+Analysis of Anomalous Film Growth when Yttrium Oxide Thin Films are Exposed to 7.2eV Light
Alison WellsDr. David D. AllredDevon MortensonKristal Chamberlain
![Page 2: + Analysis of Anomalous Film Growth when Yttrium Oxide Thin Films are Exposed to 7.2eV Light Alison Wells Dr. David D. Allred Devon Mortenson Kristal Chamberlain](https://reader036.vdocuments.mx/reader036/viewer/2022062805/5697c0261a28abf838cd5912/html5/thumbnails/2.jpg)
+Background
Group members took some samples to Berkeley for measurements using the Advanced Light Source.
When they got back needed to put it in the plasma cleaner. Why? Because there is a sort of “gunk”
composed mainly of hydrocarbons deposited on samples.
Problem: the plasma cleaner was broken.
Solution: Use the excimer (VUV) lamp instead.
![Page 3: + Analysis of Anomalous Film Growth when Yttrium Oxide Thin Films are Exposed to 7.2eV Light Alison Wells Dr. David D. Allred Devon Mortenson Kristal Chamberlain](https://reader036.vdocuments.mx/reader036/viewer/2022062805/5697c0261a28abf838cd5912/html5/thumbnails/3.jpg)
+Background Continued
After approximately 5 minutes under the VUV lamp, the sample became visibly thicker.
Use ellipsometry measurements to determine if this is true.
The Mystery
![Page 4: + Analysis of Anomalous Film Growth when Yttrium Oxide Thin Films are Exposed to 7.2eV Light Alison Wells Dr. David D. Allred Devon Mortenson Kristal Chamberlain](https://reader036.vdocuments.mx/reader036/viewer/2022062805/5697c0261a28abf838cd5912/html5/thumbnails/4.jpg)
+Ellipsometry Measurements: Y2O3Before cleaning: 24.94
nmAfter 5 min VUV: 31.061
nmGenerated and Experimental
Photon Energy (eV)1.0 2.0 3.0 4.0 5.0 6.0 7.0
Y in
de
gre
es D
in d
eg
ree
s0
20
40
60
80
100
-200
-100
0
100
200Model Fit Exp Y -E 75°Model Fit Exp D-E 75°
0 si_jaw 1 mm1 sio2_jaw 2.000 nm2 ema y2o3/30% void 24.733 nm3 polycarb 0.000 nm4 srough 0.500 nm
Generated and Experimental
Photon Energy (eV)1.0 2.0 3.0 4.0 5.0 6.0
Y in
de
gre
es D
in d
eg
ree
s
0
20
40
60
80
100
-100
0
100
200
300Model Fit Exp Y -E 70°Exp Y -E 72°Exp Y -E 74°Exp Y -E 76°Exp Y -E 78°Exp Y -E 80°Model Fit Exp D-E 70°Exp D-E 72°Exp D-E 74°Exp D-E 76°Exp D-E 78°Exp D-E 80°
0 si_jaw 1 mm1 sio2_jaw 1.800 nm2 y2o3 constants based on 091130b on si 31.061 nm3 srough 0.500 nm
![Page 5: + Analysis of Anomalous Film Growth when Yttrium Oxide Thin Films are Exposed to 7.2eV Light Alison Wells Dr. David D. Allred Devon Mortenson Kristal Chamberlain](https://reader036.vdocuments.mx/reader036/viewer/2022062805/5697c0261a28abf838cd5912/html5/thumbnails/5.jpg)
+In Search for an AnswerBig question is: What’s going on here?
![Page 6: + Analysis of Anomalous Film Growth when Yttrium Oxide Thin Films are Exposed to 7.2eV Light Alison Wells Dr. David D. Allred Devon Mortenson Kristal Chamberlain](https://reader036.vdocuments.mx/reader036/viewer/2022062805/5697c0261a28abf838cd5912/html5/thumbnails/6.jpg)
+First Theories
First thought: the yttrium is not fully oxidized. Too thick
Is it possible that the VUV lamp is actually depositing material onto the sample? Not possible that more Y2O3 is being added to film.
Subject a blank silicon substrate to same VUV treatment and look for film deposition. No growth
![Page 7: + Analysis of Anomalous Film Growth when Yttrium Oxide Thin Films are Exposed to 7.2eV Light Alison Wells Dr. David D. Allred Devon Mortenson Kristal Chamberlain](https://reader036.vdocuments.mx/reader036/viewer/2022062805/5697c0261a28abf838cd5912/html5/thumbnails/7.jpg)
+First Set of Conclusions
Oxidation of Silicon Substrate Thickness decreases in furnace
Only other option is that what is already on the film is somehow being altered.
It doesn’t seem likely that the VUV lamp is depositing material onto our film.
![Page 8: + Analysis of Anomalous Film Growth when Yttrium Oxide Thin Films are Exposed to 7.2eV Light Alison Wells Dr. David D. Allred Devon Mortenson Kristal Chamberlain](https://reader036.vdocuments.mx/reader036/viewer/2022062805/5697c0261a28abf838cd5912/html5/thumbnails/8.jpg)
+Second theories and Tests (cont.)Necessity of VUV Interaction with Sample
![Page 9: + Analysis of Anomalous Film Growth when Yttrium Oxide Thin Films are Exposed to 7.2eV Light Alison Wells Dr. David D. Allred Devon Mortenson Kristal Chamberlain](https://reader036.vdocuments.mx/reader036/viewer/2022062805/5697c0261a28abf838cd5912/html5/thumbnails/9.jpg)
+Second theories and Tests (cont.)Necessity of an ozone
![Page 10: + Analysis of Anomalous Film Growth when Yttrium Oxide Thin Films are Exposed to 7.2eV Light Alison Wells Dr. David D. Allred Devon Mortenson Kristal Chamberlain](https://reader036.vdocuments.mx/reader036/viewer/2022062805/5697c0261a28abf838cd5912/html5/thumbnails/10.jpg)
+
Look at Neighboring OxideWhat would happen to a scandium oxide when exposed to same VUV treatment.
New Theories
![Page 11: + Analysis of Anomalous Film Growth when Yttrium Oxide Thin Films are Exposed to 7.2eV Light Alison Wells Dr. David D. Allred Devon Mortenson Kristal Chamberlain](https://reader036.vdocuments.mx/reader036/viewer/2022062805/5697c0261a28abf838cd5912/html5/thumbnails/11.jpg)
+Comparing Oxides
May be slightly hydroscopic
Reactively Sputtered sample
Insoluble in water
Natural oxidation vs. reactive sputtering
Y2O3 Sc2O3
Water in the voids
![Page 12: + Analysis of Anomalous Film Growth when Yttrium Oxide Thin Films are Exposed to 7.2eV Light Alison Wells Dr. David D. Allred Devon Mortenson Kristal Chamberlain](https://reader036.vdocuments.mx/reader036/viewer/2022062805/5697c0261a28abf838cd5912/html5/thumbnails/12.jpg)
+Ellipsometry Measurements: Natural Oxidized Sc2O3
Before VUV: 22.842 nm After 40 min: 23.310 nm
![Page 13: + Analysis of Anomalous Film Growth when Yttrium Oxide Thin Films are Exposed to 7.2eV Light Alison Wells Dr. David D. Allred Devon Mortenson Kristal Chamberlain](https://reader036.vdocuments.mx/reader036/viewer/2022062805/5697c0261a28abf838cd5912/html5/thumbnails/13.jpg)
+Ellipsometry Measurements: Reactively Sputtered Sc2O3
Before Cleaning: 12.528 nm After 5 min VUV: 13.218 nm
![Page 14: + Analysis of Anomalous Film Growth when Yttrium Oxide Thin Films are Exposed to 7.2eV Light Alison Wells Dr. David D. Allred Devon Mortenson Kristal Chamberlain](https://reader036.vdocuments.mx/reader036/viewer/2022062805/5697c0261a28abf838cd5912/html5/thumbnails/14.jpg)
+Ellipsometry Measurements: Reactively Sputtered Sc2O3
After 10 min VUV: 14.406 nm After 20 min VUV: 15.524 nm
![Page 15: + Analysis of Anomalous Film Growth when Yttrium Oxide Thin Films are Exposed to 7.2eV Light Alison Wells Dr. David D. Allred Devon Mortenson Kristal Chamberlain](https://reader036.vdocuments.mx/reader036/viewer/2022062805/5697c0261a28abf838cd5912/html5/thumbnails/15.jpg)
+Ellipsometry Measurements: Reactively Sputtered Sc2O3
After 40 min VUV: 17.902 nm After 70 min VUV: 17.203 nm
![Page 16: + Analysis of Anomalous Film Growth when Yttrium Oxide Thin Films are Exposed to 7.2eV Light Alison Wells Dr. David D. Allred Devon Mortenson Kristal Chamberlain](https://reader036.vdocuments.mx/reader036/viewer/2022062805/5697c0261a28abf838cd5912/html5/thumbnails/16.jpg)
+The Mystery Continues
Thicker Films
Use XPS to look at oxygen to metal ration
Observe other oxides
Deposit Silicon cap over samples
Future Work
![Page 17: + Analysis of Anomalous Film Growth when Yttrium Oxide Thin Films are Exposed to 7.2eV Light Alison Wells Dr. David D. Allred Devon Mortenson Kristal Chamberlain](https://reader036.vdocuments.mx/reader036/viewer/2022062805/5697c0261a28abf838cd5912/html5/thumbnails/17.jpg)
+
Thank YouBrigham Young University Physics DepartmentDr. David D. AllredBYU Thin Film Optics Research Group