units in the cellulose polymer contain three hydroxyl groups, of which one is primary and two are secondary. By acetylating all of the hydroxyl group in cellulose a triacetate is obtained with a polymetric structure which may be represented thus:

The triacetate is soluble in chloroform, and a fibre known as Lustron was spun from chloroform solution in early small-scale American manufacture (1914-1924). If the triacetate is partially hydrolysed to give a mixture with an average of 2 ½ acetyl groups per glucose residue the product loses solubility in chloroform, but becomes soluble in acetone. A different product, which is insoluble in acetone, is obtained by direct introduction of 2 ½ acetyl groups; presumably the less accessible hydroxyl groups are the last to be acetylated and the last to be re-formed on hydrolysis. During the First World War incompletely acetylated cellulose was produced on a large scale for use as a dope for aircraft fabric. After the war efforts to find a new use for it led to the production of cellulose acetate fibre by British Celanese Corporation. The commercial product contains an average of 2-3 acetyl groups per glucose residue, and

7

is known as secondary acetate, or simply ‘acetate’. It is spun from acetone solution. In spite of an inconveniently low melting-point acetate fibre attained great success and is still extensively used, but in recent years it has been partly superseded by other synthetic fibres. It was appreciated in the early days that the dyeing of acetae differs from that of the natural fibres and viscose in that fibre serves as a solvent for the dye. In 1923 work on dyes in the form of aqueous dispersions was carried out independently by British Celanese Corporation and British Dyestuffs Corporation. The SRA colours of British Celanese Corporation were dispersions of aminoazo or hydroxyazo dyes obtained by means of the surface-active agent sulphated ricinoleic acid. Other dispersing agents used included alkyl sulphates, alkaryl sulphonates and fatty alcohol-ethylene oxide condensates (a long alkyl chain being usually present in the molecule), and the dispersions obtained by applying them with various milling techniques were often so fine as to be easily mistaken for true solutions. British Dyestuffs Corporation marketed dispersed aminoazo and hydroxyazo dyes in their Dispersol range, and this is still maintained by ICI (formed in 1926 by a union of British dye stuffs Corporation with other firms). The Duranol range is a parallel range of dispersed dyes of the anthraquinone series. Dyes of these types are now produced by many manufactures. Whereas the dyes were formerly supplied only as aqueous dispersionsthey are now usually marketed in the form of re-dispersible powders which yield suitable dispersions on stirring with water. Hydroxyalkylamino groups impart a small degree of watersolubility and assist dispersibility; coupling components such as N-ethyl- N- B-hydroxyethylaniline or N, N-di (B-hydroxyethyl) aniline aretherefore commonly used. Many of the earlier yellow and orange dyes proved to be phototropic, but it was found that this groublesome characteristic can be largely avoided by introducing nitro or other negative groups into the dye molecule; these substituents restrain trans cis isomerizatrion. Since dye molecules must be fairly small in order that they dissolve readily in the fibre monoazo dyes are commonly used, but a few disazo dyes are included in commercial ranges. Blacks are obtained by diazotising aminoazo dyes on the fibre and developing with a solution of 3-hydroxy-2-naphthoic acid. In 1936 a range of water-soluble dyes for acetate was marketed by ICI under the name Solacet. Their solubility was due to the presence of a sulphuric ester group (-- OSO3Na), usually introduced by sulphation of a B-hydroxyethlamino group, which did not seriously impair affinity for the fibre. The unsuitability of conventional water-soluble dyes for acetate fibres is apparently due to the presence of highly ionised – SO3-Na+ groups rather than their solubility in water. In consequence of the of the development of dispersed dyes with improved dyeing and fastness properties the Solacet range has now been superseded. Many dyes developed for acetate have now been applied to the newer synthetic fibres, and the manufactured ranges have been extended specially for these outlets. The term ‘Acetate dyes’ has therefore, been discarded in favour of ‘Disperse dyes’ so that all applications may be included. Disperse dyes for fibres other than acetate are described later. Examples of azo disperse dyes applied to acetate are shown in Table 4.6; violet and blue dyes are included, but disperse dyes of these shades are derived mainly from the anthraquinone series.

1.2.7 Cellulose Triacetate Fibres:Cellulose triacetate was manufactured in the United States during the period 1914-24, but the process was unsatisfactory because the only suitable solvent then

8

commercially available was chloroform, and this was both toxic and expensive. Methylene dichloride is a suitable solvent of low toxicity, and it became available fairly cheaply about 1930, but by the eat time secondary acetate was fully established. Later, however, when the hydrophobic fibres nylon and ‘Terylene’ had achieved great success, the possibilities of triacetate as an inexpensive fibre sharing some of their good properties became apparent, and it has now been introduced as a commercial fibre under names such as Tricel (Courtaulds Ltd.), Armel (Celanese Corporation of America) and Trilon (Canadian Celanese Ltd.). It has good shrink- and crease-resistance, is quickdrying, shows good fastness to wet treatments and can be heat-set without loss of lustre. As it has a higher melting point the hazards associated with the ironing of fabrics of secondary acetate are largely avoided. Because of its hydrophobic character triacetate is less easily dyed than acetate, but suitable dyes can be selected from existing ranges of disperse dyes. Whereas acetate is dyed at 75o–80oC, triacetate requires a temperature at or near the boil. If the fabric is to be heat-set for pleats the dyes used must be stable at 200oC.

1.2.8 Poyamide Fibres:

Nylon 6,6 and Nylon 6 can be dyed by many disperse, acid and direct dyes. Since many suitable dyes are available, commercial ranges are usually selected from products already manufactured for other purposes, and (apart from the reactive dyes discussed later) new structures have not been required. It has proved very difficult to manufacture nylon with uniform dyeing properties, and for this reason dyes with good leveling properties are necessary. In this respect disperse dyes have a great advantage in that they conceal fibre irregularities. For high wet-fastness acid dyes are preferred, but very careful application is necessary in order to secure level dying. These dyes often show better wet-fastness properties on nylon than on wool because of the hydrophobic character of the former. Fastness to light, however, is often slightly lower on nylon than on wool. The affinity of acid dyes for Nylon 6 is higher than that for other types because polycaprolactam fibres contain a higher proportion of free amino groups Ranges of acid dyes for nylon are classified by the makiers so that users may select dyes with good leveling or good wet-fastness properties according to their requirements, there are also ranges with intermediate properties and others specially designed for fabric printing.

1.2.9 Polyester Fibres:

In the course of the exploratory work that led to the development of nylon W.H. Carothers examined aliphatic polyesters but abandoned them in favour of the more promising polyamides. Subsequently, however, the late J.R. Whinfield and J.T. Dickson of The Calico Printers’ Association re-examined polyesters for the purpose. They extended the work to aromatic compounds and obtained a polymer with excellent fibre-forming properties from terephthalic acid and ethyleneglycol. This has the structure (3). The important fibre ‘Terylene’ was based on this

9

Work, and was first prepared in the laboratory in 1941. Development and production of the fibre were carried out by ICI, and this fibre is now manufactured under various names on a very large scale in many parts of the world. Dimethyl terephthalate is now commonly used in place of the free acid so that the terminal carboxlic acid group is esterified. Since n has a value of about 80 the properties of the fibre are not greatly affected. The ester is preferred as starting material because it is more easily purified, and purity is essential in the manufacture of high polymers. ‘Terylene’ fibre is highly hydrophobic, withstands attack by bacteria, moulds, months, acid and alkali, has high strength even in wet conditions, is superior to nylon in resistance to light, can be heat-set and has glood di-electric properties. It is largely used for manufacture of net curtains, in blends with wool for suitings and other outerwer,k and for many industrial purposes. The hydrophobic nature of ‘Terylene’, its tightly packed molecular structure and its lack of reactive groups all render it unreceptive to dye molecules. Certain disperse dyes can be applied, but under normal conditions adsorption is slow and only pale shades are obtained. Much better penetration is obtained by dyeing at about 12Oc under pressure, and the special dyeing machinery required is now in general use. Since diffusion is slow in conditions of normal use, dyeings obtained in this way have good wet-fastness properties. Suitable dyes must be selected for this process since not all will withstand the high temperature without change of shade. Disperse dyes can also be applied at temperatures below 100oC by the aid of ‘carriers’ added to the dyebath. These agents are supplied under various brand names, such as ‘Tumescal’ (ICI), and usually consist of compounds such as o- or phydroxydiphenyl. Their presence greatly facilitates the dyeing process, but the mode of action is not fully understood. This process enables dyeing to be carried out in standard machines, but it is somewhat expensive and has disadvantages in that the carriers are often difficult to remove completely; their presence may cause a noticeable odour and sometimes impairment of light-fastness. Polyester fibres can be dyed by the Thermosol process (DuPont), which consists in padding with disperse dye and a thickening agent, then drying and heating at 175o – 200oC for about one minute. Under such conditions the dye is absorbed rapidly; after scouring to remove loose colour the dyed material is finished in the usual way.

10

1.2.10 Polypropylene Fibres:

Polyethylene has many applications in the plastic industry, but its low melting-pointrenders it unsuitable for fibre formation. Its homologure polypropylene exists in various forms according to the disposition of the substituent methyl groups; the isotactic polymers, in which these groups are all attached on the same side of the main carbon chain, can be spun and drawn into fibres. Catalysts promoting formation of isolactic polymers were discovered by Zeigler, and the process was further developed by Natta and others Polyproplene fibres and hydrophobic and resist chemical attack, but they are not readily dyed. Certain disperse dyes can be applied, but only pale and medium shades are obtainable. Many methods have been described in the paten literature whereby the fibre may be modified to confer affinity for acid or basic dyes. Side chains carrying polar groups may be grafted to the main polymer chain, or basic substances may be included in the melt from which the fibre is spun. Much attention has been paid to a method whereby a compound of a polyvalent metal such as nickel, zinc or aluminium is incorporated in the fibre, which can then be dyed with metalisable dyes.

1.2.11 Polyurethane Fibres:Several elastomeric fibres developed in America are based on polymeric structures containing urethane (--NHCOO--) linkages. Full details of the processes used are not available but complex cross-linked polymers with rubber-like properties are obtained from polyesters or polyethers containing terminal hydroxyl groups by means of a series of reactions involving di-isocyanantes and diamines. Typical examples of such fibres are Lycra (Du Pont) and Vyrene (U.S. Rubber Co.), which are extensively used for foundation garments and swimsuits. These fibres have advantages over rubber in strength, resistance to oxidation, perspiration and cosmetic oils, also in whiteness and affinity for dyes. They are readily dyed by acid, basic and disperse dyes, but fastness properties are in general rather low.

1.2.12 Polyacrylonitrile Fibres:The simplest, polyacrylonitrile fibres are straight polymers of

acrylonitrile with structure where n varies from600 to 2000. The first commercial fibre of this type was Orlon, introduced by DuPont in 1948. It can be dyed by basic dyes or by acid dyes in presence of copper sulphate. Various modified acrylic fibres (often called ‘modacrylic’ fibres) are now obtained by copolymerizing acfrylonitrile with other substances, and dyeing properties are thereby improved; Orlon as now manufactured is a copolymer, but the identity of the second component has not been disclosed. Acrilan (Chemstrand Corporation), Dynel (Union Carbide Corporation) and courtelle (Courtaulds Ltd.) are other modified acrylic fibres. In general acid, disperse, basic and vat dyes can be applied to these fibres, but acid dyes are not recommended for Courtelle. The older basic dyes often show better light

11

fastness on acrylic fibres than on natural fibres, but new basic dyes have been developed with fastness properties on polyacrylonitrile that are fully compatible with modern standards.

12

2.1 DyestuffDyestuff is organic or inorganic substances which can absorb light and reflect some lights to show color. Actually, the dyestuff is water soluble substances.

2.2 PigmentPigment is a substance that can absorb light and reflect some lights to show color but it is water insoluble substances. Normally it is used for printing (with the presence of binder) or mass-coloration of the synthetic fibers.

2.3 CRITERIEA FOR A SUITABLE DYESTUFF

1. Cheap 2. Non-toxic 3. Compatible to other dyes and chemicals 4. High color strength 5. Better brightness 6. Better fastness 7. Good levelness on the materials

2.4 Exhaustion of the dye stuff to the fibers is as follows:

1. Moving of dyestuff from dye bath to surface of the fiber 2. Adsorption of the dyestuff into the surface of the fiber 3. Diffusion of the dyestuff into the center of the fiber.

2.5 Classification of Dyestuffs

Dyestuffs can be classified according to two ways1. According to common parent structure2. According to application

2.5.1. Classification according to common parent structure or Chemical classification of dyes:

The chemical constitution of dyes are varied that it is difficult to classify them into distinct groups. The colour index classifies dyes as shown.

1. Nitro dyes.2. Nitroso dyes.3. Azo (Monazo) dyes.4. Azoic dyes.

13

5. Stilbene dyes6. Tgri0aryl methane dyes.7. Xanthenei dyes.8. Quinoline dyes.9. Methine dyes.10. Acridine dyes.11. Nitro dyes.12. Sulphur dyes.13. Thiazole dyes.14. Thizine dyes.15. Indamine dyes.16. Oxazine dyes.17. Azine dyes.18. Lectone dyes.19. Anthra quinine dyes.20. Indigoid dyes.21. Phthalocyanin dyes.

2.5.2 CHEMISTRY OF SOME DYESTUFF

(1) Nitro Dyes:Nitro dyes are polynitro derivatives of phenols containing at least one nitro group ortho or para to the hydroxyl group. They are of relatively little importance industrially, because the colours are not very fast. Examples of this class are picric acid (2,4,6-trinitrophenol), Maritus yellow (2, 4-dinitro-1-naphthol), and Naphthol yellow S (2,4-dinitro-1- naphthol-7-sulphonic acid). Naphthol yellow S can be used to dye wool, and is one of thecolours permitted in foods. Naphthol yellow S can be used to dye wool, and is one of the colours permitted in foods.

1. Naphthol yellow S can be used to dye wool, and is one of the colours permitted in foods.

(2) Azo Dyes:

The azo dyes represent the largest and the most important group of dyes. They are characterised by the presence of one or more azo groups (–N=N–), which form bridges between two or more aromatic rings. Preparation of azo dyes involves the following two steps.

14

Step 1. Conversion of primary aromatic amines into diazonium compounds by treatment with sodium nitrite in excess hydrochloric acid (Diazotisation)

Step2. Coupling of diazonium compounds with phenols, naphthols, or other aromatic amines. Coupling with phenols and naphthols is carried out in basic solution; coupling with amines is carried in acid solution.

The above reactions are carried out at low temperatures (0 – 5o) because diazonium compounds are usually unstable. In the resulting dyes an aromatic system joined to the azo group is the chromophore, and the hydroxyl group or amino group is an auxchrome. To simplify the description of azo dyes, only the coupling step will be shown. It will be assumed that the diazonium compound was obtained by diazotisation of the corresponding amine.(a) Aniline Yellow: Solvent Yellow 1. It is p-aminoazobenzene. Aniline yellow is the simplest azo dye and is obtained by coupling benzenediazonium chloride with aniline in acidic medium

Aniline yellow is used as a dye for oils and lacquers, and is also an intermediate for other dyes.(b) Chrysoidine: Basic Orange 2. It is 2, 4-diaminoazobenzene. Chrysoidine is prepared by coupling benzenediazonium chloride with mphenylenediamine.

(3) Diphenlymethane Dyes:

Auramine O: It is one of the most valuable of the diphenylmethane dyes. It is obtained by heating Michler’s ketone with ammonium chloride and zinc chloride at 160oC.

15

Auramine O is used to dye wool, silk, silk, nylon, rayon and paper.(4) Triphenylmethane Dyes:Triphenylmethane dyes can be identified by common structural cature shown below. Notice that the central carbon atom is joined to two benzene rings and to p-quinoid

group.

Triphenylmethane dyes are not fast to light or washing, however, except when applied to acrylic fibres. They are used in large quantitiesfor colouring paper, and typewriter ribbons where fastness to light is not so important.

(a) Malachite Green: It is obtained by condensing benzaldehyde (1 molecule) with N, N-

dimethylaniline (2 molecules) in the presence of concentrated sulphuric acid to give a leuco base (Gr. Leuco, colourless). Oxidation of the leuco base with lead peroxide followed by treatmen with hydrochloric acid yields the dye.

16

(b) Pararosaniline: It is the simplest triphenylmethane dye. Pararosaniline is obtained by consdensinig p-toluidine (1 molecule) with aniline (2 molecules) in the presence of nitrobenzene to give a colourless carbinol. Nitrobenzene serves both as a solvent and an oxidising agent. Treatment of the carbinol with hydrochloric acid yields the dye. Pararosaniline has been used to dye cotton, wool and silk.

(5) Xanthene Dyes:Xanthene dyes can be identified by a common structural feature shown below. They are obtained by condensing phenols with phthalic anhydride in the presence of zinc chloride, sulphuric acid, or anhydrous oxalic acid. Examples of this class are fluorescein, eosin, and rhodamine B.

17

(a) Fluorescene. It is prepared by heating resorcinol (2 molecules) and phthalic anhydridge (1 molecule) with zinc chloride at 190oC

Fluorescein is of no value as a dye. It is red powder, which is insoluble in water. A dilute solution of fluorescein in sodium hydroxide gives a strong yellow-green fluorescence

when exposed to light. It is used to trace pollution of water supplies by sewerage, since if a small quantity of it is put in at the suspected source of pollution, the colour will be detectable at some distance from the source, even after extensive dilution. During World War II, fluorescein was used as a sea marker for airmen who had to bail out from aeroplanes over water. It also aided searchers in locating them. Fluorescein is also used as a mild purgative. The sodium salt of fluorescein is called Uranine. It is used to dye wool and silk. (6) Phthaeleins:Phthaleins are related to xanthene dyes and are made in the same way. Phenolphthalein: It is prepared by condensing phenol (2 molecules) with phthalic

anhydride (1 molecule) in the presence of zinc chloride at 120oC

Phenollphthalein is not a dye. It is colourless solid, mp 261oC.Phenolphthalein is insoluble in water, but dissolves in alkalis to form deep red solutions. This is due to the formation of a disodium salt, the ion of which is coloured because of resonance. When excess of strong alkali is added, the solution of phenolphthalein becomes colourless. This is attributed to the formation of a trisodium salt, the ion of which is colourless because of loss of resonance and quinoid structure.

18

Because of the colour changes shown above, phenolphthalein is used as an indicator in acid-base titrations. Phenolphthalein is an extremely powerful laxative, and this accounts for its widespread use as a denaturant for laboratory alchohol.(7) Indigoid and Thioindigoid Dyes:Indigoid. It is the parent compound of indigoid dyes and has been used in this country from times immemorial. Egyptian mummy clothes, which are 5000 years old, were dyed with it. Indigo was originally obtained from plants of indigofera group. The leaves from these plants were covered with water and allowed to stand for several hours. Enzymes present in the plants brought about fermentation, as a result of which the β-glucoside of indoxyl (known as indican) in the leaves was converted into indoxyl and glucose. Upon exposure to air the indoxy was oxidised to indigo.

19

Natural indigo contains an isomer of indigo known as indirubin(Indigo Red), and other impurities in varying proportions. Most of the indigo used at the present time is a synthetic product. It has replaced the natural stuff because of cheapness, purity, and uniformity of the manufactured dye.Preparation of Indigo. It may be obtained:(1) By Heumann’s First Indigo Synthesis (1890). This involves the condensation of aniline with chloroacetic acid to give Nphenylglycine. The phenylglycine is then fused with sodium hydroxide and sodamide at 250oC to form indoxyl, which on oxidation by air yields the dye.

N-Phenylglycine is now obtained in much higher yield by interaction of aniline and the bisulphite compound of formaldehyde at 50-60oC, followed by treatment with aqueous sodium cyanide, and hydrolysis of the resulting nitrile.

20

(2) By Heumann’s Second Indigo Synthesis (1896): This involves the condensation of anthranilic acid with chloroacetic acid to form N-phenyl-o-carboxylic acid. This is then fused with sodium hydroxide and sodamide to produce unstable indoxylic acid, which decarboxyhlates to give indoxyl. Oxidation of indoxyl by air yields the dye.

21

Structure of Indigo: The structure of indigo has been deduced from consideration of facts and conclusions such as the following. 1. Elemental analysis and molecular weight determinations show that the molecular formula of indigo is C16H10O2N2. 2. Fusion of indigo with sodium hydroxide at low temperature produces anthranilic acid. This indicates the presence of a benzene ring attached to one carbon atom and one nitrogen atom in the ortho position.

3. Oxidation of indigo with nitric acid yields only two molecules of isatin. This indicates that the indigo molecule contains two identical units joined together, and that each unit on oxidation produces a

molecule of isatin.The following two possible structures of indigo meet this requirement.4. Oxidation of indoxyl by air yields indigo.From above, it follows that (A) represents the structure of indigo. This has been confirmed by the following synthesis by Baeyer (1872).

22

X-Ray analysis shows that mostly indigo exist in the more stable transform. However, derivatives of both are known.(a) Tyrian Purple. It is 6, 6’-dibromoindigo. Its discovery was later than that of indigo but it is believed to have been known in 1600 BC.

23

Tyrian purple occures naturally in the purple snail, Murex Brandaris. It takes about 12000 snails to produce 1.4 g of the dye. This explains its rarity and why the colour of mercial value.(b) Thioindigo. It is analogues to indigo in which the two –NH–

groups are replaced by sulphur atoms. Thioindigo may be obtained by the reaction of thiosalicylic acid, with chloroacetic acid, followed by fusion with sodium hydroxide and oxidation by air. Thiosalicylic acid itself is made by diazotisation and reaction with hydrogen sulphide.

Thioindigo is used to dye cotton, wool and polyesters.(8) Anthraquinoid Dyes:Anthraquinoid dyes can be identified by a common structural feature shown below.

Notice that a p-quinoid group is fused to two other benzene rings.

Anthraqluinoid dyes are used for dyeing wool, silk, nylon, cotton, leather and paper. The most important dye in this group is alizarin. Alizarin. It is 1,2-dihydroxyanthraquinone. Alizarin derives its name from the fact that it was first

obtained from the roots of the madder plant (Fr. Alizari, madder). It is now prepared from phthalic anhydride by the following six steps.Step 1. Phthalic anhydride is treated with benzene in the presence of AlCl3 to give o-benzoylbenzloic acid. (Friedel-Crafts Reaction)

24

Step 2. O-Benzoylbenzoic acid is cyclized by treatment with concentrated sulphuric acid to form anthraquinone.

Step 3. Anthraquinone is heated with fuming sulphuric acid at 180oC to give anthraquinone-2-sulphonic acid.

Step 4. Anthraquinone-2-sulphonic acid is converted into its sodium salt by treatment with sodium hydroxide.

Step 5. Sodium salt of anthraquinone-2-sulphonic acid is fused with sodium hydroxide in the presence of potassium chlorate at 200oC under pressure to give sodium salt of 1, 2-dihydroxyanthraquinone. The purpose of potassium chlorate is to provide oxygen for the oxidation of the carbon atom at C-1.

25

Step 6. Sodium salt of 1,2-dihydroxyanthraquinone is treated with sulphuric acid to yield 1,2-dihydroxyanthraquinone (Alizarin).

Alizarin can also be made by condensing phathalic anhydride with catechol in the presence of sulphuric acid at 180oC (See Below). Alizarin forms ruby red crystals, mp 290oC. It is insoluble in water and ethanol. It dissolves in alkalis to give purple solutions. Alizarin is used to dye cotton and wool. It is also used for making printing inks.Structure of Alizarin: The structure of Alizarin has been deduced as follows:1. Elemental analysis and molecular weight determinations show that the molecular formula of alizarin is CI4H3O4: 2. Reduction of alizarin with zinc dust at 400oC produces anthracene. This indicates that it has the same carbon skeleton as that of anthracene.3. Alizarin reacts with acetic anhydride to form a diacetate. This indicates the presence of two hydroxyl groups in the molecule.4. Alizarin can be prepared by condensing phthalic anhydride and catechol in the presence of sulphuric acid at 180oC. This shows that alizarin is a dihydroxy derivative of anthraquinone and both – OH groups are substituted in the same benzene ring.

The above facts limit our choice to two structural formula for alizarin.

26

5. Alizarin on nitration yields two isomeric mononitro derivatives, both of which on oxidation give phthalic acid. This shows that in each of these derivatives, the – NO2 group is substituted on the hydroxylated benzene ring.Let us now write down the possible mononitro derivatives from (A) and (B).Mononitro derivatives from (A):

2.5.3 DYE CLASSES ACCORDING TO APPLICATION

1. BASIC DYESThe colours are very bright, but not very fast to light, washing, perspiration. Fastness is improved if they are given an after-treatment or steaming, e.g. French Silk dyes are basic dyes and should be steamed to fix.

2. ACID DYESThese are acidified basic dyes, intended for use on protein fibres but can be used on nylon and acrylics. They have a fair light fastness but poor wash fastness

3. PREMETALLIZED DYESThese are an acid dyes with the addition of one or two molecules of chromium. The dyesgive mutetonings, not unlike those of natural dyes. They are the synthetic dyes mostly used by weavers who dye their own yarns.

27

4. DIRECT DYESThese substantive dyes colour cellulose fibres directly in a hot dyebath without a mordant, to give bright colours. They are not very fast to light or to washing. Direct dyes are generally any dyes which use salt as their only fixative, e.g. Dylon dyes (not to be confused with reactive dyes, which use salt plus other chemicals).

5. AZOIC (NAPHTHOL) DYESThese are another sort of direct dye, but ones that are extremely fast to washing, bleach and light. They are intended for cellulose fibres and can be used successfully on protein fibres, although the colours are different. These dyes are widely used all over Asia and Australia for batik and direct application. They can be used to give interesting texture colour effects on fabric, thread or paper. Their use for straight silk painting is minimal because of the difficulty in achieving evenness of painted colour.

6. DISPERSE DYESOriginally developed for acetate fibres, these are now the major dyes for synthetics. They are not soluble in water, but in the actual fibres themselves. They require a carrier to swell the fibres so that the finely ground particles can penetrate. They are dyed hot, like direct dyes, but do not use salt. Disperse dyes are widely used for heat transfer printing (Polysol). Dye is printed or painted onto paper and heat pressed onto fabric. Prints have excellent light and wash fastness and strong bright colours. Their major disadvantage is that only synthetic fabrics can be used.

7. VAT DYESVat dyes are the fastest for cellulose fibres. The dye is made soluble with alkali, put in a 'vat' with a reducing agent, usually sodium hydrosulphite, which removes all oxygen from the liquid, and the fabric is dyed, then oxidized in the air to achieve the true colour. Synthetic indigo is a characteristic vat dye, but there are many colours available

8. REACTIVE DYESReactive dyes are the most recent of dyes. These are the most popular in the world among fibre and fabric artists, used at first only by surface designers, but recently by weavers as well. There are now reactive dyes for a wide range of fibres, e.g. cotton (PROCION), silk and wool (PROCILAN). The dye actually reacts with the fibre molecules to form colour and is, as a result, extremely fast to both light and washing. There are hot and cold water reactive dyes, in fact there is a dye for almost every need. They can be most successfully used for silk painting, with a much better colour fastness than the traditional basic dyes, and are already used by batik artists. we can identify a reactive dye by the alkali used to set off the fixation process, which requires time to take place (silk and wool reactives uses acetic acid). Assistants used are salt, soda ash and resist salt, and sometimes bicarbonate of soda and urea. Reactive dyes are equally suited to screen printing polychromatic printing, fabric painting yarn and piece dyeing.

2.6 Dyestuff SelectionFastness is always influencedby the type and constructionand the treatment (heat setting of the fiber, and the typeand family of dyestuff.Dyes should show similar

28

diffusionand trichromatic behaviorand fixation rates. The combi-nation of fibers, dyes and auxiliaries must be selected carefully

29

2.7 Dyes used for Textile IndustryDyes for the textile dyeing can also be grouped according to the fibres to which they can be applied. The strength of the dye-fibre attraction is called “Affinity”. Each class of dye has a unique chemistry, structure and way of bonding to the fibre. Colour consents are now being enforced and therefore dye fixation levels are becoming more important. Selection of the right dyes helps to minimise effluent losses. Typical dye fixation levels for most of the dye classes are shown in the table

30

3.1 Dyeing

Dyeing is the application of color to the whole body of a textile material with some degree of color fastness. Textiles are dyed using continuous and batch processes and dyeing may take place at any of several stages in the manufacturing process (i.e., prior to fiber extrusion, fiber in staple form, yarn, fabric, garment). Most of textile dyeing is done in finishing departments of basic textile manufacturing facilities, although there are also several commission dye houses. From an environmental perspective, dyeing has typically been viewed as a waste water issue due to large quantities of water, chemicals, and auxiliaries (such as salt). Dyeing is essentially a mass transfer process where the dye diffuses in solution, adsorbs onto the fiber surface, and finally, within the fiber. Dyeing is complicated by the fact that there are many sources of color variations, such as dyes, substrate, and preparation of substrate, dyeing auxiliaries used, and water. Processing variables such as time, temperature, and dye liquor ratio (pounds of dye bath to pounds of cloth) also affect dyeing results. There are hundreds of dyes within several dye classes, each of which exhibits different results when applied to different types of fabric. Various types of dyeing machines are used for both continuous and batch processes. Every dye system has different characteristics in terms of versatility, cost, tension of fabric, use of carriers, weight limitations, etc. Dyeing systems can be aqueous, non-aqueous (in organic solvents), or use sublimation (thermosal, heat transfer). Hydrophilic fibers such as cotton, rayon, wool, and silk, are typically easier to dye as compared with hydrophobic fibers such as acetate, polyesters, polyamides, and polyacrylonotriles. The four basic steps in the dyeing process are: dissolving or dispersing dye; diffusing dye onto the fiber surface; absorbing dye onto the fiber surface; and diffusing dye into the fiber. Batch dyeing involves moving the dye liquor through the goods or moving the goods through the dye liquor. The textile material is immersed in the dyebath during the entire period of dyeing. In batch dyeing, a certain amount of textile substrate, usually 220 to 2200 pounds, is loaded onto a dyeing machine and is brought to equilibrium or near equilibrium with a solution containing the dye. Once immersed in the dyebath, because the dyes have an affinity for the fibers, the dye molecules leave the dye solution and enter the auxiliary chemicals and controlled dye bath conditions (mainly temperature) accelerate and optimize the action. The dye is fixed in the fiber using heat and/or chemicals after which the substrate is washed to remove unfixed dyes and chemicals. There is a trend to use of lower liquor ratios (pounds of dye bath to pounds of cloth) in batch dyeing, which lends benefits such as faster heating/cooling and less waste. Batch equipment can usually be purchased as atmospheric (operated below 212 °F) or pressurized (operated to about 280 °F) machines. Most batches dyeing are being done using pressurized machines, although some facilities use atmospheric machines, especially for fabric dyeing. Atmospheric dyeing might be required for fleeces and stretch fabrics, such as Lycra®, which typically cannot be dyed using jet equipment. Dyeing processes in pressurized machines release no HAP emissions to the atmosphere since the process is totally enclosed and the pressure is released at the end of the dyeing process by cooling the dye bath which is subsequently drained before opening the dyeing machine. However, in some cases, the drying of the pressure-dyed substrate releases HAP emissions. Continuous processes typically consist of dye application, dye fixation with chemicals or heat, and washing. Almost all continuous dyeing is done at atmospheric pressure. Continuous dyeing is usually used for long runs of polyester/cotton fabrics and involves immersing fabrics in a relatively concentrated dye bath for short periods. Textiles are fed continuously into a

31

dye range at speeds usually between 540 and 2690 feet per minute and a concentrated solution of dyes and chemicals (held in pads) is moved evenly and uniformly to the goods with thorough penetration. A pad mangle helps apply pressure to squeeze dye solution into the fabric and the dye is usually diffused or fixed by heating in a steamer or oven. Dye fixation on fiber occurs much more rapidly in continuous dyeing as compared to batch dyeing. After fabrics are dyed, they are dried in ovens or tenter frames after washing to remove un-reacted chemical or loose dye. Fabric that is processed through atmospheric batch dyeing is not dried at the dye range; it is sent to finishing and may be finished wet or dry. Various classes of dyes can be used, e.g. disperse for synthetics and direct for cellulosics. Dyes used in the textile industry are mostly synthetic and are derived from coal tar and petroleumbased derivatives. Dyes are sold as powders, granules, pastes, liquid dispersions, and solutions.Not only are d yes applied in different ways, and they also impart color using different mechanisms. Dyes can be classified according to chemical constitution or method of application. Dyestuffs can work on principles of electrostatic bonding, covalent bonding, or physical entrapment. For example, acid dyes work through the mechanism of electrostatic bonding, whereas disperse dyes work by physical entrapment. Different dye classes exhibit different affinities depending on the type of fiber, although even dyes within the same classes can show wide affinity variations. They also exhibit different properties such as their fastness under end use conditions such as light, laundering, or dry cleaning. Various combinations of chemical auxiliaries and process conditions (temperature and pressure) may be used to better fix the dye on the fabric or impart specific characteristics. For example, a dye bath may contain the dyestuffs along with appropriate auxiliaries such as wetting agents and also specific chemicals such as acetic acid or sodium hydroxide. The use of higher temperatures and superatmospheric pressures have reduced the need for dye carriers (chemical accelerants) that were required at lower temperatures for the use of disperse dyes on synthetic substrates, such as polyester.

Staining:Staining is an unpleasant of dyeing in the area that we do not want

3.2 A BRIEF HISTORY OF DYEING.

Ever since primitive people could create, they have been endeavoring to add color to the world around them. They used natural matter to stain hides, decorate shells and feathers, and paint their story on the walls of ancient caves. Scientists have been able to date the black, white, yellow and reddish pigments made from ochre used by primitive man in cave paintings to over 15,000 BCE. With the development of fixed settlements and agriculture around 7,000-2,000 BCE man began to produce and use textiles, and would therefore add color to them as well. Although scientists have not yet been able to pinpoint an exact time where adding color to fibers first came into practice, dye analysis on textile fragments excavated from archaeological sites in Denmark have placed the use of the blue dye wood along with an as yet unidentified red dye in the first century CE.

In order to understand the art and history of dyeing, we must first understand the process of dyeing itself. According to Webster’s dictionary, dyeing is “the process of coloring fibers, yarns or fabrics by using a liquid containing coloring matter for imparting a particular hue to a substance.” There are three basic methods of

32

“imparting a particular hue to a substance.” The first is by staining an item, a without the benefit of some sort of chemical fixative to preserve the color. The next is the use of pigmentation, wherein the color is fixed to the surface of an object by another adhesive medium. A true dye is when the color of a substance is deposited on another substance in an insoluble form from a solution containing the colorant.

Natural dyes can be broken down into two categories: substantive and adjective. Substantive, or direct dyes, become chemically fixed to the fiber without the aid of any other chemicals or additives, such as indigo or certain lichens. Adjective dyes, or mordant dyes, require some sort of substance, (usually a metal salt) to prevent the color from washing or light-bleaching out. Most natural dyes are adjective dyes, and do require the application of a mordant (the metal salt) solution to the fibers at some point in the dyeing process. Aluminum and iron salts were the most common traditional mordants, with copper, tin and chrome coming into use much later. In rural areas where these metals were not widely available, plants were also used as mordants, especially those that have a natural ability to extract such minerals from the earth, such as club moss. Most ancient and medieval dyers mordanted their yarns and fabrics before dyeing them. Alum and Iron were used as mordants in Egypt, India and Assyria from early times, as there are many alum deposits in the Mediterranean region. Medieval dyers used alum, copper and iron as mordants, and cream of tartar and common salt were used as to assist in the dyeing process. </< b>B>

Different fibers also have different tendencies to absorb natural and synthetic dyes. Protein and cellulose fibers (the two main divisions for fibers used historically in spinning and dyeing) need to be mordanted differently because of their structural and chemical composition. Mordants to cellulose fibers such as cotton and linen usually involve the use of washing soda or tannins to create an alkaline dye bath. Tannins (plantstuffs, such as oak galls containing tannic acid) are widely used in dyeing cellulose fibers as they attach well to the plant fibers, thus allowing the dyes to attach thmselves to the tannins, wheras they might not be able to adhere to the fibers themselves (Tannins are sometimes classified as mordants in and of themselves, but are usually considered a chemical to assist in the dyeing process.) Mordants for protein fibers, like wool and silk, are usually applied in acidic dye-baths. Alum with the assistance of cream or tartar, is the most common mordant used to assist the dyes inn taking to the fibers.

Since the difference in mordanting different fibers has been mentioned, it would remiss not to spend a moment on the historic nature of the fibers themselves. Wool, a protein-based fiber, has been found in Europe dating back to 2000 BCE. It was a common medieval fabric in both dyed and natural colors, and was processed by both professional manufacturers and housewives. Silk, another protein-based fiber, was imported from China to Persia as early as 400-600 BCE. It became quite popular in the Late Middle Ages, and major silk manufacturing centers were set up in France, Spain and Italy. These silk production centers also became centers of dye technology, as most silk was dyed and required the highest quality dyes available. Cotton was considered a luxury fabric, as it was imported all the way from India and usually dyed or painted before it was shipped. Cotton was also valued because of the brightness and colorfastness of the dyes used to color it, and also for its use in making candle wicks. Samples of cotton fabrics have been found in India and Pakistan dating to 300

33

BCE, but it did not appear in Europe until the 4th century. Cotton waving establishments were formed in Italy in the 13th & 14th centuries ut they did not make a significant economic impact on the industry as they produced a coarser quality of fabric than the imported fabric, and therefore had difficulty in obtaining a good supply of cotton fiber.

Scientists are almost certain that dyeing was practiced throughout the world, but it is difficult to obtain proof on this for two reasons. First, not all cultures left written records of their practices. Second, because of the wide variance of environmental conditions and degree of geological disturbance, it is not easy to fine well-preserved evidence of dyed textiles in many archaeological sites. A Chinese text from 3,000 BCE lists dye recipes to obtain red, black and yellow on silks. Ancient Indian texts describe several different yellow dyestuffs, how to obtain reds from the wood and bark of certain trees, and also notes the use of indigo to create blues on cotton. In central and South America they dyed bast fibers (plant fibers) in shades of red and purple with the bodies of the cochineal insects.

A Greek artifact known as the Stockholm Papyrus details dyestuffs and techniques in almost a recipe fashion as it was practiced Egypt in the third and fourth centuries CE. The great detail in which the preparation of the fibers and the dyeing materials and the dyeing process itself are recorded has led scholars to believe that it had to have been practiced for thousands of ears previously in order to raise the process to such a science and art. It discusses mordanting the fibers using alum, copper and iron oxides to darken or “sadden” the red, blue, green and purple dyes, as well as the occasional use of tin and zinc. It describes over ten different recipes for using alkanet (Anchusa tinctoria) root as a dye employing camel and sheep urine, lentils, vinegar, wild cucumber and barley malt among others as aids to producing color. It also gave rcipes on obtaining purple hues by over dyeing the alkanet with woad (Isatis tinctoria), madder (Rubia tinctrum), kermes (made from the dried bodies of the female shield louse or scale insect (Kermers ilicis)) and the heliotrope plant (Heliotropium arborescens). Excavated coptic textiles dating from the fourth to the sixth century CE show use of weld (Reseda luteola) to produce yellow, madder and woad for dark purple, and blue from indigo (Indigofera tinctoria). Scientists have been able to date a red obtained from Egyptian madder root from the fourteenth century BCE.

In the Mediterranean before the advent of Christianity, a whole dyeing industry arose around Tyrian purple. Tyrian purple is produced from the mucous gland adjacent to the respiratory cavity within some species of Purpura and Murex species of shellfish (Schetky, 4). The shells were crushed to extract this fluid, which only turns purple once it has been applied to the fiber and exposed to light and oxidation with the air. The Phoenicians, skillful shipbuilders and sailors that they were, scoured the coastlines for sight of these whelk shells, and established a dye works and trading station wherever they found a plentiful population of these shellfish. Coastal Indians of Mexico were also using shellfish, but their delicate method involved blowing and tickling the shellfish to get them to spit out the dye precursor directly onto the cotton fibers. Even Ireland can produce archaeological evidence of dyeing with the native dog-whelk shells in the seventh century CE. Both Discorides, the Greek physician and pliny the Elder, the Roman naturalist, mention in their first century works the preparation and dyeing of wool with various shellfish to produce colors of red, blue,

34

purple and violet after first being mordanted with soapwort (Saponaria officinalis), oxgall or alum. Both authors also mention the use of Indigo from the Orient to obtain blues, and Herodotus describes its use in a 450 BCE text. Dioscorides also mentions other dye palants of the ancient world, including madder, saffron (Crocus sativus) and weld for yellow, and woad for blue. (Walnut shells (Juglans nigra), oak bark (Quercus sp.), pomegranate flowers (Punica granatum) and broom (Genista tinctoria) were also used in conjunction with various mordants; but galls formed on trees could mordant themselves, being high in tannic acid.

In Europe the art of dyeing rose to new heights with the diversity of climate, culture and migration/invasion waves. This further influenced by the direct impact of trade instigated by the Crusades and furthered by the growing cultural awareness of the Renaissance period-everyone in Europe wanted the exotic, colorful dyestuffs from the Orient, and later rom the Americas. Caravans of camels would cross the Gobi desert for centuries bringing goods from China to the Mediterranean. By the 12th

century the two main trade routes for imported dyestuffs headed through Damascus: the first led rom Baghdad to Damascus to Jerusalem and Cairo, the other went to Damascus to Mosul to the Black Sea to Byzantium (Istanbul).

Venice was one of the major early centers for imported dyestuffs, supplying Brazilwood (Caesalpinia sappan) from the East, lac (another insect dye) and indigo from India from the fifteenth century CE onward. Dyers of Italy soon became adept in their use, in 1429 the Venetian dyer’s guild wrote a book for its members containing a number of different dye recipes, including Brazilwood and lac. The Plictho de Larti de Tentori by Venetian author Giovanni Ventur Rosetti (sp-also listed as Giovanventura Rosetti) in the 1450s lists instructions for using both lac and indigo, as well as 217 other recipes for dyeing cloth, linen, cotton and silk with many varieties of dyestuffs. It would remain the best source for dyeing instruction for the next 200 years.

From Venice the dyestuffs were traded by ship around the coast of France to Flanders, Southampton and London; in the Mediterranean at Florence, Pisa and genoa; and northward on the continent to the distribution centers of Basle and Frankfurt. Basle was a noted center of trade for saffron, the expensive yellow obtained from certain species of crocus. In later years crocus were grown in that area directly, and the crop became such a vital part of the local economy that they crocus was featured on the city’s coat of arms. Frankfurt housed trade fairs from the twelfth to fourteenth centuries that dominated the trade of man dyestuffs, but mainly that of locally grown woad, the only blue dyestuff available to European dyers before the coming of indigo. Many regions in Germany specialized in growing and processing the woad through its complex fermentation process, and strict legislation was placed on every aspect of the trade.

The government of Spain controlled the trade of cochineal, the red dye from the bodies of the Cochineal bugs of Central America. In 1587 approximately 65 tons were shipped to Spain, and from there northward throughout Europe. Italian dyers shunned cochineal in favor of the already established dye kermes, made from the dried bodies of the female shield louse or scale insect. It’s use was first recorded in 1727 BCE and it was long the standard red dye for silk, wool and leather, but the intense colorific value and relative cheapness of cochineal soon eliminated most of the kermes use in England, so Spain hung on to control of their lucrative monopoly.

35

European dyers reached their height of skill in the thirteenth century, mainly use to the guild systems who vigilantly maintained a high standard of quality. In many countries dyers were graded by the guild system, the master dyers being allowed to use the major “fast” dyes while their lesser colleagues were restricted to the slower, “fugitive” dyes. In some places it was forbidden to possess, let alone use, major dyestuffs unless you were a member of a guild. In Germany, the dyers and wood workers were regulated by the guilds, each grower having to present his crop to a “sworn dyer” to determine its quality, weight and condition before it could be sold. English producers of wood had fewer restrictions mainly that of a proclamation in 1587 to restrict growers to certain field size and ensure that no wood mills were sited within three miles o a royal residence, market town or city because of the highly offensive odor they emit. Even the local doctors in Venice in 1413, city fathers, to prohibit dyeing with either wood or ox-blood after March first because of the “unhealthy smell.”. France had developed an extensive and efficient textile industry by the 13th century and also increased the dyers craft by developing varied techniques to achieve additional colors from the basic dyestuffs. At the end of the 16th century, there were over 220 master dyers listed in Paris alone.

While the powerful guild system had numerous dyestuffs with which to blend their color palates of fiber for the bluebloods and wealthy merchants, dyeing in the lower classes was a bit more restrictive. Without the money (or connections) to buy indigo, cochineal and turmeric, clothing in the country tended to natural colours-whites, blacks, browns, grays, and tans of the natural colors of the fibers themselves, with the reds, greens and yellows of local plants used for both food, medicine and dyes. In short, home dyers used any plants they could lay their hands on that world give a good color. Some colors were even derived accidentally. Washing bee hives in preparation for making mead could yield yellows and gold’s. Blackberries and Bilberries that stained the fingers of pickers could also be used to achieve pale blues and purples, although these were not often color or lightfast. In England, the multitudinous variety o lichens and mosses produced greens, grays and browns.

By the seventeenth century a world-wide shipping and trading network was in place, allowing dyestuffs from all parts of the world to be brought to Europe. Legislation from earlier centuries to protect the growers and users of specific dyestuffs was overturned in favor of new demands and standards set by the growing consumer-focused society who wanted more colors and better quality. In the eighteenth and nineteenth centuries the practice of colonialism insured that there would always be a supply of foreign dyestuffs, and the Industrial Revolution met the demands of large-scale productions while finding new ways to make he colors brighter and longer-lasting to wear and washing.

As textile weaving technology advanced with the advent of machines to spin, design and weave fabric, dyers were forced to be able to produce dyes with exact shades, matching color lots and most importantly, ones that would stand “to the new mechanical and chemical processing. In addition, exporters wanted colors that would stand up to tropical sunlight and still be exotic enough for foreign tastes. Dyers in turn demanded from their suppliers purer chemicals and dyestuffs of consistent quality. Hand in hand, dyers, manufacturers, chemists, and dyestuff producers worked hand in hand to keep up with the progress of technology. Chemists in many countries had

36

found a means of extracting highly concentrated powders or pastes from traditional dyestuffs that made stronger colors, such as cochineal carmine and madder garancine. Other procedures were used to extract indigo that gave us sulphonated indigo and Saxon blue. A few novel dyes (precursors of future chemical dyes) such as the yellow obtained from picric acid also made an appearance. With the tremendous rise in the interest of Chemistry in the mid nineteenth century, several important innovations in dyeing came about. W.H. Perkins, a student of celebrated European scientist Wilhelm von Hoffman, accidentally discovered the first synthetic dye in an attempt to synthesize quinine. The 18-year old student’s purple precipitate, later called mauviene, was quickly put into industrial application, allowing the young Perkins to start his own factory in London to commercially produce his dyestuff. Two years letter a synthetic red dye called magenta or fuchsine was patented in France, and hardly a year passed until the end of the century without a new synthetic dye being patented.

Eventually, the old natural dyes lost popularity in favor of the newer synthetic ones. By the end of the nineteenth century a few Scottish tweed producers were the only ones still using natural dyes, and now the use of natural dyes on a commercial scale barely exists, mainly in remote areas where people have either little access to synthetic dyes or a vested interest in retaining their ancient dyeing customs. Use of natural dyes is gaining popularity again with the renaissance in hand crafting, most notable in the fields of spinning and weaving, basketry, papermaking and leather craft. There is also renewed scientific and historic interest in natural dyeing, both to help identify dyestuffs in recently discovered archaeological finds and to preserve the dyed textiles housed in museums and private collections. As Su Grierson says in her book Dyeing and Dyestuffs, “Whilst the dyeing industry of today keeps pace with modern science, the future use of natural dyes will also follow a new path, but one firmly rooted in tradition.”

3.3 MODERN CONCEPTS OF THE THEORY OF DYEING It appears that the mechanism of dyeing depends on the nature of both the dye

and the fibre. Textile fall into two main groups : vegetable and animals vegetable fibre is cellulose fibre, e.g. cotton, lined, flax, hemp and jute. Animal fibres are protein fibre, e.g. wool, silk and leather.

There is also a third type of fibres, the artificial and synthetic fibres e.g. rayon’s (cellulose-type) and nylons (protein-type).

Dyeing was already practiced inn ancient times and has undergo many changes in its development. The first hypothesis of purely mechanical character attempting to explain the processes underlying dyeing was advanced in 1740-41. According to this hypothesis the fibre has pores which particles of dyes penetrate at high temperature; when the dye bath cools, the pores of the fibre contract, thus fastly retaining the dye. The problem of the different behavior of dyes in respect to various kinds of the fibre was not referred to.

For about one and half a century, the dyeing process was considered was only from the mechanical stand point without paying due regard to chemical essence o the

37

process, only at the end of the 19th century, when chemistry was developed, the chemical nature of dyeing process was revealed.

New theories is come replace the old erroneous ones. thus, as a result of the work carried out by two groups of English chemist-S Neale collaborators and J. Belton, it was found that inn the process of dyeing, the was first absorbed by the external surface of the fibrous materials and than started to diffuse inside in the molecular-disperse state. this was the determining feature of the kinetics of the process.

At organic fibres, cellulose,, protein and synthetic have one feature in common; they are all macromolecules having a linear structure and more or less oriented along the fibre axis. Macromolecules contain a great number of identical or similar atoms linked by covalent bond. Most high polymers from which the fibres are composed contain active functional groups, such as hydroxyl, carboxyl, nitrile and amino groups. In cross longitudinal directions, macromolecules are interconnected by the force of intermolecular attraction and in separated cases, by chemical bonds (wool keratin). The super molecular structure of the fibrous polymer is characterized y chain having in some portion a very regular arrangement crystalline region) and a maximum density of packing and in other portions, regions with less regular arrangement (amorphous region) and a maximum density of packing and in other portions, regions with less regular arrangement (amorphous region) with loose structure.

3.3.1 Sticking of dyes to fibres:This depends on the dye and the fibre to which the dye is attached. Protein-based fibres such as wool and silk have free ionisable CO2H and NH2 groups on the protein chains which can form an electrostatic attraction to parts of the dye molecule. For example the sulphonate group, SO3 -, on a dye molecule can interact with a NH3 +

group on the protein chain.

Cotton is a polymer with a string of glucose units joined together. Indigo which is used to dye denim jeans is a vat dye. Indigo is insoluble in water. The reduced form of indigo is soluble. Cotton is soaked in a colourless solution of the reduced form. This is then oxidized to the blue form of Indigo which precipitates in the fibres. Direct dyes are applied to the cotton in solution and are held to the fibres by hydrogen bonds and instantaneous dipole-

induced dipole forces. These are weak compared with covalent bonds hence these dyes are only fast if the molecules are long and straight. Fibre reactive dyes actually form covalent bonds with fibre molecules and are therefore extremely colour fast. A dye molecule is reacted with the molecule trichlorotriazine:

38

Trichlorotriazine can react with either –OH groups (present in cotton) or –NH groups (present in wool and nylons), thus effectively bonding the dye to the fabric.

3.2.2 DYE AND DYE SOLUTIONSAll water-soluble dyes use in the textile industry is electrolytes. In the aqueous

solution dissociate into ions with positive and negative charge :(a) into the dye coloured ion and (b) into the usual colorless compensation ion with an opposite charge.

The solution properties and the behavior or dyes in course of the dyeing process are of great interest. It is established that the salt of the dyes in the solution are electrolytically dissociated and their ions may from more or less large aggregates. The possible types of dye ions association in aqueous solution, according to the data presented by E. Valko, may be represented by the following three schemes (where A and B are an anion and a cation respectively)

I II III

For the dye cation C+ (nC)n+ m(CA)nCn+

For the dye anion A- (nA)n- m(CA)nAn-

Scheme I represent the complete dissociation of the dye into ions, scheme II association of the dye into ions and scheme II aggregate particles including molecules.

39

Scheme I is typical of an electrolyte and scheme III of a colloidal particle. The intermediate from (scheme-II) called the ionic micelle is characteristic of colloidal electrolytes.

The size of dye particles in solution usually depends on the temperature as well as on the concentration of the electrolytes contained in the solution.

3.2.3 SURFACE POTENTIAL OF FIBRESWhen fibrous materials is immersed in water or in aqueous solution, important

electrochemical phenomena take place due to the absorption of certain ions from the solution or to the dissociation of ionic groups contain in the fibres. Electrical change formed on textile fibre at their immersion into water due to the electrostatic attractive or repellent forces influence the distribution of coloured ions in the solution, thus promoting the interaction with the fibre of ions having an opposite charge and on the contrary, creating an energy barrier the approach to the fibre of ions with the same charge, e.g. the protein fibre saturated with (positively charged)- NH3 groups is attract by the negatively charged (acid) dye anions. + --NH3 + D –NH2D.

Conversely, the negatively charged ions of a direct dye will be repelled by the surface potential of the cellulose fibre, this potential barrier will have to be overcome before the ions enter the fibre. Whenever a dye anion will be energy-content of dye anions can be raise by increasing the temperature of the dye solution. Hence, at higher temperature, a greater portion of dye ions will e able to overcome the potential barrier and penetrates into the fibre.

3.2.4 THE NATURE OF THE FORCE BETWEEN THE DYE AND THE FIBRE MOLECULES

The fixation of dye depends on the physical and chemical properties of the dye and on the kind and properties of the fibrous material. Evidently, the dye is retained on the fibre by the physical and chemical forces of interaction. The attractive forces between dye and the fibre molecules may be classified as follows:1. Electrostatic attraction between charged sites exists in protein and polyamide

fibres.2. Attraction by induction between ionic dyes and non-ionic dyes fibre. Induction

forces of second type above are very small and may be ignored.3. Polar van der wall’s forces such as hydrogen bonds, e.g. such polar force are to

Hydrogen adjacent molecules of water as follows :

H H H H

H-O H-O H-O H- O

Non-polar van der wall’s dispersion force, e.g. in aqueous dye-bath, non-polar bonding will occur between surface which are predominately hydrophobic.

4. Chemical forces, e.g. the sole example of a chemical bond between cellulose and de molecules is in the case of reactive dyes where a covalent bond is performed

40

between hydroxyl groups and reactive halogen containing groups in the dye molecules.

3.3 Flow diagrammatic representation of dyeing process:

3.4 CLASSIFICATION OF DYEING PROCESS

1. Mass-coloration of the molten fibers This method is for dyeing the molten fibers or plastic chips or textile polymers with pigment dyes. After that, the molten or polymers will extrude from a spinneret to form fibers. Normally, the synthetic fibers are added with white pigment in order to give a hiding power (non-see through fabrics).

Advantage: give excellent fastness

Disadvantage: very difficult to clean

2. Fiber Dyeing is the method of dyeing fibers before blending with other colors to give fancy yarns or fabrics.

Note: This is used for special purposes only.

41

3. Yarn Dyeing is the method of dyeing yarns in forms of hanks or packages dyeing. This will give Scottish’s style fabrics, carpet with many colors and styles. Note: This is used in hand loom weaving in the Northern and North-eastern parts of Thailand.4. Fabric Dyeing is the method after weaving, knitting, or non-woven to make fabrics. This is very popular method of dyeing as the dyed fabrics will be processed further to

garment industries very easily. Dyeing forms of the fabric dyeing can be used in 2 ways: 1. Open width form using the fabrics to spread without any creases and dye them.2. Rope form using the fabrics with the form like a rope (many creases and look like “a rope”)

3.5 Some people classify into:

1. Exhaustion Process

This method is using lot of water as shown in “Liquor Ratio (ratio between water and goods)” This should immerge the goods into dye solution for a long time in order to let the dye penetrate into the goods. This will lead to produce more waste water than the continuous process. Advantage: inexpensive, no need to train the worker to look after and run them properly.Disadvantage: lots of water needed, very slow process (60-120 mm/batch.) 2. Continuous Process This method is designed by putting different machinery into a sequence so that it can produce the dyed fabric in one pass.

Advantage: very fast process (10-100 m/min), small amount of water in the process. Disadvantage: very expensive, need to train the worker to look after and run them properly. Example of the open width form fabric dyeing

42

.

Examples of the rope form fabric dyeing loading and unloading reel heat exchange

5. Garment Dyeing: This method is the last process of the dyeing of goods. However, the penetration of the dye solution may not be completely passed to the fibers such as between the seams, buttons, zippers etc. Normally, it is used for

lingerie, socks, sweater dyeing etc.

43

44

4.1 DEFINATION: a chemical or formulated chemical product which enables a processing operation in preparation, dyeing, printing or finishing to be carried out more effectively, or which is essential if a given effect is to be obtained’.

4.2 NECESSITY OF AUXILIARIES IN TEXTILE DYEING(a) To prepare or improve the substrate in readiness for coloration by

– scouring, bleaching and desizing – wetting – enhancing the whiteness by a fluorescent brightening effect

(b) To modify the sorption characteristics of colorants by – acceleration – retardation – creating a blocking or resist effect – providing sites for sorption – unifying otherwise divergent rates of sorption – improving or resisting the migration of dyes

(c) To stabilize the application medium by – improving dye solubility – stabilizing a dispersion or solution – thickening a print paste or pad liquor – inhibiting or promoting foaming – forming an emulsion – scavenging or minimizing the effects of impurities – preventing or promoting oxidation or reduction

(d) To protect or modify the substrate by – creating or resisting dye ability – lubricating the substrate – protecting against the effects of temperature and other processing conditions

(e) To improve the fastness of dyeings, as in – the after treatment of direct or reactive dyes – the after treatment of acid dyes on nylon – the chroming of mordant dyes on wool or nylon – giving protection against atmospheric influences, as in UV absorbers or

inhibitors of gas-fume fading – back-scouring or reduction clearing

(f) To enhance the properties of laundering formulations (fluorescent brightening agents).

4.3 Some have more than one purposeAn auxiliary to improve dye solubility may also accelerate (or retard) a coloration process, or an emulsifying agent may also act as a thickening agent; pH-control agents may both stabilize a system and also affect the rate of dye sorption. Undesirable effects during handling, through effluent discharge to surface waters, through discharge to the atmosphere (e.g. via stenter gases), through consumer contact with the finished product (e.g. skin sensitivity) or during the eventual disposal of solid wastes (e.g. incineration or landfill)

45

4.4 CLASSIFICATION:A) Non-surfactantsB) Surfactants,

Non-surfactants Simple electrolytes, acids and bases, both inorganic and organic. E.g., sodium

chloride, sodium acetate, sulphuric acid, acetic acid and sodium carbonate, together with complex salts (such as sodium dichromate, copper(II) sulphate, sodium ethylenediaminetetra-acetate, sodium hexametaphosphate),

Oxidising agents(hydrogen peroxide, sodium chlorite) Reducing agents (sodium dithionite, sodium sulphide). Anionic polyelectrolytes such as sodium alginate or carboxymethylcellulose, used

mainly as thickening agents and migration inhibitors, also fall within the class of nonsurfactants;

So too do sorption accelerants such as ophenylphenol, butanol and methylnaphthalene, although they normally require an emulsifier to stabilise them in aqueous media.

Fluorescent brightening agents (FBAs) form another large class of nonsurfactant auxiliaries

Surfactants: Organic in nature and more complex structures

DEFINITION: ‘An agent, soluble or dispersible in a liquid, which reduces the surface tension of the liquid’ In coloration processes this reduction in surface tension usually takes place at a liquid/liquid or liquid/solid interface, although liquid/gas interfaces are also occasionally important

46

47

4.5 Classification of Dyeing Auxiliaries according to function

Dyeing Auxiliaries1. Sequestrant.2. Lubricants / Anticreasant.3. Pretreatment Chemicals4. Levelling and Dispersing Agent.5. Sewuestering, Dispersing and Levelling Agentfor Reactive dyeing.6. Antifoam.7. pH Control and buffer system.8. Desizing Agent9. Yarn Lubricant10. Mercerising agent11. Dyefixing agent12. Optical Brightener.13. Soaping Agent / Washing off Agent.

4.5.1 Sequestrant:

The most undesirable impurities in Fibre, Common salt, Glauber salt, Caustic Soda and Soda ash are the di- and tri-valent cations, e.g., Ca++, Mg ++ Cu ++, Fe+++ etc. These ions increase hardness of the process bath and generate iron oxides in the bath. Calcium and Magnesium reacts with alkali and precipitates as a sticky substance on the textile material, which creates patchy dyeing and discoloration of the fibre. The ferric oxide with cellulose and creates small pinhole on the fibres also damages the machinery by scale formation in the nozzles and base.

To overcome these deleterious effects in the scouring and bleaching bath adequate amount of sequestrant must be used. Sequestrants prevent di-and tri-valent metal ions, e.g., Cu++, Fe +++ , Mn ++, Ca++, Mg++ etc from interfering with the chemical processing of the textile material. It prevents catalytic damage of cellulosic fibres in bleaching hath during hydrogen peroxide bleaching.

48

In Dye-bath Ca++, Mg ++, Fe +++ attack the dye molecules and forms aggregates of molecules which deposits on the fabric as dye spots and also they prevent the reaction process. Dye bath sequestrant should be of different strength than that of the scouring and bleaching baths. Because some dyes have metal compounds and if powerful chelating agents are used than it will attack the metal compound of dye.

4.5.2 Lubricating / Anticreasant.

Wet processing and dye-bath lubricants are used in any operation in which rope marks, creases, crows feet buffing, abrasion can occur on textiles. In low liquor ratios, full-loaded winches and jets when heavy materials re processed, fiber lubricant is essential. The basic requirement is that is it should from a thin uniform protective coating around the fiber to lower the surface friction and flexural rigidity, thus minimizing the formation of durable creases during high temperature processing. The most suitable lubricant should have the properties so that it helps to emulsify, it does not undergo phase separation with extreme changes in pH and temperature, e.g. it is stable in high temperature and over a wide range of pH; and it should have excellent compatibility with all the chemicals in treatment bath, Suitable products are relatively hydrophobic surfactants, many of which also contain a proportion of solubilized or emulsified oil or wax.

4.5.3 Pretreatment Chemical :a. Detergent & Wetting agent for cellulosic fibers.b. Oil stain removerc. Hydrogen peroxide Stabilizer.d. Single0Bath Scouring & bleaching Agent.e. Hydrogen Peroxide Killer;f. Biopolish.

In both 1-bath and 2-bath process, a number of important auxiliaries with specific properties are necessary along with 2-basic chemicals, as shown in the blocks below, Pretreatment process Bleaching bath 2. Bath process 1. Bath process

49

Scouring/Boiling off

Detergent & WettingAgent Oil stain remove

Basic Chemical:Alkali

Bleaching Bath

Detergent & Wetting AgentAntifoaming AgentSequestrantLubricant/AntecreasantOil stain removePeroxide StabilizerBasic Chemical:AlkaliHydrogen Peroxide

Bleaching Bath

Detergent & Wetting AgentAntifomking AgentSequestrantLubricant/AntecreasantPeroxide StabilizerBasic Chemical:AlkaliHydrogen Peroxide

Peroxide killer is used after both processes for eliminating residual hydrogen peroxide.Detergent & Wetting agent or Cellulosic fibres:

The purpose of scouring is to reduce the level of fats, waxes, oils, dirt and so forth on the substrate. Apart from the aesthetic benefits of clean fabric, the major technical reason for scouring is to improve the extent and uniform of absorbency for subsequent processes, especially coloration.

In scouring 1, surface-active products function as primary, rather than auxiliary agents as the basic requirements are for good wetting power and detergency, the latter property generally including the ability to remove, emulsify and suspend the extraneous matter in the liquor. Not all good detergents possess good wetting properties; hence a combination of surface-active agents to provide both wetting and detergency may be preferable. Detergency can be significantly improved with the use of additional chemicals usually referred to as “builders” the chief of which undoubtedly alkali in the form of sodium carbonate or hydroxide.

4.5.4 Levelling and Dispersing Agent:

Unleveled dyeing problems can be of two categories: Gross unlevelness throughout the material or localized unlevelness e..g. barriness, skitteriness. There are two fundamental mechanisms that can contribute to a dyeing.a. Control of the exhaustion dye so that it is taken up evenly.b. Migration of dye after initially unleveled absorption on the fibre.c. Non-ionic agent usually from water soluble complexes with the dye, some degree

of solubilization being involved.d. Ionic agent are primarily dye-of fibre-substantive ; in the former case they tend to

form complexes with the dye and there is competition between the leveling agent and the fibre for the dye, while in the latter case the competition is between the leveling agent and the dye for the fibre.

4.5.5 Sequestering, Dispersing and Levelling Agent for Reactive Dyeing :

It increases the solubility of dyes and controls the exhaustion of dyes so that these are taken up evenly on the substrate. It effectively chelates Ca, Mg ions which otherwise create while spots on the substrate. It also sequesters other di-and tri-valent metal ions without impairing the metal complex dyes, and thus yiels uniformly dyed fabric.

4.5.6 Antifoam:Where the present and persistence of foam is a nuisance, defoaming agents or

antifoams are used. For maximum efficiency deform should be added to baths when necessary.

There two groups of defoamers one that is water-soluble surfactants and other is water insoluble emulsions of silicones of organic-based the most effective defoamers are where the water-soluble compounds are used as vehicles for silicones of organic emulsions.

50

4.5.7 pH Control and buffer system :

Many disperse dyes required controlled 4.5-5 and practically all disperse dyes give good results in this pH range and are much more sensitive to minor changes in pH. Thus there is greater awareness of the actors that not only determine pH but also helps to stabilize it against interferences, in particular, from any acids or alkalies carries over from previous process.

A buffered system is necessary for precise control of pH. By the use of that tends to resist changes arising from contaminations entering y way of the substrate of the water supply.

4.5.8 Desizing Agent:

Desizing is essentially a part of the scouring process, and rapid removal of size is very important in the present trend towards continuous preparation processes. Starch-based products and especially solubilised starches are still the sizes, most commonly used on cellulosic goods. The are most frequently removed y enzymes treatment, which since effect it affects only the starch product ensure that the cellulosic fibre is undamaged; baterial amkulase id increasingly replacing malt and pancreatic enzymes. The efficiency of desizing is often taken for granted, whereas incomplete of uneven size removal is just likely to be the cause of uneven dyeing or printing as inadequate scouring.

4.5.9 Yarn Lubricant:

In the textile industry, a smooth production process is essential for perfect results and smooth production needs yarn and sewing thread lubricants. Yarn lubricant are essential for dyed yarn used in modern knitting machine. They significantly improve the slip properties of yarn and sewing thread, increased heat resistance, better sewabilitym, reduced thread breakage and increase the lustre.

4.5.10 Mercerizing Agent:

The objective of mercerizing is to oil the cotton fibre, increase its lustre strength and dyeability. Traditionally a cold solution of 25-26% by mass of sodium hydroxide is used, although better penetration and more even treatment is obtained with the more recent hot mercerizing technique. The addition of a wetting agent to the mercerizing liquor give better penetration and more even treatment, the main requirements being for a combination of stability and powerful wetting action.

4.5.11 Dye Fixing Agent:

Properties of a good fixing agent includes good capability with cross linking agents without promoting yellowing effect; good leveling and migration properties, does not affect the shade, has good affinity for the fiber, stable to steaming and dry heat, and improved all round fastness properties of the fabric or yarn. Fixative is generally used after completing the dyeing or in printing paste.

51

4.6.12 Optical Brightener:

An Optical Brightening Agent (OBA), also called Fluorescent Brightening Agent (FBA) or Fluorescent whiteners (FW), are strongly fluorescent substance that emits light in the blue-violet region of the visible spectrum. In the Color Index, OBA or FBA’s are classified and are given C.I. number, i.e. they are treated as dyes. When present on a substrate, OBA increase the apparent reflectance of the substrate and makes it appear “whiter than white”. To evaluate an OBA it is necessary to apply the product and measure the whiteness, preferably with a spectrophotometer.

4.5.13 Soaping Agent / Washing off Agent:

The important of proper washing after dyeing is painfully known to all dyers, particularly the difficulty in washing off the unfixed dye in order to meet the required fastness standard. The main functions of soaping agent are to:a) Disperse the unfixed substanted hydrolyzed dyes, and solubilise and emulsify these into the aqueous medium and keep these substances in suspension.b) Prevent redeposition of hydrolyzed dyes and other particles of colloidal substance into the textile material.c) Removes the alkaline earth metal ions which have already deposited on the dyed material.d) Prevent the precipitation of insoluble calcium or magnesium salt.

4.5.14 Finishing Chemicals:

The Quality of softness is very difficult to define, although it is often confused with only lubricity. Softness is more than lubricity, but these other attributes are difficult to define scientifically. The various products used soften are divided into silicone, anionic, non-ionic, amphoteric and reactive types, all of which falls under two basic chemical classes: (a) Fatty acid derivatives and (b) silicon derivatives, by far the most important softness today are the silicon derivatives and fatty acid cationic types; however non-ionic softeners is used for textile materials because of its non-yellow effect and compatibility with OBA. Relevant properties of softeners include aqueous solubility, exhaustion, durability to washing, and compatibility with other additives to the textile materials

4.6 Water in the Textile and Carpet Industry

Quality of process water is very critical and important for a successful dye and print operation. Especially water hardness is of importance. Hard water will result in higher usage of chemicals, thickeners and in bad results of dyeing and printing. A water softener is recommended and in any way needed for the water used by the steam generator. In case of high concentration of other minerals, elements and impurities it is strongly recommended to use filters, chemicals and other methods to reduce or remove them.

52

4.7 Thickeners (Gum)

As regards quality played by the flow behavior of the printing paste. This is influenced by the thickener used. There is an extensive range of products available for a wide variety of fibers, carpet qualities, dye classes and printing methods .Thickener is a must in the printing process. It keeps the\dyestuff on top of the fiber to avoid 'frosting'. In addition it prevents the dye from migrating between the piles.

4.7.1 Thickener for screen printing:

Most thickeners for screen printing are made of Guar, Xanthan, seaweeds (= natural thickener).These type of thickeners are relatively in expensive. The thickener is normally mixed to a so called 'stock thickener'- thickener with a very high viscosity which is then mixed in a certain portion (about 30-50%) with water, dye and other additives. The result is there a dye made print paste with a certain viscosity. The viscosity depends on the printing process and the quality of the carpet.

4.8 AUXILLIARIES USED WITH DIFFERENT DYES:

4.8.1 Dyes for Cellulosic Fibers:

Direct Dyes (Anionic): They can be dyed directly on cellulosic fibers. Without the presence of salt, when the fibers are immerged in water, it will show

53

anionic charge which repels the dyes. Adding salt into the dye bath, it will reduce anionic on the fibers so the dyes can get closer and adsorb into the fibers. Advantage: cheap, easily dyed on fibersDisadvantage: poor wet fastness and some dyes have poor light fastness.

Textile Auxiliaries:1. Salt - reduce negative charges on the fibers 2. Water - dyeing media 3. Fixing Agent - enhance wet fastness but usually reduce light fastness

Dyeing Conditions:(Exhaustion): dyeing lOOoC x 30-90 mm fixing 6OoC x 20 mm.(Continuous) pad --> dry --> steam --> wash --> soap --> dry

Reactive Dyes (Anionic): They can be dyed on cellulosic fibers. The mechanism is nearly the same as described in direct dyes.

Advantage: high wet fastness due to covalent bonding (Chemical Bonding) between fibers and dyes, easily dyed on fibers.

Disadvantage: Expensive.

Dyeing Conditions:

1. Continuous Process:

1.1 Pad-dry-bake This is very easy method for cotton or cotton blends fibers.1.2 Pad-dry-Pad (Chemical)-Steam This will give brighter and more intense color than method 1.1.1.3 Pad-batch This will put the goods into the dye solution and squeeze with 2 rubber rollers to get rid of excess water and then batch at room temperature for 1-2 days. 2. Exhaustion Process: This method will be used in small factory. Dyeing conditions will be 40-8OoC for 30-90 mm depending to the types and structures of the dyes.

Textile Auxiliaries: 1. Salt - reduce negative charges on the fibers 2. Water - dyeing media. 3. Soda Ash - excite the dye to link with the fibers with covalent bonding. Therefore, it enhances wet fastness 4. Fixing Agent - enhances wet fastness for heavy shade but usually reduce light fastness. Vat Dye (Anionic when soluble):

The dye is named from the container (Vat) that used for rotting the dye with alkali solution. This crucial process will reduce the dye from insoluble to soluble dye (suitable for exhaustion in the cellulosic fibers). Now the manufacturer can synthesize man-made vat dye.

Dyeing Process:

54

1. Dissolve dye into water (insoluble dye) 2. Vatting process by reducing the insoluble dye in alkali condition. (Soluble dye) 3. Absorb into fibers (soluble dye) 4. After dyeing, oxidize the dye with oxidizing agent (insoluble dye) 5. Wash and soap the goods

Dyeing Conditions:

1. Continuous Process:

1.1 Pad-dry-Pad (Chemical): The solution of the dye is prepared without adding reducing agent to ensure leveling dyeing. After that, the goods are passed to chemical bath to reduce the dye into soluble dye and fix within the goods. Oxidizing agent is added to the goods and converted to insoluble dyes. 1.2 Pad-oxidize-pad-oxidize (many times): This will put the goods into the dye solution and squeeze with 2 rubber rollers to get rid of excess water, oxidize with the air and then immerse into the dye solution again and again to allow the dye penetrate into the goods.

Textile Auxiliaries: 1. Salt - reduce the negative charges on the fibers 2. Sodium hydroxide - adjusts pH to the dyeing bath and makes the suitable conditions for reducing agent.3. Sodium hydrosulfite - reducing agent for the vat dyes. 4. Water - dyeing media 5. Oxidizing agents - (Hydrogen peroxide or Acetic acid or Air) oxidize the soluble to insoluble dye

(Sulfur Dye Anionic when soluble) :The dyeing process has the same process as described in the vat dye except that using Sodium sulfide instead of Sodium hydrosulfide.

Dyes for Synthetic Fiber:

Disperse Dye (polyester, nylon, and acetate) (non-ionic): The dye is named from less water soluble and normally appeared in dispersion in water. The dye shows no charge due to the groups presented in the dye molecules.

Dyeing Conditions:1. Insoluble dye in water 2. Less water soluble 3. Water insoluble in polyester fibers

1. Exhaustion Process:

55

1.1 At boil with carrier, this process is suitable for acetate fiber and pale shade polyester fiber dyeing. Carrier is an auxiliary for swollen fiber in order to allow more dyes absorbing in. Now the use of carrier is reduced because it may be a carcinogen. 1.2 At l3OoC without carrier with the high temperature, the dyes will be dissolved into smaller molecules and the void in fiber structure will be opened. This will give heavy shade. 2. Continuous Process Pad --> Pre-dry (100oC Thermo fixation (18OoC reduction clearing (RC)

Printing with Disperse Dyes: With the sublimation property, the dyes can be printed on paper, place the fabric with a printed paper and then using an iron with high temperature pressed on the paper. The dyes will transfer from paper to polyester fiber. This is called “Transfer Printing”.

Textile Auxiliaries: 1. Dispersing Agent - makes the dye solution stable and disperses in the dye bath.2. Acid - adjust pH to the suitable condition for the dye bath. 3. Carrier - swell the fiber and dissolve the dye to make the dye getting into fiber. 4. Leveling agent - make more leveling dyeing (some will have adverse effect on slower dyeing) 5. Water - dyeing media

Acid Dye (Anionic): The dye is called acid because it needs acidic dyeing condition. It can be dyed on protein fibers (silk, wool, and other animal fibers) and on polyamide fibers. Acidic condition will give the fibers showing positive charge. As the negative charge will attach directly to positive charge, and penetrate into the fibers. Dyeing conditions: l00oC x 30-60 mm

Textile Auxiliaries: 1. Leveling agent - for levelness dyeing.2. Retarding agent - for inhibiting the dye not attach to fibers too fast.3. Acid - adjust the dyeing condition and make the fibers to show positive charges.4. Water - dyeing media.

Basic Dye (Cationic) The dye shows positive charge. Normally, the dye can be applied on wool, silk and poly-acrylonitrile (acrylic). Dyeing Conditions: l00oC x 30-60 mm Dyes Dyeing Condition (pH) Acid (Wool) 2-4, 4-6, 6-8 (depends on types of dyes) Acid (Nylon) 4.5-5.5, on types of dyes) Basic 3.5-4Direct 7.0 Disperse (Polyester) 5-6 Disperse (Acetate) 6.5-7.0Disperse (Triacetate) 4.5-6.5Reactive 7.0 (Exhaustion) 11.0 (Fixing)

56

Textile Auxiliaries:1. Leveling agent - for levelness dyeing.2. Retarding agent - for inhibiting the dye not attach to fibers too fast.3. Acid - adjust the dyeing condition and make the fibers to show negative charges.4. Water - dyeing media.

57

5.1 Synthesis of Reactive Auxiliaries for Dye Resist Treatment of Wool

5.1.1 Abstract: Three reactive auxiliaries containing s-triazine-based reactive groups were synthesized and the dye resist effects achieved on wool were evaluated. The results obtained indicated that, the dye resist 2 effect achieved with the bi-functional reactive Auxiliary (R ) was exhibited the highest value. The effect of the dye bath pH, salt concentration, dyeing temperature, dyeing time, conc. of dye and conc. Of auxiliaries were also studied. Good fastness properties of the dyed fabric were achieved.

Keywords: Reactive auxiliaries, dyeing wool, dye resist, colour strength, fastness properties

5.1.2 INTRODUCTION

Auxiliary products of various types are commonly used in the dye bath during the low temperature dyeing of wool. Such [1] chemicals are used to promote dye bath exhaustion and to achieve level dyeing[2]. A resist process may be defined [3] as one which modifies a textile fiber in such away that when the resist treated fiber is subsequently dyed, it absorbs dye to a lesser extent or at a slower rate than untreated fiber. Various treatments have been proposed for imparting dye resist effects to wool, for example, sulphonation,acetylation, glyoxylation, deposition of polymers, alkaline chlorination and treatment with formaldehyde,sulphamic acid[4,5], tannic acid /metal salts, synthetic tanning agents[6,7,8] and also colourless reactive compounds[9,10]. Among them reactive dye resist agents are preferred due to their easy handling and application[10]. A viable dye resist agent must be completely cured and bound firmly to the wool substrate in order to achieve satisfactory dye resist effects[11]. Increasing the substantivity between the substrate and the dye resist agents is one of the most important factors needed to improve dye resist effects.In order to increase this substantivity one possible effective dye resist method would be to covalently bind the dye resist agents to the wool substrate using suitable fiber reactive groups[11]. In this work we synthesized three reactive auxiliaries containing s-triazine based reactive groups which were used for treating wool. Three acid dyes containing different number of sulphonic acid groups were used for dyeing treated wool.

5.1.3 MATERIALS AND METHODS

Material and Chemicals: Scoured and bleached wool fabric with the following characteristics was purchased from Misr for Spinning and Weaving Company, Mahalla El-Kobra, Egypt; weight 205 gm-2, 72 ends per inch, 64 picks per inch. Before using, the fabric was treated with a solution containing 5g L-1 non-ionic detergent (Hostapal CV, Clariant), at 50 oC for 30 min.Then, the fabric was thoroughly washed with water and air dried at room temperature. Diamino benzene sulphonic acid (95% assay), cyanuric chloride (99% assay) and sulphanilic acid (99% assay) were supplied by Aldrich.All other chemicals employed were of analytical grade. The codes, the chemical names and chemical structures of the synthesized reactive auxiliaries are given in table (1).

58

Dyes: Three acid dyes which have different numbers of sulphonate groups were used (fig.1). The commercial names and color Index names for these dyes are given in table (2).

Reactive Dyes for Purification of Chemicals:

Cyanuric Chloride: Cyanuric chloride [1 2 ] was crystallized from petroleum ether (b.p90-100 ºC), and dried under vacuum at room temperature.

Sulphanilic Acid: 100 gm of sulphanilic acid in about 500 ml sodium carbonate solution was boiled then filtered and made strongly acid with hydrochloric acid. The solution was then neutralized with 1N sodium carbonate. The hot solution was cooled to 0 ºC with stirring and the precipitate of sodium sulphanilate was filtered off. The crystals were dissolved in 500 ml distilled water and the solution was filtered and then acidified with concentrated hydrochloric acid. The material was then re-crystallized from hot distilled water and dried at 120 ºC overnight.

59

1-amino -8 naphthol -3, 6 disulphonic acid (H acid):

Sodium carbonate (20gm) was added to a solution of 100 gm of (H acid) in 750ml of hot distilled water, followed by 5gm of activated charcoal. The suspension was stirred for 20 min and filtered by suction. H acid was precipitated by adding 50 ml of conc. HCL, then filtered by suction and washed with distilled water. The Mother H acid was dried overnight.

Procedures:

Synthesis of 2,4 dichloro – s -triazine -6- yl- p- 1 amino phenyl sulphonic acid sodium salt(R )[13]:

Sulphanilic acid (20 gm in 100 ml water) was added slowly to cyanuric chloride (22 gm in 200 ml acetone containing about 100 gm ice) whilst maintaining the pH of the solution at 7 by the addition of 2 N sodium carbonate. the reaction mixture was stirred for 1.5-2h the product was filtered off, washed thoroughly with acetone and then oven dried.

Synthesis of 2, 5-Bis (2, 4 dichloro-s-triazine-6-yl) - 2 amino phenyl sulphonic acid sodium salt (R):

Cyanuric chloride (20 gm) in acetone (100ml) and ice was added to a solution of 2,5- diamino benzene sulphonic acid(10 gm) as a slurry, whilst maintaining the pH at 7 by the addition of a solution of saturated sodium carbonate. The reaction mixture was stirred for 3h and the product was filtered off, washed thoroughly with acetone and then oven dried.

Synthesis of 2, 4- dichloro-s- triazine-6-yl-amino-8- 3 naphthol 3, 6 disulphonic acid sodium salt (R) [14]:

20 gm (H-acid) was dissolved in 1N sodium bicarbonate solution, the solution diluted to 250 ml and neutralized with acetic acid. this solution was dropped simultaneously into a well stirred suspension of finely divided cyanuric chloride (10 gm)in acetone and ice water (2:1)at 0ºC over 3h when pH was stable at 7 the reaction was complete, the product was filtered off and dried at room temperature.

Characterization of Products: Melting points were measured by a Gallankamp Melting Point Apparatus. IR Spectra were obtained (KBr discs) on Pue Unicam Spectra 1000.1HNMR Spectra were measured on 3 2 avarian 400 MHz Spectrometer for solutions in (CD) 4 SO using SiMe as internal standard.Mass Spectra were performed on HP model MS-5988. Microanalyses for C, H and N were performed on Avario Elementry (table 3). Analytical data were obtained from the service laboratory center in NRC.

5.1.4 Application of Reactive Auxiliaries: The wool samples were treated with each compound at various concentrations (1, 2, 4, 8 and 16% oww) by an exhaustion process using liquor ratio of 20:1. Auxiliary were added and the process was started at

60

40 °C and run for 20 minutes, during which pH 4 was established, salt ammonium sulphate (1% oww). Then the bath was raised to the boil over 30 minutes and held for 60 minutes at 100 ºC. Afterwards, samples were rinsed for 15 minutes and dried at room temperature.

5.1.5 Determination of Mass Gain: Weight gain was determined on the basis of oven dry weight, measured before and after the application of the reactive auxiliaries.

Fig. 2: The effect of pH on resist effectiveness of 1 2 3 auxiliaries (R , R , R ), conditions: temperature100 0 C, time 40 min., dye conc. 3%,conc. of salt 1%and conc. of auxiliaries 4%.

Fig. 3: the effect of the temperature on Resist 1 2 3 effectiveness of auxiliaries (R ,R ,R ), conditions : pH 4, time 40 min.dye conc. 3% ,conc. of salt 1% and conc. of auxiliaries 4%.5.1.6 Dyeing of Wool Fabric: The resist effectiveness of reactive auxiliaries on wool was evaluated using the three dyes listed in table (2). Dyeing process was carried out in a dye bath containing ammonium sulphate (0.5-2.5% oww), using a liquor ratio of 20:1 at pH (3-8 ),the dye bath temperature (40- 100 ºC ) and dyeing

61

time(20- 90 minutes) and dye conc. (1- 4 %). Afterwards, samples were rinsed for 15 minutes and dried at room temperature.5.1.7 Dye Resist Evaluation: To evaluate dye resist effectiveness, the treated wool samples were dyed in a competition with untreated wool (differential dyeing technique,DD), we quantified the dye resist effectiveness (RE) of the different auxiliaries by calculating RE values from the reflectance values (K/S) of the dye treated and untreated wool samples.K/S values were obtained at the wavelength of maximum dye absorption: untreated treated [(K/S ) - (K/S )]%Resist = ------------------------------- x 100Untreated (K/S)

5.1.8 RESULTS AND DISCUSSIONS

Dyeing:

Effect of Dye Bath pH: Figure 2 shows that the pH values of the dye bath have a considerable effect on the dyeability of wool fabrics with dye resist technique, 1 2 3 DD process using the auxiliaries R , R and R and acid red 27. The effect of the dye bath pH can be attributed to the correlation between auxiliary structure and wool fabric. It can be seen from the results given 2 in fig (2) that the R treated wool achieves a higher 3 1 dye resist at the same pH value than the R and R treated wool. One might be attempted to deduce that 2 this differences arises because R reactive resist contains two s- triazine reactive moieties which leads 2 to a higher degree of fixation of R at pH 4 to the wool fiber. As clearly observed in figure (2) it was noticed from the figure that higher dye ability at pH 4 and then the dye ability decreases as the pH increases.

Effect of Temperature: The effect of temperature on the dye ability of wool fabrics with dye resist technique, 1 DD process using the auxiliaries R , R and R and acid red 27 was conducted at different temperatures (40-100oC). As shown in figure (3), it is clear that the dye resist increases with increasing dyeing temperature for the three used auxiliaries R, R, R and reaches maximum value at 100oC.

62

Fig. 4: The effect of time on Resist effectiveness of 2 3 auxiliaries (R, R, R), conditions: pH 4, temperature100 0 C, dye conc. 3 %, conc. Of salt 1% and conc. of auxiliaries 4%.

Fig. 5: The effect of conc. of salt on Resist 2 3 effectiveness of auxiliaries (R , R , R ), conditions: pH 4, temperature100 0 C, time 40 in, dye conc. 3 %and conc. of auxiliaries 4%.

63

Fig. 6: the effect of the conc. of dye on Resist 2 3 effectiveness of auxiliaries (R, R, R), conditions: pH 4 temperature100 0C, time 40min., conc. of salt1%and conc. of auxiliaries4%.

Fig. 7: The effects of conc. of auxiliaries on Resist 2 3 effectiveness of auxiliaries (R, R, and R), conditions: pH 4, time 40 min., temperature 100oConc. Of salt 1% and dye conc.3% of acid red 27.

Effect of Dyeing Time: The effect of time on the dye ability of wool fabrics with dye resist technique, 2 3 DD process using the auxiliaries R 1 R2and R3and cid red 27 was conducted at different temperatures 20-90 min.). As shown in fig. (4), it is clear that the dye resist increased as the dyeing time increase up to40 min, and then it began to decrease.

64

Effect of the Salt Conc.: The effect of conc. of salt on the dye ability of wool fabrics with dye resist technique, DD process using the auxiliaries R, R and3 R and acid red 27 was conducted at different conc. (0.5-2.5% oww). As shown in figure (5), it is clear that he dye resist increases with increasing conc. of salt and reaches maximum value at 1% oww and then it began to decrease.

Effect of the Dye Bath Conc.: The effect of the dye bath conc. on the dye ability of wool fabrics with dye resist technique, DD process 1 2 3 using the auxiliaries R , R and R was conducted at different dye bath conc. (1-4% oww) of acid red 27. As shown in figure (6), it is clear that the dye resists increase with the increasing of dyeing concentration and reaches the maximum value at 3% of dye concentration.

Effect of the Conc. of Auxiliaries: The effect of the conc. of auxiliaries on the dye ability of wool fabrics with dye resist technique, DD process using the 1 2 3 auxiliaries R, R and R was conducted at different conc. of auxiliaries (1, 2, 4,8 and16%oww). As shown in figure (7), it is clear that the dye resistant increases with the increasing of the concentration of auxiliaries and reaches the maximum value at (4% oww) of auxiliary concentration.

DD and DR techniques: After reaching the optimum 1 conditions for dyeing treated wool using R, R2, R3, to obtain maximum dye resist effect, we investigated the effectiveness of the auxiliaries using two different dyeing processes at the same conditions. The treated wool was dyed separately (dye resist technique, DR) to estimate the overall dye resist effect. On the other hand treated wool samples were dyed in competition with untreated wool (differential dyeing technique, DD) to estimate the differential dyeing behavior. The three acid dyes listed in table (2) were used. The obtained results suggest that the dye resist 2 effect achieved with the bi-functional reactive resist (R ) was superior to that achieved by the mono-functional 1 reactive resist (R ).The explanation for this difference might be that there are cross links introduced by the

65

Auxiliaries Alt: alteration Sc: staining on cotton Sw: staining on wool 0: sample without treatment of auxiliaries

Fig. 8 a,b: Resist effectiveness of R versus auxiliary uptake of the fibers

66

67

Fig. 9a,b: Resist effectiveness of R versus auxiliary uptake of the fibers.

68

Fig. 10a,b: Resist effectiveness of R versus auxiliary uptake of the fibres bi-functional groups of (R ),increasing the substantivity between the substrate and the dye resist agents which is one of the important factors needed to improve dye resist effects. Figures (8, 9, 10) show the resist effectiveness of the three auxiliaries used, depending on the amount of auxiliary fixed to the fibers. At low auxiliary uptake, the three compounds differ greatly 2 from each other. At equal weight gain, R shows a 3, 3 better resist effect than R and R in turn have better 1 resist effect than R . Above an uptake of 7.2%, the resist effectiveness of the auxiliaries tends toward a limiting resist value for the three dyes used. It must be concluded that other factors such as molecular configuration, in addition to ionic/ hydrophobic mechanism, could affect the achieved weight gains, since the inductive effect of the electron withdrawing nitrogen on the s- triazines activates the reactive centers on the carbon atoms of s-triazines more than those of other hetero-cycles. Moreover, the electro negativity of the leaving groups adjacent to the reactivity of the reactive centers. Also molecular structures of the dyes used have an effect on the dye resist values obtained. Acid red 27 gives higher values of dye resist that is because this dye contains three sulphonic acid groups, thus strong electrostatic forces are built up between treated fibers and dye, which leads to an efficient electrostatic repulsion of the dye molecules. The dye is not absorbed quite readily and is not able to penetrate into the fibers [17]. It can be seen from the results given in 2 fig (8, 9, 10) that the R treated wool achieves a higher 1 weight gain than the R treated wool. One might be attempted to deduce that this differences arises because2 R reactive resist contains two s- triazine reactive moieties which leads to a higher degree of fixation of 2 R to the wool fiber.

Fastness Properties: Fastness properties of the dyed fabrics are shown in table 4.The results indicated that 1ated wool with the three auxiliaries R ,R ,R using the three acid dyes give good to very good results for 2 rubbing, perspiration, light and washing fastness R 1 3 shows better fastness properties than R and R with the three acid dyes.

5.1.9 Conclusion:

69

Three reactive auxiliaries containing striazine- based reactive groups were synthesized and the dye resist effects achieved on wool were evaluated using two different techniques DR, DD. The obtained results suggested that the dye resist effect achieved with the bifunctional reactive resist was superior to that achieved by the monofunctional reactive resist and the DD technique gives better dye resist effect than DR one. Good fastness properties of the dyed fabric were achieved.

5.2 The Effect of UV Absorbers on Ultra Violet Protection Properties of Dyed Cellulosic Fibres.

5.2.1 Abstract

Several reactive dyes derivatives of C.I. Reactive Red 198 have been prepared. Three of these dyes included additional UV-absorber systems based on 2’-hydroxy-benzotriazole. The spectrophotometric properties of the dyes obtained were measured, and their application properties on three different types of cotton fabric were examined. It was found that newly-prepared dyes could be applied to the cotton fabric by the pad dyeing method, which gives a higher dyeing efficiency than the exhaustion method. the type of the fabric used has a significant influence on the measured UPF value. It was found that the new products gave excellent UV protection properties to dyed textiles, although only minor improvement was observed in comparison with the reference dye.

5.2.2 Introduction

In practice, the UV protection properties of textiles are characterized by the UPF value of a particular fabric. UPF is the abbreviation of the Ultraviolet Protection Factor, The UPF of textiles depends on their chemical composition and physical structure (thickness, porosity, method of manufacturing). The second important factor which affects the UPF of textiles is the presence on the fabric of various chemicals such as dyes and other auxiliaries. It was experimentally found that among natural fibres the best protection against UV radiation is given by wool. On the other hand, from the practical and aesthetic viewpoints, in summer we usually wear clothes which are made from undyed cotton, a natural fibre which provides only little protection from the ultraviolet radiation. The introduction of dyes and other auxiliaries which possess their own significant absorption in the UV region can increase the protection properties of this fibre. In practice, a series of special UV absorbers are used in order to protect textiles and to improve the light-fastness of the coloured fabrics. These compounds absorb the harmful UV radiation in the region of 250-400 nm and rapidly convert it to harmless heat. Among various chemical structures, one of the most important groups are 2’-hydroxyphenyl-benzotriazoles such as Tinuvin 326 (Figure 1), commercialised by Ciba-Geigy [4]. This product is widely used for polyester fi-bres dyed by the exhaustion method. The specific nature of the hydrogen bridge for-med in the molecule is responsible for its protective properties. In the excited state of the molecule, after absorbing the part of radiation, the proton from the bridge is transferred from the oxygen atom of the hydroxyl group to the nitrogen atom of the benzotriazole ring. This leads to a new excited state with lower energy, from which the molecule can easily return to the first basic state [5]. A similar absorber (Figure 2) was designed to improve the photostability of the anionic dyes applied while dyeing

70

the wool. The sulphonic group in its molecule gives solubility in water and allows fixation of t he absorber onto the fibre [6]. At present, other special compounds are also used to increase the protective properties of coloured or undyed fabrics against UV radiation. For example, for

Figure 1. Chemical structure of the UV absorber ‘Tinuvin 326’.

Figure 2. Water-soluble UV absorber of the benzotriazole-type.cotton and cotton blends, studies recommend Cibatex UPF, a water-soluble oxalic acid dianilide with two reactive groups (no structure details known). It is applied by the exhaustion (1-4%) or pad batch methods (15-50 g/dm3) with reactive or direct dyes [3]. One interesting experiment in this area was an attempt to incorporate the UV-ab-sorbers system (of the benzophenone and benzotriazole type) to the molecule of dispersed dye (Disperse Yellow 42) used in polyester fabric. One example of such a prepared dye is presented in Figure 3. A slight improvement of light fastness in the dyeing fabric was observed in some cases of these dyes [7].

Figure 3. Disperse Yellow 42 with built-up UV absorber.

71

Thus, the purpose of our research was the synthesis and examination of the application properties of bifunctional reactive dyes for cellulose fibres which included an additional UV absorber fragment in their molecule. The structure of these dyes is presented in Figure 4.

Figure 4. The general structure of the prepared dyes

In this formula, A was a typical moderator used in the synthesis of reactive dyes such as methanilic acid (A1) in the case of the standard reference dye (C.I. Reactive Red 198), or the amino group (A2). In the case of other dyes, we used as A specially prepared water-soluble UV-absorbers, derivatives of the 2’-hydroxyphenyl-ben-zotriazole presented by structures (A3, A4, and A5) in Table In the present work, it was anticipated that cotton fabric coloured with some of the synthesised dyes would also exhibit increasing protective properties in comparison with fabric dyed with the standard dye.

5.2.3 Experimental

The UV absorbers were prepared by the methods usually used in the case of other benzotriazole derivatives. Absorber A3 was prepared by a coupling reaction of diazotized 3-amino-4-nitrobenzenesulphonic acid with 4-hydroxyacetanilide, followed by the reduction of the nitro group of the monoazo dye to the triazole ring with simultaneous hydrolysis of the acetylamino group (scheme shown in Figure 5):\

72

Figure 5. The synthesis route of the absorber A3.

A4 was prepared in a similar way to A3, but 4-methylphenol was used as a coupling agent. The resultant 2’-hydroxy-4’-methylphenylbenzotriazole-6-sulphonic acid was then coupled with diazotized methanilic acid, and the azo bond was reduced to the amino group.

Absorber A5 was prepared by coupling diazotized 2-aminophenol-4-sulphonic acid with 1,3-phenylenediamine, and the oxidation of the resultant o-aminoazo dye with copper salts in a boiling aqueous-ammonia environment

73

Table 2. Spectrophotometric properties of Absorbers A3-A5

.

Reactive dyes P1-P5 were prepared by the condensation of 1,3,5-trichloro-s-triazine (cyjanuric chloride) with 1-amine-8-hydroxy-3,6-naphtalenedisulphonic acid (H acid) at the temperature of 0-5°C and pH=1.0±0.2. The completiong of this reaction was confirmed by testing each sample on filter paper with an Ehrlich reagent. No colour present means that all the aromatic amine had overreacted with the cyjanuric chloride. Such prepared ‘triazinyl-H’ acid was then coupled with diazotized 4-(β-sulphatoethyl)sulphonylaniline (‘paraester’) at the temperature of 0-5°C and pH=7.0±0.2. The last step of the synthesis was the condensation of dichlorotriazinyl dye with amine A at the temperature of 35-40°C and pH=7.0±0.2. The latter step was monitored by paper chromatography (Whatman 3 paper, developing phase 1% aqueous NaCl). The synthesis route of the reactive dyes is presented in the scheme in Figure 6. Synthesised dyes P1-P5 were examined for their UV spectra in the UV-VIS region. .

Figure 6. The synthesis route of prepared dyes, derivatives of C.I. Reactive Red 198

Table 4. The exhaustion degree, fixation degree and total dyeing efficiency of prepared dyes.

74

All the prepared dyes were subjected to application examinations, during which the following cellulose fabrics were used:

bleached cotton fabric with linen weave, weight 107 g/m2 (Fabric X);bleached cotton with linen weave, weight 104 g/m2 (Fabric Y);bleached cotton satin, weight 119 g/m2 (Fabric Z).

Dyeing was carried out by the exhaustion method (1% and 2% dyeings, dyebath ratio 1:20 in the presence of 50 g/dm3 sodium chloride and 20 g/dm3 sodium carbonate). The percentage degree of exhaustion was calculated from spectrophotometric measurements according to formula

2

1

BE=(1- )×100%

B (1)

Where: B1 – the absorption of the dyebath at λmax before dyeing;B2 – the absorption of the dyebath at λmax after dyeing.The results of these measurements are listed in Table 4.

Each fabrics was also coloured with the same dyes by the use of the pad dyeing method. Each bath contained the following elements: 1 g dye, 10 g of urea, 1 g NaHCO3 , 5 cm3 10% solution of 3-nitrobenzenesulphonic acid sodium salt (Nitrole S), 5 cm3 5% solution of sodium alginate, and was completed to 50 cm3 with distilled water). The fixation of the dyes was carried out at the temperature of 130°C over 5 minutes.

In order to more precisely characterise the prepared dyes, their fixation on the fabric X was measured. Any unfixed dye was stripped from a sample of dyed fabric by repeated hot extraction with pyridine-water azeotrope. After drying, the fabric sample was then dissolved in concentrate sulphuric acid and poured onto a water-ice mixture.

75

The concentrations of dyes in these solutions were measured spectrophotometrically. The same procedure was repeated with the samples of the dyed fibre which were not extracted with the water-pyridine system. The percentage degree of fixation was then calculated from formula (2):

(2)where: C1 – the absorption of the dissolved sample of the fabric without extraction with the

pyridine-water azeotrope, C2 – the absorption of the dissolved sample of the fabric extracted by the pyridine-

water azeotrope. The total efficiency of the dyeing process was calculated from formula (3):The results of these measurements are listed in Table 4.Finally, the dyeing textiles were examined for their protective properties according to the European Standard. The measurements of UV transmittance were carried out with the double beam Beckman DK-2A spectrophotometer equipped with an Ulbricht sphere and powered by a hydrogen lamp. The UPF factor was calculated from formula (4):

(3)where: E(λ) - the solar spectral irradiance, W/m2nm;ε(λ) - the erythema action spectrum;Ti(λ) - the spectral transmittance sample i at the wavelength λ;Δλ - the interval of the wavelength, nm.The results obtained are presented graphically in Figures 10 and 11.

5.2.4 Results and Conclusions As can be seen from the results presented in Figure 7 and Table 2, all the examined absorbers exhibit significant absorption in the near UV region as was expected. The A4 absorber has the broadest absorption band, so one may expect the best increase in UV protecting properties after building it up to the dye molecule. Similar properties might also be expected in the case of absorber A3, which possesses the highest value of the molar absorption coefficient.

76

The analysis of the data presented in Figure 8 and in Table 3 shows that introducing other moderators than metha-nilic acid to the dye molecule, such as am-monia, results in only a small decrease in their molar absorption coefficients εmax, in comparison with the standard dye P1. Some decrease in the absorption intensity in the UV-B ultraviolet region absorption spectra (280-315 nm) is also visible, probably due to the absence of the aromatic ring of the methanilic acid in P2.

The absorption curves of the dyes P3-P5 presented in Figure 9 show that incorporating the 2’-hydroxybenzotriazole system into the dye molecule results in the increase in absorption in the UV region, which is especially visible in the case of dye P5, and also in the case of dye P4. On the other hand, due to the radical increase in the molecular weight of these dyes, their molar absorption in the visible region is much lower than in the case of the reference dye P1. The decrease in colour intensity of the newly-prepared dyes is much greater than was expected. All the factors mentioned above also influence the application properties of the prepared dyes. As can be seen from the data presented in Table 4, in several cases (Dye P4), probably due to the structural disturbance of the dye molecule, the degree of exhaustion on the coloured fabric is visibly decreased. More comparable results were obtained during the pad dyeing method with an average dyeing efficiency of 80–90%. For this reason, prepared dyes could more readily be used in this method, or in the printing of cellulose fibres. Figures 10 and 11 present the values of the UPF factor calculated from the measurements of transmitted UV radiation through the cotton fabrics used. As it mentioned earlier, the results again show that the physical properties of the examined fabrics have a crucial influence on their UPF factor. The higher protection properties of the uncoloured fabric are increased to a much greater extent after the dyeing process. This is especially visible in the case of Fabric X and Fabric Z, where an increase from ‘moderate’ and ‘good’ to ‘excellent’ protection can be observed for several dyes.

Comparing the new dyes with the reference C.I. Reactive Red 198 (P1), one may note that dye P3 gives the best UPF factor for the exhausting method, while in the pad dyeing method the best results are obtained for the dye P4, although both these values are practically very close to those of the reference dye. However, if one considers the fixation degree on the fibre of the reference dye in comparison with the new dyes, improvement of up to 10% of the UV-protecting properties may be observed in the latter case. This result is however rather unimportant from the practical point of view, so one may rather consider the use of new benzotriazoles as the components of fibre-reactive, colourless UV absorbers, as we suggested in our earlier work.

5.3 Influences of Non-ionic Auxiliaries on Absorption of Acid Milling Dyes & on Colour Characteristics of Wool Fibre.

5.3.1 Abstract:

The influence of non-ionic auxiliaries on absorption of the acid milling CI Acid Blue 80 dye on wool fibre and on the colour changes of dyed fabric has been investigated. The kinetics of dye absorption and the colour characteristics of dyed fabric, including washing fastness, were determined. A non-ionic surfactant based on poly-ethoxylated

77

alkylphenol enables dyeing at low temperatures, colour characteristics and wash fastness to be improved, whereas the alkylaminoethoxylated product enhances the dyeing rate at higher temperatures. The variation of colour yield values in the dyed fabric which occur due to the use of non-ionic auxiliaries or the difference in dyeing temperatures is explained and discussed

5.3.2 Introduction:

Higher-affinity dyes, such as acid milling dyes with larger molecules, do not penetrate into the wool fibre at lower temperatures, and dyeing unlevelness or ring dyeing becomes a major problem. Ring dyeing can give problems such as reduced fastness, shade change, or poor rubbing fastness. Localized unlevelness is primarily related to the physical and/or chemical non-uniformity of the substrate; a typical example of this is skitteriness in wool dyeing. One of the fundamental mechanisms that can contribute to level dyeing is the migration of dye after initially unlevel sorption into the fibre [1]. As a fibre, wool is heterogeneous, both chemically and physically. In the case of wool without the damage in cuticle cells, it is assumed that the dye uptake in the early stage of adsorption is subject to the dyeing behavior of the intercellular regions of the cuticle-cuticle (surface) layer [2]. Dye most readily enters the fibres by diffusion through the intercellular region between the scale cells of the wool fibre, penetrates fairly rapidly into the non-keratinous endocuticle region of the surface layer, and soon reaches equilibrium with the dye in the outer solution. Within the cuticle cells, the endocuticle and then the exocuticle become coloured, as the dye travels through the intercellular cement and penetrates into the cells from their undersides [2]. It has been established that an increase in dye bath exhaustion and the improved levelness of dyeing with selected milling acid dyes could be obtained when sparingly water-soluble organic compounds are added to the dye bath, or wool fibres are pre-treated before dyeing.

Riva et al have investigated the influence of pre-treating wool with a non-ionic auxiliary on dye sorption, and assumed that the enhancement of the increase in dye bath exhaustion and the faster rate of dyeing are due to the sorption of the auxiliary by the wool [4]. The partial solubilisation of free fatty acids of a lipid layer of cellular membrane complex (CMC) due to the treatment of the wool with non-ionic polyglycol ethers and the modification of the hydrophobic domains of the CMC in wool fibres were proved.

In the present work we examine the influence of how acid dye is taken up by wool fabric on the changes in colour characteristics that occur thanks to applied non-ionic auxiliary dyeing agents and temperature.

78

Figure 1. Chemical formula of C. I. Acid Blue 80 dye.

5.3.3 Experimental

Materials

The initial merino wool fabric corresponds to ISO 105/F: 1985 (E). The dye used in this study was CI Acid Blue 80 (Sandolan Milling Blue N-BL 150), supplied by Clariant and purified by recrystallisation three times: dissolving in hot dimethylformamide, precipitation by acetone, and then filtered. The dyeing auxiliaries non-ionic products, ethoxylated alkylnonylphenol and the dispersing agent mixture Lanasan LT (NPE), are recommended for use in low-temperature wool dyeing (Clariant); alkylaminoethoxylate and the glycolic ether mixture (AAE) Rucogal MSC (Rudolf Chemie) are recommended for use in wool and polyamide levelling dyeing. The other analytical-grade reagents were used without purification.

Dyeing

Before dyeing, the fabric samples were immersed for one hour in 0.1M acetic acid buffer adjusted to a pH of 4.2±0.05. We measured the dyeing rates in a dye bath with an initial concentration of dye of 1.7×10-4 mol/l or 2.3% owf. The dyeing took place in a laboratory apparatus with a magnetic bar stirrer and cylinder to girdle the 10×20 cm fabric sample with dyeing liquor at a pH of 4.2±0.05. After dyeing, the dye bath’s pH was unchanged. In all dyeing, we adopted the liquor-to-fibre ratio of 200:1 and a temperature of 60 °C or 85 °C. Dyeing was carried out both in the absence and pres-ence of auxiliaries (1.8% owf) up to the dye absorption equilibrium. At the end of the dyeing process, the samples were rinsed thoroughly in water and dried in open air. Conventional dyeing in the presence of electrolyte was carried out using 10% owf sodium sulphate and 4% owf ammonium sulphate. Dye concentration in the dye bath was measured at the start, after 5, 10, 15, 20, 30, 45, 60, 90 minutes, and up to the dye’s exhaustion.

Dyeing characteristics

Dye absorption was calculated from the difference in dye concentration before and after dyeing time t. Dye concentration in liquor was measured in a 10-mm cell using the Spectronic Unicom Genesys TM spectrophotometer. On completion of dyeing, the

79

wool fabric samples were removed from the liquor, rinsed in water to remove any loosely adsorbed dye, and dried in air.

The percentage dye bath exhaustion E was calculated according to Equation 1:

where Ao and Ad are the adsorbances at 590 λmax of Acid Blue 80 dye, initially in the dye bath and of residual dye in the dye bath respectively.

For the dyed fabric samples, the light diffuse reflectance measurements were per-formed with a Spectroflash SF 450 Plus spectrophotometer (Datacolour), and the colour yield values were calculated according to the Kubelka-Munk function (K/S ) by Equation 2 [10]:

(2)

where:

K - absorbance, S - scattering,R - reflectance.

Evaluating the colour parameters

Samples for colour measurements were prepared by folding the dyed wool fabric five times to give samples measuring about 3×3cm. Five points on each trial sample were measured using a spectrophotometer. The colour parameters were evaluated by means of the Cielab system and the modified CIE L* C * h* (D65/10o) system. The following colour parameters for the dyed samples were obtained by the digital Cielab system: L* – lightness, a* – redness if positive coordinate, or greenness if negative coordinate, b* – yellowness if positive coordinate, or blueness if negative coordinate, C* – chromaticity, h – hue of the colour, X – coordinate x, Y – coordinate y, Z – coordinate z [10].The values of colour difference (ΔE) for the dyed samples after relative treatments were calculated by Equation 3 [10]:

2 2 2( ) ( ) ( )E L a b (3)

ΔL*=L*trl-Lin, Δa*=a*trl-a*in, Δb*=b*trl-b*in Lin, a*in, and b*in are parameters of initial species before the relevant treatments.

80

The ΔE deviation of all treated samples was no higher than 0.2. The coordinates of the colours obtained and the results of the ΔE value determinations are summarised in Tables 1-3.The yellowness index YI of the wool fabric samples in the blank dyeing trials was calculated using equation 4 [10]:

1.28 1.06100 %

X ZYI

Y

(4)

where: X, Y, and Z are the C/2 CIE tri-stimulus values of the specimen.

The level of wool fibre damage occurring during the blank dyeing of the wool fabric was determined by means of tryptophan fluorescence intensity changes. The fluorescence spectra were measured with an MPF-4 fluorescence spectrophotopmeter (HITACHI). Samples of the blank dyed wool fabric signals (λex=295 nm, λex=346 nm) were measured and quantified by comparison with those of the initial untreated fabric. The dyeing rate constants were calculated using a modified Cegarra-Puente equation (5) suitable for exhaustion baths:

L*trl, a*trl, and b*trl are parameters of trials, i.e. after blank dyeing (treatment of undyed fabric under dyeing conditions, but without using dye) or after washing the dyed fabric samples.

2

2ln[ ln(1 )] ln lntC

a t a kC

(5)

where a is a coefficient depending on exhaustion, Ct is the dye concentration in the fibre at time t, C∞ is the dye concentration at the equilibrium, K is the absorption rate constant, and t is the dyeing time.

Determining fastness

The samples were washed using an Isal AG 4006 Basel/Schweiz apparatus with rotating stainless-steel hermetic autoclaves, according to standard ISO 105/C06 A1S at 40 °C for 30 min. Colour difference (ΔE) and colour yield (K/S) data were obtained with a Data colour SF450 Plus apparatus under illumination D65 using 10° standard observation angle. Each sample was measured five times and the average values were calculated.

5.3.4 Results and discussions

Dyeing rate Figures 2 and 3 show the plots of the dyeing rate and relative dye uptake

Table 1. Effect of auxiliaries and temperature on dye exhaustion (E, % ), kinetic constant (K)and on colour yield of wool fabric; Colorimetric measurements data of fabric dyed using auxiliaries;Abbreviations given in Figure 1.

81

Ct/C∞ against the square root of dyeing time t1/2 for dyeing in solution without any auxiliaries (A) and in the presence of dyeing organic auxiliaries (NPE or AAE) or electrolyte (EL) respectively. The values for the kinetic constant K in the absence and in the presence of auxiliaries are presented in Table 1. It is clear from these results that the application of the non-ionic surface active agent NPE for dyeing at 60 °C leads to a considerable increase in the apparent dye uptake, while in the presence of weakly cationic alkylaminoethoxylate AAE, the rate of dye absorption was even lower compared with that for dyeing without auxiliary. The application of the dyeing auxiliary NPE as well as AAE makes the whole quantity of dye to penetrate the fibre at 85 °C more readily as suggested by the dye exhaustion and dyeing rates.From Figure 2 and Table 1, the NPE at 60 °C temperature can also be seen to cause the higher increase in total dye absorption absorption and the rate of dyeing, compared with the figures for AAE. As mentioned above, alkoxyethylated nonylphenol has a significant effect on the cellular membrane complex (CMC) of wool fibre [5], while the alkylaminoethoxylates, which combine non-ionic and cationic properties, are capable of forming complexes with acid dyes, facilitate solubilisation, and provide level dyeing of wool [3]. Non-ionic alkylphenolethoxylate-type surfactants, in contrast to alkylaminoethoxylates, are not considered to have a structural effect on the levelling agent, but are known to be adducts which form complexes with wool fibre by means of hydrophobic interaction between hydrophobic sites [12]. Mieusset et al have shown that when dyeing with a 1:2 metal complex dye, a quick initial surfactant absorption by wool occurred regardless of the manner of surfactant application. Surfactant absorption is followed by pronounced desorption, with an increase of temperature and dye exhaustion [13].Mieusset et al have shown that when dyeing with a 1:2 metal complex dye, a quick initial surfactant absorption by wool occurred regardless of the manner of surfactant application. Surfactant absorption is followed by pronounced desorption, with an increase of temperature and dye exhaustion.

Figure 3 shows that the intercept on the dye absorption axis, which proves the existence of a barrier of diffusion, is significantly reduced in the case of NPE; with AAE it did not reduce, compared with that during dyeing in the absence of an auxiliary. The results presented in Figure 1 and Table 1 also show that when dyeing was carried out at 85 °C, the AAE produced a higher increase in the total dye absorption and dyeing rate, particularly in the early dyeing stage.

It is known from the relevant literature [1] that the gradual decomposition of complexes between the levelling agent and the dye can occur when the dyeing temperature increases. Therefore it is assumed that at a higher temperature, the decomposition of AAE and anionic dye complexes could be a factor influencing the renewal of acid milling dye’s affinity for wool fibre. The Blockage of electronegative sites of wool, due to the interaction with AAE containing amino

82

groups could take place in this case, and an increase in the amount of the net positive charge on the protein accessible to dye should therefore also be an important factor in dye absorption.

Colour yield and colour characteristics:

In general, the colour yield for dyed wool should be related to the amount of dye in a fibre, albeit only up to a certain dye concentration [10]. The K/S of dyed samples in this study has been measured, and the results are presented in Table 1. The results show that when the fabric samples were dyed at 60 °C, there was a significant variation in the ratio of K/S values and dye exhaustion, which is proportional to the amount of dye in the fibre. The variation of this ratio was small or disappeared completely when dyeing occurred at 85 °C. A comparison of dye exhaustion and colour yield data for the dyeings obtained at 60 °C and 85 °C temperature respectively shows that at the same level of dye exhaustion, for example dyeings at 60 °C and 85 °C temperature respectively, higher K/S values are obtained for samples dyed at higher temperature. This allows us to assume that when the dye absorption on the fibre is faster and exhaustion tends to be completed, the dye is transferred from the endocuticle to the sulphur-rich exocuticle rather than into the cortex, and therefore for dyeings at 85°C, the colour yield was higher in all the cases studied. Our assumption is in agreement with the conclusion made by Wolf et al [14]. Summarising the study of the results by TEM of morphological changes within the fibre of wool during the sorption and diffusion of 1:2 metal complex dyes, these authors have stated that the sorption of dyes or surfactants is accelerated by morphological changes within the cuticle-cellular membrane complex, which is the adsorption zone, or within the main diffusion path endocuticula, and did not depend on the cortex penetration capacity [14]. For the samples dyed at 60 °C, we have studied the effect of auxiliaries on the rate of dyeing and on changes to colour yield (K/S) values. The ratio of K/S values were compared with the ratio of kinetic constant values (K) for corresponding dyeings. The result was surprising, because the ratio of kinetic constant values taken

83

from Table 1 KNPE/KA and the ratio of respective colour yield values (K/S)NPE/(K/S)A were equal to 1.3 and 1.2 respectively. In other words, this compar-ison shows that the colour yield of dyed wool fibre depends also on the rate of dye absorption, and not only on the amount of dye in the fibre. The comparison of K and K/S values for NPE with respect to the corresponding values for dyeing, in the absence of auxiliary (KAAE ) and (K/S)AAE respectively, show that KNPE /KAAE =1.5 and (K/S)NPE /(K/S)AAE =1.2. Thus, the results presented above allow us to assume that the increase in the rate of dye uptake should be considered to be due to the facility of increase on the amount of dye in the surface layer cuticle of wool fibre. The approximate calculation of the amount of active sites represented by the basic groups of cuticle proteins should be less than 8.3×10-5equiv/g. In the cellular-mem-brane complex and endocuticle jointly, the amount of basic groups should be less than 3.8×10-5 equiv/g, while the amount of dye used in this study was 4.3×10-5 mol/g. Thus, the dye absorbed in the wool fibres should correspond to to approximately half the amount of the basic groups considered in the cuticle.

Our results as presented and discussed above are in agreement with the general statement made by Rippon, that for non-reactive dyes, no thermodynamic equilibrium with wool is established until the dye transfer into the keratinous regions is complete. If the dye remains largely in the non-keratinous regions, rapid diffusion out of the fibre can occur, and poor wet fastness properties are obtained [3].

The results presented in Table 1 show that dyeing at 60 °C both without the auxiliary and in the presence of AAE results in lower values of both the Cielab coordinates and the K/S values, compared with those for samples dyed in the presence of NPE. These results are consistent with the values of dye exhaustion and dyeing rate constants for the corresponding dyeings presented in Table 1. Increasing the dyeing temperature up to 85 °C significantly enhanced the redness (a*) of samples dyed in the presence of AAE, while for the samples dyed in the presence of NPE as well as in the absence of the auxiliary, chroma (C*) values were reduced.

Colour difference

The colour differences of dyed wool samples could have been influenced by the increase in wool yellowness or the reduction in the amount of melanin occurring due to damage to the fibre during dyeing. The migrations of dye into or out of the fibre during washing or thermal and hydrothermal treatment are also noted to be very important factors in colour change [15]. We therefore attempted to determine whether the colour difference of wool fabric dyed with milling Acid Blue 80 could depend on the extent of fibre damage occurring during dyeing, on the change in the yellowness index value, or on dye migration during dyeing or the washing of dyeings. In this study, we introduced trials with benzyl alcohol, which is known as a very efficient auxiliary for wool dyeing at low temperature, but which unfortunately damages fibres. We expected that benzyl alcohol should be used to determine whether a relationship is reliably predictable between the colour change or the yellowing of fabric and the level of fibre damage occurring during blank dyeing.

84

Table 2. Colour difference and fibre damage by means of fluorescence emission intensity changes in blank dyed wool fabric; Abbreviations given in Figure 2. • 3% v/v of benzyl alcohol was added into the bath of blank dyeing.

Table 2 shows the colour difference and yellowness index values of the blank dyed fabric samples, which have been prepared while maintaining all the other selected conditions of dyeing, with the exception that the dye was not applied in these trials. As could be seen, the extent of colour change was higher for dyeings obtained without the auxiliary. The most significant colour change was when dyeing occurred in the presence of benzyl alcohol, which was used in this study for comparison. The data of fluorescence emission spectroscopy of the blank dyed wool fabric samples shows a marked reduction in the fluorescence emission of tryptophan; that is, a significant degree of the wool fibre damage was also caused in the sample which had been dyed in the absence of the auxiliary, but longer exposed to dyeing conditions , than those with NPE or AAE. The samples dyed in the presence of benzyl alcohol showed an especially marked lowering in the fluorescence emission of tryptophan, an increase in the yellowness index value and in colour difference. However, the colour difference was not dependent upon the wool fibre damage occurring during blank dyeing in the presence of the electrolyte. It can thus be concluded that neither the increase in yellowness index value of wool fibre nor the fibre damage occurring during dyeing was responsible for the general colour difference of the dyeings due to the auxiliaries applied in this study.

In the light of the findings shown in Table 3, an attempt was made to explain the beneficial effect of temperature and dyeing auxiliaries on colour wash fastness, colour change and colour yield change during the treatment of dyed wool fabric. The corresponding colorimetric data for the dyeings after wash fastness testing are displayed in Table 3. The comparison of the changes in redness (Δa*), blueness (Δ(-b*)), chroma (ΔC*) and colour difference ΔE values for dyed fabric samples show the extent to which each of the different dyeings after washing was changed in terms of colour loss from the original dyeings. Table 3 shows that the extent of changes for the samples dyed while applying NPE at 60 °C were generally small, compared with those for AAE or for dyeings without an auxiliary. The dyeing at 85 °C resulted in an increase of the degree of colour change for AAE, but did not do so for the electrolyte, or for dyeings prepared without an electrolyte. Theoretically, the ability of a surface active levelling agent such as AAE to form

85

Table 3. Changes of colour characteristics after wash fastness testing of fabric dyed using auxiliaries; Abbreviations given in Figure 2.

dye water-soluble complexes is an important factor within the fibre. The stability of the AAE-dye complexes which are formed under selected dyeing conditions could be responsible for AAE sorption into the inner layers of the fibre, either alone or together with dye, and therefore a relatively greater colour change due to washing the dyed fabric could occur. As seen from Table 3, the blueness (-b) of dyeings after washing for AAE was significantly higher; that is to say, we could observe the result of dye migration from the inner to the outer layers of the fibre. In the case of control dyeing without auxiliary or dyeing in the presence of electrolyte at a temperature 85 °C, the colour washing fastness by means of colour difference was higher due to the absence of the auxiliary, which can modify the dye solubility and hence leads to a lower dye affinity for wool fibre.

5.3.5 Conclusions

The dyeing behaviour of wool at low temperature using acid milling dyes and non-ionic auxiliary agents have been investigated. Our work shows the effect of temperature and auxiliaries on dyeing on acid milling dye equilibrium, rate of dye uptake, colour yield and colour coordinates of dyed wool fabric. The use of a non-ionic auxiliary based on alkylphenolethoxylate enhances both the rate of dyeing and the colour yield of fabric at 60 °C, while the increase in dye substantivity, dyeing rate and colour yield for alkylaminoethoxylate is most important at higher temperatures. Increasing dyeing temperature from 60 °C to 85 °C, or using auxiliaries, leads to a change in the colour yield of the wool fibre, which in general depends on dyeing rate when dyeing is extended up to the equilibrium. From colour coordinate measurement data, it is apparent that the colour changes of the dyed fabric sam samples which occur due to the variation of dyeing temperature are most important, presumably due to a variation of the dye-auxiliary complexes’ stability and the change of dye affinity for wool, when alkylaminoethoxylate is used as a dyeing auxiliary.

5.4 Utilization of MLV Liposomes as a Carrier in Dyeing of Wool/Polyester

86

5.4.1 Abstract

Liposomes are lipid-water systems that can carry hydrophobic and hydrophilic materials because of their amphiphilic structures.Application of liposomes in dyeing and finishing textiles is a new technology based on targeting and slow release which can lead to dyeing at lower temperature along with energy savings and lower environmental impacts. In this research work, a practical method for dyeing wool/polyester blends with disperse dye using liposome-forming compounds is proposed. Multi-lamellar liposomes (MLV) were prepare from Soya lecithin with 45% phosphatidylcholines and applied as an auxiliary in dyeing of wool/polyester fabric with disperse dye under different experimental conditions of the temperatures, time and liposome concentrations. The effect of liposomes in dye-bath on dye exhaustion and dyed fabric properties was investigated to achieve optimum conditions. The results were compared with those obtained with and without conventional dyeing auxiliary which showed that the presence of liposomes in the dye-bath helps to enhance the absorption of disperse dye on the wool/polyester fabric which was evaluated by colour strength (K/S). An increase on K/S was observed more significant for the samples dyed at 110ºC for 60 min using 2% owf (on weigh of fabric) liposomes. Dyeing at higher temperature and longer time with higher liposome concentrations doesn’t increase the final exhaustion remarkably. The tensile strength, wash and light fastness of samples have not been changed significantly.

Keywords: MLV, Wool/polyester dyeing, Colour strength (K/S)

5.4.2 Introduction

Liposomes are defined as any structure composed of lipid vesicle bilayers that enclose a volume, and liposomes containing a dye are generally large, irregular, and unilamellar [1]. Liposomes have attracted a great deal of scientific interest because of two reasons. First, liposomes can provide an excellent model for membranes. Second, these phospholipic bilayers are being developed as a controlled delivery system for therapeutic agents [2]. Although initially slow to exploit the technology of liposomes, the textile industry has now produced a wide variety of innovations using the basic principles of targeting slow release, and protection of sensitive chemicals, principally in dyeing and finishing [3]. The schematic structure of liposomes is illustrated in

Figure 1.

Blending polyester with wool is an attempt to achieve a combination of the most desirable features of both fibers, providing fabrics with good properties. Dyeing wool is usually carried out in a boiling bath, but wool damage during dyeing process is not severe provided suitable dyeing condition are chosen [4]. Polyester has a high glass

87

transition temperature, approximately 80°C, and so dyeing with disperse dyes is done at high temperature. If a low dyeing temperature is selected in order to avoid damaging the wool, the disperse dye uptake on the polyester will not be adequate to achieve a good dyeing. On the other hand wool maybe damaged unacceptably if high dyeing temperature or prolonged dyeing times are adopted in order to increase dye uptake on polyester. Carriers are useful agents for wool/polyester blends and permit dyeing at relatively low temperatures, although they have some disadvantages, e.g. being toxic and harmful to the environment [5, 6]. In attempt to decrease high energy costs, expensive machinery investment, and undesirable effects such as wool damage during the conventional dyeing process and protect environment, alternative method for dyeing wool/polyester blends with disperse dye is using liposome-forming compounds. Although wool/polyester blends are industrially dyed simultaneously with wool and polyester dyes and previous studies have already determined the effect of liposomes on wool dyeing, this study focuses on the action of liposomes on wool/polyester blend dyeing with disperse dyes. Therefore, we try to prepare and produce multi-lamellar liposomes (MLV) from Soya lecithin with 45% phosphatidylcholine and study the influence of liposomes in dye-bath at different temperature, exhaustion time and concentration during in wool/polyester dyeing with disperse dye. The dyeing temperature and time was optimized with optimum concentration of liposomes. The tensile strength, wash and light fastness properties of samples have also reported.

5.4.3 Experimental

Materials and Methods

The material to be dyed was woven wool/polyester fabric supplied by Iran Merinous (Ghom, Iran). Soya lecithin (containing 45% phosphotydilcholin) with phase transition temperature (Tc) of -18ºC was prepared by Lipoid (Germany). The disperse dye Sumikaron Blue EF-BL (C.I.Disperse blue 56) was used; its chemical structure

indicated in Figure 2 [7]. Carrier used was TANAVOL supplied by Tanatex Chemical Co. (Netherlands), CATA PON 310N as a nonionic detergent and CATA PERS 200 NDF as a dispersing agent from Catan Chemical Co. (Iran).

Fig 2. Chemical structure of C.I.Disperse blue 56 dye. Dyeing was done in an Ahiba Polymat Data Color dyeing machine and the reflectance spectras of the dyed samples determined by ACS Spectra Sensor �� integrated with an IBM-PC. The wash-fastness of the liposomes treated dyed fabric was measured according to ISO 150-C03 [8]. For light-fastness measurements, the samples were exposed to the daylight for 7 dyes according to the daylight ISO 105-B02 in Xenotest 150S\ machine [9] and changes in the colour (fading) were assessed bye the blue scale. Also the tensile strength of the samples evaluated according to ASTM 5035:1974 [10].

88

Preparation of MLV Liposomes:

Multilamellar Liposomes were prepared following the thin film hydration method [11]. A lipid film was formed by removing the organic solvent under low vacuum along with temperature by rotary evaporation (temperature bath being 35- 40ºC) from Soya lecithin solution in chloroform. Aqueous phase containing distilled water was added to the lipid film. The solution was then swirled to remove the lipid from the walls of the flask and glass beads, also to disperse large lipid aggregates; glass beads were added to facilitate dispersion. After preparation, the resulting milky liposome suspension was left to equilibrate for 15 minutes and applied in wool/polyester dyeing process.

Dyeing Procedure:

Before dyeing, the wool/polyester samples should be cleaned to become free from the impurities. Therefore, samples were scoured using 1 gr/l nonionic detergent at a liquor ratio of 40:1 for 30 min at 60ºC. The samples were then rinsed with warm water and tap water and then dried at room temperature. Wool/polyester samples were treated with liposomes, without liposomes or with conventional auxiliaries. The dye bath were prepared with different concentrations of prepared MLV liposomes (0%, 1%, 2%, 3% o.w.f.), 2% o.w.f (on weight of fabric) disperse dye (Sumikaron Blue EF-BL) and dispersing agent at a liquor ratio of 40:1; acetic acid was added to adjust the pH to 4.5-5.5. Dyeing in Polymat dyeing machine was initiated at room temperature and the temperature raised by 2ºC/min until the maximum temperature (95ºC, 110ºC or 120ºC) was reached, remaining there for 45, 60 or 75 minutes. The samples were then rinsed with tap water and dried at 60ºC for 10 minutes The reflectance values and the corresponding CIE L*, a*, b*, C* and h0 of the dyed samples were measured using a Datacolor Texflash spectrophotometer interfaced to a digital PC under illuminant D65, using a 100 standard observer with UV component included and specular component excluded. The distribution of disperse dye on the wool/polyester samples were determined by the K/S values calculated according to the Kubelka-Munk equation from the amount of reflectance (R) at the maximum wavelength (� max

5.4.4 Results and Discussions

Dyeing Profiles

The color strengths (K/S value) were calculated according to the equation1 from the reflectance amount of samples at the maximum wavelength (which give maximum dye absorption). All of the dyed samples indicated the minimum value of reflectance at 460nm (_max). The K/S values of wool/polyester samples dyed with disperse dye, applied liposome concentrations from 0% to 3% o.w.f at three different temperatures (95ºC, 110ºC and 120ºC) and exhaustion times (45, 60 and 75 min) were obtained It can be observed from figure 3, 4 and 5 that any increase in time of dyeing and concentrations of liposome caused an increase in the values of K/S. Enhancement of

89

(K/S) values is more significant at 110ºC than 95ºC and 120ºC. Because of compact crystalline structure of polyester dyeing at low temperature (95ºC) doesn.t lead to achieve satisfactory dye absorption. Increasing of temperature to 120ºC, with different exhaustion time and liposomes concentrations doesn.t raise the K/S values significantly even in some samples, decrease in K/S values observed. This could be related to the liposomes stability. The liposome above the 85ºC gradually converted to the smaller particles of phospholipids. These changes of the particle size of phospholipid lead to coating of wool/polyester surface with a layer of phospholipid at 120ºC which leads to decrease the value of K/S.

Fig 3. K/S values of the dyed samples with different liposomes concentration and exhaustion time and at 95ºC.

Fig 4. K/S values of the dyed samples with different andliposomes concentration and exhaustion time at 110ºC.

Fig 5. K/S values of the dyed samples with different liposome concentration and exhaustion time at 120

90

The results also indicated that although the samples dyed without liposomes at 120ºC have a higher value of K/S comparing with the samples dyed with liposomes at 110ºC according to figure 4 and 5, but their differences were not significant along with having preferences rather than synthetic auxiliaries e.g. not being toxic and harmful to the environment. It can be concluded that in dyeing of wool/polyester with disperse dyes, utilization of 2% o.w.f liposomes in dye-bath at 110ºC for 60 min, clearly reduce the dyeing temperature about 10ºC compared with a conventional dyeing process. These results are in accordance with the results obtained by Marti for thedyeing of wool/polyester with disperse dye. 3.2 Fabric Properties in Liposome Dyeing 3.2.1 Wash & Light Fastness

In order to study the effect of liposomes on the dyed wool/polyester samples, wash and light fastness were tested and the results listed in Tables 1 and 2. The results showed that dyeing with liposome doesn.t have clear effect on wash and light fastness of samples compare with those dyed with conventional dyeing process

Tensile Strength

The results of tensile strength test for dyed wool/polyester samples were shown in figure 6. The influence of dyeing temperature on the

strength of wool component was found to be very significant, even at short dyeing times (45 min). The rate of decrease in tensile strength decreased with increasing dyeing temperature. For this reason it is not recommendable to expose the wool component to be dyed at above 110°C. Considering figure 6, comparing the tensile strength obtained by dyed samples with 2 % liposome and conventional dyeing (with carrier at 95°C and without auxiliaries at 120°C) for 60 min, reveals that increasing temperature and time of dyeing decrease the tensile strength which is more rapidly above 110°C and 60 minute. Also less decrease in tensile strength of dyed samples with 2% liposome is observed compared with samples dyed conventionally

91

Fig 6. Tensile strength of wool/polyester samples dyed with disperse dye as a function of dyeing temperature for 60 min.

5.4.5 Conclusions

In this work, applications of liposomes as a carrier in dyeing of wool/polyester by some of the synthetic dyes have already been reported. From our results, it concluded that a new method of wool/polyester dyeing using disperse dye C.I. Disperse Blue 56 by means of large multilamellar liposomes could be considered appropriate for improving dye exhaustion on samples and reduce the dyeing temperature approximately 10ºC. The optimum dyeing condition of wool/polyester fabric with this disperse dye is under 110°C for 60 minute with 2% liposomes concentration. Also using liposomes could lead to decrease high energy costs, expensive machinery investment, and undesirable effects such as wool damage during the dyeing process and protect environment.

92

Conclusion:

The process of applying dye to a textile material or fibre is known as dyeing of textile fibre. Auxiliaries are essential in the field of textile dying to achieve the desired goal effectively and without facing difficulties. There are several hundreds of auxiliaries and they perform very important role in the respected field of dyeing. New dyeing auxiliaries in different types dye stuffs and dyeing process are constantly being developed. Research is also going on to make the older ones more efficient. The classification, function, necessity and different auxiliaries used with different dye stuff have already been studied. The study of textile dyeing auxiliaries enables us to know the influence of auxiliaries in fixing, absorption, exhaustion, sticking, improving the substrate in readiness for colouration, stabilizing the application medium, improving the fastness of dyeing etc. Here the synthesis of reactive auxiliaries for dye resist treatment of wool, the effect of UV absorbers on ultra violet protection properties of dyed cellulosic fibre, the influence of non ionic auxiliaries on absorption of acid milling dye, the utilization of MLV liposome as a career in dye have been studied.

93

REFERENCES

1. Cegarra, A. Riva and R. Prieto, 1996. Sorption ofnon ionic auxiliary products by wool and its ifluence on dyeing with acid dyes,JSDC., 1996. 112: 114.

2. Myung, J., Kim P. Jae and Joonseok Koh, 2006. Synthesis of heteromultifunctional dye-resist agents containing chloro-s-triazine and á-bromoacrylamide and their dye-resist properties in wool fabrics, Coloration Technology., 122: 227.

3. Textile Terms and Definitions, 1986. 8th edn, Textile Institute, Manchester. 4. Lewis, D.M., B. Cameron, D.M. Lewis and Palithrope, 1992. Parctical dye

resist treatments for printing and cross dyeing of wool, M.T., Proc.7th int.wool Text.Res.Conf.Tokyo., 5: 79-89.

5. Jeon, B.D, M.T. Palithrope and S.K. Davide, 1992. Dye resist effects on sulphamic acid treated wool, Dyes &Pigments., 19: 99.

6. Burkinshaw, S.M. and N. Nikolaides, 1991. Acommercial syntan as an anionic dye resist agent for wool, Dyes & Pigments., 15: 225.

7. Burkinshaw, S.M. and N. Nikolaides, 1991. Further studies of the use of commercial syntans as anionic dye resist agents for wool, Dyes & Pigments., 16: 299.

8. Supriyanta, N. and S.K. David, 1992. Dye resist effects on silk fabric treated with sulphamic acid and sandospace R, Dyes &Pigments., 18: 297.

9. Bell, V.A. and D.M. Lewis, 1983. Text. Res. J., 53: 125.10. Bell, V.A. and D.M. Lewis, 1984. and Palithrope, Chemical treatments

desigened to modify the affinity of wool for dyes, M.T., JSDC., 100: 223.11. Haarer, J. and H. Hocker, 1994. New reactive auxiliaries for dye resist

treatment of wool Part I, Text Res J., 64: 480.12. Perrin, D.D., W.L.F. Armago and D.R. Perrin, 1980. Purification of laboratory

chemicals,2nd edn.Pergamon Press,Oxford., 182.13. Lewis, D.M. and M.T. Palithrope, 1984. JSDC., 100: 56.14. Feriz-David, H.E. and M.T. Palithorpe, 1984. JSDC., 100: 223.15. Church, JS., AS. David, PJ. Scammells and DJ. Tucker, 1999. Rev Prog Col.,

29: 85.16. Church, JS., AS. David, PJ. Scammells and DJ. Tucker, 1998. Dyes and

Pigments., 39: 313.17. Jutta, H. and H. Hartwig, 1994. New reactive auxiliaries for dye resist

treatment of wool Part II18. Textile Res. J., 64(10): 578-538.19. J. Shore, Colorants and auxiliaries. Vol. 2, Auxiliaries, SDC, Bradford,

England, 1990, p. 429, 430. 20. 2. K. Joko, J. Koga, Proc. 9th Internat. Wool Text. Res. Conf. 1990, p. 19 - 26. 21. D. M. Lewis, Wool Dyeing, SDC, Bradford, England, 1992, p. 92, 40. 22. A. Riva, J. Cegarra, R. Prieto, JSDC, 1996, 112: p. 114 - 116. 23. L. Coderch, O. Lopez, De la Maza, A. M. Manich, J. L Parra., J.Cegarra,

Textile Res. J., 1997, vol. 67, p. 131 - 136. 24. A. Riva, I. Algaba, R. Prieto, Colour. Technol., 2002, 118, p. 59 - 63. 25. N. S. Yoon, Y. J. Lim., M. Tahara, T. Takagishi, Textile Res. J., 1996, vol. 66,

p. 329 - 336. 26. R. Treigiene, J. Musnickas, Materials Science, 2001, 7, No 4, p. 313 - 318.

94

27. J. Musnickas, A. Kantautas, V. Rupainytė, R. Treigienė, Materials Science, 2004, 10, No 4, p. 359 - 362.

28. R. McDonald, Colour Physics for Industry, SDC, Bradford, England, 1997, p. 534.

29. J. Cegarra J. (Publio Puente), J. Valldeperas, The Dyeing of Textile Materials, Textilia, Turin, Italy, 1992, p. 126.

30. N. Schonfeldt, Grenzflachenaktive Athylenoxid-Addukte, Stuttgart, 1976, 750.31. J-L. Mieusset, C. Kramer, C. Koll, E. Deniz, K. Wolf, Dtsch. Wollforschungs-

int. Der TH Aachen e V., Germany. DWI Reports,1994, 113.32. K. Wolf, K. Phan, C. Kramer, R. Engering, H. Hocker, Dtsch.

Wollforschungsint RW TH, Aachen, Germany. DWI Reports, 1997, 119.33. K. Schafer, Melliand Textilberichte, 2001, 6, 520-523. [1] Gomes, J.I.N.R,

.Controlling Exhaustion of Reactive Dyes on wool by Microencapsulation with Liposomes., Textile Research Journal, vol. 67, no. 7, pp 537-541, July. 1997.

34. De la Maza, A., Parra, J.L., Bosch, P., Coderch, L.A., .Large Unilamellar Vesicle Liposomes for Wool Dyeing: Stability of Dye-Liposome Systems and Their Application on Untreated Wool., Textile Research Journal, vol. 62, no. 7, pp 406-413 1992.

35. De la Maza, A., Parra, J.L., Manich, A.M., .Lipid Bilayers Including Cholesterol as Vehicles for Acid Dyes in Wool Dyeing Textile Research Journal, vol. 63, no. 11, pp 643-649, 1993.

36. Marti, M., Coderch, L.A., de La Maza, A., Manich, A., and Parra, J.L., .Phosphatidylcholine Liposomes as Vehicles for Disperse Dyes for Dyeing Polyester/Wool Blends., Textile Research Journal, vol. 68, no. 3, pp. 209-218, March. 1998.

37. Carrion Fite, F., J., .Dyeing Polyester at Low Temperatures: Kinetics of Dyeing with Disperse Dyes., Textile Research Journal, vol. 65, no. 6, pp. 362-368, June. 1995.

38. Wang, J., Asnes, H., .One bath Dyeing of Wool/Polyester Blends with Acid and Disperse Dyes, Part 1-Wool Damage and Dyeing Conditions., Society of Dyers and Colourists., vol. 107, pp. 274-279, 1991.

39. Colour Index, Fourth Edition, SCD, 2001.40. Textiles International Standard for colour fastness to washing: sections AO2

& AO3, Grey scale for assessing change in colour and staining, 1th Ed., 1978.41. Textiles International Standard for colour fastness to artificial light: Xenon arc

fading lamp test, 3th Ed., 1988.42. Annual Book of American Society for Testing and Materials Standards:

Section 7, Textile _, 1999.43. Lasic D.D., .Liposomes in Gene Delivery., CRC Press, pp 67-95, 1997.

95